Abstract
One-dimensional chiral interface channels can be created at the boundary of two quantum anomalous Hall (QAH) insulators with different Chern numbers. Such a QAH junction may function as a chiral edge current distributer at zero magnetic field, but its realization remains challenging. Here, by employing an in-situ mechanical mask, we use molecular beam epitaxy to synthesize QAH insulator junctions, in which two QAH insulators with different Chern numbers are connected along a one-dimensional junction. For the junction between Chern numbers of 1 and −1, we observe quantized transport and demonstrate the appearance of the two parallel propagating chiral interface channels along the magnetic domain wall at zero magnetic field. For the junction between Chern numbers of 1 and 2, our quantized transport shows that a single chiral interface channel appears at the interface. Our work lays the foundation for the development of QAH insulator-based electronic and spintronic devices and topological chiral networks.
Similar content being viewed by others
Introduction
Topological materials are unique solid-state systems that exhibit topologically protected boundary states (i.e., edge/surface states). As a consequence of the intrinsic protection that prevents impurity scattering and allows for manipulations and measurements, these topological edge/surface states have been predicted to be useful for the next generation of quantum-based electronic and spintronic devices as well as topological quantum computations1,2. Over the past ~15 years, topological band theory has played a key role in the discovery of new topological materials1,2,3,4. The interplay between the bulk topology and protected edge/surface states in topological materials is usually referred to as the bulk-boundary correspondence. In other words, the formation of the topological edge/surface states is guaranteed by the topological character of the bulk bands. In addition to the edge/surface states in naturally occurring topological materials, topologically protected interface states can also be engineered at the interfaces between two materials with different topological invariants.
The quantum anomalous Hall (QAH) insulator is a prime example of two-dimensional (2D) topological states and possesses dissipation-free chiral edge states (CESs) on its boundaries4,5,6,7,8,9,10. In QAH insulators, the Hall resistance is quantized at h/e2 and the longitudinal resistance vanishes under zero magnetic field. The QAH effect was first realized in magnetically doped topological insulators (TI), specifically, Cr-doped and/or V-doped (Bi, Sb)2Te3 thin films7,8,10,11,12,13,14,15. More recently, the QAH effect was also observed in thin flakes of intrinsic magnetic TI MnBi2Te4 (Ref. 16) and moiré materials formed from graphene17 or transition metal dichalcogenides18. According to topological band theory, chiral interface channels (CICs) also appear at the interfaces between two QAH insulators with different Chern numbers C. The CIC number is determined by the difference in C between these two adjacent QAH insulator domains. The CIC propagating direction (i.e., chirality) is dictated by the relative orientation of the spontaneous magnetization in the two QAH insulators1,2,19. Therefore, the creation and manipulation of CESs and/or CICs can facilitate the development of topological chiral networks20,21, which have the potential for applications in energy-efficient QAH-based electronic and spintronic devices. Moreover, it has been proposed that chiral Majorana physics in QAH/superconductor heterostructures can be probed by placing a grounded superconductor island on the domain boundary between C = + 1 and C = −1 QAH insulators in a Mach-Zehnder interferometer configuration22,23. Magnetic force microscope (MFM)24 and the Meissner effect of a bulk superconductor cylinder25 have been employed to create a magnetic domain wall (DW) in QAH insulators, which is unfeasible for device fabrication. Therefore, the synthesis of a designer magnetic DW in a QAH insulator (i.e., a junction between C = + 1 and C = −1 QAH insulators) and the junction between two QAH insulators with arbitrary C are highly desirable with exceptional promise for potential topological circuit applications.
