Abstract
Polariton lasers are coherent light sources based on the condensation of exciton-polaritons in semiconductor microcavities, which occurs either in the kinetic or thermodynamic (Bose-Einstein) regime. Besides their fundamental interest, polariton lasers have the potential of extremely low operating thresholds. Here, we demonstrate ultra-low threshold polariton lasing at room temperature, using an all-dielectric, GaN membrane-based microcavity, with a spontaneously-formed zero-dimensional trap. The microcavity is fabricated using an innovative method, which involves photo-electrochemical etching of an InGaN sacrificial layer and allows for the incorporation of optimally-grown GaN active quantum wells inside a cavity with atomically-smooth surfaces. The resulting structure presents near-theoretical Q-factors and pronounced strong-coupling effects, with a record-high Rabi splitting of 64 meV at room-temperature. Polariton lasing is observed at threshold carrier densities 2.5 orders of magnitude lower than the exciton saturation density. Above threshold, angle-resolved emission spectra reveal an ordered pattern in k-space, attributed to polariton condensation at discrete levels of a single confinement site. This confinement mechanism along with the high material and optical quality of the microcavity, accounts for the enhanced performance of our polariton laser, and pave the way for further developments in the area of robust room temperature polaritonic devices.
Similar content being viewed by others
Introduction
Exciton-polaritons are composite half-photon half-exciton states, existing inside semiconductor microcavities in the so called “strong-coupling” regime1. Due to their bosonic nature, polaritons were identified early-on, as a means to produce an unconventional “laser”, which does not require population inversion2. From a device point of view, polariton lasers are attractive for their potential to display extremely low thresholds of operation in comparison with conventional semiconductor lasers3. Room temperature operation of a GaAs polariton light emitting diode has been previously demonstrated4, 5. However, polariton lasers using GaAs6,7,8,9 or CdTe10 active layers are limited to cryogenic temperatures, due to their relatively weak exciton binding energy. Wide bandgap semiconductors are better suited for high temperature operation, based on their higher exciton binding energy and oscillator strength, as well as more efficient carrier relaxation due to enhanced exciton-phonon interaction. Several polariton lasing experiments at 300 K have been reported using GaN11,12,13,14 or ZnO15, 16 as active layers. GaN is the most interesting of these materials in view of its capabilities for electrical injection, since it can be doped both n- and p-type.
Previous demonstrations of GaN polariton lasing relied on bulk material11, quantum wells (QWs)12 or even nanowires13 as active medium. Realizations using bulk GaN or QWs present limitations imposed by the modest optical quality of the active layers, grown on highly mismatched silicon substrates17, or on strongly disordered AlInN/AlGaN distributed Bragg reflectors (DBRs)18. Better performance (lower threshold) is achieved in the case of a single defect-free GaN nanowire embedded in an all-dielectric microcavity. However, the nanowire approach is hardly scalable and electrical injection schemes are difficult to implement. Recently, an electrically injected polariton laser has been demonstrated, using bulk GaN as active layer in an in-plane edge-emitting microcavity14. The device has shown low current thresholds, but is rather complex to fabricate and certainly defies the benefits of vertical emission geometry.
In this article, we produce an ultra-low threshold, optically-pumped GaN QW polariton laser in the standard vertical geometry, operating at room temperature. Unlike previous works, the laser is fabricated by utilizing a photo-electrochemical (PEC) etching method19,20,21,22,23,24, which makes it possible to use optimally-grown GaN/AlGaN QWs as active medium, embedded in a 3λ/2-thick membrane with atomically-smooth surfaces. The PEC method is completed by the deposition of dielectric DBRs on both sides of the membrane. It should be noted that the method is fully compatible with electrical injection schemes, provided an appropriate PIN structure is incorporated within the membranes and contacts are made directly on them to bypass the high resistivity of the dielectric DBRs. The strong coupling regime is observed at 300 K with a Rabi splitting as high as 64 meV. Polariton lasing is observed under quasi-continuous excitation at an average threshold pumping power Pth = 4.5 W/cm2, corresponding to a threshold carrier density 2.5 orders of magnitude lower than the exciton saturation density. Such threshold is the lowest reported so far for a bulk or QW GaN polariton laser system. Interestingly, angle-resolved photoluminescence (PL) experiments above threshold, exhibit an ordered condensation pattern in k-space, attributed to quantum confinement of polaritons at a single trapping site. We argue that this trapping mechanism along with the high material and optical quality of the microcavity are at the origin of the ultra-low threshold observed in our polariton laser.
