Abstract
Phonon engineering of solids enables the creation of materials with tailored heat-transfer properties, controlled elastic and acoustic vibration propagation, and custom phonon–electron and phonon–photon interactions. These can be leveraged for energy transport, harvesting, or isolation applications and in the creation of novel phonon-based devices, including photoacoustic systems and phonon-communication networks. Here we introduce nanocrystal superlattices as a platform for phonon engineering. Using a combination of inelastic neutron scattering and modeling, we characterize superlattice-phonons in assemblies of colloidal nanocrystals and demonstrate that they can be systematically engineered by tailoring the constituent nanocrystals, their surfaces, and the topology of superlattice. This highlights that phonon engineering can be effectively carried out within nanocrystal-based devices to enhance functionality, and that solution processed nanocrystal assemblies hold promise not only as engineered electronic and optical materials, but also as functional metamaterials with phonon energy and length scales that are unreachable by traditional architectures.
Similar content being viewed by others
Introduction
Colloidal semiconducting or metallic nanocrystals (NCs) can be assembled from solution into densely packed 2D or 3D superlattices (Fig. 1)1,2,3,4,5. A key feature of these NC superlattices is their tunability6. The NC building blocks of the superlattice can be synthesized with precise control over composition, size, shape, and surface-terminating ligands7,8. This tunability has been used to engineer the electronic and optical structure of NCs, and is recognized as key for a wide array of applications, including LEDs, solar cells and photo-detectors, transistors, phase-change memory, and thermoelectric devices9,10,11,12,13. Furthermore, the inter-NC spacing and packing of the NCs into these superlattices can be tuned by the size and shape of the NCs and choice of ligand1,14, with structures ranging from primary crystal structures (e.g., cubic3,15, BCC14, FCC16, and hexagonal2) to complex binary systems (e.g., NaCl, MgZn2…)5,17. This multi-parameter tunability can potentially be exploited to control the collective vibrational structure of the NC superlattice, which would enable the design of new materials via phonon engineering.
The vibrational structure of NC superlattices is complex. The types of vibrations and phonons expected in NC-superlattices are shown in Fig. 1. A superlattice containing NNC NCs, each containing NA atoms in its core and ligand shell, has 3NNC NA-6 degrees of atomic freedom. NNC(3NA-6) of these are the vibrations of the atoms making up the ligand and the NCs. A majority of the vibrational modes of organic ligand species, glig(ω) occur at high energies (i.e., ~100 meV and above). Vibrations of the atomic lattice of the NC cores, gNC(ω), including the bulk-like phonons of the NC core and the localized vibrations of the surface atoms18,19, occur at intermediate energies (~1–100 meV). The remaining 6NNC – 6 atomic degrees of freedom contribute to excitations of the NC superlattice, related to displacements (3NNC – 6) and hindered rotations (3NNC) of the NCs about their equilibrium positions. The 3NNC – 6 vibrational modes of the NC superlattice (i.e., superlattice phonons, with density gSL(ω)) can be long range and coherent, as evidenced previously by the observation of acoustic standing wave excitations in NC superlattice thin films20.
Here, using the well-studied system of lead sulfide (PbS) NCs linked with dithiol ligands, we model and directly measure gSL(ω) for 3D NC-superlattices. We show that gSL(ω) can be systematically tuned through selection of the NC size and choice of ligand. This demonstrates that NC-superlattices are not only promising designer electronic and optical materials, but also solution-processable, phonon-engineerable solids. In particular, we highlight that the design of long-range phonons in NC superlattices can be used to achieve materials with novel low temperature properties, and that the vibrational structure in NC superlattices enables them to be used as functional 2D and 3D acoustic metamaterials spanning energy and length scales not achievable using standard methods.
Results
Modeling superlattice phonons
To gain an understanding of the expected phononic structure and energy scale for a NC superlattice, we model it as a three-dimensional mass-spring system, where the NCs are the masses, m, and the surface terminating ligands are the springs providing a force constant, k, between neighboring NCs.
