Abstract
A 2-Q antiferromagnetic order of the ferromagnetic dimers was found below TN = 2.9 K in the Shastry-Sutherland lattice BaNd2ZnS5 by single crystal neutron diffraction. The magnetic order can be understood by the orthogonal arrangement of local Ising Nd spins, identified by polarized neutrons. A field was applied along [1 -1 0] to probe the observed metamagnetic transition in the magnetization measurement. The field decouples two magnetic sublattices corresponding to the propagation vectors q1 = (½, ½, 0) and q2 = (−½, ½, 0), respectively. Each sublattice shows a “stripe” order with a Néel-type arrangement in each single layer. The “stripe” order with q1 remains nearly intact up to 6 T, while the other one with q2 is suppressed at a critical field Hc ~1.7 T, indicating a partial disorder. The Hc varies with temperature and is manifested in the H-T phase diagram constructed by measuring the magnetization in BaNd2ZnS5.
Similar content being viewed by others
Introduction
Exotic non-trivial magnetic behavior has emerged in magnetic systems with geometrical frustration. The kagome and triangular lattices are common examples of two-dimensional (2D) frustrated lattices1,2. More elusive is the 2D orthogonal dimer lattice famously realized in the material SrCu2(BO3)23,4, which has been discovered to host a quantum spin liquid phase5,6,7,8. This lattice can be described by the Shastry-Sutherland (SS) model which consists of a 2D orthogonal arrangement of the spin dimers where the ratio between the two magnetic interactions, δ = J/J’ with J and J’ as the antiferromagnetic inter- and intra-dimer interactions, respectively, is critical for controlling magnetic states in the Shastry-Sutherland lattice (SSL)9. The δ ratio of 0.675 and 0.765 separate the dimer singlet, plaquette singlet and Néel phase, respectively, in the phase diagram of the SS model10,11.
Resultantly, rich magnetic phase diagrams have been constructed for SSL materials from the field-induced evolution of the magnetic order. One common feature are fractionalized magnetization plateaus, which likely originate from the transition of a dimer singlet ground state to the formation of superstructures of the field-induced triplet dimers such as in SrCu2(BO3)210,12,13,14,15,16,17,18,19,20,21. The SSL is also found in families such as the rare earth tetraborides RB4 (R = rare earth)22,23,24, BaR2TO5 (R = rare earth, T = transition metal)25,26,27,28, R2T2In (R = rare earth, T = transition metal)29,30,31 and RE2Pt2Pb (R = rare earth)32. The magnetic ordered states can vary significantly from the insulator SrCu2(BO3)2 which possesses a Heisenberg type exchange interaction to the metallic RB4 family where a Ruderman-Kittel Kasuya-Yosida (RKKY) type interaction is observed between the moments giving it a long-rang order and possessing Ising-like moments oriented perpendicular to the SSL planes33,34,35. However, SSL materials such as Yb2Pt2Pb32,36,37,38,39, have been found to exhibit field-induced metamagnetic transitions associated with partially disordered states, where at low temperatures a Luttinger liquid state has been realized.
Consequently, only very few SSL materials were reported to possess ferromagnetic dimers, including the insulator BaNd2ZnO525 and metallic TmB423,34,40. Considering the newly explored BaR2TO5 family, although it is chemically diverse, the formation of the SSL will only occur for the lighter rare earth elements and successful single crystal growth has not been reported. The sulfide counterpart, BaR2TS5, which crystallizes into the same space group (I4/mcm) as the SSL BaR2TO5 materials, remains largely unexplored and recently large single crystals of BaNd2ZnS541,42 have been synthesized exhibiting a TN = 2.9 K. The dimers of the SSL in BaNd2ZnS5 are formed by the Nd atoms having inter-dimer lengths of 4.151 Å and intra-dimer lengths of 3.596 Å. A metamagnetic transition is observed in the M(H) with H along [1 −1 0], indicating this SSL material an excellent candidate for studying the intricate dimer physics from the field-induced magnetic phase evolution.
In this work, we report a 2-Q magnetic order in the SSL BaNd2ZnS5, determined by single crystal neutron diffraction. We utilize polarized neutrons to provide insight into the local magnetic anisotropy of the Nd spins and reveal the origin of the 2-Q magnetic order. The resulting field-induced evolution of the magnetic phases were characterized by magnetization measurements with the critical input from single crystal neutron diffraction. A partially disordered dimer liquid state was found and a “spin-flip-or-flop” mechanism was proposed to describe the dimer liquid state.
