Abstract
Solid-state electrolytes with high ionic conductivities are crucial for the development of all-solid-state lithium batteries, and there is a strong correlation between the ionic conductivities and underlying lattice structures of solid-state electrolytes. Here, we report a lattice manipulation method of replacing [Li2OH]+ clusters with potassium ions in antiperovskite solid-state electrolyte (Li2OH)0.99K0.01Cl, which leads to a remarkable increase in ionic conductivity (4.5 × 10‒3 mS cm‒1, 25 °C). Mechanistic analysis indicates that the lattice manipulation method leads to the stabilization of the cubic phase and lattice contraction for the antiperovskite, and causes significant changes in Li-ion transport trajectories and migration barriers. Also, the Li||LiFePO4 all-solid-state battery (excess Li and loading of 1.78 mg cm‒2 for LiFePO4) employing (Li2OH)0.99K0.01Cl electrolyte delivers a specific capacity of 116.4 mAh g‒1 at the 150th cycle with a capacity retention of 96.1% at 80 mA g‒1 and 120 °C, which indicates potential application prospects of antiperovskite electrolyte in all-solid-state lithium batteries.
Similar content being viewed by others
Introduction
All-solid-state lithium batteries (ASSLBs), using solid-state electrolytes (SSEs) to replace organic polymer separators and liquid electrolytes in conventional Li-ion batteries, have triggered intensive research studies because of their merits of potentially improved safety1,2,3. Besides, ASSLBs based on Li-metal anodes are expected to break through the energy density bottleneck, which benefits from the compatibility of SSEs with Li-metal and the mechanical strength of SSEs to prevent the penetration of Li dendrites4,5,6. Consequently, a variety of SSEs have been investigated in recent years, including argyrodite7,8, thio-phosphate9,10, sodium superionic conductor (NASICON)11,12, garnet13,14, antiperovskite15,16,17, and others18.
Still, there are many limitations to overcome for these candidate SSEs. For example, garnet SSEs need high-temperature sintering for densification with high-energy consumption and have huge interfacial resistance against Li-metal anodes19. The NASICON-type SSEs would be deteriorated in contact with Li-metal due to the reduction of Ge4+ or Ti4+20,21,22. Although sulfide-based SSEs (e.g., Li10GeP2S12, Li7P3S11) with excellent ionic conductivity (>1 mS cm−1) may support the operation of ASSLBs at room temperature (RT), the electrochemical instability and the harmful H2S gas produced by exposure to air restrict their practical applications5,23.
Recently, antiperovskite ionic conductors, as special SSEs, have been gaining increasing attention15,24,25. In the aspect of synthesis, antiperovskite (e.g., Li2OHCl) SSEs could be easily prepared by one-step heating treatment of low-cost ingredients (equimolar LiOH and LiCl) and densified at low temperature with low energy consumption25. In terms of stability to Li-metal, the antiperovskite family has been proven to be stable to metallic lithium during the cycling of solid-state batteries26,27. Particularly, the low melting point (∼300 °C) of antiperovskite is rare in the reported candidate SSEs28, which inspires the concept of ‘melt-infiltration’ SSE technology and enables the potential for scalable, low-cost manufacturing of ASSLBs29. However, the undesirable ionic conductivity of Li2OHX (X = Cl, Br) hinders the further development of antiperovskite in ASSLBs, especially the ionic conductivity of orthorhombic Li2OHCl is only 10‒4−10‒5 mS cm‒1 at RT (~25 °C)26,30.
Keeping the crystal in the metastable phase is a conventional method to improve the ionic conductivity of SSEs. Typically, the ionic conductivity of Li7La3ZrO12 was remarkably improved after the cubic phase was stabilized by Al/Ta doping31,32. The nano-porous structure stabilized the metastable phase of β-Li3PS4 and enhanced the ionic conductivity by 3 orders of magnitude9. Similarly, the ionic conductivity of Li2OHCl increased significantly after the phase transition from orthorhombic to cubic around 30–50 °C26, which inspires us to attempt to improve the ionic conductivity of antiperovskite SSEs by lattice manipulation.
Herein, we report a lattice manipulation method of replacing cation clusters with potassium ions in antiperovskite, resulting in a remarkable increase of ionic conductivity of (Li2OH)0.99K0.01Cl to 4.5 × 10‒3 mS cm‒1 at 25 °C, which is 32 times higher than that of Li2OHCl and 2 orders of magnitude higher than that of previously reported26. The in situ powder X-ray diffraction (PXRD) and differential scanning calorimetry (DSC) revealed the phase transition mechanism, and double confirmed the stabilizing effect of K-doping on the metastable cubic phase of antiperovskite. The PXRD, powder neutron diffraction (PND), and atomic pair distribution function (PDF) refinements indicated that the substitution of K+ for [Li2OH]+ cluster led to the stabilization of the cubic phase and lattice contraction. Both bond-valence site energy (BVSE) and ab initio molecular dynamics (AIMD) calculations reveal the advantages of (Li2OH)0.99K0.01Cl over Li2OHCl in three-dimensional migration trajectories from the perspective of ionic transport mechanism. Furthermore, the Li||Li symmetric cell employing (Li2OH)0.99K0.01Cl exhibits stable cycling performance at 80 °C over 500 h, at current densities of 0.1 mA cm‒1 (with an areal capacity of 0.05 mAh cm‒1) and 0.2 mA cm‒1 (with an areal capacity of 0.1 mAh cm‒1). By combining (Li2OH)0.99K0.01Cl electrolyte with the excess Li-metal anode and the LiFePO4 (LFP) cathode (loading of 1.78 mg cm‒2), we report an ASSLB achieving a specific capacity of 116.4 mAh g‒1 with a capacity retention of 96.1% by the 150th cycle when operated at 80 mA g‒1 and 120 °C.