In this work, we synthesize QAH insulator junctions in magnetic TI/TI multilayer heterostructures by employing an in-situ mechanical mask in our MBE chamber. Our electrical transport measurements show quantized transport in these QAH insulator junctions, which indicates the appearance of the CICs near the magnetic DW. For the junction between C = + 1 and C = −1 QAH insulators, we find two parallel propagating CICs at the magnetic DW. For the junction between C = 1 and C = 2 QAH insulators, one CES tunnels through the QAH DW entirely, while the second CIC propagates along the QAH DW. The number of CICs is determined by the difference in C between the two QAH insulators. We show these QAH insulator junctions with robust CICs are feasible for device fabrication and thus provide a platform for the development of QAH-based electronic and spintronic devices and topological quantum computations.
Results
MBE growth and electrical transport measurements
All QAH junction samples are grown on heat-treated ~0.5 mm thick SrTiO3(111) substrates in a commercial MBE chamber (Omicron Lab10) (Method; Supplementary Figs. 1 to 3). The Bi/Sb ratio in each layer is optimized to tune the chemical potential of the sample near the charge neutral point7,8,26,27,28. The electrical transport measurements are carried out in a Physical Property Measurements System (Quantum Design DynaCool, 1.7 K, 9 T) and a dilution refrigerator (Leiden Cryogenics, 10 mK, 9 T) with the magnetic field applied perpendicular to the sample plane. The mechanically scratched Hall bars are used for electrical transport measurements. More details about the MBE growth and electrical transport measurements can be found in Methods.
The junction between C = + 1 and C = −1 QAH insulators
We first focus on the junction between C = + 1 and C = −1 QAH insulators (Fig. 1a). To create this junction, we grow 2 quintuple layers (QL) (Bi,Sb)1.74Cr0.26Te3/2 QL (Bi,Sb)2Te3/2 QL (Bi,Sb)1.74Cr0.26Te3 sandwich heterostructure. Next, by placing an in-situ mechanical mask as close as possible to the sample surface (Supplementary Fig. 1), we deposit 2 QL (Bi, Sb)1.78V0.22Te3 on one side of the sample. Since the coercive field (μ0Hc) of V-doped (Bi, Sb)2Te3 films is much larger than that of Cr-doped (Bi, Sb)2Te3 films8,29, the μ0Hc of the Cr-doped (Bi, Sb)2Te3 sandwich layer is enhanced as a result of the existence of the interlayer exchange coupling30,31,32. We note that the middle 2 QL undoped (Bi, Sb)2Te3 layer is chosen here to couple the magnetizations of the two Cr-doped (Bi, Sb)2Te3 layers. As a consequence, the areas with (i.e., Domain II) and without (i.e., Domain I) 2 QL (Bi, Sb)1.78V0.22Te3 possess different values of μ0Hc. When an external μ0H is tuned between two μ0Hcs, an antiparallel magnetization alignment appears between Domain I (with μ0Hc1) and Domain II (with μ0Hc2). Therefore, a junction between C = + 1 and C = −1 QAH insulators is created (Figs.1a, 1b, and Supplementary Figs. 4–10). Such a QAH DW can persist at zero magnetic field (Fig. 2d, e, and Supplementary Figs. 9, 10).
To characterize its magnetic property, we perform reflective magnetic circular dichroism (RMCD) measurements on the junction between C = + 1 and C = −1 QAH insulators at T = 2.5 K (Fig. 1c–g, and Supplementary Fig. 4). The RMCD signals of both C = + 1 and C = −1 QAH domains show hysteresis loops with different values of μ0Hc, confirming the ferromagnetic properties of the magnetic TI multilayers. The μ0Hc1 value of Domain I is ~0.035 T, while the μ0Hc2 value of Domain II is ~0.110 T (Fig. 1f, g). By mapping the samples under μ0H~ −0.075 T, between μ0Hc1 and μ0Hc2, we recognize Domain I and Domain II. This further confirms that a magnetic DW is created at the boundary of Domain I and Domain II (Fig. 1d, e, and Supplementary Fig. 4). Next, we perform electrical transport measurements on Domain I and Domain II at T = 25 mK and at the charge neutral point Vg = Vg0. Both domains show well quantized C = 1 QAH effect. For Domain I, the Hall resistance ρyx under zero magnetic field [labeled as ρyx(0)] is ~0.988 h/e2, concomitant with ρxx(0) ~0.003 h/e2 (~80 Ω) (Fig. 1h). For Domain II, ρyx(0)~0.985 h/e2 and ρxx(0) ~0.0008 h/e2 (~20 Ω) (Fig. 1i). At T = 25 mK, the values of μ0Hc1 and μ0Hc2 are found to be ~0.195 T and ~0.265 T, respectively. Both values are much larger than those measured in RMCD at T = 2.5 K (Fig. 1f, g). Therefore, when μ0Hc is tuned between μ0Hc1 and μ0Hc2, Domain I and Domain II possess antiparallel magnetization alignment, and thus a junction between C = + 1 and C = −1 QAH insulator is established.