Results and discussions
Zero field magnetic structure
BaNd2ZnS2 exhibits 2D SSL layers of magnetic Nd3+ (J = 9/2) atoms separated by layers of Ba and Zn atoms and coordinated by S atoms. Nd3+ has a Kramers doublet ground state and behaves as a pseudospin 1/243. Figure 1a, describes the Nd SSL where J’ represents the intradimer interaction (nearest-neighbor) and J the interdimer interaction (next-nearest-neighbor), a typical SS interaction model. To understand the magnetic anisotropy of the Nd3+ spins in BaNd2ZnS5, we measured the local magnetic susceptibility tensor of the Nd3+ spins by polarized neutron diffraction44,45. The local symmetry of the Nd atomic site, the 8h site of space group I4/mcm, implies the principal axes of the ellipsoid are along the [1 1 0], [1 −1 0] and [0 0 1] directions. The bulk magnetic measurements have revealed the magnetic moments are easy in-plane42. Therefore, only one-field-direction along [1 −1 0], was selected to detect the in-plane magnetic anisotropy of the Nd3+ spins. By measuring reflections in spin-up and spin-down neutron channels, we obtained 17 good-quality flipping ratios to refine two free susceptibility tensor parameters in-plane. A suitable fitting of the flipping ratios could be reached, as shown by the Fig. 1b plot of the experimental versus calculated flipping ratios, using the software CrysPy. The in-plane principal axes of the Nd3+ magnetization ellipsoids, Fig. 1c, were found to be orthogonal to the dimer bond consistent with an Ising-spin nature with lengths χ// = 0.183(22) μB/T and χ┴ = 0.033(22) μB/T. Similar to Yb2Pt2Pb32 the magnetic moments are found within the plane of the SSL and orthogonally arranged between two magnetic sublattices that satisfy the Ising behavior, contrary to that in SrCu2(BO3)214 and TmB423. Instead of the well-known SSL interaction model, the resulting formation seemingly favors an effective square lattice magnetic model where J’ and J” are the potential interaction paths, as indicated by the orange line (i.e. the dimer bond) and the dashed black line, respectively, in Fig. 1f32. The symmetric terms of interaction J produce zero energy contribution due to the orthogonality of the spin arrangement between the neighboring orthogonal dimer bonds (shown in Fig. 1a as a standard SS spin model but ignored in Fig. 1f due to the zero-energy contribution from J for the Ising spins). While the antisymmetric terms of J in the spin Hamiltonian (see the full description in the SI) are likely weak as well, this will be shown by the field measurements presented later. Future inelastic neutron scattering measurements are needed to further confirm the interaction speculation here and interpret the spin dynamics in BaNd2ZnS5.
a SSL sublattice of Nd atoms in the ab plane. b Experimental versus calculated flipping ratio plot. c Local magnetic anisotropy of Nd dimers is showed by magnetic susceptibility tensors drew as ellipsoids in unit cell of BaNd2ZnS5. d Temperature-dependent order parameter of peak (½ ½ 2), red line is the empirical power law fitting, I ~ (Tm – T/Tm)2β. e Experimental versus calculated structure factors at zero field. f 2-Q magnetic structure model for BaNd2ZnS5, the blue and orange represent the sublattices with q1= (½, ½, 0) and q2= (-½, ½, 0), respectively, and the light and dark color shades represent the different layers along the c axis. The J’ and J” interaction paths correspond to the dimer bond and the dashed black line, respectively. The Jz represents the nearest spin–spin interaction between layers.
