Abstract
Integrating and manipulating the nano-optoelectronic properties of Van der Waals heterostructures can enable unprecedented platforms for photodetection and sensing. The main challenge of infrared photodetectors is to funnel the light into a small nanoscale active area and efficiently convert it into an electrical signal. Here, we overcome all of those challenges in one device, by efficient coupling of a plasmonic antenna to hyperbolic phonon-polaritons in hexagonal-BN to highly concentrate mid-infrared light into a graphene pn-junction. We balance the interplay of the absorption, electrical and thermal conductivity of graphene via the device geometry. This approach yields remarkable device performance featuring room temperature high sensitivity (NEP of 82 pW\(/\sqrt{{\bf{Hz}}}\)) and fast rise time of 17 nanoseconds (setup-limited), among others, hence achieving a combination currently not present in the state-of-the-art graphene and commercial mid-infrared detectors. We also develop a multiphysics model that shows very good quantitative agreement with our experimental results and reveals the different contributions to our photoresponse, thus paving the way for further improvement of these types of photodetectors even beyond mid-infrared range.
Similar content being viewed by others
Introduction
Hyperbolic phonon-polaritons (HPPs) are hybridized modes of ionic oscillations and light present in polar dielectric materials, such as hexagonal-BN (hBN)1,2,3,4,5,6,7 that show interesting optical properties such as extreme subwavelength ray-like propagation and sub-diffraction light confinement (~λ0/100)1,8,9,10,11, among others. In fact, novel nano-optoelectronic platforms can be attained by merging HPPs functionalities with other 2D materials-based devices, such as graphene photodetectors governed by the photothermoelectric (PTE) effect. This mechanism generates a photoresponse in graphene pn-junctions12,13,14,15,16,17,18,19 driven by a temperature gradient and Fermi level asymmetry across the channel. Nevertheless, one of the limitations of these detectors is the low light absorption of graphene, especially for mid-IR frequencies where the photon energy becomes comparable to the typical doping level of graphene reaching the Pauli blocking regime20,21. This is further exacerbated by the small photoactive area of graphene pn-junctions16,22, limited by the cooling length of the hot carriers (0.5–1 μm)13,14,22,23. These limitations can be overcome by exciting HPPs and focusing them towards the photoactive area and consequently absorbing them in graphene. However, efficient exploitation of HPPs for mid-IR photodetection still remains unexplored24,25. In this work, we embed hBN and graphene within metallic antennas in order to couple their plasmonic interactions with HPPs and achieve highly concentrated mid-IR light on a graphene pn-junction for sensitive and fast mid-IR photodetection.
Results
Device operation principle
Our design (depicted in Fig. 1a–c) combines several mechanisms to achieve high field concentration for both incident light polarizations. Specifically, when light is polarized parallel to the bow-tie antenna axis (transverse magnetic, TM-polarization, Fig. 1d), it excites its localized surface plasmon resonance (LSPR) spectrally located at λ ≈ 5–7 μm (Supplementary Figs. 1 and 2a). As a result, the antenna concentrates the incoming mid-IR light into its gap that is situated just above the graphene pn-junction (i.e. the detector photoactive area)16. At the same time, the near-fields produced within the antenna hot-spot contain high momenta and thus efficiently launch HPPs ascribed to the spectral overlap of the antenna’s LSPR with the hBN upper reststrahlen band (RB) range (λ ≈ 6–7 μm. These HPPs propagate as guided modes and interfere within the graphene pn-junction, producing high absorption across this small localized region. Likewise, when light is polarized perpendicularly to the bow-tie antenna axis (transverse electric, TE-polarization, Fig. 1e), it produces strong light concentration in the gap of the H-shaped antenna, acting as the split-gate, ascribed again to its LSPR spectrally located at λ ≈ 5.5–7.5 μm (Supplementary Figs. 2b and 3). This phenomenon will also launch hBN HPPs at the gate edges, which will be guided and interfered within the photoactive area.
a Schematic representation of the photodetector consisting of H-shaped resonant gates of 4.2 μm of total length, with a hBN-encapsulated H-shaped graphene channel transferred on top, contacted by source and drain electrodes. A bow-tie antenna of 2.7 μm of total length is placed on top of the 2D stack. The local gates serve to create a pn-junction in the central part of the graphene channel (by applying voltages VL and VR), where the antenna gap and gate gap are located. Both narrow gaps are on the order of ~100 nm. The scale bar corresponds to 0.5 μm. b Side view of the device design (not to scale) with indications of the materials' thicknesses. c Optical image of the photodetector. The dashed lined circle indicates the typical beam spot size obtained at λ = 6.6 μm. The scale bar corresponds to 2.5 μm. d Cross section view of the simulated total electric field intensity (∣E∣2) normalized to the incident one (∣E0∣2) along the antenna main axis when light is polarized parallel to the bow-tie antenna (TM-polarization) axis as indicated in the illustration on the left. The white scale bar corresponds to 250 nm. e Same as (d) but for light polarization perpendicular to the bow-tie antenna (TE-polarization) and parallel to the local gates as shown in the schematic on the left.