Results
The main steps for the fabrication of our GaN microcavity are illustrated in Figs 1 and S1, with details given in Methods. A schematic of the sample structure is shown in Fig. 1a, including the sacrificial InGaN layer to be removed by PEC etching. The sample is grown by molecular beam epitaxy on a GaN/Al2O3 template, in the optimal growth conditions to obtain a high optical quality of the active region. The quality of the as-grown GaN/Al0.05Ga0.95N QWs is confirmed prior to etching, by optical characterization. Specifically, the QW PL linewidth measured at 20 K is merely 7 meV, which is a state of the art value for GaN/AlGaN QWs25, going up to 28 meV at 300 K. The PL intensity drops only by a factor of 24 between 20 K and 300 K, whereas the lifetime of the QW emission at room temperature remains quite long, around 275 ps (Supplementary Fig. S2). The latter reflects the fact that non-radiative recombination channels are significantly reduced in our structure, compared to the QWs grown on monolithic nitride DBR where the room temperature lifetime is 10 ps26. The above characteristics make these optimally-grown QWs excellent candidates for polaritonic devices. Following PEC etching, the etched surface of the detached membranes is atomically smooth, as confirmed by atomic force microscopy (AFM) returning a root-mean-square (RMS) roughness of barely 0.65 nm over a 5 × 5 μm2 of scanned area (Supplementary Fig. S1). This value should be compared with the 3.4 nm RMS roughness26, measured on the surface of a monolithic AlInN/GaN DBR used in hybrid GaN polariton lasers11, 12. In the next step, the membranes are transferred onto a bottom SiO2/Ta2O5 DBR, thus forming a half-microcavity. The reflectivity spectrum from such a half-microcavity at 300 K is shown in Supplementary Fig. S1c, depicting a pronounced negatively-detuned cavity mode with a Q-factor of ~85, along with a QW excitonic feature. A prior knowledge of the cavity mode position is crucial for the precise design and deposition of the top HfO2/Al2O3 DBR in order to form a full microcavity, as shown in Fig. 1b.
To establish the polaritonic properties of the full microcavity structures, a study of angle-resolved PL as a function of temperature is performed on a membrane, henceforth labelled “membrane 1”, using the k-space setup in imaging mode (cf. Methods). Figure 2a depicts the lower polariton branch (LPB) dispersion at 20 K, showing distinct strong coupling behaviour at large angles, where the LPB flattens out due to interaction of the cavity mode with the QW excitons. The position of the QW excitons is marked by the straight line corresponding to emission from “uncoupled” QW excitons, i.e. weakly-coupled QWs which are not at the antinodes of the standing wave. The upper polariton branch (UPB) is not observed in our experiments, something typical for nitride microcavities, where UPB features are either weak12 or not visible11.
As the temperature increases (cf. Fig. 2b–d), the QW exciton approaches the cavity mode and the LPB dispersion redshifts and becomes flatter. The LPB-to-exciton redshift ratio is around 2:3. At 230 K (Fig. 2c), we distinguish an additional branch at large angles with dispersive characteristics, which corresponds to the middle polariton branch (MPB) due to photon coupling with the excitons located at the 25 nm GaN spacer (cf. sample description in Methods). In Supplementary Fig. S3, the MPB is visible already at 80 K in the less negatively-detuned “membrane 2”. At 300 K (Fig. 2d), the uncoupled excitons lose intensity while the dispersive nature of the MPB and its anti-crossing with the LPB becomes more visible. An increase in the LPB linewidth is also observed with temperature, in line with phonon-related exciton broadening27.
The room temperature PL spectrum obtained at 10° from membrane 1, using the k-space setup in spectroscopy mode, is shown in Fig. 1c (solid line). The narrow line at 3.402 eV having a linewidth of 10.8 meV corresponds to the LPB, whereas the weaker peak at 3.453 eV is associated to uncoupled QW excitons. In order to extract the cavity Q-factor, a transfer matrix model28, 29 is used to estimate the absorption spectrum at an incident angle of 10°, which is then used to fit the PL data assuming direct proportionality between absorption and spontaneous emission30. Two excitons are defined in the model: the QW exciton at 3.453 eV and the GaN spacer exciton at 3.422 eV, each containing contributions from the A and B excitons of the respective sections, and having a homogeneous linewidth of 28 meV at 300 K. The latter was confirmed by PL measurements on bulk and QW samples, giving very similar results. Inhomogeneous broadening effects are ignored here, based on the much smaller exciton linewidths at low temperature. As shown in Fig. 1c, the model (red-dashed line) precisely simulates the experimental data assuming a cavity mode at 3.415 eV with linewidth of ≈1.93 meV, membrane thickness of ≈206 nm, and losses of 50 cm−1 and 100 cm−1 in the DBR mirrors and active region, respectively. The corresponding Q-factor is ≈1770, which is close to the theoretical Q-factor of ≈2350, estimated based on the same model, assuming no losses in the cavity.
