Abstract
The use of solid-state electrolytes to provide safer, next-generation rechargeable batteries is becoming more feasible as materials with greater stability and higher ionic diffusion coefficients are designed. However, accurate determination of diffusion coefficients in solids is problematic and reliable calculations are highly sought-after to understand how their structure can be modified to improve their performance. In this paper we compare diffusion coefficients calculated using nonequilibrium and equilibrium ab initio molecular dynamics simulations for highly diffusive solid-state electrolytes, to demonstrate the accuracy that can be obtained. Moreover, we show that ab initio nonequilibrium molecular dynamics can be used to determine diffusion coefficients when the diffusion is too slow for it to be feasible to obtain them using ab initio equilibrium simulations. Thereby, using ab initio nonequilibrium molecular dynamics simulations we are able to obtain accurate estimates of the diffusion coefficients of Li ions in Li6PS5Cl and Li5PS4Cl2, two promising electrolytes for all-solid-state batteries. Furthermore, these calculations show that the diffusion coefficient of lithium ions in Li5PS4Cl2 is higher than many other potential all-solid-state electrolytes, making it promising for future technologies. The reasons for variation in conductivities determined using computational and experimental methods are discussed. It is demonstrated that small degrees of disorder and vacancies can result in orders of magnitude differences in diffusivities of Li ions in Li6PS5Cl, and these factors are likely to contribute to inconsistencies observed in experimentally reported values. Notably, the introduction of Li-vacancies and disorder can enhance the ionic conductivity of Li6PS5Cl.
Similar content being viewed by others
Introduction
Finding alternative materials for use in technologies for energy production and storage is one of the challenges that scientists are facing today. In 1991, the Sony corporation introduced the first commercial Li-ion batteries as a power source1. Since then much research has been carried out to improve the performance and quality of Li-ion batteries2,3. Compared to other energy storage materials, Li-ion batteries have shown advantages such as higher energy density and longer life-times2,4. However, after almost three decades of using these batteries, they still have a critical safety problem that is partly due to the use of organic liquid electrolytes. The flammability and low thermal stability of liquid electrolytes mean batteries with liquid electrolytes can leak or ignite if they become overheated5,6. Due to current and future applications of rechargeable batteries in products such as cell phones, laptops, energy storage for short-haul airplanes and electric vehicles, it is very important for industries to find a safe replacement.
In recent years, the all-solid-state battery (ASSB) has been introduced. This type of battery works in the same way as traditional Li-ion batteries, with the most significant difference being in their electrolytes. Instead of flammable liquid electrolytes, ASSBs have inorganic solid electrolytes with higher thermal stabilities7,8. Compared with liquid and polymer electrolytes, ASSBs are safer, lighter, have higher energy density, and are more durable9,10,11. Also, many solid electrolytes are suitable for use in combination with cathode materials with higher potential capacities because of their large window of electrochemical stability12.
A solid-state electrolyte that is comparable with its liquid counterpart in terms of performance should be able to conduct lithium ions from the cathode material to the anode material efficiently. In order to achieve this, the ionic conductivity of the electrolyte should be higher than approximately 10−3 S cm−1 at room temperature13.
Determination of the conductivity of solid-state electrolytes is complicated in experiments due to the challenges in reproducible synthesis of the materials and the sensitivity of the conductivity on structure. Computational methods provide a resource that can be used to determine conductivity and its dependence on structure and composition of the crystalline materials. In computations, these parameters can be precisely controlled, unlike experimental studies where impurities and defects can be present, which are sensitive to the synthetic conditions and difficult to characterize. In order to avoid difficulties in development of force fields for these systems where charge transfer and polarizability are likely to play a role, ab initio molecule dynamics simulations are attractive and have been widely employed. However, because of the relatively low conductivity of solid-state electrolyte materials (usually lower than 10−3 S cm−1), in most cases it is very computationally expensive, and sometimes impossible, to directly calculate an accurate value for conductivity of the materials at room temperature using ab initio molecular dynamics simulations14,15. One way to solve this problem is to calculate the diffusion coefficient at high temperatures and use the Arrhenius relation to predict a value for ionic diffusion at room temperature14,16. However, the relative errors in the final value of the conductivity is likely to be large because statistical errors in the high-temperature data lead to even larger relative errors in the extrapolated results14 Therefore, alternative computational methods that can give reliable estimates of the diffusion coefficient need to be applied to study these systems. We show that ab initio (AI) nonequilibrium molecular dynamics (NEMD) simulations can be used to this effect. Although AI-NEMD simulations were used to determine the ionic conductivity of LiBH4 in a previous study17, the results in that study were not compared with results from AI equilibrium molecular dynamics (EMD) simulations. Therefore one aim of this work is to demonstrate that AI-NEMD simulations enable reliable estimates of the diffusion coefficients to be obtained for materials with diffusivities that are unable to be directly determined using equilibrium calculations. These results can be used to predict materials worthy of consideration as solid-state electrolytes and to identify reasons for variation in experimental measurements.
Among the all-solid-state electrolytes, sulfide-based electrolytes are one of the most promising candidates due to their moderate electrochemical stability, good mechanical properties, and ionic conductivities that are higher than many other potential solid-state electrolytes18,19,20,21. The Li-argyrodites are a family of sulfide-base electrolytes based on Li7PS6, some of which have relatively high ionic conductivity of 10−5–10−3 S cm−1 at room temperature22. The Li-argyrodites form a high and low-temperature phase and the ionic conductivity is greater in the high-temperature phase. Most of the higher conductivity argyrodite structures, including Li7PS6, are not stable at room temperature. However, it has been shown that by making Li vacancies and incorporating halogens into the structure of Li7PS6, it is possible to form structures with empirical formula Li6PS5X (X = Cl, Br and I) that are stable in the higher conductivity phase at room temperature23,24. Experiments show that Li6PS5X (X = Cl, Br and I) have the same crystallographic structures (space group \(F\bar 43m\)) as Li7PS6 and the ionic conductivity of Li6PS5Cl and Li6PS5Br at room temperature is high enough to be considered for battery technology25,26. In addition, the effects of halide disorder has been investigated24. Li6PS5Cl is reported to have a conductivity of ~10−3 S cm−1 at room temperature and to be electrochemically stable up to 7 V versus Li/Li+26,27. Calculations have suggested that extra halogens and Li-vacancies result in higher conductivities and it has been proposed that Li5PS4Cl2 could be an alternative material, although it has not yet been synthesized28.
