Abstract
The synthesis of supramolecular polymers with controlled architecture is a grand challenge in supramolecular chemistry. Although living supramolecular polymerization via primary nucleation has been extensively studied for controlling the supramolecular polymerization of small molecules, the resulting supramolecular polymers have typically exhibited one-dimensional morphology. In this report, we present the synthesis of intriguing supramolecular polymer architectures through a secondary nucleation event, a mechanism well-established in protein aggregation and the crystallization of small molecules. To achieve this, we choose perylene diimide with 2-ethylhexyl chains at the imide position as they are capable of forming dormant monomers in solution. Activating these dormant monomers via mechanical stimuli and hetero-seeding using propoxyethyl perylene diimide seeds, secondary nucleation event takes over, leading to the formation of three-dimensional spherical spherulites and scarf-like supramolecular polymer heterostructures, respectively. Therefore, the results presented in this study propose a simple molecular design for synthesizing well-defined supramolecular polymer architectures via secondary nucleation.
Similar content being viewed by others
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Introduction
In recent years, living supramolecular polymerization (LSP) has emerged as a promising tool for synthesizing complex supramolecular homo- and heterostructures, offering meticulous control over their shapes and dimensions1,2,3,4. The pioneering work in this field began with the research groups led by Winnik and Manners et al., who first reported the living crystallization-driven self-assembly (LCDSA)5. They used poly(ferrocenyldimethylsilane) cored block copolymers to synthesize various supramolecular nanoarchitectures such as one-dimensional (1D) cylinders6,7,8, 2D platelets9,10, dendritic micelles11,12, rod-coil micelles13, and 3D spherulites14,15 with excellent precision to name a few. Despite the significant progress in the supramolecular polymerization of small molecules, realizing LSP was challenging as no rational design principles were available to create dormant monomers or aggregates. To this end, Sugiyasu et al. demonstrated LSP in small molecules using hydrogen-bonded (H-bonded) porphyrins, which form metastable J-aggregates16. Shortly after, Aida et al. also achieved kinetically trapped monomers using H-bonded corannulenes via intramolecular H-bonding17. Both these trapped states are activated using thermodynamically stable SPs as seeds to form SPs with controlled lengths. These inspiring outcomes further led to synthesizing block SPs with controlled sequences18,19,20,21,22,23.
Over the past few years, a few researchers have reported the phenomenon of molecular self-assembly operating at higher hierarchical levels, thereby modulating the topology of functional SPs through a secondary nucleation mechanism24,25,26,27,28,29. While this phenomenon has been comprehensively studied theoretically and experimentally in the context of amyloid self-assembly30,31,32,33, it remains a relatively unexplored frontier within the domain of functional SPs. Recently, Yagai et al. have reported the creation of molecularly interlocked nanostructures with a remarkably high level of organization through the utilization of a secondary nucleation strategy28. Similarly, Sugiyasu et al. have described the formation of double-stranded Archimedean spirals through a secondary nucleation event25. George et al. have recently reported the emergence of secondary nucleation-mediated surface-anchored self-sorted SPs, secondary SPs, and the production of seed-induced, non-covalently cross-linked hydrogels24,27,29. Despite these interesting results, achieving fine control over the topology of functional SPs requires a much-needed understanding of the molecular structure, kinetics, and underlying mechanisms that govern secondary nucleation.
Currently, LSP and secondary nucleation pathways are explored in small molecule-based H-bonded π-systems mainly because of two reasons: (i) growth via the nucleation-elongation process and (ii) the ease of achieving kinetically trapped monomers/aggregates16,17,34,35,36,37,38,39,40,41,42,43. However, H-bonding interactions typically result in 1D morphology owing to the strong directionality of H-bonding functional groups34,35,36,37,38,39. Hence, the synthesis of complex supramolecular architectures using H-bonded π-systems is limited to a few sets of molecules25,28,44,45. On the other hand, Che et al. demonstrated LSP using non-H-bonded π-systems by activating their off-pathway aggregates via homo and hetero-seeding methods leading to the synthesis of interesting homo and block supramolecular architectures46,47,48. However, rational molecular design principles to realize LSP and secondary nucleation in other types of π-systems that form SPs without the aid from H-bonding interactions need to be formulated for further exploration. In this context, we have recently reported that non-H-bonded simple π-systems such as alkyl perylene diimides (PDIs) show cooperative supramolecular polymerization guided solely by dispersive interactions with cooperative factors on par with H-bonded π-systems49. Hence, exploring alkyl PDIs to realize LSP and secondary nucleation pathways can broaden the scope of small molecules and expand the non-covalent synthesis toolbox to create complex supramolecular architectures. However, the generation of dormant monomers or off-pathway aggregates from alkyl PDIs must be addressed.
Here, we present a noticeable improvement in the field of SPs by expanding the structural diversity of monomers that display LSP and secondary nucleation to synthesize SPs with interesting topologies. For this purpose, we have selected a simple π-system, PDI substituted with 2-ethylhexyl side chains (2EH-PDI), as it is known to form SPs via nucleation-elongation mechanism (Fig. 1a)49. Despite the lack of any H-bonding functional groups, 2EH-PDI forms dormant monomers in solution from the monomeric states upon rapid cooling due to the existence of multiple conformations at high temperatures. By optimizing the solvent conditions, we successfully stabilized the 2EH-PDI molecules as dormant monomers in solution at room temperature (Fig. 1b). Next, these dormant monomers were converted into complex supramolecular architectures via seed-induced LSP and secondary nucleation. To accomplish this, we have employed three distinct seeding methods: (i) homo-seeding, (ii) shear forces, and (iii) hetero-seeding (Fig. 1b, c). By adding various mol% of prefabricated 2EH-PDI SP seeds (homo-seeding), we could synthesize 1D SPs with controlled lengths, with the primary nucleation-elongation event taking precedence. Interestingly, when we mechanically agitated the dormant 2EH-PDI monomers via shear forces (stirring or pipetting) in a controlled manner, inducing seed formation within the solution, we observed the formation of SPs with 3D spherical spherulite architectures50, where the secondary nucleation-elongation promoted the growth of SPs around the seed. While stir-induced secondary nucleation is commonly observed in amyloid systems51 and the crystallization of inorganic crystals52,53, it is a relatively rare phenomenon in functional SPs. Similarly, for hetero-seeding experiments, we have utilized 2D platelets formed by PDI substituted with propoxyethyl chains (PE-PDI) (Fig. 1a). In this case, the secondary nucleation event promotes the growth of 1D SPs of 2EH-PDI above and below the surface of 2D platelets of PE-PDI across their length, resulting in scarf-like SP heterostructures (Fig. 1c). Such a controlled fabrication of SP architectures using simple π-systems via secondary nucleation at an elevated hierarchical level represents an important achievement. Moreover, we also provided the direct visualization of the formation of SP heterostructures in solution using optical microscopy.
a Chemical structures of 2EH-PDI and PE-PDI. b Schematic representation of the formation of dormant monomers by 2EH-PDI and their transformation to thermodynamically stable supramolecular polymers (SPs) via seeded living supramolecular polymerization. c Schematic representation providing an overview of three non-covalent synthesis approaches, demonstrating how the activation of dormant monomers of 2EH-PDI leads to the formation of 1D SPs via homo-seeding, 3D spherical spherulites via shear forces and scarf-like SP heterostructures via hetero-seeding.
