Abstract
Single-phase concentrated solid-solution alloys (SP-CSAs) have recently gained unprecedented attention due to their promising properties. To understand effects of alloying elements on irradiation-induced defect production, recombination and evolution, an integrated study of ion irradiation, ion beam analysis and atomistic simulations are carried out on a unique set of model crystals with increasing chemical complexity, from pure Ni to Ni80Fe20, Ni50Fe50, and Ni80Cr20 binaries, and to a more complex Ni40Fe40Cr20 alloy. Both experimental and simulation results suggest that the binary and ternary alloys exhibit higher radiation resistance than elemental Ni. The modeling work predicts that Ni40Fe40Cr20 has the best radiation tolerance, with the number of surviving Frenkel pairs being factors of 2.0 and 1.4 lower than pure Ni and the 80:20 binary alloys, respectively. While the reduced defect mobility in SP-CSAs is identified as a general mechanism leading to slower growth of large defect clusters, the effect of specific alloying elements on suppression of damage accumulation is clearly demonstrated. This work suggests that concentrated solid-solution provides an effective way to enhance radiation tolerance by creating elemental alternation at the atomic level. The demonstrated chemical effects on defect dynamics may inspire new design principles of radiation-tolerant structural alloys for advanced energy systems.
Similar content being viewed by others
Introduction
A new direction of research to substantially enhance alloy performance has been stimulated in material science due to the recent success in fabrication of single-phase concentrated solid-solution alloys (SP-CSAs)1,2,3,4,5. Historically, alloy development with desired performance focused on traditional alloys, where enhanced radiation resistance relied largely on unique microstructural heterogeneity to mitigate displacement damage6. In contrast to traditional alloys (containing one or two principle elements), SP-CSAs contain two to five or more elements at high concentration, sometimes at equal or near-equal concentration. As a result, the concept of “solvent” and “solute” in traditional alloys is irrelevant6. Although SP-CSAs contain 2–5 equal or near-equal concentration of elements, interestingly almost all SP-CSAs have either fcc or bcc structures. The formation of phases depends mainly on the enthalpy of mixing (ΔH mix ), entropy of mixing (ΔS mix ) and atomic size difference (δ)3, 7. According to Gibbs free energy of mixing ΔG mix = ΔH mix − TΔS mix , entropy can stabilize a phase by lowering free energy with higher entropy, provided that enthalpy is constant.
In these CSAs, the random arrangement of multiple elemental species on a crystalline lattice results in atomic-level elemental alternation that creates disordered local chemical environments. Two distinctive intrinsic properties are expected: (1) unique electronic structures that significantly enhances scattering of electrons, reduces the thermal conductivity and affects energy dissipation; and (2) unique site-to-site lattice distortions that lead to complex energy landscapes and affect defect migration and mass transport. Compared to traditional alloys, SP-CSAs possess improved mechanical and chemical properties7,8,9,10, which may be attributed to the intrinsic properties of CSAs. The next generation nuclear power reactors will undergo harsh service conditions that include intense radiation flux, higher operating temperature, severe corrosive environment and high stress11, 12. SP-CSAs might be good candidate materials for nuclear power applications, if their superior mechanical properties can be complemented with high radiation resistance13. These alloys might also find applications in high-energy rare isotope beam facilities and concentrating solar power plants having extreme corrosive and radiation environments14, 15.
Austenitic steels are widely used as core structural material, as well as used for cladding on the inside surface of the pressure vessel of current water-cooled nuclear fission reactors. They are also proposed for next generation fission and fusion reactors, where excellent radiation resistance is the primary concern12, 16. Current austenitic steels are susceptible to void swelling, irradiation-assisted stress corrosion cracking, decrease in fracture toughness and radiation-induced segregation (RIS)17, 18. The RIS can provoke phase instability, embrittlement, and stress corrosion cracking issues12, 19, whereas void swelling can trigger unacceptable dimensional expansion and can lead to degradation of fracture toughness18, 20. Due to these adverse effects of radiation, austenitic steels are facing new challenges in the applications of next generation nuclear reactors. Recently, systematic ion beam study on FeNiMnCr SP-CSA has been peroformed at temperatures ranging from room temperature to 700 °C and midrange doses of 0.03–10 dpa using 5.8 MeV Ni ion. The FeNiMnCr alloy has demonestrated significant suppression of RIS, no observable void formation and lower defect cluster size compared to conventional single phase Fe-Cr-Ni and Fe-Cr-Mn austenitic alloys21. An enhancement of radiation tolerance with the suppression of void formation have been reported in Ni-based CSAs at elevated temperature with a peak damage dose of 60 dpa5.
Despite the recent intensive investigations on SP-CSAs, relatively few studies have been performed on their response to prolonged irradiation. Egami et al. have reported that, due to atomic level stresses and chemical heterogeneity, thin films of simple model binary alloys and Zr-Hf-Nb solid solution alloys show high radiation resistance under electron irradiation13. Molecular dynamics (MD) simulations of the cumulative irradiation of Fe-based binary alloys, having different percentages of Ni and Cr, show more damage accumulation in the face-centered cubic (fcc) alloys than in the body-centered cubic (bcc) ones22. Recently, MD simulations and experimental studies on irradiation of equiatomic single-phase NiFe and NiCoCr alloys have demonstrated noticeable damage reduction, as compared to pure Ni23. The observed damage reduction is explained by the reduced dislocation mobility, which results in smaller and fewer defect clusters in the alloys compared to elemental Ni. This result is supported by a recent experimental study on irradiation induced defect evolution in Ni and NiFe binary alloys; where at low-fluences, the equiatomic NiFe alloy demonstrated higher radiation resistance than pure Ni24.
In reactor environments, irradiation-induced point defect formation, migration and evolution are the primary reasons for the microstructural changes that affect the performance of structural materials. Controlling defect formation and migration in structural materials is, therefore, critical for designing materials with high radiation tolerance. While a few studies have demonstrated the potential benefit of improved irradiation resistance in SP-CSAs, especially the link between energy dissipation and defect evolution due to ferro- and anti-ferromagnetic interactions (the first distinctive aspect of these SP-CSAs)25, we utilize a set of model systems with increasing chemical complexity to reveal the second distinctive aspect of SP-CSAs by showing a unique link between modified energy landscapes and defect dynamic processes – an underappreciated but remarkable research field.