To account for the observed polariton branches and estimate the Rabi splitting of the system, a Hamiltonian model29 described in detail in the Supplementary Information is used to simulate the angle-dependent data at 300 K, with parameters in line with the transfer matrix model. The two excitons, indicated as red dashed lines in Fig. 2d, interact with the cavity mode (green line) according to their respective coupling constants, forming three polariton branches and reproducing precisely the experimental dispersions. The unusual shape of the dispersions at the anticrossing between LPB and MPB is due to the relatively weak coupling constant of the bulk excitons in our structure, as discussed in the Supplementary Information. The splitting of the cavity mode and UPB at large angles is due to TE/TM splitting31. The Rabi splitting of the system is estimated to be ≈64 meV at the anti-crossing point between the LPB and UPB dispersions. To ensure the accuracy of the model, the PL response of two other membranes - membranes 2 and 3, with different detunings, is accurately simulated (cf. Supplementary Fig. S4) by simply varying their respective thickness, keeping all other parameters constant, including the coupling strength of the excitons, returning very similar Rabi splitting values.
The non-linear optical properties have been studied on membrane 5 at 300 K, exciting with a pulsed laser at 266 nm. Figure 3 presents the evolution of the angle-dependent PL emission as a function of the excitation power, reported as the ratio with respect to the average pumping power at threshold (Pth = 4.5 W/cm2). All images here are obtained using k-space setup in imaging mode. In parallel, Fig. 4a presents the corresponding PL spectra around k || = 0, recorded using the same setup in spectroscopy mode. At low powers (0.39 · Pth), a dispersion curve is observed in Fig. 3a, similar to Fig. 2d, containing LPB and MPB contributions, as fitted (solid lines) using the Hamiltonian model. We denote the lower polariton branch as LPB1, also indicated in the spectra of Fig. 4a. In Fig. 4a, with increasing power, LPB1 broadens without any visible change of its energy position. At 0.81 · Pth, a second peak appears at higher energy (LPB2), which becomes clearly resolved just below threshold, at 0.96 · Pth. The two vertical dot-dashed lines are guides to the eye showing the evolution of the two LPB’s with power. The LPB2 is also observable in the k-space data of Fig. 3b, showing a clear dispersive behaviour, which is also simulated in the Hamiltonian model (dot-dashed line) by solely adjusting the cavity thickness with respect to LPB1. Figure 4b plots the power-dependent evolution of the spectrally integrated intensity around the LPB lines. The onset of lasing is visible at extremely low average power densities of 4.5 W/cm2 (Pth), marked with a dashed line. This value is four times lower compared to similar experiments on GaN QW microcavities12 using same excitation source. The integrated intensity shows an S-like behaviour with pump power, corresponding to 1/β ≈ 50, about two orders of magnitude lower compared to previous works using dielectric DBR only on one side11. It should be noted that in the context of a polariton laser the β-factor represents the fraction of polaritons spontaneously-emitted in the mode undergoing stimulated scattering11.
Above threshold, the spectra reveal three narrow peaks in the energy range between LPB1 and LPB2, as depicted in the inset of Fig. 4a, marked as ‘1’, ‘2’ and ‘3’. Level ‘3’ has the highest intensity at threshold, followed by ‘2’ and finally ‘1’. The corresponding image in Fig. 3c, at 1.04 · Pth, shows a distinct multimode pattern in k-space corresponding to levels ‘2’ and ‘3’, whereas the emission from level ‘1’ is relatively weak. The system is in the strong coupling regime, as visible from the dispersion being flatter and well below the cavity modes corresponding to LPB1 and LPB2 (green solid and dashed lines), confirming polariton lasing vs. photonic lasing. The different levels follow an interesting power-dependent behaviour as seen in Fig. 3c–f and inset of Fig. 4a. Level ‘3’, first blueshifts and then redshifts with increasing pump power, whereas levels ‘1’ and ‘2’ redshift, with ‘2’ gaining maximum intensity already at 1.07 · Pth. At higher powers, maximum lasing occurs from level ‘1’ followed by ‘2’ and ‘3’.
