Abstract
Control and understanding of ensembles of skyrmions is important for realization of future technologies. In particular, the order-disorder transition associated with the 2D lattice of magnetic skyrmions can have significant implications for transport and other dynamic functionalities. To date, skyrmion ensembles have been primarily studied in bulk crystals, or as isolated skyrmions in thin film devices. Here, we investigate the condensation of the skyrmion phase at room temperature and zero field in a polar, van der Waals magnet. We demonstrate that we can engineer an ordered skyrmion crystal through structural confinement on the μm scale, showing control over this order-disorder transition on scales relevant for device applications.
Similar content being viewed by others
Introduction
Skyrmions are topologically nontrivial quasiparticles made up of a collection of rotating magnetic spins1,2,3 or, more recently, electric dipoles4,5. In many magnetic systems, this stems from broken inversion symmetry in the crystal, resulting in a Dzyaloshinskii-Moriya interaction (DMI), or at interfaces, leading to the Rashba effect, that can stabilize such topologically nontrivial spin configurations2,6. Due to the topological protection from weak fluctuations and the ability to manipulate them with a magnetic field or charge current, magnetic skyrmions are of significant interest for next generation information technologies7,8,9,10,11. Neuromorphic computing architectures based on skyrmions have been proposed, using the diffusion of skyrmions and the resulting magnetoresistance to carry out probabilistic computing12,13,14. Additionally, magnetic skyrmions can be used to control spins through the topological Hall effect, where an electron interacts with the Berry curvature of the skyrmion to generate an emergent electric field15,16,17. These phenomena, both skyrmion motion and the topological Hall effect, are sensitive to the ground state of the system, wherein the arrangement of the skyrmions can have significant consequences on the resulting properties6,18,19,20. A fundamental understanding and pathways to control such ensembles of skyrmions is then important for realization of advanced computational devices based on skyrmion kinetics or spin transport. In this vein, the arrangement of magnetic skyrmions becomes exciting from perspectives of both fundamental physics and device engineering.
Since their discovery, control of the shape21,22,23,24 and long range ordering25,26,27 of magnetic skyrmion ensembles has been an open challenge, often explored through magnetic field, temperature and thin film interactions. In two-dimensional (2D) systems, in the absence of structural defects or kinetic limitations, the behavior of such 2D ensembles can be described by the Hohenberg-Mermin-Wagner theorem, which states that true long-range, crystalline order cannot exist due to logarithmic fluctuations of the order parameter. This occurs because the energy associated with site displacement is small enough in 2D that the increase in entropy associated with the formation of density fluctuations becomes favorable28,29,30. An extension of this is the Kosterlitz–Thouless–Halperin–Nelson–Young (KTHNY) theory, which describes the melting of 2D objects with continuous symmetry through the unbinding of topological defects due to thermal fluctuations31,32,33. KTHNY melting is distinct from 3D phase transitions in that it proceeds from an ordered solid to a disordered liquid through a quasi-ordered hexatic phase that is present in 2D systems. The solid-to-hexatic phase transition is driven by the dissociation of dislocation pairs; when dislocations with opposite Burgers’ vectors are coupled, as in the 2D solid phase, the topology of the lattice of skyrmions remains invariant and order is preserved. Upon dissociation of the dislocations, long-range translational order is destroyed, but orientational order is preserved. The hexatic-to-liquid phase transition is then driven by thermal unbinding of these dislocations into disclinations, which destroys any remaining orientational order25,31,32,33,34,35. This quasi-long-range degree of crystallinity in the hexatic phase distinguishes it from the liquid phase quantitatively, as the orientational correlation function decays algebraically instead of exponentially (Supplementary Fig. 1).
As a 2D arrangement of quasi-particles, one could envision that the ensemble of magnetic skyrmions can be explained within the framework of the KTHNY theory. This has been observed in certain cases25, as well as in other 2D systems such as colloids, liquid crystals, atomic monolayers, and superconducting vortices34,35,36,37,38,39. The presence of crystallographic and/or magnetic disorder, however, will interfere with the ideal KTHNY behavior. Pinning sites that can affect the thermal motion and (dis)association of dislocations and disclinations will prevent model KTHNY phase transitions, and subsequently limit ordering to short-range40,41. In this way, phase transitions will be suggestive of hexatic and ordered phases, but the ordered state may not be realized on experimental timescales27,42.
It has been previously shown, using Lorentz transmission electron microscopy, that Bloch-type magnetic skyrmions in bulk, single crystal Cu2OSeO3 can undergo KTHNY-type melting with a magnetic field25. Additionally, skyrmion ordering has been studied in the ultrathin magnetic film Ta (5 nm)/Co20Fe60B20 (0.9 nm)/Ta (0.08 nm)/MgO (2 nm)/Ta (5 nm), but KTHNY behavior was only alluded to and not fully realized27. The authors claim that the increased size of orientational domains in the sample is indicative of a transition to the hexatic phase, but the timescales required for the system to fully relax kinetically are not reasonably achievable. With this as background, in this work, we study the formation and solidification of Néel-type magnetic skyrmions in a novel layered, polar magnetic metal, (Fe0.5Co0.5)5GeTe2.