In a mass-spring model, the energy of the phonon modes will scale with \(\sqrt {k/m} = \sqrt {n\left( r \right)k_{{\mathrm{lig}}}/m}\), where n(r) is the number of ligands providing an interaction between neighboring nanocrystals of radius r, and klig is the effective spring constant of a single ligand. In the case of dithiol ligands, we assume that longitudinal stretch/compression of the dithiol carbon backbone will dominate the overall mechanical interactions between neighboring NCs, and ignore the impact of shearing/flexing of the ligands. We determine kLig using density functional theory (DFT) to compute the total energy E(x) of the ligand as a function of its compression or extension, x, with \(E\left( x \right) - E\left( 0 \right) = 1/2\;k_{{\mathrm{lig}}}x^2\). As an example, in Fig. 2a we show the calculated E(x) for hexane-dithiol (HDT) (blue dots) and the fit (black line), which highlights that the carbon-backbone of the dithiol ligands exhibit a harmonic response. We compute klig for four dithiol ligands of varying carbon-backbone lengths, ethanedithiol (EDT, NC = 2), butanedithiol (BDT, NC = 4), hexanedithiol (HDT, NC = 6), and dodecanedithiol (DDT, NC = 12), and we find a decreasing klig with increasing carbon backbone length (Fig. 2b). n(r) will depend on the structure of the NC superlattice, but will scale with rα, with 2 ≥ α ≥ 1, the upper and lower bounds corresponding to superlattice structures where neighboring NCs are face-sharing or edge sharing respectively.
Small angle x-ray scattering studies of PbS NC thin films have demonstrated their assembly into FCC, BCC, and related structures14,21,22, depending on the NC size and ligand, with facet to facet separations in the superlattice corresponding to the nominal length of the ligands employed. The resulting superlattice lattice constants are therefore \(a_{{\mathrm{SL}}} \approx 2r_{{\mathrm{NC}}} + \ell _{{\mathrm{lig}}}\), where rNC and \(\ell _{{\mathrm{lig}}}\) are the NC radius and nominal ligand length respectively. For the thiol ligands studied here, \(\ell _{{\mathrm{EDT}}}\) = 0.45 nm, \(\ell _{{\mathrm{BDT}}}\) = 0.69 nm, \(\ell _{{\mathrm{HDT}}}\) = 0.94 nm, \(\ell _{{\mathrm{DDT}}}\) = 1.7 nm. For PbS NC superlattices with thiol ligands a FCC structure is expected for smaller NCs (<3 nm radius) (Fig. 2c)16.
The analytical form for the phonon density of states for an FCC lattice is shown in Fig. 2d. However, a real NC superlattice will have some disorder that will depend on the quality of the NC synthesis and the methods and conditions used to assemble the NCs into the superlattice1,3. We can numerically compute gSL(ω) for disordered superlattices by constructing the dynamical matrix, D, for the mass-spring model and diagonalizing it, \({\mathbf{D}}{\mathbf{\varphi}} = - \omega ^2{\mathbf{\varphi }}\), where ω is the frequency of the normal mode φ. We take the masses mi from a normal distribution with standard deviation σm and assume a uniform distribution of spring constants kij, for the springs connecting mass i and j, with width β. With increasing disorder, the sharp transverse-acoustic (TA) and longitudinal-acoustic (LA) peaks of gSL(ω) broaden and eventually merge into a single broad, low energy peak (analogous to the Boson Peak of disordered atomic/molecular lattices)23,24, at high amounts of disorder. For solution processed PbS superlattices, which will be inherently disordered, we can expect a gSL(ω) between the two extremes in Fig. 2d.