In this paper, we study the production and accumulation of point defects in pure Ni and Ni-based binary and ternary alloys. The binary and ternary alloys selected for this study are all single-phase concentrated solid solutions with various chemical complexity and yet have a simple fcc structure26. This model system includes pure Ni, Ni80Fe20 and Ni50Fe50 with increasing elemental randomness at the atomic level. The two binaries (Ni80Fe20 and Ni80Cr20) result from randomly replacing 20% of the atoms in Ni with either Fe or Cr, and the ternary Ni40Fe40Cr20 is formed by further replacing half of the Ni atoms in Ni80Cr20 with Fe atoms. Some of the model crystals of interest in this work (without the element Co that was included in some previous studies of stable concentrated solid-solution alloys25,26,27) are not far from a few of the alloys already under consideration for nuclear applications, but are based on different design principals12, 28. In this work, damage production and accumulation in these alloys due to irradiation are investigated using ion irradiation experiments and MD simulations. Although, the radiation dose (<0.13 dpa) of current work is considerably lower than the realistic applications, it demonstrates that the damage behavior of model SP-CSAs can be modified at the early stage in radiation environment. Our hypothesis is that modifying alloy chemical complexity (composition complexity) will enable us to control defect dynamics at the early stage of radiation damage to ultimately enhance radiation tolerance at the later stage under extreme radiation conditions29. The research focus is to: (1) understand the chemical effect of changing alloy compositions and elements but still retaining a simple fcc structure; and (2) demonstrate that controlled atomic-level elemental alternation in concentrated solid-solution alloys is an effective design principle to create modified energy landscapes that can have substantial impact on defect evolution. Such knowledge is important for new defect engineering paradigms benefiting broader science and technology.
Results and Discussion
Irradiation response in Ni and Ni-based alloys
Recent studies have suggested that compositional complexity strongly affects the electrical, thermal and magnetic properties of concentrated solid-solution alloys25, 26. Electrical resistivity exhibits a strong dependence on the type of elements, and the CSAs containing Cr exhibit an order of magnitude higher resistivity than those alloys without Cr. To evaluate alloying or concentration effects, the crystals chosen in this work have different percentages of Fe and Cr content. By investigating the irradiation response of model Ni and Ni alloys, we will gain insights on how modifying alloying elements and concentration affects defect dynamics.
The RBS/C spectra for 1.5 MeV Ni ion irradiated elemental Ni, Ni80Fe20, Ni80Cr20, and Ni50Fe50 are shown in Fig. 1a–d, respectively, together with the spectra for Ni40Fe40Cr20 irradiated with 1.5 MeV Mn ions (Fig. 1e). A virgin spectrum along the <001> direction, which corresponds to pristine single crystals, and a random spectrum, which corresponds to a fully amorphous structure, are included. The χ min for the virgin spectra is less than 6% that indicates the high crystalline quality for all the samples. The backscattering yield increases with increasing ion fluence, which suggests accumulation of radiation damage. The 80:20 binaries show better radiation resistance compared to elemental Ni at low ion fluences (<6.0 × 1013 cm−2), as indicated by the lower backscattering yields. When comparing the response of Ni80Fe20 and Ni80Cr20 to Ni50Fe50, a further enhancement of the radiation resistance is observed for Ni50Fe50. No significant difference in radiation response is identified under current irradiation conditions between the ferro- or anti-ferromagnetic couplings of Ni–Fe or Ni–Cr in Ni80Fe20 and Ni80Cr20. The clear damage suppression observed in Ni50Fe50 may be attributed to local environmental changes, such as the number and arrangement of the first and second neighbors of Ni or Fe with increasing Fe concentration from 20% to 50%. The results in Fig. 1 suggest that the intrinsic properties of elemental species and local arrangement (concentration) are key factors for controlling defect dynamics. In addition, the results from Fig. 1 do not indicate a significant difference in radiation resistance between the ternary Ni40Fe40Cr20 alloy and the binary Ni50Fe50 alloy beyond the uncertainty of the experimental measurements. These results emphasize that the concentration of specific elements could be as effective as the number of elements on tuning the irradiation response of CSAs.
RBS spectra of the irradiated alloys. Spectra recorded from (a) Ni, (b) Ni80Fe20, (c) Ni80Cr20 and (d) Ni50Fe50 single crystals irradiated with 1.5 MeV Ni ions, and (e) Ni40Fe40Cr20 irradiated with 1.5 MeV Mn ions, at various ion fluences. Both virgin and random spectra are included to indicate the damage-free level before irradiation and the fully amorphous (or random) level, where no crystallinity exists. The higher backscattering yield suggests more irradiation-induced damage. For visual clarity, only every five data points are shown.
Damage accumulation
In this section, we elaborate on the damage accumulation in the model alloys using both atomistic simulations and experiments. Increased radiation resistance of equiatomic NiCo and NiFe alloys compared to pure Ni has been reported previously under Au ion irradiation. The results showed that the damage yield in NiCo is about half that in Ni, while the damage yield in NiFe is even lower compared to NiCo25. To examine the role of increasing complexity from simple solid solutions to more complex, we compare damage production and accumulation under prolonged overlapping cascade events in the model crystals, going from simple Ni and binaries to more complex Ni40Fe40Cr20. From the MD simulations, the evolution of FPs with respect to the number of overlapping recoils in these model systems is given in Fig. 2a. The results show that the highest numbers of FPs are produced in pure Ni, compared to the other alloys. In the binary alloys, Ni50Fe50 exhibits fewer radiation-induced FPs than the 80:20 alloys. The difference in defect production between Ni80Fe20 and Ni80Cr20 is evident for the higher number of recoils (>90 recoils) or dose; whereas the numbers of FPs largely overlap at lower numbers of recoils (<50 recoils). A similar trend was previously observed for the accumulation of 5 keV recoil cascades, where Ni80Cr20 produced 1.7 times fewer FPs than the Ni80Fe20 alloy30. Compared to 5 keV cascades, the difference in radiation tolerance between these two alloys is less pronounced for 25 keV recoils.
