Abstract
With the further miniaturization and integration of multi-dimensional optical information detection devices, polarization-sensitive photodetectors based on anisotropic low-dimension materials have attractive potential applications. However, the performance of these devices is restricted by intrinsic property of materials leading to a small polarization ratio of the detectors. Here, we construct a black phosphorus (BP) homojunction photodetector defined by ferroelectric domains with ultra-sensitive polarization photoresponse. With the modulation of ferroelectric field, the BP exhibits anisotropic dispersion changes, leading an increased photothermalelectric (PTE) current in the armchair (AC) direction. Moreover, the PN junction can promote the PTE current and accelerate carrier separation. As a result, the BP photodetector demonstrates an ultrahigh polarization ratio (PR) of 288 at 1450 nm incident light, a large photoresponsivity of 1.06 A/W, and a high detectivity of 1.27 × 1011 cmHz1/2W−1 at room temperature. This work reveals the great potential of BP in future polarized light detection.
Similar content being viewed by others
Introduction
Polarization is an important property of light, besides intensity, frequency, and phase. Correspondingly, polarization detectors play a vital role in environmental monitoring, remote sensing, medical detection, and navigation1,2. Polarization imaging technology is very efficient and reliable in identifying targets in a complicated environment. Traditional polarization detector technique usually requires the integration of complex optical structures to obtain and analyze the polarization information of targets, such as a polarization photodetector with a single quantum well sandwiched in plasmonic micro-cavity3. However, in order to satisfy the development of photodetectors in the direction of high integration and miniaturization, the use of polarization-sensitive materials as a functional layer is a more direct approach to realize polarization detection.
For the distinct lamellar structure and remarkable electrical and optical properties, two-dimensional (2D) materials are supposed important candidates for ultrathin devices and super integrated devices4,5. Among them, 2D materials with anisotropic structure and polarization sensitivity, such as BP, black arsenic (b-As), GeSe, GeAs, ReS2, and ReSe2, have shown great advantages and potential in the development of highly integrated polarization detectors6,7. To characterize the polarization sensitivity of the photodetectors, one crucial figure of merit PR is defined and given by the expression PR = Iph_maximum/Iph_minimum. In practical application, the PR of the photodetector is supposed to be higher than 208. However, most polarization photodetectors based on anisotropic 2D materials show small PRs (commonly less than 10)6. Polarization imaging technology needs a polarization ratio as larger as possible. Therefore, it is urgent to enhance the PR of those 2D materials photodetectors by introducing physical or chemical methods. Among most anisotropic 2D materials, BP has a puckered hexagonal structure with armchair-shaped along armhair (AC) direction and zigzag-shaped along zigzag (ZZ) direction, and benefits from its thickness-tunable direct bandgap and ultrahigh carrier mobility of more than 1000 cm2V−1s−1, making it one of the best candidates for polarization detection materials9. However, due to the low dichroic ratio and conductivity ratio, the polarization sensitivity of intrinsic BP-based polarization detectors is still unsatisfactory.
Several approaches to enhance the polarization ratio of photodetectors based on 2D materials have emerged in the past decade. The built-in electric field in PN junctions can greatly enhance the efficiency of linear dichroism photodetectors, enhancing the polarization ratio. Such as BP vertical homojunction (35)10, BP/MoS2 heterojunction (>100)11, and graphene/PdSe2/Ge heterojunction (112.2)12. Artificial metamaterials with sub-wavelength structures can spatially confine light on the nanometer scale and enhance light absorption of 2D materials. With bowtie apertures on BP surface, the polarization ratio of the detector increase to 8.713. More interestingly, isotropic materials can realize polarization light detection if some non-centrosymmetric plasmonic nanoantennas are fabricated on the surface. For instance, the graphene mid-infrared photodetector with bulk photoresponse can realize calibration-free polarization detection at zero bias14. By tuning the orientation of nanoantennas, the polarization ratio of graphene photodetector even varies from positive to negative8. Another method is utilizing an external electric field to enhance the anisotropic PTE efficiency of BP, which is proposed by first-principles and model calculation15. Nevertheless, it is a lack of reports about real devices fabricated according to this method.
Considering that BP is very sensitive to the external electric fields of its highly susceptible electronic state, it brings many possibilities for tuning the band structure, electron transport, and photoelectric conversion process of BP. Under the modulation of a high electric field (1.9 V/nm), a single-layer BP becomes a Dirac semimetal with anisotropic dispersion, which is linear in the AC direction and quadratic in the ZZ direction16. By virtue of the Stark effect, the bandgap of a 5 nm-thick BP can be effectively reduced more than 0.18 eV by vertical electric field17. More than that, the photoluminescence (PL) peak of the 20-layer BP can be continuously tuned from 3.7 to 7.7 μm by a moderate displacement field up to 0.48 V/nm18. However, there are few studies on the electric field tuning BP anisotropic photoelectric properties, which are used to explore a photodetector with higher polarization sensitivity.
