Abstract
Chemical doping is one of the most important strategies for tuning electrical properties of semiconductors, particularly thermoelectric materials. Generally, the main role of chemical doping lies in optimizing the carrier concentration, but there can potentially be other important effects. Here, we show that chemical doping plays multiple roles for both electron and phonon transport properties in half-Heusler thermoelectric materials. With ZrNiSn-based half-Heusler materials as an example, we use high-quality single and polycrystalline crystals, various probes, including electrical transport measurements, inelastic neutron scattering measurement, and first-principles calculations, to investigate the underlying electron-phonon interaction. We find that chemical doping brings strong screening effects to ionized impurities, grain boundary, and polar optical phonon scattering, but has negligible influence on lattice thermal conductivity. Furthermore, it is possible to establish a carrier scattering phase diagram, which can be used to select reasonable strategies for optimization of the thermoelectric performance.
Similar content being viewed by others
Introduction
Thermoelectric (TE) materials enable direct conversion between heat and electricity. They can be used to generate electricity based on the Seebeck effect when a thermal gradient exists or to transfer heat against temperature gradient based on the Peltier effect when an electric current is applied1. Many thermoelectric materials are being explored for power generation applications, such as half-Heusler2, PbTe3,4,5, silicides6, CoSb37, and Mg3Sb28. The energy conversion efficiency for TE materials depends heavily on the TE material performance. Practical applications require further improvement on the performance of TE materials. This is quantified by the thermoelectric figure of merit, zT = α2σT/(κele + κlat), where α, σ, T, κele, and κlat are the Seebeck coefficient, the electrical conductivity, the absolute temperature, the electronic thermal conductivity, and the lattice thermal conductivity, respectively9. Good TE materials generally have features as Phonon Glass Electron Crystal, which means good electrical transport properties, characteristic of crystalline semiconductors, and a low thermal conductivity, characteristic of glasses10.
The optimization of TE performance is complex, requiring manipulation and optimization of both the electrical and thermal transport11. This includes controlling the underlying scattering mechanisms, e.g. alloy scattering12, ionized impurity scattering13, carrier-carrier scattering14, acoustic and optical phonon scatterings15 for the charge carriers, and phonon anharmonicity16,17,18, atomic rattling19, nanostructuring20, and glass-like or superionic behavior21,22,23 for the phonons. Due to the diverse temperature dependences of the scattering mechanisms, electrical and thermal conductivities, in general, exhibit different temperature dependences. For instance, the carrier mobility follows μac ∝ T−3/2 for acoustic phonon dominated scattering, μpe ∝ T−1/2 for piezoelectric scattering, or μi ∝ T3/2 for ionized impurity scattering24, while the lattice thermal conductivity follows κU ∝ T−1 for Umklapp scattering or κal ∝ T−1/2 for alloy scattering25,26.
On the other hand, the scattering rates for the carrier scattering mechanisms also show strong carrier concentration dependences (n for electron concentration, p for hole concentration), and may be more complex than the standard parabolic band expressions noted above. As an example, changes in carrier concentration could alter the carrier energy or carrier density of states around the Fermi level, and hence influence the acoustic phonon scattering and the mobility27. As demonstrated in Fig. 1a, the carrier transport in most TE semiconductors, except the lead chalcogenides, are dominated by the phonon scattering, and the mobility shows almost monotonous decrease with the carrier concentration, n or p15,28,29,30,31. The temperature and carrier concentration dependences of the scattering provide possibilities for the manipulation of the transport properties. Therefore, mapping of a carrier scattering phase diagram in the space of temperature and carrier concentration would provide a useful guidance for optimization or design of TE materials, such as the study of BXGa (X = Be, Mg, and Ga) compounds32.
Half-Heusler (HH) TE compounds, which are used for promising power generation applications, have attracted extensive attentions in recent years33,34. Since the study of ZrNiSn compounds35,36,37, large zT values above unity can be obtained in both n-type and p-type HH alloys38,39. The carrier transport mechanism underlying their high TE performance has been a focus of study. Current studies of the carrier transport mechanisms in half-Heusler compounds mainly focus on acoustic phonons, alloy, and grain boundary scatterings. These exhibit distinct temperature dependences12,40,41,42. On the other hand, the carrier concentration dependent carrier mobility, µ(n/p), of HH compounds has been rarely studied. As summarized in Fig. 1b, µ(n/p) of both n-type and p-type HH compounds exhibits a non-monotonous behavior and the peak µ(n/p) usually occurs near to the optimal n/p of the system, where the zT peaks40,41,42,43. This indicates that the carrier scattering mechanisms in HH compounds have strong dependences on the carrier concentration. The decrease of µ(n/p) at high n/p region is generally thought to be a result of the acoustic phonon scattering, as exhibited in Fig. 1a. However, the increase of µ(n/p) in the low n/p region suggests some other important scattering mechanisms, which are not well understood and motivate further study.
Here, we use high-quality single and polycrystalline samples, and various probes, including electrical and thermal transport measurements, neutron powder diffraction (NPD) and inelastic neutron scattering (INS) measurements, and first-principles calculations, to identify the electron and phonon transport behavior of Sb-doped ZrNiSn, a representative HH TE system. We reveal important scattering beyond the acoustic phonon scattering. Specifically, ionized impurity, grain boundary, and polar optical phonon scatterings are shown to contribute significantly in controlling the electrical transport. Moreover, the effect of electron–phonon interactions on lattice thermal conductivity is comprehensively analyzed. Based on these results and analysis, a carrier scattering phase diagram is established. This could serve as a guide in further improvement of the TE performance in HH compounds.
