Abstract
Mg3(Sb,Bi)2 is a promising thermoelectric material suited for electronic cooling, but there is still room to optimize its low-temperature performance. This work realizes >200% enhancement in room-temperature zT by incorporating metallic inclusions (Nb or Ta) into the Mg3(Sb,Bi)2-based matrix. The electrical conductivity is boosted in the range of 300–450 K, whereas the corresponding Seebeck coefficients remain unchanged, leading to an exceptionally high room-temperature power factor >30 μW cm−1 K−2; such an unusual effect originates mainly from the modified interfacial barriers. The reduced interfacial barriers are conducive to carrier transport at low and high temperatures. Furthermore, benefiting from the reduced lattice thermal conductivity, a record-high average zT > 1.5 and a maximum zT of 2.04 at 798 K are achieved, resulting in a high thermoelectric conversion efficiency of 15%. This work demonstrates an efficient nanocomposite strategy to enhance the wide-temperature-range thermoelectric performance of n-type Mg3(Sb,Bi)2, broadening their potential for practical applications.
Similar content being viewed by others
Introduction
Thermoelectric (TE) technology that enables the direct conversion between heat and electricity is a promising approach to easing the fossil fuel shortage and promoting the sustainable development1,2. The energy conversion efficiency of TE devices is determined by the performance of TE materials, which is characterized by the dimensionless figure of merit, \({zT}={S}^{2}\sigma T/({\kappa }_{L}+{\kappa }_{e})\), where S is the Seebeck coefficient, σ is the electrical conductivity, \(T\) is the absolute temperature, κL is the lattice thermal conductivity, and κe is the electronic thermal conductivity. Considering that S, σ, and κe are strongly coupled with each other through the carrier concentration, the key to enhancing the TE performance lies in decoupling or synergistically controlling these TE parameters.
Most TE materials, such as PbTe3,4, SnSe5,6, and Cu2Se7,8, exhibit superior performance at high temperatures (approximately above 773 K), whereas their room-temperature performance is inferior to the commercial Bi2Te39,10. However, due to the high cost of Te element, it is vital to seek and develop economical substitutes for Bi2Te3 to further scale up TE device fabrication11,12. Currently, Mg3(Sb,Bi)2 is rendered as an ideal candidate for near-room-temperature applications, owing to the superb TE performance at low temperatures originating mainly from the intrinsically low κL as a result of its complex crystal structure13,14,15,16. Meanwhile, the multivalley characteristics of n-type Mg3(Sb,Bi)2 can ensure outstanding electrical transport properties, beneficial to yielding high TE performance.
In recent years, the near-room-temperature performance of Mg3(Sb,Bi)2 has been improved by multiple strategies. By constructing the solid solutions with different Bi to Sb ratios, the band structure could be modified and the peak zT value shifted towards a lower temperature17,18,19. Moreover, the interest in interface engineering in Mg3(Sb,Bi)2 is growing, particularly focusing on the grain boundary engineering and two-phase interface engineering. On one hand, many strategies such as increasing sintering temperature20, Mg-vapor annealing15, and Cu21 or Nb wetting phase22 at grain boundaries, are employed to promote grain growth with the aim of optimizing the heterogeneity and electrical resistance of grain boundaries in Mg3(Sb,Bi)223,24. However, this improvement is more pronounced at low temperatures probably due to the stronger carrier scattering at grain boundaries. On the other hand, by introducing highly conductive secondary phases, such as graphene nanoplatelets25 and metal inclusions26, at grain boundaries, the band structure at the grain boundaries can be bended, which helps to filter the low-energy electrons and enhance the electrical properties. Therefore, the introduction of highly conductive metal nanoparticles is expected to reduce the interfacial barrier in the Mg3(Sb,Bi)2 system.
Herein, high zT values of ~ 2.0 were obtained in Mg3(Sb,Bi)2 by incorporating built-in metallic nano-inclusions. Given the good wettability at the grain boundaries of Mg3(Sb,Bi)2, Nb was added into the Mg3Sb1.5Bi0.49Te0.01 matrix prepared by mechanical alloying (MA) combined with spark plasma sintering (SPS). The heterogeneous interfaces induced by the nano-sized Nb inclusions together with the grain size controlled by the high-temperature sintering strategy played vital roles in modulating the electrical transport properties. It was inferred that the embedded Nb inclusions at grain boundaries could reduce the interfacial barriers, so the carriers can pass easily through the interfaces. Meanwhile, the S can be obviously enhanced in the Mg3(Sb,Bi)2 with Ta addition, indicating that these built-in metallic nano-inclusions effectively modified the interfacial barriers and enhanced the contribution from high-energy electrons to transport properties. Along with the diminished κL due to enhanced nanoparticle scattering, the zT values of 0.1Nb/Mg3Sb1.5Bi0.49Te0.01 significantly increased to 0.80 at 300 K and 2.04 at 798 K, respectively. A conversion efficiency of 15% under ΔT = 470 K was attained for the single-leg device, showing great commercial prospects in a wide temperature range (300–798 K).
