Abstract
The Mott metal-insulator transition—a manifestation of Coulomb interactions among electrons—is known as a discontinuous transition. Recent theoretical studies, however, suggest that the transition is continuous if the Mott insulator carries a spin liquid with a spinon Fermi surface. Here, we demonstrate the case of a quasi-continuous Mott transition from a Fermi liquid to a spin liquid in an organic triangular-lattice system κ-(ET)2Cu2(CN)3. Transport experiments performed under fine pressure tuning have found that as the Mott transition is approached, the Fermi liquid coherence temperature continuously falls to the scale of kelvins, with a divergent quasi-particle decay rate on the metal side, and the charge gap continuously closes on the insulator side. A Clausius-Clapeyron analysis provides thermodynamic evidence for the extremely weak first-order nature of the transition. These results provide additional support for the existence of a spinon Fermi surface, which becomes an electron Fermi surface when charges are delocalized.
Similar content being viewed by others
Introduction
In a Mott insulator, mutually interacting spins are generally ordered at low temperatures. However, antiferromagnetic interactions are self-conflicting for spins on a triangle-based lattice, which may fall into exotic states called quantum spin liquids1,2. Indeed, spin liquids were substantiated in κ-(ET)2Cu2(CN)3 and EtMe3Sb[Pd(dmit)2]2 (ET and dmit denote BEDT-TTF=bis(ethylenedithio)tetrathiafulvalene and 1,3-dithiole-2-thione-4,5-dithiolate, respectively), which are organic materials with triangular lattices3,4; they exhibit unconventional spin excitations of a gapless or marginally gapped nature3,4,5,6,7,8,9. These properties lead to an intriguing proposal of delocalized spin excitations—spinons with a Fermi surface10,11—which has recently been discussed in a strong spin–orbit-coupled triangular-lattice YbMgGaO4 system as well12,13.
In both organic materials, the spin liquids reside near the Mott metal-insulator transition, which is accessible by applying pressure14,15,16,17. The vicinity to the Mott transition is theoretically suggested to be essential to the emergence of spin liquids in triangular lattices2,10. In a sense that any conventional symmetry breaking does not follow, the metal-insulator transition of spin liquids is a genuine Mott transition, at which only the charge degrees of freedom are frozen, as Mott originally conceptualized. The conventional Mott transition is a first-order transition with a clear discontinuity, as shown by various experiments18 and the celebrated dynamical mean-field theory (DMFT)19. However, if the spin excitations in the spin liquid are delocalized as suggested theoretically, the itineracy of the electrons is lost in the charge sector on the Mott transition but persists in the spin sector as fractionalized spinons that hold a Fermi surface, leading to an unconventional Mott localization of electrons; indeed, a continuous Mott transition distinct from the conventional cases is predicted20,21,22. Thus, a close examination of the Mott transition is expected to provide insight into the fractionalization of particles in condensed matter.
Here, we investigate the charge transport of κ-(ET)2Cu2(CN)3 under precisely controlled pressures to reveal how the Fermi liquid and the spin liquid meet in the pressure (P)−temperature (T) plane. We present that the Fermi liquid coherence temperature continuously falls to the scale of kelvins, with a divergent quasi-particle decay rate on the metal side, and the charge gap gradually closes on the insulator side. In addition, a Clausius-Clapeyron analysis of the P−T phase diagram yields thermodynamic evidence for the extremely weak first-order nature of the transition. These findings provide additional support for the existence of a spinon Fermi surface in the spin liquid phase.
Results
Pressure–temperature phase diagram
κ-(ET)2Cu2(CN)3 is a layered organic system composed of conducting ET layers and insulating Cu2(CN)3 layers. In the conducting layers, the ET molecules form dimers, which constitute a nearly isotropic triangular lattice with a half-filled band23 (Supplementary Fig. 3). The in-plane resistance was measured with the standard dc four-probe method. Hydrostatic pressure was applied by using, as pressure media, helium gas for P < 200 MPa and Daphne 7373 oil or DEMNUM S-20 oil for P > 200 MPa. Experimental details are described in Methods.