Results
Electrical and thermal transport properties
High-quality ZrNiSn1−xSbx polycrystalline samples were made by levitation melting and spark plasma sintering (see Methods for details). All the polycrystalline samples contain 5–7% more interstitial Ni on the 4d (¾, ¾, ¾) site (Supplementary Fig. 1), being consistent with the previous electron probe microanalysis40. Temperature dependences of the mobility in these polycrystalline samples were studied over the temperature range of 5 K to 315 K (variation of nH with T and Sb content are shown in Supplementary Fig. 3). µ(T) of Sb-doped samples monotonically decreases with temperature (Fig. 2a), since the acoustic phonon and alloy scatterings contribute importantly to the electron scattering. Meanwhile, the undoped ZrNiSn parent sample exhibits a positive dependence of µ(T) on temperature, opposite to the doped samples. Similar to n-type Mg3(Sb,Bi)2 system, this kind of increasing trend of µ(T) raises the issue of the carrier scattering mechanism in underdoped TE materials with low carrier concentration or with small grain size44,45, i.e., does the increased µ(T) below the crossover temperature stems from the grain boundary scattering or ionized impurity scattering44,45?
One direct way to answer this question would be a comparative study of the temperature-dependent electrical conductivity of both polycrystalline and single-crystalline samples, thereby addressing the issue of grain boundary scattering. High-quality single crystalline ZrNiSn1-xSbx samples were then grown by a Sn-flux method46 (details are given in Methods). The corresponding µ(T) is presented in Fig. 2b. The µ(T) of the undoped ZrNiSn single crystal, which by nature does not have grain boundaries, still shows an increasing trend with T. This indicates that ionized impurities might dominate the electron transport. The µ(T) for the Sb-doped ZrNiSn1-xSbx crystals exhibits a decreasing trend with T, similar to the doped polycrystalline samples (Fig. 2a). The carrier concentration dependent µ(n) at 300 K of both polycrystalline and single-crystalline samples is displayed in Fig. 2c. The µ(n) of single crystals is larger than that of polycrystalline samples at low n region (<1021 cm−3) while they converge at the high n heavily doped region (>1021 cm−3), indicating that grain boundaries also play a significant role in scattering electrons of lightly doped polycrystalline samples. Additionally, the non-monotonous dependence of µ(n), as observed in the representative polycrystalline HH systems (Fig. 1b), is also shown in the single crystalline ZrNiSn1-xSbx samples.
We now turn to the thermal transport. The lattice thermal conductivity κlat of polycrystalline ZrNiSn1-xSbx samples over the temperature range of 2 K to 300 K is shown in Fig. 2d (temperature dependences of the electronic resistivity ρ, Lorenz number L, electronic thermal conductivity κele, and total thermal conductivity κtot are provided in Supplementary Fig. 4). It is surprisingly found that over the whole studied temperature range Sb doping does not show a significant effect on the κlat of ZrNiSn. This is true even for the extreme case where 12% of Sn was replaced by aliovalent Sb. The atomic mass and radius of Sb are close to those of Sn. Nonetheless, the fact that such a high content of aliovalent doping does not obviously affect the phonon propagation is unexpected, since in many solid materials even partial isotopic substitution can lead to a significant changes in the κlat47,48. In the very similar case of Sn-doped ZrCoSb1-xSnx HH compounds, replacement of 10% of the Sb by Sn results in a large reduction of ~45% in the κlat near room temperature43. Similarly, in p-type NbFeSb-based compounds, aliovalent doping also significantly suppresses the lattice thermal conductivity33,49. Therefore, the present result together with the non-monotonous dependence of µ(n) motivate further exploration of the underlying electron and phonon transport mechanisms in the ZrNiSn1-xSbx system.
Phonon density of states
To understand the effects of electron doping on the electron and phonon transport properties in ZrNiSn-based HH compounds, it is necessary to consider electron–phonon interactions. We begin with the phonons. Phonon density of states (DOSs) measurements for ZrNiSn1−xSbx with different electron concentrations were carried out on the High-Resolution Chopper Spectrometer, BL12 HRC, at MFL of J-PARC. The momentum and energy dependence of powder-averaged dynamical structure factor, S(Q, E), of ZrNiSn at 300 K, as an example, are shown in Fig. 3a. The phonon signal shows normal Q2 dependence. The neutron-weighted phonon DOSs were obtained by integration of the S(Q, E) over the range of momentum transfers 0.4 ≤ Q ≤ 6.0 Å−1. The carrier concentration dependence of neutron-weighted phonon DOSs of ZrNiSn1−xSbx is shown in Fig. 3b. Three phonon bands, 0–18.5 meV, 18.5–25.5 meV, and 25.5–33 meV, are observed, corresponding to one acoustic phonon band and two optical phonon bands, respectively. Due to the different ratios of neutron scattering cross-section over atomic mass, σ/m, of the different elements, the motions of Ni are overemphasized while those for Zr and Sn/Sb are underestimated. The phonon DOS as obtained from first-principles calculations shown in Fig. 3c for ZrNiSn with proper neutron weighting is in good agreement with experimental data (see Supplementary Fig. 5 for calculated phonon DOSs without neutron weighting).