The absorption process in the graphene is mediated mostly by interband transitions, which mainly occur in the regions within the gap of the gates where the graphene doping is sufficiently small to avoid Pauli blocking (Supplementary Figs. 4 and 5). The excited carriers quickly relax (<100 fs)23 into a local hot equilibrium Fermi–Dirac distribution by electron–electron scattering. Subsequent cooling mechanisms include electron–phonon scattering (~1 ps)13,14,22,23,26 and heat diffusion away from the junction area. As a result, a symmetric electronic temperature profile Te(x) is produced in the graphene junction13,14,24, giving rise to a thermoelectric voltage VPTE ∝ S(x) ∇Te(x), where x runs along the graphene channel and S(x) represents the Seebeck coefficient which is tunable by the gates. Since ∇Te(x) is antisymmetric, an antisymmetric S(x) is also needed to maximize the net PTE response, which is achieved by applying opposite voltages to the two gates (Supplementary Figs. 4 and 5). In addition to HPPs promoting absorption in graphene, they also absorb light themselves. However, due to the large (~103) heat capacitance mismatch between graphene electrons and lattice, the HPP absorption does not amount to any meaningful temperature rise and thus does not contribute to the device PTE response.
Photocurrent characterization and spectral response
To reveal the spatial intensity profile of the beam focus at λ = 6.6 μm, we scan the sample with xyz-motorized stages and measure the photocurrent (IPTE) as shown in Fig. 2a. As a result, we observe the Airy pattern of the beam, which implies that we obtain a well-focused beam (see Methods) and high sensitivity at this wavelength considering the small irradiance input of 0.2 μW/μm2. Next, we investigate the photoresponse as a function of the two gate voltages (VL and VR), shown in Fig. 2b, which reveals the photocurrent mechanism and optimal doping level. We find that when sweeping the gate voltages independently, the photocurrent follows several sign changes resulting in a 6-fold pattern, which indicates that the photodetection is driven by the PTE effect, as also shown in other studies in the mid-IR range24,27,28. The highest values of photocurrent occur at pn or np configuration, specifically at VL = 1.6 V (170 meV) and VR = −0.82 V (−130 meV), which are relatively low doping levels. We note that when applying a voltage bias in the graphene channel, the photocurrent remains constant while the source-drain current increases linearly with bias (Supplementary Fig. 6). This allows us to discard other mechanisms such as photogating and bolometric effects that would increase significantly with voltage bias.
a Scanning photocurrent map (log scale) across the mid-IR beam focus at λ = 6.6 μm. The white scale bar corresponds to 20 μm. We obtain a FWHM of 6.1 μm. We use a small input power (Pin) of 13.7 μW (irradiance of 0.2 μW/μm2). b Photocurrent map as a function of the two gate voltages at λ = 6.6 μm. c Experimental (dots) and theoretical (dashed lines) spectral external responsivity of the device for TM-polarization and (d) for TE-polarization. The highlighted region corresponds to the hBN RB (λ = 6.2–7.3 μm). For (c and d), we set the gate voltages to a pn-junction configuration close to the optimal with VL = 0.5 V (97 meV) and VR = −0.5 V ( −100 meV). We use the same doping level for the theoretical simulations.
To determine the photodetector spectral response, we measure the TM-polarization (Fig. 2c) external responsivity (see Methods) as a function of excitation wavelength. We obtain high values up to 15 mA/W within 6–7 μm at the hBN RB. On the other hand, for TE-polarization (Fig. 2d), we observe two responsivity peaks, the first one (up to 22 mA/W) again within the hBN RB (6–7 μm) and a second peak (3.5 mA/W) around 8 μm. We also plot the simulated responsivity that is extracted from the multiphysics simulations, which considers the exact geometry of the photodetector and the whole device photoresponse (optical excitation, carrier distribution and relaxation, heat diffusion and thermoelectric current collection. See further details in Supplementary Notes 1–4). We observe very good qualitative and quantitative agreement between experimental and theoretical responsivity, which we explore in the following by analyzing each component involved in the photoresponse.