Li6PS5Cl is an argyrodite electrolyte for which there has been much experimental and computational research. However, due to various difficulties mentioned above, the diffusion mechanism in this material is not fully understood and the predictions of the conductivity using computational and experimental results vary over orders of magnitude15,16,23,26,27,28,29.
The main aims of this paper are to compare AI-NEMD simulations with standard AI-EMD simulations and show that AI-NEMD methods can be used to determine ionic conductivity in low conductivity materials such as all-solid-state electrolytes. All our simulations use ab initio molecular dynamics simulations, so we drop ‘AI-’ from the acronyms AI-EMD and AI-NEMD from this point on. We firstly consider Li5PS4Cl2 because it has a lithium ion self-diffusion coefficient that is sufficiently high that EMD simulations can readily be used for its calculation. Thus, the ionic conductivity of Li5PS4Cl2 can be determined at different temperatures and using both EMD and NEMD methods. The results are used to demonstrate the accuracy that can be achieved using both methods, and the statistical errors resulting from extrapolation using the Arrhenius equation. The ionic conductivity of Li6PS5Cl at room temperature is then determined using NEMD simulations and the results are compared with other computational and experimental results. This material has a much lower diffusion coefficient than Li5PS4Cl2, and past results determined using EMD simulations have differed by several orders of magnitude. Finally, the methods are used to study Li6PS5Cl with vacancies and defects to help identify the reasons for different experimental reports of the conductivity of Li6PS5Cl16,23,26,27,28,29.
Results
Argyrodite structures
The Li6PS5Cl argyrodite structure is cubic with space group \(F\bar 43m\) (space group number 216)30. A supercell based on 2 unit cells each containing 4(Li6PS5Cl), which has 104 atoms (8 primitive unit cells), was considered for all the calculations on this material. In this work the unit cell lattice parameters were determined by energy minimization and were 10.08 Å × 10.08 Å × 10.08 Å. Figure 1 shows the crystal structure of Li6PS5Cl. In this structure the Li ions occupy 48h Wyckoff positions, and S atoms are distributed on 4a and 4c-sites. Sulfurs in the 4a-sites are bound to the phosphorous atoms (4b-sites) forming PS43- (labelled S1), sulfurs as S2− are in 4c-sites and are surrounded by Li ions (labelled S2). The Cl ions are distributed in 4a-sites as well.
Li is purple, sulfur is yellow, chlorine is green, and phosphorous atoms, which are in the center of the PS43− tetrahedral ion, are light purple54.
The pure and defective structures were formed based on the Li6PS5Cl crystal structure. Details of the defective Li6PS5Cl structures are described below. To model the Li5PS4Cl2 structure, the S2 sulfur ions were replaced by chloride ions, and to keep the structure charge balanced, one of the Li ions surrounding each S2 was removed from the structure28.
Ionic conductivity of Li5PS4Cl2
For Li5PS4Cl2, calculation of the diffusion coefficient was feasible using EMD and NEMD simulations at 300 K, 600 K, 800 K and 1000 K. Therefore, this system provides a sample where the accuracy of the EMD and NEMD methods can be compared, and the direct calculation at 300 K can be compared with the result from extrapolation of high temperature-data using the Arrhenius equation (see Methods).
The EMD simulations at 300 K, 600 K, 800 K and 1000 K were run for 45, 40, 20 and 20 ps, respectively. The results of these EMD simulations were used to obtain the average MSD of the Li ions and results for 10 system replicas at each temperature, and the statistical errors at each temperature were obtained. In each case the trajectories were examined to ensure that the simulation times (ranging from 10 × 45 ps to 10 × 20 ps) were sufficient to observe diffusion of Li ions well away from their initial sites. Figure 2a–c shows the MSD of the Li ions as a function of time at 300, 600 and 800 K for the 10 independent trajectories. For diffusive motion, the MSD increases linearly with time at long times, and the slope is related to the diffusion coefficient through Eq. (7). Figure 2d–f shows the average MSD of the ten replicas including the error bars (one standard error in the mean) from which the self-diffusion coefficient and the corresponding conductivity of the material can be determined with an estimate of the precision of the calculation. Note that although diffusive behavior is observed, the value of the MSD at 35 ps for the simulation at 300 K simulation is only ~6 Å2. This is because the MSD is defined as mean square displacement averaged over all Li ions, and not all the 40 equivalent Li ions diffuse on the timescale of the simulation. This is reflected in the size of the error bars for this sample. The values obtained for the self-diffusion coefficient and conductivity are shown in Table 1.
For solid-state electrolytes that have low conductivity at room temperature (~10−3 S cm−1 or lower) it is computationally expensive to directly calculate a precise value for the conductivity at room temperature using ab initio simulations. To solve this issue it is common to calculate the conductivity of the material at higher temperatures and extrapolate the data to room temperature to give an estimate of the conductivity16,31. An Arrhenius plot of the values of the conductivity calculated from the EMD simulations of the Li ion in Li5PS4Cl2 from the MSDs at different temperatures is shown in Fig. 3 (red data points). Note that plots of the conductivity as a function of temperature in Fig. 3 and subsequent figures show the conductivity multiplied by the temperature versus the reciprocal temperature to enable consistency with Arrhenius behavior to be assessed. Furthermore, to demonstrate how extrapolated results compare with the values that are directly determined, the predicted results obtained from extrapolation of the 600 and 800 K data are shown. Measurements at many temperatures are normally recommended when an Arrhenius extrapolation is required. Certainly more than two points are required to test if Arrhenius behavior is observed. However, if the purpose is not to test for Arrhenius behavior but to obtain precise diffusion coefficients for a material where this is known to be valid, having many measurements at extreme temperatures (10 measurements at two temperatures in this case) is likely to provide lower statistical error in the extrapolation due to the dependence of the error in the slope on the range of the data.
Based on the MSD calculations, Li5PS4Cl2 has an ionic conductivity of 0.35 ± 0.05 S cm−1 at 300 K. Figure 3 shows that by considering the data at 600 and 800 K, the calculated conductivity using extrapolation gives an ionic conductivity between 0.17 and 0.37 S cm−1 at 300 K. This agrees with the directly calculated value. However, even though the statistical errors for the higher temperature results are small compared to the values, the relative error at lower temperatures is large due to the extrapolation, as can be seen from Fig. 3. Including the result at 1000 K in the extrapolation gave a result of between 0.17 and 0.33 S cm−1 at 300 K. Only a small change was observed by adding an extra higher temperature because a large change in temperature is required to obtain a very different value of the reciprocal temperature. Care should be taken that the higher temperature does not result in phase changes or alternative mechanisms of diffusion and consequent non-Arrhenius behavior.