Results and discussion
Structure determination
The phase structures of antiperovskite were distinctly transformed by K-doping (Fig. 1a), and the PXRD patterns of Li2OHCl and (Li2OH)1‒xKxCl at RT (~25 °C) are presented in Fig. 1b. For Li2OHCl, all peaks are assigned to the orthorhombic phase (Pmc21 space group) without any other distinct impurities. In contrast, the patterns of (Li2OH)1‒xKxCl with K-doping exhibit distinct cubic phase (\({Pm}\bar{3}m\) space group) characteristics, which indicates that K-doping makes (Li2OH)1‒xKxCl maintain the higher crystal symmetry. The in situ PXRD patterns of Li2OHCl in the range between 30 and 100 °C are shown in Fig. 1c, which indicates that Li2OHCl underwent a reversible phase transition between 40 and 50 °C. Taking the peaks at 30° to 35° 2θ as examples, the distinct three peaks (orthorhombic) turned into a sharp single peak (cubic), when the temperature rose from 40 to 50 °C. On the other hand, (Li2OH)0.99K0.01Cl remains the same PXRD pattern characteristics of cubic phase in the range between 30 and 100 °C (Fig. 1d).
a Schematic diagram of cubic phase of antiperovskite stabilized by K-doping (Li in blue, O in red, H in yellow, Cl in green, K in purple). b PXRD patterns of orthorhombic Li2OHCl and cubic (Li2OH)1‒xKxCl at RT (~25 °C). c In situ PXRD patterns of Li2OHCl in the range between 30 and 100 °C. d In situ PXRD patterns of (Li2OH)0.99K0.01Cl in the range between 30 and 100 °C. e DSC curve of Li2OHCl. f DSC curve of (Li2OH)0.99K0.01Cl.
Also, the phase transition process is confirmed by the DSC results. As presented in Fig. 1e, the endothermic peak at 44 °C and exothermic peak at 27 °C corresponds to the reversible phase transition between orthorhombic phase and cubic phase of Li2OHCl, and the endothermic peak at 302 °C and exothermic peak at 290 °C represent the melting and crystallization temperature, respectively. In contrast, except for melting and crystallization peaks, there are no other peaks for (Li2OH)0.99K0.01Cl (Fig. 1f), which indicates that there is no phase transition from 20 °C to melting temperature. Besides, as the concentration of K-doping increases, the melting point decreases from 301 °C ((Li2OH)0.99K0.01Cl) to 295 °C ((Li2OH)0.9K0.1Cl) (Supplementary Fig. 1), which may be attributed to the fact that K+ ions disturbed the original ordering lattice arrangement in Li2OHCl and reduced the lattice energy33.
To gain an in-depth understanding of the relationship between K-doping and the lattice structures, the PXRD, PND, and PDF data were analyzed by structure refinements, respectively. As presented in Fig. 2a‒c, all the PXRD, PND, and PDF data can be well simulated by the orthorhombic Li2OHCl or cubic (Li2OH)1‒xKxCl (see Supplementary Tables 1–12 for detailed crystallographic information). For orthorhombic Li2OHCl, the crystal structure can be refined by the space group PmC21 (No. 26). The Li+ occupy two different Wyckoff positions (2a and 2b) and the OH‒ ions are coordinated square-planarly by Li+ ions, which leads to a highly anisotropic and 2D structure (Figs. 1a, 2d). The H atoms occupy Wyckoff positions 4c around the O atom and have four possible crystallographic equivalent positions according to the PND data. For cubic (Li2OH)1‒xKxCl, the lattices possess the higher symmetry and can be characterized by the space group \({Pm}\bar{3}m\) (No. 221). The OH‒ ions are coordinated by Li+ ions, forming [Li6OH] octahedra with one-third of Li vacancies for charge balance (Figs. 1a, 2d). The H atoms occupy Wyckoff positions 6e and 12i, and split into eighteen possible crystallographic equivalent positions according to the PND data. Unconventionally, as the foreign ions, the doping mechanism of K+ ions in cubic (Li2OH)1‒xKxCl needs to be discussed carefully. Firstly, K and Li pertain to the congeners with similar chemical properties, so it seems logical to consider that K replaces the lattice site of Li and leads to the increase in cell size. Unexpectedly, with the increase of K doping (as shown in the EDS and XPS results of Fig. 3b, c), the lattice parameters obtained from PXRD and PND consistently decrease (Fig. 3a), which indicates that K may not occupy the Li sites. Also, the same interesting results are observed in (Li2OH)1‒xKxBr system (Supplementary Fig. 2). Secondly, it is assumed that K replaces Li in the antiperovskite lattice. The simulated PXRD according to the assumed structure model presents distinctly different characteristics from the observed (e.g., the relative intensity of the diffraction peaks from 40° to 60°, Supplementary Fig. 3), which negates this hypothesis from the side. Thirdly, when refining the occupancy of O separately, it is always greater than 1.0, which indicates that there may be a larger atom at this site. Meanwhile, more Li vacancies emerge with the increase of K-doping according to the refinement results of PND. Hence, we infer that K+ ions may be located at (0, 0, 0) site and replace the [Li2OH]+ cluster in [Li6OH] octahedron (with one-third of Li vacancies), which leads to the disappearance of the original six coordination structure between OH‒ and Li+ (Fig. 3d, e). It should be noted that the two unsubstituted Li+ of [Li6OH] octahedron remain in the lattice and still coordinate with OH‒ in other adjacent octahedra, and (Li2OH)1‒xKxCl with K+ substituted [Li2OH]+ cluster is charge balanced overall. Fourthly, the partial PDF data (Supplementary Figs. 4, 5) indicate that the nearest anion to K+ is Cl‒, and it can be approximated that the coordination environment of K+ in (Li2OH)1‒xKxCl is similar to that in KCl (space group: \({Pm}\bar{3}m\), Materials Project34, No. mp-23289). Hence, the bonding mode between K+ and Cl‒ also implies the formation of solid solution (Li2OH)1-xKxCl. Likewise, a similar mechanism has been reported in previous work, in which I‒ ions substitute BH4‒ tetrahedral clusters and stabilize the metastable superionic phase of LiBH4 at RT35,36,37,38. Fifthly, the tolerance factor (0.794) of Li2OHCl is out of the stable range from 0.8 to 1.0 (Eq. 1) and close to the lower range value, where RLi is the radius of Li+ (0.76 Å), RCl is the radius of Cl‒ (1.81 Å), and ROH is the radius of OH‒ (1.53 Å)39,40. While the radius of K+ (1.38 Å) is smaller than that of OH‒ in (Li2OH)1‒xKxCl, which contributes to the tolerance factor changing towards the stable range of cubic perovskite-type structure. Also, the formation energy (Ef) of (Li2OH)26KCl27 supercell (3 × 3 × 3) is calculated to be ‒0.599 eV, indicating that the proposed structural model of K+ replacing [Li2OH]+ cluster in (Li2OH)1‒xKxCl is reasonable. Therefore, based on the analysis of PXRD, PND, and PDF data, it can be concluded that the doping of K+ ions in the antiperovskite lattice causes the unconventional double effects, that is, the stabilization of metastable cubic phase and the contraction of lattice (Fig. 3e). It is noteworthy that the doping mechanism involving K+ ions in (Li2OH)1‒xKxCl significantly differs from that of F‒ ions in Li2OHCl0.9F0.1 of our previously reported work41, despite both lattice manipulation methods enabling the transformation of antiperovskite electrolytes from orthorhombic to cubic phase. In the case of Li2OHCl0.9F0.1, F‒ ions are conventionally introduced into the lattice to replace Cl‒ ions. Whereas, K+ ions substitute for the [Li2OH]+ clusters in an unconventional manner in (Li2OH)1‒xKxCl lattice to form a solid solution.