Electron–phonon interaction and lattice thermal conductivity
A careful comparison of the phonon DOSs in Fig. 3b shows that the optical phonon bands exhibit clear changes with n. A prominent tail is present above 30 meV for the parent ZrNiSn sample, which gradually becomes smaller with increasing n. However, the calculated phonon transport properties of ZrNiSn demonstrate that the optical phonons above ~25 meV have much smaller group velocity (Fig. 3d), and suffer stronger scattering (Fig. 3e). Hence, they have a quite small contribution to the average lattice thermal conductivity, κlat, (<~1.5%, Fig. 3f), and the changes in the optical phonons cannot make a palpable influence on κlat. In addition, the acoustic phonon band in Fig. 3b is insensitive to changes in n. This is one indication of relatively weak coupling between electrons and acoustic phonons. This weak coupling could be attributed to the symmetry-protected non-bonding orbitals-electron states or impotent acoustic phonons deformation potentials50. Since the acoustic phonons are the main carriers for thermal energy with large group velocity (Fig. 3d) and small scattering rate (Fig. 3e), it might be the overall weak interaction between the electrons and heat-carrying acoustic phonons and the negligible contribution of the optical phonons (above ~25 meV) that make the κlat does not show obvious changes in the polycrystalline ZrNiSn1−xSbx compounds with different carrier concentrations or Sb contents (Fig. 2d).
LO–TO splitting and polar optical phonon scattering
We turn to the observed non-monotonous behavior of µ(n) (Figs. 1b and 2c). The 25.5–33 meV optical phonon band of the ZrNiSn parent sample, which contains the prominent tail, can be decomposed into two peaks as shown in Fig. 4a. To understand the origin of the tail, first-principles calculations of phonon dispersion are performed. As shown in Fig. 4b, the degeneracy of longitudinal optical (LO) phonon and transverse optical (TO) phonon at ~28 meV is lifted around the Brillouin zone center, corresponding to the LO–TO splitting. The peaks centered at ~28.9 meV in Fig. 4a corresponds to the TO branches, while the ~31.9 meV one represents the LO branch.
The LO–TO frequency (energy) difference is due to the long-range electric field in an insulator51. This polarization field is produced by the LO phonon vibration, which in turn can raise the frequency of LO branch (see methods for details). In addition, this polarization field also imposes a strong disturbance on the carrier transport, via the Fröhlich electron-phonon interaction27,52. This coupling between electrons and polar optical phonons can be assessed by the dimensionless polar coupling constant:
ħ is the Planck constant, m* is the effective mass of electrons, ωLO is the LO frequency, and ε∞ and εs are the high-frequency and static dielectric functions. The observation of the LO–TO splitting in ZrNiSn confirms that HH compounds exhibit polar chemical bonds53. This mixed bonding can also be important for the thermal conductivity54. The polar coupling constant, αPO, for ZrNiSn is estimated as 0.32, indicating that the polar optical phonon scattering could play an important role in electrical transport properties.
We now turn to the collapse of the tail in the phonon DOSs with Sb doping (Fig. 3b). The optical phonon energy is connected to the reduced-atomic-mass by the relation: ωop ∝ Mr−1/2, where the reduced-atomic-mass is defined as \(M_{\mathrm{r}} = 1/\mathop {\sum }\limits_a \left( {1/M_a} \right)\), where Ma is the mass of atom a in unit cell. However, the modification of the optical phonon energy by 12% doping of Sb is less than 0.04%, which is too small to explain the change observed in the phonon DOSs.
Instead, the screening effect needs to be considered to explain the collapse of the LO–TO splitting. The presence of free carriers and the concomitant screening can modify both the electron-LO phonon interaction and the dispersion of the LO optical phonons, such as Kohn anomaly of the phonon branch in metals55. For the LO–TO splitting, the additional restoring force of the LO vibrations is a Coulomb interaction. This Coulomb interaction can be well screened by free carriers. This can be described in the Thomas-Fermi approximation (see methods for details)56. Higher free carrier concentration leads to better screening, shorter Thomas-Fermi screening length, rTF, and hence smaller Coulomb interaction and LO–TO splitting as schematized in Fig. 4c. The phonon DOSs (in Fig. 4d) from first-principles calculations with consideration of the screening effect reproduce this change (detailed changes in the phonon dispersion with Sb doping are given in Supplementary Fig. 6). This change is also confirmed by the reduced LO–TO splitting as determined from the phonon DOSs measurements (see Fig. 4e). This reduction of LO–TO splitting could also be well simulated (dashed line in Fig. 4e) with the screening model as described with Eqs. (2) and (4) in Methods. In addition, this reduced LO–TO splitting or polarization field is accompanied by a raising mobility, µpo(n), that is limited by polar optical phonon scattering40. However, the release of the polar optical phonon scattering is accompanied by an enhancement of the acoustic phonon scattering as shown in Fig. 2c. This crossover lead to an optimal carrier concentration and mobility around n = 3–5 × 1020 cm−3 for the TE performance of ZrNiSn-based compounds (Fig. 2c).
Following the screening scenario, additional free charge carriers could enhance the screening effect in all semiconductors, and transitions between different carrier scattering mechanisms are expected from the low n/p region to the high n/p region, hence a non-monotonous carrier mobility. However, of the semiconductors listed in Fig. 1, only the lead chalcogenides and half-Heusler compounds are known to exhibit non-monotonous behavior at room temperature. To explain the different dependences of carrier mobility on carrier concentration, the polar coupling constants of the half-Heusler compounds are calculated using the Eq. (1) (see Supplementary Table 1 and Supplementary Fig. 7 for details). A comparison of the polar coupling constants between different samples is shown in Fig. 4f. Compared with the lead chalcogenides and half-Heusler compounds, the polar coupling is much weaker in InSb, CoSb3, and GaAs compounds, indicating smaller, and perhaps negligible polar optical phonon scattering in those compounds. Therefore, screening of the polar optical phonon scattering does not make important changes to the carrier mobility in those compounds. In contrast, the screening of polar optical phonon scattering in the more strongly-polar lead chalcogenides and half-Heusler compounds would noticeably tune the dominant carrier scattering mechanisms, leading to the non-monotonous behavior.