Next, we perform magneto-transport measurements across the magnetic DW at T = 25 mK and Vg = Vg0. The schematic of the Hall bar device is shown in Fig. 2a. The μ0H dependence of the longitudinal resistance across the magnetic DW ρ14,23 and ρ14,65 is shown in Fig. 2b, c, respectively. The red (blue) curves represent upward (downward) μ0H sweeps. When Domain I and Domain II have the parallel magnetization alignment, the entire sample behaves as a QAH insulator with 1D CESs along its edges and thus both ρ14,23 and ρ14,65 vanish. Since μ0Hc of Domain II (i.e., μ0Hc2 ~0.265 T) is larger than that of Domain I (i.e., μ0Hc1 ~0.195 T), sweeping external μ0H first reverses the magnetization of Domain I. Therefore, when μ0H is tuned between μ0Hc1 and μ0Hc2, the magnetizations of Domain I and Domain II are in antiparallel alignment and thus a magnetic domain boundary is formed in a C = 1 QAH insulator (Figs. 1a and 2a), consistent with our RMCD results on the same device (Fig. 1d, e, and Supplementary Fig. 4). For the Domain I-downward-Domain II-upward state, ρ14,23~2.017 h/e2 and ρ14,65 ~0.024 h/e2. However, for the Domain I-upward-Domain II-downward state, ρ14,23 ~ 0.018 h/e2 and ρ14,65 ~ 2.009 h/e2. During each magnetization reversion, the quantized transport via the dissipation-free CES in the corresponding domain fades away. Therefore, half of the sample becomes dissipative and a large longitudinal resistance peak appears. This is the reason for the two-peak feature in ρ14,23 (Fig. 2b), ρ14,65 (Fig. 2c), and ρ14,14 (Fig. 2f). To examine the quantized transport across the magnetic DW in a C = 1 QAH insulator, we measure μ0H dependence of ρ14,23 and ρ14,65 at different gate voltages Vg under different DW configurations (Supplementary Fig. 7). We note that these quantized transport behaviors can be well interpreted by the Landauer–Büttiker formalism based on the assumption that each CIC has ~50% transmission probability through the magnetic DW between Domain I and Domain II (Fig. 2a; Supplementary Note 4). Finally, we demonstrate that this artificial magnetic DW in a C = 1 QAH insulator persists at zero magnetic field by minor loop measurements (Fig. 2d, e, and Supplementary Figs. 9, 10).
Figure 2f shows the μ0H dependence of the two-terminal resistance ρ14,14 at T = 25 mK and Vg = Vg0. By tuning the magnetizations of Domain I and Domain II from parallel to antiparallel alignments, the value of ρ14,14 is found to change from ~ h/e2 to ~2 h/e2, confirming the assumption that the transmission probability of the CIC through the magnetic DW is ~50%. Figure 2g shows the μ0H dependence of the Hall resistance ρ14,23–65, which is measured by contact configurations 2,3 and 6,5. Here contacts 2 and 3 are connected, same for contacts 5 and 6. The observation of the zero Hall resistance plateau for μ0Hc1 < μ0H < μ0Hc2 validates the appearance of the two parallel CICs at the magnetic DW. The same behavior is also observed in the second device with the contacts directly sitting on the magnetic DW boundary (Supplementary Fig. 9f). We note that in this device the two-terminal resistance along the magnetic DW ρ78,78 is ~ h/2e2 under μ0Hc1 < μ0H < μ0Hc2, further validating the emergence of two parallel CICs at the magnetic DW between C = + 1 and C = −1 QAH insulators (Supplementary Fig. 9g).
