Abstract
Chiral magnetic phases with an unconventional topological twist in the magnetization are of huge interest due to their potential in spintronics applications. Here, we present a general method to induce such exotic magnetic phases using interfacial phase frustration within artificially grown superlattices. To demonstrate our method, we consider a multilayer with two different chiral magnetic phases as the competing orders at the top and bottom and show, using Monte Carlo calculations, that the interfacial phase frustration is realized at the central layer. In particular, we obtain three unconventional phases: a checkerboard skyrmion crystal, an incommensurate skyrmion stripe, and a ferrimagnetic skyrmion crystal. In these frustration-induced phases, the spin chirality-driven topological Hall conductivity can be largely enhanced. This method provides a playground to realize unconventional magnetic phases in any family of materials that can be grown in superlattices.
Similar content being viewed by others
Introduction
Magnetic frustration arises from the incompatibility of the interactions between magnetic degrees of freedom in a lattice with the underlying crystal geometry and often produces exotic ground states, such as spin ice and spin liquids1,2. These frustration-stabilized magnetic phases opened a window to understand the fundamentals of magnetism and to use them in technological applications, as exemplified by the search for quantum spin liquids3,4,5. The collective behavior of the spins, influenced by the frustration, often leads to chiral correlations in otherwise non-chiral ordered magnetic ground states6,7. Specifically, chiral magnetic textures are the focus of intense investigation because of their potential in spintronic applications, and for their role in producing topological Hall effects from the emergent magnetic field created by the magnetic texture8,9,10.
A prominent example of such chiral magnetic texture with a continuous winding of magnetization is a skyrmion, stabilized commonly as a triangular crystal in various bulk compounds and interfaces by competing Heisenberg ferromagnetic exchange and relativistic Dzyaloshinskii-Moriya interaction (DMI)11,12,13,14,15,16. The skyrmion crystal phase was also theoretically predicted to be stabilized without DMI in geometrically-frustrated magnets or in highly-symmetric lattices with long-range Ruderman–Kittel–Kasuya–Yosida interaction17,18,19,20. Three-dimensional variants of skyrmions, viz., skyrmion strings21, chiral bobbers22, and hopfions23 have been experimentally observed. However, the variety of these chiral magnetic textures beyond the skyrmion crystal is severely limited by the available magnetic interactions in bulk compounds.
In this work, we propose a method to create unconventional magnetic phases by using interfacial magnetic phase frustration as a driving mechanism. In the conventional geometrical frustration, as in spins in a triangular lattice, couplings at various distances lead to unconventional phases due to competing tendencies. Here, in a multilayer geometry, the competition arises at the center of a multilayer ensemble where dominant top and bottom states are not compatible with one another, thus stabilizing exotic central magnetic phases through interfacial phase frustration (IPF). In Fig. 1, we show a sketch of our proposed platform, involving two 5d compounds at top and bottom, such as SrIrO3 and CaIrO3 with robust DMI coupling, as well as metallic lanthanum manganites La1−xSrxMnO3 (LSMO). The interface-induced DMI from the iridate generates, e.g., chiral magnetic phases in thin LSMO regions16,24. In this set-up, the two LSMO layers can acquire a variety of magnetic phases including a spiral or a skyrmion crystal with various radii, depending on the doping level in the LSMO and the DMI strength at the iridate/LSMO interfaces. When two different magnetic phases are realized in the two LSMO layers, the interface between them will suffer the IPF that will produce an unconventional magnetic phase. We verified our proposal by performing Monte Carlo (MC) calculations using a spin Hamiltonian for a magnetic multilayer. We consider three cases and obtain three unconventional magnetic phases: (i) a checkerboard skyrmion crystal (CSkX) that appears from the competition between two orthogonally-aligned spin spirals, (ii) an incommensurate skyrmion stripe (ISkS) that arises from the competition between a spin spiral and a triangular skyrmion crystal, and (iii) a ferrimagnetic skyrmion crystal (FSkX) that arises from the competition between a triangular skyrmion crystal and a standard antiferromagnet. The emergent phases in the middle layer are unconventional, multi-q magnetic textures and are predicted to stabilize in future experimental investigations. The CSkX is particularly interesting as it is created without any external magnetic field and is, therefore, promising for spintronic application. Furthermore, the CSkX produces a large topological Hall effect, induced by a nonzero scalar spin chirality, which is absent in the competing spin spirals. Thus, chirality arises from non-chiral components.