To determine the ionic conductivity of solid-state electrolytes Aeberhard et al.17 used an alternative approach that has been widely applied in classical simulations, but had not been used in ab initio simulations, and is based on NEMD simulations (see Methods). They determined the self-diffusion coefficient of hexagonal LiBH4 at 535 K. In the present work, to show the accuracy of NEMD simulations this method was used to predict the self-diffusion coefficients and conductivities of Li5PS4Cl2 at 300 K, 600 K, 800 K and 1000 K, and the results are compared with the results determined from the EMD MSD calculations.
In order to calculate the ionic conductivities from NEMD simulations, it is necessary to determine the conductivity at several fields to identify the linear response regime (the region where the color current increases from zero at Fc = 0, linearly with the field). The linear response regime cannot be predetermined, and must be tested in each case. To identify the linear regime, at least two points with similar values for the conductivity or the diffusion coefficient are required. At each field in the linear regime, 10 simulations were carried out for 15 ps, 13 ps, 5 ps and 5 ps at 300 K, 600 K, 800 K and 1000 K, respectively. These times were selected to give a total computational effort similar to that required for the EMD simulations. Figure 4a, b shows the time integral of the color current due to a color field of Fc = 0.04 eV Å−1 for Li5PS4Cl2 at 600 K using the methodology described above. Figure 4c shows the time integral of the color current due to color fields of 0.02 and 0.03 eV Å−1 at 300 K. Figure 5 shows the time-averaged color current density of the Li ions as a function of field strength at 300, 600 and 800 K and the linear regime was identified as being between 0 eV Å−1 and ~0.03, 0.04 and 0.02 eV Å−1, respectively.
a Time-integral of the Li ion color current () in Li5PS4Cl2 due to a color field as a function of time for 10 independent simulations at 600 K using NEMD simulations and a color field Fc = 0.04 eV. The averages over 20 independent simulations of the time-integral of the color current of the Li ions as a function of time in Li5PS4Cl2 for a system b at 600 K with a color field Fc = 0.04 eV Å−1 and c at 300 K with color fields of Fc = 0.02 eV Å−1 and Fc = 0.03 eV Å−1. The results of the 20 simulations are shown in Supplementary Fig. 1.
The Arrhenius plot for the conductivities calculated using NEMD simulations at different temperatures is presented in Table 1 and shown by the blue data in Fig. 3. The values obtained by the EMD and NEMD methods agree to within the limits of error (within one standard error of the mean). The conductivity of the material at 300 K is also estimated by extrapolating from higher temperatures. Comparing the red and blue lines in Fig. 3, it is clear that using similar total simulation times for NEMD and EMD calculations at 300, 600 and 800 K, the statistical errors in the NEMD simulation results were almost the same as the statistical errors of the results from the EMD method. This was true for the results obtained for direct measurement at 300 K and from extrapolation of the high temperature results to 300 K. These outcomes are consistent with the fact that for this highly diffusive system, the lithium ions are readily able to move between different regions of the sample in all cases and a field is not required to force the ions from one ‘cage’ to the next.
Collective diffusion coefficient of Li5PS4Cl2
The Nernst-Einstein equation is often used to relate the conductivity to the self-diffusion coefficient. However, if the diffusing atoms or molecules in the studied sample are not moving independently during diffusion then this might not be an adequate approximation and the collective diffusion coefficient should be considered32. The self and collective diffusion coefficients will be the same if the diffusing atoms or molecules move independently of each other, but they will differ otherwise (for example, if they move as a cluster). We therefore used Eq. (8) to calculate the collective diffusion coefficient for Li5PS4Cl2 and compare this to the self-diffusion coefficient to check that this approximation is adequate for the systems we consider. The most diffusive pure system we considered in this manuscript was used for this purpose. It was selected because the statistical error is much larger for the collective diffusion calculations than for the self-diffusion calculations and it would be difficult to draw conclusions if the statistical error is too large.
Figure 6 compares the MSD of the ions and their center of mass for Li5PS4Cl2 at 800 K. Note that the ion MSD was determined from 10 independent runs and the ion center of mass MSD from 30 independent runs (each run for 20 ps), yet the error bars for the ion MSD remain much smaller. This is because each of the ions in the sample could provide an independent contribution to the MSD. It is clear that the MSD calculated in both ways agree to within the limits of error for this material and therefore the self and collective diffusion coefficients will agree. The agreement is consistent with independent behavior of single Li ions in Li5PS4Cl2 during the diffusion process and therefore gives us confidence that for this system the conductivity can be calculated using the self-diffusion coefficient.
Ionic conductivity of Li6PS5Cl
Since simulation times for diffusive motion scale approximately inversely with the diffusion coefficient33, in systems with low conductivity it is expected that EMD simulations would need to be very long to obtain accurate results, and at some stage no movement of ions between regions or cages in the electrolyte will be observed in a feasible time-scale. From the calculations on Li5PS4Cl2, it was found that combining NEMD simulations at high temperatures with extrapolation to low temperatures could give accurate results. Therefore, we propose that this could be a way of extending the range of materials for which the conductivity can be calculated by providing a method when the conductivity is so low that EMD simulations cannot be used. Here we test this proposal by calculating the ionic conductivity of Li6PS5Cl using NEMD simulations.
Both EMD and NEMD simulations were carried out with the aim of calculating the conductivity and understanding the mechanism of diffusion in pure Li6PS5Cl, Li6PS5Cl with S-Cl disorder (S and Cl swapping positions) and Li6PS5Cl with both Li+ vacancies and S-Cl disorder.