Here, (Fe0.5Co0.5)5GeTe2 (FCGT) is studied as a polar magnetic metal, a metallic magnet which intrinsically breaks spatial inversion symmetry, that hosts stable magnetic Néel skyrmions at room temperature and zero magnetic field43,44 (Supplementary Fig. 2). The parent material Fe5GeTe2 is a centrosymmetric ferromagnet45,46, but breaking of spatial inversion symmetry emerges at 50% Co alloying, potentially due to chemical ordering of the transition metal site and a switch from ABC to AA’ stacking of the layers44 (Fig. 1a). Broken inversion symmetry gives rise to a bulk Dzyalozhinski-Moriya interaction (DMI), allowing for stabilization of stripe cycloidal domains and/or a Néel skyrmion phase at room temperature2. Both the stripe domains and skyrmions can be observed using magnetic force microscopy (MFM), which probes the magnetostatic force on a scanning probe tip. Here, we use this technique to study the quasi-static phase changes of the skyrmion ensemble in an exfoliated sample as a function of temperature and to evaluate our control over their ordering (Fig. 1b, c).
Understanding the emergence of long range order in the FCGT skyrmion ensemble is the focus of this work. We observe an exponential change in the order parameters through the phase transition, suggesting that an ordered phase may be achievable at room temperature, if the role of structural/chemical defects or kinetic obstacles can be overcome. Through spatial confinement of the device which imposes an ordering director field, we are able to overcome this pinning energy and engineer an ordered skyrmion crystal at room temperature, demonstrating control over this order-disorder transition on scales relevant for device applications.
Results
In a 125 nm thick FCGT flake, when slowly cooled below the stabilization temperature of ~314 K, the helimagnetic domains present at high temperature condense into an assembly of Néel skyrmions44, when perturbed by a magnetic field. This stabilization temperature is significantly below the Tc of 350 K. The assembly of skrymions is initially disordered, but its correlation length progressively increases as the temperature is further decreased, reaching a stable, but still disordered, state at ~306 K (Fig. 2a). It can be reversed with temperature, melting from the stable glassy state and increasing in disorder, until the skyrmions disappear into a uniform magnetic state (Supplementary Fig. 4). In the 2D-solid phase, lattice sites should be largely 6-fold coordinated, disturbed only by pairs of correlated dislocations (neighboring pairs of neighboring 5- and 7-fold sites) with opposite Burgers’ vectors, preserving translational and orientational order31,32,33. In the hexatic phase, these dislocations should no longer be bound, and free dislocations allow only quasi-long range orientational order. In our system, where 5(7)-fold coordinated sites are shown in purple (green) in Fig. 2a, b, free dislocations are still present in significant concentrations below the transition temperature at ~306 K, indicating that we are not reaching a 2D-solid phase. Additionally, we see an increase in the number of free 5- or 7-fold sites (disclinations), as we increase the temperature from 300 K to 314 K. This is a hallmark of a 2D-liquid, as the presence of disclinations will destroy the quasi-long-range order. These phase changes are generally suggestive of KTHNY behavior, but the fact that we have never observed the 2D-solid phase may be indicative of magnetic or crystalline defects randomly perturbing the system, forcing the skyrmion lattice into a state of quenched disorder when measured at laboratory timescales27. In the low-temperature, frozen state, ~75% of sites are 6-fold coordinated, which decreases exponentially as temperature is increased, reaching ~40% of sites being 6-fold just before the complete dissolution of the skyrmion phase (Fig. 2d, e). This exponential trend is mirrored in the correlation length extracted from the radial distribution function, which increases from melting to ~308 K, at which point it saturates to a finite value. This saturation of the exponential correlation length is again indicative of frozen translational disorder, as this parameter should otherwise diverge in a solid47.
a MFM images of the FCGT skyrmion lattice at different temperatures. Scale bars are 2 μm. b Voronoi polyhedra showing the number of nearest neighbors for each skyrmion in the image. Green(purple) sites have more(less) than 6 nearest neighbors. When the green and the purple sites neighbor one another, a dislocation is formed from bound topological defects, which is indicative of the disordering in the hexatic phase. c Magnified image of bound defects, illustrating the 5–7 pairs caused by displacement of a single line of skyrmions. The image is scaled up from the box in (a and b). d Histogram of the number of nearest neighbors per site per temperature. We see that that the variance of the Gaussian distribution increases as the temperature is increased. e Peak value of the probabilities of an ideal 6-fold site in (d), showing exponential decay above ~306 K. f Radial distribution function and, (g), correlation length as a function of temperature, showing similar decay as temperature is increased. Correlation length is defined as the last peak in (f) before the intensity decays to 5% of the initial peak.
Quantitative assignment of phases is possible through the bond orientational parameter, which exhibits different behaviors in the solid, hexatic, and liquid phases25. The bond orientational parameter can be defined as:
where \({N}_{{nn}}\) is the number of nearest neighbors for the site at position \({{{{{\bf{r}}}}}}\) and \({\theta }_{j}\) is the angle between the bond to nearest neighbor \(j\) and an arbitrary, but fixed, axis. This asymptotes to 1 if the bonds to the nearest neighbor sites are arranged in a hexagonal array, and to 0 if far from hexagonality. This is shown in Fig. 3a, where the shade of blue indicates the value of \(\left|{\Psi }_{6}({{{{{\bf{r}}}}}})\right|\). The correlation function of \({\Psi }_{6}({{{{{\bf{r}}}}}})\),
where \({N}_{r}\) is the number of sites distance \(r\) apart, can then be used to quantitatively define the phase of the system. A solid phase will have long range order and \({g}_{6}\left({{{{{\bf{r}}}}}}\right)\) will not decay over distance, the hexatic phase will have short- but not long-range order and \({g}_{6}\left({{{{{\bf{r}}}}}}\right)\) will decay algebraically, and in a liquid phase will decay exponentially (Supplementary Fig. 1). Here, we observe exponential decay of \({g}_{6}\left({{{{{\bf{r}}}}}}\right)\) at all temperatures (Fig. 3). This indicates that our system is in the 2D liquid phase at all temperatures. The rate of decay, \(\xi\), however, follows the same exponential trend with temperature as the probability of nearest neighbors in Fig. 2, implying a phase change at the saturation temperature. We hypothesize that this condensation process between ~314 and 306 K, which seems to kinetically freeze the skyrmions into a glassy state with very-short-range ordered domains, would be the liquid-to-hexatic phase transition described in KTHNY theory but is inhibited by kinetic pinning. This is likely due to crystallographic defects which introduce inhomogeneities into the magnetic or orbital lattices40,41,48,49.