Our modeling provides easy insight into how gSL(ω) of NC-superlattices can be tailored by changing the mass of the NCs (e.g., by changing their size or composition) and/or the effective spring constants (e.g., though the packing geometry or the type of ligand). For FCC PbS NC superlattices fabricated with typical NC sizes (r = 1.5–4 nm) and thiol ligands, we can expect TA/LA Van Hove singularities (peaks in the gSL(ω)) at energies \(\hbar \omega _{{\mathrm{TA}}}\sim 1.2\hbar \sqrt {k/m}\), \(\hbar \omega _{{\mathrm{LA}}}\sim 2\hbar \sqrt {k/m}\), within a range of ~0.4–2 meV (Supplementary Note 1).
Measuring superlattice phonons
To measure these superlattice vibrations, we turn to inelastic neutron scattering (INS)25. Both inelastic x-ray scattering (IXS)19 and INS have been employed to measure the vibrational density of states stemming from atomic vibrations within the NCs (gNC(ω)). While IXS has the advantage that measurements can be performed on thin films (i.e., tens of nanometers), it does not have sufficient energy resolution to probe gSL(ω). We therefore turn to INS, performed at the time-of-flight spectrometer FOCUS at SINQ, and use an incident neutron energy of 3.27 eV (wavelength of 5.0 Å) to obtain an energy resolution of ~82 μeV (FWHM) at 0 meV energy transfer. Samples consist of ~8–10 g of PbS NCs synthesized using an upscaled approach26 and condensed into a powder of NC superlattice crystallites with a solution-based ligand exchange (Supplementary Note 2)25. While the large sample sizes required for INS prevents us from employing state-of-the-art superlattice formation procedures1,2,3,4, our calculations indicate that superlattice phonons will still be observed in a disordered system (Fig. 2d). Extraction of gSL(ω) from INS is non-trivial due to the overlap with quasi-elastic scattering centered at 0 energy transfer, which results from reorientational motion of the surface terminating ligands27. We therefore develop a fully automated analysis procedure to extract gSL(ω) from INS and apply it identically to all measurements on all samples (Supplementary Note 3).
In Fig. 3a, we plot the extracted NC superlattice phonon density of states, gSL(ω), for a series of NC-superlattices fabricated with increasing NC radii of r = 1.6, 1.9, 2.5, and 3.3 nm, all with HDT ligands. The extracted gSL(ω) for all samples consists of a broad double peaked distribution, characteristic of the phonon density of states of a disordered FCC superlattice, and at an energy range consistent with our modeling above. The position of the first peak (TA) of the distribution shows the expected energy scaling with NC radius of ћω ∝ r−1 (Fig. 3b). In Fig. 3c, we plot the gSL(ω) for a series of four samples with 1.6 nm radii NCs fabricated with different ligands. As expected, the energetic scale of gSL(ω) increases with a decrease in the carbon backbone length of the dithiol ligand. While the scaling for the BDT, HDT, and DDT follows the trend klig1/2 (Fig. 3d), the characteristic energy of the EDT sample is lower than expected from the mass-spring model. As we discuss in Supplementary Note 1, this likely stems from interactions between the superlattice phonons and the lattice vibrations of the NC cores, reducing the energies of the superlattice phonons.
These experimental results validate that phonons of NC-superlattices can be modeled as mass-spring systems and systematically engineered. Due to their solution processability as thin films or packed powder samples, they offer phonon engineering from the sub-micron to centimeter length scales and at energies in the 0–2 meV range, opening up new form factors, energy bandwidths, and use cases for meta-materials.