Spectral and spatial analysis of the photoresponse
We first identify the behavior of the resonant mechanisms, in terms of field intensity enhancement and spatial localization by studying the absorption enhancement in graphene (G) across the channel in the x direction (averaging over 500 nm in the y direction, see Fig. 1a, b for axis definition) and as a function of the wavelength as shown in Fig. 3. We define G as follows: G(λ, r) = Absdevice(λ, r)/Absair(λ, r), which is the ratio between the graphene absorption incorporating all the elements of the device (e.g. antenna, contacts, etc.) to that of suspended graphene as a function of λ and the position vector r. G and responsivity are proportionally related via the electronic temperature gradient as shown in Supplementary Fig. 5 and Supplementary Note 2.
Simulations of the absorption enhancement in graphene (G) along the source-drain direction (x direction as shown in Fig. 1a, b, where x = 0 is located at the center of the gate gap) as a function of the wavelength, for TM (a) and TE-polarization (b). (c) and (d) correspond to (a) and (b), respectively, but with wavelength-independent refractive index for hBN (n = 2.4).
In the TM-polarization case shown in Fig. 3a, we observe very high G values at the antenna LSPR (λ ~ 6 μm). The value of G peaks around 6.8 μm due to the hybridization of the hBN HPPs with the antenna LSPR and to the constructive interference of the propagating HPPs occurring at x ~ ±100 nm. In fact, the different spatial patterns of G arise from the wavelength dependence of the HPP propagation angle in hBN following the equation \(\tan \theta (\omega )={\rm{i}}\sqrt{{\varepsilon }_{x,y}(\omega )}/\sqrt{{\varepsilon }_{z}(\omega )}\) (refs. 1,24,29). For longer wavelengths, we find a negligible G between 7 and 7.3 μm that corresponds to the hBN transverse optical (TO) phonon. We observe that the highest G values are only found for the spatially confined region (from x ~ −100 to 100 nm) where the antenna and gates overlap, which is designed to coincide with the graphene pn-junction (see Supplementary Figs. 7, 8 and 17–23 regarding the Supplementary Discussion 1). Nevertheless, in the hBN RB we find large G values outside this tightly localized region due to HPP propagation.
For TE-polarization (Fig. 3b), we find the maximum values of G between 6.2 and 6.6 μm due to the gate LSPR hybridization with HPPs and their strong constructive interference at x = 0. For longer wavelengths, we identify a G peak centered at 8.5 μm that corresponds to SiO2 phonon-polaritons (PPs) hybridization with the gate LSPR as presented in Supplementary Figs. 2 and 9.
To further elucidate the role of the antennas in G, we simulate the system without the contribution of the HPPs using wavelength-independent refractive index values for the hBN (Fig. 3c, d). For TM-polarization (Fig. 3c), we observe a peak around 6 μm that corresponds to the antenna LSPR and its resonance tail extending up to 8 μm. For TE-polarization, in contrast, Fig. 3d shows high values of G across a broader wavelength range (5.5–7.5 μm) due to the complex shape of the gates and their interactions with the source–drain contacts (Supplementary Fig. 3). Although in Fig. 3d we observe lower G values compared to Fig. 3c (Supplementary Fig. 2), we obtain higher values of G in TE-polarization when combining the gate LSPR with HPPs (Fig. 3b) ascribed to its higher spectral overlap with the hBN RB and due to the stronger constructive interferences of the HPPs excited by the gates.
To evaluate the coupling between the bow-tie antenna LSPR and the hBN HPPs, we study the responsivity as a function of the antenna length for TM-polarization as shown in Fig. 4a (Supplementary Fig. 10). We observe some hBN HPP excitation when using an antenna non-resonant (green line) within the hBN RB range, in which case we obtain a maximum responsitivity of 4 mA/W. In the case of the semi-resonant antenna (experimental antenna, shown in blue line), whose LSPR partially overlaps with the RB spectral range25, the responsivity increases to 17 mA/W, respectively. However, this can be significantly improved if we use a longer antenna (red line) such that its LSPR peak fully overlaps with the hBN HPPs peak, thus obtaining 65 mA/W.
a Simulations of responsivity for TM-polarization for different antenna lengths. Different cases are presented: non-resonant antenna within the hBN RB spectral range (antenna total length of L = 1.8 μm, shown in green), semi-resonant antenna (L = 2.7 μm shown in blue, which corresponds to the experimental antenna) and resonant antenna (L = 4.8 μm, shown in red). b Simulations of responsivity and NEP as a function of gate tip width and graphene (following the exact shape of the gates) as shown in the schematic for TE-polarization at λ = 6.5 μm. The tip length is 855 nm, which includes the gap between the gates of 155 nm. The source-drain distance is 2.6 μm and electrodes width is 2 μm as in the measured device. c Same as b but as a function of the gate tip length as shown in schematic. The tip width is 500 nm.