a The Rietveld refinements of PXRD data of orthorhombic Li2OHCl and cubic (Li2OH)1‒xKxCl. b The Rietveld refinements of PND data of orthorhombic Li2OHCl and cubic (Li2OH)1‒xKxCl. c The small-box least-square refinements of PDF data of orthorhombic Li2OHCl and cubic (Li2OH)1‒xKxCl. d The crystal structure of orthorhombic Li2OHCl and cubic (Li2OH)1‒xKxCl according to the refinement results.
a The lattice parameters of (Li2OH)1‒xKxCl decreases with the increase of K-doping according to the PXRD and PND data. b The energy-dispersive X-ray spectroscopy (EDS) analysis of K in (Li2OH)1‒xKxCl, and the error bars represent the standard deviation obtained by three independent measurements. c The X-ray photoelectron spectroscopy (XPS) of K 2P in (Li2OH)1‒xKxCl. d The unit cell of cubic (Li2OH)1‒xKxCl. e Illustration of lattice contraction and cubic phase stabilization induced by K-doping.
Ionic conductivity
The ionic conductivities of (Li2OH)1‒xKxCl electrolytes were assessed through temperature-dependent EIS. The Nyquist plots, as shown in Supplementary Fig. 6, indicate the current response of SSEs to a voltage disturbance at various frequencies and temperatures. Using the Nyquist curve of (Li2OH)0.99K0.01Cl at 25 °C as an illustrative example (Supplementary Fig. 7), it presents a characteristic semicircle pattern at high frequencies indicating the series combination of bulk and grain boundary resistance, and the linear segment at low frequencies signifying ion blocking electrode. When fitting the plot using the equivalent circuit, it yields a total resistance (R) of 25.529 kΩ, comprising a bulk resistance (Rb) of 529 Ω and a grain boundary resistance (Rgb) of 25.0 kΩ. Subsequently, the ionic conductivity can be calculated as 4.5 × 10‒3 mS cm‒1 using the formula σ = D/(Rπr2), where D (∼0.9 mm), R (∼25.529 kΩ), r (∼0.5 cm) represent the thickness, total resistance, and radius of the (Li2OH)0.99K0.01Cl electrolyte, respectively.
Figure 4a displays Arrhenius plots for the (Li2OH)1‒xKxCl electrolytes indicating the correlation between ionic conductivity and temperature within the temperature range of 25 and 120 °C. For Li2OHCl, after undergoing the phase transition from the orthorhombic to the cubic at 44 °C (Fig. 1c–e), both the ionic conductivity in the reported work26 and this work exhibit a sharp increase. Noteworthily, due to the presence of LiCl impurity (about 30°, 35° 2θ) in Li2OHCl previously reported, its ionic conductivity is lower than in this work. For (Li2OH)1‒xKxCl, because the cubic phase is always kept in the range from 25 to 120 °C, the ionic conductivities increase steadily and linearly with the increase in temperature. In particular, the ionic conductivity of (Li2OH)0.99K0.01Cl is significantly increased to 4.5 × 10‒3 mS cm‒1 at 25 °C, which is 2 orders of magnitude higher than that of Li2OHCl previously reported (1.7 × 10‒5 mS cm‒1)26 and 32 times higher than that of Li2OHCl in this work (1.37 × 10‒4 mS cm‒1). Besides, the activation energies of cubic Li2OHCl and (Li2OH)1‒xKxCl are obtained from the slope in the Arrhenius plots based on the formula: σ = A exp (‒Ea/kBT). In which σ is the ionic conductivity, A is the preexponential parameter, Ea is the activation energy, T is absolute temperature, and kB is the Boltzmann constant. Meanwhile, the activation energies increase as the concentration of K-doping increases, from 0.56 eV ((Li2OH)0.99K0.01Cl) to 0.62 eV ((Li2OH)0.9K0.1Cl).
a The Arrhenius ionic conductivity plots of antiperovskite in the temperature range from 25 to 120 °C, the ionic conductivity data of Li2OHCl (black) are reproduced from the work of Z. D. Hood et al.26. b Schematic diagram of nonequivalent sites for Li+ ions transport in the orthorhombic lattice. c Schematic diagram of equivalent sites for Li+ ions transport in the cubic lattice, Li+ ions in blue, Cl‒ ions in green. d The activation energy of (Li2OH)1‒xKxCl increases with the increase of K-doping, and the error bars represent the standard deviation calculated by linearly fitting the Arrhenius ionic conductivity plots. e The ionic conductivity of (Li2OH)1‒xKxCl decreases with the increase of K-doping. f The Li–O bond distance of (Li2OH)1‒xKxCl decreases with the increase of K-doping according to the PDF data.