IPF paves the way to study artificial electrodynamics and unconventional magnetic excitations hosted by the frustration-stabilized magnetic phase in magnetic multilayers. It also broadens the class of chiral magnetic phases hosting skyrmions. This IPF can be realized generically using any two different competing magnetic phases. The primary advantage of the generation of unconventional magnetic orders via IPF is that the periodicity of the generated textures can be controlled by changing the constituent magnetic phases above and below. Additional potential material platforms for the experimental realization of the proposed IPF include superlattices of transition-metal oxide interfaces involving manganites in which a plethora of magnetic phases are already available for both Sr- and Ca-doped compounds25,26,27,28, chiral magnets e.g., MnSi and MnGe, as well as quasi-two-dimensional magnets, such as CrI3 or Fe3GeTe2. Similar frustration-induced patterns can also be found in the domain walls between two or more magnetic phases29.
Results
Model
Consider a multilayer heterostructure, with the top and the bottom layers hosting two different stable magnetic phases, such as the LSMO 1 and LSMO 2 layers in Fig. 1. The magnetic phases of LSMO, above and below our focus—the central layer, are influenced by the iridate/LSMO(1,2) interfaces. They can be described by the following Hamiltonian, with a ferromagnetic Heisenberg exchange coupling (because LSMO has a metallic ferromagnetic phase in a broad Sr-doping region), a DMI term from the iridates, and a single-ion uniaxial anisotropy
Si represents a classical spin vector at site i, J is the ferromagnetic exchange between neighboring spins, D is the DMI coupling, \({\hat{e}}_{ij}\) is the unit vector connecting sites i and j, and Az is the strength of uniaxial anisotropy along the z direction. The values of these parameters define separately the magnetic ground states in each layer. We keep the spin amplitude S = 1 and exchange coupling amplitude J = 1 throughout this paper, for simplicity. The individual layers are coupled via a ferromagnetic Heisenberg exchange coupling \({{{\mathcal{H}}}}\,=\,-J\,{\sum }_{\langle ij\rangle }\,{{{{\bf{S}}}}}_{i}\,\cdot \,{{{{\bf{S}}}}}_{j}\). We consider a five-layer heterostructure and perform MC annealing to obtain the spin configurations in all layers.
Checkerboard skyrmion crystal
We first consider two spin spirals as the top and bottom layers. The spin spiral phase, which appears with a finite DMI in the absence of any magnetic field or uniaxial anisotropy, has two degenerate spiral solutions, aligned mutually orthogonal to each other. One of these two preferred directions can be realized by directional tuning of a magnetic anisotropy30 or strain mismatching31. In our MC calculations, these two spin spirals were spontaneously generated along the preferred directions by applying a small inplane anisotropy, described by \({{{{\mathcal{H}}}}}_{{{{\rm{in}}}}}^{{{{\rm{aniso}}}}}\,=\,-{A}_{{{{\rm{in}}}}}\,{\sum }_{i}\,({S}_{xi}^{2}\cos \theta +{S}_{yi}^{2}\sin \theta )\) along θ = 45∘ and θ = 135∘ at the top and the bottom layers, with Ain = 0.05 J. Figure 2a–d shows the spin configurations at different layers of the considered five-layer heterostructure. The competition between the two spin spirals produces an unconventional checkerboard skyrmion crystal (CSkX). The spin structure factor \(S({{{\bf{q}}}})\,=\,(1/N){\sum }_{ij}\langle {{{{\bf{S}}}}}_{i}\,\cdot \,{{{{\bf{S}}}}}_{j}\rangle {e}^{-i{{{\bf{q}}}}\cdot {{{{\bf{r}}}}}_{ij}}\)—where rij is the position vector connecting spins Si and Sj and N is the total number of lattice sites—is shown in the inset of Fig. 2b and characterizes the double characteristic-momenta q of the CSkX. Skyrmions are known to arise in non-centrosymmetric systems with a DMI and in centrosymmetric magnets with a geometrically-frustrated triangular lattice. It was unclear if skyrmions could appear without inversion symmetry breaking or geometrical frustration. Recent experiments reported a square skyrmion crystal in GdRu2Si2, which is not explained by any of these two known mechanisms32. Our results may shed light on the origin of the reported square arrangement of skyrmions in centrosymmetric itinerant magnets.