Results
In general, both the carrier and phonon transports are significantly modulated by the Nb-rich secondary phases rather than Nb substitution. The electrical properties of the xNb/Mg3Sb1.5Bi0.49Te0.01 samples (Fig. 1) sintered at both the low and high temperatures show significant improvement after Nb addition, especially at 300–500 K. The near-room-temperature σ is positively correlated with sintering temperature and Nb content (Fig. 1a). Notably, the σ of 0.1Nb/Mg3Sb1.5Bi0.49Te0.01 sintered at 1073 K is elevated to 7.6 × 102 S cm−1 at room temperature, showing 30% enhancement compared to the unadded sample. The σ of the x = 0.2 sample is even higher than that of the sample with x = 0.1. The absolute value of S increases with temperature but remains almost constant after Nb addition (Fig. 1b). However, a slight decrease in S is observed at low temperatures in the x = 0.2 sample. Due to the highly enhanced σ with negligible changes to S, a high PF (over 31 μW cm−1 K−2) is obtained in 0.1Nb/Mg3Sb1.5Bi0.49Te0.01 at room temperature, as shown in Fig. 1c; this value ranks the highest among the data reported for Mg3(Sb,Bi)215,21,27,28 in earlier studies. Essentially, the S contributes more to the high PF while the σ is comparable to the values reported in other literatures, as demonstrated in Supplementary Fig. 1. The electrical properties of the sample with x = 0.05 and 0.15 are also shown in Supplementary Fig. 2. Clearly, with Nb addition, the temperatures corresponding to the highest σ and PF also shift towards lower values, representing the optimization of electrical transport performance at low temperatures.
To provide clear insights into the superior electrical transport properties, the Hall carrier concentration (\({n}_{{{{{{\rm{H}}}}}}}\)) and mobility (\({\mu }_{{{{{{\rm{H}}}}}}}\)) were measured (Fig. 1d). The results of Hall measurement suggest that the \({\mu }_{{{{{{\rm{H}}}}}}}\) of the x = 0.1 sample shows a remarkable increase at low temperatures, whereas this enhancement is obviously weakened above 450 K. Meanwhile, all the Nb-added samples sintered at 1073 K show enhanced \({n}_{{{{{{\rm{H}}}}}}}\) within the entire temperature range compared to the unadded sample; the \({n}_{{{{{{\rm{H}}}}}}}\) increases with increasing Nb content. Due to the increased \({n}_{{{{{{\rm{H}}}}}}}\), the carrier scattering is enhanced, resulting in a decrease in \({\mu }_{{{{{{\rm{H}}}}}}}\) for 0.2Nb/Mg3Sb1.5Bi0.49Te0.01. The weighted mobility (\({\mu }_{{{{{{\rm{W}}}}}}}\)) is also calculated, shown in Supplementary Fig. 3. The x = 0.2 sample maintains a high \({\mu }_{{{{{{\rm{W}}}}}}}\) similar to that of x = 0.1, demonstrating noteworthy improvement compared to the unadded sample. On the contrary, the variation trend of \({n}_{{{{{{\rm{H}}}}}}}\) with Nb content is different for the samples sintered at 923 K. In fact, the changes in \({n}_{{{{{{\rm{H}}}}}}}\) and \({\mu }_{{{{{{\rm{H}}}}}}}\) cannot be solely ascribed to the variable point defects (e.g. Mg vacancies29 or doping atoms27) as thought conventionally, because the carrier scattering induced by point defects is usually more intense in the high-temperature range, which significantly affects the electrical properties at high temperatures. Mostly, the increased \({n}_{{{{{{\rm{H}}}}}}}\) leads to a lower S. But there is an inconsistency between the trend of the S and \({n}_{{{{{{\rm{H}}}}}}}\) for the 1073 K-sintered samples. This may be attributed to the reduced interfacial barriers allowing more high-energy carriers to contribute to the S (this will be anatomized later). Therefore, a higher S is still observed in x = 0.1 sample with an increased \({n}_{{{{{{\rm{H}}}}}}}\). In general, according to σ = \({n}_{{{{{{\rm{H}}}}}}}e{\mu }_{{{{{{\rm{H}}}}}}}\), where e is the electronic charge, the increased \({n}_{{{{{{\rm{H}}}}}}}\) and \({\mu }_{{{{{{\rm{H}}}}}}}\) contribute in tandem to enhancing σ. As a result, Nb addition not only provides extra electrons but also enhances \({\mu }_{{{{{{\rm{H}}}}}}}\) near room temperature. By contrast, the reduced mobility at high temperatures is probably assigned to the enhanced electron scattering. Meanwhile, the slight decrease in S mainly stems from the increased \({n}_{{{{{{\rm{H}}}}}}}\). Similarly, a more pronounced decrease in S is observed due to higher \({n}_{{{{{{\rm{H}}}}}}}\) in the x = 0.2 sample. Nevertheless, the augmented electron concentration donated by Nb still guarantees higher σ (a 17% increase at 798 K), leading to enhanced PF at high temperatures. This might be ascribed to a small amount of Sb atoms being consumed from the matrix caused by the formation of Nb3Sb phase.