To demonstrate the current splitting function of the QAH junction, we perform current distribution measurements to directly detect the two parallel CICs at the junction interface. As shown by the red lines in Fig. 3a–d, we first inject a bias current I of ~1 nA at contact 1 and measure the currents flowing to the ground through contacts 2 (I2) and 3 (I3 = I - I2) with all other floating contacts. When Domain I and Domain II have negative parallel magnetization (i.e., M < 0) alignment, ~97% of the drain current is found to flow through contact 2, while ~3% of the drain current flows through contact 3 (Fig. 3a, e). The nonzero drain current through contact 3 is attributable to residual dissipation channels in the QAH insulator device33,34. However, when Domain I and Domain II have positive parallel magnetization (i.e., M > 0) alignment, ~5% of the drain current flows through contact 2, while ~95% of the drain current flows through contact 3 (Fig. 3c, e). For μ0Hc1 < μ0H < μ0Hc2, i.e., under the Domain I-upward-Domain II-downward configuration, we find I2 = I3, which is direct evidence for the existence of two parallel propagating CICs at the magnetic DW (Fig. 3b, e). However, for -μ0Hc2 < μ0H < -μ0Hc1, i.e., under the Domain I-downward-Domain II-upward configuration, I2 is no longer equal to I3. Instead, I2 and I3 switch the dominance as soon as the magnetic DW appears (i.e., at -μ0Hc1) (Fig. 3d, e). This is a result of the bias current directly flowing to contact 2 without passing through the magnetic DW under Domain I-downward-Domain II-upward configuration. Mirroring behaviors (Fig. 3f) are observed when we measure the currents flowing to the ground through contacts 5 (I5) and 6 (I6 = I – I5) with all other floating contacts, as shown by the blue lines in Fig. 3a–d. The existence of the two parallel propagating CICs at the magnetic DW is further confirmed by injecting the bias current at contact 4 (Supplementary Figs. 8, 10).
The junction between C = 1 and C = 2 QAH insulators
Since the Chern number C of the QAH insulators in magnetic TI/TI multilayers can be tuned by altering the magnetic TI/TI bilayer periodicity27,28, the junction between the two QAH insulators with two arbitrary C can be achieved by growing different periods of magnetic TI/TI on the two sides of the sample. Here we use the junction between C = 1 and C = 2 QAH insulators as an example (Fig. 4 and Supplementary Figs. 11, 12). As shown in Fig. 4a, Domain I is 3QL (Bi, Sb)1.74Cr0.26Te3/4QL (Bi, Sb)2Te3/3QL (Bi, Sb)1.74Cr0.26Te3 sandwich heterostructure with the C = 1 QAH state, while Domain II is [3QL (Bi, Sb)1.74Cr0.26Te3/4QL (Bi, Sb)2Te3]2/3QL (Bi, Sb)1.74Cr0.26Te3 penta-layer heterostructure with the C = 2 QAH state27,28. We perform electrical transport measurements on this QAH junction with the Hall bar configuration as shown in Fig. 4b. We find that the Hall resistance ρ14,26 of Domain I is ~0.987 h/e2 and ρ14,35 of Domain II is ~0.494 h/e2 under zero magnetic field at T = 25 mK and Vg = Vg0, confirming the C = 1 and C = 2 QAH states in Domain I and Domain II, respectively (Fig. 4c). After we establish the presence of this junction between C = 1 and C = 2 QAH insulators, we