From the temperature-dependence of the magnetic scattering at (½ ½ 2), Fig. 1d, the magnetic order appears at ~ 3 K, consistent with the reported TN = 2.9 K from the magnetic susceptibility measurements42. The solid red line in Fig. 1d, corresponds to the power law fitting of the intensity, I ~ (TN – T/TN)2β, with a TN reasonably fixed at 2.95 K, and a β ~ 0.08(1) which is smaller than the expected β = 1/8 for a 2D Ising system32 and could be a result of the nature of the spin dimer lattice. As a product of the single crystal polarized neutron diffraction results, a suitable magnetic structure model could be immediately determined since the fit could be appropriately constrained with moments perpendicular to the dimer bonds. A 2-Q AFM model consisting of two magnetic sublattices indexed by the propagation vectors q1 = (½, ½, 0) and q2 = (-½, ½, 0), resembling the AFM 2-Q structure for BaNd2ZnO525 but with a different magnetic symmetry, best fit the zero-field data. The magnetic symmetry P_C4/nnc (#126.385) was then determined using the k-SUBGROUPSMAG program from the Bilbao Crystallographic server. Based on the body centered symmetry, the SSL layers are separated by a centering translation resulting in two inequivalent propagation vectors that each connects to one magnetic sublattice with a “stripe” order when viewing two layers together. Therefore, a FM interlayer interaction, Jz, also needs to be considered, which is likely as weak as J” due to the larger atomic distance between interacting spins, however, necessary to stabilize the magnetic order at zero field, distinct from the magnetic order reported in BaNd2ZnO525. Each SSL layer individually exhibits a Néel phase arrangement where the potential interaction paths consist of a dominant FM J’ and a weak AFM J”. The refined Nd magnetic moment was determined to be 2.6(1) μB. Figure 1e shows a plot of the calculated structure factor square (F2calc) versus the observed one (F2obs) and the magnetic structure can be seen in Fig. 1f where the orange and blue atoms represent the two different sublattices and the overlapping layers along the c axis are indicated by the light and dark color shades.
Field-induced phase evolution
The magnetization curves below TN of BaNd2ZnS5 show kinks around 1.7 T for fields along the [1 −1 0] direction, as shown by Fig. 2a, indicating a metamagnetic transition. To investigate this transition, single crystal neutron diffraction measurements were performed with an applied magnetic field of 2 and 6 T parallel to the [1 −1 0] direction. As the field-induced transition emerges around 1.7 T, at 1.4 K, the field-dependent magnetic scattering at (1.5 1.5 1) disappears at 1.7 T (see Fig. 2c) signifying the stripe phase with q2 = (-½, ½, 0) is no longer present. Therefore, the kink shown in the magnetization measurement is a signature of the magnetic order-disorder transition in the magnetic sublattice with spins parallel to the field and the corresponding field can be viewed as the critical field HC for this transition. For the other magnetic sublattice, the magnetic peak (½ ½ 4) gradually decreases with the field increasing but the majority of the magnetic peak signal is maintained up to 6 T (see Fig. 2c inset). By analyzing the neutron diffraction data collected at 2 and 6 T at 1.4 K, the refined magnetic moments for the stripe phase of the q1 magnetic sublattice with spins along [1 1 0], perpendicular to the field direction, were determined to be 2.8(1) and 2.6(1) μB, respectively.
a Magnetization measurement with H//[1 −1 0] from 1.8 to 3.8 K. b Plots of dM/dH measured at constant temperature from 1.8 to 3.8 K, data were smoothed for the derivation, with an inset of dM/dH|max versus temperature as derived from the maximum value of the sharp peak in dM/dH, the red line represents the power-law dependence ~ T−n (n = 3.1). c Field-dependent order parameter from 0 to 2 T at (1.5 1.5 1). The inset for the field-dependent order parameter from 2 to 6 T at (½ ½ 4). d Experimental versus calculated structure factors at 2 T (red circles) and 6 T (blue triangles). e The refined magnetic structure of the partially disordered phase at 2 T and f the field polarized state at 6 T with the square lattice of FM spin dimers shown by the dashed dark orange lines.
At 2 and 6 T the observed magnetic reflections from the diffraction patterns could be all indexed by q1 = (½, ½, 0), while no peaks could be indexed with q2 = (−½, ½, 0) when considering the body centering translation symmetry. Note, the body-centered unit cell is not a primitive cell and so q1 and q2 are not equivalent. From the k-SUBGROUPSMAG program, the low symmetry space group P1 (#1.1) was initially selected to test the potential magnetic models under field. The resulting refinement reveals a partially disordered state of ferromagnetic dimers at 2 T in one magnetic sublattice (Fig. 2e) and while the AFM order in the other magnetic sublattice with moments along [1 1 0] (q1 magnetic sublattice) survives (Fig. 2e and 2f). The results also indicate the two magnetic sublattices are interaction-decoupled and can be separated under an applied field, which confirms that the interaction J between the two magnetic sublattices is weak, i.e., no strong antisymmetric exchange interactions between the orthogonally arranged neighboring Nd spin dimers. This separation can also be observed as two TN’s connected to the two sublattices under field, see Supplementary Figs. S1 and S2. Considering the magnetic interaction distance and the localized f-electron feature for the rare-earth spins, both J” and Jz are much weaker compared to the intra-dimer interaction J’. Therefore, the SSL in BaNd2ZnS5 can be viewed as two decoupled square lattices of ferromagnetic dimers that are loosely 3-dimensionally connected. While the magnetic phase transitions induced by the field up to 6 T along [1 −1 0] at 1.4 K is likely only within the q2 magnetic sublattice with Nd3+ moments along [1 −1 0]. Therefore, the following discussions will be focused on only the magnetic dimer square sublattice with spins parallel to the field [1 −1 0] (the square lattice of FM spin dimers is shown in Fig. 2e and f as the dark orange line for the magnetic sublattice with spins along [1 −1 0]).