Ferroelectrics is a kind of dielectric material with spontaneous electric polarization. It provides a strong local field exceeding 1 V/nm, which can effectively improve the photoelectric properties of most semiconductor materials19,20,21. Here, we demonstrate an ultra-sensitive polarization-resolved photodetector with BP in-plane homojunction defined by ferroelectric domains. The dominant photoelectric conversion mechanism is photothermoelectric (PTE) effect of the device at zero or small bias, which converts heat into electricity, and enables ultra-broadband photodetection without cooling22. BP is supposed to be a kind of potentially promising thermoelectric material with anisotropic in-plane thermal conductivity, whose thermoelectric power can be improved via an external electric field23. Considering that the external electric field has an anisotropic tunable effect on the band structure of BP, the ultrahigh ferroelectric field enhances the thermoelectric conversion efficiency in the AC direction. Thus, the PTE current in the device is increased in the AC direction and causes an enhanced polarization detection ratio. More importantly, BP is p-doped and n-doped by the up-polarized (Pup) and down-polarized (Pdown) ferroelectric domains to form an in-plane PN junction. Under illumination, the built-in field in the homojunction accelerates the separation of photo-generated electron-hole pairs and further improves the photocurrent collection efficiency. Therefore, based on this device architecture, combining PTE effect and photovoltaic (PV) effect, BP embraces an ultrahigh polarization sensitivity (PR = 288, at 1450 nm incident light), a large photoresponsivity of 1.06 A/W, and a high detectivity of 1.27 × 1011 cm Hz1/2W−1 at room temperature and atmospheric condition.
Results
Device structure designed based on photoelectric mechanism
In order to obtain a low dark current and a high polarization ratio, and to combine the PTE effect and PV effect in one device, we designed and prepared a BP in-plane PN homojunction defined by the ferroelectric field. The few-layer BP is transferred on the SiO2/Si substrate, and the BP is doped into p-type and n-type with up-polarized and down-polarized ferroelectric domains, as shown in Fig. 1a. For traditional BP field-effect transistors (FET), the PTE photocurrent is affected by the electrical doping of the metal electrodes24. When the doping level is uniform, the carriers will be driven by the temperature gradient and transported in opposite directions, leading to a zero net current (Fig. 1b).
When introduced a PN junction in BP (BP in-plane PN junction), there will be a positive contribution to the PTE current on both sides (Fig. 1c). Such a mechanism worked well in graphene24. The thermoelectric conversion efficiency is governed by ZT = S2\(\sigma\)/(KL + Ke), where S is Seebeck coefficient, \(\sigma\) is electrical conductivity, KL and Ke are lattice and electronic components of the thermal conductivity, respectively25. The ZT value in the AC direction is certainly larger than that in the ZZ direction, which is consistent with the electronic band structure and carrier transport properties26. There are some methods to enhance ZT value, including modifying band structure, quantum confinement effect, band convergence, and reducing lattice thermal conductivity22. The lattice thermal conductivity is almost determined by the intrinsic properties of the material, therefore electronic band engineering is the main strategy because \(\sigma\) and S are dominated by the band structure and Fermi level. Here, the Seebeck coefficient is tuned by the external electric field. The Seebeck coefficient of the n-doped area is larger than that of p-doped area for BP23, as shown in Fig. 1c, which also promotes the PTE current flow directionally from the n-doped to the p-doped area.
Moreover, the electric field has a remarkable tunable effect on the band structure in the AC direction, while the band structure in the ZZ direction hardly changes16. Figure 1d shows the band structure of BP in the fresh state and doped state. With an external electric field, the bandgap (Eg) is narrowed owing to the giant Stark effect16,17. Figure 1e and f is cross-sectional views (in the armchair and zigzag direction) of the two states in Fig. 1d. Angle-resolved photoemission spectroscopy (ARPES) has proven that high electric fields can change the band structure of BP anisotropically16. Under the doping of the electrostatic field, the shape of the band structure in the AC direction changes obviously, while that in the ZZ direction is almost unchanged. It is not difficult to speculate that the electrical conductivity of the AC direction has increased even more. Thus, the ZT in the AC direction is larger than that in the ZZ direction, leading to a higher PTE current in the AC direction. Consequently, the designed BP in-plane PN homojunction device will have more sensitive in polarization resolution.