We firstly consider pure Li6PS5Cl. There are two distinct types of motion in this system. One where a set of 6 Li ions move in an octahedral region about an S2 sulfur atom and another where the Li ion moves (jumps) between these octahedral regions (or cages). If the timescale for the jumps is longer than the simulation time, then a diffusion coefficient cannot be determined from the simulation. Using EMD simulations of Li6PS5Cl, no jumps between cages were observed in 10 independent trajectories of 100 ps at 300 and 450 K and very few, or no, jumps were observed for the trajectories at 600 K. This suggests a very low diffusion coefficient of the material at 300 K (less than ~10−4 S cm−1) and demonstrates the difficulty of measuring the value of the conductivity through EMD simulations33. However, it was possible to obtain the conductivity values using NEMD simulations at both 600 K and 800 K, where jumps could be observed, and the conductivity at 300 K was estimated using extrapolation of these results, assuming Arrhenius behavior. In Fig. 7, the red unfilled squares show the calculated conductivities at 600 and 800 K (the error bars are smaller than the symbols), and the lines show the bounds of predictions for the conductivity of pure Li6PS5Cl at lower temperatures. As can be seen from Fig. 7, the conductivity of the pure Li6PS5Cl is predicted to be 10−5–10−4 S cm−1. The simulation time required to obtain similar precision for the conductivity of Li6PS5Cl using the EMD method at 600 and 800 K was prohibitive, and we were not even able to estimate a mean and standard error because jumps did not occur. An alternative would be to consider higher temperatures but the extrapolation errors would be greater if the minimum temperature is higher, and it could lead to a disruption of the structure and non-Arrhenius behavior for the diffusion coefficient. Therefore the NEMD approach is more appropriate in this case.
Data for the Li ion conductivity in pure (red squares and lines) and S-Cl disordered (blue squares) Li6PS5Cl from this work. The lines show bounds for the predicted Li ion conductivity in pure (red lines) and S-Cl disordered (blue lines) Li6PS5Cl obtained by extrapolation, assuming Arrhenius behavior for the diffusivity. The other points are computational and experimental results from the literature. The cross (×)16 and the plus (+) sign28 are computational results and filled37 and unfilled37 squares, filled38 and unfilled26 triangles, filled34 and unfilled30 circles and the bold unfilled circle29 are experimental results. For statistical errors in the results (where available), see Table 2.
The Li ion conductivity for pure Li6PS5Cl has previously been determined experimentally29,30,34 and computationally16,28 at 300 K and these results are also shown in Fig. 7 as circles (experimental data) and crosses (computational data). It can be seen there are differences in the orders of magnitude of results at 300 K. Of particular note is that the computational results from the literature for pure Li6PS5Cl at 300 K differ by 5 orders of magnitude and are between one and four orders of magnitude different from the experimental results. The lower value was obtained by extrapolation of data for simulations at 600 K and higher. Therefore it seems that there are no reliable computational estimates of the diffusion coefficient for this system prior to the current work. Our computational prediction is similar to the highest experimental result. The statistical error in the computational results from the previous studies were not reported in most cases, but is expected to be high based on the computational time and supercell sizes considered, and the inherent error propagation when extrapolating the data for materials with low conductivity. It is clear that for this system, the low jump frequency of Li ions in Li6PS5Cl at room temperature (~109 s−1 according to ref. 37) requires extrapolation of the higher temperature to predict the conductivity at lower temperatures and use of NEMD.
The experimental results differ by a factor of two, and it was proposed in the literature that this could be due to the annealing temperature of the samples which causes different degrees of Cl and S disorder35, the level of the crystallinity26,36, existence of extra chlorine in the synthesized structure, Li vacancy in the structure36, and existence of impurities37 of the synthesized samples. The effects of some of these factors are considered in the sections below.
We now consider the effect of disorder in Li6PS5Cl. It has been proposed that the high conductivity of Li6PS5Cl observed in some experiments could be due to disorder of Cl and S atoms30,36,37. To test and understand this, we consider a model of the structure with disorder, based on the experimentally observed structure. In the structure, 25% of the Cl ions that are occupying 4a sites in Li6PS5Cl are exchanged with S2 ions which are occupying 4c sites. Data from EMD simulations were then used to determine the conductivity of the disordered structure at 600 K and 800 K. The results are shown in Fig. 7 as filled blue squares (the error bars are smaller than the symbols). Assuming Arrhenius behavior, the results are extrapolated to lower temperatures as shown by the blue lines in Fig. 7. Experimental results for the conductivity of the disordered structure are shown in Fig. 7 as squares and triangles26,35,37,38 and reported computational values28 are shown as plus signs (+). Considering the error bars, our calculated value for the conductivity of disordered structure agrees with the recent experimental reports of Yu et al.37. According to our results, the conductivity of the disordered structure is approximately two orders of magnitude higher than the pure structure. Therefore it is clear that this apparently small change in the structure which involves swapping 4 of the 104 atoms, results in a very significant change in the conductivity. This indicates that slight defects in the pure crystal could lead to very different experimental conductivities.
The diffusion pathways of the Li ions in the ordered and disordered structures at 600 K were also determined using EMD simulations and are shown in Fig. 8. Comparing the pathways, it is apparent that introducing disorder by swapping the positions of Cl and S ions significantly changes the motion of the Li ions. As seen in Fig. 8a, b, in the pure systems Li ions move inside the octahedral cages formed by the PS43− (see Fig. 1) and the absence of pathways between the cages indicate that the energy barrier for diffusion out of the cages is high compared to the thermal energy available, and consequently the ionic conductivity of the pure crystal is too low to be determined from these EMD simulations. However, in the disordered structure a channel between the cages is evident in the right half of the structure (where the ions are swapped) in Fig. 8c, d. This indicates that in the direction of the new channel, the barrier energy for Li ion diffusion to the other cages is much smaller than it was in the pure structure and Li ions move in the disordered part of the structure relatively easily. The presence of a channel with a lower energy barrier explains the increase in the ionic conductivity of the disordered Li6PS5Cl. Also, variation in the concentration of S2-Cl disorder and dispersion of the disordered sites could explain the different experimentally reported conductivities.
Different views of the Li ion trajectories are shown in a, b for pure and c, d for S-Cl disordered Li6PS5Cl at 600 K monitored for 50 ps. The violet, yellow, green and light purple atoms are lithium, sulfur, chlorine and phosphorus, respectively. The small violet dots show the diffusion pathways of the lithium ions. The boxes show one simulation supercell.