The enhanced charge carrier transport is closely associated with microstructures. As shown in Fig. 2a, the grain size of the 923 K-sintered samples is estimated to be about 2 μm. The grain growth seems insensitive to Nb addition (Fig. 2a, b), but the σ at room temperature is improved. For the 1073 K-sintered samples (Fig. 2c, d), the grain size increases more than threefold in value (~7.2 μm), compared to that of the 923 K-sintered samples. Interestingly, by elevating sintering temperature, only a slighter increase in grain size (from 2.3 to 3.7 μm) was observed for the x = 0.1 sample. In spite of smaller grain size, the\(\,{\mu }_{{{{{{\rm{H}}}}}}}\) of the Nb-added samples is still retained a high level (158.4 cm2 V−1 s−1), even higher than that of the unadded samples (134.8 cm2 V−1 s−1). This result conflicts with the conventional view that the room-temperature σ increases with grain size, because of the reduced density of electrically resistive grain boundaries15,20,24. The smaller grain size in the Nb-added samples sintered at 1073 K contributes to enhancing the grain boundary resistance, but the presence of Nb inclusion is able to cancel the negative effect of grain boundaries on electrical properties near room temperature. As shown in the X-ray diffraction (XRD) patterns (Supplementary Fig. 4), extra Bragg reflection peaks are detected at 38.4° in the Nb-added samples. The energy-dispersive X-ray spectroscopy (EDS) elemental mapping on the fracture surface (Supplementary Fig. 5) also confirms the existence of Nb-rich secondary phases in the Nb-added samples. The Nb inclusion is further investigated by a microscope equipped with an EDS detector in the Cs-corrected high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) mode (Fig. 3a–e). It is found that the Nb-rich secondary phases distribute randomly at grain boundaries. The atomic ratios of the central region of the Nb inclusion are shown in Fig. 3f, matching well with the chemical composition of Mg4.5Nb86.0Sb9.5. Furthermore, the EDS analysis also indicates that the Nb atoms do not enter the lattice of the matrix, as shown in Supplementary Fig. 6. More Nb-rich inclusions, about ten to hundreds of nanometers in diameter, are observed in Supplementary Fig. 7. These inclusions help to pin grain boundaries, hindering grain boundary migration and suppressing grain growth.
Back to the question: how does Nb benefit the electrical transport? Considering the facts that increased grain boundaries enhance the interface resistance and Nb inclusions increase the number of interfaces, it is not difficult to infer that the interfaces between Nb and matrix should own lower resistance than the grain boundaries. Therefore, the embedded Nb inclusions at grain boundaries should help to reduce the interfacial barriers and weaken the grain boundary scattering, which promotes carrier transport, as schematically shown in Fig. 3g. Essentially, it may be derived from the weak interface scattering due to the good wettability of Nb to the grains22. It is known that interface scattering is more effective in the low-temperature range. This also explains why the improvement in \({\mu }_{{{{{{\rm{H}}}}}}}\) becomes negligible in the high-temperature range. In addition, the resulting metal-semiconductor interfaces modulate the scattering mechanisms. In 0.1Nb/Mg3Sb1.5Bi0.49Te0.01, the absolute value of the temperature exponent derived from the Hall mobility is higher than that of the matrix. It indicates that the grain boundary scattering mechanism is partially involved for the large-grain samples. The modified interfacial effect by metallic inclusions cancels the decrease in mobility caused by grain boundary scattering, making the acoustic phonon scattering dominant. Figure 3h presents the high-resolution transmission electron microscopy (HRTEM) image of the interface between the matrix and Nb inclusions. The corresponding fast Fourier transform (FFT) patterns (Fig. 3i, j) illustrate the crystal structures of Mg3(Sb,Bi)2 and Nb3Sb viewed in the [\(01\bar{1}\)] zone axis. The Nb-Sb binary phase diagram can serve as evidence for the presence of stable Nb3Sb phase (Supplementary Fig. 8a)30. However, no peaks of the Nb3Sb phase are observed in the XRD patterns (Supplementary Fig. 4), indicating that only a small amount of Nb3Sb is formed at the interface. The Sb in the matrix may diffuse to the Nb inclusion, leading to the formation of new secondary phases near the interfaces. The Nb3Sb phase has a resistivity of 7 × 10−7 Ω m at 298 K31, which is slightly higher than the value of 1.6 × 10−7 Ω m for Nb metal32 but much lower than that of the matrix. These composition-transition interfaces with high conductivity further support the modulation of interfacial barriers by Nb inclusions. Similar interfacial structures between the matrix and the metallic inclusions are displayed in Supplementary Fig. 9. The inclusions perhaps have a core-shell-like structure with Nb as the main body and a small amount of Nb3Sb as the coating layer, as demonstrated in Supplementary Fig. 8b. As there is no orientation relationship between the Nb3Sb phase and the matrix, the Nb-rich inclusions are unlikely to be in situ informed. The modulation of the scattering mechanisms by Nb inclusions remarkably improves the mobility. Besides, due to the formation of the Nb3Sb phase near the interface, a small amount of Sb atoms in the matrix would be inevitably consumed by Nb. As shown in Supplementary Fig. 10, the results of electron probe microanalysis (EPMA) confirmed that the atomic ratio of Sb/Mg in the matrix of x = 0.1 sample is lower than that of the unadded sample. The decreased Sb/Mg ratio may suppress the formation of Mg vacancies, which is beneficial to increasing the \({n}_{{{{{{\rm{H}}}}}}}\) and hence the σ of Mg3(Sb,Bi)2. Moreover, the investigation of the Nb/Mg3SbBi interface also confirms that Nb is in good contact with the matrix without macroscopic secondary phases33,34.
