Abstract
A hallmark of many unconventional superconductors is the presence of many-body interactions that give rise to broken-symmetry states intertwined with superconductivity. Recent resonant soft X-ray scattering experiments report commensurate 3a0 charge density wave order in infinite-layer nickelates, which has important implications regarding the universal interplay between charge order and superconductivity in both cuprates and nickelates. Here we present X-ray scattering and spectroscopy measurements on a series of NdNiO2+x samples, which reveal that the signatures of charge density wave order are absent in fully reduced, single-phase NdNiO2. The 3a0 superlattice peak instead originates from a partially reduced impurity phase where excess apical oxygens form ordered rows with three-unit-cell periodicity. The absence of any observable charge density wave order in NdNiO2 highlights a crucial difference between the phase diagrams of cuprate and nickelate superconductors.
Similar content being viewed by others
Main
The discovery of superconductivity in infinite-layer nickelates1, and its analogy to its cuprate antecedents, offers a unique opportunity to better understand the key ingredients for high-temperature superconductivity. Although nickelates and cuprates share many commonalities, including a broadly similar crystal and electronic structure1, strong correlations, antiferromagnetic excitations2,3 and a superconducting dome4,5,6, there are also many distinctions between the two families. These include the very different transition temperatures1,4,5, the relative oxygen and 3d character of the doped holes7,8, and the hybridization between the 3d and rare-earth states9. One important apparent similarity between the two families is the report of charge density wave order in a variety of infinite-layer nickelates by resonant soft X-ray scattering (RSXS)10,11,12,13. This discovery, if correct, would suggest a ubiquitous interplay between charge order and superconductivity in the phase diagram of both cuprates and nickelates, with important implications for a universal theory of high-temperature superconductivity.
Nevertheless, there are clear distinctions between the charge order reported in cuprates and nickelates. In cuprates, the wavevector is typically incommensurate and strongly doping dependent14,15,16, whereas in NdNiO2 and PrNiO2, it is locked to q = (1/3, 0) (refs. 11,12,13). Additionally, charge ordering in cuprates is strongly temperature dependent15,16,17,18,19,20, whereas reports in nickelates exhibit a weak temperature dependence with no clear transition or onset10,12,13. To better understand the nature of putative charge ordering in the infinite-layer nickelates, we have investigated the q = (1/3, 0) superlattice peak in a series of samples with varying levels of reduction. We discover that the superlattice peak is entirely absent in fully reduced, single-phase NdNiO2 samples, and instead arises from partially reduced impurity phases, namely, NdNiO2.33 (Nd3Ni3O7) or NdNiO2.67 (Nd3Ni3O8), produced during the reduction process, where excess apical oxygen atoms form ordered rows with three-unit-cell periodicity. This reveals that charge ordering with 3a0 periodicity is not intrinsic to the infinite-layer nickelates—a discovery with important implications for our understanding of the phase diagram of nickelates and its relationship to cuprates.
To produce a sequence of NdNiO2 samples with nominally identical Nd:Ni stoichiometry21 and variable oxygen content, we have employed a combination of reactive-oxide molecular-beam epitaxy to synthesize the precursor perovskite and atomic hydrogen reduction to access the oxygen-deficient phases. A consistent series of perovskite films of NdNiO3 (20 pseudocubic unit cells thick) with excellent crystallinity and sharp metal–insulator transitions were synthesized on SrTiO3. Following synthesis, all the films were capped by 2–3 unit cells of SrTiO3 and exposed to a beam of >50% atomic hydrogen produced by a thermal cracker22. Although the reduction of perovskite nickelates has typically been achieved using CaH2 and NaH powder1,5,23, atomic hydrogen offers the benefit of independent control over the sample temperature and reducing environment, as well as fast reaction times (<20 min).
Using this approach, we have synthesized a series of samples ranging from the pristine parent perovskite NdNiO3 (sample A) to oxygen-deficient intermediate phases NdNiO2+x (samples B and C) and infinite-layer NdNiO2 (samples D–I), all of which were characterized by conventional X-ray diffraction (XRD) and transport measurements. All the NdNiO2 samples appear highly crystalline and single phase by XRD, with low-temperature resistivities of 350–700 μΩ cm, comparable with or lower than undoped films on SrTiO3 (refs. 4,5,24) and LSAT25 (Fig. 1a,b; Supplementary Information shows the data for samples G–I). Further information about the growth and reduction procedures are available in Methods.
a, Cu Kα θ–2θ XRD measurements of a sequence of thin films ranging from NdNiO3 (sample A) to partially reduced NdNiO2+x (samples B and C) and NdNiO2 (samples D–F). b, Electrical transport measurements of the same series of samples. c, Total-electron-yield (TEY) XAS measurements of this sample series taken at the Ni L3 edge with the electric field ε parallel to the sample a axis. d,e, RSXS measurements of NdNiO2 samples D–F; rocking curves through the nominal charge order position of q = (–1/3, 0) at the Ni L3 (d) and Nd M5 (e) edges at σ and π polarizations, respectively. The plotted intensity is the measured scattered intensity I divided by the incident-beam intensity I0, without any background subtraction. Traces in a and c–e have been vertically offset for clarity.