It has been proposed that Li vacancies can be present in samples of Li6PS5Cl which would be expected to increase their Li ion conductivity36. In a study considering this36, the experimentally synthesized sample was suggested to have experimental formula Li5.6PS4.8Cl1.2 after annealing. We note that the charges are not balanced in the proposed empirical formula, Li5.6PS4.8Cl1.2. However, a similar formula with charge balance is Li5.8PS4.8Cl1.2. To study the effect of the combination of a Li-vacancy, extra Cl ions and fewer S2 ions35 on the ion conductivity of the Li6PS5Cl, we remove two Li ions from the Li6PS5Cl supercell (8 unit cells) and replace two S2 ions with two Cl ions39 giving a new structure of Li5.75PS4.75Cl1.25, which is similar to the empirical formula given in the literature (Li5.8PS4.8Cl1.2). The ionic conductivity of this structure at 300 K was calculated to be 0.09 ± 0.03 S cm−1, which is several magnitudes higher than the pristine Li6PS5Cl solid electrolyte (6 × 10−5–3 × 10−4 S cm−1) and higher than the estimated value for Li6PS5Cl with disorder of the S2 and Cl atoms only (6 × 10−3–1 × 10−1 S cm−1). The estimated value for the ionic conductivity is also higher than that reported in ref. 36 (1.1 × 10−3 S cm−1), but the sensitivity to vacancies and disorder means that these would not be expected to agree due to the difference in empirical formulas. Clearly, Li vacancies and substitution of an S ion with a Cl ion significantly increase the diffusion in the structure. This increase is expected because the Li vacancies and the smaller size of the Cl ions and the S2 ions will provide more space movement of the Li ions, and the disorder introduced by the replacement of the S2 ions with Cl ions will facilitate diffusion as discussed above (see Supplementary Fig. 2 for the diffusion pathways in Li5.75PS4.75Cl1.25 at 450 K).
Table 2 presents a summary of conductivities of the different type Li6PS5Cl structures (pure, disordered and structures having both disorder and Li vacancies) from experimental and computational reports. Based on the results from our calculations and previously reports16,23,26,28,29,30,36, it can be concluded that the conductivity of pure Li6PS5Cl is relatively low (10−5–10−4 S cm−1). However, impurities like Li-vacancies, grain boundaries, and ion disorder introduced during their synthesis would affect the final conductivity of the synthesized argyrodite electrolyte.
Discussion
In this paper, the diffusion mechanism of Li ions in Li6PS5Cl and Li5PS4Cl2 and the diffusion coefficients/conductivity were studied in detail. Comparison of the EMD and NEMD methods show that both methods can be used to predict the ionic diffusion of these materials when their ionic conductivity is around 10−3–10−2 S cm−1. If these materials have much lower ionic conductivity (e.g., at lower temperatures), the EMD simulation times required to get precise and reproducible results are not currently feasible. However, we show that it is feasible to use NEMD to determine diffusion coefficients of solid-state electrolytes with conductivities of around 10−6–10−4 S cm−1.
Agreement of the results from these methods showed that they are both able to provide reliable estimates of conductivity when the conductivity is sufficiently high. However, for solid-state electrolyte with low conductivity, which are common at temperatures closer to room temperature, it is necessary to use NEMD simulations. The advantage of NEMD over EMD calculations increases as the diffusivity decreases. This is because the time required to explore a material in equilibrium simulations is inversely proportional to the diffusion coefficient33 whereas the applied field will also contribute to this in NEMD simulations.
We note, that if the diffusion is not isotropic it will be necessary to carry out several NEMD simulations with fields in different directions in order to obtain the diffusion coefficients. Therefore the efficiency of the NEMD calculations would be reduced in this case. However, it will still be advantageous, or necessary, at sufficiently low fields.
We also studied the conductivity of Li5PS4Cl2 and Li6PS5Cl in detail and the effect of disorder and defects on diffusion of the Li ions in Li6PS5Cl. Based on the results from our calculations, Li5PS4Cl2 is predicted to be a highly conductive solid electrolyte although it has not yet been synthesized. For Li6PS5Cl, although the pure material has a relatively low ion conductivity (6 × 10−5–3 × 10−4 S cm−1 at 300 K) we confirmed that by increasing Li vacancies of the structure or introducing disorder in the ionic positions of the Cl and S ions, it is possible to enhance the ion conductivity of this structure. Although these systems had been studied previously, the size of the error bars made it difficult to ascertain the effects. It can be concluded that the higher experimentally reported conductivity of Li6PS5Cl could be due to combinations of Li ion vacancies and Cl-S ion disorder or maybe higher concentration of halogen (Cl) after annealing. We note that our computational results either predict conductivities that are higher than the experimental results, or on the high end of the range of experimental results. There are some systematic errors in the computations that might contribute to this including the system size that can be modelled, the level of theory used in the ab initio molecular dynamics simulations and changes in the lattice parameters during diffusion which is carried out at under constant volume conditions. However, the presence of grain boundaries, impurities, disorder and the inhomogeneous distribution of disordered sites in the experimental samples could also explain the differences between the experimental and computational results. Importantly, the computational results are reproducible and the trends due to changes in the structure indicate ways in which a material can be tuned to increase the conductivity which is crucial for the improvement of solid-state-electrolytes.
Methods
Ab initio molecular dynamics simulations
Ab initio Born-Oppenheimer molecular dynamics simulations were performed using the CP2K/Quickstep package40,41 and a modified version of this that incorporated the NEMD algorithm discussed below. The Perdew-Burke-Ernzerhof (PBE) generalized gradient approximation (GGA)42 was selected for the DFT exchange-correlation functional. To correct for van der Waals interactions the DFT-D343 method was used. Pseudopotentials of Goedecker, Teter and Hutter (GTH) were employed44 The DZVP-MOLOPT-SR-GTH45 basis set was selected because it is optimized for calculating molecular properties in gas and condensed phases. This is a Gaussian and plane-wave (GPW) basis46 and a cutoff energy of 280 Ry was selected. A 1 × 1 × 1 k-point mesh (Γ point) was used in all calculations and preliminary optimization calculations indicated that using grid introduced errors of less than 0.01 Å for lattice parameters and errors of less than 0.06 eV for the energy per unit cell. The optimized lattice constants (10.08 Å) are 2.5% larger than the experimentally reported value for Li6PS5Cl, and similar to results reported in earlier computational work16,28.