Raman spectroscopy evolution of BP under ferroelectric field
Generally, Raman spectroscopy can provide structural and electronic information without destructing the material27. More importantly, the Raman spectroscopy technique is also an efficient method to measure the thermal conductivity and explore the electron-phonon interaction of 2D materials26,28. The classical Raman scattering theory denotes the Raman intensity (I) is given by:
where ei and es are the incidents and scattered light, respectively, R is the Raman tensor, which is related to the derivative of the dielectric tensor for the phonon vibration29. For the polarized Raman spectroscopy of BP, the Raman intensity reflects the anisotropic electron-photon and electron-phonon interactions27. Therefore, by comparing the Raman spectral intensities of excitation light with different polarization angles, the coupling interaction of electron-photon and electron-phonon can be obtained. According to our previous analysis and inference, when BP is doped by an external electric field, the electronic structure in the AC direction will change obviously, but the electronic structure in the ZZ direction will not change. As a result, as shown in Fig. 2a, the Ag2 phonons along the AC direction should perform a remarkable strong resonance enhancement at 0°.
As shown in Fig. 2b, three typical Raman peaks Ag1 (out of plane mode), B2g (in-plane mode along ZZ direction), and Ag2 (in-plane mode along AC direction) of BP are located at 366, 443, and 472 cm−1, respectively. It was observed and proved that the intensity of these three peaks is different from each other, as a result of the anisotropic structure of BP29. To further study the electron-photon and electron-phonon interactions of BP, polarized Raman spectra were measured on the same sample. Because the anisotropic electrical and optical properties are mainly decided by intralayer structure for few-layer BP, we mainly discuss the in-plane Raman peaks of BP. To verify the regulating effect of the electric field on BP, we performed the polarized Raman spectra characterization when BP was in the fresh state and doped state (n-doped by a ferroelectric field). To control variables and ensure the reliability of the data, we performed this experiment under the same conditions (measured at the same position on the same sample, using a 514 nm laser with the same power of 1.25 mW and the same integration time) in step of 15° from 0° to 180°.
The experiment results are shown in Fig. 2c–e, and the detailed data can be found in Supplementary Fig. 1. Figure 2c shows the Raman spectra of different polarization angles (0°, 30°, 60°, and 90°). The intensities of the three Raman peaks are all enhanced after electrostatic doping. As mentioned above, the Raman intensity reflects the electron-photon and electron-phonon coupling interactions. From the near-infrared absorption spectrum (Supplementary Fig. 2), the electron-photon interaction seems nearly unchanged. Thus, it is reasonable to infer that the ferroelectric field enhances the electron-phonon coupling interaction of BP. By comparing the ratio of in-plane and out-of-plane phonon vibrations, we can estimate the degree of molecular deformation and quantify the electron-phonon coupling interactions30. Figure 2d and e show the extracting intensity ratio of Ag2/Ag1 and B2g/Ag1, respectively. When the polarization of the excitation laser is aligned along the AC direction, the intensity ratio of Ag2/Ag1 reaches the maximum value, which is inconsistent with the previous reports17. After the modulation of the ferroelectric field, the ratio of Ag2/Ag1 increased from 1.42 to 1.73 at 0° but did not change at 90°. In contrast, the ratio of B2g/Ag1 is 0.93 (0°) and 0.97 (90°) in the fresh state, and decreases to 0.84 and 0.87 after doping. The BP crystal shows more obvious deformation in the AC direction than that in the ZZ direction. It can be concluded that A2 g along the AC direction shows stronger electron-phonon interaction with polarization light at 0° while B2g in zigzag direction shows weaker interaction for polarization light at 0° and 90°. The electron-phonon interaction plays an important role in reducing thermal conductivity31,32. Therefore, the enhanced electron-phonon interaction in the AC direction indicates that the ZT in the AC direction decreases while ZT in the ZZ direction doesn’t change. In other words, the ZT ratio is improved by the ferroelectric field. The Pup and Pdown ferroelectric fields have similar effects on BP according to experimental results shown in Supplementary Fig. 3.
Optoelectronic properties of the BP in-plane homojunction
Based on the above analysis and experiment results, we designed and prepared a BP in-plane homojunction defined by ferroelectric domains. Poly(vinylidene fluoride-trifluoroethylene) (P(VDF-TrFE)) is employed as the ferroelectric layer. Arbitrary patterned ferroelectric domains can be obtained through piezoelectric force microscopy (PFM) technology. The device structure is shown in Fig. 3a, and the device can usually work at zero bias for low dark current (Idark)20. Cross-section of the device analyzed by high-resolution transmission electron microscopy (HR-TEM), as shown in Fig. 3b. There is a very clear interface between BP and P(VDF-TrFE) and the BP thickness is 4.8 nm (~9 layers). Energy-dispersive X-ray spectroscopy (EDS) elemental mapping of fluorine (F), phosphorus (P), and silicon (Si) correspond to P(VDF-TrFE)/BP/SiO2 layers in the HR-TEM image. The ferroelectric film is up-polarized and down-polarized via PFM technology, and then BP is p-doped and n-doped by these ferroelectric domains. Figure 3c demonstrates the phase image of the device and the corresponding optical image is shown in the inset. The phase difference along the red dashed line between Pup state (p-doped region) and Pdown state (n-doped region) reveals that the ferroelectric film is patterned into two opposite domains with 180° domain wall. More detailed information about P(VDF-TrFE) polarized by PFM can be found in Supplementary Figs. 4-5. By measuring the transfer curves, the Debye length in the up-polarized state and down-polarized state are 88 nm and 55 nm, respectively. Thus, the ferroelectric field can fully modulate this BP of dozens of nanometers. The detailed calculation process is provided in Supplementary Fig. 6.