X-ray absorption spectroscopy (XAS) measurements on all the samples are shown in Fig. 1c, and RSXS measurements on three representative infinite-layer NdNiO2 samples (samples D–F) are presented in Fig. 1d,e. The XAS spectra of all three NdNiO2 samples appear similar and closely match with the published measurements9,26, with a single peak at the Ni L3 edge (852.4 eV) with no visible prepeak at the O K edge. Despite the apparent similarity between these samples, only sample D exhibits a superlattice peak at the putative charge order wavevector of q = (1/3, 0). As shown in previous reports, this peak is observed on the Ni L edge (Fig. 1d) as well as the Nd (rare-earth) M edge (Fig. 1e), and exhibits a strong polarization dependence, namely, Iσ/Iπ ≈ 4 at hν = 852.3 eV, consistent with prior measurements11,13. The estimated in-plane correlation length of ξ = 12–20 nm is also qualitatively similar to earlier reports10,11,12,13. Finally, a weak dependence on the out-of-plane momentum transfer L is observed with a maximum at roughly L = 0.31(2) reciprocal lattice units (r.l.u.), again consistent with earlier measurements (all the momenta in this text are quoted in r.l.u. with reference to the NdNiO2 lattice; a = 3.905 Å, c = 3.286 Å). In contrast, the superlattice peak was not observed in samples E and F, which is notable since sample E exhibited the lowest resistivity of all the samples. Additional measurements on samples G and H were measured at a separate beamline and exhibited an extremely weak q = (1/3, 0) feature at the sample centre, whereas sample I showed no superlattice features whatsoever. Supplementary Information provides further details of the measurements on samples E–I.
This discrepancy across nominally similar NdNiO2 samples suggests that some unknown variable, potentially associated with sample disorder or oxygen non-stoichiometry, influences the presence of the 3a0 superlattice peak. One possibility is that the charge density wave order is intrinsic to infinite-layer nickelates, but triggered by the presence of atomic-scale disorder within the lattice. Alternatively, the peak could originate from an impurity phase produced during the reduction process, which would imply that the charge order observed to date does not play a role in the phase diagram of infinite-layer nickelates.
To distinguish between these scenarios, we have investigated partially reduced, oxygen-deficient perovskite phases NdNiO2+x (samples B and C). Sample B was only lightly reduced, with its XRD data nearly indistinguishable from the perovskite (sample A), but with a substantially broadened metal–insulator transition and increased sample resistance (Fig. 1a,b). Sample C was reduced further and shows an intermediate out-of-plane lattice constant of c = 3.66 Å and highly insulating electrical transport as expected for a predominantly oxygen-deficient perovskite phase27. The XAS spectra of sample B exhibit the typical two-peak structure observed in perovskite nickelates on the Ni L3 edge28, as well as a strong prepeak at the O K edge; sample C is markedly different, with a sharp peak at 852.7 eV, shoulder at 852.0 eV and weak secondary peak at 854.3 eV, indicative of an oxygen-deficient perovskite phase29,30.
In Fig. 2a, we show the RSXS measurements of sample C, which exhibit a peak at q = (1/3, 0) virtually identical to the superlattice peak in sample D and the literature10,11,12,13 in nearly all respects: wavevector, energy dependence, polarization dependence, temperature dependence and correlation length, with the exception that it is extremely intense (100–400 times stronger than that observed in sample D). This peak also displays a strong L dependence, with a maximum at 0.30 r.l.u (d/3 = 3.65 Å). The strong similarity between the superlattice features in samples C and D suggests a common origin: ordered oxygen-deficient phases arising from an incomplete reduction process. In reduced nickelates, excess apical oxygens can form ordered phases, such as the brownmillerite structure of La2Ni2O5 (refs. 31,32,33), where the apical oxygen atoms form alternating rows. Other related structures also exist with different periodicities, such as Nd3Ni3O7 (refs. 34,35,36), Pr3Ni3O7 (refs. 34,35), La3Ni3O8 (ref. 37) and (Pr,Ca)4Ni4O11 (ref. 38). Recent in situ XRD studies indicate that the reduction pathway from bulk NdNiO3 to NdNiO2 occurs first via the formation of an intermediate-phase Nd3Ni3O7 (ref. 36), where one-third of the apical oxygen sites are occupied and are ordered into chains with 3a0 periodicity (Fig. 2c). This 3 × 1 × 3 superstructure of the original pseudocubic unit cell would naturally give rise to a superlattice peak at q = (1/3, 0, 1/3). This suggests that sample C is probably predominantly Nd3Ni3O7, and that an incomplete reduction of any NdNiO2 samples would also leave traces of the Nd3Ni3O7 phase behind (sample D).
a, H scans, at constant L, at the Ni L3 and Nd M5 edges for sample C are presented without background subtraction. Data for sample D, after removal of a cubic fluorescent background and rescaling for visibility, are included for reference. b, Rocking curves through q = (1/3, 0) on lightly reduced sample B, presented without background subtraction but vertically offset for clarity. c, Illustration of a potential intermediate-phase structure for Nd3Ni3O7 from a top-down view of the a–b plane of NiO2 where two-thirds of the rows of apical oxygen atoms are removed, forming a 3a0 supercell along the a axis.