In Fig. 4c, we plot the occupation number as a function of angle for various pump powers, defined for a given power as the ratio of the spectrally-integrated PL intensity at each angle over the corresponding cavity fraction \({|{C}_{{k}_{\parallel }}|}^{2}(\theta )\) shown in Supplementary Fig. S5. The occupation number is normalized to unity, at k || = 0, just below threshold (0.96 · Pth). At powers below threshold, the occupation increases linearly with power, and exhibit higher occupation at large angles due to the bottleneck effect32,33,34. The evidence of bottleneck up to threshold powers indicates that the relaxation time of LPB polaritons remains longer than their lifetime at k || = 0. This implies that polariton lasing/condensation occurs in the kinetic35 rather than the thermodynamic regime10. Just above threshold, the occupation at larger angles somewhat subsides, with a tremendous increase around k || = 0, as expected for a polariton laser10,11,12, 26.
Polariton lasing is further confirmed by the calculation of the exciton densities involved in the process, based on the excitation level and a simple system of rate equations described in the Supplementary Information. The obtained threshold polariton density per laser pulse and per QW at k || = 0 is N 1 ≈ 2.24 × 1010 cm−2. Considering the exciton fraction |X 0|2 for LPB1 at k || = 0 (cf. Supplementary Information and Supplementary Fig. S5a), the corresponding threshold exciton density at k || = 0 is given by N X = N · |X 0|2 ≈ 7 × 109 cm−2, which is 2.5 orders of magnitude lower than the exciton saturation density in GaN QWs36, and 3.5 orders of magnitude lower than the electron-hole pair density needed for population inversion in a standard GaN laser diode37. In line with the low exciton densities in our system, we also note the absence of any noticeable blueshift of LPB1 up to threshold (cf. Fig. 4a), in contrast to previous works where significant blueshifts have been reported11,12,13.
In fact, assuming that the blueshift of the LPB line is less than 0.2 meV, which is the detection limit of our system, we obtain as described in the Supplementary Information the upper bound for the total exciton density at threshold of N 2D ≤ 4.7 × 1010 cm−2. This value is more than 40 times smaller than the exciton saturation density in these QWs, further demonstrating polariton lasing.
Having established ultra-low-threshold polariton lasing, we turn now our attention to the k-space pattern of Fig. 3. The ordered pattern can be attributed to polariton condensation in a single spontaneously-formed zero-dimensional polariton trap16, 38, similarly to observations in engineered polariton landscapes39,40,41,42,43,44. Inhomogeneities related to the epitaxial growth and etching process can lead to membrane thickness variations of ≈1−2% (≈2−4 nm), which can act as polariton localization sites. Generally, the simultaneous observation of multiple confinement sites gives rise to a disordered pattern in k-space, like the one shown in Supplementary Fig. S6. To explain the data in Fig. 3, we assume the existence in our membrane of two types of uniformly-etched flat regions having a thickness difference of 3.6 nm, corresponding to the 20.9 meV energy difference between the cavity modes of the two LPBs in Fig. 3(c–f). The confinement site consists of a small-in-size LPB1 insertion, in a wider LPB2 region, as schematically depicted in the “inverted” energy profile of Fig. 4d. For simplicity, we assume a square-like trap, and solve the two-dimensional Schrödinger’s equation:
where V(x, y) = V(x) + V(y) is the in-plane square-shaped potential trap having a depth of ~20.9 meV, Ψ pol (x, y) is the polariton envelope wavefunction and m pol is the polariton effective mass, estimated here to be 6.87 × 10−5 times the free electron mass based on the cavity/exciton fraction for LPB1 at k || = 0. Using the trap width as the sole adjustable parameter, the discrete (1, 2, 3) energy levels in Fig. 5a just above threshold (1.04 · Pth), can be nicely reproduced by the simulations (dashed lines) for a trap width of 1.53 μm. The real-space wavefunctions fitting the three levels (1, 2, 3) are plotted in Fig. 5(b–d). Using the standard notation for two-dimensional wavefunctions in a square potential well, the ground wavefunction Ψ pol (1, 1) shown in Fig. 5b, accurately simulates level ‘1’, both in energy and shape in k-space. Similarly, the superposition of the degenerate states Ψ pol (1, 2) and Ψ pol (2, 1), shown in Fig. 5c, precisely matches the energy location of level ‘2’, as well as its distribution in k-space with a central node. Finally, level ‘3’ is located between the levels associated to Ψ pol (2, 2) and the degenerate states Ψ pol (1, 3) and Ψ pol (3, 1). The superposition of these three states in Fig. 5d reproduces the k-space pattern of level ‘3’.