The Isd–Vsd characteristics of the BP in-plane PN homojunction were measured under 300 K and 1450 nm laser illumination, as shown in Fig. 3d. The photocurrent increases with the polarization angle changes from 90° to 0°, which conforms to the linear dichroism of BP33. The maximum short-circuit current (Isc) and open-circuit voltage (Voc) obtained at 0° are 1.58 nA and 0.016 V, respectively. The Isc and Voc measured in this work are at the same level with BP homojunction defined by the local electrostatic gating34. Figure 3e shows the dependence of the device photocurrent on the polarization angle of the incident light, where the wavelength of the incident light is 520 nm and 1450 nm. The PR is 3.9 at 520 nm, which is a slight increase compared to that of pristine BP. Excitingly, the device shows ultrahigh polarization sensitivity at 1450 nm with a PR as high as 288. The ultrahigh polarization sensitivity can be attributed to the superimposed effect of PTE and PV effect. For PTE effect, the carrier mobility ratio is enhanced because of the enhanced anisotropy of the band structure. According to the polarization Raman spectra, the electron-phonon interaction in the AC direction is enhanced by the remanent polarization field, indicating the reduced thermal conductivity in the AC direction. Thus, the PTE photocurrent ratio increases. For PV effect, the polarization ratio can be increased to one or two orders of magnitude. The built-in electric field can separate photo-generated electron-hole pairs and promote the PTE current to move directionally. The polarization photoresponse characteristics under other wavelengths are shown in Supplementary Fig. 7. The PR of the device increases with a longer wavelength, Because the wavelength is closer to the bandgap, the dichroism is more obvious9. The polarization photocurrent mappings with polarization angles of 0°, 30°, 60°, and 90° are shown in Fig. 3f. It is obvious that the photoelectric conversion mainly occurs at the ferroelectric domain wall and diffuses to the electrodes on both sides. This broad photocurrent mapping implies that there is another mechanism (PTE effect) to generate electron-hole pairs besides PV effect22. From the photocurrent mappings, the photocurrent can be regarded as a directional and global current like other photothermal devices and the built-in electric field determines the flow direction of photo-generated carriers.
BP FET and BP homojunction defined by electrostatic gating
To verify the enhancement effect of the external electric field on the polarization photoresponse of BP, we fabricated a BP FET with P(VDF-TrFE) as the gate dielectric (device structure is shown in the inset of Fig. 4a). Figure 4a shows the output characteristics of the device when the P(VDF-TrFE) is at the fresh and the polarization states. The symmetrical Isd–Vsd curves indicate that good Ohmic contact is realized. When P(VDF-TrFE) is polarized by the external gate voltage, the remanent polarization field restrained the carrier concentration in BP, and the drain current decreased at the same bias. Figure 4b demonstrates the polarization photoresponse characteristics of the device at the fresh and polarization states, where the incident light wavelength is 520 nm and 1450 nm (Vsd = 0.2 V), respectively. More detailed data is shown in Supplementary Fig. 8. When the device is in the fresh state, the PR is 1.36 at 520 nm and 1.72 at 1450 nm, while in the doped state, PR increases to 1.62 at 520 nm and 2.42 at 1450 nm. This enhancement polarization sensitivity is consistent with our previous deduction (the PRs of pristine BP at different wavelengths are shown in Supplementary Fig. 9). However, the large dark current in this device hinders its sensitivity to light. For the high carrier concentration of BP, even a small bias will lead to a large dark current. Although the device can work at zero bias with low dark current based on the Schottky junction, the opposite current flow is an obstacle to collecting photo-generated carriers. We performed the spatial photocurrent mapping of the device under zero bias, as shown in Fig. 4c, there are two obvious junctions between the BP and the electrodes. However, the photocurrent (PTE current) still transports at the opposite direction, as analyzed in Fig. 1b, hindering the collection of photocurrent.