To further investigate this hypothesis, we have also performed RSXS measurements on sample B, which should only be in the initial stages of the conversion from NdNiO3 into a brownmillerite-like Nd3Ni3O7 phase. The XRD and XAS measurements of this sample (Fig. 1a,c) are indistinguishable from the data for pristine NdNiO3 (sample A). Nevertheless, RSXS measurements (Fig. 2b) also show the q = (1/3, 0) peak with identical characteristics (L, energy and polarization dependence) and comparable intensity with sample D. The fact that sample B exhibits no obvious trace of the infinite-layer phase and still exhibits a clear q = (1/3, 0) superlattice peak demonstrates that this feature does not originate from intrinsic charge ordering within the infinite-layer phase itself. In fact, the q = (1/3, 0) peaks appear to be more reminiscent of Bragg peaks observed in resonant scattering from cuprates with oxygen ordering (for example, ortho-YBa2Cu3O6+δ), as opposed to intrinsic charge density wave order39,40. There, the strong resonant enhancement on the Cu L edge arises from the local oxygen environment strongly modifying the electronic structure of the Cu atoms, and a similar resonant enhancement at the Ni L edge should likewise occur for oxygen ordering in nickelates.
In Fig. 3a, we show the energy dependence of the q = (1/3, 0, 1/3) peak intensity in samples C and D (shaded), together with the background fluorescence measured off the superlattice peak (white). Because the superlattice peak intensity is far stronger in sample C, the relative strength of the background fluorescence in sample D is much larger than in sample C. Nevertheless, a two-peak resonance profile is apparent in both samples at the Ni L3 edge with only a weak response at the L2 edge, similar to prior measurements on NdNiO2 (ref. 11). Assuming a structural origin arising from oxygen ordering, the superlattice peak should also be observable in the off-resonance case. In Fig. 3b,c, we show a series of scans across q = (1/3, 0) for samples C and D, spanning a 235 eV range about the Ni and Nd resonances. Although the intensity is weaker than the on-resonance case, the persistence of the peak strongly supports a structural origin. The temperature dependence of the scattering peak is shown for samples B–D (Fig. 3d). Similar to prior reports10,12,13, the peak shows a smooth decrease in intensity by 15–20% between 20 and 370 K, with no obvious change in the correlation length. This weak dependence—without a transition—is fairly similar to the temperature dependence of superlattice peaks resulting from the oxygen ordering in YBa2Cu3O6+δ (refs. 40,41), as opposed to the more dramatic temperature dependence of the CDW order18,40.
a, Fixed-wavevector resonant energy profiles both on and off the scattering peak for samples C and D. The shaded region indicates intensity attributable to the resonant scattering above the fluorescent background (white). b,c, Rocking curves through q = (1/3, 0) for a wide range of photon energies around the Ni L and Nd M resonances for sample C (b) and sample D (c); traces have been vertically offset for clarity, but no background subtraction has been applied. d, Temperature dependence of peak amplitude A and correlation length ξ = 2π/Δq, at both edges for samples B–D. The error bars represent the fitting uncertainty in the extracted quantities (A and ξ); they define the range of values obtained by fitting the RSXS data with different models of the fluorescence background (that is, different polynomial degrees and fits over different ranges). The grey line is a guide to the eye.
We also observe a strong dependence of the q = (1/3, 0) peak intensity in sample G for the measurement location on the 10 × 10 mm2 sample (Supplementary Information). Due to the spread of the atomic hydrogen beam and thermal gradients, the edges of the sample are not as well reduced as the centre—correspondingly, we observe a clear superlattice peak near the edge of the sample, which decreases in intensity approaching the sample centre. Spatially resolved synchrotron hard XRD measurements at the same locations confirm the prevalence of intermediate reduction products at the edge of sample G, versus fully reduced NdNiO2 near the centre, thereby correlating the presence of the resonant feature with that of intermediate phases on the same sample.
Prior powder XRD studies of bulk Nd3Ni3O7 reveal that the excess apical oxygens form octahedrally coordinated chains that run perpendicular to the NiO2 planes and which are separated by 3a0 (ref. 34). Another potential arrangement is to have the apical oxygens form pyramidal chains that lie within the NiO2 plane and are oriented along the a axis (Fig. 4a). In addition, Nd3Ni3O8 (NdNiO2.67), where two rows of apical oxygens are occupied followed by a row of vacancies, would likewise generate the same superlattice peak at q = (1/3, 0, 1/3), although this phase has not been previously reported. Scanning transmission electron microscopy (STEM) measurements on a separate, partially reduced sample (sample J) are detailed in Fig. 4b,c,d. The Fourier transform of a high-angle annular dark-field image reveals 1/3-order diffraction peaks corresponding to 3a0 ordering along both a and c, consistent with other recent transmission electron microscopy measurements on uncapped NdNiO2 films42. Additionally, annular bright-field data show regions with two filled apical oxygen chains alternating with a single vacant chain, consistent with the Nd3Ni3O8 structure shown in Fig. 4a, where the apical oxygen chains are directed into the page. Sample J was prepared using the same conditions as samples D–I, but with a four-unit-cell SrTiO3 cap. Although RSXS measurements were not performed on sample J, XRD and transport measurements (Supplementary Information) indicate that this sample is less reduced than sample D as both NdNiO2 and intermediate-phase peaks are visible in lab-based XRD. Since the difference in formation energies of the various ordered oxygen structures is small, it is possible that multiple compositions or structures of Nd3Ni3O7,8 could exist within our series of samples, depending on factors such as the reduction conditions or epitaxial strain43. A more detailed investigation of the precise structures of Nd3Ni3O7 or Nd3Ni3O8 in our thin films is currently the subject of further investigation. Nevertheless, the key point is that all the configurations of Nd3Ni3O7 or Nd3Ni3O8 will form a 3 × 1 × 3 supercell that will generate the q = (1/3, 0) superlattice peak at the observed wavevector. Finally, a macroscopic sample would be expected to possess equal domains of chains along both in-plane directions, in which case the superlattice peaks would then be observable along both H and K directions.