Results
Formation of dormant monomers
Previously, we reported that 2EH-PDI forms SPs in methylcyclohexane (MCH) and dimethyl sulfoxide (DMSO) via a cooperative mechanism49. 2EH-PDI (50 μM) is molecularly soluble in chlorinated solvents such as chloroform (CHCl3) and dichloroethane (DCE), as evidenced by UV-vis absorption spectra which shows characteristic monomeric peaks at 490 nm and 515 nm (Supplementary Fig. 1). In MCH, 2EH-PDI (50 μM) forms SPs, as evidenced by relatively broad absorption spectra and a new redshifted band at 575 nm (Supplementary Fig. 1). These SPs could be reversibly transformed into monomers at high temperatures (~363 K), as evident from the UV-vis spectra (Supplementary Fig. 2a). We have studied the supramolecular polymerization and depolymerization process of 2EH-PDI by monitoring its degree of polymerization (α) at 515 nm, (α @ 515 nm). Above the elongation temperatures (Te), α is zero as 2EH-PDI (50 μM) exists as monomers (Supplementary Fig. 2b). Interestingly, thermal hysteresis was observed in MCH during the supramolecular polymerization and depolymerization process. While heating (SPs → monomers), Te of 2EH-PDI (50 μM) was observed at 353 K. However, in the cooling process (monomers → SPs), the critical elongation temperature (Te‘) was reduced to 330 K (Supplementary Fig. 2b). These results revealed the presence of pathway complexity, where the 2EH-PDI monomers get trapped in a higher energy metastable state upon cooling the solution from monomers to form SPs (Figs. 1b and 2a). Probing the absorbance (A) at 515 nm (A @ 515 nm) indicates that by increasing the percentage of good solvent, such as DCE, the temperature region of the hysteresis loop enhanced (Fig. 2b and Supplementary Figs. 3–6). Monomers of 2EH-PDI have a higher absorbance at 515 nm than its SPs. Hence, the decrease in the absorbance at 515 nm is an indication of supramolecular polymerization of 2EH-PDI (Fig. 2b and Supplementary Figs. 3–6)49. At 10 vol% of DCE in MCH (MCH*), we obtained the kinetically trapped monomeric state (dormant monomer) at room temperature (Fig. 2 and Supplementary Fig. 6). Here, the cooling rate also dictates the stability of the dormant monomer. In MCH*, the dormant monomer of 2EH-PDI obtained by the cooling at a rate of 10 K min−1 is more stable (~ 25–30 min) at 303 K than cooling rates of 1, 3, and 5 K min−1 (Fig. 2a, c).
a Synthesis of dormant monomers of 2EH-PDI. Heating the supramolecular polymers (SPs) formed at 303 K to 353 K leads to the formation of monomers in MCH*. Later, by rapid cooling (10 K/min.) to 303 K led to the formation of dormant monomers. When these dormant monomers were left undisturbed at 303 K, SPs were formed over a period of 90 min. b Temperature-dependent UV-vis absorption variation of 2EH-PDI monitored at monomer wavelength (515 nm) at various volume percentages of DCE in MCH (c = 50 μM). c Time-dependent UV-vis absorption variation of the 2EH-PDI at 515 nm at various cooling rates in MCH* (c = 50 μM) at 303 K.
In the case of H-bonded π-systems, intramolecular H-bonding is shown to be responsible for the formation of dormant monomers17,19,36,39. However, in 2EH-PDI it is surprising to see the formation of dormant monomers despite the lack of any H-bonding interactions. To gain insights into the kinetically trapped states of 2EH-PDI, gas phase semi-empirical and quantum chemical calculations of the 2EH-PDI monomer were performed using GAUSSIAN1654. Note that the reported energies are computed in the gas phase and will likely be altered in the presence of an explicit solvent. The details of the computational methods were provided in the Supplementary Information (Supplementary Note 2). Since all molecules exist in the monomeric state above the critical temperature, as a first step, we used quantum calculations to explore all possible conformations of the 2EH-PDI molecule. We computed the two-dimensional potential energy surface (PES) by varying the two dihedral angles, each belonging to a side chain, defined between the π-plane and the side chains (C-N-C-C), using the semi-empirical PM6 method55. Fig. 3a depicts the PES of the 2EH-PDI molecule, revealing several minima regions (highlighted as yellow colored dots). In the next step, we optimized each structure within the density function theory formalism using the ωB97xD/6-31 g(d) level of theory56. We identified six stable conformers of 2EH-PDI with energy differences ranging from 0 to 5 kJ/mol. These conformations mainly fall into two types: chair and boat. In both cases, the alkyl moieties are positioned at angles of approximately 30 or 80° with respect to the π-plane. Figure 3b illustrates the three chair-type conformations (labeled as 1c, 2c, and 3c) arranged according to their stability. The analogous boat-type conformations (labeled as 1b, 2b, and 3b, respectively) are provided in Supplementary Information (Supplementary Fig. 7). Each boat conformer has the same energy as its analogous chair conformation. The 1c conformer is the most stable among all chair-type conformers, with an energy lower by 2.5 kJ/mol and 4.9 kJ/mol compared to 2c and 3c, respectively.
a Potential energy surface of 2EH-PDI molecule calculated using the semi-empirical PM6 method. The energy values, in kJ/mol, are shown on the color bar, and the two axes correspond to the two dihedral angles between the π-plane and the two side chains (C-N-C-C). All subsequent results were obtained using density functional theory. b Structure of the 2EH-PDI molecule in three chair-type conformations labeled as 1c, 2c, and 3c. c Probability of finding each conformation at 353 K, calculated using the Boltzmann factor. d Relative energies (in KJ/mol) of the six conformers (shown in black) and the associated interconversion energy barriers (displayed in red), were both computed using density functional theory.
The spatial arrangement of the 2-ethylhexyl side chains of 1b, 2b, 3b, 2c, and 3c conformations of 2EH-PDI molecules constrains the π-π stacking interactions due to steric hindrance or defects. However, due to its favorable side chains spatial arrangement, the stack formed by the 1c conformer results in maximum π-π stacking interactions and lower steric hindrance, facilitating the formation of the stack49. This implies that the 1c conformer serves as the active species for the growth of a supramolecular polymer, and its higher concentration in the solution is necessary to observe stack formation. We calculated the probabilities of finding each conformation in the solution at 353 K using the Boltzmann factor, as shown in Fig. 3c. The results indicate that approximately 60% of 2EH-PDI molecules adopt conformations 1c and 1b, while two-thirds of the remaining molecules are in conformations 2c and 2b. As a result, it is expected that in the solution, conformation 1c and 1b dominates, while other conformers are also significantly present. This disparity in the conformational population can lead to a decrease in the concentration of active monomers, resulting in the observed hysteresis during the cooling process. This finding aligns with the hypothesis proposed by Würthner and his team, who suggested that the kinetic inactivation of monomers depends on the energetic interplay between kinetically trapped, inactive species and active species for supramolecular polymerization36.