The variation in the relative intensity of levels 1, 2, and 3 with the pump power, displayed in Fig. 3c–f and inset of Fig. 4a, can be understood as follows. At low power, most of the polariton emission comes from the LPB1. Polaritons corresponding to the LPB2 relax either into the LPB1 regions or into the square-like trap, losing visibility at low powers. With increasing pump power, the polariton density increases, producing a broadening of LPB1. At powers just below threshold, the occupation of LPB1 seems to saturate, leading to a significant increase of the polariton density in the LPB2. Interestingly, polariton lasing occurs first at the confined levels of the trap, strongly suggesting the beneficial role of zero-dimensional confinement in the condensation process45, most likely due to relaxation of the exciton-phonon selection rules. Just above threshold, at 1.04 · Pth, level ‘3’ has the highest intensity, followed by level ‘2’ and ‘1’. This can be explained by the longer polariton lifetime of level ‘3’, as it is closer to the excitonic reservoir than the lower levels. In other words, it is easier for the polariton population to build-up in level ‘3’, followed by level ‘2’ and finally ‘1’. The high intensity of level ‘3’ just above threshold, can also be attributed to the fact that it consists of three near-degenerate states, in comparison with level ‘2’ consisting of two degenerate states, and finally level ‘1’ having just a single state38. Beyond threshold, stimulated scattering33, 34 takes over, driving more efficiently polaritons into the lower states, as shown in the inset of Fig. 4a. Therefore at 1.26 · Pth, level ‘1’ has the highest intensity, followed by levels ‘2’ and ‘3’. It should be noted that the power dependence of the multi-level emission above threshold is consistent with the fact that our polariton laser is still in the kinetic regime.
To conclude, an ultra-low threshold GaN polariton laser is demonstrated at room temperature, using a high-Q, all-dielectric, quantum-well microcavity, with a spontaneously-formed zero-dimensional trap. Polariton lasing is observed at carrier densities, 2.5 orders of magnitude lower than the exciton saturation density and 3.5 orders of magnitude lower than the electron-hole pair densities needed for population inversion in a conventional laser. The lasing spectra reveal an ordered pattern in k-space, attributed to polariton condensation at discrete levels of a single confinement site. The zero-dimensional confinement along with the superior material and optical quality of the structure, explain the enhanced characteristics of our polariton laser. Our results are likely to spur new activity in the area of robust room temperature polaritonics.
Methods
The GaN layers are grown along the [0001] direction by plasma-assisted molecular beam epitaxy (MBE), on an n-type GaN template grown on c-sapphire by metalorganic chemical vapour deposition. The basic structure, depicted in Fig. 1a, consists of 33 pairs of GaN/Al0.05Ga0.95N (2.7 nm/2.7 nm) QWs deposited on a 25-nm-thick GaN spacer layer, which separates the QWs from the 25-nm-thick In0.12Ga0.88N sacrificial layer. The room-temperature PL emission of the In0.12Ga0.88N layer peaks at 430 nm. The GaN/Al0.05Ga0.95N heterostructure is not as “shallow” as one may think based on the low Al-content. The bandgap difference between well and barrier layers is already ~100 meV, which including strain effects is distributed 60:40 in the conduction and heavy-hole lineups, respectively, providing a good base for sufficient confinement. In addition, the carrier confinement is further enhanced by the sawtooth-like potential profiles due to the polarization-induced internal fields, present in all nitride heterostructures grown along a polar axis. Experimentally, we know that the thermal escape over the barrier layers is not a limiting factor in our case based on the relatively small PL intensity drop between low and room temperature, and the fact that the corresponding activation energy deduced from the Arrhenius plot of Supplementary Figure S2a is ~26 meV, which is three times smaller compared to the ~75 meV energy difference between QW emission and barrier energy gap. The dimensions of the membranes are defined by means of optical lithography using a thick photoresist AZ 9260. Then, samples are dry etched in a conventional Reactive Ion Etching system using BCl3 and Cl2, leading to rectangular mesas 700 nm deep. The remaining photoresist mask is removed by acetone/propanol/Di-H2O, while a short exposure to O2 plasma further ensures that no photoresist residues are left on the sample surface. Then, PEC etching of the sacrificial layer is performed inside an electrochemical cell, using KOH electrolyte with a molarity as low as 0.0004, while illuminating the sample with a 405 nm laser diode. The detailed description of the procedure can be found elsewhere19, 21. An optical microscope image of the sample after PEC etching (Supplementary Fig. S1a) shows detached membranes lying on the surface. For the transfer process, a proposed liquid-mediated adhesion mechanism is employed in order for the membranes to be detached from the top of the mesas and transfer top-face down onto a DBR structure, deposited on sapphire by e-beam evaporation and consisting of 11 pairs of λ/4 SiO2/Ta2O5 layers with respective nominal thicknesses of 59.6 nm and 44 nm, forming thus a half-microcavity sample (inset of Supplementary Fig. S1c). The full microcavity is completed by covering the membrane with 10 pairs of λ/4 HfO2/Al2O3 (40.3 nm/50.6 nm) DBRs using atomic layer deposition (ALD). The cross-sectional scanning electron microscopy (SEM) image in Fig. 1b shows a membrane sandwiched between the two sets of DBRs.