Neutron diffraction revealed that the q2 stripe order is fully suppressed by the field at the critical field HC ~ 1.7 T. Field-induced magnetic signal on top of the nuclear Bragg peaks were refined as uniformly aligned moments of 1.2(2) μB at 2 T for the magnetic sublattice with the spin Ising axis along [1 −1 0] // H, i.e., 0.6(1) μB per Nd3+ if averaging it for the whole magnetic lattice, consistent with the increased magnetization in the bulk measurement. If we consider the model of the square lattice of ferromagnetic dimers as described above, each ferromagnetic dimer includes two parallel aligned spin-half moments and so makes a spin-1 dimer with S = 1 as the ground state. When a field is applied, two kinds of dimer spin transitions among three magnetic components (SZ = −1, 0, +1) can occur and cause the order-disorder transition and yield the average induced moment as seen by neutrons. One is a spin-flip transition from SZ = −1 to SZ = +1 and the other one is a spin-flop transition from SZ = −1 to SZ = 0, the quantum version of the well-known spin-flop transition in a weak-magnetic-anisotropic AFM system46,47. Both spin component transitions are illustrated in Fig. 3b. The flipped or flopped spin dimers are disordered in the lattice space because no additional superlattice ordering peaks were observed. Therefore, we refer to this partial disorder as a liquid-like state, i.e., dimer liquid. More dynamic measurements are needed to further characterize the nature of the dimer liquid state in contrast to the reported Luttinger liquid state in the SSL material Yb2Pt2Pb48, the quantum spin liquid phase in the Kitaev honeycomb-lattice RuCl349, and the magnetization plateau phases in the SSL material SrCu2(BO3)210,12,13,14,15,16,17,18,19,20,21. At 6 T the square magnetic sublattice with Nd spins along [1 −1 0] enters a field polarized state and has a refined magnetic moment of 2.8(1) μB, the magnetic structure is shown in Fig. 2f.
a Field versus TN (H–T) phase diagram with H//[1 −1 0], the magnetic susceptibility, magnetization and neutron data are represented by the light blue diamonds and blue triangles for the two measurements which were performed, yellow circles and green squares, respectively. The H-T phase diagram overlays a contour plot mapping the values of dM/dH obtained at constant temperatures, the values of dM/dH are represented by the color scale. b A possible dynamical magnetic pattern at the HC, the dotted red-circle highlights the spin-flip transition from SZ = −1 to SZ = +1 and the dotted black-circle highlights the spin-flop transition from SZ = −1 to SZ = 0, the orange balls in the black-circle symbolize no magnetic moment is present.
Phase diagram and spin dimer liquid
We can construct the field-temperature (H–T) phase diagram from the magnetization data upon varying temperature since neutron diffraction reveals that the kink observed in the magnetization indicates the disorder transition from the stripe order in the q2 magnetic sublattice. The critical field HC at each temperature can be better observed as a sharp peak in the plots of dM/dH (see Fig. 2b), where upon cooling, the HC shifts towards higher fields, HC ~1.5 T at 1.8 K. Above HC, the transition to the field polarized state can be seen by the broad bump feature at higher field. A contour plot mapping the values of dM/dH obtained from 1.8 to 3.8 K, is depicted in a H versus T (H–T) phase diagram describing the magnetic sublattice with spins parallel to the field direction [1 −1 0], Fig. 3a, based on the bulk magnetization (circles) and susceptibility (diamonds and triangles) measurements under the field along [1 −1 0] and neutron data (square). Phase I represents the 2-Q magnetically ordered stripe phase while phase II is the dimer liquid phase. The contour plot of dM/dH clearly defines the regions for Phase I and II and furthermore the transition to the field polarized state as Phase III. According to the neutron diffraction measurement at 1.4 K, no additional magnetic order was observed when the stripe phase enters the spin dimer liquid state, Phase II, at 1.7 T, indicating the critical region is further narrowed towards a possible critical point.