Incommensurate skyrmion stripe
Next, we focus on the second exotic state that we found, by considering a triangular skyrmion crystal at the top layer and a spin spiral at the bottom layer, as depicted in Fig. 3b and c, respectively. The lower critical magnetic field to obtain the skyrmion crystal depends on the DMI strength33, and therefore, in a heterostructure setting with two different values of the DMI strengths, the top and the bottom layers can host skyrmion crystal and spin spiral phases at a finite magnetic field. More interestingly, a skyrmion crystal can be stabilized by a uniaxial anisotropy without the need of any magnetic field, as observed, for example, in the quasi-two-dimensional van der Waals magnet Fe3GeTe234. In our MC calculation, the skyrmion crystal is realized in the presence of a perpendicular magnetic anisotropy at the top layer, at zero magnetic field. As shown in Fig. 4, the spin configuration stabilized at the central layer by the IPF, due to the top skyrmion crystal and bottom spin spiral, is an unconventional multi-q magnetic phase which we call incommensurate skyrmion stripe (ISkS) since the diagonal stripe order consists of four types of incommensurate skyrmionic patterns. Note the appearance of a skyrmionic diagonal pattern induced by the bottom layer which does not have skyrmions. Specifically, the spin structure factor S(q), shown in the inset of Fig. 3b, reveals multiple peaks. A careful inspection of this S(q) profile indicates that among the nine peaks there are five characteristic momenta q for this ISkS—the peak at zero momentum is for the ferromagnetic correlation, one of the two bright peaks inclined along 45∘ is for the diagonal stripe order, and three out of the six hexagon-shaped peaks are for the skyrmionic correlations.
Ferrimagnetic skyrmion crystal
In our third case, we consider a magnetic trilayer with a skyrmion crystal at the top layer and staggered antiferromagnetic order at the bottom layer. This situation can appear in our considered multilayer with different amounts of doping in the top and bottom LSMO layers. As in the previous case, the skyrmion crystal is stabilized in our MC calculations by a finite DMI and an uniaxial anisotropy. On the other hand, the antiferromagnetic order is achieved in our spin Hamiltonian by a negative Heisenberg exchange constant J = −1, without DMI and uniaxial anisotropy. The magnetic configuration, generated at the central layer due to the IPF, is shown in Fig. 4a, b, while the skyrmion crystal at the top layer and the antiferromagnetic configuration at the bottom layer are shown in Fig. 4c and d. The IPF-stabilized texture contains remnants of the skyrmion crystal in the background of a ferrimagnetic order, thus the name ferrimagnetic skyrmion crystal (FSkX). The spin structure factor S(q), shown in the inset of Fig. 4b, reveals a multi-q pattern which has fingerprints of both the skyrmion crystal and the antiferromagnetic order.
Topological Hall response
Magnetic skyrmions are known to produce a topological Hall effect due to the emergent magnetic field \({B}_{z}\,=\,\frac{1}{2}{{{\bf{n}}}}\,\cdot \,\left(\,{\partial }_{x}{{{\bf{n}}}}\,\times \,{\partial }_{y}{{{\bf{n}}}}\right)\) generated from the magnetic texture, where n represents the spin vector on the unit sphere created by the spin angles8,9. Even though the proposed IPF mechanism is applicable to any type of magnetic phases—irrespective of its chiral nature—because the three cases considered in this study are related to skyrmions—either as top and bottom components or induced by IPF—we analyzed the topological Hall response for the IPF-stabilized magnetic phases and compare with that of the constituent phases.