To further explore the likelihood of transitions between these conformers, we conducted calculations to determine the energy barriers involved, as depicted in Fig. 3d. The results reveal that the interconversion among either chair-type or boat-type conformations requires approximately 4 kBT of energy, while the conversion from the 1c to 1b conformer requires approximately 14 kBT of energy. These energy barriers are sufficiently high to hinder spontaneous nucleation, thereby governing the critical temperature during cooling. This observation is further supported by the dependence of the critical temperature on the cooling rates (Fig. 2c). Therefore, our computational findings suggest that thermal hysteresis primarily arises from the coexistence of multiple conformations at high temperatures. The elevated energy barriers inhibit the transition of kinetically trapped species into active species, which are essential for supramolecular polymerization.
Homo-seeding
The formation of dormant monomers by 2EH-PDI (50 μM) in MCH* encouraged us to carry out LSP by adding the prefabricated SP seed of 2EH-PDI (Fig. 4). When a DCE solution of 2EH-PDI is injected into MCH, to result in the final solvent composition as MCH* (final concentration:50 μM), it spontaneously assembles into SPs of various lengths (Supplementary Fig. 8). Upon sonication of these long polydisperse SPs for 1 h at 303 K, they fragmented into many short seed-like fibers with active chain ends (Fig. 4c). UV-vis absorption and fluorescence spectra revealed that sonication did not alter the aggregation behavior 2EH-PDI (Supplementary Fig. 9), and the average length of seed particles is around 700–800 nm (Fig. 4c). Seeded growth polymerization was attempted immediately by adding the seed solution to the dormant monomers of 2EH-PDI, and the final concentration of the solution was kept constant at 50 μM (Fig. 4a). As previously stated, the final length of SP always depends upon the mass ratio of added seed to monomer solution16. In this perspective, we have added different mol% of seed to dormant monomers and monitored through UV-vis spectroscopy and FE-SEM. The UV-vis absorption spectra of dormant monomers solution after adding the 5 mol% sonicated seed showed a sudden decrease in the monomeric absorption peaks at 515 nm and 480 nm, with an increase in the absorbance of the band at 575 nm (Fig. 4b and Supplementary Fig. 10). To further investigate the seed-indued living growth of 2EH-PDI dormant monomers, we have added different mol% of seeds and monitored the kinetics of LSP (Fig. 4b). As expected, spontaneous elongation without any lag time was observed (Fig. 4b), and the length of resultant fibers analyzed by FE-SEM experiments has shown a systematic increase in the length of SPs with a decrease in seed mol%. From FE-SEM studies, we found that the average length of the fibers prepared from [2EH-PDImonomer] / [2EH-PDI seed] ratios of 19:1, 3:1, and 1:1 are 6 μm, 2 μm, and 1 μm, respectively, with the average seed length being 700–800 nm (Fig. 4d–f).
a Schematic illustration of the homo-seeding approach of dormant monomers. b Time-dependent absorption changes observed for the 2EH-PDI dormant monomers monitored at 515 nm after adding different mol% of seed. FE-SEM images of 2EH-PDI obtained by spin coating the solutions on a silicon wafer c after sonication of prefabricated fibers, d, e, and f after performing LSP to 2EH-PDI dormant monomers at varying [2EH-PDImonomer] / [2EH-PDI seed] ratios of 1:1, 3:1, and 19:1 respectively (c = 50 μM, l = 10 mm, solvent = MCH*). The images in c–f are representative of three experiments.
To obtain a clear understanding of the molecular mechanism, we conducted kinetic analyses at various concentrations of dormant monomer, specifically 40 µM, 45 µM, 50 µM, and 55 µM while keeping seed concentration constant at 12.5 µM. We monitored the growth kinetics by measuring changes in the absorbance at 480 nm (A @ 480 nm). The scaling exponent, which characterizes how the lag time of reaction or half-time (t50) varies with the initial monomer concentration, was determined by the double-logarithmic plot of t50 against monomer concentration, as depicted in Supplementary Fig. 11a under seeded conditions24,25,26,27,28,29,30. The obtained value for the scaling exponent is γ = −1.20 ± 0.09, corresponding to reaction order n1 = 2.4. In the present case, we have not observed any fragmentation, and it is a monomer-dependent process hence γ can be a more negative value than −151,57. The growth kinetics were modeled using a seed-induced nucleation-elongation framework from amyloid software (http://www.amylofit.ch.cam.ac.uk)30 and fit well with the experimental data (Supplementary Note 3, Supplementary Fig. 11 and Supplementary Table 1). However, the same kinetic data showed a less favorable fit for the secondary nucleation-elongation model (Supplementary Fig. 12 and Supplementary Table 1). The above observations clearly indicate that the conversion of dormant monomers of 2EH-PDI into SPs via homo-seeding takes place through the primary nucleation-elongation mechanism.
3D spherical spherulites via secondary nucleation (shear-induced assembly)
Given prior publications on how mechanical agitation, such as stirring, aids the rate-determining nucleation process35,37,58, we conducted time-dependent kinetic investigations of MCH* containing dormant monomers of 2EH-PDI with stirring (Fig. 5). As expected, the nucleation process is expedited at 60 RPM, as seen by decreased monomeric absorbance after 10 min (Fig. 5b and Supplementary Fig. 13). Surprisingly, FE-SEM studies revealed that resultant self-assembled structures have 3D spherical spherulite-like structures (Fig. 5a, e and Supplementary Fig. 14)14,15,50. In most circumstances, the morphology obtained in LSP is the same as that obtained in thermodynamically controlled SPs. Although mechanical agitation, such as stirring or pipetting, speeds up the nucleation process, previous reports indicate that it has little effect on the morphology of SPs37. In the present case, mechanical agitation creates 3D spherical spherulites (vide infra) with micrometers length in all directions (Fig. 5e, f and Supplementary Fig. 14a–c). We conducted a concentration-dependent kinetic analysis by monitoring the absorbance at 480 nm while maintaining a constant stirring rate of 60 RPM to understand the growth mechanism further. All the kinetic profiles exhibited a sigmoidal-like transition, which included a lag phase followed by an exponential phase (Fig. 5d). In stark contrast when considering homo-seeding, we observed spontaneous growth in kinetics, characterized by a non-sigmoidal nature and the absence of any lag phase (Fig. 5b). These characteristics are typical of the secondary nucleation-elongation process24,25,26,27,28,29,30. We determined the scaling exponent as γ = −3.0 ± 0.37 (Fig. 5c), which is higher than the value obtained in homo-seeding experiments. This further indicates the presence of secondary nucleation events with a secondary reaction order of n2 = 5. Furthermore, we comprehensively analyzed all the kinetics and found that all the data fit well with the unseeded secondary nucleation model, with an average mean squared error (MSE) value less than 0.0007 (Fig. 5d, Supplementary Note 3 and Supplementary Table 2), in contrast to the unseeded primary nucleation-elongation model, where the average mean squared error (MSE) value is more than 0.006. These kinetic analyses strongly suggest that the growth of 3D spherulites via shear forces takes place through a typical secondary nucleation-elongation mechanism.