The above ionic conductivity results could be understood from the perspective of lattice structure. Generally, the ionic conductivity of metastable phase is higher than that of stable phase. For example, the ionic conductivity of Li7La3ZrO12 (LLZO) was remarkably improved after the metastable cubic phase was stabilized by Al/Ta doping at RT31,32. This is because, with the higher symmetry, the cubic LLZO lattice possesses more Li equivalent sites, which is beneficial for Li-ions to transport to multiple vacancy directions42. Moreover, lattice vacancy is another important factor affecting the transport of Li+ ions8. According to the crystallographic information (Supplementary Tables 1–12), the occupancy of Li1 and Li2 in orthorhombic Li2OHCl is close to 1. In comparison, there are about one-third of Li vacancies in cubic (Li2OH)1‒xKxCl, which is helpful for the transport of Li+ ions in the lattice. Therefore, with more Li equivalent sites and more Li vacancies (Fig. 4b, c), the ionic conductivity of (Li2OH)1‒xKxCl is distinctly higher than that of Li2OHCl at RT. On the other hand, a longer Li-anion bond usually means a wider diffusion pathway and a weaker interaction force between Li and anion43. According to the PDF data, the Li-O bond length of (Li2OH)1‒xKxCl increases with the decrease of K-doping (Fig. 4f). Hence, the lattice of (Li2OH)0.99K0.01Cl is more favorable for the transport of Li+ ions with the lowest activation energy of 0.56 eV (Fig. 4d), leading to the highest ionic conductivity of 4.5 × 10‒3 mS cm‒1 at 25 °C (Fig. 4e). It should be noted that the ionic conductivity of (Li2OH)0.99K0.01Cl is slightly higher than that of cubic Li2OHCl after phase transition, which may be attributed to a small number of cluster defects caused by K-doping, and there may be a mutual restriction relationship between cluster defects and Li-O bond length in affecting ionic conductivity of (Li2OH)1‒xKxCl.
Besides, the migration pathways of Li+ ions and associated energy barriers were calculated by the BVSE method. In the case of orthorhombic Li2OHCl, as previously demonstrated in our studies41, the [Li1-Li2-Li1] trajectory in a–c plane has been identified as a favorable pathway for the transport of Li+ ions, featuring an effective barrier of 0.513 eV. However, the 3D long-range migration of Li+ ions along [Li1-Li1] trajectory requires overcoming a higher barrier of 0.832 eV. This finding underscores that the dominant mode of Li+ ions transport in Li2OHCl occurs within the 2D plane. In contrast, for (Li2OH)0.99K0.01Cl in this study (Fig. 5a–c), the isotropic [Li1-Li1] trajectory forms a 3D percolating network with an effective migration barrier of 0.326 eV, resulting in the much higher ionic conductivity. Indeed, the merits of the 3D transport pathway have been exemplified in the cubic Li2OHCl0.9F0.1 structure in our prior study41, which corresponds to the Li+ ions migration barrier of 0.439 eV. However, due to the stronger Li‒F bonds introduced by F-doping compared to the original Li‒Cl bonds, the barrier that needs to be overcome for Li+ ions migration along the [Li1-Li1] trajectory in Li2OHCl0.9F0.1 (0.439 eV) is higher than that in (Li2OH)0.99K0.01Cl (0.326 eV). Also, AIMD calculations embody the advantages of cubic K-doped antiperovskite in 3D migration trajectories. As shown in Fig. 5d, f, Li atoms trajectories in the orthorhombic Li2OHCl show a local distribution around the lattice sites, and the MSD of Li atoms keeps steady with the simulation time. In contrast, Li atoms in cubic K-doped antiperovskite lattice exhibit significant dispersion characteristics and 3D migration trajectories (Fig. 5e), and the MSD of Li atoms is obviously higher than that of other atoms (Fig. 5g), which indicates that the ionic conductivity measured in experiments is attributed to Li+ diffusion. Coincidentally, the nuclear density maps derived from PND data using the maximum entropy method (MEM) also confirm the characteristics of the 3D transport path of Li+ ions in cubic (Li2OH)0.99K0.01Cl from experimental evidence (Supplementary Fig. 8).
a, b BVSE analysis for cubic (Li2OH)0.99K0.01Cl with the Li+ ions potential map, in which the dotted lines represent the topology of the Li+ ions migration pathways. c Energy profile of Li+ ions pathways in (Li2OH)0.99K0.01Cl as estimated from the BVSE models. d, e AIMD calculations: trajectories of Li atoms in orthorhombic lattice and cubic K-doped lattice. f, g MSD of different atoms in orthorhombic lattice and cubic K-doped lattice.
Electrochemical performance of (Li2OH)0.99K0.01Cl
In addition to demonstrating the high ionic conductivity of (Li2OH)0.99K0.01Cl, its electrochemical performance was systematically studied. As presented in Fig. 6a–c, the Li|(Li2OH)0.99K0.01Cl|Li symmetric cell remained stable after long-term galvanostatic cycling (current density of 0.1 mA cm‒2, areal capacity of 0.05 mAh cm‒2, 500 h; current density of 0.2 mA cm‒2, areal capacity of 0.1 mAh cm‒2, 500 h) at 80 °C without any distinct polarization. Moreover, a critical current density (CCD) test was conducted on (Li2OH)0.99K0.01Cl to investigate the short-circuit tolerance (Fig. 6d). With the increase of the current density from 0.05 mA cm‒2 to 0.7 mA cm‒2, the cell voltage increased steadily from 12 mV to 173 mV.
a The galvanostatic cycling of Li|(Li2OH)0.99K0.01Cl|Li symmetric cell at the current density of 0.1 mA cm‒2 (areal capacity of 0.05 mAh cm‒2, 500 h) and 0.2 mA cm‒2 (areal capacity of 0.1 mAh cm‒2, 500 h). b, c Insets of the specific period of the galvanostatic cycling. d The critical current density (CCD) test for investigating the short-circuit tolerance of (Li2OH)0.99K0.01Cl. The Li||Li symmetric cell was applied with a gradually increasing current density and was charged or discharged for 30 min at each current density during the CCD test. e The CV curve of (Li2OH)0.99K0.01Cl in the range of ‒0.5 to 3.5 V (versus Li/Li+) at the scanning rate of 1 mV s‒1. f The LSV curve of (Li2OH)0.99K0.01Cl at the scanning rate of 1 mV s‒1 and starting at the open-circuit voltage (∼2.1 V) (versus Li/Li+). All of the above electrochemical tests were performed at 80 °C.