To consider the impact that a chiral magnetic phase, such as those predicted, would have on the transverse Hall conductivity, it is useful to investigate the local scalar spin chirality χ(ri), which is a real-space equivalent of the Berry curvature that produces the Anomalous Hall Effect and is defined as
where 〈ijk〉 represents three neighboring lattice sites on a triangule of spins within the considered square lattice grid. The profile of χ(ri) for the three IPF-stabilized magnetic phases is depicted in Fig. 5a–c, revealing a finite scalar spin chirality in all three phases. In order to compute the transverse Hall conductivity of these magnetic phases, we consider the following mobile fermions double-exchange Hamiltonian
where t is the nearest-neighbor electron hopping energy and JDE is the Hund exchange coupling strength between the itinerant electron spin σ and the localized spin Si at a particular layer. In other words, we consider mobile electrons in the background of the fixed IPF textures. The topological Hall conductivity is obtained via the canonical Kubo formula
where fm is the Fermi function at temperature T and energy eigenvalue ϵm, \({\hat{j}}_{x}\) is the current operator along the x direction, \(\left|m\right\rangle\) is the mth eigenvector of \({{{{\mathcal{H}}}}}_{{{{\rm{DE}}}}}\), and η is the relaxation rate. We used t = 1, JDE = 1, and η = 0.1 for the present analysis, with no qualitative difference in the description for other choices, as discussed before16. In Fig. 5d, we present the topological Hall conductivity for the magnetic textures that we consider in the three cases discussed above. Clearly, \({\sigma }_{{}_{{{{\rm{TH}}}}}}\) is finite for all three chiral magnetic phases stabilized by the IPF. Notably, \({\sigma }_{{}_{{{{\rm{TH}}}}}}\) acquires a finite value for the CSkX phase, even though the contribution from the spin spirals on the top and the bottom layers are nearly zero. This finding, therefore, could be "fingerprints" useful in deciphering topological Hall signals from magnetic multilayers where the top and bottom spin spirals are oriented along different directions. We also note that \({\sigma }_{{}_{{{{\rm{TH}}}}}}\) from the other two IPF-stabilized magnetic phases, viz., ISkS and FSkX, are comparable to that of the constituent skyrmion crystal, which implies that the resultant topological Hall effect will be nearly doubled that of the expected value from only the skyrmion crystal. The appearance of topological Hall effect from non-skyrmionic magnetic phases is an interesting topic of recent discussion33,35. The current findings support these theoretical predictions, albeit via a totally different IPF platform, and seek further experimental studies in this direction—exploring topological Hall effect from non-skyrmionic chiral magnetic textures.
In our five-layer structures, the extreme top and the bottom layers represent the stable constituent magnetic phases, while the central layer reveals the IPF-induced magnetic phase. The second and fourth layers show deformed intermediate magnetic configurations, as shown in Figs. 2a, 3a, and 4a, and these layers can also possess a finite scalar spin chirality or topological charge. We also noted that despite the little imperfections in the top and bottom spin configurations that we obtained via MC annealing, the IPF-induced pattern at the central layer defines an unconventional state.
Discussion
The interfacial DMI, which is primarily responsible for the chiral magnetic interactions, can be controlled in 3d–5d transition-metal-oxide-based superlattices, such as those made of manganite/iridate interfaces by engineering the interfacial inversion symmetry36,37. With advancements in the deposition techniques, the layer thickness can also tune the Rashba-type interfacial DMI, Dresselhaus-type bulk DMI, and the anisotropy in the B20 structures, such as CrGe/MnGe/FeGe and their superlattices38. Additional strain control in these B20 structures can, furthermore, create complex spin textures from the superposition of different helical domains39. Therefore, the CrGe/MnGe/FeGe compounds could be used for the experimental realization of the discussed IPF and generate unconventional magnetic phases. Besides transition metal oxide interfaces and chiral magnets hosting skyrmions, the IPF may be explored in quasi-two-dimensional magnets, such as CrI3, or Fe-based van der Waals magnets, such as Fe3GeTe2.