Comparison of damage accumulation. Damage accumulation in pure Ni, Ni80Fe20, Ni50Fe50, Ni80Cr20 and Ni40Fe40Cr20 alloys from both irradiation simulation and experiment. (a) Accumulation of point defects with increasing numbers of cumulative recoils and the corresponding dose in dpa. This is an average of two sets of cumulative recoil simulations. (b) Relative disorder in the model systems as the function of dose at damage peak (~400 nm).
The ternary Ni40Fe40Cr20 alloy exhibits the best radiation resistance to the accumulation of 25 keV recoil cascades, producing the lowest number of FPs compared to the binaries and pure Ni. The damage accumulation curves are nearly linear and coincident with each other for pure Ni and the binary 80:20 alloys at low doses (below 50 recoils); whereas in case of Ni40Fe40Cr20, the defect accumulation curve starts to deviate from linearity and from the other alloys at a much lower dose, corresponding to about 10 recoil cascades. The total number of FPs produced in the Ni40Fe40Cr20 alloy is approximately a factor of 2.0 lower compared to pure Ni and approximately 1.4 times lower than the 80:20 binary alloys. This behavior suggests very efficient in-cascade damage recombination and dynamic annealing in the ternary alloy compared to pure Ni and the binary alloys. In the conventional MD simulations, due to limited time scale, the dose rate is several orders of magnitude higher than for a reactor environment or for the ion irradiation experiments shown in Fig. 1 and Fig. 2b. Under actual experimental conditions, the point defects have longer time to migrate and recombine between cascade events. As a result, the actual damage accumulation rate in the MD simulations may be overestimated, but the relative difference or trend in defect production, cluster formation and damage accumulation behavior should be valid using this approach.
By employing an iterative process that is described in detail in ref. 31, the relative disorder profiles are derived from the RBS/C spectra and plotted as a function of dose (in dpa) in Fig. 2b for Ni irradiated Ni, Ni80Fe20, Ni50Fe50, Ni80Cr20 and Mn irradiated Ni40Fe40Cr20, respectively. A disorder level of “0” refers to a pristine single crystal, and a level of “1” corresponds to a fully amorphous phase. Some data are taken from a previous publication32. At relatively low doses (up to ~0.13 dpa), enhanced radiation resistance is confirmed as the elemental complexity increases from Ni to the ternary alloy. On the other hand, the damage evolution of Ni50Fe50 and Ni40Fe40Cr20 are similar, indicating the need for understanding different coupling strengths between elements.
Based on both the simulation (Fig. 2a) and experimental results (Fig. 2b) presented above, we can divide the radiation response of these materials into three groups. In the first group, pure Ni is very sensitive to ion irradiation. In the second group, the 80:20 binary alloys moderately suppress damage accumulation, as compared to Ni. Finally, Ni50Fe50 and Ni40Fe40Cr20 alloys demonstrate the best radiation response based on their damage accumulation behavior. By increasing randomness in the NiFe alloy from 80:20 to 50:50, the damage accumulation is suppressed very efficiently, and the damage level is comparable to that of the ternary alloy at lower dose (below 50 recoils). There is good qualitative agreement between simulation and experiment, particularly at lower doses. In both cases, we see overlapping damage levels at the lowest doses; whereas the damage profiles start to deviate from each other at higher doses, following the three groups discussed above.
The results in Figs 1 and 2 demonstrate how material properties can be altered dramatically by varying the elemental type and concentration of alloying elements. A previous study demonstrated that Ni33Co33Cr33 and Ni25Co25Fe25Cr25 outperformed Ni50Fe50 in radiation resistance; whereas Ni33Fe33Co33 and Ni50Fe50 are comparable6. This evidence, including the results shown in Figs 1 and 2, suggest strong coupling of Cr‒Co and Ni‒Fe, but relatively weak coupling of Ni‒Cr in the Ni-based alloys, may be used to tune the atomic transport and defect dynamics in a non-equilibrium radiation environment. This hypothesis also suggests that the radiation response of alloys is not simply dependent on the number of alloying elements, but is also affected by the coupling of specific elements.
Damage in single cascade
In comparison to previous results for 5 keV primary knock-on atom (PKA) cascades30, the average numbers of FPs produced in a single cascade as a function of PKA energy for these compositions are shown in Fig. 3. The results show a non-linear trend of defect production with increasing energy of recoil. The difference in the number of FPs between the alloys for all PKA energies is within the limits of uncertainty, except for pure Ni. On the other hand, we see a clear difference of defect production in overlapping cascade simulations for both 5 keV30 and 25 keV (Fig. 2) damage accumulation curves. This indicates that in-cascade damage recombination during irradiation plays an important role in the suppression of defect accumulation in these alloys. There is no noticeable difference between Ni and Ni-based alloys in defect production for 5 keV single cascades. In contrast, we see significant damage reduction in alloys compared to pure Ni for 25 keV single recoils.
Interstitial cluster formation and evolution
In the previous section, overall defect production and accumulation are shown to vary significantly in different alloys. In this section, we focus on the clustering of point defects in the alloys under irradiation. Figure 4 compares the interstitial clustering behavior for all the alloys after 150 overlaps of 25 keV cascades. In pure Ni, interstitials primarily form medium to large defect clusters, with a number of clusters exceeding 50 interstitials in size, and only a few isolated interstitials (cluster size of 1). On the other hand, small and medium size defect clusters containing 2 to 30 point interstitials are the main features of the binary alloys. There are some additional differences in the size distribution of the interstitial clusters in the Ni80Fe20 and Ni80Cr20 alloys. The number of interstitials in large clusters (cluster size of 31–50 and 51+) is relatively higher in Ni80Fe20, compared to Ni80Cr20. A different cluster formation behavior is observed for Ni50Fe50 and Ni40Fe40Cr20 alloys, which tends more toward a smaller cluster size. In other words, the cluster size distribution for these alloys is quite the opposite of that found in pure Ni. In Ni50Fe50 and Ni40Fe40Cr20 alloys, large cluster formation is negligible (cluster size of 31–50 and 51+); instead, interstitials primarily remain as clusters containing 2–10 point defects or as isolated point defects. In all compositions, medium and large interstitial clusters often produce dislocation loops lying on the {111} plane.