A similar temperature dependence of the behavior of HC in Fig. 3a has been observed in the phase diagrams of geometrically frustrated lattices exhibiting field-induced quantum criticality, such as CoNb2O650,51 and RuCl349, constructed from heat capacity measurements under field. A possible explanation of such a H–T behavior in BaNd2ZnS5 can be explained by field-melting the stripe ordered phase through “spin-flip-or-flop” transitions. The H–T phase diagram could also suggest the possibility that quantum criticality may exist in BaNd2ZnS5 at the lowest temperature. Additional evidence is shown by the plot of dM/dH|max versus T in the Fig. 2b inset that demonstrates the power law fitting ~T-n, where it has been constrained to n = 3.1 to assess the possibility of quantum critical fluctuations as determined for the antiferromagnet CePtIn452. Down to 1.8 K BaNd2ZnS5 resembles that of the linear higher temperature region in the power law fitting of CePtIn4, suggesting a certain similarity of the two systems. To explore these scenarios and reveal the enigmatic magnetic ground state of BaNd2ZnS5, low temperature heat capacity, magnetization and inelastic neutron scattering measurements are required. In summary, single crystals of BaNd2ZnS5 from the BaR2ZnS5 family have been successfully synthesized and studied by magnetic bulk measurement and neutron diffraction under magnetic field. Ising magnetic anisotropy of the Nd spins is revealed by the local magnetic susceptibility method with polarized neutrons and their Ising directions are orthogonal to the dimer bonds. Such an arrangement of Ising spins implies symmetric exchange interactions cannot couple the orthogonally arranged dimers. The zero-field magnetic order is a 2-Q AFM order of FM dimers with Nd spins along their local Ising directions. Two magnetic sublattices with q1 = (½, ½, 0) and q2 = (-½, ½, 0) constitute the 2-Q structure and respond to the field along [1 −1 0] differently. The q2 magnetic order is suppressed at a critical field, responsible for the kink observed in the magnetization measurement. While the q1 magnetic sublattice stays mostly unchanged until 6 T. According to this information, we built the H-T phase diagram from the bulk magnetization and magnetic susceptibility. A critical region was manifested as a spin dimer liquid phase growing out between the stripe phase at lower field and the field polarized phase at upper field. “Spin-flip” and “spin-flop” mechanisms were proposed to explain the formation of the liquid state. Whether the dimer liquid phase could condense at an ultra-low temperature deserves further study. As BaNd2ZnS5 exhibits a unique 2-Q magnetic square lattice with weak interactions between orthogonal dimers, it can be an exciting candidate to exhibit unique high order symmetries and a potential host for exotic quantum phases. Future dynamic studies including inelastic neutron scattering can provide insight into magnetic interactions and emergent states in the BaNd2ZnS5 SSL and discover interesting dynamic properties of ferromagnetic dimers. An effort in synthesizing large, high quality single crystals is thus called for, as available high-quality single crystals make all these possible.
Methods
Neutron diffraction
To determine the magnetic order single crystal neutron diffraction experiments on the HB-3A DEMAND53 at the High Flux Isotope Reactor at Oak Ridge National Laboratory. A 1.5 mm sample was measured with the two-axis mode down to 1.4 K using a cryomagnet and a wavelength of 1.542 Å from a bent Si-220 monochromator54. The measurement was performed with an applied magnetic field of 0, 2 and 6 T parallel to [1 −1 0]. The Bilbao Crystallography Server55 was used for the magnetic symmetry analysis and Fullprof software56 for the magnetic structure refinement. Polarized single crystal neutron diffraction measurements was likewise performed on the HB-3A DEMAND with a polarized neutron beam of 1.542 Å and the calibrated neutron polarization is 72%. The crystal was loaded in a closed-cycle refrigerator with a permanent magnet set providing the fixed field of 0.5 T along [1 −1 0]. We measured 17 flipping ratios at 5 K, above TN. To analyze the resulting flipping ratios the CrysPy software57 was used.