a Schematic illustration of the formation of 3D spherical spherulites by 2EH-PDI via secondary nucleation-elongation triggered by the application of shear forces (stirring) to its dormant monomers. b Illustration of differences between primary nucleation (homo-seeding) and secondary nucleation (stirring at 60 RPM) events. The sigmoidal growth of the 2EH-PDI dormant monomer under stirring indicates the presence of the secondary nucleation process. The circles on the kinetic profiles indicate the half-time. c log-log plot of the half-times of stir-induced (60 RPM) supramolecular polymerization versus the original concentration of 2EH-PDI. Symbols represent the experimental data; solid line is a power law fit. This fit shows a linear trend with a slope of −3.00 ± 0.37 referred to as the exponent coefficient (γ), indicating a monomer-dependent secondary nucleated supramolecular polymerization process. Since there is no seed is added externally, the concentration of the seed is zero. d Kinetic profiles of the concentration-dependent experiments at 60 RPM were obtained by monitoring the absorbance at 480 nm while varying the dormant monomer (2EH-PDI) concentrations to 40 μM, 45 μM, 50 μM, and 55 μM. FE-SEM images of 2EH-PDI, obtained by spin coating the solutions on a silicon wafer after stirring the dormant monomers at e 60 RPM, f 120 RPM, and g 600 RPM for 60 min at 303 K (c = 50 μM, solvent = MCH*). The images in e–g are representative of three experiments.
Owing to their large 3D structures, the solutions having spherulites are inhomogeneous compared to the solutions having 1D SPs formed via primary nucleation (Supplementary Fig. 16a). We have also noticed that spherulites have better thermal stability than 1D SPs. A 50 µM solution of 2EH-PDI SPs with spherulite morphology synthesized via secondary nucleation (stirring at 60 RPM) showed a melting temperature of 312 K, which is 7 K higher than the 1D SPs obtained via primary nucleation (with 5 mol% seed) (Supplementary Fig. 16b). Moreover when taken in 70% DCE in MCH at 303 K, 1D SPs are dissociated into monomers in less than 10 min, whereas 3D spherulites took more than 20 min (Supplementary Fig. 16c–e). All these observations suggest that the 3D spherulite structures of 2EH-PDI formed via a secondary nucleation event are more robust than its 1D SPs formed via a primary nucleation event.
We noticed that up to 300 RPM, we could observe the formation of 3D spherical spherulites, and the size of spherulites decreased with increasing the RPM (Fig. 5e, f and Supplementary Fig. 14a–c). However, after stirring at 600 RPM, we could observe mostly 1D SPs and a few spherulites (Fig. 5g and Supplementary Fig. 14d). To understand the stability of spherulites at 600 RPM, we synthesized them at 60 RPM and stirred them at 600 RPM for 1 h. Interestingly, FE-SEM data reveal that these spherulites are stable even when the solution is subjected to strong mechanical agitation up to 600 RPM (Supplementary Fig. 17). However, when the dormant monomers of 2EH-PDI were stirred at 600 RPM, mostly 1D SPs were formed. To understand this further, we conducted kinetic growth studies of 2EH-PDI at 600 RPM across four different concentrations and obtained a scaling exponent (γ) close to −2.0 (Supplementary Fig. 18a). The primary nucleation reaction order (nc) and secondary nucleation reaction order (n2) were determined to be 4 and 3, respectively. Notably, the kinetic data showed a good fit for both the unseeded primary nucleation-elongation model (Supplementary Fig. 18) and the secondary nucleation-elongation model (Supplementary Fig. 19). This suggests that supramolecular polymerization at 600 RPM is driven by both primary and secondary nucleation events, resulting in the formation mixture of 1D fibers and 3D spherical spherulites (Supplementary Fig. 14d). This phenomenon was also observed in protein aggregation, particularly in amyloid formation, where both primary and secondary nucleation events occur51,59,60.
We have also noticed that mechanical agitation via repetitive pipetting can also induce the formation of 3D spherical spherulites like stirring (Fig. 6 and Supplementary Fig. 20). To monitor the temporal evolution of the spherulites, we conducted a series of FE-SEM examinations at different intervals after applying weak mechanical stimuli such as pipetting. For this purpose, we have applied 5–6 times repetitive pipetting to the MCH* solution containing dormant monomers and left it undisturbed at 303 K. In this case, the assembly process began with a 5-min lag period, as indicated in Fig. 6a, b, and we observed the hedrite morphology after 5 min (Fig. 6d). The formation of intermediate X-shape (hedrite) morphology in the initial stages of growth is a characteristic of spherulite formation50,61. With the increase in time, we have observed fibril growth in all directions via small-angle branching50,61, resulting in the formation of star-shaped morphology (Fig. 6e, f). We got larger 3D spherulite structures with increasing branches after 50 min (Fig. 6g and Supplementary Fig. 20b–d). The 3D structure of spherulite was further confirmed by FE-SEM images that provide a side view, which was obtained by tilting the substrate up to 70° (Supplementary Fig. 20c). To avoid any ambiguity on the formation of 3D spherulites in solution, the dormant monomers solution of 2EH-PDI in MCH* was mechanically agitated via repetitive pipetting (5–6 times), and the resultant solution was observed under the optical microscope. Interestingly, after some time, we see the formation of 3D spherulite structures in solution (Fig. 6c). This unambiguously proves that the formation of 3D spherulites via slow mechanical agitation occurs in the solution.
a UV-vis absorption spectra of 2EH-PDI dormant monomers (red), one hour after applying the slow mechanical agitation via repetitive pipetting (green), LSP after adding 10 mol% seed (blue) in MCH*. b Time-dependent variation in the absorbance of 2EH-PDI at 515 nm after applying the mechanical agitation via repetitive pipetting to the dormant monomer (green). The control experiments by adding the 10 mol% seed (blue) and 0 mol% seed (red) to the dormant monomers of the 2EH-PDI are shown for comparison. c Optical microscopy image of the spherulites obtained in MCH* after applying the slow mechanical agitation via repetitive pipetting. d–g FE-SEM images of 2EH-PDI, obtained by spin coating the solutions on a silicon wafer after d 5 min., e 15 min., f 30 min. g 50 min. of applying the mechanical agitation via repetitive pipetting to the dormant monomers of 2EH-PDI (c = 50 μM, solvent MCH*). The image in c is representative of three experiments, images in d–f are representative of one experiment, and the image in g is representative of three experiments.