Low-Temperature properties of superlattice phonons
Due to the low energy (ћω/kB ~10–20 K) and low number density (~103–104 fewer than the atomistic vibrations of the NC and the ligands), the impact of superlattice phonons on material properties will be particularly evident at ultra-low temperatures where the thermal occupation of ligands and NC core vibrations is negligible28,29. Interestingly, even though the superlattice phonons energies are low, their corresponding group velocities are similar to those in bulk PbS due to the several-nm length scale lattice constant of the NC-superlattice a (e.g., for 1.6 nm NCs with BDT vg,LA ∝ ωa/π ~1.5 meV 3.9 nm/ћπ ~3 103 m/s, whereas for bulk, vg,LA ∝ ~10.5 meV 0.6 nm/ћπ ~3 103 m/s). Therefore, below 4 K, properties such as the lattice heat capacity and thermal conductivity of the NC superlattice can match or even slightly exceed that of the bulk. This is emphasized in Fig. 4a, which shows the lattice thermal conductivity, κlat, from the longitudinal acoustic (LA) phonon mode normalized by the phonon mean free path:
Since carrier mobility in NC superlattice is temperature activated30, NC-superlattices will be robust insulators at low-temperature. Figure 4a shows that, at low temperatures, the thermal conductivity of the PbS NC superlattice could be two orders of magnitude larger than the well-known, electrically insulating thermal conductors, diamond and aluminum-nitride. This assumes of course highly ordered superlattices with large mean free paths, but large mean free paths in these materials should be in general be facilitated by the large a.
A prerequisite to the NC superlattice being used as a phonon engineered material at low temperatures is of course reliant on the phononic structure being maintained at these temperatures. We therefore measure the gSL(ω) of the r = 1.6 nm NCs and HDT ligand sample between 25 and 300 K (Fig. 4b). The extracted gSL(ω) is similar for all temperatures with a sharpening and slight blueshift of the features with decreasing temperature, which is consistent with increased ordering (leading to lower disorder in k) and a densification of NC-solid at low temperature (leading to an increase in k)16. We propose that this ordering and densification comes from suppression of the reorientational motion of the ligands at low temperatures. To test this hypothesis, we perform fixed-window scans on the PbS-HDT sample at the neutron backscattering spectrometer MARS at SINQ, which provides a high energy resolution (~13 μeV) and enables the rapid acquisition of the temperature evolution of the reorientational motion of the ligands27. The QENS intensity is constant below ~175 K (Fig. 4c), and then starts to rapidly increase, indicating an increased flexibility of the ligands. These findings highlight that NC superlattices maintain their phononic structure across a broad temperature range, and that cooling to cryogenic temperatures can reduce the extent of disorder in the NC superlattice and inter-NC interactions. These results suggest that NC superlattices will be highly effective electronically insulating, thermal conductors at ultra-low temperatures, which could make them of interest, for example, as a thermal dissipation coating in cryo-CMOS devices.
Discussion
In summary, this demonstration of phonon engineering in NC superlattices indicate that they are poised to become not only designer electronic and optical materials2,3, but also phononic solids, where the phonon density of states (gSL(ω), gNC(ω), and glig(ω)) can be engineered through the choice of ligand and the composition, size, shape, and surface of the NCs18,31.
While here we have focused on acoustic phonons of simple monatomic superlattices, this platform can be extended towards the creation of complex phononic structures traditionally targeted by the meta-materials community32,33,34. Phonon engineering has been predominately demonstrated with acoustic metamaterials35,36,37,38,39 on a macroscopic scale40,41. The design of specialized organic42 and inorganic43 ligands can enable more complex inter-NC mechanical interactions, beyond the stretch/compressive forces provided by the thiol ligands investigated here. Including the full range of elastic interactions, such as sheer and torsional forces, would unleash the power of complex phonon design algorithms44. Furthermore, by controlling the shape, and therefore exposed surfaces of the NCs, the functional group of the ligands can be tailored to link between specific NC facets7,8,45, enabling the definition of specific directional interactions in the superlattice. Although assembly techniques for NC-superlattices must continue to be developed so that they can compete with macroscopic metamaterials in terms of complexity, NC-superlattices enable phonon engineering at length and energy scales not easily achievable with existing platforms.