a Bond orientational maps of skyrmions as a function of temperature, where the magnitude of the bond orientational parameter, \(|{\Psi }_{6}\left({{{{{\bf{r}}}}}}\right)|\), is shown in blue. Qualitatively, the orientational order of the lattice decreases with increasing temperature. Scale bars are 2 μm. b Orientational correlation function, \({g}_{6}\left(r\right)\), as a function of temperature, which follows an exponential decay at all temperatures. Fits to \({e}^{-\frac{r}{\xi }}\) are shown as dotted lines. The predicted ideal KTNHY algebraic decay behavior with exponent 1/4 is shown as a solid black line. c The exponent \(\xi\) from panel (b) plotted as a function of temperature, showing a clear exponential decrease as temperature is increased. Inset is the temperature range above saturation. d Average \(|{\Psi }_{6}\left({{{{{\bf{r}}}}}}\right)|\) as a function of temperature, that shows exponential decay of the orientational order with respect to temperature falling off quickly above ~306 K. Inset shows the temperature range of clear exponential behavior. Light green points in parts (c and d) are superimposed from low-temperature MFM measurements.
In plan-view dark field (scanning) transmission electron microscope images (DF-(S)TEM), FCGT flakes show clear dislocation lines with spacings on the order of 100–200 nm (Fig. 4a). In a layered hexagonal system, these are similar to the well-studied stacking faults in graphite and other vdW crystals50,51,52,53,54,55. Under a 2-beam condition, g·b analysis shows that these dislocations possess Burgers‘ vectors along \(\langle 11\bar{2}0\rangle\), Fig. 4b, consistent with the stacking faults that most easily form in layered hexagonal systems due to the ease of in-plane slip50,56. We can then use 4D-STEM (Methods) to reconstruct the strain fields \({\varepsilon }_{11}\), \({\varepsilon }_{22}\), and \({\varepsilon }_{12}\) that occur due to these stacking faults, observing values of up to ~1.5% strain (Fig. 4d–g). Nonuniform fields of this mangitude would be sufficient to disrupt KTHNY behavior, indicating that these structual defects inherent to layered materials are preventing condensation of the hexatic phase34,35,57.
Defect-driven quenching of phase transitions and order in magnetic systems is specifically reminiscent of the breakdown of long-range order in random field Ising magnets41,42, where magnetic defects make ordering kinetics extremely slow and the disordered state becomes frozen at low temperatures47. This is qualitatively consistent with previous results which show that pinning from crystalline defects can impede skyrmion motion1,8,58. In our study, this is supported by the average of \({\Psi }_{6}({{{{{\bf{r}}}}}})\), in addition to the correlation length in Fig. 2g, which saturates below ~308 K, instead of continuously increasing as is observed in typical hexatic transitions3,25,27. Our conclusion is also in agreement with the results in ref. 27, in which the authors also do not observe a true hexatic phase in a magnetic skyrmion lattice, indicated by exponential decay in \({g}_{6}\left(r\right)\), but attribute it to the arbitrarily long timescales associated with condensation. If this is true and condensation of the hexatic and solid phases is not achievable on a reasonable time scale due to pinning, can we engineer the introduction of a new field that favors ordering to overcome these kinetic limitations and influence formation of the ordered phase? Intuitively, this should be possible, as it is analogous to other disordered functional systems such as relaxor ferroelectrics59 and spin glasses60 where strong fields can force an otherwise frozen/disordered order parameter into a long-range ordered state61.
Discussion
Previous studies on magnetic skyrmion lattices have indicated that physical confinement may influence the formation of isolated skyrmions or skyrmion arrays24,26,62,63,64. It has been previously shown in FeGe nanowires fabricated from bulk, single crystals, that creating devices on the scale of ~4–5 skyrmion widths can force the skyrmions into a close packed array26. This is an important consideration for potential device-scale applications, as the skyrmion lattice will impact dynamics and transport9. This has, however, not been investigated when it comes to skyrmion crystal phases, and the stability of the skyrmion lattice. Here, we first simulate confinement using the boundary conditions of our micromagnetic simulations, which has previously been used to accurately describe the behavior of skyrmions in FCGT43,44.