Equilibrium and nonequilibrium equations of motion
Both EMD and NEMD simulations were used to calculate the diffusion coefficients of the materials in the NVT ensemble. The equations of motion for the EMD simulations are:
where qi is the position, pi is the momentum and mi is mass of atom i, Fi is the interatomic force on atom i and α couples the atoms to the Nosé-Hoover thermostat. A chain thermostat with the chain number of 3 (the default for CP2K) was applied for the EMD calculations:
In the above equations Q, Q1 and Q2 are the friction coefficients which were all given equal values of 3 in the equilibrium simulations, kB is Boltzmann’s constant, T is the target temperature and g is the number of degrees of freedom of the system.
The nonequilibrium method used to determine the diffusion coefficients is the color diffusion algorithm (for Li-ions) which has been widely applied in classical molecular dynamics simulations47,48,49,50. Using this algorithm, the equations of motion for the atoms or ions are given by Eqs. (1) and (2), except for the Li ions where the equation of motion for the momentum Eq. (2) is modified to include a force due to a color field, Fc:
Here ci is the color charge (or color label) of each of the Li ions. The sum of the color charge should be zero to ensure there is no drift in the total moment of the system, however the choice of these charges is arbitrary. Usually, half of the Li ions are given a positive color charge (+1) and the other half a negative color charge (−1). The color field does not affect the PS43−, S2− and Cl− ions and the color charges do not affect the way Li+ ions interact with each other—it just determines their response to the field. For NEMD calculations a chain thermostat was not used as it is inappropriate for the nonequilibrium simulations51. The equation of motion for the thermostat for nonequilibrium study is therefore given by Eq. (3) where α2 is equal to zero. For calculations of properties of nonequilibrium systems, the thermostat needs to be applied to the peculiar momentum of the conductive ions. However, because we are extrapolating to zero field, this is not problematic and it is appropriate to use Eq. (6). The color field forces the Li ions to move in response to the field, but as mentioned above, it does not change the interatomic interactions (the electric charge on the Li ions is maintained as +1 and contributes to the Coulomb interactions between atoms that is part of Fi). With a color field applied, Li ions with opposite color charges will experience forces that tend to move them in opposite directions through the diffusion channel. The color field should be strong enough to generate a color current and low enough that the color field’s response (color current) to be in the linear regime. The result, on average, will be a color current in the direction of the field. We note that the total momentum of the system is initially zero, and the equations of motion and selection of charges ensure that this is maintained at all times so that the center of mass of the system does not drift.
The EMD and NEMD equations of motions were integrated using the velocity Verlet algorithm with a time step of 1 fs. Where statistical errors are reported, they are one standard error in the mean (the standard deviation of multiple runs, divided by the square root of the sample size).
Calculation of diffusion coefficients and conductivity
The mean square displacement (MSD) of Li ions was used to calculate the diffusion coefficient from EMD simulations. The self-diffusion coefficient is given by the Einstein relation:
where Ds is self-diffusion coefficient, ∆ri(t) is displacement of the ith of N Li ions over a period, t, and \(\left\langle ... \right\rangle\) indicates an ensemble average. The collective diffusion coefficient Dc (or Li center of mass diffusion coefficient) is given by:
where ri(t) is the position of the ith Li ion at time t. The self- and collective diffusion coefficients differ if the ions do not move independently. The conductivity experimentally measured from the application of an electric potential will correspond to the collective diffusion coefficient whereas nuclear magnetic resonance experiments give the self-diffusion coefficient. We note that the statistical error in the computations of the self-diffusion coefficient will be lower than the collective diffusion, so if they are expected to have similar values, it is advantageous to consider the self-diffusion coefficient.
From the self-diffusion coefficient, the ionic conductivity of the material, σ, can be calculated using the Nernst–Einstein equation50:
where n is the ion density of Li, e is the elementary electron charge and Z the valence of Li.
Using the NEMD simulations, the self-diffusion coefficient can be determined from the color current produced by the color field. As noted above, this method has previously been used to determine the self-diffusion coefficient of a solid-state electrolyte with low conductivity17. The color current is given by:
where vi is the velocity of ith Li ion. At low fields, the color current in the direction of the field (\(J_c = {\mathbf{J}}_c \cdot {\mathbf{F}}_c/\left| {{\mathbf{F}}_c} \right|\)) will be linearly proportional to the field, \(F_{\mathrm{c}} = \left| {{\mathbf{F}}_{\mathrm{c}}} \right|\), when the systems is in a steady state, and then for the color charges used in this work:
where N is the number of lithium ions subject to a color field. If a different selection of color charges was used, N in Eq. (11) should be replaced with \(\mathop {\sum}\nolimits_i^N {c_i^2}\). The value of the field below which there is a linear relationship between the color current and applied field will depend on the system and conditions such as temperature. Therefore to use this expression in practice, simulations need to be carried out to determine that critical field. Furthermore, although the color current changes with the color field, in the linear regime the statistical error in the color current does not change. Therefore, to obtain results with the lowest statistical error it is best to use the maximum field for which linear response occurs. For ergodic systems, the ensemble average of the color current in Eq. (11) can be replaced with a time-average, giving:
So if the field is in the x-direction, the self-diffusion coefficient can also be written as:
The field adds a force to the particles in the direction of the field, and has a similar effect to reducing the activation energy barrier for diffusion52. If the diffusion process can be modelled as a jump process, the expected time for a single jump will increase exponentially with the size of the activation barrier, and therefore application of the field will allow systems with much lower diffusion coefficients to be considered for a given simulation time. In practice, this means that greater advantage for NEMD calculations is expected for systems where the diffusion coefficient is low.
Due to the dependence of the ionic conductivity of solid-state electrolytes on temperature, high-temperature ionic conductivities determined from MD simulations can be used to estimate the diffusion coefficients of the electrolytes at lower temperatures using the Arrhenius relationship:
where Ea is the activation energy and D0 is the diffusion pre‐exponential factor. Using Eq. (9) this can also be written in terms of the ionic conductivity of the system,
Note that for our system where only the Li ions are mobile and move independently, the conductivity determined from the Einstein relationship for the self-diffusion, Eq. (7), can also be expressed as a Green-Kubo relationship,
Furthermore, if the assumption of independency of movement of the Li ions is relaxed, then it can be calculated from the collective diffusion coefficient and the Green-Kubo relationship is,
We choose to use the Einstein expressions in this work, which circumvents problems associated with convergence of the time correlation functions in (16) and (17). Of relevance given that this study considers ab initio molecular dynamics simulations of conductivity, it has interestingly been demonstrated that Green-Kubo expression gives the same results using integer charges and velocities of discrete sites (similar to this work), and the mean square dipole displacement obtained using Born charges of each atom53.