The above results vividly illustrate the remarkable sensitivity of 2EH-PDI supramolecular polymerization to even minor alterations in reaction conditions. The self-assembly behavior of 2EH-PDI is primarily governed by the dominant primary nucleation event in the homo-seeding approach. However, by introducing shear forces through actions like pipetting and stirring, we could bias its self-assembly pathway, initiating secondary nucleation events that result in the formation of 3D spherical spherulite structures. In this context, the anticipated mechanism involves the agitation of dormant monomers, which facilitates generating a limited number of small nuclei (Fig. 5a). This, in turn, promotes secondary nucleation of high-energy dormant monomers on the small nuclei, followed by elongation in all directions, leading to the formation of low-energy SPs with spherulite architecture. Notably, stir-induced secondary nucleation events have been well-documented in processes such as crystallization52,53 and protein aggregation51. However, it is worth mentioning that, to the best of our knowledge, no previous reports exist regarding their occurrence in functional SPs. Here, we demonstrated an important example where dormant 2EH-PDI monomeric building blocks would lead to the formation of 3D spherulites via mechanical agitation, which is not the case in homo-seeding experiments.
Supramolecular polymer heterostructures via secondary nucleation (Hetero-seeding)
The results obtained from homo-seeding and shear-induced assembly further encouraged us to explore the hetero-seeding approach (Fig. 7). It has already been demonstrated that supramolecular block copolymers can be synthesized using LSP via a hetero-seeding process, which can provide excellent structural and sequence control10,11,12,13,18,19,20,21,22. For the hetero-seeding approach, we prepared a PE-PDI having a propoxyethyl side chain at the imide positions (Fig. 1a). Like 2EH-PDI, PE-PDI also self-assembles in MCH* via J-aggregation and forms 2D platelets (Supplementary Fig. 21 and further explanation there). PE-PDI seeds were prepared in MCH* via sonication for 1 h at 303 K and 50 mol% of these were added to the dormant monomers of 2EH-PDI. We found a drop in 2EH-PDI monomeric wavelength absorbances (λmax = 515 nm) after a 5-min lag period (Fig. 7a, b). FE-SEM images revealed that 1D SPs of 2EH-PDI were grown on the surface of 2D platelets of PE-PDI and oriented across their length (Fig. 7c and Supplementary Fig. 22). Contrary to homo-seeding, which demonstrated spontaneous growth without any lag phase (Fig. 4b), the presence of a lag phase lasting for 5 min and the growth of 2EH-PDI fibers on the surface of PE-PDI seeds suggests the presence of a secondary nucleation-elongation mechanism (Fig. 7b).
a Schematic illustration for formation SP heterostructures obtained by adding PE-PDI 2D platelets to 2EH-PDI dormant monomers via secondary nucleation. b Time-dependent variation in the absorbance of 2EH-PDI dormant monomers at 515 nm after adding the 50 mol% of PE-PDI seeds (blue) and spontaneous polymerization of 2EH-PDI (red) is shown for comparison. c FE-SEM image of SP heterostructures synthesized via hetero-seeding approach by adding 50 mol% PE-PDI 2D platelets seeds to 2EH-PDI dormant monomers. d log-log plot of the half-times of hetero-seeding supramolecular polymerization versus the original concentration of 2EH-PDI. Symbols represent the experimental data; solid line is a power law fit. This fit shows a linear trend with a slope of −3.46 ± 0.09 called exponent coefficient (γ), which suggests a monomer-dependent, seed-induced secondary nucleated supramolecular polymerization process. e Kinetic profiles of the concentration-dependent hetero-seeding experiments, obtained by monitoring the absorbance at 480 nm of 2EH-PDI, at constant seed concentration ((PE-PDI)concentration: 25 μM) while varying the dormant monomer concentrations of 2EH-PDI to 40 μM, 45 μM, 50 μM, and 62 μM. The sigmoidal growth of the 2EH-PDI dormant monomers indicates a secondary nucleation-elongation process. f Bright-field microscopy images showing time-dependent growth of SP heterostructures after mixing the 50 mol% of PE-PDI seeds to the 2EH-PDI dormant monomers in MCH* (encircled with dashed lines of blue, pink, and magenta). g Kinetics of growth of SP heterostructures from the PE-PDI seeds encircled in blue, pink and magenta dashed lines in panel (f) was tracked via image analysis to follow the increase in pixel area corresponding to the growth of new fibrils from the seeds. The image in c is representative of four experiments, and the images in f are representative of three experiments.
Like homo-seeding experiments, we conducted hetero-seeding experiments using various dormant monomer concentrations (40, 45, 50, and 62 μM) of 2EH-PDI, while maintaining a constant seed concentration of 25 μM for PE-PDI. In all cases, the kinetic profiles exhibited a sigmoidal-like transition characterized by a lag phase followed by an exponential phase, which indicates the occurrence of a secondary nucleation event induced by seeding (Fig. 7e). As the monomer concentration increased from 40 μM to 62 μM, there was a noticeable decrease in the half-time. Plotting the half-time against the monomer concentration on a double-logarithmic scale yielded a scaling coefficient γ of −3.46 ± 0.09 (Fig. 7d), demonstrating a linear relationship and sign of a secondary nucleation event. Additionally, we derived a secondary nucleation reaction order of n2 = 6 from this analysis. Furthermore, we conducted a comprehensive analysis of all the kinetics and found that they fit well with the secondary nucleation model, with an average mean squared error (MSE) value less than 0.0004 (Fig. 7e and Supplementary Table 4). These kinetic analyses strongly support the growth of SPs of 2EH-PDI on the surface of PE-PDI seeds via a hetero-seeding approach triggered by a typical secondary nucleation process.
Since the PDI is common in both 2EH-PDI and PE-PDI, we expected that SPs of 2EH-PDI would grow from the ends of PE-PDI20. However, FE-SEM studies demonstrated that SPs of 2EH-PDI are grafted on the surface of the PE-PDI nanoplatelets (Fig. 7c and Supplementary Fig. 22). To gain further insights into this phenomenon, we have conducted powder X-ray diffraction (PXRD) studies on SPs of 2EH-PDI, PE-PDI and their heterostructures (Supplementary Fig. 23). PXRD revealed that 2D platelets of PE-PDI are more crystalline than 2EH-PDI SPs. The SPs of 2EH-PDI showed a broad and low intense peak at 2θ = 4.31° (d-spacing of 2.05 nm) indicating a poor crystalline order. On the other hand, the 2D platelets of PE-PDI showed good crystalline order, as evidenced by several sharp and high-intensity peaks. The first peak was observed at 2θ = 5.54°, corresponding to a d-spacing of 1.6 nm. Successive peaks at 0.8 nm (2θ = 11.09°) (d/2), 0.54 nm (2θ = 16.45°) (d/3), and 0.44 nm (2θ = 19.96°) (~d/4) are also observed. This indicates the lamellar-like packing of PE-PDI molecules with interdigitation of side chains in the 2D platelets (Supplementary Fig. 23). This observation further suggests that the side chain variation results in disparate crystal packing for both PDI derivatives. Due to these dissimilar lattice structures, 2EH-PDI monomers do not grow at the chain ends of PE-PDI and prefer to grow on the surface of PE-PDI via secondary nucleation (Fig. 7a). Hence, the crystalline nature of individual structures is also retained in the heterostructures (Supplementary Fig. 23). We have further controlled the grafting density of 2EH-PDI SPs on the surface of PE-PDI 2D platelets by varying the mol% of PE-PDI (Supplementary Fig. 24). By decreasing the mol% of PE-PDI seeds from 50% to 30%, we have observed increased covering of the PE-PDI surface by the SPs of 2EH-PDI compared to 50 mol% of the seed (Fig. 7c, and Supplementary Fig. 24a, b). By further decreasing the mol% of PE-PDI seeds to 15%, their surface is fully grafted by the SPs of 2EH-PDI (Supplementary Fig. 24c, d).