In our micromagnetic simulations, we artificially create a confined strip of material by fixing the left and right boundary conditions, while making the top and bottom periodic (hereafter semi-periodic) Fig. 4. Compared to a cell with fully periodic boundary conditions, we see a clear difference where the skyrmions in the periodic cell relax to a disordered, liquid ground state, while the skyrmions in the confined, semi-periodic cell relax to a hexatic phase (Fig. 5). This difference is also clearly seen qualitatively in the structure factor (inset in Fig. 5a) and in the number of dislocation sites, Fig. 5b. In this simulation, we speculate that ordered skyrmions form at the fixed boundary, which allows for nucleation of larger, more uniform domains. We observe this more directly in Fig. 5d, showing the Euler angle \(\varTheta={{\arg }}\left({\Psi }_{6}\left({{{{{\bf{r}}}}}}\right)\right)/6\). \(\varTheta\) indicates the average rotation of a skyrmion lattice site with respect to the x-axis and allows us to distinguish domains of uniform rotation/mosaicity27. Here, the color corresponds to the average rotation of the site, meaning areas of uniform color correspond to mosaic domains in the skyrmion lattice. With periodic boundary conditions, we see small, well-defined domains, which are largely absent in the simulated images with fixed boundaries. Additionally, looking at the average order parameter as a function of the spacing between the fixed boundary conditions, we see that in the smallest case, when the lattice is most confined, the skyrmions are most ordered, then approaching the liquid phase as the spacing is widened and the area becomes bulk-like (Supplementary Fig. 6). We assert that the presence of the boundary exerts an orientating director field, conjugate to the orientational order parameter, making true long range orientational order of the skyrmions possible. This enhances both the orientational and positional orders of the skyrmion crystal. We note, however, that in our engineered systems KTHNY theory is no longer directly applicable. KTHNY theory is true in the infinte limit, thus the confined region is explicitly not pure-KTHNY behavior. Notably, however, the liquid-hexatic-phase transition can still be observed in systems where nonlinear potentials and finite size effects are present65,66,67,68, making the KTHNY terminology a useful framework for the interpretation of the order-disorder transition.
a DF-TEM shows the nominally single phase flake hosts dislocations with periodicities on the order of ~100 nm. b In two beam conditions along the \(30\bar{3}0\) and \(0\bar{3}30\) axes, these dislocations decrease in contrast, indicating that the Burgers‘ vectors lie along \(\langle 11\bar{2}0\rangle\). c Virtual dark-field images can also be generated from a 4D-STEM dataset by integrating the Bragg peak intensities from reflections. From this data, we are able to calculate the projected in-plane strain fields \({\varepsilon }_{11}\) (d), \({\varepsilon }_{22}\) (e), and \({\varepsilon }_{12}\) (f), along with the in-plane rotation \(\phi\) (g). We note the mis-tilt artifact is inevitable in the present method for strain determination, as shown in red diagonal stripes in (d and e).
a Simulated real space images of the skyrmion lattices with periodic (left) and semi-periodic (right) boundary conditions. The fixed edges are shown in orange. Insets show the associated diffraction patterns. Scale bars are 2 μm. b Nearest neighbor map of the same images, where greater(less)-than-6 nearest neighbor sites are shown in green(purple), and (c) bond orientational maps where the magnitude of \(|{\Psi }_{6}\left({{{{{\bf{r}}}}}}\right)|\) is shown in blue. d Euler angle of the skyrmion lattice sites from −30° to +30°, with respect to the x axis. Areas of similar color are mosaic domains which are rotationally uniform. e Radial distribution function, (f), histogram of the number of nearest neighbors, and (g), orientational correlation function \({g}_{6}\left(r\right)\), where the simulation with periodic boundary conditions shows liquid-like decay and the simulation with semi-periodic boundary conditions shows hexatic-like decay. Shaded regions correspond to standard deviation over 10 simulations. h Average orientational order as a function of aspect ratio and the space between the two aperiodic boundary conditions.
Experimentally, we create spatial confinement by overlapping two thick (114 nm and 214 nm) FCGT flakes in a single rectangular region. These thicknesses were chosen as they are both within the regime to stabilize Néel skyrmions as shown by previous work44. The flakes do not interact electrically due to a large thickness of flakes compared to the interface and the transfer process in the air, leading to ~5 nm of adsorbates at the interface. This implies their interaction is governed by long range magnetostatics and this overlapped bilayer region behaves like a thicker region within a semi-periodic, but finite, potential. This semi-classical interaction is supported by the fact that the skyrmions in the bilayer region are ~1.5x the size of those in the thinner regions (Fig. 6e), which is consistent with the thickness dependent size changes in FCGT governed by Kittel’s law44. This is also illustrated in Supplementary Fig. 9, where the simulated bilayer hosts skyrmions that extend through the entire structure, effectively behaving as a thicker magnet. In the free monolayer and confined bilayer regions, the results parallel those of the simulation, where the monolayer region is stable in a 2D liquid phase, but the confined, bilayer region is in a hexatic phase. We consider the monolayer region to be bulk-like due to its lateral size compared to that of the skyrmions. This is quantified by the structure factor (Fig. 6a), where we see clear differentiation between amorphous-like and crystalline behaviors, and the \({g}_{6}\left(r\right)\) parameter (Fig. 6f), which decays exponentially in the monolayer region and algebraically in the bilayer region. We posit that this is due to the imposition of a uniaxial director field at the boundary, which overcomes the elastic energy of the native defects and effectively decreases the energy required to grow larger, more ordered domains. In this case, where the device size is comparable to ~20x the skyrmion lattice constant, this director field is enough to override the kinetic limitations preventing stabilization of the ordered hexatic phase. Another factor to this difference between the monolayer and bilayer samples may be that strain and pinning defects in the bilayer are averaged across the two flakes, potentially reducing the composite nonuniformity. This averaging of properties can also be observed with the equilibrium lattice constant of the skyrmions in the bilayer, where we see the anisotropies of the individual layers average out in the bilayer system and behave like a single sample.