Interstitial cluster size distribution. Comparison of interstitial cluster size distribution between Ni, Ni80Fe20, Ni50Fe50, Ni80Cr20 and Ni40Fe40Cr20 alloys after 150 cumulative recoils (0.015 NRT dpa). Data are taken as an average of two sets of recoil simulations. Error bars show the standard error of the mean.
To understand the growth mechanism of the final interstitial clusters presented in Fig. 4, we turn our focus to the evolution of interstitial cluster sizes at different number of recoils. Figure 5 shows the interstitial cluster size distribution with increasing recoil number for pure Ni and the alloys. The newly created interstitials at higher recoil numbers demonstrate a preference to diffuse to a specific cluster size based on alloy composition. This preference can be divided into three categories. First, in pure Ni, new point defects primarily contribute to the growth of big defect clusters with increasing number of recoils; whereas single point defects saturate at 10 overlapping cascades. This is evident from the growth rate of the 51+ defect clusters compared to other cluster sizes. Second, in the 80:20 binary alloys, cluster sizes between 2 and 30 dominate and increase with the number recoils; whereas isolated interstitials saturate at 50 overlapping cascades. In particular, the number of isolated interstitials decreases slightly in the Ni80Fe20 alloy (150 recoils), which suggests that the rate of recombination and diffusion of isolated defects are higher than for newly created interstitials. Finally, in Ni50Fe50 and Ni40Fe40Cr20 alloys, new defects mainly contribute to the growth of small clusters (2–10 defects), and isolated point defects saturate at around 100 overlapping cascades, particularly for the ternary alloy.
Interstitial cluster size distribution at different recoil events. Comparison of interstitial cluster size distribution between Ni, Ni80Fe20, Ni50Fe50, Ni80Cr20 and Ni40Fe40Cr20 alloys at 10, 50, 100 and 150 recoil events. Data are taken as an average of two sets of recoil simulations. Error bars show the standard error of the mean.
The cluster analysis results shown in Fig. 5 suggest that with increasing cascade overlap, some point defects are effectively annealed due to recombination; at the same time, some interstitials diffuse to grow clusters and form dislocation loops. Such cluster size variation is attributed to alloy composition or chemical complexity. The cluster formation behavior can be explained by taking into account the mobility of interstitials among the different compositions. Interstitial mobility and diffusivity is highest in pure Ni compared to the alloys. Aidhy at el. have reported that interstitials are more mobile in pure Ni than the Ni50Fe50 and Ni80Cr20 alloys33. Defect formation and migration energy in Ni and Ni-based binary and ternary alloys are studied using ab initio calculation based on density functional theory, classical MD and kinetic activation-relaxation technique (k-ART)34,35,36. Vacancy move through the Fe sublattice, whereas Ni-Ni dumbbells are the most stable form of interstitial due to lower formation energy and they prefer to move through Ni sublatttice. In alloys, amount of Ni sublattice is reduced compared to pure Ni, this means slow diffusion of interstitials. For example, in pure Ni, the interstitial atom can jump to any of the 12 nearest neighbours, whereas the jump number will be limited in alloys. There are non-favorable atom pairs, even in a small cluster of interstitials. The migration energy of interstitial is also higher in alloys compared to pure Ni, which also contributes to the slow diffusion of interstitials. The migration energy of vacancy in Ni and Ni-based alloys is very high and very low diffusivity at low temperature. So, at room temperature and in MD time scale damage evolution is mainly contributed by interstitial diffusion. It has also been shown that the diffusivity of Ni atoms in pure Ni is higher than in the Ni45Fe40Cr15 ternary alloy37. Diffusion is even more sluggish in the five component (CoCrFeMnNi) high-entropy alloys38. Due to high mobility and diffusivity, isolated point defects can interact with each other and more readily form defect clusters in Ni. With increasing cascade overlap, large clusters form at the expense of small clusters and isolated point defects. In the binary and ternary alloys, small and medium sized clusters dominate due to the restricted mobility of point defects and small clusters. Significant suppression of radiation induced void swelling is reported in Ni-based SP-CSAs at 500 °C. Enhanced swelling resistance is attributed to the tailored migration behavior of interstitial defect clusters5. Very recently, Granberg and coworkers have studied edge dislocation mobility in pure Ni compared with NiFe and NiCoCr alloys23. They have concluded that the dislocations are less mobile in NiFe as compared to pure Ni, and the ternary NiCoCr alloy shows even lower mobility than the binary NiFe. Thus, compared to pure Ni, small clusters in these alloys cannot diffuse easily to form larger clusters. Dislocation mobility is lowest in the third category of alloys, namely Ni50Fe50 and Ni40Fe40Cr20, which results in only one cluster consisting of more than 50 interstitials in Ni40Fe40Cr20 and no large clusters in the Ni50Fe50 alloy (Fig. 4).
Vacancy cluster formation and evolution
The numbers of vacancies in different cluster size distributions are summarized in Fig. 6. Cluster formation dynamics is very different for vacancies than for interstitials. Vacancies typically remain as isolated point defects and small clusters (2–10 point defects) for all the materials studied. The number of vacancies forming clusters decreases with increasing cluster size. Binary and ternary alloys do not produce any large vacancy clusters (>51 vacancies). The number of vacancies in medium sized clusters (31–50 vacancies) are also insignificant compared to isolated vacancies. We have previously reported a similar pattern of vacancy cluster size distribution for the accumulation of 5 keV recoil cascades30. Studies have shown that vacancies are immobile until 700 K, and start to diffuse around 1000 K in pure Ni33. The probability of isolated vacancies and small clusters to diffuse and form larger vacancy clusters is therefore low. In general, Ni produces relatively larger vacancy clusters compared to other alloys, due to both a higher vacancy yield in Ni and a lower vacancy mobility in the alloys. Small vacancy cluster formation in pure Ni and the alloys (as shown in Fig. 6) might therefore result from a violent collision process and short-time (a few ps) cascade heating rather than from long-term diffusion processes (ns or longer).