a, Schematic of the reduction pathway from the perovskite NdNiO3 to the intermediate oxygen-deficient phases of Nd3Ni3O7 or Nd3Ni3O8 and the infinite-layer NdNiO2; the corresponding samples measured in this study that lie on this pathway are also shown. b–d, STEM images of a mixed-phase sample (sample J) containing Nd3Ni3O7,8 intermediate phases. Fourier transform image (b) and corresponding high-angle annular dark-field image (c) of a defective region are shown. The positions of the third-order peaks in the Fourier transform are circled in green. An annular bright-field image showing two filled rows of apical oxygens (d), followed by one row of missing apical oxygen positions, corresponding to the schematic for Nd3Ni3O8 in a. In this image, the apical oxygen chains run into the page.
Our results suggest the scenario illustrated in Fig. 4a. The reduction of NdNiO3 into NdNiO2 occurs via the production of an intermediate, partially reduced Nd3Ni3O7 and/or Nd3Ni3O8 phase, where excess apical oxygen atoms (or vacancies) are ordered into rows with 3a0 periodicity forming a 3 × 1 × 3 supercell with a superlattice peak at the putative charge order wavevector of q = (1/3, 0, 1/3) (sample C). Because of its extremely strong intensity in the on-resonance case, this peak is detectable even if very small amounts of the partially reduced phase are present at levels nearly undetectable by conventional techniques (XRD, transport and XAS; that is, samples B, D and H). This picture is supported by a multitude of our observations: (1) the superlattice peak is absent in the plurality of low-resistivity, fully reduced NdNiO2 samples (samples E, F and I); (2) the superlattice peak from Nd3Ni3O7,8 (sample C) exhibits nearly identical energy, polarization and temperature dependence to NdNiO2 (sample D) as well as prior measurements on RENiO2 (refs. 10,11,12,13); (3) the peak is commensurate to the lattice and observable well off-resonance, indicating a strong structural component; (4) even a lightly reduced NdNiO3 sample devoid of any detectable NdNiO2 exhibits the superlattice peak (sample B); (5) position-dependent measurements correlate the q = (1/3, 0) peak, observed by RSXS, with the presence of partially reduced phases, observed by hard XRD at the same locations on the same sample (sample G); and (6) the direct observation of excess apical oxygen ordering with 3a0 periodicity in a partially reduced sample by STEM (sample J).
The presence of an ordered oxygen impurity phase also explains numerous discrepancies and unusual features in the literature. The strong intensity on the rare-earth edge is surprising for a charge ordering scenario, since the coupling of the rare-earth 4f electrons to the Ni3d electrons should be relatively weak and indirect, but should naturally occur for a structural Bragg peak where the Nd ions are displaced due to oxygen ordering. In addition, prior reports claim the presence/absence of a superlattice peak in uncapped versus capped samples of NdNiO2. Our measurements indicate that although the capping layer alone does not dictate the presence of the superlattice peak (all the samples were capped), even small variations in reduction conditions can result in residual amounts of Nd3Ni3O7,8. The doping dependence of the intensity of the superlattice peak, which is the strongest for the undoped parent compound and vanishing near x = 0.20, may also be naturally explained by the presence of an excess oxygen impurity phase. Bulk studies indicate that Sr doping, which increases the average targeted Ni valence of RE1−xSrxNiO2, makes the material easier to reduce36. Thus, the addition of Sr may naturally diminish the amount of residual RE3Ni3O7,8 in a sample and suppress the intensity of the q = (1/3, 0) Bragg peak. Finally, although our study is limited to NdNiO2+x, these findings should broadly apply to all infinite-layer nickelates, since Pr3Ni3O7 and La3Ni3O8 also form 3 × 1 × 3 superstructures and are known to be the reduction products of PrNiO3 and LaNiO3, respectively34,35,37. Although the superlattice peak in LaNiO2 shares many overall similarities with those in (Nd,Pr)NiO2, including its energy and temperature dependence, it does exhibit some subtle apparent differences, particularly a very slight displacement from the commensurate q = (1/3, 0) wavevector (Δq ≈ 0.01 r.l.u) (ref. 10) at x = 0. Future experiments will be important for conclusively determining the origins of the superlattice peak in the other members of infinite-layer nickelates. Although we focus here specifically on ordered excess oxygen phases, this highlights the role that excess oxygen may play in reduced films more broadly. The ordered excess oxygen phases appear to be highly insulating, and therefore, small inclusions may not substantially contribute to the electrical properties as a whole when averaging over an entire macroscopic sample. Nevertheless, if low concentrations of excess apical oxygen ions are randomly distributed, it is conceivable that they could potentially act as hole dopants, which could be consistent with traces of superconductivity observed in nominally undoped LaNiO2 (ref. 6).