Finally, we comment on the details of the phonon modes based on first-principles calculations. The results are shown in the insets of Fig. 4b. The primitive unit cell of ZrNiSn contains three atoms, and therefore, there are 6 optical phonon branches. The three high energy optical phonon branches correspond to the LO–TO splitting, while the other three low energy optical phonon branches do not present obvious LO–TO splitting. For both the high and low energy branches, the Ni and Sn atoms vibrate in opposite directions. This is consistent with the molecular orbitals analysis of ZrNiSn, where the Ni and Sn atoms primarily form (NiSn)4- clusters and then bond with the Zr4+ cations to form the ZrNiSn compound57. The difference between the high and low energy branches relates to the vibration of Zr. Given that the Ni atoms sit at the centers of both the Zr and Sn tetrahedrons, the opposite vibration of both the Zr and Sn with respect to the Ni would involve relatively larger chemical bonding forces, and hence correspond to the higher energy optical phonon branches. The small LO–TO splitting for the low energy optical phonon can then be attributed to the relatively larger group velocity and small displacement of the (NiSn)4- cluster with respect to the Zr sublattice.
Discussion
The effects of dielectric screening on carrier mobility are not just limited to the polar optical phonon scattering58,59. Rather we find other important effects. Polar optical phonon scattering becomes weak at low temperature, because of the Bose factor that means that there are no excited optical phonons at low temperature. However, the non-monotonous behavior of the µ(n/p) does not disappear at low temperature, but becomes more evident as depicted in Supplementary Fig. 8. This phenomenon is attributed to the screening of the ionized impurity and grain boundary scatterings, since these are the dominant scattering mechanisms at low temperatures. Taken the ionized impurity scattering as an example, the potential of the ionized impurities in heavily doped semiconductor cannot be described by the bare Coulomb potential, \(\varphi (r) \propto \frac{1}{r}\), any more, while a new formula in the Thomas-Fermi approximation, \(\varphi (r) \propto \frac{1}{r}{\mathrm{exp}}( - \frac{r}{{r_{{\mathrm{TF}}}}})\), should be applied56. As schematized in Supplementary Fig. 9, the screened potential drops more quickly than the bare Coulomb potential, and then the scattering is weaker.
According to the definition of the Thomas-Fermi screening length (see Eq. (5) in Methods), the screening effect becomes weaker with increasing temperature. Nonetheless, it is still effective at higher temperature, even at 800 K40. This is important for the manipulation of the carrier scattering mechanisms in the ZrNiSn-based compounds. In addition, our previous study demonstrated that the polar optical phonon, acoustic phonon, and alloy scatterings, which are the main carrier scattering mechanisms at 300 K, still play the dominated roles at higher temperature, and crossover between these scattering mechanisms can also been realized by introducing the screening effect40.
In summary, different carrier scattering mechanisms in ZrNiSn-based half-Heusler compounds are studied with high-quality single and polycrystalline crystals, combined with electrical transport measurements, neutron powder diffraction and inelastic neutron scattering measurements, as well as theoretical calculations. With increasing carrier concentration n, a crossover of the carrier mobility µ(n) and optimal TE performance are found in the region of n = 3–5 × 1020 cm−3. This crossover of µ(n) corresponds to the variation of the dominant scattering mechanisms, from ionized impurity and grain boundary scattering to acoustic phonon/alloy scatterings at low temperature, or from polar optical phonon scattering to acoustic phonon/alloy scatterings at high temperature. These crossovers between different dominant scattering mechanisms are realized through the screening of the ionized impurity, grain boundary and polar optical phonon scattering, and the enhancement of acoustic phonon/alloy scatterings. On the bases of these insights into the different carrier scatterings, a carrier scattering phase diagram may be derived. This is shown in Fig. 5, and could be used as a guide for the further improvement of the TE properties in the half-Heusler TE materials. For example, grain boundaries, which are frequently employed to reduce lattice thermal conductivity, have an adverse effect on carrier transport in lightly doped half-Heusler compounds, e.g. NbFe0.95Ti0.05Sb60. This would work against the efforts to suppress the lattice thermal conductivity in improving TE performance. However, the grain boundary scattering for carrier transport could be well screened in heavily doped semiconductor, e.g. NbFe0.8Ti0.2Sb, and the introduction of grain boundaries could successfully improve the TE performance49. We expect the establishment of such a carrier scattering phase diagram in other TE systems could also help to choose reasonable and effective strategies for the optimization of TE performance.
Methods
Synthesis
Ingots of nominal ZrNiSn1−xSbx (x = 0.00, 0.04, 0.08, and 0.12) compounds were synthesized by levitation melting of stoichiometric amount of Zr, Ni, Sn, and Sb under argon atmosphere. The melting was carried out three times to ensure homogeneity. The ingots were ground into powder, and then sintered using spark plasma sintering (SPS-1050, Sumitomo Coal Mining Co.) at 1193 K for 10 min under a pressure of 65 MPa in vacuum. The densities of the as-sintered samples are 95% of theoretical densities. Then, the SPS-samples were used for both physical properties and neutron scattering measurements. NPD measurements (Supplementary Fig. 1) do not show discernible impurity phases. All samples show extra Ni at the vacancy site, and the occupancy varies between 4.9% and 6.4%, being consistent with previous results from Electron Probe Microanalysis measurements40.