After that, the cell voltage fluctuated unsteadily and dropped to a lower value, which indicates that (Li2OH)0.99K0.01Cl can tolerate a current density of 0.7 mA cm‒2 before short-circuit. Both cyclic voltammetry (CV) and linear sweep voltammetry (LSV) were carried out at 80 °C and the scan rate of 1 mV S‒1 to investigate the electrochemical stability of (Li2OH)0.99K0.01Cl. For the CV test (Fig. 6e), the scanning curve is highly stable in the range of ‒0.5-3.5 V (vs. Li/Li+), indicating the (Li2OH)0.99K0.01Cl electrolyte is stable enough to resist reduction by Li-metal. For the LSV test (Fig. 6f), the scanning curve shows that the current increases suddenly at 4.0 V (vs. Li/Li+), corresponding to the oxidative decomposition of (Li2OH)0.99K0.01Cl. Therefore, the (Li2OH)0.99K0.01Cl electrolyte is stable in the voltage range of ‒0.5 to 4.0 V (vs. Li/Li+) according to the results of CV and LSV, which suggests that it is suitable for ASSLBs with charging voltage below 4.0 V (e.g., Li|SSEs|LFP ASSLBs).
Performance of Li|(Li2OH)0.99K0.01Cl|LiFePO4 ASSLB
As shown in Fig. 7a, b, the charge–discharge tests of Li|(Li2OH)0.99K0.01Cl|LFP ASSLB present excellent stability, low polarization, and reversibility of redox reactions in a 2.9–3.8 V range. The cell exhibits a capacity retention of 96.1% by the 150th cycle with a specific capacity of 116.4 mAh g‒1 when operated at a specific current of 80 mA g‒1 and 120 °C, and there are no obvious changes in the shape of the voltage signatures (Fig. 7b). Overall, the ASSLB employing (Li2OH)0.99K0.01Cl electrolyte exhibits long-term stable cycling performance. More importantly, no liquid electrolyte or interface modification layer was introduced in any preparation process of the cell, in contrast to the majority of other solid-state battery studies44,45,46,47.
a The cycling performance of Li|(Li2OH)0.99K0.01Cl|LFP ASSLB at the specific current of 80 mA g‒1 (current density of 0.18 mA cm‒2) and 120 °C. b The voltage profiles of Li|(Li2OH)0.99K0.01Cl|LFP ASSLB cycled between 2.9 and 3.8 V. c The three-dimensional images of Li|(Li2OH)0.99K0.01Cl|LFP ASSLB obtained by CT scanning. d The cross-sectional morphology of the interface between LFP cathode and (Li2OH)0.99K0.01Cl electrolyte observed by SEM. e The cross-sectional morphology of the interface between Li-metal anode and (Li2OH)0.99K0.01Cl electrolyte observed by SEM.
Furthermore, the Li|SSE|LFP cell was disassembled to observe the volume distribution and the morphology of SSE-electrode interfaces after cycles. As presented in Fig. 7c, the three-dimensional images obtained by computed X-ray tomography (CT) scanning exhibit the integrity of Li|(Li2OH)0.99K0.01Cl|LFP ASSLB in volume distribution, without structural damage and interface failure. Also, good adhesion can be observed in the transition region between (Li2OH)0.99K0.01Cl and Li metal anode (Fig. 7d), as well as the transition region between (Li2OH)0.99K0.01Cl and LFP cathode (Fig. 7e). In particular, the (Li2OH)0.99K0.01Cl bulk shows good uniformity and density without obvious porosity and graininess only by cold pressing and heating treatment at 120 °C. This rare advantage indicates that the low melting point of antiperovskite SSEs is favorable for its densification with low-energy consumption, unlike garnet19 and NASICON11 SSEs that need about 1000 °C sintering temperature to densify.
Methods
Material synthesis
The (Li2OH)1‒xKxCl (0 ≤ x ≤ 0.1) were prepared by simply grinding stoichiometric amounts of LiOH (>99%), LiCl (>99%), and KOH(>99%) and one-step heating to 400 °C at the rate of 5 °C min‒1 for 1 h in a nickel crucible. Then the molten products were quenched to room temperature into another empty nickel crucible. All the above preparations were performed under Ar atmosphere.
Material characterizations and analysis
PXRD measurements were conducted on a Rigaku SmartLab 9 kW diffractometer with Cu Kα radiation (λ = 1.5406 Å) to analyze the structures of (Li2OH)1‒xKxCl. All samples were sealed with Kapton film under the inert atmosphere before PXRD measurements. During the in situ PXRD testing in the temperature range of 30–100–30 °C, the samples were sealed in a vacuum chamber with an X-ray transparent beryllium window. The PND was measured at the Multiple Physics Instrument at the China Spallation Neutron Source (0.1–3 Å of wavelength range), and each sample was sealed in a Ti–Zr tube with a diameter of 8.9 mm. The Bank 6 PND data was selected for refinement because of its high resolution and wide d-spacing range (0.4–2.4 Å). DSC analysis was conducted on a NETZSCH STA 449 instrument, and samples were sealed in aluminum crucible under N2 atmosphere with a heating and cooling rate of 5 °C/min. X-ray photoelectron spectroscopy (XPS) was recorded on a PHI 5000 VersaProbe II spectrometer with Al Kα X-rays. Field emission scanning electron microscopy (SEM, Hitachi SU8230) was used to observe the cross-sectional morphology of the interface between SSE and electrode, which was equipped with a liquid-nitrogen-cooled silicon detector to perform the energy-dispersive X-ray spectroscopy (EDS). PXRD and PND Rietveld refinements were performed by the Fullprof software48 to analyze the space group, crystal lattice parameters, and atom locations of antiperovskite Li2OHCl and (Li2OH)1‒xKxCl. In order to verify the PXRD results and confirm the effect of K-doping on the lattice structures of (Li2OH)1‒xKxCl, the X-ray total scattering was performed on the PANalytical Empyrean powder diffractometer with Ag Kα radiation (0.559 Å) and GaliPIX3D detector at RT. The sample was sealed into a glass capillary with a diameter of 1.0 mm. The total scattering data were collected in the range from 2 to 140° in 17 h. The obtained coherent X-ray scattering data IC(Q) was converted into the structure-function S(Q), and the structure-function S(Q) was Fourier transformed into PDF with a Q range of 0.4−20 Å−149. The PDF refinements were performed by PDFgui50.