Moreover, the ability to independently tune phononic and electronic properties in NC-superlattices is particularly promising. Phonon engineering at the atomistic level is typically limited by the fact that electronic and phononic properties are intrinsically linked. In the case of NC superlattices, electronic properties (like phononic properties) are tunable by the choice of NC size46,47, shape48, chemical composition49,50, and ligand51. However, electronic coupling between neighboring NCs and the reorganizational energy associated charge transfer govern electronic properties, while the mechanical properties of the ligand and the mass of the nanocrystal dominate the long range superlattice vibrations. Thus, electronic properties could be changed while phononic properties remain the same by, for example, placing a shell around the NC cores that changes the NC bandgap and electronic coupling between neighboring nanocrystals but keeps the NC masses the same. Alternatively, switching the ligand (e.g., from ethanedithiol to benzenedithol) could change the effective spring constant of the system while keeping the electronic properties the same (i.e., inter-NC spacing and electronic coupling would be similar). Furthermore, the ability to tune the spatial confinement of the charge carriers (e.g., with multilayer shells, alloys, and electronegativity of ligands), to select optical band gap (e.g., with NC size), and to introduce phononic bandgaps (e.g., with complex superlattice structures using NCs of different masses), provides opportunities to selectively tune electron-phonon, phonon–photon, and phonon–phonon interactions in NC superlattices.
The ease of their solution fabrication, the new length scales and energies achievable with NC superlattices, and their unique low temperature properties will hopefully stimulate new dialog about the opportunities for these systems as phononic materials and devices.
Methods
Density functional theory calculations of thiol spring constants
Geometry optimization, electronic structure calculations, and ab initio molecular dynamics (AIMD) were performed within the CP2K program suite utilizing the quickstep module52. Calculations are carried out using a dual basis of localized Gaussians and plane-waves53, with a 300 Ry plane-wave cutoff. Double-Zeta-Valence-Polarization (DZVP)54, Goedecker–Teter–Hutter pseudopotentials55 for core electrons, and the Perdew–Burke–Ernzerhof (PBE) exchange correlation functional are used for all calculations. Convergence to 10–8 in Self-Consistent Field calculations is always enforced.
The equilibrium geometry (stretch x = 0) of the thiols are first determined through a full relaxation of the molecules. For each stretch amount, x, the molecules are uniformly stretched such that the sulfur-sulfur distance is stretched by x, the geometry of the molecule is then fully relaxed with only the position of the two sulfurs fixed. The resulting energies of the minimized geometries are then taken as E(x).
Calculating g SL(ω)
We construct the dynamical matrix as described in the main text, and diagonalize it to obtain gSL(ω). With disorder, we average gSL(ω) over 100 stochastic realizations of the dynamical matrix. Calculations are performed on lattices with dimensions of 16 × 16 × 16 conventional BCC/FCC unit cells with periodic boundary conditions.
Sample preparation
PbS NC solutions were synthesized using an upscaled synthesis approach26. For the 1.6 nm NCs, 2 separate syntheses were mixed into a single solution for preparation of the ligand series. PbS NC-solid powders were prepared identically to our previous INS experiments25, using a fixed molar concentration of 8 mM for all four dithiol ligands.
INS/QENS measurements
Each measured sample consisted of ~8 g of PbS powder, prepared as described above. The powder is held in a cylinder (d = 12 mm, h = 40–50 mm) made of 3 layers of aluminum foil. Data reduction for both INS and QENS measurements were performed using the DAVE software package56.
INS was performed at the cold-neutron time-of-flight spectrometer (FOCUS) at Swiss Spallation Neutron Source SINQ. For INS, a Vanadium standard with dimensions 5.0 cm × 1.5 cm × 0.2 mm thick was used to measure the incident neutron energy and for detector efficiency calibration, and determination of the instrument resolution. For INS spectra all samples were measured for ~8 h. Measurement of the empty sample holder subtracted as background.
QENS experiments were performed at the indirect time-of-flight backscattering spectrometer MARS at SINQ. Scattered neutrons with energy of 1.85 meV (6.65 Å) were filtered with the (006) reflection of the mica analyzers in near-backscattering configuration. The choice of the incident energy range defined the energy transfer window. For the QENS signal intensity, the scattering was summed between 0.02 and 0.05 meV, which represents well the quasielastic part of the spectrum. The temperature dependence of the background is negligible; therefore, it was not measured, nor subtracted from the data.