The undoped and Sb-doped ZrNiSn1−ySby single crystals were grown by a Sn Flux method. The starting powders of Zr, Ni, Sn, and Sb were mixed together in a molar ratio of 1: 1: 10: y (y = 0–0.10). The mixtures were sealed in a dry quartz tube under high vacuum, which was heated up to 1100 °C in 15 h and further dwelled for 24 h. After that, the tube was slowly cooled down to 650 °C at a rate of 2 °C/h. Single crystals were obtained after a centrifuging process to remove the Sn flux. The as-grown single crystals with typical size of 2 mm were checked and oriented at room temperature by a Laue X-ray diffractometer, which show sharp and distinct diffraction spots (Supplementary Fig. 2), indicating high quality and crystallinity.
Physical properties
The electrical and thermal transport properties are characterized using the Physical Property Measurement System (PPMS) with the electrical transport option and thermal transport options. To keep consistent, the electrical resistivity was measured along [110] direction for all the single crystals, while the magnetic field was applied along [\(1\bar 11\)] direction during the Hall resistivity measurement. Hall carrier concentration nH was calculated using the equation nH = 1/(eRH), where e is the unit charge and RH is the Hall coefficient. The carrier mobility μH was calculated using μH = RH/ρ. The Lorenz number is calculated by the single parabolic band model12.
Neutron powder diffraction
Approximately 3 grams samples were ground into powder in agate mortar and used for NPD measurements. The measurements were taken on the Super High Resolution Powder Diffractometer, BL08 SuperHRPD, at the Material and Life Science Experimental Facility (MLF) of Japan Proton Accelerator Research Complex (J-PARC) and on the General Purpose Powder Diffractometer, GPPD, at the China Spallation Neutron Source. Vanadium sample can were used in the measurements. The NPD patterns were collected over the temperature range of ~10 K to ~300 K. Rietveld refinement were performed using the Z-Rietveld software.
Inelastic neutron scattering
The inelastic neutron scattering measurements were performed using the High Resolution Chopper Spectrometer, BL12 HRC, at MFL of J-PARC. Approximately 13 grams of powder samples were wrapped in aluminum foil and then sealed in thin-walled cylindrical Al can, filled with low-pressure helium gas. The incident neutron energies, Ei = 66 meV, was used with an energy resolution (full width at half maximum) of ΔE/Ei ~5%. The measurements were performed at 10 K, 100 K, 200 K, and 300 K with a closed-cycle He refrigerator. Correspondingly, the empty Al can was also measured in identical conditions at all temperatures. All of the spectra were normalized with respect to the total incident flux. The time-of-flight data were reduced with the HANA (a program for data reduction collected on HRC). Then, the obtained powder-averaged dynamical structure factor S (Q, E) were analyzed in the incoherent-scattering approximation after substracting background, multiphonon and multiple scattering as well as the elastic peak using the DAVE61 and GetDOS programs62. Integration of the S (Q, E) spectra over the range of momentum transfers 0.4 ≤ Q ≤ 6.0 Å−1 leads to neutron-weighted phonon DOSs for the samples.
First-principles calculations
The ab initio calculations were performed by using the projector augmented wave (PAW) method, as implemented in the Vienna ab initio simulation package (VASP)63,64. The generalized gradient approximation (GGA) was used for the exchange–correlation functional65, and a plane-wave energy cutoff of 450 eV was adopted. The phonon DOS and dispersions of ZrNiSn and Sb-doped ZrNiSn were calculated by using the frozen phonon method, as implemented in the Phonopy package66. The phonon group velocities, the scattering rates, and lattice thermal conductivities were obtained via the shengBTE package, in which we considered the interactions between atoms to their fourth nearest neighbors67. A 4 × 4 × 4 supercell (192 atoms) was used in both procedures. For the structural optimization of the unit cell, the k-points was chosen as 8 × 8 × 8, and the convergence accuracy of force was 10−5 eV/Å. For the supercells with displacements, only Γ point was considered. The energy convergence criterion was 10−7 eV throughout the work.
Physical model of LO–TO splitting and screening effect
The frequency (energy) difference between LO and TO arises from the long-range electric field generated by ionic polarization with the LO phonon vibration. Following the physical model proposed by Born and Huang51, the relation between LO and TO is described as68:
where ωLO and ωTO are the frequencies of LO and TO, eq is the unit vector along the momentum direction of q, \({\mathbf{e}}_{{\mathrm{LO}}}^a\) is the \(|{\mathbf{q}}| \to 0\) limit of the eigenvector of the dynamical matrix of the LO mode, Ma is the mass of atom a in unit cell, \({\cal{Z}}_a\) is the Born effective charge of atom a, which reflect the change in polarization in response to the atom displacement, and \(\Psi \left( {\mathbf{q}} \right)\) is the Coulomb interaction in Fourier space, defined as:
where ε∞ is the high-frequency (optical) dielectric function. In the limit of \(|{\mathbf{q}}| \to 0\), the Eq. (1) could be simply replaced by the Lyddane-Sachs-Teller relationship: \(\omega _{{\mathrm{LO}}}^2/\omega _{{\mathrm{TO}}}^2 = \varepsilon _{\mathrm{s}}/\varepsilon _\infty\), εs is the static dielectric function69.
Presence of free carriers and the concomitant screening effect can modify both the electron-LO phonon interaction and the dispersion characteristics of the LO optical phonons. Then, the Coulomb interaction in the momentum space is modified by a factor of \(|{\mathbf{q}}|^2r_{TF}^2/\left( {1 + |{\mathbf{q}}|^2r_{TF}^2} \right)\) according to the Thomas–Fermi approximation, and then the Eq. (3) can be rewritten as:
Where rTF is the Thomas–Fermi screening length (or Debye length), and is defined as:
Where kB is the Boltzmann constant. Higher n leads to smaller rTF, and smaller rTF means better screening effect. Enhanced screening effect leads to a smaller modified Coulomb interaction, and hence smaller LO–TO splitting as schematized in Fig. 4c.