Through a multimodal investigation of a large sequence of samples with varying levels of reduction, we conclude that charge ordering with 3a0 periodicity is not intrinsic to the infinite-layer nickelates. The superlattice peak previously identified as charge ordering at q = (1/3, 0) originates from the three-unit-cell ordering of excess apical oxygen ions in small amounts of brownmillerite-like inclusions of Nd3Ni3O7 or Nd3Ni3O8 produced during the reduction process. Topotactically reduced complex oxides present an exciting new frontier in quantum materials1,44, but this work also highlights some of the materials challenges inherent in these systems. We demonstrate RSXS as a highly sensitive and powerful probe for investigating these reduced compounds, which can detect even trace amounts of impurity phases. Although the phase diagrams of nickelates and cuprates show many similarities, including a superconducting dome and strong antiferromagnetic fluctuations on the underdoped side, this work establishes a clear distinction between the two families, namely, the fact that charge ordering does not appear to be directly relevant to the phase diagram of nickelates. This finding should have important implications for understanding universal models of high-temperature superconductivity, and may help to explain some of the key differences between the two families of materials.
Methods
Sample synthesis and characterization
Thin films of NdNiO3 were grown on SrTiO3(100) substrates using reactive-oxide molecular-beam epitaxy in a Veeco GEN10 system using elemental beams of Nd (Alfa Aesar, 99.900%) and Ni (Alfa Aesar, 99.995%). Substrates were etched to prepare a TiO2-terminated surface45 and annealed before growth at 650 °C until a clear reflection high-energy electron diffraction pattern was observed. Growths were performed at substrate temperatures between 480 and 500 °C in background pressures between 2 and 6 × 10−6 torr of ~80% distilled ozone. Initial flux calibration was performed by monitoring the reflection high-energy electron diffraction oscillations during the growths of binary oxides Nd2O3 on (ZrO2)0.905(Y2O3)0.095(111) and NiO on MgO(100) using the parameters outlined elsewhere46. Further stoichiometric optimization was performed by minimizing the NdNiO3(002)pc plane spacing21. Following the growth of the nickelate layer, a SrTiO3 capping layer was grown at 500 °C in a background pressure of 2 × 10−6 torr, following the calibration of the Sr and Ti sources by monitoring the reflection high-energy electron diffraction oscillations.
Samples were reduced using a beam of atomic hydrogen produced by a thermal source22,47, where molecular H2 is passed through a heated tungsten capillary (>1,900 °C) where it disassociates into individual atoms before interacting with the sample. Reductions were performed in an ultrahigh-vacuum chamber (Pbase < 1 × 10−10 torr) located on the same vacuum manifold as the molecular-beam epitaxy growth system at temperatures between 250 and 310 °C and hydrogen fluxes ranging between 1.8 and 2.7 × 1015 atoms cm–2 s–1. Typical reductions involved between 12 and 15 min of exposure to the atomic hydrogen beam to produce samples appearing fully reduced by lab-based XRD (samples D–I).
The structural quality of both perovskite and reduced samples were determined using Cu Kα1 XRD measurements performed on a PANalytical Empyrean X-ray diffractometer. Electrical transport measurements were performed using both a custom-built liquid-helium-cooled four-point probe measurement station (base temperature, 4 K) and a Quantum Design physical property measurement system (base temperature, 2 K). Finite-size factors were accounted for using the methods discussed elsewhere48. Contacts were prepared by either application of a dot of indium metal underneath a gold contact pin or by ultrasonic aluminium wire bonding.
RSXS measurements
The RSXS measurements were performed at the REIXS beamline of the Canadian Light Source on a four-circle diffractometer in an ultrahigh-vacuum chamber (P < 5 × 10−10 torr). The nominal photon flux and energy resolution were I0 = 5 × 1011 photons s–1 and ΔE/E ≈ 2 × 10−4, respectively. The incoming X-ray polarization was selected to be in either the σ (ε⊥ scattering plane) or π (ε∥ scattering plane) configuration with the polarization of scattered X-rays unmeasured. The measurements were conducted at photon energies between 815 and 1,050 eV with either a microchannel plate or a silicon drift detector with an angular acceptance of 0.9°. The silicon drift detector is an energy-resolved detector, with a resolution larger than 50 eV, which allows for the removal of the substantial oxygen fluorescence background produced by the SrTiO3 substrate. A precise alignment to the film crystallographic axes was achieved by detecting the (001), (101) and \((\overline{1}01)\) Bragg peaks of the SrTiO3 substrate with an energy of 2.5 keV.
Additional RSXS measurements (Supplementary Information) were performed at beamline 8.0.1 of the Advanced Light Source. For these measurements, a fixed π-polarization geometry was used and the nominal photon flux and energy resolution were ~1013 photons s–1 and ΔE/E ≈ 7 × 10−4, respectively. The fluorescence yield and scattering signal were recorded using a GaAsP photodiode (with an aluminium window to block visible light and photoelectrons) mounted at 100 mm from the sample with an acceptance angle of 3°. To consistently calibrate the photon energies between different beamlines, a perovskite–nickelate sample (sample A) was measured at both endstations as an energy reference. The energy scale was then defined with respect to the NdNiO3 Ni L3 peaks at 852.6 and 854.3 eV and O K prepeak at 527.9 eV to align with prior literature measurements9,10,28,49. All the momenta are quoted in r.l.u. relative to the NdNiO2 lattice, where a = 3.905 Å and c = 3.286 Å.