a MFM micrograph of a sample with two, monolayer FCGT flakes and a rectangular, bilayer region of overlap. The edges of this region are shown in orange. The calculated structure factors are shown at left. Scale bar is 2 μm. b Nearest neighbor and (c) bond orientational maps of the same image. The monolayer regions can be characterized by long chains of topological defects, whereas the bilayer region forms an approximately single hexatic domain, commensurate with the direction of the confined edges. d Euler angle, \(\Theta\), showing the rotational order of the skyrmion lattice sites. The monolayer region shows clear mosaic domains, while the confined, bilayer region is much more uniform. e Radial distribution function showing the increased lattice parameter of the bilayer region, indicating that it behaves semi-classically as a thicker flake of FCGT. f Histogram of the number of nearest neighbors. g \({g}_{6}\left(r\right)\), where the monolayer regions show a 2D liquid and the bilayer region shows hexatic behavior. Fits to exponential and algebraic decay are shown as dotted lines.
Here we investigate the stability of the lattice of Néel-type skyrmions in FCGT. We show that the system does not follow true KTHNY behavior and condense into a 2D solid, but does undergo a freezing transition at ~304 K, significantly below the Tc, where the disordered skyrmions are frozen into a more ordered, but still glassy, lattice, down to cryogenic temperatures. From (S)TEM imaging, we show the presence of native dislocations in the sample which lead to large nonuniform strain fields sufficient to disrupt KTHNY behavior. We show that by confining the device, however, we are able to impose a strong enough ordering field to overcome this elastic nonuniformity, stabilizing a hexatic phase and engineering the order-disorder transition.
Methods
Sample synthesis
Single crystals of (Fe0.5Co0.5)5–δGeTe2 were grown by the chemical vapor transfer method43,45, with iodine used as the transport agent. Elemental Fe (99.99%), Co (99.99%), and Te (99.999%) powders and small Ge pieces (99.999%), and were used in synthesis. The starting raw materials were mixed in the nominal molar ratio Fe:Co:Ge:Te = 3:3:1:2 inside a glovebox. The starting mixture was vacuumed and sealed inside a quartz tube, then reacted at 750 °C under isothermal conditions for 7 to 10 days. For MFM measurement, flakes were exfoliated and transferred to Si substrates using the tape method. For TEM measurement, flakes were transferred from Si substrates to SiN TEM windows with PDMS using standard 2D-material techniques.
Magnetic force microscopy
Near-room-temperature MFM measurements were performed using an Asylum Research MFP-3D system. Low-temperature MFM measurements were performed with a homemade variable-temperature MFM (Rutgers University). The tips were coated with nominally 100-nm Co by magnetron sputtering. The MFM signal (the shift of resonant frequency) is proportional to the out-of-plane stray field gradient, which was extracted by a phase-locked loop (SPECS). MFM images were taken with constant-height noncontact mode.
Statistical analysis
Statistical analysis was done in python using a combination of original code and the Freud69 numerical statistics python package. Skyrmion locations were found using the scikit-image python package after applying a Laplacian-of-Gaussian filter. Manual corrections were carried out where necessary. Delaunay triangulation and Voronoi tessellation were performed algorithmically in the scipy python package to define nearest neighbor skyrmions, \({{{{{{\bf{r}}}}}}}_{{ij}}\),.
Pair distribution functions (PDF) were calculated as:
where \({{{{{\bf{r}}}}}}\) is a vector in real space, \(N\) is the total number of skyrmions and \({{{{{{\bf{r}}}}}}}_{{ij}}\) is the vector between skyrmions \(i\) and \(j\). The structure factor was calculated from the PDF:
where \({{{{{\bf{q}}}}}}\) is a vector in reciprocal space. Orientation independent radial distribution functions were calculated as:
where \(r\) is a distance. The calculations of \({\Psi }_{6}\left({{{{{\bf{r}}}}}}\right)\) and \({g}_{6}\left(r\right)\) are defined in the text.
DF-(S)TEM
Dark-field (DF) transmission electron microscopy (TEM) experiments were carried out in a 2-beam condition, where the transmitted beam and a single diffracted beam allow for matching real space image features to defects with specific crystallographic orientations. Experimental data were collected on an FEI Titan ThemIS operating at 300 keV with a 0.68 m camera length and the diffraction patterns were indexed using a dynamical scattering simulation from the python Py4DSTEM package70.
The four-dimensional (4D-) scanning transmission electron microscopy (STEM) experiments were performed using an electron microscopy pixel array detector (EMPAD), where the 2D electron diffraction pattern was recorded over a 2D grid of real space probe positions, resulting in 4D datasets. Experimental data were acquired using a FEI Titan operated at 300 keV under field-free condition (Lorentz mode) with 150 pA beam current, 0.7 mrad semi-convergence angle, and a dwell time of 1 ms.