To explore the positive effect of PV effect in improving the polarization sensitivity of the device, we also fabricated a BP in-plane homojunction defined by local electrostatic gating. According to a previous report, a vertical BP homojunction enables higher sensitivity in polarized light detection12. Under illumination, the photo-generated electrons and holes in the PN junction are separated by the built-in electric field, thereby enhancing the polarization sensitivity of the photodetector. The few-layer BP used here is ambipolar and retains a slight p-doping property (as shown in Supplementary Fig. 6b), indicating that both hole and electron doping can be achieved by electrostatic doping34. Here, a BP in-plane homojunction was fabricated, and the gate dielectric is h-BN (the device structure is shown in the inset of Fig. 4d). In-plane PN junction (Vg1 = −3 V, Vg2 = 3 V) or NP junction (Vg1 = 3 V, Vg2 = −3 V) can be realized by applying opposite voltages to the two gates. As shown in Fig. 4d, this BP in-plane PN junction achieves a rectification of over 100 under a suitable gate voltage configuration (more output and transfer curves of this device can be found in Supplementary Fig. 10). When tuned into PN junction, this BP PN junction exhibits an obviously enhanced polarization sensitivity at zero bias. As shown in Fig. 4e, the PR is 3.44 at 520 nm incident light and 6.2 at 1450 nm incident light (more detailed data are shown in Supplementary Fig. 11). Figure 4f is a spatial photocurrent mapping at 520 nm incident light, and the inset is the optical image of the device. By comparing the optical image and photocurrent mapping image, it is unambiguously seen that the photon-generated carriers mainly appear in the PN junction area defined by the split bottom gates. This slit-shaped current mapping and non-linear output curve indicate it is a typical PN junction device, whose photoresponse is dominated by PV effect22,35. We do not rule out the PTE effect in this device for the photocurrent area is larger than the slit between a pair of split gates. However, it is the PV effect that dominates the photoresponse in this BP PN junction rather than the PTE effect (notably different from broad photocurrent mapping in Fig. 3f). It is probable that the strong PV effect introduces a large built-in electric field, forcing the photoelectric conversion to concentrate in the PN junction area and decreasing the photoresponse of the BP non-junction area.
Through the above design and mechanism analysis, the BP in-plane PN junction defined by ferroelectric domains exhibits excellent polarized light detection performance. Moreover, other figures of merits of the device have also been characterized in detail. The dynamic response under 1450 nm incident light, measured by switching on/off the mechanical chopper, is shown in Fig. 5a. As a photovoltaic device, this BP in-plane PN homojunction has a fast photoresponse speed with a rising time (tr) of 361 μs and decay time (tf) of 362 μs, which are shorter than that of BP photoconductive devices (usually several milliseconds or longer, as shown in Supplementary Fig. 9b). Compared with BP PN homojunctions fabricated via other approaches (Al-doping and chemical-doping), the device in this work also shows superior photoresponse speed36,37. The responsivity R = Iph/Peff and detectivity D* = RA1/2(2eIdark)−1/2 under various incident optical powers are calculated and shown in Fig. 5b. The device has a responsivity of up to 1.06 A/W and detectivity of up to 1.27 × 1011 cm Hz1/2W−1, which is larger than most BP-based photodetectors. To better evaluate the performance of the device, we also measured spectral-noise density (Supplementary Fig 12). The D* is calculated as 1 × 1011 cm Hz1/2W−1, which is in good agreement with the calculation result based on dark current. The external quantum efficiency (EQE) of the device is given by the expression EQE = (Iph/Peff)(hc/eλ) and shows a maximum of 90.8% under weak light signal conditions (Fig. 5c). Such a high efficiency may be attributed to the carrier multiplication by hot carriers in BP (Fig. 5d), which is prevailing in low-dimensional materials for their strong Coulombic interactions38. When under the illumination of photoexcitation at energy above the energy gap, photo-generated carriers appear at the elevated positions in the conduction band and valence band, resulting in intravalley scattering of the carriers by delivering the excess energy to phonons (step 1). The photo-generated carriers scatter and stimulate the additional electron across the bandgap to the conduction band, resulting in carrier multiplication (step 2). Carrier multiplication has been proposed to enhance the efficiency of photodetectors. Therefore, this device shows a large EQE. To further demonstrate the performance advantages of BP in-plane PN homojunction defined by ferroelectric domains, we compared it with BP10,13, BP homojunction made by other methods10, 2D heterojunctions11,12,39,40, nanowires41,42,43,44, and other materials with dichroism45,46,47. Our device has obvious advantages in both PRs and responsivity, are shown in Fig. 5e. The responsivity of the device in this work is at the advanced level. More importantly, our device processes ultrahigh polarization sensitivity than those devices reported previously (detailed information is shown in Supplementary Table1).