Computational methods
BVSE calculations were used to simulate Li+ ions migration pathways and evaluate migration barrier heights and performed with the softBV program51,52 using the structure models according to the Rietveld refinement data. Bond-valence site energy landscapes of a test Li+ ion were calculated for a 3D grid of points with a resolution of 0.1 Å. Details about the softBV approach and the type of force field employed for the BVSE calculations can be found elsewhere51,52. The AIMD calculations were carried out by using the projector augmented wave method in the framework of the density functional theory (DFT) as implemented in the Vienna ab-initio Simulation Package (VASP)53 and performed by using the Verlet algorithm and the NVT ensemble with a Nosé−Hoover thermostat at 550 K54. A system contains 3 × 3 × 3 supercell ((Li2OH)26KCl27) was used for the AIMD calculations of cubic K-doped antiperovskite, and the simulation cell for orthorhombic system was constructed from a 2 × 2 × 3 replication of the orthorhombic Li2OHCl unit cell. The plane-wave energy cutoff of 520 eV was chosen for AIMD simulations. The time step was set to 1 fs, and all supercell systems were simulated for 60 ps after an initial 2 ps equilibration period, and a 1 × 1 × 1 k-mesh grid was used for the Brillouin-zone sampling. The mean-squared displacement (MSD) data were extracted from the AIMD trajectories of atoms. The maximum entropy method (MEM) analysis was performed with the program Dysnomia55 using an input file containing observed structure factors from the NPD data of Bank 6. Visualization of nuclear densities and extraction of 2D displays was then performed in the program Vesta56. The formation energy (Ef) is calculated from the energy difference between cubic Li2OHCl and K-doped structure (Eq. 2) to demonstrate the validity of (Li2OH)1‒xKxCl structure model.
where E[(Li2OH)27Cl27], E[(Li2OH)26KCl27], E[LiOH], and E[KOH] represent the DFT energies of Li2OHCl supercell (3 × 3 × 3), K-doped supercell (3 × 3 × 3), LiOH bulk phase and KOH bulk phase, respectively.
Cell assembly and electrochemical measurements
Ionic conductivities in the temperature range of 25–120 °C were obtained from electrochemical impedance spectroscopy (EIS) at frequencies from 1 Hz to 1 MHz. Before the EIS measurements, Li2OHCl and (Li2OH)1‒xKxCl powders (~140 mg) were pressed into pellets by 480 MPa pressure in an insulative mold (inner diameter = 10 mm), and two stainless-steel rods were clamped on both sides of the pellet as the current collectors. The electrochemical stability window of (Li2OH)0.99K0.01Cl was determined by cyclic voltammetry (CV) and linear sweep voltammetry (LSV) measurements. In the CV and LSV tests, the SSE pellets were sealed in 2032 coin-type cells, Li metal was used as the counter electrode and Au foil (diameter of 9 mm) was used as the working electrode. The CV was measured between ‒0.5 V and 3.5 V (versus Li/Li+) at a scanning rate of 1 mV/s at 80 °C, and LSV was measured from open-circuit voltage (~2.1 V) to 5 V (versus Li/Li+) at a scanning rate of 1 mV/s at 80 °C. All the above measurements were performed on an electrochemical workstation analyzer (AUTOLAB M204).
The Li|SSE|Li symmetric batteries were sealed in 2032 coin-type cells and then carried out at different current densities at 80 °C. Before assembling the Li|SSE|Li symmetric cells, (Li2OH)0.99K0.01Cl powders (~100 mg) were pressed into SSE pellets in a stainless-steel mold (inner diameter = 9 mm), and then heated at 280 °C for 10 h for densification. The ASSLBs were assembled in polyether-ether-ketone (PEEK) molds by employing LFP as cathode, together with Li-metal anode and (Li2OH)0.99K0.01Cl SSE located between the cathode and the anode. For the cathode electrodes, the commercial LFP powders were mixed with the Li3InCl6 SSE powders (MTI Corp.) with a weight ratio of 70: 30 by grinding for 30 min. The ASSLBs were fabricated as follows: 70 mg of the (Li2OH)0.99K0.01Cl powders were pressed under 240 MPa to form an SSE layer with a thickness of around 400 μm. Then, 2 mg of cathode composite powders were spread onto the side of the SSE layer and pressed under 480 MPa. Finally, the Li foil (thickness of 100 µm, diameter of 9 mm and areal capacity of 20.6 mAh cm‒2) was attached to the other side of the SSE layer by pressing under 50 MPa to assemble the integrated ASSLB. After 12 h annealing at 120 °C for densification of SSE in the PEEK mold, the galvanostatic charge–discharge cycling of ASSLBs was carried out between 2.9 and 3.8 V at 120 °C. All the above measurements were conducted on the Wuhan Land battery tester.
Reporting summary
Further information on research design is available in the Nature Portfolio Reporting Summary linked to this article.
Data availability
The source data used in this study are available from Figshare (https://doi.org/10.6084/m9.figshare.22811984).
References
Quartarone, E. & Mustarelli, P. Electrolytes for solid-state lithium rechargeable batteries: Recent advances and perspectives. Chem. Soc. Rev. 40, 2525–2540 (2011).