Next, we examine the impact of the H-shaped gates excited at λ = 6.5 μm with TE-polarization on the responsivity and NEP (noise-equivalent power, see Methods) by varying the width and length of the gate tip and graphene, while keeping the source-drain distance and width fixed as indicated in Fig. 4b, c. Fig. 4b shows that the responsivity (NEP) increases (decreases) when decreasing the tip width down to an optimal value of 500 nm (same as the experimental value). This is ascribed to the balancing act of absorption, electrical resistance and thermal conductance: larger absorption and lower thermal conductance increase the temperature gradients, but a smaller electrical conductance also reduces the photocurrent and thus the responsivity (Supplementary Fig. 11 and Supplementary Discussion 1). Note that electrical and thermal conductivity are ultimately proportional through the Wiedemann-Franz law. For the case of the gate tip length, however, the optimum is found around 1.45 μm, which is larger than the experimental one (855 nm), pointing to future design and performance improvements (Supplementary Figs. 3 and 11). These results highlight the importance of the gate and graphene channel shapes on PTE performance and the vital role of multiphysics modeling in understanding and optimizing such a complex device.
Speed, sensitivity, and device benchmark
Now we discuss the technological relevance of our photodetector. First, we measure the photodetection speed by using as reference a commercial fast mercury–cadmium–telluride (MCT) detector. We plot in Fig. 5a the quantum cascade laser (QCL) voltage (brown line) together with the photoresponses of the MCT (blue line) and our device (black circles). The signal of the MCT detector reveals the pulse shape of the laser. We fit an exponential function to the initial peak to determine the rise time (shown in red lines), obtaining a value of 9.5 ns, which is close to its datasheet value of 4.4 ns. In the case of our photodetector, we find a rise time of 17 ns (22 MHz) when using a current amplifier with 14 MHz bandwidth. This suggests that our time-resolved measurements are limited by the current amplifier bandwidth (Supplementary Fig. 12), meaning that the actual rise time may be shorter. In fact, our theoretical calculations predict a speed of 53 ps (Supplementary Note 5).
a Time-resolved photodetection traces at λ = 6.6 μm, compared with a MCT detector (both plotted in black dots and blue line respectively) and the respective QCL voltage signal (brown line). The QCL pulse width corresponds to 496 ns. The photovoltage fits are shown in red lines. We obtain rise times of 9 ± 3 ns and 17 ± 3 ns for the MCT and our device respectively. b Photocurrent as a function of laser power (Pdiff = Pin × Adiff/Afocus, see Methods) for different wavelengths on a log-log scale. Circles correspond to the data points, while the dashed lines represent the fits according to \({I}_{{\rm{PTE}}}\propto {P}_{{\rm{diff}}}^{\gamma }\). Among all cases, γ ranges from 0.92–0.98. We observe linear photoresponse over three orders of magnitude of power (limited by the power meter sensitivity range for Pin calibration). These results suggest that we are operating in the weak heating regime (Te − Tl << Tl)16,23, as in the strong heating regime (Te − Tl >> Tl), a sublinear behavior is expected (γ = 0.5)16,23. Here Te is the electronic temperature and Tl is the graphene lattice temperature, which the latter is in thermal equilibrium with the environment.
The sensitivity of the detector is best expressed in terms of external responsivity, which the maximum measured value is 27 mA/W (92 V/W, Supplementary Fig. 13), yielding a noise-equivalent-power of 82 pW/\(\sqrt{{\rm{Hz}}}\) (refs. 24,30,31,32,33), assuming the graphene thermal noise as the dominating noise source16,34,35. We emphasize that the zero-bias operation leads to low noise levels and a very low power consumption, which is given by the voltage applied to the gates. Furthermore, our design allows sensitive detection in different polarizations (Supplementary Fig. 14), which is a limitation for the mentioned graphene detectors24,30,31,32. Additionally, our device exhibits a wide dynamic range by showing linear photoresponse over three orders of magnitude as shown in Fig. 5b, which is an issue for other types of graphene detectors31 and commercial detectors such as MCT36. It also has a very small active area given by the antennas’ cross-sections, which implies high spatial resolution and opens the possibility of arranging it into high density photodetector pixels30,37 that are CMOS compatible38. All of these performance parameters combined make our device an interesting platform that fulfills the ongoing trend of decreasing the size, weight and power consumption (SWaP) of infrared imaging systems36.