The Nb nano-inclusions not only influence the carrier transport but also interact with phonons. The temperature dependence of total and lattice thermal conductivity is shown in Fig. 4a and Supplementary Fig. 2. The κ and κL decrease first and then increase upon the addition of Nb. A relatively low κ of 0.45 W m−1 K−1 is obtained for 0.1Nb/Mg3Sb1.5Bi0.49Te0.01 sintered at 1073 K. On one hand, the κ and κL are significantly reduced due to the abundant vacancies and vacancy clusters as a consequence of the loss of volatile elements at high sintering temperatures (detailed discussion is provided in our previous work)35. On the other hand, the κL is further reduced by nanoparticle scattering. The sizes of Nb secondary phase are averaged about 200 nm in diameter but are distributed from 10 to 1000 nm, which cover a large range of phonon mean free paths. The variable κL is probably related to the different interfacial thermal resistance originating from the layered or granular bonding between metal and matrix. Notably, it was reported that the κ increased when the thin wetting Nb layer was formed at grain boundaries22. In this case, the two-phase model equivalent to a one-dimensional series circuit can be utilized to understand the increase in κ24, which probably stems from the reduction in interfacial thermal resistance. When Nb exists in the form of secondary phases (from nano to sub-micron scales), the additional scattering centers induced by these nano-inclusions contribute to the reduction in κL by suppressing the propagation of phonons. However, the κ significantly increases when the amount of Nb increases to more than 0.1; higher fractions of thermally conducting Nb phases are more likely to affect the κ through its intrinsic nature. When the contribution from the high κ of Nb phase (53.7 W m−1 K−1) overweighs the reduction in κ by phonon scattering, the κ and κL will rise. Moreover, due to the more pronounced Mg volatilization during high-temperature sintering, no Mg-rich phase is observed in the unadded and Nb-added samples, which is confirmed by the EDS analysis (Supplementary Figs. 5 and 11), excluding the effect of excessive Mg on κ. The total TE performance is enhanced by Nb nano-inclusions in conjunction with high-temperature sintering, as shown in Fig. 4b. The room-temperature zT value increases from 0.38 to 0.80 and the peak zT value is elevated from 1.53 to 2.04 for 0.1Nb/Mg3Sb1.5Bi0.49Te0.01 due to the increased PF and reduced κ, showing ~110% and 33% enhancement, respectively. Moreover, the TE properties of the as-prepared samples exhibit good repeatability, which can be confirmed by the data in Supplementary Fig. 12.
Furthermore, since Nb and tantalum (Ta) are mainly found in tantalite and are symbiotic with each other, the Ta is expected to exhibit similar behaviors. As expected, similar enhancement in the TE performance was discovered in the Ta-added Mg3(Sb,Bi)2 sintered at 1073 K. Figure 5a depicts the temperature-dependent electrical conductivity and Seebeck coefficient of 0.1Nb/Mg3Sb1.5Bi0.49Te0.01 and 0.1Ta/Mg3Sb1.5Bi0.49Te0.01 prepared under the same conditions. Different from the significant increase after Nb addition, the σ only increases slightly after Ta addition. Yet it is worth noting that the S increases with Ta addition, especially at high temperatures. Based on the simultaneous optimization of σ and S, the PF of 0.1Ta/Mg3Sb1.5Bi0.49Te0.01 is up to 32 μW cm−1 K−2 at 323 K and close to 20 μW cm−1 K−2 at 798 K, as shown in Fig. 5b. Interestingly, the improvement in electrical properties near room temperature is the same as the case relevant to Nb but less dramatic, while the effect of Ta becomes more pronounced at high temperatures. As shown in Supplementary Table 1, both \({n}_{{{{{{\rm{H}}}}}}}\) and \({\mu }_{{{{{{\rm{H}}}}}}}\) of the Ta-added sample slightly increase at room temperature, but are less than the values of the Nb-added sample. Similar to the Nb-added samples, nanoscale Ta metal inclusions randomly distribute at grain boundaries in 0.1Ta/Mg3Sb1.5Bi0.49Te0.01, as demonstrated in Supplementary Figs. 13–15. The reason may be that both Nb and Ta are refractory and have good chemical stability. The scanning electron microscope (SEM) images of the fracture surfaces shown in Supplementary Fig. 16 display the grain size of Nb-added and Ta-added samples. The grain size of the Ta-added sample approximately decreases to the level of that of the Nb-added samples, which is also attributed to the pinning effect of inclusions at grain boundaries. The embedded Ta nano-inclusions at grain boundaries should have the similar effect as Nb. However, no Ta-rich secondary phases similar to Nb3Sb were formed under the present experimental conditions; in fact, that no Ta-Sb binary phase diagram was reported might account for why the Ta addition did not affect the carrier concentration as in the case of the Nb-added samples.