The main points of the present results for κ-(ET)2Cu2(CN)3 are featured in the P–T phase diagram (Fig. 1a–c), which was constructed on the basis of the resistivity data described below (Fig. 2a–d). The first-order transition curve separating the spin liquid insulator and a metal (or a superconductor) shows a characteristic bending profile (Fig. 1a) and leads to a fan-shaped quantum critical region at high temperatures15 (Fig. 1b, c). The temperature region of a Fermi liquid, in which the resistivity follows the T2 law, is strongly suppressed as the Mott boundary is approached. The proximity of the superconducting phase to the spin liquid phase is confirmed. Figure 2a shows the temperature dependence of resistance for P = 0–202 MPa, where a systematic variation from an insulating behaviour to a metallic behaviour emerges. For P ≥ 135 MPa, the resistance exhibited jumps with barely recognizable hysteresis, indicating a weak first-order Mott transition; we define Pc = 135 MPa as the critical pressure of the Mott transition at low temperatures. The non-monotonic temperature dependence of resistance near 120 MPa, which appears strange, is reasonable, considering the bending of the quasi-continuous Mott transition line towards higher pressures with increasing temperature. As the temperature decreases from approximately 15 K to several kelvins at a fixed pressure of P≲135 MPa, the system approaches the metallic phase because the bent first-order transition line (dT/dP > 0) nears the fixed pressure at low temperatures (see Fig. 1a). In addition, the present Mott transition has a quasi-continuous nature. Thus, the approach to the Mott boundary by cooling causes a decrease in the charge gap in the insulating side and possibly results in a decrease in resistance with temperature. Eventually, the resistance increases on further cooling because the system is located in the Mott insulating side at a finite distance from the Mott transition line, which is nearly vertical at temperatures below ∼5 K. An absence of a resistance jump for T ≥ 20 K (Fig. 2d) means that the critical endpoint of the Mott transition is located between 16 and 20 K, which is approximately half of the critical endpoint in κ-(ET)2Cu[N(CN)2]Cl, 40 K24.
Critical behaviour on the metal side
Figure 2b shows the resistance in the metallic phase plotted against T2. The T2 dependence expected in a conventional Fermi liquid, R(T) = R0 + AT2, holds over a limited low-temperature range below the coherence temperature T*, which is pushed down to the order of kelvin near the Mott boundary (Fig. 1a–c). The three orders of magnitude drop of T* from the bare energy scale of the bandwidth, ~0.5 eV (~6000 K)16, suggests that the system is situated near the quantum critical regime. Referring to theoretical investigations21,22, T* might correspond to the crossover temperature between a Fermi liquid and marginal Fermi liquid, in which the quasi particles are scattered by critical fluctuations of gauge field. The locations of T* and the quantum critical region in the pressure–temperature phase diagram (Fig. 1c) are overall consistent with the theoretical prediction. The coefficient A of the T2 term, normalized to the room temperature resistance value of each sample, is enhanced as the Mott boundary is approached (Fig. 3), indicating an increase in quasi-particle decay rate. The divergent behaviour of A persists in the very vicinity of Pc, |P−Pc| < 50 MPa, whereas the increase in A becomes weak in the vicinity of the conventional Mott transition (see Supplementary Fig. 8). The pressure dependence of A is well fitted by a power-law, A ∝ |P−Pc|−0.75 ± 0.01, which does not show an excellent agreement with the theoretical prediction21 of the quasi-particle decay rate near the quantum Mott transition, γqp ∝ |P−Pc|−2ν (2ν∼1.34). The gentler divergence in the experiment than in the theory may reflect the weak first-order nature of the transition. In conventional correlated electron systems, A is proportional to the square of effective mass, and thus a power-law divergence of A is linked to a power-law divergence of the effective mass. Note, however, that this may not be the case in the quantum Mott transition of a spin liquid, according to quantum-field21 and phenomenological25 theories; namely, the effective mass may not diverge in a power-law manner.