Discussion
The device concept introduced in this work can be extended to detectors for other wavelengths or more specific functionalities such as hyperspectral imaging and spectroscopy. Our approach can also be combined with HPPs in other regions of the mid-IR and long-wave infrared range such as MoO3 (refs. 39,40,41). Additional tuning and wavelength sensitivity can be realized by controlling the hyperbolic material’s thickness24,42 or shape1,43,44,45.
Methods
Device fabrication
First, we fabricate the H-shaped local gates structure with a total length of 4.2 μm, a total width of 2 μm and a narrow width region (tip) of 500 nm on a Si/SiO2 substrate using electron beam lithography (EBL) followed by evaporation of titanium (2 nm)/gold (30 nm). The gap between the gates is 155 nm. Afterwards, we transfer a hBN/graphene/hBN stack onto the metallic gates. We cleave and exfoliate the top and bottom hBN and the graphene onto freshly cleaned Si/SiO2 substrates, stack them following the Van der Waals assembly technique46,47 and release onto the gates. We then use EBL with a PMMA 950 K resist film to pattern source and drain electrodes and expose the device to a plasma of CHF3/O2 gases to partially etch the Van der Waals stack. Subsequently, we deposit side contacts of chromium (5 nm)/gold (80 nm) and lift off in acetone as described in ref. 46. We then etch the hBN-encapsulated graphene into an H-shape using a CHF3/O2 plasma and deposit 17 nm of Al2O3 using atomic layer deposition (ALD). Finally we pattern the bow-tie antenna of 2.7 μm total length (L) and with a small gap of 200 nm between its branches with EBL and deposit titanium (2 nm)/gold (80 nm). We point out that the bow-tie antenna and gate dimensions were selected based on preliminary optical simulations based on a simplified device, ignoring bow-tie antenna interactions with gates and metal electrodes, resulting in the non-optimal performance as evident from Fig. 4. By performing 2-terminal configuration electrical measurements as a function of the gate voltages (varying VL and VR both at the same potential), we attain 12,000 cm2 V−1 s−1 as a lower bound of the estimated mobility (Supplementary Figs. 15, 16 and Supplementary Note 4).
Measurements
We use a pulsed QCL mid-IR laser (LaserScope from Block Engineering) that is linearly polarized and has a wavelength tuning range from λ = 6.1 to 10 μm. We scan the device position with motorized xyz-stage. We modulate the mid-IR laser employing an optical chopper at 422 Hz and we measure the photocurrent using a lock-in amplifier (Stanford Research). We focus the mid-IR light with a reflective objective with a numerical aperture (NA) of 0.5. We measure the mid-IR power using a thermopile detector from Thorlabs placed at the sample position.
For the time-resolved measurements, we set the QCL wavelength to λ = 6.6 μm with a pulse width of 496 ns. We use a MCT as a reference detector from VIGO System model PCI-2TE-13. We measure the photoresponse using a current amplifier from FEMTO model DHPCA-100 with switchable gain and acquire the signal with an oscilloscope from Teledyne Lecroy model HDO6000.
Responsivity and NEP calculation
The external responsivity is given by: Responsivity = (IPTE/Pin) × (Afocus/Adiff)16,34,48,49, where Pin is the power measured by the commercial power meter, Afocus is the experimental beam area at the measured wavelength and Adiff is the diffraction-limited spot size. We measure the photocurrent IPTE from the output signal of the lock-in amplifier VLIA considering \({I}_{{\rm{PTE}}}=\frac{2\pi \sqrt{2}}{4\xi }{V}_{{\rm{LIA}}}\) (refs. 34,48,49), where ξ is the gain factor in V/A (given by the lock-in amplifier). We use the ratio Adiff/Afocus for estimating the power reaching our photodetector since Adiff is the most reasonable value one can attain when considering the detector together with an optimized focusing system (e.g. using hemispherical lens) and it is widely used in the literature for comparing the performances among photodetectors16,34,48,49. Note that this simple geometrical scaling is not used here to predict the exact performance at a hypothetical diffraction-limited spot but rather as clear