All the RSXS traces in the manuscript, with the exception of the data shown in Fig. 2a, are presented as unsubtracted raw data, namely, I/I0, where I is the intensity measured on the detector and I0 is the incident-beam intensity determined from the current on a mesh located upstream on the beamline. In Fig. 2a, a cubic background was subtracted only from sample D, to better compare it with sample C. In Fig. 3d, the temperature dependence of the peak areas and correlation lengths were obtained after subtracting a fixed, temperature-independent second- or third-order polynomial background, which was unchanged (apart from a scaling factor) for each sample. Supplementary Fig. 4 shows the raw data for these temperature series.
Spatially resolved hard XRD measurements
Scanning X-ray microdiffraction measurements were conducted at beamline 26-ID of the Advanced Photon Source at Argonne National Laboratory. A liquid-nitrogen-cooled Si(111) double-crystal monochromator was used to achieve an energy resolution of ΔE/E = 10−4 at a photon energy of 10.0 keV, and the scattered X-ray signal was recorded with an area detector, each pixel extending 0.00075 Å−1 along the Ewald sphere. The collimated X-ray beam was reduced to a spot size of 100 μm (full-width at half-maximum) using slits, yielding a flux of ~1010 photons s–1. The beam was vertically rastered along the sample, perpendicular to the scattering plane, to minimize the beam footprint and ensure that the spatial resolution of the linescan matched the beamwidth. A three-dimensional reciprocal-space map was obtained every 100 μm along a 4 mm line by rocking the sample by 4° per step in 41 steps and measuring a spatial linescan at each angle; Supplementary Fig. 11b shows projections of the map onto the L axis of the substrate/film.
STEM measurements
STEM characterization was performed on a cross-sectional lamella prepared with the standard focused-ion-beam lift-out procedure using a Thermo Fisher Helios G4 UX focused ion beam. High-angle annular dark-field imaging and annular bright-field–STEM imaging were performed on a Cs-corrected Thermo Fisher Scientific Spectra instrument at 300 kV and 30 mrad probe convergence semiangle. For high-precision structural measurements, a series of 40 rapid-frame images were acquired and subsequently realigned and averaged by a method of rigid registration optimized to prevent lattice hops50, resulting in a high-signal-to-noise-ratio, high-fidelity image of the atomic lattice.
Data availability
All data needed to evaluate the conclusions of this study are available in this Article and its Supplementary Information. Datasets generated and analysed during the course of this study are available at https://doi.org/10.34863/r44d-xt74. Source data are provided with this paper.
Change history
12 February 2024
A Correction to this paper has been published: https://doi.org/10.1038/s41563-024-01832-0
References
Li, D. et al. Superconductivity in an infinite-layer nickelate. Nature 572, 624–627 (2019).
Lu, H. et al. Magnetic excitations in infinite-layer nickelates. Science 373, 213–216 (2021).
Fowlie, J. et al. Intrinsic magnetism in superconducting infinite-layer nickelates. Nat. Phys. 18, 1043–1047 (2022).
Li, D. et al. Superconducting dome in Nd1−xSrxNiO2 infinite layer films. Phys. Rev. Lett. 125, 027001 (2020).
Zeng, S. et al. Phase diagram and superconducting dome of infinite-layer Nd1−xSrxNiO2 thin films. Phys. Rev. Lett. 125, 147003 (2020).
Osada, M. et al. Nickelate superconductivity without rare earth magnetism: (La,Sr)NiO2. Adv. Mater. 33, 2104083 (2021).
Jiang, M., Berciu, M. & Sawatzky, G. A. Critical nature of the Ni spin state in doped NdNiO2. Phys. Rev. Lett. 124, 207004 (2020).
Goodge, B. H. et al. Doping evolution of the Mott-Hubbard landscape in infinite-layer nickelates. Proc. Natl Acad. Sci. USA 118, e2007683118 (2021).
Hepting, M. et al. Electronic structure of the parent compound of superconducting infinite-layer nickelates. Nat. Mater. 19, 381–385 (2020).
Rossi, M. et al. A broken translational symmetry state in an infinite-layer nickelate. Nat. Phys. 18, 869–873 (2022).
Tam, C. C. et al. Charge density waves in infinite-layer NdNiO2 nickelates. Nat. Mater. 21, 1116–1120 (2022).
Krieger, G. et al. Charge and spin order dichotomy in NdNiO2 driven by the capping layer. Phys. Rev. Lett. 129, 027002 (2022).
Ren, X. et al. Symmetry of charge order in infinite-layer nickelates. Preprint at https://arxiv.org/abs/2303.02865 (2023).
Blanco-Canosa, S. et al. Resonant X-ray scattering study of charge-density wave correlations in YBa2Cu3O6+x. Phys. Rev. B 90, 054513 (2014).
Fink, J. et al. Phase diagram of charge order in La1.8−xEu0.2SrxCuO4 from resonant soft X-ray diffraction. Phys. Rev. B 83, 092503 (2011).