study its properties by measuring ρ14,23 and ρ14,65 across the QAH DW (Fig. 4b). For M > 0, ρ14,23 is found to be ~0.021 h/e2 at zero magnetic field, concomitant with ρ14,65 ~0.526 h/e2. However, for M < 0, ρ14,23 ~0.527 h/e2 and ρ14,65 ~0.022 h/e2 at zero magnetic field (Fig. 4d, e). In other words, the values of ρ14,23 and ρ14,65 always differ by -h/2e2 for M > 0 or +h/2e2 for M < 0 at Vg = Vg0. This constant difference is further demonstrated in the (Vg-Vg0) dependence of ρ14,23(0) and ρ14,65(0) plots (Fig. 4f, g). In addition to the four-terminal resistance ρ14,23 and ρ14,65, we also measure the two-terminal resistance ρ14,14 of the junction between C = 1 and C = 2 QAH insulators. The value of ρ14,14 is found to be ~h/e2 in the well-defined magnetization regime (Supplementary Fig. 12). We note that the ρ14,14 behavior of the junction between C = 1 and C = 2 QAH insulators is essentially similar to that of the individual C = 1 QAH insulator33. This observation confirms that only one chiral edge channel carries current from contact 1 to contact 4.
Discussion
To further understand the property of the CIC at the DW between C = 1 and C = 2 QAH insulators, we assume that the transmission probability of the CIC through the DW between C = 1 and C = 2 QAH insulators is P. Based on the Landauer–Büttiker formalism35, \({\rho }_{{{{{\mathrm{14,23}}}}}}=\frac{1-P}{P}\frac{h}{{e}^{2}}\) and \({\rho }_{{{{{\mathrm{14,65}}}}}}=\frac{2-P}{2P}\frac{h}{{e}^{2}}\) for M > 0 (Fig.4b and Supplementary Fig. 13). We can see that the difference between ρ65 and ρ23 is always ~h/2e2, independent of the value of P. In our devices, the C = 1 and C = 2 QAH insulators have the same coercive field (μ0Hc) and always have parallel magnetization alignment, so the two QAH insulators share the same CES chirality and thus P~1 (Fig. 4b). Therefore, the chiral edge current can flow through the DW between the C = 1 and C = 2 QAH insulators and ρ14,23(0)~0 and ρ14,65(0)~h/2e2 for M > 0 (Fig. 4f).
We further perform current distribution measurements on the junction between the C = 1 and C = 2 QAH insulators. By injecting a bias current I of ~1 nA at contact 1 or 4, we measure the currents flowing to the ground through contacts 5 (I5) and 6 (I6 = I – I5) with all other floating contacts. When the bias current is injected through contact 1, only one CES carries current from contact 1 to contact 4 (Fig.4b and Supplementary Fig. 12), so I5 and I6 switch the dominance during reversing M (Fig. 4h). However, when the bias current is injected through contact 4, two CESs carry the current. For M > 0, one CES passes through the C = 1 QAH domain entirely and flows through contact 6, while the other CES travels along the DW and flows through contact 5. Therefore, the value of I5 is equal to I6 for M > 0, supporting the transmission probability of the CIC through the DW between C = 1 and C = 2 QAH insulators P~1. For M < 0, both CESs of the C = 2 QAH insulator carry current from contact 4 to contact 5 clockwise, and thus the value of I5 is much larger than I6 (Fig. 4i). Therefore, the junction between C = 1 and C = 2 QAH insulators acts as a chiral edge current divider at zero magnetic field.