Data availability
All relevant data are available from the corresponding author upon reasonable request.
References
Balents, L. Spin liquids in frustrated magnets. Nature 464, 199–208 (2010).
Lacroix, C., Mendels, P. & Mila, F. eds. Introduction to Frustrated Magnetism: Materials, Experiments, Theory. vol. 164 (Springer, 2011).
Smith, R. W. & Keszler, D. A. Synthesis, structure, and properties of the orthoborate SrCu2(BO3)2. J. Solid State Chem. 93, 430–435 (1991).
McClarty, P. A. et al. Topological triplon modes and bound states in a Shastry–Sutherland magnet. Nat. Phys. 13, 736–741 (2017).
Yang, J., Sandvik, A. W. & Wang, L. Quantum criticality and spin liquid phase in the Shastry-Sutherland model. Phys. Rev. B 105, L060409 (2022).
Dwivedi, V., Hickey, C., Eschmann, T. & Trebst, S. Majorana corner modes in a second-order Kitaev spin liquid. Phys. Rev. B 98, 054432 (2018).
Eschmann, T., Dwivedi, V., Legg, H. F., Hickey, C. & Trebst, S. Partial flux ordering and thermal Majorana metals in higher-order spin liquids. Phys. Rev. Res. 2, 043159 (2020).
King, A. D., Nisoli, C., Dahl, E. D., Poulin-Lamarre, G. & Lopez-Bezanilla, A. Qubit spin ice. Science 373, 576–580 (2021).
Sriram Shastry, B. & Sutherland, B. Exact ground state of a quantum mechanical antiferromagnet. Phys. B+C. 108, 1069–1070 (1981).
Guo, J. et al. Quantum phases of SrCu2(BO3)2 from high-pressure thermodynamics. Phys. Rev. Lett. 124, 206602 (2020).
Corboz, P. & Mila, F. Tensor network study of the Shastry-Sutherland model in zero magnetic field. Phys. Rev. B 87, 115144 (2013).
Miyahara, S. & Ueda, K. Superstructures at magnetization plateaus in SrCu2(BO3)2. Phys. Rev. B 61, 3417–3424 (2000).
Kodama, K. et al. Magnetic superstructure in the two-dimensional quantum antiferromagnet SrCu2(BO3)2. Science 298, 395–399 (2002).
Takigawa, M. et al. Incomplete Devil’s Staircase in the Magnetization Curve of SrCu2(BO3)2. Phys. Rev. Lett. 110, 067210 (2013).
Jaime, M. et al. Magnetostriction and magnetic texture to 100.75 Tesla in frustrated SrCu2(BO3)2. Proc. Natl. Acad. Sci. 109, 12404–12407 (2012).
Sebastian, S. E. et al. Fractalization drives crystalline states in a frustrated spin system. Proc. Natl. Acad. Sci. 105, 20157–20160 (2008).
Matsuda, Y. et al. Magnetization of SrCu2(BO3)2 in ultrahigh magnetic fields up to 118 T. Phys. Rev. Lett. https://doi.org/10.1103/PhysRevLett.111.137204 (2013).
Kageyama, H. et al. Exact dimer ground state and quantized magnetization plateaus in the two-dimensional spin system SrCu2(BO3)2. Phys. Rev. Lett. 82, 3168–3171 (1999).
Kodama, K. et al. Field-induced effects of anisotropic magnetic interactions in SrCu2(BO3)2. J. Phys.: Condens. Matter 17, L61–L68 (2005).
Zayed, M. E. et al. 4-spin plaquette singlet state in the Shastry–Sutherland compound SrCu2(BO3)2. Nat. Phys. 13, 962–966 (2017).
Koga, A. & Kawakami, N. Quantum Phase Transitions in the Shastry-Sutherland Model for SrCu2(BO3)2. Phys. Rev. Lett. 84, 4461–4464 (2000).
Berrada, A. et al. Synthese, cristallogenese, proprietes magnetiques et effets magnetostrictifs spontanes de quelques tetraborures de terres rares. Mater. Res. Bull. 11, 1519–1526 (1976).
Siemensmeyer, K. et al. Fractional magnetization plateaus and magnetic order in the Shastry-Sutherland magnet TmB4. Phys. Rev. Lett. 101, 177201 (2008).