Hücker, M. et al. Stripe order in superconducting La2−xBaxCuO4 (0.095 ≤ x ≤ 0.155). Phys. Rev. B 83, 104506 (2011).
Tranquada, J., Sternlieb, B., Axe, J., Nakamura, Y. & Uchida, S. Evidence for stripe correlations of spins and holes in copper oxide superconductors. Nature 375, 561–563 (1995).
Ghiringhelli, G. et al. Long-range incommensurate charge fluctuations in (Y,Nd)Ba2Cu3O6+x. Science 337, 821–825 (2012).
Comin, R. et al. Charge order driven by Fermi-arc instability in Bi2Sr2−xLaxCuO6+δ. Science 343, 390–392 (2014).
Blanco-Canosa, S. et al. Momentum-dependent charge correlations in YBa2Cu3O6+δ superconductors probed by resonant X-ray scattering: evidence for three competing phases. Phys. Rev. Lett. 110, 187001 (2013).
Li, Y. et al. Impact of cation stoichiometry on the crystalline structure and superconductivity in nickelates. Front. Phys. 9, 719534 (2021).
Tschersich, K. G., Fleischhauer, J. P. & Schuler, H. Design and characterization of a thermal hydrogen atom source. J. Appl. Phys. 104, 034908 (2008).
Hayward, M. A., Green, M. A., Rosseinsky, M. J. & Sloan, J. Sodium hydride as a powerful reducing agent for topotactic oxide deintercalation: synthesis and characterization of the nickel(i) oxide LaNiO2. J. Am. Chem. Soc. 121, 8843–8854 (1999).
Lee, K. et al. Aspects of the synthesis of thin film superconducting infinite-layer nickelates. APL Mater. 8, 041107 (2020).
Lee, K. et al. Linear-in-temperature resistivity for optimally superconducting (Nd,Sr)NiO2. Nature 619, 288–292 (2023).
Rossi, M. et al. Orbital and spin character of doped carriers in infinite-layer nickelates. Phys. Rev. B 104, L220505 (2021).
Kawai, M. et al. Reversible changes of epitaxial thin films from perovskite LaNiO3 to infinite-layer structure LaNiO2. Appl. Phys. Lett. 94, 082102 (2009).
Bisogni, V. et al. Ground-state oxygen holes and the metal-insulator transition in the negative charge-transfer rare-earth nickelates. Nat. Commun. 7, 13017 (2016).
Abbate, M. et al. Electronic structure and metal-insulator transition in LaNiO3−δ. Phys. Rev. B 65, 155101 (2002).
Li, J. et al. Sudden collapse of magnetic order in oxygen-deficient nickelate films. Phys. Rev. Lett. 126, 187602 (2021).
Crespin, M., Levitz, B. Y. P. & Gatineau, L. Reduced forms of LaNiO3 perovskite. J. Chem. Soc., Faraday Trans. 2 79, 1181–1194 (1983).
Moriga, T. et al. Characterization of oxygen-deficient phases appearing in reduction of the perovskite-type LaNiO3 to La2Ni2O5. Solid State Ionics 79, 252–255 (1995).
Alonso, J. A. & Martínez-Lope, M. J. Preparation and crystal structure of the deficient perovskite LaNiO2.5, solved from neutron powder diffraction data. J. Chem. Soc., Dalton Trans. 17, 2819–2824 (1995).
Moriga, T. et al. Reduction of the perovskite-type LnNiO3 (Ln=Pr, Nd) to Ln3Ni3O7 with monovalent nickel ions. Solid State Ionics 74, 211–217 (1994).
Moriga, T., Hayashi, M., Sakamoto, T., Orihara, M. & Nakabayashi, I. Reduction processes of rare-earth nickelate perovskites LnNiO3 (Ln=La, Pr, Nd). Solid State Ionics 154–155, 251–255 (2002).
Wang, B.-X. et al. Synthesis and characterization of bulk Nd1−xSrxNiO2 and Nd1−xSrxNiO3. Phys. Rev. Mater. 4, 084409 (2020).
Sayagués, M., Vallet-Regí, M., Caneiro, A. & González-Calbet, J. Microstructural characterization of the LaNiO3−y system. J. Solid State Chem. 110, 295–304 (1994).
Wu, Y.-m et al. Topotactically induced oxygen vacancy order in nickelate single crystals. Phys. Rev. Mater. 7, 053609 (2023).
Hawthorn, D. G. et al. Resonant elastic soft X-ray scattering in oxygen-ordered YBa2Cu3O6+δ. Phys. Rev. B 84, 075125 (2011).
Achkar, A. J. et al. Distinct charge orders in the planes and chains of ortho-III-ordered YBa2Cu3O6+δ superconductors identified by resonant elastic X-ray scattering. Phys. Rev. Lett. 109, 167001 (2012).
Strempfer, J. et al. Oxygen superstructures throughout the phase diagram of (Y,Ca)Ba2Cu3O6+δ. Phys. Rev. Lett. 93, 157007 (2004).
Raji, A. et al. Charge distribution across capped and uncapped infinite layer neodymium nickelate thin films. Small 19, 2304872 (2023).