Vacancy cluster size distribution at different recoil events. Comparison of vacancy cluster size distribution between Ni, Ni80Fe20, Ni50Fe50, Ni80Cr20 and Ni40Fe40Cr20 alloys at 10, 50, 100 and 150 recoil events. Data are taken as an average of two sets of recoil simulations. Error bars show the standard error of the mean.
Figure 7 shows the evolution of vacancy clusters to form SFT in Ni80Fe20 and elemental Ni. After the 15th recoil in Ni80Fe20 (Fig. 7a), a vacancy cluster is formed with one well-defined {111}-side plane. No vacancy cluster was found to exist for fewer recoils, so this cluster formed entirely during the 15th recoil event. After some rearrangement of vacancies following the 16th and 17th consecutive recoils, a perfect SFT with an edge length of four vacancies forms during the 18th recoil. Figure 7b presents irradiation-assisted formation of similar vacancy-like SFT in Ni with an edge length of seven vacancies. Other binary and ternary alloys produce truncated SFT. Besides single isolated SFT, some coupling of SFT along an edge length or a plane are also observed. It is important to note that only a small fraction of defects produce perfect SFT. Other defects consist of isolated point defects, defect clusters and truncated SFT. A few studies have been carried out to understand the formation mechanism of SFT in fcc metals during ion irradiation by MD simulation39, 40. In particular, Nordlund et al. have shown that, in fcc Cu and Au, SFT can form directly in the atom-depleted zone at the center of a collision cascade by four intersecting {111} vacancy stacking faults and simultaneous atom rearrangement39. The SFT observed in the current study can also be described using this method due to the simulation conditions and features of the SFT. Experimentally, SFT are observed in high purity (containing Fe, Ni and Cr) and model austenitic alloys, irradiated at both high and low doses41, 42. In contrast, SFT are either absent or present in high density in commercial austenitic alloys, depending on the impurity content43, 44.
SFT formation. Illustration of the growth of a perfect stacking fault tetrahedron as a function of recoil number, where spheres represent empty lattice sites (vacancies). (a) A perfect stacking fault tetrahedron formation in Ni80Fe20, gradually formed at 15, 16, 17 and 18 consecutive recoils. The final view shows a different angle of the SFT after the 18th recoil. (b) Gradual SFT formation in Ni at 38, 39 and 45 recoils.
Previous high resolution transmission electron microscopy (HRTEM) studies of irradiated Ni and Ni-based alloys have revealed both interstitial type dislocation loops and vacancy-type SFT. Lu et al. have observed SFT in single crystalline pure Ni, NiCo and NiFe alloys irradiated with 3 MeV Au ions to a fluence of 5 × 1015/cm2 27. The vacancy-type SFT are mostly dispersed in the matrix but there are some coupled SFT that form parallelograms. Interstitial dislocation loops of about 1–8 nm diameter have also been observed under TEM33. A previous study of comparison between MD simulation and TEM image suggests that higher number of large defect clusters are produced in elemental Ni compared to binary and ternary alloys23. Therefore, the irradiation-induced defect structures of current simulations are in good agreement with experimental observations.
Conclusions
Damage accumulation due to cumulative irradiation of Ni, Ni80Fe20, Ni80Cr20, Ni50Fe50 and Ni40Fe40Cr20 alloys has been studied in both ion irradiation experiments and molecular dynamics simulations. The single crystals of these alloys have been irradiated with 1.5 MeV Ni or Mn ions at fluences ranging from 1 × 1013 cm−2 to 1 × 1014 cm−2. In MD simulations, overlapping cascades of 25 keV recoils have been used to simulate damage accumulation. The binary and ternary alloys show efficient suppression of defect production and accumulation. The accumulated damage is not linear with either increasing number of recoils or recoil energy, indicating the importance of in-cascade damage recombination in the final state of damage production. Larger interstitial clusters are produced in Ni; whereas, the average cluster size decreases when 20% of the Ni atoms in pure Ni are substituted with Fe or Cr. Even further reduction of damage accumulation is evident in Ni50Fe50 and Ni40Fe40Cr20, both of which exhibit increasing randomness of local atomic arrangements that significantly modify the first and second nearest neighbors. The results indicate a decrease in defect mobility with increasing alloy complexity, which is also supported by previous experimental and simulation studies. SFT-like vacancy clusters are produced in all compositions. The results from using both experimental irradiations and MD simulations in these integrated studies suggest that changing the complexity of concentrated solid solution alloys can alter defect accumulation and evolution under extended irradiation environments. Strong coupling of Cr‒Co and Ni‒Fe, but relatively weak coupling of Ni‒Cr, in the Ni-based concentrated solid solution alloys may be utilized to tune the atomic transport and defect dynamics in a non-equilibrium radiation environment. This combination emphasizes that the radiation response of complex alloys is not simply dependent on the number of alloying elements but is also affected by the coupling of specific elements. This approach of designing materials based on manipulation of alloy complexity may result in new radiation tolerant materials.
Methods
Experiment
The ion irradiation and ion beam analysis of single crystal Ni, Ni80Fe20, Ni50Fe50, Ni80Cr20 and Ni40Fe40Cr20 were performed at the Ion Beam Materials Laboratory (IBML)45 at the University of Tennessee, Knoxville. 1.5 MeV Ni (for Ni, Ni80Fe20, Ni50Fe50 Ni80Cr20) and 1.5 MeV Mn (for Ni40Fe40Cr20) ion irradiations were performed to produce damage profiles with peak values of disorder at a depth of around 400 nm in order to minimize surface sink effects46. During ion irradiation, a defocused ion beam was wobbled over a 3.0 × 3.0 cm2 area by two raster scanners at 517 Hz (horizontal) and 64 Hz (vertical) to ensure uniformity45. An ion flux of 3.5 × 1011 cm−2 was used to reach ion fluence ranged from 1.0 × 1013 cm−2 to 1.0 × 1014 cm−2. The corresponding doses were predicted using the stopping and range of ions in matter (SRIM) code, under the quick calculation of damage option, and ranged from 0.01 to 0.13 dpa (displacements per atom)47. A displacement threshold energy of 40 eV was applied for Ni, Fe and Cr in all SRIM calculations. After ion irradiations, Rutherford backscattering spectrometry in channeling geometry (RBS/C) using 3.5 MeV He ions was performed in-situ along the <001> direction. All the ion irradiations and RBS/C measurements were performed at room temperature under a high vacuum25, 45.