The appearance of a multi-q order is a generic property of the IPF-induced phases. These multi-q phases can harbor soft magnetic modes that can be controlled by an electric field, leading to a characteristic magnetoelectric effect18. Furthermore, due to the frustration, these multi-q phases may allow skyrmions and anti-skyrmions to be present together in an exotic thermodynamic phase that can host magnetic monopoles17.
The IPF-induced phases are, in general, expected to appear below the critical temperatures of the constituent magnetic phases in the multilayer, whichever is lesser. The chiral magnetic phases including the SkX commonly appear below 100 K, as revealed by topological Hall effect measurements40,41,42,43. Therefore, the three unconventional SkX phases that we discuss here are also expected to appear within a similar temperature range. Nonetheless, by choosing constituent phases that persist at higher temperatures, it is possible to realize unconventional magnetic phases at higher temperatures.
There is a growing interest in three-dimensional chiral magnetic phases for the urge to understand the complexity arising from topology and frustration in three dimensions, and also for their potential spintronic applications23,44,45. With the layer control that is predicted here, it would be possible to achieve unconventional magnetic phases with potential functionalities. The synthetic spin-orbit coupling available in these exotic skyrmion crystals may also be useful in fault-tolerant topological quantum computing46,47.
To summarize, we proposed a method to stabilize never-observed-before magnetic phases by using interfacial phase frustration in multilayers. As example, we obtained three exotic magnetic phases in our MC calculations, generated by this interfacial phase frustration. We hope that the proposed frustration mechanism will open a path, aiding the search for unconventional magnetism in three dimensions.
Methods
Monte Carlo simulations
We perform Monte Carlo (MC) annealing to obtain the ground state spin configuration in the discussed magnetic multilayer. We consider periodic boundary conditions in plane and use the Metropolis spin update procedure. The ground state magnetic configurations at the top two and the bottom two layers in our five-layer structure were first stabilized by performing MC annealing, without any communication between the top two and bottom two layers. Next, we switch on the interlayer coupling between all the layers and perform MC annealing in the entire multilayer. During this process, we start from a completely random spin configuration at the middle layer. In the MC annealing processes, we start at a high-temperature T = 5J and very slowly reduce the temperature down to T = 0.001 J. At each temperature, a large number of MC spin updates, typically of the order of 1011, were performed to avoid being trapped in metastable states.
Data availability
Data are available from the corresponding author upon reasonable request.
Code availability
Simulation codes are available from the corresponding author upon reasonable request.
References
Bramwell, S. T. & Gingras, M. J. P. Spin ice state in frustrated magnetic pyrochlore materials. Science 294, 1495–1501 (2001).
Balents, L. Spin liquids in frustrated magnets. Nature 464, 199–208 (2010).
Kitaev, A. Fault-tolerant quantum computation by anyons. Ann. Phys. 303, 2–30 (2003).
Savary, L. & Balents, L. Quantum spin liquids: a review. Rep. Prog. Phys. 80, 016502 (2016).
Batista, C. D., Lin, S.-Z., Hayami, S. & Kamiya, Y. Frustration and chiral orderings in correlated electron systems. Rep. Prog. Phys. 79, 084504 (2016).
Taguchi, Y., Oohara, Y., Yoshizawa, H., Nagaosa, N. & Tokura, Y. Spin chirality, Berry phase, and anomalous Hall effect in a frustrated ferromagnet. Science 291, 2573–2576 (2001).
Grohol, D. et al. Spin chirality on a two-dimensional frustrated lattice. Nat. Mater. 4, 323–328 (2005).