Data availability
All relevant data are available from the authors.
References
Dong, A., Chen, J., Vora, P. M., Kikkawa, J. M. & Murray, C. B. Binary nanocrystal superlattice membranes self-assembled at the liquid-air interface. Nature 466, 474–477 (2010).
Boneschanscher, M. P. et al. Long-range orientation and atomic attachment of nanocrystals in 2D honeycomb superlattices. Science 344, 1377–1380 (2014).
Rainò, G. et al. Superfluorescence from lead halide perovskite quantum dot superlattices. Nature 563, 671–675 (2018).
Montanarella, F. et al. Lasing supraparticles self-assembled from nanocrystals. ACS Nano 12, 12788–12794 (2018).
Talapin, D. V. et al. Quasicrystalline order in self-assembled binary nanoparticle superlattices. Nature 461, 964–967 (2009).
Talapin, D. V., Lee, J.-S., Kovalenko, M. V. & Shevchenko, E. V. Prospects of colloidal nanocrystals for electronic and optoelectronic applications. Chem. Rev. 110, 389–458 (2010).
Boles, M. A., Ling, D., Hyeon, T. & Talapin, D. V. The surface science of nanocrystals. Nat. Mater. 15, 141–153 (2016).
Owen, J. The coordination chemistry of nanocrystal surfaces. Science 347, 615–616 (2015).
Liu, M. et al. Hybrid organic–inorganic inks flatten the energy landscape in colloidal quantum dot solids. Nat. Mater. 16, 258–263 (2017).
Konstantatos, G. et al. Ultrasensitive solution-cast quantum dot photodetectors. Nature 442, 180–183 (2006).
Talapin, D. V. & Murray, C. B. PbSe nanocrystal solids for n- and p-channel thin film field-effect transistors. Science 310, 86–89 (2005).
Ortega, S. et al. Bottom-up engineering of thermoelectric nanomaterials and devices from solution-processed nanoparticle building blocks. Chem. Soc. Rev. 46, 3510–3528 (2017).
Ibáñez, M. et al. High-performance thermoelectric nanocomposites from nanocrystal building blocks. Nat. Commun. 7, 10766 (2016).
Weidman, M. C., Smilgies, D.-M. & Tisdale, W. A. Kinetics of the self-assembly of nanocrystal superlattices measured by real-time in situ X-ray scattering. Nat. Mater. 15, 1–8 (2016).
Wetterskog, E. et al. Tuning the structure and habit of iron oxide mesocrystals. Nanoscale 8, 15571–15580 (2016).
Gilmore, R. H. et al. Inverse temperature dependence of charge carrier hopping in quantum dot solids. ACS Nano 12, 7741–7749 (2018).
Shevchenko, E. V., Talapin, D. V., Kotov, N. A., O’Brien, S. & Murray, C. B. Structural diversity in binary nanoparticle superlattices. Nature 439, 55–59 (2006).
Yazdani, N. et al. Tuning electron–phonon interactions in nanocrystals through surface termination. Nano Lett. 18, 2233–2242 (2018).
Yazdani, N. et al. Measuring the vibrational density of states of nanocrystal-based thin films with inelastic X-ray scattering. J. Phys. Chem. Lett. 9, 1561–1567 (2018).
Poyser, C. L. et al. Coherent acoustic phonons in colloidal semiconductor nanocrystal superlattices. ACS Nano 10, 1163–1169 (2016).
Weidman, M. C., Yager, K. G. & Tisdale, W. A. Interparticle spacing and structural ordering in superlattice pbs nanocrystal solids undergoing ligand exchange. Chem. Mater. 27, 474–482 (2015).
Zaluzhnyy, I. A. et al. Quantifying angular correlations between the atomic lattice and the superlattice of nanocrystals assembled with directional linking. Nano Lett. 17, 3511–3517 (2017).