To summarize, by placing an in-situ mask inside the MBE chamber, we show it is possible to grow two QAH insulators with different Chern numbers separated by a well-defined 1D junction in the form of a DW. Through systematic magneto-resistance measurements with different contact configurations that show the expected quantized and dissipation-free transport with appropriate current distribution, we demonstrate the creation of CICs at the DW between two QAH insulators and find that the number of CICs is determined by the Chern number difference between the two QAH insulators. For the junction between C = + 1 and C = −1 QAH insulators, two parallel CICs propagate along the magnetic DW. For the junction between C = 1 and C = 2 QAH insulators, one CES tunnels through the QAH DW entirely and the other CIC propagates along the QAH DW. Our work provides a comprehensive understanding of the CES/CIC behavior in QAH insulators and advances our knowledge of the interplay between two QAH insulators. Moreover, the synthesis of the junction between two QAH insulators with different Chern numbers provides a unique opportunity to develop a transformative information technology based on the dissipation-free CES/CIC in QAH insulators.
Methods
MBE growth
The QAH insulator junctions (i.e., where two QAH insulators with different C are connected) used in this work are fabricated by using an in-situ mechanical mask in a commercial MBE system (Omicron Lab10) with a base vacuum better than ~2 × 10−10 mbar. The sharp boundary between two QAH insulators is achieved by placing the in-situ mechanical mask as close as possible to the sample surface. All magnetic TI multilayer heterostructures are grown on heat-treated ~0.5 mm thick SrTiO3(111) substrates. Before the growth of the QAH insulator junctions, the heat-treated SrTiO3(111) substrates are first outgassed at ~600 °C for 1 h. Next, high-purity Bi (99.9999%), Sb (99.9999%), Cr (99.999%), V (99.999%), and Te (99.9999%) are evaporated from Knudsen effusion cells. During the growth of the magnetic TI multilayers, the substrate is maintained at ~230 °C. The flux ratio of Te per (Bi + Sb + Cr/V) is set to be greater than 10 to prevent Te deficiency in the films. The Bi/Sb ratio in each layer is optimized to tune the chemical potential of the entire magnetic TI multilayer heterostructure near the charge neutral point. The growth rate of both magnetic TI and TI films is ~0.2 QL per minute.
The in-situ mechanical mask is made from a 0.1 mm thick tantalum (Ta) foil with a physical dimension of ~2 mm × 10 mm. The Ta foil mask is mounted on a custom-designed flag-style sample holder with a Ta screw (Supplementary Fig. 1a). Before the MBE growth, the Ta foil mask is placed in a position where the heat-treated SrTiO3(111) is uncovered. A few periods of magnetic TI/TI multilayers are first grown to form Domain I. Next, a magnetic arm is used to rotate the Ta foil mask ~90 degrees to cover half of the sample and then additional periods of magnetic TI/TI multilayers are grown to form Domain II (Supplementary Fig. 1b).
Electrical transport measurements
All QAH insulator junction samples for electrical transport measurements are grown on 2 mm × 10 mm insulating SrTiO3(111) substrates are scratched into a Hall bar geometry with multiple pins (Figs. 2a, 4b) using a computer-controlled probe station. The width of the Hall bar is ~0.5 mm. The electrical ohmic contacts are made by pressing indium dots on the films. The bottom gate is prepared by flattening the indium dots on the back side of the SrTiO3(111) substrates. Transport measurements are conducted using a Physical Property Measurement System (Quantum Design DynaCool, 1.7 K, 9 T) for T ≥ 1.7 K and a Leiden Cryogenics dilution refrigerator (10 mK, 9 T) for T < 1.7 K. The excitation currents are 1 μA and 1 nA for the PPMS and the dilution measurements, respectively. Unless otherwise noted, the magneto-transport results shown in this work are the raw data. More transport results are found in Supplementary Figs. 5 to 12.
RMCD measurements
The RMCD measurements on MBE-grown QAH insulator junction samples are performed in a closed-cycle helium cryostat (Quantum Design Opticool) at T ~2.5 K and an out-of-plane magnetic field up to 0.5 T. A ~633 nm laser is used to probe the samples at normal incidence with the fixed power of ~1 µW. The AC lock-in measurement technique is used to measure the RMCD signals. The RMCD map is taken by stepping an attocube nanopositioner. The experimental setup has been used in our prior measurements on MBE-grown MnBi2Te4 films36.