Simulation
Numerical results were found using the micromagnetic simulation package Mumax3 running on the Lawrencium computing cluster at Lawrence Berkeley National Lab. The simulated area is a cuboid of dimensions 2500 nm × 2500 nm × 100 nm, divided into 5 nm × 5 nm × 5 nm cells. Effective medium material parameters used are A = 5.5 × 10−12 J m−1, D = 0.7 mJ m−2, Ms = 301 kA m−1. The 5 nm cell size is below the exchange length given by \({l}_{{ex}}=\sqrt{\frac{2A}{{\mu }_{^\circ }{{m}_{s}}^{2}}}\, \approx \, 9.8\) nm. To model the hexagonal order parameter as a function of different geometries, simulations were run with a range of aspect ratios from (500 nm × 2500 nm) to (2500 nm × 2500 nm) these simulations were performed with both fixed and semi-periodic boundary conditions (periodic on y boundary, fixed on x boundary). To quantify hexatic order in a statistically significant way a sample size of N = 10 different random seeds were used as initial conditions to position the nucleation sites of the Skyrmions. Simulations were relaxed from the initial state to reach a near-ground state condition and then advanced for 1000 ns to incorporate thermal ordering effects.
Data availability
The MFM data generated in this study have been deposited in the Zenodo database under accession code 8011829. Other data used in these experiments are available from the authors upon reasonable request.
References
Büttner, F., Lemesh, I. & Beach, G. S. D. Theory of isolated magnetic skyrmions: from fundamentals to room temperature applications. Sci. Rep. 8, 4464 (2018).
Kanazawa, N., Seki, S. & Tokura, Y. Noncentrosymmetric magnets hosting magnetic skyrmions. Adv. Mater. 29, 1603227 (2017).
Kläui, M. Freezing and melting skyrmions in 2D. Nat. Nanotechnol. 15, 726–727 (2020).
Das, S. et al. Observation of room-temperature polar skyrmions. Nature 568, 368–372 (2019).
Das, S. et al. Local negative permittivity and topological phase transition in polar skyrmions. Nat. Mater. 20, 194–201 (2021).
Kurumaji, T. et al. Skyrmion lattice with a giant topological Hall effect in a frustrated triangular-lattice magnet. Science 365, 914–918 (2019).
Litzius, K. et al. Skyrmion Hall effect revealed by direct time-resolved X-ray microscopy. Nat. Phys. 13, 170–175 (2017).
Woo, S. et al. Observation of room-temperature magnetic skyrmions and their current-driven dynamics in ultrathin metallic ferromagnets. Nat. Mater. 15, 501–506 (2016).
Tomasello, R. et al. A strategy for the design of skyrmion racetrack memories. Sci. Rep. 4, 6784 (2014).
Brearton, R. et al. Deriving the skyrmion Hall angle from skyrmion lattice dynamics. Nat. Commun. 12, 2723 (2021).
Jiang, W. et al. Direct observation of the skyrmion Hall effect. Nat. Phys. 13, 162–169 (2017).
Zázvorka, J. et al. Thermal skyrmion diffusion used in a reshuffler device. Nat. Nanotechnol. 14, 658–661 (2019).
Huang, Y., Kang, W., Zhang, X., Zhou, Y. & Zhao, W. Magnetic skyrmion-based synaptic devices. Nanotechnology 28, 08LT02 (2017).
Prychynenko, D. et al. Magnetic skyrmion as a nonlinear resistive element: a potential building block for reservoir computing. Phys. Rev. Appl. 9, 014034 (2018).
Bruno, P., Dugaev, V. K. & Taillefumier, M. Topological hall effect and berry phase in magnetic nanostructures. Phys. Rev. Lett. 93, 096806 (2004).
Karnieli, A., Tsesses, S., Bartal, G. & Arie, A. Emulating spin transport with nonlinear optics, from high-order skyrmions to the topological hall effect. Nat. Commun. 12, 1092 (2021).
Kanazawa, N. et al. Large topological hall effect in a short-period helimagnet MnGe. Phys. Rev. Lett. 106, 156603 (2011).
Mook, A., Göbel, B., Henk, J. & Mertig, I. Magnon transport in noncollinear spin textures: anisotropies and topological magnon Hall effects. Phys. Rev. B 95, 020401 (2017).
Raju, M. et al. Colossal topological hall effect at the transition between isolated and lattice-phase interfacial skyrmions. Nat. Commun. 12, 2758 (2021).
Shiomi, Y., Kanazawa, N., Shibata, K., Onose, Y. & Tokura, Y. Topological Nernst effect in a three-dimensional skyrmion-lattice phase. Phys. Rev. B 88, 064409 (2013).
Gruber, R. et al. Skyrmion pinning energetics in thin film systems. Nat. Commun. 13, 3144 (2022).
Litzius, K. et al. The role of temperature and drive current in skyrmion dynamics. Nat. Electron 3, 30–36 (2020).
Romming, N., Kubetzka, A., Hanneken, C., von Bergmann, K. & Wiesendanger, R. Field-dependent size and shape of single magnetic skyrmions. Phys. Rev. Lett. 114, 177203 (2015).
Jin, C. et al. Control of morphology and formation of highly geometrically confined magnetic skyrmions. Nat. Commun. 8, 15569 (2017).
Huang, P. et al. Melting of a skyrmion lattice to a skyrmion liquid via a hexatic phase. Nat. Nanotechnol. 15, 761–767 (2020).
Du, H. et al. Edge-mediated skyrmion chain and its collective dynamics in a confined geometry. Nat. Commun. 6, 8504 (2015).
Zázvorka, J. et al. Skyrmion lattice phases in thin film multilayer. Adv. Funct. Mater. 30, 2004037 (2020).
Hohenberg, P. C. Existence of long-range order in one and two dimensions. Phys. Rev. 158, 383–386 (1967).