Atom probe tomography (APT) analyses on the Ni-xFe (x = 0–60) alloys have shown that these alloys remain random solid solution after the Ni ion irradiations at room temperature to a dose of ~6.5 dpa, which is beyond the dose range of the present study32. Moreover, recent neutron diffraction studies48 have revealed only fcc peaks for the Ni80Cr20 alloys at room temperature without superlattice peaks (e.g. Ni2Cr), confirming a single-phase solid solution. Furthermore, our own microstructure and X-ray diffraction characterization of the Ni40Fe40Cr20 used here confirms a single-phase solid solution. Further studies are needed to investigate the phase stability of Ni80Cr20 and Ni40Fe40Cr20 under ion irradiation at room temperature to high doses, but we assume that these two alloys remain a random solid solution form at the low irradiation doses (<0.13 dpa) in the present study. The room temperature specific heat of these alloys are very similar from 0.4 to 0.5 J. g−1. K−1 but their values varies significantly with temperature due to magnetic state and possible short-range order-disorder transitions48, 49. The room temperature lattic parameters determinted using neutron diffraction measurement is largest for Ni, which is followed by Ni80Cr20 and Ni50Fe50. Below the Curie temperature, the thermal diffusivity and conductivity of Ni50Fe50 is higher than Ni80Cr20 but smaller than elemental Ni.
Cascade simulation
The recoil simulations were performed using the LAMMPS and PARCAS codes, which are based on classical MD methods50,51,52. The LAMMPS code was used to create a random mixture of elements to mimic the random nature of SP-CSAs. Irradiation simulations were performed using the MD code PARCAS. In the simulations, a variable time step is used, where the time step is inversely proportional to the total force that the recoil atom experiences and its velocity, using a proportionality constant50. The interaction between atoms in pure Ni, Ni50Fe50, Ni80Fe20, Ni80Cr20 and Ni40Fe40Cr20 alloys were described using the embedded atom method (EAM) potential by Bonny et al.53. This potential was developed to study the formation and evolution of radiation defects, particularly point defects produced during collision cascades. This is suitable to model stable fcc NiFeCr compositions with a focus on compositions around the Fe70Ni10Cr20 alloy, and not suitable for the study of phase stabilities. Besides the bcc phase, this potential does not consider phases like FeCr sigma, Ni2Cr and FeNi2. The self-diffusion coefficients of different constituent elements in the NiFeCr alloys determined using this potential are in the order D cr > D Ni > D Fe . The self-diffusion coefficient of Cr is higher, which is in good agreement with broad experimental observations. In the case of Ni and Fe, both D Ni > D Fe and D Fe > D Ni observations are reported54,55,56.
The simulation cell size was 284 × 284 × 284 Å3 containing 2,050,000 atoms. Initially, the cell was relaxed at 300 K and zero pressure, utilizing a Berendsen temperature and pressure control57. Periodic boundary conditions were applied in all directions to replicate an infinitely large bulk system58. The electronic stopping was applied as a friction force for atoms with kinetic energies higher than 1 eV and calculated using the SRIM code version 201347, 50. The effects of damage accumulation in Ni, Ni80Fe20 and Ni80Cr20 alloys due to the overlapping of 5 keV recoil cascades have been studied previously30. In this paper, 25 keV recoil cascades were employed to account for the higher energies in the recoil spectra from ion and neutron irradiation, and the results are compared to some previous results for 5 keV recoil cascades and with experiment. To mimic the random nature of overlapping cascades, the simulation cell was shifted by a random displacement vector between zero and the cell size in the [100], [010] and [001] directions before each subsequent recoil simulation. After that, one recoil was initiated by a Ni atom close to the center of the simulation cell with an energy of 25 keV in a random direction. This allowed a uniform distribution of crystal damage and avoided cascades interacting with the cell borders. The simulation time (100 ps) was chosen so that the system cooled down and no energetic interactions remained in the system. Details of the simulation procedure can be found elsewhere22, 30. A total of 150 recoil simulations were performed to achieve a damage dose equivalent to 0.015 NRT-dpa, which yielded good statistics for characterization of the final damage state59.
Defect analysis of the simulation cells
The Voronoi cell method was used to identify vacancies and interstitials. In this approach, atoms of the defective crystal configuration were assigned to Wigner-Seitz-cell-Voronoi polyhedra centered at the lattice sites of the ideal reference crystal. Polyhedra with no atoms were labeled as vacancies and polyhedra with 2 or more atoms were labeled as interstitials51.
In addition, a cluster connectivity analysis was done for all investigated cases. Interstitial and vacancy clusters were identified separately. Defects identified by the Voronoi cell method were used as input for this analysis. All defects within a fixed cut-off radius from each other were interpreted to be a part of the same defect cluster. The cut-off radius was set as the second-nearest-neighbor distance (3.65 Å), which is the general cut-off distance used in several previous studies22, 60. Defects were visualized with the program OVITO61.
The Voronoi cell method is reliable for determining the number of surviving Frenkel pairs (FPs), but it cannot identify the structures with correlated atomic displacements typical of stacking faults. To identify stacking fault tetrahedra (SFT), the equivalent sphere (ES) method of defect analysis was used. A sphere radius of 0.3a0, where a0 is the lattice parameter, was used to reliably detect SFT. Details of the analysis method can be found in other publications22, 39, 62.
References
Yeh, J. W. et al. Nanostructured high-entropy alloys with multiple principal elements: Novel alloy design concepts and outcomes. Adv. Eng. Mater. 6, 299–303 (2004).
Lucas, M. S. et al. Absence of long-range chemical ordering in equimolar FeCoCrNi. Appl. Phys. Lett. 100, 251907 (2012).
Guo, S. & Liu, C. T. Phase stability in high entropy alloys: Formation of solid-solution phase or amorphous phase. Prog. Nat. Sci. Mater. Int. 21, 433–446 (2011).