performance benchmark so to consistently compare different device architectures measured at differed focusing conditions. We usually have a ratio of Afocus/Adiff ≈ 7. This ratio is given by \({A}_{{\rm{diff}}}/{A}_{{\rm{focus}}}=\frac{{w}_{0,{\rm{diff}}}^{2}}{{w}_{0,{\rm{x}}}{w}_{0,{\rm{y}}}}\). In order to obtain w0,x and w0,y we use our experimental observation that the photocurrent is linear in laser power and measure the photocurrent while scanning the device in the x- and y-direction. Consequently, the photocurrent is described by Gaussian distributions \(\propto {{\rm{e}}}^{-2{x}^{2}/{w}_{0,{\rm{x}}}^{2}}\) and \(\propto {{\rm{e}}}^{-2{y}^{2}/{w}_{0,{\rm{y}}}^{2}}\), where w0,x and w0,y are the respectively obtained spot sizes (related to the standard deviation via σ = w0/2 and to the FWHM = \(\sqrt{2\mathrm{ln}\,(2)}{w}_{0}\)). We usually achieve w0,x = 5.05 μm and w0,y = 5.40 μm at λ = 6.6 μm (Supplementary Fig. 13b). For the diffraction-limited spot, we consider \({w}_{0,{\rm{diff}}}=\frac{\lambda }{\pi }\), with λ the mid-IR laser wavelength. The diffraction-limited area is hence taken as \({A}_{{\rm{diff}}}=\pi {w}_{0,{\rm{diff}}}^{2}={\lambda }^{2}/\pi\). Additionally, the noise-equivalent power (NEP) that characterizes the sensitivity of the photodetector is defined as NEP = Inoise/Responsivity and considering that our unbiased photodetector has a very low noise current that is limited by Johnson noise, we use a noise spectral density \({I}_{{\rm{noise}}}=\sqrt{\frac{4{k}_{{\rm{B}}}T}{{R}_{{\rm{D}}}}}\), where kB corresponds to the Boltzmann constant, T is the operation temperature (300 K) and RD the device resistance.
Data availability
The data that support the plots within this paper and other findings of this study are available from the corresponding author upon reasonable request.
References
Caldwell, J. D. et al. Sub-diffractional volume-confined polaritons in the natural hyperbolic material hexagonal boron nitride. Nat. Commun. 5, 5221 (2014).
Caldwell, J. D. et al. Low-loss, infrared and terahertz nanophotonics using surface phonon polaritons. Nanophotonics 4, 44–68 (2015).
Basov, D. N., Fogler, M. M. & García De Abajo, F. J. Polaritons in van der Waals materials. Science 354, aag1992 (2016).
Low, T. et al. Polaritons in layered two-dimensional materials. Nat. Mater. 16, 182–194 (2016).
Giles, A. J. et al. Ultralow-loss polaritons in isotopically pure boron nitride. Nat. Mater. 17, 134–139 (2018).
Hu, G., Shen, J., Qiu, C. W., Alù, A. & Dai, S. Phonon polaritons and hyperbolic response in van der Waals materials. Adv. Optical Mater. 1901393, 1–19 (2019).
Foteinopoulou, S., Devarapu, G. C. R., Subramania, G. S., Krishna, S. & Wasserman, D. Phonon-polaritonics: enabling powerful capabilities for infrared photonics. Nanophotonics 8, 2129–2175 (2019).
Dai, S. et al. Graphene on hexagonal boron nitride as a tunable hyperbolic metamaterial. Nat. Nanotechnol. 10, 682–686 (2015).
Nikitin, A. Y. et al. Nanofocusing of hyperbolic phonon polaritons in a tapered boron nitride slab. ACS Photonics 3, 924–929 (2016).
Tamagnone, M. et al. Ultra-confined mid-infrared resonant phonon polaritons in van der Waals nanostructures. Sci. Adv. 4, 4–10 (2018).
Autore, M. et al. Boron nitride nanoresonators for Phonon-Enhanced molecular vibrational spectroscopy at the strong coupling limit. Light Sci. Appl. 7, 17172–17178 (2018).
Lemme, M. C. et al. Gate-activated photoresponse in a graphene p–n junction. Nano Lett. 11, 4134–4137 (2011).
Gabor, N. M. et al. Hot carrier-assisted intrinsic photoresponse in graphene. Science 334, 648–652 (2011).
Song, J. C. W., Rudner, M. S., Marcus, C. M. & Levitov, L. S. Hot carrier transport and photocurrent response in graphene. Nano Lett. 11, 4688–4692 (2011).
Koppens, F. H. L. et al. Photodetectors based on graphene, other two-dimensional materials and hybrid systems. Nat. Nanotechnol. 9, 780–793 (2014).
Castilla, S. et al. Fast and sensitive terahertz detection using an antenna-integrated graphene pn junction. Nano Lett. 19, 2765–2773 (2019).
Peng, C. et al. Compact mid-infrared graphene thermopile enabled by a nanopatterning technique of electrolyte gates. N. J. Phys. 20, 083050 (2018).