We have also explored possibilities to provide the direct visualization of the growth of SPs of 2EH-PDI on PE-PDI in solution via hetero-seeding (Fig. 7f, g). For this purpose, we have taken the MCH* solution containing dormant monomers of 2EH-PDI and 50 mol% of PE-PDI seeds in rectangular long capillary cells. Initially, we observed only 2D platelets of 2EH-PDI seeds in the solution. As time proceeds, we observe the emergence of SPs of 2EH-PDI from 2EH-PDI 2D platelet seeds across their length (Fig. 7f and Supplementary Movie 1). This is further supported by the increase in pixel area due to the growth of new fibrils from the seeds (Fig. 7g). Similar observations are made when these solutions are visualized under fluorescence mode (Supplementary Fig. 25 and Supplementary Movie 2). These observations unambiguously prove PE-PDI seeds induce the supramolecular polymerization of 2EH-PDI dormant monomers via secondary nucleation in solution. Notably, such a direct visualization of the growth of SPs allows us to understand the temporal evolution of complex supramolecular structures from small molecular building blocks. The kinetics of growth probed through UV-vis experiments in 10 mm cuvette are slower than the optical microscopy experiments done in rectangular capillaries due to the mass transport limitations in narrow channels of capillaries (Fig. 7b, g). The growth of SPs of 2EH-PDI from PE-PDI seeds within 200 µm rectangular capillaries followed by bright-field microscopy showed quick saturation of the growth within 3 min due to rapid depletion of local concentration of dormant monomers (Fig. 7g). On the other hand, in UV-vis absorption experiments performed in 10 mm cuvette, fresh monomers are continuously available to the growing SPs on the seeds. As a result, the process takes longer time (>20 min.) for the saturation.
Next, we have also explored the possibility of selectively disassembling one of the components from scarf-like 2D heterostructure. Interestingly, we found that SPs of 2EH-PDI have less thermal stability than PE-PDI 2D platelets in MCH*. The SPs 2EH-PDI showed melting at 307 K and significant depolymerization was observed at 323 K (Supplementary Fig. 26a, b). In contrast, PE-PDI seed particles are stable up to 330 K in MCH* (Supplementary Fig. 26a, c). Taking advantage of differences in thermal stability, the SP heterostructure solution was heated at 323 K for 15 min, and this hot solution was coated on the silicon wafer. FE-SEM images revealed the absence of SP heterostructure and the presence of segregated SPs of 2EH-PDI and 2D platelets of PE-PDI (Supplementary Fig. 26d). This indicates that at 323 K, SPs of 2EH-PDI are melted and detached from the surface of 2D platelets of PE-PDI and formed separately, probably during solvent evaporation. On the other hand, when this solution was cooled from 323 K to 303 K, and coated on a silicon wafer after waiting for an hour at 303 K, we observed the formation of SP heterostructures from FE-SEM images (Supplementary Fig. 26e, f). Furthermore, we immersed the silicon wafer containing SP heterostructures in MCH* solvent at 323 K for various time intervals and visualized them through FE-SEM, which showed only 2D platelet morphology (Supplementary Fig. 27b–d). This is due to the selective depolymerization and dissolution of SPs of 2EH-PDI at 323 K from the surface of PE-PDI seeds into MCH* solution.
Discussion
In this manuscript, we have presented a simple molecular design (2EH-PDI) to synthesize dormant monomers, which can be explored for architectural control of SPs via LSP and secondary nucleation. Theoretical studies indicate that dormant monomers of 2EH-PDI are formed due to the statistical distribution of various conformers of 2EH-PDI monomers in the solution at high temperatures. We found the distinct nucleation events during the supramolecular polymerization of dormant monomers through homo-seeding, shear-induced assembly, and hetero-seeding, resulting in the creation of elegant supramolecular architectures such as 3D spherulites and scarf-like SP heterostructures. Interestingly, mechanical agitation of dormant monomers of 2EH-PDI not only biases the mechanism of supramolecular polymerization from primary nucleation to secondary nucleation but also significantly alters the topology of SPs (1D SPs to 3D spherical spherulites). Moreover, the 3D spherulites obtained via secondary nucleation are more robust than corresponding 1D SPs obtained via primary nucleation. Low thermal stability SPs of 2EH-PDI than 2D platelets of PE-PDI allowed us to remove and reattach the former ones from scarf-like SP heterostructures selectively. Our results further indicate that in addition to well-explored H-bonded π-systems for LSP and architectural control, simple π-systems such as alkylated PDIs would also be worth exploring in the same direction. This would be useful to expand the toolbox for non-covalent synthesis and provide access to complex supramolecular architectures.
Methods
Preparation of dormant monomers
A solution of 2EH-PDI (0.3 mL) in DCE was injected into 2.7 mL of methylcyclohexane (MCH), promptly leading to the formation of SPs (Final concentration: 50 μM, final solvent composition: 10% DCE in MCH). Subsequently, this SPs solution was heated to 353 K, resulting in the formation of a monomeric state in the solution. Upon cooling this hot monomeric solution to 303 K at a rate of 10 K/min, kinetically trapped dormant monomers were formed and exhibited stability for over 30 min. Utilizing these kinetically trapped dormant monomers, three distinct seeding experiments were conducted, as outlined below.
Homo-seeding
In this experiment, prefabricated SPs of 2EH-PDI in 10% DCE in MCH were sonicated for 1 h at 303 K. To synthesize SPs with controlled lengths, different mol% of seed was introduced into the dormant monomers of 2EH-PDI to result in a final concentration of 50 μM. For kinetic analysis, the seed concentration was fixed at 12.5 μM, and the dormant monomers concentration varied to 40, 45, 50, and 55 μM at 303 K.
Shear-induced assembly
Following the formation of dormant monomers of 2EH-PDI (40, 45, 50, 55, and 60 μM) at 303 K in 10% DCE in MCH, the solution was agitated at various RPM levels (60, 120, 300, and 600 RPM). We have also used reparative pipetting (five to six times) of dormant monomers 2EH-PDI in 10% DCE in MCH for shear-induced assembly experiments.