Discussion
In summary, we have designed and fabricated a BP in-plane PN homojunction defined by ferroelectric domains with ultrahigh polarization sensitivity at room temperature. By performing the polarized Raman spectroscopy measurements, we have analyzed and obtained the enhancement effect of the ferroelectric field on the electron-phonon interactions along the AC direction. The PTE current in the AC direction increases because of reduced thermal conductivity and enhanced carrier mobility, thereby increasing the polarization detection ratio. By introducing the PN junction with the upward and downward ferroelectric field, the photo-generated carriers are separated more efficiently with the action of the built-in electric field. Moreover, the PV effect also has a positive effect on improving the polarization detection ratio of the device. As both the PV effect and the enhanced PTE effect contribute to the photocurrent anisotropic transport process, this BP in-plane PN junction-based photodetector shows an ultrahigh polarization ratio of 288 at 1450 nm incident light and at room temperature and atmosphere. The responsivity of 1.06 A/W and the detectivity of 1.27 × 1011 cm Hz1/2W−1 are at an advanced level among similar devices. This design principle might also apply to other anisotropic materials, providing a train of thought in designing high-performance polarization-resolved photodetectors. To abtain full polarization information, it is possible to envision an imaging system based on BP flakes with four orientation (0°, 45°, 90°, and 135°).
Methods
Device fabrication
For the BP in-plane homojunction constructed by ferroelectric field and BP FET, few-layer BP samples were prepared by mechanical exfoliation method and transferred onto 285 nm-thick SiO2/Si substrates. The source and drain electrodes (chromium/gold (Cr/Au), 15/35 nm) were deposited on the BP through standard e-beam lithography and metal deposition techniques. P(VDF-TrFE) film with 100 nm thickness was prepared by spin-coating method. For BP in-plane PN homojunction constructed by ferroelectric field, P(VDF-TrFE) were polarized via PFM technology. For BP FET, P(VDF-TrFE) was polarized by the top gate and the 10 nm-thick aluminum film was deposited by thermal evaporation and patterned by photolithography as the top gate transparent electrode. For BP PN junction defined by local electrostatic gating, a pair of split bottom gates (Cr/Au, 15/25 nm) was fabricated on a 285 nm-thick SiO2/Si substrate by standard e-beam lithography and metal deposition techniques. 20 nm-thick h-BN was transferred on the gates. Then, few-layer BP was transferred on h-BN, and the source and drain electrodes (Cr/Au, 15/35 nm) were deposited. Then, poly(methyl methacrylate) (PMMA) film was coated on this device to protect it from oxygen and water.
Materials characterization
A Lab Ram HR800 from HORIBA spectrometer and an Olympus ×100 objective lens were used for Raman measurements. All the polarized Raman measurements were illuminated with a 514.5 nm wavelength laser of 1.25 mW power under ×100 objective. A linear polarizer (Thorlabs) was used for polarized Raman measurements. The TEM and EDS measurements were performed by JEOL JEM2100F TEM with EX-24063JGT EDS. AFM and PFM measurements were performed using PFM mode by Cypher S from Asylum Research.
Electrical and optoelectronic characterization
In this study, all electronic and optoelectronic measurements were performed at room temperature and under ambient conditions. Electronic measurements were conducted using a commercial Keysight B1500A. All the optoelectronic measurements were taken by a MStarter 200 optoelectronic measurement system from Maita Optoelectronic Technology Co., LTD.
Data availability
All technical details for producing the figures are enclosed in the Supplementary Information. All other relevant data are available from the corresponding author upon request. Source data are provided with this paper.
References
Rubin, N. A. et al. Matrix Fourier optics enables a compact full-Stokes polarization camera. Science 365, eaax1839 (2019).
Ran, W. et al. Integrated polarization-sensitive amplification system for digital information transmission. Nat. Commun. 12, 6476 (2021).
Li, Q. et al. High-polarization-discriminating infrared detection using a single quantum well sandwiched in plasmonic micro-cavity. Sci. Rep. 4, 6332 (2014).
Jiang, J. et al. Recent advances in 2D materials for photodetectors. Adv. Electron. Mater. 7, 2001125 (2021).
Zhu, K. et al. The development of integrated circuits based on two-dimensional materials. Nat. Electron. 4, 775–785 (2021).
Li, X. et al. Review of anisotropic 2D materials: controlled growth, optical anisotropy modulation, and photonic applications. Laser Photonics Rev. 15, 2100322 (2021).
Wu, Z. et al. Large-scale growth of few-layer two-dimensional black phosphorus. Nat. Mater. 20, 1203–1209 (2021).
Wei, J., Xu, C., Dong, B., Qiu, C.-W. & Lee, C. Mid-infrared semimetal polarization detectors with configurable polarity transition. Nat. Photon. 15, 614–621 (2021).
Xia, F., Wang, H. & Jia, Y. Rediscovering black phosphorus as an anisotropic layered material for optoelectronics and electronics. Nat. Commun. 5, 4458 (2014).