All the results in this paper are based on five specific membranes, which are described in Table 1. Their precise thickness is estimated from linear transfer matrix and Hamiltonian model simulations. It should be noted that in these calculations, the membrane thickness is the only adjustable parameter.
Most optical measurements were performed using an Acton triple-grating imaging spectrograph, with a focal length of 0.5 m, a resolution of 0.02 nm at 435.8 nm, and an accuracy of ±0.02 nm. The spectra were recorded using a 600 grooves/mm grating, blazed at 300 nm. For PL measurements, the sample is excited with a continuous wave He-Cd laser emitting at 325 nm. The lasing measurements are performed by excitation with a frequency-quadrupled Nd-YAG (neodymium-doped yttrium aluminum garnet) laser emitting at 266 nm, with a pulse repetition rate of 7.58 kHz and a pulse width of 0.51 ns. At this wavelength, the absorption coefficient of GaN is ~1.8 · 105 cm−1 46, implying that more than 97% of the incident pump light is absorbed by the 200 nm-thick membranes during the lasing experiments. Reflectivity characterization is performed using a 150 W Xe lamp. For PL and reflectivity measurements, samples are placed on the cold finger of a He closed-circuit cryostat. The excitation beam, at normal incidence, is focused using an aspherical lens with a numerical aperture NA = 0.63, and the PL/reflectivity signal is collected through the same optical path using a beam splitter. The focus of the aspherical lens is adjusted for the main emission wavelength, around 360 nm. As a result, the 325 nm laser is focused down to a diameter of 9 μm, and the 266 nm laser presents a spot size of 60 × 10 μm2, due to its elliptical profile. The PL/reflectivity is focused onto the spectrometer using a final collection lens.
For angle-dependent measurements, an additional lens (Fourier plane imaging lens) is positioned before the final lens, allowing PL/reflectivity imaging of the Fourier plane into the spectrometer (k-space setup). This k-space setup can be operated in two modes: (1) spectroscopy mode, where signal from only a few angles is probed and averaged, giving a single spectrum, and (2) imaging mode, where the entire k-space as a function of angle, limited by the NA of the system, is recorded in a single shot.
Time-resolved PL measurements were performed using a Hamamatsu M5675 Streak camera and a frequency-tripled Ti:Sapphire laser emitting at 266 nm, with a pulse width of 150 fs, repetition rate of 76 MHz and an average power density of 2 W/cm2.
References
Weisbuch, C., Nishioka, M., Ishikawa, A. & Arakawa, Y. Observation of the coupled exciton-photon mode splitting in a semiconductor quantum microcavity. Phys. Rev. Lett. 69, 3314–3317 (1992).
İmamoğlu, A., Ram, R. J., Pau, S. & Yamamoto, Y. Nonequilibrium condensates and lasers without inversion: Exciton-polariton lasers. Phys. Rev. A 53, 4250–4253 (1996).
Deng, H., Weihs, G., Snoke, D., Bloch, J. & Yamamoto, Y. Polariton lasing vs. photon lasing in a semiconductor microcavity. Proc. Natl. Acad. Sci. 100, 15318–15323 (2003).
Tsintzos, S. I., Pelekanos, N. T., Konstantinidis, G., Hatzopoulos, Z. & Savvidis, P. G. A GaAs polariton light-emitting diode operating near room temperature. Nature 453, 372–375 (2008).
Tsintzos, S. I., Savvidis, P. G., Deligeorgis, G., Hatzopoulos, Z. & Pelekanos, N. T. Room temperature GaAs exciton-polariton light emitting diode. Appl. Phys. Lett. 94, 071109 (2009).