Gao, Z. et al. Promises, challenges, and recent progress of inorganic solid-state electrolytes for all-solid-state lithium batteries. Adv. Mater. 30, 1705702 (2018).
Schwietert, T. K. et al. Clarifying the relationship between redox activity and electrochemical stability in solid electrolytes. Nat. Mater. 19, 428–435 (2020).
Fan, L., Wei, S., Li, S., Li, Q. & Lu, Y. Recent progress of the solid-state electrolytes for high-energy metal-based batteries. Adv. Energy Mater. 8, 1702657 (2018).
Kim, K. J., Balaish, M., Wadaguchi, M., Kong, L. & Rupp, J. L. M. Solid-state Li–metal batteries: challenges and horizons of oxide and sulfide solid electrolytes and their interfaces. Adv. Energy Mater. 11, 2002689 (2021).
Balaish, M. et al. Processing thin but robust electrolytes for solid-state batteries. Nat. Energy 6, 227–239 (2021).
Kraft, M. A. et al. Inducing high ionic conductivity in the lithium superionic argyrodites Li6+xP1–xGexS5I for all-solid-state batteries. J. Am. Chem. Soc. 140, 16330–16339 (2018).
Adeli, P. et al. Boosting solid-state diffusivity and conductivity in lithium superionic argyrodites by halide substitution. Angew. Chem. Int. Ed. Engl. 58, 8681–8686 (2019).
Liu, Z. et al. Anomalous high ionic conductivity of nanoporous beta-Li3PS4. J. Am. Chem. Soc. 135, 975–978 (2013).
Hayashi, A., Noi, K., Sakuda, A. & Tatsumisago, M. Superionic glass-ceramic electrolytes for room-temperature rechargeable sodium batteries. Nat. Commun. 3, 856 (2012).
Hou, M., Liang, F., Chen, K., Dai, Y. & Xue, D. Challenges and perspectives of NASICON-type solid electrolytes for all-solid-state lithium batteries. Nanotechnology 31, 132003 (2020).
Zhou, Q. et al. NASICON Li1.2Mg0.1Zr1.9(PO4)3 solid electrolyte for an all-solid-state Li-metal battery. Small Methods 4, 2000764 (2020).
Murugan, R., Thangadurai, V. & Weppner, W. Fast lithium ion conduction in garnet-type Li7La3Zr2O12. Angew. Chem. Int. Ed. Engl. 46, 7778–7781 (2007).
Zhao, N. et al. Solid garnet batteries. Joule 3, 1190–1199 (2019).
Wang, Y. et al. Antiperovskites with exceptional functionalities. Adv. Mater. 32, 1905007 (2020).
Zhao, Y. & Daemen, L. L. Superionic conductivity in lithium-rich anti-perovskites. J. Am. Chem. Soc. 134, 15042–15047 (2012).
Gao, L. et al. Mechanism of enhanced ionic conductivity by rotational nitrite group in antiperovskite Na3ONO2. J. Mater. Chem. A 8, 21265–21272 (2020).
Campanella, D., Belanger, D. & Paolella, A. Beyond garnets, phosphates and phosphosulfides solid electrolytes: New ceramic perspectives for all solid lithium metal batteries. J. Power Sources 482, 228949 (2021).
Wang, C. et al. Garnet-type solid-state electrolytes: Materials, interfaces, and batteries. Chem. Rev. 120, 4257–4300 (2020).
Gao, L. et al. Antiperovskite ionic conductor layer for stabilizing the interface of NASICON solid electrolyte against Li metal in all-solid-state batteries**. Batteries & Supercaps 4, 1491–1498 (2021).
Chung, H. & Kang, B. Mechanical and thermal failure induced by contact between a Li1.5Al0.5Ge1.5(PO4)3 solid electrolyte and Li metal in an all-solid-state Li cell. Chem. Mater. 29, 8611–8619 (2017).
Hartmann, P. et al. Degradation of NASICON-type materials in contact with lithium metal: Formation of mixed conducting interphases (MCI) on solid electrolytes. J. Phys. Chem. C 117, 21064–21074 (2013).
Zhang, Q. et al. Sulfide-based solid-state electrolytes: Synthesis, stability, and potential for all-solid-state batteries. Adv. Mater. 31, 1901131 (2019).
Gao, S. et al. Hydride-based antiperovskites with soft anionic sublattices as fast alkali ionic conductors. Nat. Commun. 12, 201 (2021).
Guo, L. et al. The electrolysis of anti-perovskite Li2OHCl for prelithiation of high-energy-density batteries. Angew. Chem. Int. Ed. 60, 13013–13020 (2021).
Hood, Z. D., Wang, H., Samuthira Pandian, A., Keum, J. K. & Liang, C. Li2OHCl crystalline electrolyte for stable metallic lithium anodes. J. Am. Chem. Soc. 138, 1768–1771 (2016).
Yin, L., Yuan, H., Kong, L., Lu, Z. & Zhao, Y. Engineering Frenkel defects of anti-perovskite solid-state electrolytes and their applications in all-solid-state lithium-ion batteries. Chem. Commun. 56, 1251–1254 (2020).
Famprikis, T., Canepa, P., Dawson, J. A., Islam, M. S. & Masquelier, C. Fundamentals of inorganic solid-state electrolytes for batteries. Nat. Mater. 18, 1278–1291 (2019).
Xiao, Y. et al. Electrolyte melt infiltration for scalable manufacturing of inorganic all-solid-state lithium-ion batteries. Nat. Mater. 20, 984–990 (2021).
Wang, F. et al. Dynamics of hydroxyl anions promotes lithium ion conduction in antiperovskite Li2OHCl. Chem. Mater. 32, 8481–8491 (2020).
Rangasamy, E., Wolfenstine, J. & Sakamoto, J. The role of Al and Li concentration on the formation of cubic garnet solid electrolyte of nominal composition Li7La3Zr2O12. Solid State Ion. 206, 28–32 (2012).