Taraskin, S. N., Loh, Y. L., Natarajan, G. & Elliott, S. R. Origin of the boson peak in systems with lattice disorder. Phys. Rev. Lett. 86, 1255–1258 (2001).
Shintani, H. & Tanaka, H. Universal link between the boson peak and transverse phonons in glass. Nat. Mater. 7, 870–877 (2008).
Bozyigit, D. et al. Soft surfaces of nanomaterials enable strong phonon interactions. Nature 531, 618–622 (2016).
Yarema, M. et al. Upscaling colloidal nanocrystal hot-injection syntheses via reactor underpressure. Chem. Mater. 29, 796–803 (2016).
Leguy, A. M. A. et al. The dynamics of methylammonium ions in hybrid organic–inorganic perovskite solar cells. Nat. Commun. 6, 7124 (2015).
Liu, M., Ma, Y. & Wang, R. Y. Modifying thermal transport in colloidal nanocrystal solids with surface chemistry. ACS Nano 9, 12079–12087 (2015).
Ong, W.-L., Rupich, S. M., Talapin, D. V., McGaughey, A. J. H. & Malen, J. A. Surface chemistry mediates thermal transport in three-dimensional nanocrystal arrays. Nat. Mater. 12, 410–415 (2013).
Bozyigit, D., Lin, W. M. M. M., Yazdani, N., Yarema, O. & Wood, V. A quantitative model for charge carrier transport, trapping and recombination in nanocrystal-based solar cells. Nat. Commun. 6, 6180 (2015).
Schnitzenbaumer, K. J. & Dukovic, G. Comparison of phonon damping behavior in quantum dots capped with organic and inorganic ligands. Nano Lett. 18, 3667–3674 (2018).
Liu, Z. Locally resonant sonic. Mater. Sci. 289, 1734–1736 (2000).
Bilal, O. R., Süsstrunk, R., Daraio, C. & Huber, S. D. Intrinsically polar elastic metamaterials. Adv. Mater. 29, 1700540 (2017).
Fruchart, M. et al. Soft self-assembly of Weyl materials for light and sound. Proc. Natl Acad. Sci. USA 115, 3655–3664 (2018).
Coulais, C., Teomy, E., de Reus, K., Shokef, Y. & van Hecke, M. Combinatorial design of textured mechanical metamaterials. Nature 535, 529–532 (2016).
Huber, S. D. Topological mechanics. Nat. Phys. 12, 621–623 (2016).
Ma, G. & Sheng, P. Acoustic metamaterials: From local resonances to broad horizons. Sci. Adv. 2, e1501595 (2016).
Bertoldi, K., Vitelli, V., Christensen, J. & van Hecke, M. Flexible mechanical metamaterials. Nat. Rev. Mater. 2, 17066 (2017).
Cummer, S. A., Christensen, J. & Alù, A. Controlling sound with acoustic metamaterials. Nat. Rev. Mater. 1, 16001 (2016).
Paulose, J., Chen, B. G. & Vitelli, V. Topological modes bound to dislocations in mechanical metamaterials. Nat. Phys. 11, 153–156 (2015).
Serra-Garcia, M. et al. Observation of a phononic quadrupole topological insulator. Nature 555, 342–345 (2018).
André, A. et al. Electron-conducting PbS nanocrystal superlattices with long-range order enabled by terthiophene molecular linkers. ACS Appl. Mater. Interfaces 10, 24708–24714 (2018).
Kovalenko, M. V., Scheele, M. & Talapin, D. V. Colloidal nanocrystals with molecular metal chalcogenide surface ligands. Science 324, 1417–1420 (2009).
Matlack, K. H., Serra-Garcia, M., Palermo, A., Huber, S. D. & Daraio, C. Designing perturbative metamaterials from discrete models. Nat. Mater. 17, 323–328 (2018).
Zherebetskyy, D. et al. Hydroxylation of the surface of PbS nanocrystals passivated with oleic acid. Science 344, 1380–1384 (2014).