Schulz, T. et al. Emergent electrodynamics of skyrmions in a chiral magnet. Nat. Phys. 8, 301–304 (2012).
Nagaosa, N. & Tokura, Y. Topological properties and dynamics of magnetic skyrmions. Nat. Nanotechnol. 8, 899–911 (2013).
Fert, A., Reyren, N. & Cros, V. Magnetic skyrmions: advances in physics and potential applications. Nat. Rev. Mater. 2, 17031 (2017).
Rößler, U. K., Bogdanov, A. N. & Pfleiderer, C. Spontaneous skyrmion ground states in magnetic metals. Nature 442, 797–801 (2006).
Mühlbauer, S. et al. Skyrmion lattice in a chiral magnet. Science 323, 915–919 (2009).
Yu, X. Z. et al. Real-space observation of a two-dimensional skyrmion crystal. Nature 465, 901–904 (2010).
Li, X., Liu, W. V. & Balents, L. Spirals and skyrmions in two-dimensional oxide heterostructures. Phys. Rev. Lett. 112, 067202 (2014).
Das, S. et al. Observation of room-temperature polar skyrmions. Nature 568, 368–372 (2019).
Mohanta, N., Dagotto, E. & Okamoto, S. Topological Hall effect and emergent skyrmion crystal at manganite-iridate oxide interfaces. Phys. Rev. B 100, 064429 (2019).
Okubo, T., Chung, S. & Kawamura, H. Multiple-q states and the skyrmion lattice of the triangular-lattice Heisenberg antiferromagnet under magnetic fields. Phys. Rev. Lett. 108, 017206 (2012).
Leonov, A. O. & Mostovoy, M. Multiply periodic states and isolated skyrmions in an anisotropic frustrated magnet. Nat. Commun. 6, 8275 (2015).
Ozawa, R., Hayami, S. & Motome, Y. Zero-field skyrmions with a high topological number in itinerant magnets. Phys. Rev. Lett. 118, 147205 (2017).
Wang, Z., Su, Y., Lin, S.-Z. & Batista, C. D. Skyrmion crystal from RKKY interaction mediated by 2D electron gas. Phys. Rev. Lett. 124, 207201 (2020).
Park, H. S. et al. Observation of the magnetic flux and three-dimensional structure of skyrmion lattices by electron holography. Nat. Nanotechnol. 9, 337–342 (2014).
Zheng, F. et al. Experimental observation of chiral magnetic bobbers in B20-type FeGe. Nat. Nanotechnol. 13, 451–455 (2018).
Kent, N. et al. Creation and observation of Hopfions in magnetic multilayer systems. Nat. Commun. 12, 1562 (2021).
Mohanta, N., Christianson, A. D., Okamoto, S. & Dagotto, E. Signatures of a liquid-crystal transition in spin-wave excitations of skyrmions. Commun. Phys. 3, 229 (2020).
Yunoki, S., Hotta, T. & Dagotto, E. Ferromagnetic, A-type, and charge-ordered CE-type states in doped manganites using Jahn–Teller phonons. Phys. Rev. Lett. 84, 3714–3717 (2000).
Moreo, A., Mayr, M., Feiguin, A., Yunoki, S. & Dagotto, E. Giant cluster coexistence in doped manganites and other compounds. Phys. Rev. Lett. 84, 5568–5571 (2000).
Dagotto, E., Hotta, T. & Moreo, A. Colossal magnetoresistant materials: the key role of phase separation. Phys. Rep. 344, 1–153 (2001).
Hotta, T. et al. Unveiling new magnetic phases of undoped and doped manganites. Phys. Rev. Lett. 90, 247203 (2003).
Schoenherr, P. et al. Topological domain walls in helimagnets. Nat. Phys. 14, 465–468 (2018).
Garnier, L.-C. et al. Stripe domains reorientation in ferromagnetic films with perpendicular magnetic anisotropy. J. Phys. Mater. 3, 024001 (2020).