Yuan, H. et al. Polarization-sensitive broadband photodetector using a black phosphorus vertical p-n junction. Nat. Nanotechnol. 10, 707–713 (2015).
Bullock, J. et al. Polarization-resolved black phosphorus/molybdenum disulfide mid-wave infrared photodiodes with high detectivity at room temperature. Nat. Photon. 12, 601–607 (2018).
Wu, D. et al. Highly polarization-sensitive, broadband, self-powered photodetector based on graphene/PdSe2/germanium heterojunction. ACS Nano 13, 9907–9917 (2019).
Venuthurumilli, P. K., Ye, P. D. & Xu, X. Plasmonic resonance enhanced polarization-sensitive photodetection by black phosphorus in near infrared. ACS Nano 12, 4861–4867 (2018).
Wei, J. et al. Zero-bias mid-infrared graphene photodetectors with bulk photoresponse and calibration-free polarization detection. Nat. Commun. 11, 6404 (2020).
Fei, R. et al. Enhanced thermoelectric efficiency via orthogonal electrical and thermal conductances in phosphorene. Nano Lett. 14, 6393–6399 (2014).
Kim, J. et al. Observation of tunable band gap and anisotropic Dirac semimetal state in black phosphorus. Science 349, 723–726 (2015).
Chen, X. et al. Widely tunable black phosphorus mid-infrared photodetector. Nat. Commun. 8, 1672 (2017).
Chen, C. et al. Widely tunable mid-infrared light emission in thin-film black phosphorus. Sci. Adv. 6, eaay6134 (2020).
Wang, X. et al. Ultrasensitive and broadband MoS2 photodetector driven by ferroelectrics. Adv. Mater. 27, 6575–6581 (2015).
Wu, G. et al. Programmable transition metal dichalcogenide homojunctions controlled by nonvolatile ferroelectric domains. Nat. Electron. 3, 43–50 (2020).
Chen, Y. et al. Ferroelectric-tuned van der Waals heterojunction with band alignment evolution. Nat. Commun. 12, 4030 (2021).
Lu, X., Sun, L., Jiang, P. & Bao, X. Progress of photodetectors based on the photothermoelectric effect. Adv. Mater. 31, e1902044 (2019).
Saito, Y. et al. Gate-tuned thermoelectric power in black phosphorus. Nano Lett. 16, 4819–4824 (2016).
Wang, D. et al. Enhancing the graphene photocurrent using surface plasmons and a p-n junction. Light Sci. Appl. 9, 126 (2020).
Kanahashi, K., Pu, J. & Takenobu, T. 2D Materials for large-area flexible thermoelectric devices. Adv. Energy Mater. 10, 1902842 (2019).
Luo, Z. et al. Anisotropic in-plane thermal conductivity observed in few-layer black phosphorus. Nat. Commun. 6, 8572 (2015).
Mao, N. et al. Direct observation of symmetry-dependent electron-phonon coupling in black phosphorus. J. Am. Chem. Soc. 141, 18994–19001 (2019).
Saito, R. et al. Probing phonon dispersion relations of graphite by double resonance Raman scattering. Phys. Rev. Lett. 88, 027401 (2002).
Ling, X. et al. Anisotropic electron-photon and electron-phonon interactions in black phosphorus. Nano Lett. 16, 2260–2267 (2016).
Vallabhaneni, A. K., Singh, D., Bao, H., Murthy, J. & Ruan, X. Reliability of Raman measurements of thermal conductivity of single-layer graphene due to selective electron-phonon coupling: a first-principles study. Phys. Rev. B 96, 199903 (2016).
Liao, B. et al. Significant reduction of lattice thermal conductivity by the electron-phonon interaction in silicon with high carrier concentrations: a first-principles study. Phys. Rev. lett. 114, 11115901 (2015).
Zhu, T. et al. The role of electron-honon interaction in heavily doped fine-grained bulk silicons as thermoelectric materials. Adv. Electron. Mater. 2, 1600171 (2016).
Qiao, J., Kong, X., Hu, Z. X., Yang, F. & Ji, W. High-mobility transport anisotropy and linear dichroism in few-layer black phosphorus. Nat. Commun. 5, 4475 (2014).
Buscema, M., Groenendijk, D. J., Steele, G. A., van der Zant, H. S. & Castellanos-Gomez, A. Photovoltaic effect in few-layer black phosphorus PN junctions defined by local electrostatic gating. Nat. Commun. 5, 4651 (2014).
Lv, L. et al. Reconfigurable two-dimensional optoelectronic devices enabled by local ferroelectric polarization. Nat. Commun. 10, 3331 (2019).