Bhattacharya, P., Xiao, B., Das, A., Bhowmick, S. & Heo, J. Solid State Electrically Injected Exciton-Polariton Laser. Phys. Rev. Lett. 110, 206403 (2013).
Schneider, C. et al. An electrically pumped polariton laser. Nature 497, 348–352 (2013).
Baten, M. Z. et al. GaAs-based high temperature electrically pumped polariton laser. Appl. Phys. Lett. 104, 231119 (2014).
Sala, V. G. et al. Stochastic precession of the polarization in a polariton laser. Phys. Rev. B 93, 115313 (2016).
Kasprzak, J. et al. Bose–Einstein condensation of exciton polaritons. Nature 443, 409–414 (2006).
Christopoulos, S. et al. Room-Temperature Polariton Lasing in Semiconductor Microcavities. Phys. Rev. Lett. 98, 126405 (2007).
Christmann, G., Butté, R., Feltin, E., Carlin, J.-F. & Grandjean, N. Room temperature polariton lasing in a GaN∕AlGaN multiple quantum well microcavity. Appl. Phys. Lett. 93, 051102 (2008).
Das, A. et al. Room Temperature Ultralow Threshold GaN Nanowire Polariton Laser. Phys. Rev. Lett. 107, 066405 (2011).
Bhattacharya, P. et al. Room Temperature Electrically Injected Polariton Laser. Phys. Rev. Lett. 112, 236802 (2014).
Lai, Y.-Y., Lan, Y.-P. & Lu, T.-C. Strong light–matter interaction in ZnO microcavities. Light Sci. Appl. 2, e76 (2013).
Li, F. et al. From Excitonic to Photonic Polariton Condensate in a ZnO-Based Microcavity. Phys. Rev. Lett. 110, 196406 (2013).
Bejtka, K. et al. Strong light-matter coupling in ultrathin double dielectric mirror GaN microcavities. Appl. Phys. Lett. 92, 241105 (2008).
Christmann, G. et al. Impact of disorder on high quality factor III-V nitride microcavities. Appl. Phys. Lett. 89, 261101 (2006).
Trichas, E. et al. Bragg polariton luminescence from a GaN membrane embedded in all dielectric microcavity. Appl. Phys. Lett. 98, 221101 (2011).
Daskalakis, K. S. et al. All-dielectric GaN microcavity: Strong coupling and lasing at room temperature. Appl. Phys. Lett. 102, 101113 (2013).
Jayaprakash, R. et al. Ultra-smooth GaN membranes by photo-electrochemical etching for photonic applications. J. Mater. Sci. 49, 4018–4024 (2014).
Tamboli, A. C. et al. Room-temperature continuous-wave lasing in GaN/InGaN microdisks. Nat. Photonics 1, 61–64 (2007).
Tamboli, A. C. et al. Smooth Top-Down Photoelectrochemical Etching of m-Plane GaN. J. Electrochem. Soc. 156, H47 (2009).
Aharonovich, I. et al. Low threshold, room-temperature microdisk lasers in the blue spectral range. Appl. Phys. Lett. 103, 021112 (2013).
Feltin, E., Simeonov, D., Carlin, J.-F., Butté, R. & Grandjean, N. Narrow UV emission from homogeneous GaN∕AlGaN quantum wells. Appl. Phys. Lett. 90, 021905 (2007).
Christmann, G. In III-nitride Based Microcavities: Towards Polariton Condensation at Room Temperature. Ph.D Thesis, Ecole Polytechnique Federale de Lausanne (2009).
Jayaprakash, R. et al. Extraction of absorption coefficients from as-grown GaN nanowires on opaque substrates using all-optical method. Opt. Express 22, 19555 (2014).
Furman, S. A. & Tikhonravov, A. V. In Basics of optics of multilayer systems, 1–102 (Editions Frontières, Gif-sur Yvette 1992).
Deng, H., Haug, H. & Yamamoto, Y. Exciton-polariton Bose-Einstein condensation. Rev. Mod. Phys. 82, 1489–1537 (2010).
Van Roosbroeck, W. & Shockley, W. Photon-radiative recombination of electrons and holes in germanium. Phys. Rev. 94, 1558–1560 (1954).
Panzarini, G. et al. Exciton-light coupling in single and coupled semiconductor microcavities: Polariton dispersion and polarization splitting. Phys. Rev. B 59, 5082–5089 (1999).