Buschmann, H., Berendts, S., Mogwitz, B. & Janek, J. Lithium metal electrode kinetics and ionic conductivity of the solid lithium ion conductors “Li7La3Zr2O12” and Li7−xLa3Zr2−xTaxO12 with garnet-type structure. J. Power Sources 206, 236–244 (2012).
Liu, J. et al. Impact of doping on bonding energy hierarchy and melting of phase change materials. J. Appl. Phys. 124, 094503 (2018).
Jain, A. et al. Commentary: The Materials Project: A materials genome approach to accelerating materials innovation. APL Mater. 1, 011002 (2013).
Maekawa, H. et al. Halide-stabilized LiBH4, a room-temperature lithium fast-ion conductor. J. Am. Chem. Soc. 131, 894–895 (2009).
Miyazaki, R. et al. Room temperature lithium fast-ion conduction and phase relationship of LiI stabilized LiBH4. Solid State Ion. 192, 143–147 (2011).
Sveinbjörnsson, D. et al. Effect of heat treatment on the lithium ion conduction of the LiBH4–LiI solid solution. J. Phys. Chem. C 117, 3249–3257 (2013).
Matsuo, M. et al. Lithium superionic conduction in lithium borohydride accompanied by structural transition. Appl. Phys. Lett. 91, 224103 (2007).
Ahrens, L. H. The use of ionization potentials Part 1. Ionic radii of the elements. Geochim. Cosmochim. Acta 2, 155–169 (1952).
Hagg, G. Structural inorganic chemistry by A. F. Wells. Acta Crystallogr. 15, 921 (1962).
Gao, L. et al. Effects of fluorination on crystal structure and electrochemical performance of antiperovskite solid electrolytes. J. Energy Chem. 77, 521–528 (2023).
Thangadurai, V., Narayanan, S. & Pinzaru, D. Garnet-type solid-state fast Li ion conductors for Li batteries: Critical review. Chem. Soc. Rev. 43, 4714–4727 (2014).
Abakumov, A. M., Fedotov, S. S., Antipov, E. V. & Tarascon, J. M. Solid state chemistry for developing better metal-ion batteries. Nat. Commun. 11, 4976 (2020).
Cheng, Q. et al. Stabilizing solid electrolyte-anode interface in Li-metal batteries by boron nitride-based nanocomposite coating. Joule 3, 1510–1522 (2019).
Ye, L. & Li, X. A dynamic stability design strategy for lithium metal solid state batteries. Nature 593, 218–222 (2021).
Shi, K. et al. In situ construction of an ultra-stable conductive composite interface for high-voltage all-solid-state lithium metal batteries. Angew. Chem. Int. Ed. Engl. 59, 11784–11788 (2020).
Zhou, W. et al. Plating a dendrite-free lithium anode with a polymer/ceramic/polymer sandwich electrolyte. J. Am. Chem. Soc. 138, 9385–9388 (2016).
Rodriguez-Carvajal, J. Recent developments of the program FULLPROF, commission on powder diffraction. IUCr Newsl. 26, 12–19 (2001).
Juhas, P., Davis, T., Farrow, C. L. & Billinge, S. J. L. PDFgetX3: A rapid and highly automatable program for processing powder diffraction data into total scattering pair distribution functions. J. Appl. Crystallogr. 46, 560–566 (2013).
Farrow, C. L. et al. PDFfit2 and PDFgui: Computer programs for studying nanostructure in crystals. J. Phys. Condens. Matter 19, 335219 (2007).
Chen, H., Wong, L. L. & Adams, S. SoftBV-a software tool for screening the materials genome of inorganic fast ion conductors. Acta Crystallogr. B: Struct. Sci. Cryst. Eng. Mater. 75, 18–33 (2019).
Chen, H. & Adams, S. Bond softness sensitive bond-valence parameters for crystal structure plausibility tests. IUCrJ 4, 614–625 (2017).
Hafner, J. Ab-initio simulations of materials using VASP: Density-functional theory and beyond. J. Comput. Chem. 29, 2044–2078 (2008).
Csonka, G. I. et al. Assessing the performance of recent density functionals for bulk solids. Phys. Rev. B 79, 155107 (2009).
Momma, K., Ikeda, T., Belik, A. A. & Izumi, F. Dysnomia, a computer program for maximum-entropy method (MEM) analysis and its performance in the MEM-based pattern fitting. Powder Diffr. 28, 184–193 (2013).
Momma, K. & Izumi, F. VESTA 3 for three-dimensional visualization of crystal, volumetric and morphology data. J. Appl. Crystallogr. 44, 1272–1276 (2011).
Acknowledgements
This work was supported by the National Natural Science Foundation of China (51825201 and 52227802 to R.Z.), the National Natural Science Foundation of China (12275119 to S.H.), Guangdong Grants (2021ZT09C064 to S.H.), Shenzhen Science and Technology Program (KQTD20200820113047086 to J.Z.), Major Science and Technology Infrastructure Project of Material Genome Big-science Facilities Platform supported by Municipal Development and Reform Commission of Shenzhen. The authors are very grateful to W.Y., H.C.C., and Y.G.X. of the Multiple Physics Instrument at the China Spallation Neutron Source for their help in the neutron diffraction measurement.
Author information
Authors and Affiliations
Contributions
R.Z. and S.H. conceived the research, L.G. synthesized the materials, analyzed the crystal structures, conducted the electrochemical measurements under the guidance of R.Z., S.L., and L.W., H.Z. performed the XRD refinement with assistance from S.G., X.Z. performed the calculations with assistance from J.Z., L.G. analyzed the PDF and PND data under the guidance of J.Z. and Y.W., and discussed the mechanism analysis with Y.Z. and D.H., R.Z., and S.H. directed the entire study, L.G. handled the writing of the manuscript with other co-authors.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Gao, L., Zhang, X., Zhu, J. et al. Boosting lithium ion conductivity of antiperovskite solid electrolyte by potassium ions substitution for cation clusters. Nat Commun 14, 6807 (2023). https://doi.org/10.1038/s41467-023-42385-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-023-42385-1
- Springer Nature Limited