Data availability
The datasets generated during and/or analyzed during this study are available from the corresponding author upon request.
References
Qi, X. L. & Zhang, S. C. Topological insulators and superconductors. Rev. Mod. Phys. 83, 1057–1110 (2011).
Hasan, M. Z. & Kane, C. L. Colloquium: Topological insulators. Rev. Mod. Phys. 82, 3045–3067 (2010).
Bansil, A., Lin, H. & Das, T. Colloquium: Topological band theory. Rev. Mod. Phys. 88, 021004 (2016).
Qi, X. L., Hughes, T. L. & Zhang, S. C. Topological field theory of time-reversal invariant insulators. Phys. Rev. B 78, 195424 (2008).
Haldane, F. D. M. Model for a quantum hall-effect without landau levels: Condensed-matter realization of the “Parity Anomaly”. Phys. Rev. Lett. 61, 2015–2018 (1988).
Yu, R. et al. Quantized anomalous hall effect in magnetic topological insulators. Science 329, 61–64 (2010).
Chang, C. Z. et al. Experimental observation of the quantum anomalous hall effect in a magnetic topological insulator. Science 340, 167–170 (2013).
Chang, C. Z. et al. High-precision realization of Robust quantum anomalous hall state in a hard ferromagnetic topological insulator. Nat. Mater. 14, 473–477 (2015).
Liu, C. X., Qi, X. L., Dai, X., Fang, Z. & Zhang, S. C. Quantum anomalous Hall effect in Hg1-yMnyTe quantum wells. Phys. Rev. Lett. 101, 146802 (2008).
Chang, C.-Z., Liu, C.-X. & MacDonald, A. H. Colloquium: Quantum anomalous Hall effect. Rev. Mod. Phys. 95, 011002 (2023).
Checkelsky, J. G. et al. Trajectory of the anomalous hall effect towards the quantized state in a ferromagnetic topological insulator. Nat. Phys. 10, 731–736 (2014).
Kou, X. F. et al. Scale-invariant quantum anomalous hall effect in magnetic topological insulators beyond the two-dimensional limit. Phys. Rev. Lett. 113, 137201 (2014).
Grauer, S. et al. Coincidence of superparamagnetism and perfect quantization in the quantum anomalous hall state. Phys. Rev. B 92, 201304 (2015).
Mogi, M. et al. Magnetic modulation doping in topological insulators toward higher-temperature quantum anomalous hall effect. Appl. Phys. Lett. 107, 182401 (2015).
Ou, Y. et al. Enhancing the quantum anomalous hall effect by magnetic codoping in a topological insulator. Adv. Mater. 30, 1703062 (2017).
Deng, Y. et al. Quantum anomalous Hall effect in intrinsic magnetic topological insulator MnBi2Te4. Science 367, 895–900 (2020).
Serlin, M. et al. Intrinsic quantized anomalous Hall effect in a moiré heterostructure. Science 367, 900–903 (2020).
Li, T. et al. Quantum anomalous Hall effect from intertwined moire bands. Nature 600, 641–646 (2021).
Liu, M. H. et al. Large discrete jumps observed in the transition between Chern states in a ferromagnetic topological insulator. Sci. Adv. 2, e1600167 (2016).
Wu, B. L., Wang, Z. B., Zhang, Z. Q. & Jiang, H. Building programmable integrated circuits through disordered Chern insulators. Phys. Rev. B 104, 195416 (2021).
Varnava, N., Wilson, J. H., Pixley, J. H. & Vanderbilt, D. Controllable quantum point junction on the surface of an antiferromagnetic topological insulator. Nat. Commun. 12, 3998 (2021).
Fu, L. & Kane, C. L. Probing neutral majorana fermion edge modes with charge transport. Phys. Rev. Lett. 102, 216403 (2009).
Akhmerov, A. R., Nilsson, J. & Beenakker, C. W. J. Electrically detected interferometry of majorana fermions in a topological insulator. Phys. Rev. Lett. 102, 216404 (2009).