Gazquez, J. et al. Lattice mismatch accommodation via oxygen vacancy ordering in epitaxial La0.5Sr0.5CoO3−δ thin films. APL Mater. 1, 012105 (2013).
Kim, W. J. et al. Geometric frustration of Jahn-Teller order in the infinite-layer lattice. Nature 615, 237–243 (2023).
Koster, G., Kropman, B. L., Rijnders, G. J. H. M., Blank, D. H. A. & Rogalla, H. Quasi-ideal strontium titanate crystal surfaces through formation of strontium hydroxide. Appl. Phys. Lett. 73, 2920–2922 (1998).
Sun, J. et al. Canonical approach to cation flux calibration in oxide molecular-beam epitaxy. Phys. Rev. Mater. 6, 033802 (2022).
Tschersich, K. G. & von Bonin, V. Formation of an atomic hydrogen beam by a hot capillary. J. Appl. Phys. 84, 4065–4070 (1998).
Miccoli, I., Edler, F., Pfnür, H. & Tegenkamp, C. The 100th anniversary of the four-point probe technique: the role of probe geometries in isotropic and anisotropic systems. J. Phys.: Condens. Matter 27, 223201 (2015).
Kim, T. H. et al. Strain-driven disproportionation at a correlated oxide metal-insulator transition. Phys. Rev. B 101, 121105 (2020).
Savitzky, B. H. et al. Image registration of low signal-to-noise cryo-STEM data. Ultramicroscopy 191, 56–65 (2018).
Acknowledgements
In memory of our colleague Lena F. Kourkoutis, an outstanding scientist, mentor and microscopist. This work was primarily supported by the US Department of Energy (DOE), Office of Basic Energy Sciences, under contract no. DE-SC0019414. This research used resources of the Advanced Light Source, a US DOE Office of Science User Facility, under contract no. DE-AC02-05CH11231, as well as the Center for Nanoscale Materials and the Advanced Photon Source, both US DOE Office of Science User Facilities operated for the DOE Office of Basic Energy Sciences by Argonne National Laboratory under contract no. DE-AC02-06CH11357. Part of the research described in this paper was performed at the Canadian Light Source, a national research facility of the University of Saskatchewan, which is supported by the Canada Foundation for Innovation (CFI), the Natural Sciences and Engineering Research Council (NSERC), the National Research Council (NRC), the Canadian Institutes of Health Research (CIHR), the Government of Saskatchewan and the University of Saskatchewan. Additional support for materials synthesis was provided by the Air Force Office of Scientific Research (grant no. FA9550-21-1-0168), the National Science Foundation (no. DMR-2104427) and the Gordon and Betty Moore Foundation’s EPiQS Initiative through grant nos. GBMF3850 and GBMF9073. Substrate preparation was performed in part at the Cornell NanoScale Facility, a member of the National Nanotechnology Coordinated Infrastructure, which is supported by the NSF (grant no. NNCI-2025233). We would like to thank S. Palmer and S. Button for their assistance in substrate preparation. STEM characterizations were performed at the Cornell Center for Materials Research Facilities supported by the National Science Foundation (DMR-1719875). The microscopy work at Cornell was supported by the NSF PARADIM (DMR-2039380), with additional support from Cornell University, the Weill Institute and the Kavli Institute at Cornell. L.B. and L.F.K. acknowledge support from the Packard Foundation. G.H. acknowledges support from Severo Ochoa FUNFUTURE (no. CEX2019-000917-S) of the Spanish Ministry of Science and Innovation and by the Generalitat de Catalunya (2021 SGR 00445). K.M.S. would like to acknowledge the hospitality of ICMAB-CSIC during his sabbatical. We would like to sincerely thank J. Fontcuberta, H. Y. Hwang, W. S. Lee and D. A. Muller for helpful discussions and insights.
Author information
Authors and Affiliations
Contributions
C.T.P. and K.M.S. conceived the research and designed the experiment. C.T.P., Y.W. and V.A. synthesized, reduced and characterized the thin-film samples, with input from D.G.S. and K.M.S. C.T.P., N.K.G., Y.W., V.A., M.B., R.G., R.S., Y.-D.C., D.G.H. and F.H. performed the RSXS measurements. L.B. and L.F.K. performed the STEM experiments. B.Z.G., A.L., T.Z. and A.S. performed the synchrotron hard XRD experiments. The results were analysed and interpreted by C.T.P., N.K.G., Y.W., V.A., G.H., D.G.H. and K.M.S. C.T.P. and K.M.S. wrote the manuscript, with input from all authors.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Materials thanks Giacomo Ghiringhelli, Xingye Lu and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Supplementary Information
Supplementary Figs. 1–13 and discussion.
Source data
Source Data Fig. 1
Source data for Fig. 1.
Source Data Fig. 2
Source data for Fig. 2.
Source Data Fig. 3
Source data for Fig. 3.
Source Data Fig. 4
Source data (TIFF files) for Fig. 4.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Parzyck, C.T., Gupta, N.K., Wu, Y. et al. Absence of 3a0 charge density wave order in the infinite-layer nickelate NdNiO2. Nat. Mater. 23, 486–491 (2024). https://doi.org/10.1038/s41563-024-01797-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/s41563-024-01797-0
- Springer Nature Limited
This article is cited by
-
A noticeable absence
Nature Materials (2024)