Data availability
The data that support the findings within this paper are available from the corresponding authors upon reasonable request.
Code availability
The modified CP2K code within this paper are available from the corresponding authors upon reasonable request.
References
Blomgren, G. E. The development and future of lithium ion batteries. J. Electrochem. Soc. 164, A5019–A5025 (2017).
Chen, W. et al. Designing safe electrolyte systems for a high-stability lithium–sulfur battery. Adv. Energy Mater. 8, 1702348 (2018).
Li, M., Lu, J., Chen, Z. & Amine, K. 30 years of lithium-ion batteries. Adv. Mater. 30, e1800561 (2018).
Nishi, Y. Lithium ion secondary batteries; past 10 years and the future. J. Power Sources 100, 101–106 (2001).
Armand, M. & Tarascon, J. M. Building better batteries. Nature 451, 652–657 (2008).
Li, W., Dahn, J. R. & Wainwright, D. S. Rechargeable lithium batteries with aqueous electrolytes. Science 264, 1115–1118 (1994).
Owens, B. B. & Skarstad, P. M. Ambient temperature solid state batteries. Solid State Ion. 53-56, 665–672 (1992).
Xiayin, Y. et al. All-solid-state lithium batteries with inorganic solid electrolytes: review of fundamental science. Chin. Phys. B 25, 018802 (2016).
Takada, K. Progress and prospective of solid-state lithium batteries. Acta Mater. 61, 759–770 (2013).
Tatsumisago, M. & Hayashi, A. Sulfide glass-ceramic electrolytes for all-solid-state lithium and sodium batteries. Int. J. Appl. Glass Sci. 5, 226–235 (2014).
Kim, J. G. et al. A review of lithium and non-lithium based solid state batteries. J. Power Sources 282, 299–322 (2015).
Chen, C. H. et al. Stable lithium-ion conducting perovskite lithium–strontium–tantalum–zirconium–oxide system. Solid State Ion. 167, 263–272 (2004).
Manthiram, A., Yu, X. & Wang, S. Lithium battery chemistries enabled by solid-state electrolytes. Nat. Rev. Mater. 2, 16103 (2017).
He, X., Zhu, Y., Epstein, A. & Mo, Y. Statistical variances of diffusional properties from ab initio molecular dynamics simulations. npj Comput. Mater. 4, 18 (2018).
Baktash, A., Reid, J. C., Yuan, Q., Roman, T. & Searles, D. J. Shaping the future of solid-state electrolytes through computational modeling. Adv. Mater. 32, 1908041 (2020).
Deng, Z., Zhu, Z., Chu, I.-H. & Ong, S. P. Data-driven first-principles methods for the study and design of alkali superionic conductors. Chem. Mater. 29, 281–288 (2017).
Aeberhard, P. C., Williams, S. R., Evans, D. J., Refson, K. & David, W. I. F. Ab initio nonequilibrium molecular dynamics in the solid superionic conductor LiBH4. Phys. Rev. Lett. 108, 095901 (2012).
Sun, X. et al. Preparation, characterization and ionic conductivity studies of composite sulfide solid electrolyte. J. Alloy. Compd. 727, 1136–1141 (2017).
Park, K. H. et al. Solution-processable glass LiI-Li4SnS4 superionic conductors for all-solid-state Li-ion batteries. Adv. Mater. 28, 1874–1883 (2016).
Wu, X., Kazzi, M. E. & Villevieille, C. Surface and morphological investigation of the electrode/electrolyte properties in an all-solid-state battery using a Li2S-P2S5 solid electrolyte. J. Electroceram. 38, 207–214 (2017).
Xu, R. C. et al. Rational coating of Li7P3S11 solid electrolyte on MoS2 electrode for all-solid-state lithium ion batteries. J. Power Sources 374, 107–112 (2018).
Wang, Z. & Shao, G. Theoretical design of solid electrolytes with superb ionic conductivity: alloying effect on Li+ transportation in cubic Li6PA5X chalcogenides. J. Mater. Chem. A 5, 21846–21857 (2017).
Deiseroth, H.-J. et al. Li7PS6 and Li6PS5X (X: Cl, Br, I): possible three-dimensional diffusion pathways for lithium ions and temperature dependence of the ionic conductivity by impedance measurements. Z. Anorg. Allg. Chem. 637, 1287–1294 (2011).
Kraft, M. A. et al. Influence of lattice polarizability on the ionic conductivity in the lithium superionic argyrodites Li6PS5X (X = Cl, Br, I). J. Am. Chem. Soc. 139, 10909–10918 (2017).
Epp, V., Gün, Ö., Deiseroth, H.-J. & Wilkening, M. Highly mobile ions: low-temperature NMR directly probes extremely fast Li+ hopping in argyrodite-type Li6PS5Br. J. Phys. Chem. Lett. 4, 2118–2123 (2013).
Rao, R. P., Sharma, N., Peterson, V. K. & Adams, S. Formation and conductivity studies of lithium argyrodite solid electrolytes using in-situ neutron diffraction. Solid State Ion. 230, 72–76 (2013).
Boulineau, S., Courty, M., Tarascon, J.-M. & Viallet, V. Mechanochemical synthesis of Li-argyrodite Li6PS5X (X = Cl, Br, I) as sulfur-based solid electrolytes for all solid state batteries application. Solid State Ion. 221, 1–5 (2012).
de Klerk, N. J. J., Rosłoń, I. & Wagemaker, M. Diffusion mechanism of Li argyrodite solid electrolytes for Li-ion batteries and prediction of optimized halogen doping: the effect of Li vacancies, halogens, and halogen disorder. Chem. Mater. 28, 7955–7963 (2016).
Yubuchi, S. et al. Preparation of high lithium-ion conducting Li6PS5Cl solid electrolyte from ethanol solution for all-solid-state lithium batteries. J. Power Sources 293, 941–945 (2015).
Rayavarapu, P. R., Sharma, N., Peterson, V. K. & Adams, S. Variation in structure and Li+-ion migration in argyrodite-type Li6PS5X (X = Cl, Br, I) solid electrolytes. J. Solid State Chem. 16, 1807–1813 (2012).
Zhu, Z., Chu, I.-H., Deng, Z. & Ong, S. P. Role of Na+ interstitials and dopants in enhancing the Na+ conductivity of the cubic Na3PS4 superionic conductor. Chem. Mater. 27, 8318–8325 (2015).