Ye, L., Suzuki, T. & Checkelsky, J. G. Electronic transport on the Shastry-Sutherland lattice in Ising-type rare-earth tetraborides. Phys. Rev. B 95, 174405 (2017).
Ishii, Y. et al. Magnetic properties of the Shastry-Sutherland lattice material BaNd2ZnO5. Phys. Rev. Mater. 5, 064418 (2021).
Kaduk, J. A., Wong-Ng, W., Greenwood, W., Dillingham, J. & Toby, B. H. Crystal structures and reference powder patterns of BaR2ZnO5 (R = La, Nd, Sm, Eu, Gd, Dy, Ho, Y, Er, and Tm). NIST 104 2, (1999).
Taniguchi, T. et al. Antiferromagnetism of R2BaPdO5 (R = La, Nd, Pr, Sm, Eu, Gd, Dy, Ho). J. Alloy. Compd. 386, 63–69 (2005).
Ishii, Y. et al. High-pressure synthesis, crystal structure, and magnetic properties of the Shastry-Sutherland-lattice oxides BaLn2ZnO5 (Ln = Pr, Sm, Eu). J. Solid State Chem. 289, 121489 (2020).
Zaremba, V. I. et al. Structure and physical properties of RE2Ge2In (RE = La, Ce, Pr, Nd). Solid State Sci. 6, 1301–1306 (2004).
Tobash, P. H. et al. Crystal growth, structural, and property studies on a family of ternary rare-earth phases RE2InGe2 (RE = Sm, Gd, Tb, Dy, Ho, Yb). Chem. Mater. 17, 5567–5573 (2005).
Fischer, P. et al. Antiferromagnetic rare-earth ordering in the intermetallic compounds R2Pd2In (R = Pr, Nd). J. Phys.: Condens. Matter 12, 7089–7098 (2000).
Miiller, W. et al. Magnetic structure of Yb2Pt2Pb: ising moments on the Shastry-Sutherland lattice. Phys. Rev. B 93, 104419 (2016).
Isaev, L., Ortiz, G. & Dukelsky, J. Local physics of magnetization plateaux in the Shastry-Sutherland model. Phys. Rev. Lett. 103, 177201 (2009).
Orendáč, M. et al. Ground state and stability of the fractional plateau phase in metallic Shastry–Sutherland system TmB4. Sci. Rep. 11, 6835 (2021).
Wierschem, K. et al. Origin of modulated phases and magnetic hysteresis in TmB4. Phys. Rev. B 92, 214433 (2015).
Iwakawa, K. et al. Multiple metamagnetic transitions in antiferromagnet Yb2Pt2Pb with the Shastry–Sutherland lattice. J. Phys. Soc. Jpn. 81, SB058 (2012).
Shimura, Y., Sakakibara, T., Iwakawa, K., Ōnuki, Y. & Sugiyama, K. Magnetization steps in Yb2Pt2Pb with the Shastry-Sutherland lattice. J. Korean Phys. Soc. 63, 551–554 (2013).
Ochiai, A. et al. Field-induced partially disordered state in Yb2Pt2Pb. J. Phys. Soc. Jpn. 80, 123705 (2011).
Kim, M. S. & Aronson, M. C. Spin liquids and antiferromagnetic order in the Shastry-Sutherland-lattice compound Yb2Pt2Pb. Phys. Rev. Lett. 110, 017201 (2013).
Michimura, S., Shigekawa, A., Iga, F., Takabatake, T. & Ohoyama, K. Complex magnetic structures of a Shastry–Sutherland lattice TmB4 studied by powder neutron diffraction analysis. J. Phys. Soc. Jpn. 78, 024707 (2009).
Wakeshima, M. et al. Specific heat and neutron diffraction study on quaternary sulfides BaNd2CoS5 and BaNd2ZnS5. J. Solid State Chem. 174, 159–164 (2003).
Billingsley, B. R., Marshall, M., Shu, Z., Cao, H. & Kong, T. Single crystal synthesis and magnetic properties of a Shastry-Sutherland lattice compound BaNd2ZnS5. Phys. Rev. Mater. 6, 104403 (2022).
Lhotel, E. et al. Fluctuations and all-in–all-out ordering in dipole-octupole Nd2Zr2O7. Phys. Rev. Lett. 115, 197202 (2015).
Cao, H. et al. Ising versus XY anisotropy in frustrated R2Ti2O7 compounds as “seen” by polarized neutrons. Phys. Rev. Lett. 103, 056402 (2009).