It is necessary to point out that the screening model used here is in a static (Thomas–Fermi) approximation. It assumes that the scattering potential is static, or charge carriers are fast enough in response to movement of scattering potential, so that a screening scenario could form. This assumption is valid for static ionized impurity and grain boundary scatterings. However, it become more complex to deal with the polar optical phonon scattering. If the plasma (collective oscillation of free charges) frequency, \(\omega _{\mathrm{P}} = \sqrt {ne^2/\varepsilon _\infty m^ \ast }\), is smaller than the optical phonon frequency ωop, the charge carriers lag behind the lattice vibration, which produces an anti-screening effect, and enhances the LO–TO splitting and the polar optical phonon scattering58,70. Only when ωP > ω, can the charge carriers instantaneously respond to the lattice vibration, and then meets the prerequisite for the approximation of static screening58,70. In the case of ZrNiSn-based half-Heusler compounds, ωP is estimated as 64.28 THz when n = 1 × 1020 cm−3 (the high-frequency dielectric parameter was calculated as ε∞ = 22.07 and the calculated effective mass of electron m* = 2.8 ± 0.2 me are used here40). This value of ωP is much larger than frequency of the longitudinal optical phonon, ~7.25 THz (or ~30 meV), and the Thomas–Fermi screening model is valid in the analysis of the screening of polar optical phonon scattering here.
Data availability
The data that support the findings of this study are available from the corresponding authors on reasonable request.
References
Bell, L. E. Cooling, heating, generating power, and Recovering Waste Heat with Thermoelectric Systems. Science 321, 1457–1461 (2008).
Appel, O. & Gelbstein, Y. A comparison between the effects of Sb and Bi Doping on the thermoelectric properties of the Ti0.3Zr0.35Hf0.35NiSn half-Heusler alloy. J. Electron. Mater. 43, 1976–1982 (2013).
Guttmann, G. M., Dadon, D. & Gelbstein, Y. Electronic tuning of the transport properties of off-stoichiometric PbxSn1−xTe thermoelectric alloys by Bi2Te3 doping. J. Appl. Phys. 118, 065102 (2015).
Komisarchik, G., Fuks, D. & Gelbstein, Y. High thermoelectric potential of n-type Pb1−xTixTe alloys. J. Appl. Phys. 120, 055104 (2016).
Cohen, I., Kaller, M., Komisarchik, G., Fuks, D. & Gelbstein, Y. Enhancement of the thermoelectric properties of n-type PbTe by Na and Cl co-doping. J. Mater. Chem. C 3, 9559–9564 (2015).
Sadia, Y., Aminov, Z., Mogilyansky, D. & Gelbstein, Y. Texture anisotropy of higher manganese silicide following arc-melting and hot-pressing. Intermetallics 68, 71–77 (2016).
Tang, Y. et al. Convergence of multi-valley bands as the electronic origin of high thermoelectric performance in CoSb3 skutterudites. Nat. Mater. 14, 1223–1228 (2015).
Imasato, K. et al. Metallic n-type Mg3Sb2 single crystals demonstrate the absence of ionized impurity scattering and enhanced thermoelectric performance. Adv. Mater. 32, 1908218 (2020).
Nolas G. S., Sharp J., Goldsmid J. Thermoelectrics: Basic Principles And New Materials Developments (Springer Science & Business Media, 2013).
Rowe D. M. CRC handbook of Thermoelectrics (CRC press, 1995).
Snyder, G. J. & Toberer, E. S. Complex thermoelectric materials. Nat. Mater. 7, 105–114 (2008).
Xie, H. et al. Beneficial contribution of alloy disorder to electron and phonon transport in half-Heusler thermoelectric materials. Adv. Funct. Mater. 23, 5123–5130 (2013).
Wang, S. et al. On intensifying carrier impurity scattering to enhance thermoelectric performance in Cr-Doped CeyCo4Sb12. Adv. Funct. Mater. 25, 6660–6670 (2015).
Fischetti M. V., Vandenberghe W. G. Advanced Physics Of Electron Transport In Semiconductors And Nanostructures. (Springer, 2016).
Wang, H., Pei, Y., LaLonde, A. D. & Snyder, G. J. Weak electron–phonon coupling contributing to high thermoelectric performance in n-type PbSe. Proc. Natl Acad. Sci. USA 109, 9705 (2012).
Delaire, O. et al. Giant anharmonic phonon scattering in PbTe. Nat. Mater. 10, 614–619 (2011).
Shiga, T. et al. Microscopic mechanism of low thermal conductivity in lead telluride. Phys. Rev. B 85, 155203 (2012).
Li, C. W. et al. Phonon self-energy and origin of anomalous neutron scattering spectra in SnTe and PbTe thermoelectrics. Phys. Rev. Lett. 112, 175501 (2014).
Christensen, M. et al. Avoided crossing of rattler modes in thermoelectric materials. Nat. Mater. 7, 811–815 (2008).
Lan, Y., Minnich, A. J., Chen, G. & Ren, Z. Enhancement of thermoelectric figure-of-merit by a bulk nanostructuring approach. Adv. Funct. Mater. 20, 357–376 (2010).
Ma, J. et al. Glass-like phonon scattering from a spontaneous nanostructure in AgSbTe2. Nat. Nanotechnol. 8, 445 (2013).