Benefiting from the marginally increased n, the contribution to the S from the inclusions becomes easier to distinguish. The built-in Nb/Ta nano-inclusions may scatter the low-energy carriers more efficiently via modifying the interfacial barriers36,37. As mentioned above, the secondary phases near the interface would reduce interfacial potential barriers. It is speculated that these barriers of metal-semiconductor interfaces are lower than that of Mg-deficient grain boundaries, as demonstrated in Fig. 5c. The higher barriers at grain boundaries (Eb1) in the unadded samples would block low-energy and part of high-energy carriers. By incorporating Ta inclusions, the interfacial barrier is reduced from Eb1 to Eb2, allowing more high-energy carriers to pass through. The contribution from high-energy carriers to transport properties is enhanced, giving rise to a higher S. In the case for Nb-added samples, this modified interfacial barrier turns out to optimize σ without sacrificing S, thereby leading to enhanced PF. The S may be a synergistic result of the above effect and increased \({n}_{{{{{{\rm{H}}}}}}}\). The Pisarenko plots shown in Supplementary Fig. 17 exhibit the contribution from the modified interfacial barrier to S, where the data points deviate upward slightly. Recently, it has been reported that the Mo addition also increases the σ of Mg3(Sb,Bi)2-based materials38, indicating the great potential of other transition metals. However, the enhanced σ by Mo addition is mainly due to the grain boundary effect, different from those analyzed above for the Nb or Ta inclusions.
The incorporation of Nb and Ta nano-inclusions into the Mg3(Sb,Bi)2 matrix helps to modify the interfacial barriers, producing similar favorable modulation results. As a consequence of the optimized electrical performance, a high zT value of 2.06 is obtained in 0.1Ta/Mg3Sb1.5Bi0.49Te0.01 at 798 K, as shown in Fig. 6a. However, due to the higher κ (57.5 W m−1 K−1) as well as weaker phonon scattering originating from the larger size of Ta inclusions, the effect of Ta inclusions on reducing κ is limited (Supplementary Fig. 18). The zT values of Ta-added samples within the low- and middle-temperature range are slightly lower than that of Nb-added samples. After adding these metallic inclusions into the matrix, the zT values increase over the entire temperature range, thereby boosting the average zT value (zTave) calculated using the following formula:
where Th and Tc are the temperatures of the hot side and cold side, respectively. The zTave values reach 1.57 and 1.51 within the temperature range of 300–798 K for 0.1Nb/Mg3Sb1.5Bi0.49Te0.01 and 0.1Ta/Mg3Sb1.5Bi0.49Te0.01, respectively. The zTave values of the Nb-added sample in the temperature range 300–773 K and 300–573 K are also calculated, which are 1.54 and 1.30, respectively. Compared to the previously reported results for Mg3(Sb,Bi)2, the zTave values are at the state-of-the-art level and even superior to Bi2(Te,Se)3, which is competitive near room temperature (Fig. 6b)20,27,39,40,41,42,43. Based on such a high TE performance for the optimized sample, i.e. 0.1Nb/Mg3Sb1.5Bi0.49Te0.01 sintered at 1073 K, a single-leg device was fabricated with the Fe7Mg2Cr interface and sintered copper electrode to evaluate the TE energy conversion efficiency. As shown in Fig. 6c and Supplementary Fig. 19, a high efficiency of around 15% is obtained for a single leg under a ΔT of 470 K. The excellent reproducibility of the efficiency measured by the single legs is shown in Supplementary Figs. 20 and 21. The theoretical efficiency of the single-leg device reaches 18% as shown in Supplementary Fig. 22, but both the measured output power and heat flow deviate from the predicted value, indicating additional efforts are needed to optimize the contact layer and control the thermal radiation. In addition, a continuous measurement on the output properties (the inset of Fig. 6d and Supplementary Fig. 23) reveals that the single leg can operate over 120 h at a ΔT = 470 K with an efficiency higher than 14%, showing good service stability. Figure 6d exhibits the high-efficiency values reported in Mg3(Sb,Bi)2 system in recent years, indicating the efficiency achieved in this work rivals other multiple-leg modules but has a wider application temperature range. It is worth noting that, due to the promoted electrical transport by the metallic nano-inclusions, a competitive value is obtained in the low-temperature range, surpassing that of the classical bismuth telluride with broad prospects for commercial applications in electronic cooling.
Discussion
In summary, a high peak zT value of 2.04 at a relatively low temperature (798 K) and a remarkable zTave (300–798 K) of 1.57 for Mg3(Sb,Bi)2 were reported in this work. The fabricated single-leg device showed a high TE conversion efficiency of ~15%, which rivaled those of well-designed modules. The significantly improved TE performance was attributed to the modulation of charge carriers and phonons transport via introducing Nb/Ta inclusions at grain boundaries. The reduced interfacial barriers significantly increased the electrical conductivity in the low-temperature range. Besides, the Nb and Ta inclusions not only contributed to increasing \({n}_{{{{{{\rm{H}}}}}}}\) but also led to remarkably enhanced \({\mu }_{{{{{{\rm{H}}}}}}}\) near room temperature. As a result, the PF was significantly increased, especially at low temperatures. Combined with the effective phonon scattering effect caused by a small number of metallic inclusions, the lattice thermal conductivity was also obviously diminished. Our findings provide a new strategy to deal with the high grain boundary resistance in Mg3(Sb,Bi)2-based materials, particularly demonstrating great potential in near-room-temperature applications.