Bishop, C. B., Moreo, A. & Dagotto, E. Bicollinear antiferromagnetic order, monoclinic distortion, and reversed resistivity anisotropy in FeTe as a result of spin-lattice coupling. Phys. Rev. Lett. 117, 117201 (2016).
Khanh, N. D. et al. Nanometric square skyrmion lattice in a centrosymmetric tetragonal magnet. Nat. Nanotechnol. 15, 444–449 (2020).
Mohanta, N., Okamoto, S. & Dagotto, E. Planar topological Hall effect from conical spin spirals. Phys. Rev. B 102, 064430 (2020).
Yang, M. et al. Creation of skyrmions in van der Waals ferromagnet Fe3GeTe2 on (Co/Pd)n superlattice. Sci. Adv. 6, eabb5157 (2020).
Nakane, J. J., Nakazawa, K. & Kohno, H. Topological Hall effect in weakly canted antiferromagnets. Phys. Rev. B 101, 174432 (2020).
Yi, D. et al. Atomic-scale control of magnetic anisotropy via novel spin-orbit coupling effect in La2/3Sr1/3Mno3/SrIrO3 superlattices. Proc. Natl. Acad. Sci. 113, 6397–6402 (2016).
Skoropata, E. et al. Interfacial tuning of chiral magnetic interactions for large topological Hall effects in LaMnO3/SrIrO3 heterostructures. Sci. Adv. 6, eaaz3902 (2020).
Ahmed, A. S., Esser, B. D., Rowland, J., McComb, D. W. & Kawakami, R. K. Molecular beam epitaxy growth of [CrGe/MnGe/FeGe] superlattices: toward artificial B20 skyrmion materials with tunable interactions. J. Cryst. Growth 467, 38–46 (2017).
Repicky, J. et al. Atomic-scale visualization of topological spin textures in the chiral magnet MnGe. Science 374, 1484–1487 (2021).
Neubauer, A. et al. Topological Hall effect in the A phase of MnSi. Phys. Rev. Lett. 102, 186602 (2009).
Matsuno, J. et al. Interface-driven topological Hall effect in SrRuO3-SrIrO3 bilayer. Sci. Adv. 2, e1600304 (2016).
Wang, L. et al. Ferroelectrically tunable magnetic skyrmions in ultrathin oxide heterostructures. Nat. Mater. 17, 1087–1094 (2018).
Vistoli, L. et al. Giant topological Hall effect in correlated oxide thin films. Nat. Phys. 15, 67–72 (2019).
Fernández-Pacheco, A. et al. Three-dimensional nanomagnetism. Nat. Commun. 8, 15756 (2017).
Gao, S. et al. Fractional antiferromagnetic skyrmion lattice induced by anisotropic couplings. Nature 586, 37–41 (2020).
Mohanta, N., Okamoto, S. & Dagotto, E. Skyrmion control of Majorana states in planar Josephson junctions. Commun. Phys. 4, 163 (2021).
Mascot, E., Bedow, J., Graham, M., Rachel, S. & Morr, D. K. Topological superconductivity in skyrmion lattices. npj Quantum Mater. 6, 6 (2021).
Acknowledgements
This work was supported by the U.S. Department of Energy, Office of Science, Basic Energy Sciences, Materials Sciences and Engineering Division.
Author information
Authors and Affiliations
Contributions
All authors contributed to all aspects of this work.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Mohanta, N., Dagotto, E. Interfacial phase frustration stabilizes unconventional skyrmion crystals. npj Quantum Mater. 7, 76 (2022). https://doi.org/10.1038/s41535-022-00483-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41535-022-00483-1
- Springer Nature Limited
This article is cited by
-
Electrical detection of mobile skyrmions with 100% tunneling magnetoresistance in a racetrack-like device
npj Quantum Materials (2024)
-
Lifetime of coexisting sub-10 nm zero-field skyrmions and antiskyrmions
npj Quantum Materials (2023)