Ma, J. et al. Phonon scattering rates and atomic ordering in Ag1−xSb1+xTe2+x (x=0,0.1,0.2) investigated with inelastic neutron scattering and synchrotron diffraction. Phys. Rev. B 90, 134303 (2014).
Li, B. et al. Liquid-like thermal conduction in intercalated layered crystalline solids. Nat. Mater. 17, 226–230 (2018).
Peter Y., Cardona M. Fundamentals Of Semiconductors: Physics And Materials Properties (Springer Science & Business Media, 2010).
LaBotz, R. J. & Mason, D. R. The thermal conductivities of Mg2Si and Mg2Ge. J. Electrochem. Soc. 110, 121–126 (1963).
Klemens, P. G. Thermal resistance due to point defects at high temperatures. Phys. Rev. 119, 507–509 (1960).
Kōmoto K., Mori T. Thermoelectric Nanomaterials: Materials Design and Applications. (Springer, 2013).
Wang, H., Schechtel, E., Pei, Y. & Snyder, G. J. High thermoelectric efficiency of n-type PbS. Adv. Energy Mater. 3, 488–495 (2013).
Zawadzki, W. Electron transport phenomena in small-gap semiconductors. Adv. Phys. 23, 435–522 (1974).
Caillat, T., Borshchevsky, A. & Fleurial, J. P. Properties of single crystalline semiconducting CoSb3. J. Appl. Phys. 80, 4442–4449 (1996).
Levinshtein M., Rumyantsev S., Shur M. Handbook Series on Semiconductor Parameters (Word Scientific, 1996).
Sun, H. L., Yang, C. L., Wang, M. S. & Ma, X. G. Remarkably high thermoelectric efficiencies of the half-Heusler compounds BXGa (X = Be, Mg, and Ca). ACS Appl. Mater. Interfaces 12, 5838–5846 (2020).
Fu, C. et al. Realizing high figure of merit in heavy-band p-type half-Heusler thermoelectric materials. Nat. Commun. 6, 8144 (2015).
Xing, Y. et al. High-efficiency half-Heusler thermoelectric modules enabled by self-propagating synthesis and topologic structure optimization. Energy Environ. Sci. 12, 3390–3399 (2019).
Aliev, F. G. Gap at Fermi level in some new d- and f-electron intermetallic compounds. Phys. B 171, 199–205 (1991).
Aliev, F. G., Kozyrkov, V. V., Moshchalkov, V. V., Scolozdra, R. V. & Durczewski, K. Narrow band in the intermetallic compounds MNiSn (M=Ti, Zr, Hf). Z. Phys. B Condens. Matter 80, 353–357 (1990).
Uher, C., Yang, J., Hu, S., Morelli, D. T. & Meisner, G. P. Transport properties of pure and doped MNiSn (M=Zr, Hf). Phys. Rev. B 59, 8615–8621 (1999).
Joshi, G. et al. Enhancement in thermoelectric figure-of-merit of an N-type half-Heusler compound by the nanocomposite approach. Adv. Energy Mater. 1, 643–647 (2011).
Yu, J. et al. Unique role of refractory Ta alloying in enhancing the figure of merit of NbFeSb thermoelectric materials. Adv. Energy Mater. 8, 1701313 (2018).
Xie, H. et al. The intrinsic disorder related alloy scattering in ZrNiSn half-Heusler thermoelectric materials. Sci. Rep. 4, 6888 (2014).
Fu, C., Zhu, T., Liu, Y., Xie, H. & Zhao, X. Band engineering of high performance p-type FeNbSb based half-Heusler thermoelectric materials for figure of merit zT > 1. Energy Environ. Sci. 8, 216–220 (2015).
Qiu, Q. et al. Grain boundary scattering of charge transport in n-type (Hf,Zr)CoSb half-Heusler thermoelectric Materials. Adv. Energy Mater. 9, 1803447 (2019).
Sekimoto, T., Kurosaki, K., Muta, H. & Yamanaka, S. High-thermoelectric figure of merit realized in p-type half-Heusler compounds: ZrCoSnxSb1-x. Jpn J. Appl. Phys. 46, L673–L675 (2007).
Shuai, J. et al. Tuning the carrier scattering mechanism to effectively improve the thermoelectric properties. Energy Environ. Sci. 10, 799–807 (2017).
Kuo, J. J. et al. Grain boundary dominated charge transport in Mg3Sb2-based compounds. Energy Environ. Sci. 11, 429–434 (2018).
Fu, C. et al. Revealing the intrinsic electronic structure of 3D half‐Heusler thermoelectric materials by angle‐resolved photoemission spectroscopy. Adv. Sci. 7, 1902409 (2020).
Chen, S. et al. Thermal conductivity of isotopically modified graphene. Nat. Mater. 11, 203–207 (2012).
Lindsay, L., Broido, D. A. & Reinecke, T. L. Phonon-isotope scattering and thermal conductivity in materials with a large isotope effect: A first-principles study. Phys. Rev. B 88, 144306 (2013).
Fu, C. et al. Enhancing the figure of merit of heavy-band thermoelectric materials through hierarchical phonon scattering. Adv. Sci. 3, 1600035 (2016).
Zhou, J. et al. Large thermoelectric power factor from crystal symmetry-protected non-bonding orbital in half-Heuslers. Nat. Commun. 9, 1721 (2018).
Born M., Huang K. Dynamical Theory Of Crystal Lattices. (Clarendon press, 1954).
Ahn, D. Theory of polar‐optical‐phonon scattering in a semiconductor quantum wire. J. Appl. Phys. 69, 3596–3600 (1991).