Methods
Synthesis
Magnesium turnings (99.9%), antimony shots (99.999%), bismuth shots (99.999%), tellurium powder (99.999%), niobium powder (99.9%, 325 mesh) and tantalum powder (99.9%, 325 mesh) were weighed in accordance with the nominal stoichiometry of Mg3.2Sb1.5Bi0.49Te0.01 and Mg3.1X0.1Sb1.5Bi0.49Te0.01 (X = Nb and Ta) and then ball-milled for 8 h in the SPEX 8000D Mixer/Mill ball mill (SPEX, Metuchen, NJ, United States). To explore the effect of Nb on electrical transport properties, the powder with the composition of Mg3.1NbxSb1.5Bi0.49Te0.01 (x = 0.05, 0.15, and 0.2) was also prepared. The ball-milled powder was sintered by spark plasma sintering using the SPS 211Lx Spark Plasma Sintering Machine (Fuji Electronic Industrial Co., Tsurugashima, Saitama, Japan) at 923 K and 1073 K for 20 min under an axial pressure of 50 MPa. To fabricate the single-leg device, the sintered bulk, TE interface material (TEiM) powders and Cu powders (99.9%) were sandwiched in a graphite die and then sintered at 873 K for 10 min under a pressure of 50 MPa. The TEiM powders were generated by ball milling after mixing Fe powder (99.9%), Mg turnings (99.9%), and Cr powder (99.5%). The thicknesses of the sintered bulk and TEiM layers were 8 and 1.5 mm, respectively.
Characterization
The phase purity of the material was determined by powder X-ray diffraction (XRD) using the Bruker D8 Advance X-ray diffractometer (Bruker AXS GmbH, Karlsruhe, Germany) with Cu-Kα radiation. The grain size and crystal orientation were determined via electron backscatter diffraction (EBSD) by the ULVAC-PHI 710 Scanning Auger spectrometer (ULVAC-PHI, Inc., Chigasaki, Japan). Scanning transmission electron microscopy (STEM) observations were performed on the Spectra 300 double-Cs-corrected transmission electron microscope (Thermo Fisher Scientific Inc.) equipped with a field-emission electron source, operating at an accelerating voltage of 300 kV. Atomic resolution energy-dispersive X-ray spectroscopy (EDS) elemental mapping and analysis were conducted using the Super-X EDS detector. The morphology and microstructure were characterized by field-emission scanning electron microscopy (FESEM, Zeiss Merlin, Germany). The fracture surface morphology and elemental distribution were characterized by field-emission scanning electron microscope (FE-SEM, Gemini 2, Zeiss, Germany) equipped with an EDS detector. The quantitative analysis of elements was studied via electronic probe microscopic analysis (JXA-8230, JEOL, Japan).
Thermoelectric property measurements
The Seebeck coefficient (S) and conductivity (σ) were determined using a ZEM-3 Seebeck coefficient/electric resistance measuring system (ULVAC-RIKO Inc., Yokohama, Japan). Thermal conductivity (κ) was calculated using the equation κ = DCpρ, where the thermal diffusivity (D) was measured with the LFA 457 laser flash apparatus (Netzsch GmbH, Selb, Germany). The specific heat capacity (Cp) was derived using the Dulong–Petit law, and the density (ρ) was measured in accordance with the Archimedes method. The electronic thermal conductivity (κe) was calculated based on the Wiedeman–Franz law (κe = σLT), where the Lorenz factor (L) was estimated using the equation \(L=1.5+\exp (-\frac{\left|S\right|}{116})\)44. The Hall coefficient (RH) was determined using the Hall measurement system (ResiTest 8340DC, Tokyo, Japan). The Hall carrier concentration (\({n}_{{{{{{\rm{H}}}}}}}\)) and mobility (μH) were calculated using the equations \({n}_{{{{{{\rm{H}}}}}}}\) = 1/(eRH) and μH = σRH, respectively. The conversion efficiency (η) of the single-leg device was calculated in accordance with the equation η = P/(P + Qc ) × 100%, where the output power (P) and cold side heat flow (Qc) were simultaneously measured with the Mini-PEM testing system (Ulvac-Riko, Japan). The theoretical conversion efficiency was simulated using the COMSOL Multiphysics software.
Data availability
The data that support the findings of this study are available from the corresponding author on request.
References
Bell, L. E. Cooling, heating, generating power, and recovering waste heat with thermoelectric systems. Science 321, 1457–1461 (2008).
Snyder, G. J. & Toberer, E. S. Complex thermoelectric materials. Nat. Mater. 7, 105–114 (2008).