Mermin, N. D. & Wagner, H. Absence of ferromagnetism or antiferromagnetism in one- or two-dimensional isotropic heisenberg models. Phys. Rev. Lett. 17, 1133–1136 (1966).
Halperin, B. I. On the Hohenberg–Mermin–Wagner theorem and its limitations. J. Stat. Phys. 175, 521–529 (2019).
Kosterlitz, J. M. & Thouless, D. J. Ordering, metastability and phase transitions in two-dimensional systems. J. Phys. C: Solid State Phys. 6, 1181–1203 (1973).
Halperin, B. I. & Nelson, D. R. Theory of two-dimensional melting. Phys. Rev. Lett. 41, 121–124 (1978).
Young, A. P. Melting and the vector Coulomb gas in two dimensions. Phys. Rev. B 19, 1855–1866 (1979).
Guillamón, I. et al. Enhancement of long-range correlations in a 2D vortex lattice by an incommensurate 1D disorder potential. Nat. Phys. 10, 851–856 (2014).
Guillamón, I. et al. Direct observation of melting in a two-dimensional superconducting vortex lattice. Nat. Phys. 5, 651–655 (2009).
Brock, J. D., Birgeneau, R. J., Litster, D. & Aharony, A. Hexatic ordering in liquid crystal films. Contemp. Phys. 30, 321–335 (1989).
Aharony, A., Birgeneau, R. J., Brock, J. D. & Litster, J. D. Multicriticality in hexatic liquid crystals. Phys. Rev. Lett. 57, 1012–1015 (1986).
Takae, K. & Kawasaki, T. Emergent elastic fields induced by topological phase transitions: Impact of molecular chirality and steric anisotropy. Proc. Natl Acad. Sci. 119, e2118492119 (2022).
Negulyaev, N. N. et al. Melting of two-dimensional adatom superlattices stabilized by long-range electronic interactions. Phys. Rev. Lett. 102, 246102 (2009).
Birgeneau, R. J. Random fields and phase transitions in model magnetic systems. J. Magn. Magn. Mater. 177–181, 1–11 (1998).
Hill, J. P., Feng, Q., Birgeneau, R. J. & Thurston, T. R. Loss of long range order in the 3D random field Ising model. Phys. Rev. Lett. 70, 3655–3658 (1993).
Birgeneau, R. J. et al. X-ray and neutron scattering, magnetization, and heat capacity study of the 3D random field ising model. Phys. Rev. Lett. 75, 1198–1201 (1995).
Zhang, H. et al. A room temperature polar magnetic metal. Phys. Rev. Mater. 6, 044403 (2022).
Zhang, H. et al. Room-temperature skyrmion lattice in a layered magnet (Fe0.5Co0.5)5GeTe2. Sci. Adv. 8, eabm7103 (2022).
Zhang, H. et al. Itinerant ferromagnetism in van der Waals Fe5-xGeTe2 crystals above room temperature. Phys. Rev. B 102, 064417 (2020).
May, A. F. et al. Ferromagnetism near room temperature in the cleavable van der Waals crystal Fe5GeTe2. ACS Nano 13, 4436–4442 (2019).
Birgeneau, R. J., Yoshizawa, H., Cowley, R. A., Shirane, G. & Ikeda, H. Random-field effects in the diluted two-dimensional Ising antiferromagnet Rb2Co0.7Mg0.3F4. Phys. Rev. B 28, 1438–1448 (1983).
Iannacchione, G. S., Park, S., Garland, C. W., Birgeneau, R. J. & Leheny, R. L. Smectic ordering in liquid-crystal–aerosil dispersions. II. Scaling analysis. Phys. Rev. E 67, 011709 (2003).
Ramazanoglu, M., Larochelle, S., Garland, C. W. & Birgeneau, R. J. High-resolution x-ray study of nematic–smectic-A and smectic-A–reentrant-nematic transitions in liquid-crystal–aerosil gels. Phys. Rev. E 77, 031702 (2008).
Freise, E. J. & Kelly, A. The deformation of graphite crystals and the production of the rhombohedral form. Philos. Mag.: J. Theor. Exp. Appl. Phys. 8, 1519–1533 (1963).
Williamson, G. K. & Cottrell, A. H. Electron microscope studies of dislocation structures in graphite. Proc. R. Soc. Lond. Ser. A. Math. Phys. Sci. 257, 457–463 (1960).
Alden, J. S. et al. Strain solitons and topological defects in bilayer graphene. Proc. Natl Acad. Sci. 110, 11256–11260 (2013).
Butz, B. et al. Dislocations in bilayer graphene. Nature 505, 533–537 (2014).
Gannon, R. N. et al. Defects in layered van der Waals Heterostructures: implications for thermoelectrics. ACS Appl. Nano Mater. 4, 7943–7953 (2021).
Kim, J. H. et al. Interface-driven partial dislocation formation in 2D heterostructures. Adv. Mater. 31, 1807486 (2019).
Hull, D. & Bacon, D. J. Introduction to Dislocations. (Butterworth-Heinemann, 2001).
Lee, J., Wang, H., Dreyer, M., Berger, H. & Barker, B. I. Nonuniform and coherent motion of superconducting vortices in the picometer-per-second regime. Phys. Rev. B 84, 060515 (2011).
Ma, C. T., Xie, Y., Sheng, H., Ghosh, A. W. & Poon, S. J. Robust formation of ultrasmall room-temperature neél skyrmions in amorphous ferrimagnets from atomistic simulations. Sci. Rep. 9, 9964 (2019).