Yasuda, K. et al. Quantized chiral edge conduction on domain walls of a magnetic topological insulator. Science 358, 1311–1314 (2017).
Rosen, I. T. et al. Chiral transport along magnetic domain walls in the quantum anomalous hall effect. npj Quantum Mater. 2, 69 (2017).
Jiang, J. et al. Concurrence of quantum anomalous Hall and topological Hall effects in magnetic topological insulator sandwich heterostructures. Nat. Mater. 19, 732–737 (2020).
Zhao, Y. F. et al. Tuning the Chern number in quantum anomalous Hall insulators. Nature 588, 419–423 (2020).
Zhao, Y.-F. et al. Zero magnetic field plateau phase transition in higher chern number quantum anomalous hall insulators. Phys. Rev. Lett. 128, 216801 (2022).
Xiao, D. et al. Realization of the axion insulator state in quantum anomalous hall sandwich heterostructures. Phys. Rev. Lett. 120, 056801 (2018).
Akiba, N. et al. Interlayer exchange in (Ga,Mn)As/(Al,Ga)As/(Ga,Mn)As semiconducting ferromagnet/nonmagnet/ferromagnet trilayer structures. Appl. Phys. Lett. 73, 2122–2124 (1998).
Zhou, Z. H., Chien, Y. J. & Uher, C. Ferromagnetic interlayer exchange coupling in semiconductor SbCrTe/Sb2Te3/SbCrTe trilayer structures. Appl. Phys. Lett. 89, 232501 (2006).
Wang, F. et al. Observation of interfacial antiferromagnetic coupling between magnetic topological insulator and antiferromagnetic insulator. Nano Lett. 19, 2945–2952 (2019).
Chang, C. Z. et al. Zero-field dissipationless chiral edge transport and the nature of dissipation in the quantum anomalous hall state. Phys. Rev. Lett. 115, 057206 (2015).
Wang, S. W. et al. Demonstration of dissipative quasihelical edge transport in quantum anomalous hall insulators. Phys. Rev. Lett. 125, 126801 (2020).
Landauer, R. Spatial variation of currents and fields due to localized scatterers in metallic conduction. IBM J. Res. Dev. 1, 223–231 (1957).
Zhao, Y. F. et al. Even-odd layer-dependent anomalous hall effect in topological magnet MnBi2Te4 Thin Films. Nano Lett. 21, 7691–7698 (2021).
Acknowledgements
We thank Yongtao Cui and Weida Wu for helpful discussions. This work is primarily supported by the AFOSR grant (FA9550-21-1-0177), including MBE growth, device fabrication, and RMCD measurements. The PPMS measurements are partially supported by the ARO Award (W911NF2210159). The dilution measurements and the data analysis are partially supported by the NSF-CAREER award (DMR-1847811). C.Z.C. also acknowledges the support from the Gordon and Betty Moore Foundation’s EPiQS Initiative (Grant GBMF9063 to C.Z.C.).
Author information
Authors and Affiliations
Contributions
C.-Z.C. conceived and supervised the experiment. Y.-F.Z., D.-Y.Z., and Z.-J.Y. grew all QAH junction samples and carried out the PPMS transport measurements. R.Z., D.-Y.Z., L.-J.Z., and M.H.W.C. performed the dilution measurements. J.C. and X.X. performed the RMCD measurements. Y.-F.Z. and C.-Z.C. analyzed the data and wrote the manuscript with input from all authors.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Xuefeng Wang, Xiong Yao, and the anonymous reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhao, YF., Zhang, R., Cai, J. et al. Creation of chiral interface channels for quantized transport in magnetic topological insulator multilayer heterostructures. Nat Commun 14, 770 (2023). https://doi.org/10.1038/s41467-023-36488-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-023-36488-y
- Springer Nature Limited
This article is cited by
-
The experimental demonstration of a topological current divider
Nature Communications (2023)