Liu, Y., Cai, Y., Zhang, G., Zhang, Y.-W. & Ang, K.-W. Al-doped black phosphorus p-n homojunction diode for high performance photovoltaic. Adv. Funct. Mater. 27, 1604638 (2017).
Yu, X., Zhang, S., Zeng, H. & Wang, Q. J. Lateral black phosphorene P-N junctions formed via chemical doping for high performance near-infrared photodetector. Nano Energy 25, 34–41 (2016).
Ahmed, F. et al. Impact ionization by hot carriers in a black phosphorus field effect transistor. Nat. Commun. 9, 3414 (2018).
Zhao, S. et al. Highly polarized and fast photoresponse of black phosphorus-InSe vertical p-n heterojunctions. Adv. Funct. Mater. 28, 1802011 (2018).
Ye, L. et al. Highly polarization sensitive infrared photodetector based on black phosphorus-on-WSe2 photogate vertical heterostructure. Nano Energy 37, 53–60 (2017).
Wang, J., Gudiksen, M. S., Duan, X., Cui, Y. & Lieber, C. M. Highly polarized photoluminescence and photodetection from single indium phosphide nanowires. Science 293, 1455–1457 (2001).
Gao, L. et al. Passivated single-crystalline CH3NH3PbI3 nanowire photodetector with high detectivity and polarization sensitivity. Nano Lett. 16, 7446–7454 (2016).
Bai, R. et al. Polarization-sensitive and wide-spectrum photovoltaic detector based on quasi‐1D ZrGeTe4 nanoribbon. InfoMat 4, e12258 (2021).
Singh, A. et al. Polarization-sensitive nanowire photodetectors based on solution-synthesized CdSe quantum-wire solids. Nano Lett. 7, 2999–3006 (2007).
Wang, Y. et al. Air-stable low-symmetry narrow-bandgap 2D sulfide niobium for polarization photodetection. Adv. Mater. 32, e2005037 (2020).
Zhang, E. et al. Tunable ambipolar polarization-sensitive photodetectors based on high-anisotropy ReSe2 nanosheets. ACS Nano 10, 8067–8077 (2016).
Yang, S. et al. In-plane optical anisotropy and linear dichroism in low-symmetry layered TlSe. ACS Nano 12, 8798–8807 (2018).
Acknowledgements
This work is supported by National Key Research and Development program of China (grant no. 2021YFA1200700 (J.W.)), National Natural Science Foundation of China (grant nos. 62025405 (J.W.), 61835012 (J.W.), 61905267 (X.W.), 62105100 (Y.C.), 62075228 (X.M.), 61974153 (T.L.), and 62011530043 (H.S.)), Key Research Program of Frontier Sciences, CAS (grant no. ZDBS-LY-JSC045 (X.W.)), Strategic Priority Research Program of Chinese Academy of Sciences (grant no. XDB44000000 (J.W.)), Hundred Talents Program of the Chinese Academy of Sciences (X.W.), Science Technology Commission of Shanghai Municipality (grant no. 2151103500 (J.W.)), and Shanghai Sailing Program (grant no. 21YF1454800 (Y.Z.)).
Author information
Authors and Affiliations
Contributions
S.W. and Y.C. contributed equally to this work. J.W., X.W., and J.C. conceived and supervised the research. S.W. and X.W. fabricated the devices. Q.Z., H.C., and X.-J.W. performed the Raman measurements. S.W., Y.C., X.H., H.J., and X.T. performed the electrical and optoelectronic measurements. S.W. and Y.Z. performed the PFM measurements. S.H. and H.Y. performed the infrared spectroscopy measurements. T.L., H.S., W.H., X.M., J.C., and J.W. advised on the experiments and data anylasis. S.W., Y.C., and X.W. co-wrote the paper. All authors discussed the results and revised the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Wenjing Zhang, Jingxuan Wei and the other anonymous reviewers for their contribution to the peer review of this work. Peer reviewer reports are available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Source data
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wu, S., Chen, Y., Wang, X. et al. Ultra-sensitive polarization-resolved black phosphorus homojunction photodetector defined by ferroelectric domains. Nat Commun 13, 3198 (2022). https://doi.org/10.1038/s41467-022-30951-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-022-30951-y
- Springer Nature Limited
This article is cited by
-
Multilayer WS2 for low-power visible and near-infrared phototransistors
Discover Nano (2024)
-
Multidimensional detection enabled by twisted black arsenic–phosphorus homojunctions
Nature Nanotechnology (2024)
-
Two-dimensional materials for future information technology: status and prospects
Science China Information Sciences (2024)
-
Long-wave infrared photothermoelectric detectors with ultrahigh polarization sensitivity
Nature Communications (2023)
-
Near-infrared optoelectronic synapses based on a Te/α-In2Se3 heterojunction for neuromorphic computing
Science China Information Sciences (2023)