Schuler, S. et al. Graphene photodetector integrated on a photonic crystal defect waveguide. ACS Photonics 5, 4758–4763 (2018).
Muench, J. E. et al. Waveguide-integrated, plasmonic enhanced graphene photodetectors. Nano Lett. 19, 7632–7644 (2019).
Li, Z. Q. et al. Dirac charge dynamics in graphene by infrared spectroscopy. Nat. Phys. 4, 532–535 (2008).
Low, T. & Avouris, P. Graphene plasmonics for terahertz to mid-infrared applications. ACS Nano 8, 1086–1101 (2014).
Tielrooij, K.-J. et al. Out-of-plane heat transfer in van der Waals stacks through electron-hyperbolic phonon coupling. Nat. Nanotechnol. 13, 41–46 (2018).
Tielrooij, K. J. et al. Generation of photovoltage in graphene on a femtosecond timescale through efficient carrier heating. Nat. Nanotechnol. 10, 437–443 (2015).
Woessner, A. et al. Electrical detection of hyperbolic phonon-polaritons in heterostructures of graphene and boron nitride. npj 2D Mater. Appl. 1, 25 (2017).
Pons-Valencia, P. et al. Launching of hyperbolic phonon-polaritons in h-BN slabs by resonant metal plasmonic antennas. Nat. Commun. 10, 3242 (2019).
Bistritzer, R. & MacDonald, A. H. Electronic cooling in graphene. Phys. Rev. Lett. 102, 13–16 (2009).
Herring, P. K. et al. Photoresponse of an electrically tunable ambipolar graphene infrared thermocouple. Nano Lett. 14, 901–907 (2014).
Hsu, A. L. et al. Graphene-based thermopile for thermal imaging applications. Nano Lett. 15, 7211–7216 (2015).
Dai, S. et al. Subdiffractional focusing and guiding of polaritonic rays in a natural hyperbolic material. Nat. Commun. 6, 1–7 (2015).
Guo, Q. et al. Efficient electrical detection of mid-infrared graphene plasmons at room temperature. Nat. Mater. 17, 986–992 (2018).
Cakmakyapan, S., Lu, P. K., Navabi, A. & Jarrahi, M. Gold-patched graphene nano-stripes for high-responsivity and ultrafast photodetection from the visible to infrared regime. Light Sci. Appl. 7, 20 (2018).
Sassi, U. et al. Graphene-based mid-infrared room-temperature pyroelectric bolometers with ultrahigh temperature coefficient of resistance. Nat. Commun. 8, 14311 (2017).
Yu, X. et al. Narrow bandgap oxide nanoparticles coupled with graphene for high performance mid-infrared photodetection. Nat. Commun. 9, 1–8 (2018).
Vicarelli, L. et al. Graphene field-effect transistors as room-temperature terahertz detectors. Nat. Mater. 11, 865–871 (2012).
Generalov, A. A., Andersson, M. A., Yang, X., Vorobiev, A. & Stake, J. A 400-GHz Graphene FET Detector. IEEE Trans. Terahertz Sci. Technol. 7, 614–616 (2017).
Rogalski, A. Graphene-based materials in the infrared and terahertz detector families: a tutorial. Adv. Opt. Photonics 11, 314 (2019).
Rogalski, A., Martyniuk, P. & Kopytko, M. Challenges of small-pixel infrared detectors: a review. Rep. Prog. Phys. 79, 046501 (2016).
Goossens, S. et al. Broadband image sensor array based on graphene-CMOS integration. Nat. Photonics 11, 366–371 (2017).
Ma, W. et al. In-plane anisotropic and ultra-low-loss polaritons in a natural van der Waals crystal. Nature 562, 557–562 (2018).
Zheng, Z. et al. Highly confined and tunable hyperbolic phonon polaritons in van der waals semiconducting transition metal oxides. Adv. Mater. 30, 1–9 (2018).
Zheng, Z. et al. A mid-infrared biaxial hyperbolic van der Waals crystal. Sci. Adv. 5, 1–9 (2019).
Dai, S. et al. Tunable phonon polaritons in atomically thin van der Waals crystals of boron nitride. Science 343, 6175, 1125–1129 (2014).
Kalfagiannis, N., Stoner, J. L., Hillier, J., Vangelidis, I. & Lidorikis, E. Mid- to far-infrared sensing: SrTiO3, a novel optical material. J. Mater. Chem. C 7, 7851 (2019).
Alfaro-Mozaz, F. J. et al. Deeply subwavelength phonon-polaritonic crystal made of a van der Waals material. Nat. Commun. 10, 42 (2019).