Kandpal, H. C., Felser, C. & Seshadri, R. Covalent bonding and the nature of band gaps in some half-Heusler compounds. J. Phys. D Appl. Phys. 39, 776–785 (2006).
Feng, Z., Fu, Y., Zhang, Y. & Singh, D. J. Characterization of rattling in relation to thermal conductivity: ordered half-Heusler semiconductors. Phys. Rev. B 101, 064301 (2020).
Kohn, W. Image of the Fermi Surface in the vibration spectrum of a metal. Phys. Rev. Lett. 2, 393–394 (1959).
Singh J. Electronic And Optoelectronic Properties Of Semiconductor Structures (Cambridge University Press, 2007).
Zeier, W. G. et al. Engineering half-Heusler thermoelectric materials using Zintl chemistry. Nat. Rev. Mater. 1, 16032 (2016).
Ridley B. K. Quantum Processes In Semiconductors (Oxford University Press, 2013).
Wang, Y. et al. Doubling the ZT record of TiS2-based thermoelectrics by incorporation of ionized impurity scattering. J. Mater. Chem. C 6, 9345–9353 (2018).
He, R. et al. Achieving high power factor and output power density in p-type half-Heuslers Nb1-xTixFeSb. Proc. Natl Acad. Sci. USA 113, 13576–13581 (2016).
Azuah, R. T. et al. DAVE: a comprehensive software suite for the reduction, visualization, and analysis of low energy neutron spectroscopic data. J. Res. Natl Inst. Stand. Technol. 114, 341–358 (2009).
Lin, Y., Islam, F. & Kresh, M. Multiphonon: phonon density of states tools for inelastic neutron scattering powder data. J. Open Source Softw. 3, 440 (2018).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Togo, A. & Tanaka, I. First principles phonon calculations in materials science. Scr. Mater. 108, 1–5 (2015).
Li, W., Carrete, J. A., Katcho, N. & Mingo, N. ShengBTE: a solver of the Boltzmann transport equation for phonons. Comput. Phys. Commun. 185, 1747–1758 (2014).
Sohier, T., Gibertini, M., Calandra, M., Mauri, F. & Marzari, N. Breakdown of optical phonons’ splitting in two-dimensional materials. Nano Lett. 17, 3758–3763 (2017).
Lyddane, R. H., Sachs, R. G. & Teller, E. On the polar vibrations of alkali halides. Phys. Rev. 59, 673–676 (1941).
Ehrenreich, H. Screening effects in polar semiconductors. J. Phys. Chem. Solids 8, 130–135 (1959).
Acknowledgements
J.M. thanks the financial support from the National Science Foundation of China (No. 11774223 and No. U1732154) and a Shanghai talent program. C.G.F. thanks the financial support from the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation) – Projektnummer (No. 392228380) and the Alexander von Humboldt Foundation. J.Y. acknowledges the financial support from Natural Science Foundation of China (No. 11674211 and No. 51761135127), and the 111 project D16002. T.J.Z. thanks the financial support from the National Science Foundation of China (No. 51761135127) and the National Science Fund for Distinguished Young Scholars (No. 51725102). Q.R. thanks Dr. Jiao Lin from the Oak Ridge National Lab for the help on the phonon DOSs analysis using the GetDOS programs, and Dr. Xiaokun Gu for the discussion about LO–TO splitting. The inelastic neutron scattering data using HRC were supported with the general proposal (Proposal No. 2017A0071 and 2018B0281) of J-PARC/MLF. Some of the neutron diffraction data using SuperHRPD were taken under both the general proposal (Proposal No. 2017A0118) and the fast track proposal (Proposal No. 2017BF0804) of J-PARC/MLF, while some data using GPPD were taken under the proposal (Proposal No. P2018091800008) of CSNS.
Author information
Authors and Affiliations
Contributions
Q.R., Z.L., T.M., S.A., and J.M. designed and performed the INS experiment using HRC at the J-PARC. Q.R., M.H., S.L., S.T., T.K., and J.M. designed and performed the high-resolution neutron diffraction experiment using superHRPD at the J-PARC. Q.R., L.H., X.T., and J. M. designed and performed the neutron diffraction experiment using GPPD at the CSNS. C.G.F. and Q.Q. synthesized the samples. C.G.F. and C.F. performed the transport properties measurement. Q.R. analyzed the experiment data, along with all co-authors. J.Y. and S.D. performed the First-principles calculations. Q.R., J.Y., D.J.S., and J.M. interpreted the LO–TO splitting phenomenon. Q.R., C.G.F., T.Z., J.Y. and J.M. convinced the project and drafted the manuscript. All authors analyzed and reviewed the results, and provided input to this paper.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Tongmin Wang and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ren, Q., Fu, C., Qiu, Q. et al. Establishing the carrier scattering phase diagram for ZrNiSn-based half-Heusler thermoelectric materials. Nat Commun 11, 3142 (2020). https://doi.org/10.1038/s41467-020-16913-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-020-16913-2
- Springer Nature Limited
This article is cited by
-
Vacancies tailoring lattice anharmonicity of Zintl-type thermoelectrics
Nature Communications (2024)
-
Substantial enhancement in thermoelectric figure-of-merit of half-Heusler ZrNiPb alloys
Bulletin of Materials Science (2024)
-
Phonon slowdown
Nature Physics (2023)
-
Semiclassical electron and phonon transport from first principles: application to layered thermoelectrics
Journal of Computational Electronics (2023)
-
Structure and thermoelectric property evolution of TiFe1.1−xNixSb with the filling of Ni
Science China Materials (2023)