Hetero-seeding
Initially, PE-PDI SPs were generated by adding a DCE solution of PE-PDI 0.3 mL to 2.7 mL of MCH in a vial, resulting in the formation of 2D platelets of PE-PDI (Final concentration: 125 μM, final solvent composition: 10% DCE in MCH). These 2D platelets were sonicated for one hour at 303 K. Subsequently, this seed solution (20 vol%) was added to the dormant monomers of 2EH-PDI (40, 45, 50, and 62 μM) at a temperature of 303 K.
Data availability
The authors declare that the data supporting the findings of this study are available within the paper and its Supplementary Information files. All other information is available from the corresponding author upon request. Source data (https://zenodo.org/records/10866038) are provided with this paper.
References
Jung, S. H., Takeuchi, M. & Sugiyasu, K. Molecular self-assembly under kinetic control. In Kinetic Control in Synthesis and Self Assembly 205–229 (Elsevier, 2019).
Wehner, M. & Würthner, F. Supramolecular polymerization through kinetic pathway control and living chain growth. Nat. Rev. Chem. 4, 38–53 (2020).
Vanderzwaag, D., DeGreef, T. F. A. & Meijer, E. W. Programmable supramolecular polymerizations. Angew. Chemie Int. Ed. 54, 8334–8336 (2015).
MacFarlane, L., Zhao, C., Cai, J., Qiu, H. & Manners, I. Emerging applications for living crystallization-driven self-assembly. Chem. Sci. 12, 4661–4682 (2021).
Wang, X. et al. Cylindrical block copolymer micelles and co-micelles of controlled length and architecture. Science 317, 644–647 (2007).
Gilroy, J. B. et al. Monodisperse cylindrical micelles by crystallization-driven living self-assembly. Nat. Chem. 2, 566–570 (2010).
Li, X. et al. Monodisperse cylindrical micelles of controlled length with a liquid-crystalline perfluorinated core by 1D “self-seeding”. Angew. Chemie Int. Ed. 55, 11392–11396 (2016).
Patra, S. K. et al. Cylindrical micelles of controlled length with a π-conjugated polythiophene core via crystallization-driven self-assembly. J. Am. Chem. Soc. 133, 8842–8845 (2011).
He, X. et al. Two-dimensional assemblies from crystallizable homopolymers with charged termini. Nat. Mater. 16, 481–488 (2017).
Lei, S., Tian, J., Kang, Y., Zhang, Y. & Manners, I. AIE-active, stimuli-responsive fluorescent 2D block copolymer nanoplatelets based on corona chain compression. J. Am. Chem. Soc. 144, 17630–17641 (2022).
Zhang, Y. Dendritic micelles with controlled branching and sensor applications. J. Am. Chem. Soc. 143, 5805–5814 (2021).
Song, S. et al. Solvent effects leading to a variety of different 2D structures in the self-assembly of a crystalline-coil block copolymer with an amphiphilic corona-forming block. Chem. Sci. 11, 4631–4643 (2020).
Song, S., Zhou, H., Manners, I. & Winnik, M. A. Block copolymer self-assembly: polydisperse corona-forming blocks leading to uniform morphologies. Chem 7, 2800–2821 (2021).
Jiang, J. et al. Polyferrocenylsilane block copolymer spherulites in dilute solution. J. Am. Chem. Soc. 145, 1247–1261 (2023).
Song, S. et al. Spherulite‐like micelles. Angew. Chemie 133, 11045–11051 (2021).
Ogi, S., Sugiyasu, K., Manna, S., Samitsu, S. & Takeuchi, M. Living supramolecular polymerization realized through a biomimetic approach. Nat. Chem. 6, 188–195 (2014).
Kang, J. et al. A rational strategy for the realization of chain-growth supramolecular polymerization. Science 347, 646–651 (2015).
Sarkar, A. et al. Self-sorted, random, and block supramolecular copolymers via sequence controlled, multicomponent self-assembly. J. Am. Chem. Soc. 142, 7606–7617 (2020).
Sarkar, A. et al. Tricomponent supramolecular multiblock copolymers with tunable composition via sequential seeded growth. Angew. Chemie Int. Ed. 60, 18209–18216 (2021).
Wagner, W., Wehner, M., Stepanenko, V. & Würthner, F. Supramolecular block copolymers by seeded living polymerization of perylene bisimides. J. Am. Chem. Soc. 141, 12044–12054 (2019).
Jung, S. H., Bochicchio, D., Pavan, G. M., Takeuchi, M. & Sugiyasu, K. A Block Supramolecular polymer and its kinetically enhanced stability. J. Am. Chem. Soc. 140, 10570–10577 (2018).
Sasaki, N. et al. Multistep, site-selective noncovalent synthesis of two-dimensional block supramolecular polymers. Nat. Chem. 15, 922–929 (2023).
Khanra, P., Singh, A. K., Roy, L. & Das, A. Pathway complexity in supramolecular copolymerization and blocky star copolymers by a hetero-seeding effect. J. Am. Chem. Soc. 145, 5270–5284 (2023).
Laishram, R. et al. Secondary nucleation-triggered physical cross-links and tunable stiffness in seeded supramolecular hydrogels. J. Am. Chem. Soc. 144, 11306–11315 (2022).
Sasaki, N. et al. Supramolecular double-stranded archimedean apirals and concentric toroids. Nat. Commun. 11, 1–9 (2020).
Singh, N., Lainer, B., Formon, G. J. M., De Piccoli, S. & Hermans, T. M. Re-programming hydrogel properties using a fuel-driven reaction cycle. J. Am. Chem. Soc. 142, 4083–4087 (2020).
Sarkar, S., Sarkar, A., Som, A., Agasti, S. S. & George, S. J. Stereoselective primary and secondary nucleation events in multicomponent seeded supramolecular polymerization. J. Am. Chem. Soc. 143, 11777–11787 (2021).
Datta, S. et al. Self-assembled poly-catenanes from supramolecular toroidal building blocks. Nature 583, 400–405 (2020).
Sarkar, S., Laishram, R., Deb, D. & George, S. J. Controlled noncovalent synthesis of secondary supramolecular polymers. J. Am. Chem. Soc. 145, 22009–22018 (2023).
Meisl, G. et al. Molecular mechanisms of protein aggregation from global fitting of kinetic models. Nat. Protoc. 11, 252–272 (2016).
Rodriguez Camargo, D. C. et al. Surface-catalyzed secondary nucleation dominates the generation of toxic IAPP aggregates. Front. Mol. Biosci. 8, 1–11 (2021).
Anwar, J., Khan, S. & Lindfors, L. Secondary crystal nucleation: nuclei breeding factory uncovered. Angew. Chemie Int. Ed. 54, 14681–14684 (2015).
Törnquist, M. et al. Secondary nucleation in amyloid formation. Chem. Commun. 54, 8667–8684 (2018).
Greciano, E. E., Calbo, J., Ortí, E. & Sánchez, L. N-Annulated perylene bisimides to bias the differentiation of metastable supramolecular assemblies into J- and H-aggregates. Angew. Chemie Int. Ed. 59, 17517–17524 (2020).