Norris, D. J., Efros, A. L., Rosen, M. & Bawendi, M. G. Size dependence of exciton fine structure in CdSe quantum dots. Phys. Rev. B 53, 16347–16354 (1996).
Yazdani, N. A., Bozyigit, D., Yarema, O., Yarema, M. & Wood, V. Hole mobility in nanocrystal solids as a function of constituent nanocrystal size. J. Phys. Chem. Lett. 5, 3522–3527 (2014).
Murray, C. B., Kagan, C. R. & Bawendi, M. G. Synthesis and characterization of monodisperse nanocrystals and close-packed nanocrystal assemblies. Annu. Rev. Mater. Sci. 30, 545–610 (2000).
Yarema, O., Yarema, M., Lin, W. M. M. & Wood, V. Cu–In–Te and Ag–In–Te colloidal nanocrystals with tunable composition and size. Chem. Commun. 52, 10878–10881 (2016).
Protesescu, L. et al. Nanocrystals of cesium lead halide perovskites (CsPbX 3, X = Cl, Br, and I): novel optoelectronic materials showing bright emission with wide color gamut. Nano Lett. 15, 3692–3696 (2015).
Brown, P. R. et al. Energy level modification in lead sulfide quantum dot thin films through ligand exchange. ACS Nano 8, 5863–5872 (2014).
Vandevondele, J. et al. Quickstep: Fast and accurate density functional calculations using a mixed Gaussian and plane waves approach. Comput. Phys. Commun. 167, 103–128 (2005).
Lippert, G., Hutter, J. & Parrinello, M. A hybrid Gaussian and plane wave density functional scheme. Mol. Phys. 92, 477–488 (1997).
VandeVondele, J. & Hutter, J. Gaussian basis sets for accurate calculations on molecular systems in gas and condensed phases. J. Chem. Phys. 127, 114105 (2007).
Hartwigsen, C., Goedecker, S. & Hutter, J. Relativistic separable dual-space Gaussian pseudopotentials from H to Rn. Phys. Rev. B 58, 3641–3662 (1998).
Azuah, R. T. et al. DAVE: a comprehensive software suite for the reduction, visualization, and analysis of low energy neutron spectroscopic data. J. Res. Natl Inst. Stand. Technol. 114, 341–358 (2009).
Acknowledgements
We acknowledge support from the Swiss National Science Foundation through the Project #175889, the Quantum Sciences and Technology NCCR, and an ETH Research Grant #42-12-2. Computations were supported by a grant from the Swiss National Supercomputing Centre (CSCS; project ID s831). This work is based on experiments performed at the Swiss spallation neutron source SINQ, Paul Scherrer Institute, Villigen, Switzerland.
Author information
Authors and Affiliations
Contributions
N.Y., D. B. and V.W. devised the work, N.Y. performed the modeling, N.Y. and M.J. performed the calculations, M.Y. and O.Y. synthesized materials, N.Y., D.B., S.V. and W.M.M.L. prepared and characterized the INS/QENS samples, N.Y., D.B. and F.J. performed the neutron scattering experiments, N.Y. analyzed results, N.Y., V.W., S.H. and F.J. wrote the manuscript with input from all other authors.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Gabriel Bester, Raphaël Hermann and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Yazdani, N., Jansen, M., Bozyigit, D. et al. Nanocrystal superlattices as phonon-engineered solids and acoustic metamaterials. Nat Commun 10, 4236 (2019). https://doi.org/10.1038/s41467-019-12305-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-019-12305-3
- Springer Nature Limited
This article is cited by
-
Nanocrystal phononics
Nature Materials (2023)
-
Discovery of two-dimensional binary nanoparticle superlattices using global Monte Carlo optimization
Nature Communications (2022)
-
Spatially resolved fluorescence of caesium lead halide perovskite supercrystals reveals quasi-atomic behavior of nanocrystals
Nature Communications (2022)
-
Colloidal quantum dot electronics
Nature Electronics (2021)