Li, P. et al. Hyperbolic phonon-polaritons in boron nitride for near-field optical imaging and focusing. Nat. Commun. 6, 1–9 (2015).
Wang, L. et al. One-dimensional electrical contact to a two-dimensional material. Science 342, 614–7 (2013).
Pizzocchero, F. et al. The hot pick-up technique for batch assembly of van der Waals heterostructures. Nat. Commun. 7, 11894 (2016).
Spirito, D. et al. High performance bilayer-graphene terahertz detectors. Appl. Phys. Lett. 104, 061111 (2014).
Viti, L., Purdie, D. G., Lombardo, A., Ferrari, A. C. & Vitiello, M. S. HBN-encapsulated, graphene-based, room-temperature terahertz receivers, with high speed and low noise. Nano Lett. 20, 3169–3177 (2020).
Acknowledgements
The authors thank David Alcaraz-Iranzo, Jianbo Yin, Iacopo Torre, Hitesh Agarwal, Bernat Terrés and Ilya Goykmann for fruitful discussions. F.H.L.K. acknowledges financial support from the Spanish Ministry of Economy and Competitiveness, through the “Severo Ochoa” Programme for Centres of Excellence in R& D (SEV-2015-0522), support by Fundacio Cellex Barcelona, Generalitat de Catalunya through the CERCA program, and the Agency for Management of University and Research Grants (AGAUR) 2017 SGR 1656. Furthermore, the research leading to these results has received funding from the European Union Seventh Framework Programme under grant agreement no. 785219 and no. 881603 Graphene Flagship for Core2 and Core3. ICN2 is supported by the Severo Ochoa program from Spanish MINECO (Grant No. SEV-2017-0706). K.J.T. acknowledges funding from the European Union’s Horizon 2020 research and innovation programme under Grant Agreement No. 804349. R.H. acknowledges financial support from the Spanish Ministry of Science, Innovation and Universities (national project RTI2018-094830-B-100 and the project MDM-2016-0618 of the Marie de Maeztu Units of Excellence Program) and the Basque Government (grant No. IT1164-19). S.C. acknowledges financial support from the Barcelona Institute of Science and Technology (BIST), the Secretaria d’Universitats i Recerca del Departament d’Empresa i Coneixement de la Generalitat de Catalunya and the European Social Fund (L’FSE inverteix en el teu futur)—FEDER. D.E. acknowledges partial support from the Army Research Office MURI “Ab-Initio Solid-State Quantum Materials” Grant No. W911NF18-1-0431. J.G. was supported by the ARL-MIT Institute for Soldier Nanotechnologies (ISN). T.S. and L.M.M. acknowledge support by Spain’s MINECO under Grant No. MAT2017-88358-C3-1-R and the Aragon Government through project Q-MAD.
Author information
Authors and Affiliations
Contributions
F.H.L.K., R.H., M.A., and S.C. conceived the project. S.C. fabricated the device and performed the experiments. V.P. assisted in device fabrication and experiments. M.A. supported the device fabrication. I.V. and E.L. performed the simulations and developed the multiphysics model. S.C., T.S., and L.M.-M. assisted in the modeling. S.C., K.R., J.G. and M.A. performed preliminary optical simulations. S.C., I.V., E.L., and F.H.L.K. wrote the manuscript. J.G., S.K., and K.-J.T. assisted with measurements and discussion of the results. K.W. and T.T. synthesized the hBN crystals. D.E., R.H., K.-J.T., E.L., and F.H.L.K. supervised the work and discussed the results. All authors contributed to the scientific discussion and manuscript revisions. S.C. and I.V. contributed equally to the work.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Nezih Yardimci and the other, anonymous reviewers for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Castilla, S., Vangelidis, I., Pusapati, VV. et al. Plasmonic antenna coupling to hyperbolic phonon-polaritons for sensitive and fast mid-infrared photodetection with graphene. Nat Commun 11, 4872 (2020). https://doi.org/10.1038/s41467-020-18544-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-020-18544-z
- Springer Nature Limited
This article is cited by
-
Infrared photodetection in graphene-based heterostructures: bolometric and thermoelectric effects at the tunneling barrier
npj 2D Materials and Applications (2024)
-
Tailored plasmon polariton landscape in graphene/boron nitride patterned heterostructures
npj 2D Materials and Applications (2024)
-
Planar hyperbolic polaritons in 2D van der Waals materials
Nature Communications (2024)
-
Real-space nanoimaging of hyperbolic shear polaritons in a monoclinic crystal
Nature Nanotechnology (2023)
-
Highly directional and carrier density-independent plasmons in quasi-one-dimensional electron gas systems
Communications Physics (2023)