Marcolongo, A. & Marzari, N. Ionic correlations and failure of Nernst-Einstein relation in solid-state electrolytes. Phys. Rev. Mater. 1, 025402 (2017).
Keil, F. J., Krishna, R. & Coppens, M.-O. Modeling of diffusion in zeolites. Rev. Chem. Eng. 16, 71–197 (2000).
Rosero-Navarro, N. C., Miura, A. & Tadanaga, K. Preparation of lithium ion conductive Li6PS5Cl solid electrolyte from solution for the fabrication of composite cathode of all-solid-state lithium battery. J. Sol. Gel Sci. Technol. 89, 303–309 (2019).
Rao, R. P. & Adams, S. Studies of lithium argyrodite solid electrolytes for all-solid-state batteries. Phys. Status Solidi A 208, 1804–1807 (2011).
Yu, C., van Eijck, L., Ganapathy, S. & Wagemaker, M. Synthesis, structure and electrochemical performance of the argyrodite Li6PS5Cl solid electrolyte for Li-ion solid state batteries. Electrochim. Acta 215, 93–99 (2016).
Yu, C. et al. Facile synthesis toward the optimal structure-conductivity characteristics of the argyrodite Li6PS5Cl solid-state electrolyte. ACS Appl. Mater. Interfaces 10, 33296–33306 (2018).
Wang, S. et al. High-conductivity argyrodite Li6PS5Cl solid electrolytes prepared via optimized sintering processes for all-solid-state lithium–sulfur batteries. ACS Appl. Mater. Interfaces 10, 42279–42285 (2018).
Deiseroth, H.-J. et al. Li6PS5X: a class of crystalline Li-rich solids with an unusually high Li+ mobility. Angew. Chem. 47, 755–758 (2008).
Hutter, J., Iannuzzi, M., Schiffmann, F. & VandeVondele, J. CP2K: atomistic simulations of condensed matter systems. Wiley Interdiscip. Rev. Comput. Mol. Sci. 4, 15–25 (2014).
VandeVondele, J. et al. QUICKSTEP: Fast and accurate density functional calculations using a mixed Gaussian and plane waves approach. Comput. Phys. Commun. 167, 103–128 (2005).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Grimme, S., Antony, J., Ehrlich, S. & Krieg, H. A consistent and accurate ab initio parametrization of density functional dispersion correction (DFT-D) for the 94 elements H-Pu. J. Chem. Phys. 132, 154104 (2010).
Goedecker, S., Teter, M. & Hutter, J. Separable dual-space Gaussian pseudopotentials. Phys. Rev. B 54, 1703–1710 (1996).
VandeVondele, J. & Hutter, J. Gaussian basis sets for accurate calculations on molecular systems in gas and condensed phases. J. Chem. Phys. 127, 114105 (2007).
Lippert, B. G., Parrinello, J. H. & Michele A hybrid Gaussian and plane wave density functional scheme. Mol. Phys. 92, 477–488 (1997).
Evans, D. J. & Morriss, O. P. Non-Newtonian molecular dynamics. Computer Phys. Rep. 1, 297–343 (1984).
Arya, G., Chang, H.-C. & Maginn, E. J. A critical comparison of equilibrium, non-equilibrium and boundary-driven molecular dynamics techniques for studying transport in microporous materials. J. Chem. Phys. 115, 8112–8124 (2001).
Wheeler, D. R. & Newman, J. Molecular dynamics simulations of multicomponent diffusion. 2. Nonequilibrium method. J. Phys. Chem. B 108, 18362–18367 (2004).
Evans, D. J. & Morriss, G. P. Statistical Mechanics of Nonequilibrium Liquids. 2 edn, (ANU E Press, 2007).
Brańka, A. C. Nosé-Hoover chain method for nonequilibrium molecular dynamics simulation. Phys. Rev. E 61, 4769–4773 (2000).
Beedle, A. E. M. et al. Forcing the reversibility of a mechanochemical reaction. Nat. Commun. 9, 3155 (2018).
Grasselli, F. & Baroni, S. Topological quantization and gauge invariance of charge transport in liquid insulators. Nat. Phys. 15, 967–972 (2019).
Momma, K. & Izumi, F. VESTA 3 for three-dimensional visualization of crystal, volumetric and morphology data. J. Appl. Crystallogr. 44, 1272–1276 (2011).
Acknowledgements
D.J.S. thanks the Australian Research Council for support of this project through the LIEF and Discovery programs (LE0882357, LE160100051 and DP140100193). A.B. acknowledges support from the Australian Government through an Australian Government Research Training Program Scholarship (RTP). All authors thank Dr Qinghong Yuan for her comments and helpful discussions. We acknowledge access to computational resources at the NCI National Facility through the National Computational Merit Allocation Scheme supported by the Australian Government. This work was also supported by resources provided by the Pawsey Supercomputing Centre with funding from the Australian Government and the Government of Western Australia. We also acknowledge support from the Queensland Cyber Infrastructure Foundation (QCIF) and the University of Queensland Research Computing Centre.
Author information
Authors and Affiliations
Contributions
A.B. performed the calculations and wrote the paper. J.C.R. and D.J.S. extended the simulation code. All authors analyzed the results and revised the paper.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Baktash, A., Reid, J.C., Roman, T. et al. Diffusion of lithium ions in Lithium-argyrodite solid-state electrolytes. npj Comput Mater 6, 162 (2020). https://doi.org/10.1038/s41524-020-00432-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41524-020-00432-1
- Springer Nature Limited
This article is cited by
-
High-throughput investigation of stability and Li diffusion of doped solid electrolytes via neural network potential without configurational knowledge
Scientific Reports (2024)
-
Material design modelling for optimisation of lithium battery fast charging
Journal of Solid State Electrochemistry (2024)
-
Nonequilibrium molecular dynamics for accelerated computation of ion–ion correlated conductivity beyond Nernst–Einstein limitation
npj Computational Materials (2023)
-
Interfaces in Sulfide Solid Electrolyte-Based All-Solid-State Lithium Batteries: Characterization, Mechanism and Strategy
Electrochemical Energy Reviews (2023)
-
Ab initio Interfacial Chemical Stability of Argyrodite Sulfide Electrolytes and Layered-Structure Cathodes in Solid-State Lithium Batteries
JOM (2022)