Yeh, J. W. et al. Anomalous decrease in X-ray diffraction intensities of Cu-Ni-Al-Co-Cr-Fe-Si alloy systems with multi-principal elements. Mater. Chem. Phys. 103, 41–46 (2007).
Lu, C. et al. Enhancing radiation tolerance by controlling defect mobility and migration pathways in multicomponent single-phase alloys. Nat. Commun. 7, 13564 (2016).
Zhang, Y. et al. Influence of chemical disorder on energy dissipation and defect evolution in advanced alloys. J. Mater. Res. 31, 2363–2375 (2016).
Zhang, Y. et al. Microstructures and properties of high-entropy alloys. Prog. Mater. Sci. 61, 1 (2014).
Wu, Z., Bei, H., Otto, F., Pharr, G. M. & George, E. P. Recovery, recrystallization, grain growth and phase stability of a family of FCC-structured multi-component equiatomic solid solution alloys. Intermetallics 46, 131 (2014).
Gludovatz, B. et al. A fracture-resistant high-entropy alloy for cryogenic applications. Science 345, 1153–8 (2014).
Senkov, O. N., Wilks, G. B., Miracle, D. B., Chuang, C. P. & Liaw, P. K. Refractory high-entropy alloys. Intermetallics 18, 1758 (2010).
Allen, T., Busby, J., Meyer, M. & Petti, D. Materials challenges for nuclear systems. Mater. Today 13, 14 (2012).
Zinkle, S. J. & Was, G. S. Materials challenges in nuclear energy. Acta Mater. 61, 735 (2013).
Egami, T., Guo, W., Rack, P. D. & Nagase, T. Irradiation resistace of multicomponent alloys. Met. Mater. Trans. A 45, 180 (2014).
Bollen, G. et al. Rare isotope accelerator-conceptual design of target areas. Nucl. Instrum. Meth. A 562, 915 (2006).
Singer, C., Buck, R., Pitz-Paal, R. & Müller-Steinhagen, H. Economic Potential of Innovative Receiver Concepts With Different Solar Field Configurations for Supercritical Steam Cycles. J. Sol. Energy Eng. 136, 21009 (2013).
Garner, F. A. In Comprehensive Nuclear Materials 4, 33–95 (2012).
Zinkle, S. J., Maziasz, P. J. & Stoller, R. E. Dose dependence of the microstructural evolution in neutron-irradiated austenitic stainless steel. J. Nucl. Mater. 206, 266–286 (1993).
Maziasz, P. J. Overview of microstructural evolution in neutron-irradiated austenitic stainless steels. J. Nucl. Mater. 205, 118–145 (1993).
Kenik, E. A. & Busby, J. T. Radiation-induced degradation of stainless steel light water reactor internals. Mater. Sci. Eng. R Reports 73, 67–83 (2012).
Zinkle, S. J. In Comprehensive Nuclear Materials 1, 65–98 (2012).
Kumar, N. A. P. K., Li, C., Leonard, K. J., Bei, H. & Zinkle, S. J. Microstructural stability and mechanical behavior of FeNiMnCr high entropy alloy under ion irradiation. Acta Mater. 113, 230–244 (2016).
Vortler, K., Juslin, N., Bonny, G., Malerba, L. & Nordlund, K. The effect of prolonged irradiation on defect production and ordering in Fe-Cr and Fi-Ni alloys. J. Phys. Condens. Matter 23, 355007 (2011).
Granberg, F. et al. Mechanism of Radiation Damage Reduction in Equiatomic Multicomponent Single Phase Alloys. Phys. Rev. Lett. 116, 135504 (2016).
Jin, K., Bei, H. & Zhang, Y. Ion irradiation induced defect evolution in Ni and Ni-based FCC equiatomic binary alloys. J. Nucl. Mater. 471, 193–199 (2016).
Zhang, Y. et al. Influence of chemical disorder on energy dissipation and defect evolution in nickel and Ni-based concentrated solid-solution alloys. Nat. Commun. 6, 8736 (2015).
Jin, K. et al. Tailoring the physical properties of Ni-based single-phase equiatomic alloys by modifying the chemical complexity. Sci. Rep. 6, 20159 (2016).
Lu, C. et al. Direct Observation of Defect Range and Evolution in Ion-Irradiated Single Crystalline Ni and Ni Binary Alloys. Sci. Rep. 6, 19994 (2016).
Murty, K. L. & Charit, I. Structural materials for Gen-IV nuclear reactors: Challenges and opportunities. J. Nucl. Mater. 383, 189–195 (2008).
Zhang, Y. et al. Atomic-level heterogeneity and defect dynamics in concentrated solid-solution alloys. Curr. Opin. Solid State Mater. Sci., doi:10.1016/j.cossms.2017.02.002(2017).
Ullah, M. W., Aidhy, D. S., Zhang, Y. & Weber, W. J. Damage accumulation in ion-irradiated Ni-based concentrated solid-solution alloys. Acta Mater. 109, 17–22 (2016).
Zhang, Y. et al. Response of strontium titanate to ion and electron irradiation. J. Nucl. Mater. 389, 303–310 (2009).
Jin, K. et al. Effects of Fe concentration on the ion-irradiation induced defect evolution and hardening in Ni-Fe solid solution alloys. Acta Mater. 121, 365–373 (2016).
Aidhy, D. S. et al. Point defect evolution in Ni, NiFe and NiCr alloys from atomistic simulations and irradiation experiments. Acta Mater. 99, 69 (2015).
Zhao, S., Stocks, G. M. & Zhang, Y. Defect energetics of concentrated solid-solution alloys from ab initio calculations: Ni0.5Co0.5, Ni0.5Fe0.5, Ni0.8Fe0.2 and Ni0.8Cr0.2. Phys. Chem. Chem. Phys. 18, 24043–24056 (2016).
Zhao, S., Osetsky, Y. & Zhang, Y. Preferential diffusion in concentrated solid solution alloys: NiFe, NiCo and NiCoCr. Acta Mater. 128, 391–399 (2017).