Wagner, W., Wehner, M., Stepanenko, V., Ogi, S. & Würthner, F. Living supramolecular polymerization of a perylene bisimide dye into fluorescent J-aggregates. Angew. Chemie Int. Ed. 56, 16008–16012 (2017).
Ogi, S., Stepanenko, V., Sugiyasu, K., Takeuchi, M. & Würthner, F. Mechanism of self-assembly process and seeded supramolecular polymerization of perylene bisimide organogelator. J. Am. Chem. Soc. 137, 3300–3307 (2015).
Fukui, T. et al. Control over differentiation of a metastable supramolecular assembly in one and two dimensions. Nat. Chem. 9, 493–499 (2017).
Ogi, S., Matsumoto, K. & Yamaguchi, S. Seeded polymerization through the interplay of folding and aggregation of an amino-acid-based diamide. Angew. Chemie Int. Ed. 57, 2339–2343 (2018).
Shyshov, O. et al. Living supramolecular polymerization of fluorinated cyclohexanes. Nat. Commun. 12, 3134 (2021).
Choi, H., Ogi, S., Ando, N. & Yamaguchi, S. Dual trapping of a metastable planarized triarylborane π-system based on folding and lewis acid-base complexation for seeded polymerization. J. Am. Chem. Soc. 143, 2953–2961 (2021).
Wang, H. et al. Living supramolecular polymerization of an aza-BODIPY dye controlled by a hydrogen-bond-accepting triazole unit introduced by click chemistry. Angew. Chemie Int. Ed. 59, 5185–5192 (2020).
Greciano, E. E., Matarranz, B. & Sánchez, L. Pathway complexity versus hierarchical self‐assembly in N‐Annulated perylenes: structural effects in seeded supramolecular polymerization. Angew. Chemie Int. Ed. 57, 4697–4701 (2018).
Pal, D. S., Kar, H. & Ghosh, S. Controllable supramolecular polymerization: via a chain-growth mechanism. Chem. Commun. 54, 928–931 (2018).
Prabhu, D. D. et al. Self-folding of supramolecular polymers into bioinspired topology. Sci. Adv. 4, eaat8466 (2018).
Yagai, S., Kitamoto, Y., Datta, S. & Adhikari, B. Supramolecular polymers capable of controlling their topology. Acc. Chem. Res. 52, 1325–1335 (2019).
Ma, X. et al. Fabrication of chiral-selective nanotubular heterojunctions through living supramolecular polymerization. Angew. Chemie Int. Ed. 55, 9539–9543 (2016).
Liu, Y. et al. Emergent self-assembly pathways to multidimensional hierarchical assemblies using a hetero-seeding approach. Chem. A Eur. J. 25, 13484–13490 (2019).
Hu, K. et al. Fabrication of single-handed nanocoils with controlled length via a living supramolecular self-assembly. Chem. Mater. 31, 1403–1407 (2019).
Kotha, S. et al. Cooperative supramolecular polymerization guided by dispersive interactions. Chem. An Asian J. 17, e202200494 (2022).
Shtukenberg, A. G., Punin, Y. O., Gunn, E. & Kahr, B. Spherulites. Chem. Rev. 112, 1805–1838 (2012).
Cohen, S. I. A. et al. Proliferation of amyloid-Β42 aggregates occurs through a secondary nucleation mechanism. Proc. Natl. Acad. Sci. USA 110, 9758–9763 (2013).
Dilip, K. K., Rebecca, J. K. & Nolini, S. Chiral symmetry beaking in sodium chlorate crystallization. Science 250, 975–976 (1990).
Waghmare, R. Y., Webb, J. N., Randolph, T. W., Larson, M. A. & Glatz, C. E. Pressure dependence of subtilisin crystallization kinetics. J. Cryst. Growth 208, 678–686 (2000).
Frisch, M. J. et al. Gaussian 16, Revision B.01 (Gaussian, Inc., Wallingford, CT, 2016).
Stewart, J. J. P. Optimization of parameters for semiempirical methods V: modification of NDDO approximations and application to 70 elements. J. Mol. Model. 13, 1173–1213 (2007).
Chai, J.-D. & Head-Gordon, M. Long-range corrected hybrid density functionals with damped atom–atom dispersion corrections. Phys. Chem. Chem. Phys. 10, 6615–6620 (2008).
Knowles, T. P. J. et al. An analytical solution to the kinetics of breakable filament assembly. Science 326, 1533–1537 (2009).
Oh, J. S. et al. Chiral supramolecular multiblock copolymerization accompanying chirality transfer in heterostructures via living chain growth. Angew. Chemie Int. Ed. 62, e202300913 (2023).
Haass, C. & Selkoe, D. J. Soluble protein oligomers in neurodegeneration: lessons from the Alzheimer’s amyloid β-peptide. Nat. Rev. Mol. Cell Biol. 8, 101–112 (2007).
Zimmermann, M. R. et al. Mechanism of secondary nucleation at the single fibril level from direct observations of Aβ42 aggregation. J. Am. Chem. Soc. 143, 16621–16629 (2021).
Xiao, Y. et al. Growth mechanism of the spherulitic propylthiouracil-kaempferol cocrystal: new perspectives into surface nucleation. CrystEngComm 23, 2367–2375 (2021).
Acknowledgements
S.K.R. and K.V.R. acknowledge the Core Research Grant (SERB-CRG) from the Science and Engineering Research Board (CRG/2022/006457) for financial support. S.K.R. acknowledges the ISIRD award, IIT Kharagpur for the financial support and the National Supercomputing Mission (NSM) for providing computing resources of PARAM Shakti at IIT Kharagpur, which is implemented by C-DAC and supported by the Ministry of Electronics and Information Technology (MeitY) and Department of Science and Technology (DST), Government of India. B.V.V.S.P.K. the Core Research Grant (SERB-CRG) from the Science and Engineering Research Board (CRG/2020/006366) for financial support. S.K. thanks the CSIR, India, for the Senior Research Fellowship. R.S. thanks the UGC, India, for the Senior Research Fellowship. A.C.Y. thanks the MOE, India, for the Prime Minister research fellowship. P.S. thanks the UGC, India, for the Junior Research Fellowship. We thank Talluri Manoj from the Department of Materials Science and Metallurgical Engineering, Indian Institute of Technology Hyderabad, for his help in FE-SEM measurements.
Author information
Authors and Affiliations
Contributions
S.K. carried out experimental work, and R.S. performed theoretical studies. K.V.R. conceived the idea, designed the experiments, and directed the project. S.K.R. directed the theoretical studies. A.C.Y. performed all the FE-SEM measurements. B.V.V.S.P.K. and P.S. conducted the optical microscopy studies. K.V.R., S.K.R., S.K. and R.S. wrote the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Shiki Yagai, who co-reviewed with Sougata Datta, and the other, anonymous, reviewers for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Kotha, S., Sahu, R., Yadav, A.C. et al. Noncovalent synthesis of homo and hetero-architectures of supramolecular polymers via secondary nucleation. Nat Commun 15, 3672 (2024). https://doi.org/10.1038/s41467-024-47874-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-024-47874-5