Pei, Y. et al. Convergence of electronic bands for high performance bulk thermoelectrics. Nature 473, 66–69 (2011).
Biswas, K. et al. High-performance bulk thermoelectrics with all-scale hierarchical architectures. Nature 489, 414–418 (2012).
Zhao, L.-D. et al. Ultralow thermal conductivity and high thermoelectric figure of merit in SnSe crystals. Nature 508, 373–377 (2014).
Chang, C. et al. 3D charge and 2D phonon transports leading to high out-of-plane ZT in n-type SnSe crystals. Science 360, 778–783 (2018).
Liu, H. et al. Copper ion liquid-like thermoelectrics. Nat. Mater. 11, 422–425 (2012).
Zhao, K. et al. Solid‐state explosive reaction for nanoporous bulk thermoelectric materials. Adv. Mater. 29, 1701148 (2017).
Pan, Y. et al. Melt-centrifuged (Bi,Sb)2Te3: engineering microstructure toward high thermoelectric efficiency. Adv. Mater. 30, 1802016 (2018).
Zhuang, H.-L. et al. High ZT in p-type thermoelectric (Bi,Sb)2Te3 with built-in nanopores. Energy Environ. Sci. 15, 2039–2048 (2022).
Qin, B. et al. Power generation and thermoelectric cooling enabled by momentum and energy multiband alignments. Science 373, 556–561 (2021).
Tan, X. Y. et al. Enhanced near-room-temperature thermoelectric performance in GeTe. Rare Metals 41, 3027–3034 (2022).
Tamaki, H., Sato, H. K. & Kanno, T. Isotropic conduction network and defect chemistry in Mg3+δSb2-based layered zintl compounds with high thermoelectric performance. Adv. Mater. 28, 10182–10187 (2016).
Zhang, J. et al. Discovery of high-performance low-cost n-type Mg3Sb2-based thermoelectric materials with multi-valley conduction bands. Nat. Commun. 8, 13901 (2017).
Wood, M., Kuo, J. J., Imasato, K. & Snyder, G. J. Improvement of low‐temperature zT in a Mg3Sb2–Mg3Bi2 solid solution via Mg‐vapor annealing. Adv. Mater. 31, 1902337 (2019).
Shu, R. et al. Mg3+δSbxBi2−x family: a promising substitute for the state-of-the-art n-type thermoelectric materials near room temperature. Adv. Funct. Mater. 29, 1807235 (2019).
Mao, J. et al. High thermoelectric cooling performance of n-type Mg3Bi2-based materials. Science 365, 495–498 (2019).
Imasato, K., Kang, S. D., Ohno, S. & Snyder, G. J. Band engineering in Mg3Sb2 by alloying with Mg3Bi2 for enhanced thermoelectric performance. Mater. Horiz. 5, 59–64 (2018).
Han, Z. et al. The electronic transport channel protection and tuning in real space to boost the thermoelectric performance of Mg3+δSb2-yBiy near room temperature. Research 2020, 1–12 (2020).
Kanno, T. et al. Enhancement of average thermoelectric figure of merit by increasing the grain-size of Mg3.2Sb1.5Bi0.49Te0.01. Appl. Phys. Lett. 112, 033903 (2018).
Liu, Z. et al. Demonstration of ultrahigh thermoelectric efficiency of ∼7.3% in Mg3Sb2/MgAgSb module for low-temperature energy harvesting. Joule 5, 1196–1208 (2021).
Luo, T. et al. Nb‐mediated grain growth and grain‐boundary engineering in Mg3Sb2‐based thermoelectric materials. Adv. Funct. Mater. 31, 2100258 (2021).
Kuo, J. J. et al. Mg deficiency in grain boundaries of n‐Type Mg3Sb2 identified by atom probe tomography. Adv. Mater. Interfaces 6, 1900429 (2019).
Kuo, J. J. et al. Grain boundary dominated charge transport in Mg3Sb2-based compounds. Energy Environ. Sci. 11, 429–434 (2018).
Lin, Y. et al. Expression of interfacial Seebeck coefficient through grain boundary engineering with multi-layer graphene nanoplatelets. Energy Environ. Sci. 13, 4114–4121 (2020).
Zhao, W. et al. Superparamagnetic enhancement of thermoelectric performance. Nature 549, 247–251 (2017).
Shi, X. et al. Extraordinary n‐type Mg3SbBi thermoelectrics enabled by yttrium doping. Adv. Mater. 31, 1903387 (2019).
Shi, X. et al. Efficient Sc-doped Mg3.05–xScxSbBi thermoelectrics near room temperature. Chem. Mater. 31, 8987–8994 (2019).
Shuai, J. et al. Significant role of mg stoichiometry in designing high thermoelectric performance for Mg3(Sb,Bi)2-based n-type zintls. J. Am. Chem. Soc. 140, 1910–1915 (2018).
Lomnytska, Ya. F. & Kuz’ma, Yu. B. The Nb–Sb system. J. Alloy. Compd 413, 114–117 (2006).
Arko, A. J., Fisk, Z. & Mueller, F. M. de Haas-van Alphen effect and Fermi surface of Nb3Sb. Phys. Rev. B 16, 1387–1392 (1977).