Osetsky, Y. N., Béland, L. K. & Stoller, R. E. Specific features of defect and mass transport in concentrated fcc alloys. Acta Mater. 115, 364–371 (2016).
Tsai, K. Y., Tsai, M. H. & Yeh, J. W. Sluggish diffusion in Co-Cr-Fe-Mn-Ni high-entropy alloys. Acta Mater. 61, 4887–4897 (2013).
Tsai, M.-H. & Yeh, J.-W. High-Entropy Alloys: A Critical Review. Mater. Res. Lett. 2, 107–123 (2014).
Nordlund, K. & Gao, F. Formation of stacking-fault tetrahedra in collision cascades. Appl. Phys. Lett. 74, 2720–2722 (1999).
Kapinos, V. G., Osetskii, Y. N. & Platonov, P. A. The cascade mechanism of nucleation of vacancy loops and stacking fault tetrahedra in FCC metals. J. Nucl. Mater. 165, 286–296 (1989).
Stoller, R. E. & Odette, G. R. The effects of helium implantation on microstructural evolution in an austenitic alloy. J. Nucl. Mater. 154, 286–304 (1988).
Horiki, M. & Kiritani, M. Microstructural evolution in low-dose neutron-irradiated Fe−16Ni-15Cr alloy. J. Nucl. Mater. 212–215, 246–251 (1994).
Edwards, D. J., Simonen, E. P. & Bruemmer, S. M. Evolution of fine-scale defects in stainless steels neutron-irradiated at 275 C. J. Nucl. Mater. 317, 13–31 (2003).
Dai, Y. et al. Microstructure of both as-irradiated and deformed 304 L stainless steel irradiated with 800 MeV protons. in. Journal of Nuclear Materials 296, 174–182 (2001).
Zhang, Y. et al. New ion beam materials laboratory for materials modification and irradiation effects research. Nucl. Instrum. Methods Phys. Res. B 338, 19–30 (2014).
Foreman, A. J. E. The diffusion of point defects to the foil surface during irradiation damage experiments in the high voltage electron microscope. Radiat. Eff. 14, 175–179 (1972).
Ziegler, J. F. SRIM software package. Available at: http://www.srim.org/ (2013).
Jin, K. et al. Thermophysical properties of Ni-containing single-phase concentrated solid solution alloys. Mater. Des. 117, 185–192 (2017).
Binnatov, K. G., Katsnel’son, A. A. & Rodionov, Y. L. Atomic ordering in Ni-Fe-Cr solid solutions. Sov. Phys. J. 18, 397–398 (1975).
Nordlund, K. Molecular dynamics simulation of ion ranges in the 1–100 keV energy range. Comput. Mater. Sci. 3, 448 (1995).
Nordlund, K. et al. Defect production in collision cascades in elemental semiconductors and FCC metals. Phys. Rev. B 57, 7556–7570 (1998).
Plimpton, S. Fast Parallel Algorithms for Short-Range Molecular Dynamics. J. Comp. Phys. 117, 1–19 (1995).
Bonny, G., Castin, N. & Terentyev, D. Interatomic potential for studying ageing under irradiation in stainless steels: the FeNiCr model alloy. Model. Simul. Mater. Sci. Eng. 21, 85004 (2013).
Million, B., Růžičková, J. & Vřešťál, J. Diffusion in FeNiCr alloys with an F.C.C. lattice. Mater. Sci. Eng. 72, 85–100 (1985).
Rothman, S. J., Nowicki, L. J. & Murch, G. E. Self-diffusion in austenitic Fe-Cr-Ni alloys. J. Phys. F Met. Phys. 10, 383–398 (1980).
Smith, A. F. & Gibbs, G. B. The Volume and Grain-Boundary Diffusion of Iron in 20 Cr/25 Ni/Nb Stainless Steel. Met. Sci. J. 2, 47–50 (1968).
Berendsen, H. J. C., Postma, J. P. M., van Gunsteren, W. F., DiNola, A. & Haak, J. R. Molecular dynamics with coupling to external bath. J. Chem. Phys. 81, 3684 (1984).
Allen, M. P. & Tildesley, D. J. Computer Simulation of Liquids. Oxford University Press, Oxford (Oxford University Press, 1989).
Norgett, M. J., Robinson, M. T. & Torrens, I. M. A proposed method of calculating displacement dose rates. Nucl. Eng. Des. 33, 50–54 (1975).
Stoller, R. E. The role of cascade energy and temperature in primary defect formation in iron. J. Nucl. Mater. 276, 22–32 (2000).
Stukowski, A. Visualization and analysis of atomistic simulation data with OVITO–the Open Visualization Tool. Model. Simul. Mater. Sci. Eng. 18, 15012 (2009).
Voskoboinikov, R. E., Osetsky, Y. N. & Bacon, D. J. Computer simulation of primary damage creation in displacement cascades in copper. I. Defect creation and cluster statistics. J. Nucl. Mater. 377, 385–395 (2008).
Acknowledgements
The work was supported as part of the Energy Dissipation to Defect Evolution (EDDE), an Energy Frontier Research Center funded by the U.S. Department of Energy, Office of Science, Basic Energy Sciences. Ion beam work was performed at the University of Tennessee–Oak Ridge National Laboratory Ion Beam Materials Laboratory (IBML, http://ibml.utk.edu/) located on the campus of the University of Tennessee, Knoxville. Part of the simulation used resources of the National Energy Research Scientific Computing Center, supported by the Office of Science, US Department of Energy, under Contract No. DEAC02–05CH11231.
Author information
Authors and Affiliations
Contributions
Y.Z. and W.J.W. developed the concept and supervised the project. M.U. carried out the simulations. H.B. and K.J. grew the crystals and prepared the specimens. H.X. and G.V. carried out the ion irradiation experiments. All authors discussed and analyzed the results. M.U. and Y.Z. drafted the manuscript with inputs from all authors.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ullah, M.W., Xue, H., Velisa, G. et al. Effects of chemical alternation on damage accumulation in concentrated solid-solution alloys. Sci Rep 7, 4146 (2017). https://doi.org/10.1038/s41598-017-04541-8
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-04541-8
- Springer Nature Limited