Kleemann, W. & Dec, J. Relaxor ferroelectrics and related superglasses. Ferroelectrics 553, 1–7 (2019).
Parisi, G. Spin glasses and fragile glasses: Statics, dynamics, and complexity. Proc. Natl Acad. Sci. 103, 7948–7955 (2006).
Cowley, R. A. et al. The bicritical phase diagram of two-dimensional antiferromagnets with and without random fields. Z. Phys. B - Condens. Matter 93, 5–19 (1993).
Zhou, Y. & Ezawa, M. A reversible conversion between a skyrmion and a domain-wall pair in a junction geometry. Nat. Commun. 5, 4652 (2014).
Schönenberger, T. et al. Direct visualisation of skyrmion lattice defect alignment at grain boundaries. Nanoscale Res. Lett. 17, 20 (2022).
Matsumoto, T. & Shibata, N. Confinement of magnetic skyrmions to corrals of artificial surface pits with complex geometries. Front. Phys. 9, 774951 (2022).
Kapral, R. Progress in the theory of mixed quantum-classical dynamics. Annu. Rev. Phys. Chem. 57, 129–157 (2006).
Prestipino, S., Saija, F. & Giaquinta, P. V. Hexatic phase in the two-dimensional gaussian-core model. Phys. Rev. Lett. 106, 235701 (2011).
Udink, C. & van der Elsken, J. Determination of the algebraic exponents near the melting transition of a two-dimensional Lennard-Jones system. Phys. Rev. B 35, 279–283 (1987).
Joos, B. & Duesbery, M. S. Dislocation energies in rare-gas monolayers on graphite. Phys. Rev. Lett. 55, 1997–2000 (1985).
Ramasubramani, V. et al. Freud: a software suite for high throughput analysis of particle simulation data. Comput. Phys. Commun. 254, 107275 (2020).
Savitzky, B. H. et al. py4DSTEM: a software package for four-dimensional scanning transmission electron microscopy data analysis. Microsc. Microanal. 27, 712–743 (2021).
Acknowledgements
P.M. and R.R. acknowledge funding from the Department of Defense, ARO Grant No. W911NF-21-2-0162 (ETHOS). This work was primarily funded by the U.S. Department of Energy, Office of Science, Office of Basic Energy Sciences, Materials Sciences and Engineering Division under Contract No. DE-AC02-05-CH11231 (Quantum Materials program KC2202). D.R. and P.F. are supported by the U.S. Department of Energy, Office of Science, Office of Basic Energy Sciences, Materials Sciences and Engineering Division under Contract No. DE-AC02-05-CH11231 (Nonequilibrium magnetic materials program MSMAG). R.Y. is supported by the National Science Foundation Graduate Research Fellowship under Grant No. DGE 2146752. This research used the Lawrencium computational cluster resource provided by the IT Division at the Lawrence Berkeley National Laboratory, supported by the U.S. Department of Energy, Office of Science, Office of Basic Energy Sciences under Contract No. DE-AC02-05CH11231. The low-temperature MFM studies at Rutgers are supported by the Office of Basic Energy Sciences, Division of Materials Sciences and Engineering, U.S. Department of Energy under award no. DE-SC0018153. Y.T.S. and D.A.M. acknowledge funding support by the Department of Defense, Air Force Office of Scientific Research under award FA9550-18-1-0480. The electron microscopy studies were performed at the Cornell Center for Materials Research, a National Science Foundation (NSF) Materials Research Science and Engineering Center (DMR-1719875). The Cornell FEI Titan Themis 300 was acquired through NSF-MRI-1429155, with additional support from Cornell University, the Weill Institute and the Kavli Institute at Cornell. The authors thank M. Thomas, J. G. Grazul, M. Silvestry Ramos, K. Spoth for technical support and careful maintenance of the instruments.
Author information
Authors and Affiliations
Contributions
P.M., H.Z., R.R., and R.J.B. designed experiments. X.C., R.C., H.Z., and J.Y. synthesized samples. H.Z., Y.-T.C., and W.W. performed MFM measurements. R.Y., Y.T.S., and D.A.M. performed and analyzed (S)TEM imaging. D.R. implemented micromagnetic simulations. P.M. implemented statistical analysis. P.M., H.Z., R.J.B., R.R., and P.F. analyzed results and wrote the paper. All authors have contributed to manuscript revisions.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Yingying Wu and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Meisenheimer, P., Zhang, H., Raftrey, D. et al. Ordering of room-temperature magnetic skyrmions in a polar van der Waals magnet. Nat Commun 14, 3744 (2023). https://doi.org/10.1038/s41467-023-39442-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-023-39442-0
- Springer Nature Limited
This article is cited by
-
Geometric phase analysis of magnetic skyrmion lattices in Lorentz transmission electron microscopy images
Scientific Reports (2024)
-
Room-temperature sub-100 nm Néel-type skyrmions in non-stoichiometric van der Waals ferromagnet Fe3-xGaTe2 with ultrafast laser writability
Nature Communications (2024)
-
Above-room-temperature chiral skyrmion lattice and Dzyaloshinskii–Moriya interaction in a van der Waals ferromagnet Fe3−xGaTe2
Nature Communications (2024)
-
Spin disorder control of topological spin texture
Nature Communications (2024)
-
Reversible non-volatile electronic switching in a near-room-temperature van der Waals ferromagnet
Nature Communications (2024)