Butté, R. et al. Transition from strong to weak coupling and the onset of lasing in semiconductor microcavities. Phys. Rev. B 65, 205310 (2002).
Skolnick, M. S., Tartakovskii, A. I., Butté, R., Whittaker, D. M. & Stevenson, R. M. High-occupancy effects and stimulation phenomena in semiconductor microcavities. IEEE J. Sel. Top. Quantum Electron. 8, 1060–1071 (2002).
Stokker-Cheregi, F. et al. Polariton relaxation bottleneck and its thermal suppression in bulk GaN microcavities. Appl. Phys. Lett. 92, 042119 (2008).
Levrat, J. et al. Condensation phase diagram of cavity polaritons in GaN-based microcavities: Experiment and theory. Phys. Rev. B 81, 125305 (2010).
Rossbach, G. et al. High-temperature Mott transition in wide-band-gap semiconductor quantum wells. Phys. Rev. B 90, 201308 (2014).
Dialynas, G. E., Deligeorgis, G., Zervos, M. & Pelekanos, N. T. Internal field effects on the lasing characteristics of InGaN/GaN quantum well lasers. J. Appl. Phys. 104, 113101 (2008).
Sanvitto, D. et al. Exciton-polariton condensation in a natural two-dimensional trap. Phys. Rev. B 80, 045301 (2009).
El Daïf, O. et al. Polariton quantum boxes in semiconductor microcavities. Appl. Phys. Lett. 88, 061105 (2006).
Kaitouni, R. I. et al. Engineering the spatial confinement of exciton polaritons in semiconductors. Phys. Rev. B 74, 155311 (2006).
Lai, C. W. et al. Coherent zero-state and π-state in an exciton–polariton condensate array. Nature 450, 529–532 (2007).
Winkler, K. et al. A polariton condensate in a photonic crystal potential landscape. New J. Phys. 17, 23001 (2015).
Tao, R., Kamide, K., Arita, M., Kako, S. & Arakawa, Y. Room-Temperature Observation of Trapped Exciton-Polariton Emission in GaN/AlGaN Microcavities with Air-Gap/III-Nitride Distributed Bragg Reflectors. ACS Photonics 3, 1182–1187 (2016).
Schneider, C. et al. Exciton-polariton trapping and potential landscape engineering. Reports Prog. Phys. 80, 16503 (2017).
Bajoni, D. et al. Polariton Laser Using Single Micropillar GaAs-GaAlAs Semiconductor Cavities. Phys. Rev. Lett. 100, 047401 (2008).
Muth, J. F. et al. Absorption coefficient, energy gap, exciton binding energy, and recombination lifetime of GaN obtained from transmission measurements. Appl. Phys. Lett. 71, 2572 (1997).
Acknowledgements
The authors acknowledge fruitful discussions with Dr. Le Si Dang. This work is funded by the European FP7 Initial Training Network “ICARUS”, the European Social Fund and National resources through the THALES project “NANOPHOS” (MIS-377292) and the KRIPIS research project “PROENYL” (MIS-448305), and the Chair of Excellence program of the “Laboratoire d’excellence LANEF in Grenoble (ANR-10-LABX-51-01)”.
Author information
Authors and Affiliations
Contributions
R.J. carried out the etching and optical experiments, performed simulations and data analysis, and drafted a first manuscript. F.G.K. patterned mesas prior to etching and performed the membrane transfer. G.C. made substantial contributions in the experiments and interpretation of data. K.T. performed SEM and AFM experiments. M.H. deposited the top DBR. B.G. carried out the time-resolved PL. E.M. provided the MBE samples and revised critically the manuscript. N.T.P. directed the research project and produced final manuscript. All authors discussed the results and contributed to the final manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Jayaprakash, R., Kalaitzakis, F.G., Christmann, G. et al. Ultra-low threshold polariton lasing at room temperature in a GaN membrane microcavity with a zero-dimensional trap. Sci Rep 7, 5542 (2017). https://doi.org/10.1038/s41598-017-06125-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-06125-y
- Springer Nature Limited
This article is cited by
-
Strong coupling of hybrid states of light and matter in cavity-coupled quantum dot solids
Scientific Reports (2023)
-
Steady state oscillations of circular currents in concentric polariton condensates
Scientific Reports (2023)
-
Deterministic and replaceable transfer of silver flakes for microcavities
Frontiers of Physics (2023)
-
Polariton condensation in an organic microcavity utilising a hybrid metal-DBR mirror
Scientific Reports (2021)