Cao, H. B., Gukasov, A., Mirebeau, I. & Bonville, P. Anisotropic exchange in frustrated pyrochlore Yb2Ti2O7. J. Phys. Condens. Matter 21, 492202 (2009).
Fiebig, M., Fröhlich, D. & Thiele, H.-J. Determination of spin direction in the spin-flop phase of Cr2O3. Phys. Rev. B 54, R12681–R12684 (1996).
Ding, L. et al. Noncollinear magnetic structure and magnetoelectric coupling in buckled honeycomb Co4Nb2O9: a single-crystal neutron diffraction study. Phys. Rev. B 102, 174443 (2020).
Gannon, W. J. et al. Spinon confinement and a sharp longitudinal mode in Yb2Pt2Pb in magnetic fields. Nat. Commun. 10, 1123 (2019).
Wolter, A. U. B. et al. Field-induced quantum criticality in the Kitaev system alpha-RuCl3. Phys. Rev. B 96, 041405 (2017).
Liang, T. et al. Heat capacity peak at the quantum critical point of the transverse Ising magnet CoNb2O6. Nat. Commun. 6, 7611 (2015).
Kinross, A. W. et al. Evolution of quantum fluctuations near the quantum critical point of the transverse field ising chain system CoNb2O6. Phys. Rev. X 4, 031008 (2014).
Das, D., Gnida, D., Wiśniewski, P. & Kaczorowski, D. Magnetic field-driven quantum criticality in antiferromagnetic CePtIn4. Proc. Natl Acad. Sci. 116, 20333–20338 (2019).
Cao, H. et al. DEMAND, a dimensional extreme magnetic neutron diffractometer at the high flux isotope reactor. Crystals 9, 5 (2019).
Chakoumakos, B. C. et al. Four-circle single-crystal neutron diffractometer at the High Flux Isotope Reactor. J. Appl. Cryst. 44, 655–658 (2011).
Perez-Mato, J. M. et al. Symmetry-based computational tools for magnetic crystallography. Annu. Rev. Mater. Res. 45, 217–248 (2015).
Rodríguez-Carvajal, J. Recent advances in magnetic structure determination by neutron powder diffraction. Phys. B: Condens. Matter 192, 55–69 (1993).
Kibalin, I. A. & Gukasov, A. Local magnetic anisotropy by polarized neutron powder diffraction: Application of magnetically induced preferred crystallite orientation. Phys. Rev. Res. 1, 033100. https://github.com/ikibalin/cryspy (2019).
Acknowledgements
The research at Oak Ridge National Laboratory (ORNL) was supported by the U.S. Department of Energy (DOE), Office of Science, Office of Basic Energy Sciences, Early Career Research Program Award KC0402020, under Contract DE-AC05-00OR22725. This research used resources at the High Flux Isotope Reactor, a DOE Office of Science User Facility operated by ORNL. We acknowledge and thank Zachary Morgan for the assistance with the data reduction of the neutron diffraction experiments. We acknowledge and thank Cristian Batista for the helpful discussions. We thank Chenyang Jiang for the assistance with the experimental polarized neutron diffraction.
Author information
Authors and Affiliations
Contributions
H.C. cultivated the research; B.R.B. and T.K. synthesized single-crystal samples and performed magnetization measurements; M.M. and H.C. performed neutron scattering experiments and analyze the data; X.B. assisted with polarized neutron data analysis; X.B. and Q.M. contributed to theoretical discussion; M.M. and H.C. wrote manuscript with comments from all authors.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests. This manuscript has been authored by UT-Battelle, LLC under Contract No. DE-AC05-00OR22725 with the U.S. Department of Energy. The United States Government retains and the publisher, by accepting the article for publication, acknowledges that the United States Government retains a non-exclusive, paidup, irrevocable, world-wide license to publish or reproduce the published form of this manuscript, or allow others to do so, for United States Government purposes. The Department of Energy will provide public access to these results of federally sponsored research in accordance with the DOE Public Access Plan (http://energy.gov/downloads/doepublic-access-plan).
Peer review
Peer review information
Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Marshall, M., Billingsley, B.R., Bai, X. et al. Field-induced partial disorder in a Shastry-Sutherland lattice. Nat Commun 14, 3641 (2023). https://doi.org/10.1038/s41467-023-39409-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-023-39409-1
- Springer Nature Limited