Cox, W. R., Hayes, D. J. & Brotzen, F. R. Temperature dependence of the hall effect and resistivity in single crystals of Mo and Nb and of Mo-Rich-Re, Mo-Nb, and Nb-Rich-Zr alloys. Phys. Rev. B 7, 3580–3588 (1973).
Fu, Y. et al. Mg3(Bi,Sb)2-based thermoelectric modules for efficient and reliable waste-heat utilization up to 750 K. Energy Environ. Sci. 15, 3265–3274 (2022).
Hu, Z., Fu, Y., Jiang, M., Wang, L. & Jiang, W. Thermal stability of Nb/Mg3SbBi interface. J. Inorg. Mater. 38, 931 (2023).
Li, J. et al. Bi‐deficiency leading to high‐performance in Mg3(Sb,Bi)2‐based thermoelectric materials. Adv. Mater. 35, 2209119 (2023).
Minnich, A. J., Dresselhaus, M. S., Ren, Z. F. & Chen, G. Bulk nanostructured thermoelectric materials: current research and future prospects. Energy Environ. Sci. 2, 466 (2009).
Gayner, C. & Amouyal, Y. Energy filtering of charge carriers: current trends, challenges, and prospects for thermoelectric materials. Adv. Funct. Mater. 30, 1901789 (2020).
Wang, L. et al. Realizing high thermoelectric performance in N‐Type Mg3(Sb, Bi)2‐based materials via synergetic Mo addition and Sb–Bi ratio refining. Adv. Energy Mater. 13, 2301667 (2023).
Chen, X. et al. Excellent thermoelectric performance of boron-doped n-type Mg3Sb2-based materials via the manipulation of grain boundary scattering and control of Mg content. Sci. China Mater. 64, 1761–1769 (2021).
Chen, X. et al. Extraordinary thermoelectric performance in n-type manganese doped Mg3Sb2 Zintl: high band degeneracy, tuned carrier scattering mechanism and hierarchical microstructure. Nano Energy 52, 246–255 (2018).
Liang, J. et al. Synergistic effect of band and nanostructure engineering on the boosted thermoelectric performance of n‐type Mg3+δ(Sb, Bi)2 Zintls. Adv. Energy Mater. 12, 2201086 (2022).
Zhu, B., Wang, W., Cui, J. & He, J. Point defect engineering: Co‐doping synergy realizing superior performance in n‐Type Bi2Te3 thermoelectric materials. Small 17, 2101328 (2021).
Zhu, B. et al. Realizing record high performance in n-type Bi2Te3-based thermoelectric materials. Energy Environ. Sci. 13, 2106–2114 (2020).
Kim, H.-S., Gibbs, Z. M., Tang, Y., Wang, H. & Snyder, G. J. Characterization of Lorenz number with Seebeck coefficient measurement. APL Mater. 3, 041506 (2015).
Bu, Z. et al. An over 10% module efficiency obtained using non-Bi2Te3 thermoelectric materials for recovering heat of <600 K. Energy Environ. Sci. 14, 6506–6513 (2021).
Yin, L. et al. Reliable N-type Mg3.2Sb1.5Bi0.49Te0.01/304 stainless steel junction for thermoelectric applications. Acta Mater. 198, 25–34 (2020).
Ying, P. et al. Towards tellurium-free thermoelectric modules for power generation from low-grade heat. Nat. Commun. 12, 1121 (2021).
Zhuang, H. et al. Thermoelectric performance enhancement in BiSbTe alloy by microstructure modulation via cyclic spark plasma sintering with liquid phase. Adv. Funct. Mater. 31, 2009681 (2021).
Acknowledgements
This work was supported by The Basic Science Center Project of National Natural Science Foundation of China (grant no. 52388201) and the National Key R&D Program of China (no. 2023YFB3809400).
Author information
Authors and Affiliations
Contributions
J.-F.L., J.-W.L. and H.-L.Z. conceptualized this work. J.-W.L. performed the synthesis and thermoelectric property measurements. H.H. performed the EBSD measurement. Q.Z. carried out the STEM measurement. Z.H. and W.L. contributed to the preparation and measurement of single-leg devices. J.-W.L., B.S. and L.C. performed the structure characterizations. J.-W.L., H.-L.Z., J.Y., H.L. and Y.J. helped the analysis of the thermoelectric property data. J.-W.L., H.-L.Z., J.Y. and J.-F.L. wrote the manuscript. All authors participated in the data analysis and the manuscript editing.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Li, JW., Han, Z., Yu, J. et al. Wide-temperature-range thermoelectric n-type Mg3(Sb,Bi)2 with high average and peak zT values. Nat Commun 14, 7428 (2023). https://doi.org/10.1038/s41467-023-43228-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-023-43228-9
- Springer Nature Limited
This article is cited by
-
Exceptional figure of merit achieved in boron-dispersed GeTe-based thermoelectric composites
Nature Communications (2024)
-
Enhanced thermoelectric properties of Bi2Sr2Co2Oy ceramics by dispersing B2O3 additive
Applied Physics A (2024)