Critical behaviour on the insulator side
In the insulating phase, the resistance is characterized by a charge gap, Δ, that is deduced from the line fitting to the data of 2d(lnR)/d(1/T) at low temperatures (see Supplementary Note 6 and Supplementary Fig. 9 for details). As shown in Figs. 2c, 3, a remarkable feature is the gradual closing of the charge gap following Δ∝ |P−Pc|0.73 ± 0.04 for |P−Pc| ≳25 MPa, which suggests the quasi-continuous nature of the Mott transition. This form is close to the theoretical prediction, Δ∝ |P−Pc|0.67, for the quantum Mott transition21,22, whereas some numerical studies suggest Δ∝ |P−Pc|26,27,]. The anomalous drop in Δ for |P−Pc| < 25 MPa implies marginally gapped or gapless charge excitations in the vicinity of the Mott transition; indeed, the resistance shows a plateau in the narrow range of pressures around the Mott boundary below 10 K (Fig. 2a, d). To visualize these resistance behaviours, the logarithm of resistance is indicated by a range of colours on the P–T phase diagram (Fig. 2e), which shows that the (yellow-coloured) plateau region resides in the lower-pressure side of the Mott boundary. Remarkably, such a resistance plateau is theoretically suggested to appear at the two-dimensional quantum Mott transition of a spin liquid21,22. The predicted sheet resistance at the plateau is ~ 8 h/e2 (h is the Plank constant, and e is the elementary charge), which is smaller than the experimental sheet resistance of one conducting layer in the plateau, ~33 h/e2 (Supplementary Note 4). In the experiments, the plateau appeared in a narrow but finite pressure region, whereas it occurs only at a critical pressure and is fan shaped at high temperatures in the theoretical prediction. The disorder in real systems can extend the critical point into a finite region, which may also explain the discrepancy in the magnitude of the sheet resistance. It is suggested that disorder in the polymeric atomic configurations in the anion layers affects the charge transport at ambient pressure28.
Clausius-Clapeyron analysis of the P−T phase diagram
As seen above, the transport characteristics around the Mott boundary are featured by a substantial falloff in T*, critical behaviours of the coefficient A, closing of charge gap Δ, and resistance plateau, all of which go against the conventional first-order Mott transition but accord with the theoretical consequences of the Mott transition of a spin liquid with a spinon Fermi surface20,21,22. Below, we discuss the thermodynamics of the Mott phase diagram in terms of the Clausius-Clapeyron relation, which relates the slope of the phase boundary, ∂Pjump/∂Tjump, to the entropy difference between the neighbouring phases through SQSL−Smetal = ΔV × ∂Pjump/∂Tjump, where SQSL and Smetal are the molar entropy of the quantum spin liquid (QSL) and the metal, respectively, and ΔV (=VQSL−Vmetal) is the molar volume change. Assuming that the lattice contributions to SQSL and Smetal do not largely differ, SQSL−Smetal is approximately equal to SQSL,spin−Smetal,el, where SQSL,spin (Smetal,el) is the spin (electron) contribution to SQSL (Smetal); the validity of this assumption is argued later. The ∂Pjump/∂Tjump determined from the fitting curve of the phase boundary (Fig. 1a) gives the temperature dependence of SQSL,spin−Smetal,el with ΔV as a parameter (Fig. 4a). We also performed a Clausius-Clapeyron analysis while incorporating the temperature dependence of ΔV and found the results in Fig. 4 to be practically unaltered (see Supplementary Note 5 and Supplementary Fig. 6 for details). Because ΔV and P are thermodynamically conjugate variables, ΔV plays a role as an order parameter of Mott transition and therefore measures the strength of the first-order transition.
For evaluating SQSL,spin, Smetal,el is reasonably assumed to be γT, where γ is estimated to be ~ 27.6 mJ K−2 mol−1, referring to the spin susceptibility of χmetal = 3.8 × 10−4 emu mol−1 (ref. 29) and Wilson ratio of RW = 1, which holds in the metallic phases of κ-type compounds (Supplementary Note 2). The entropy of the spin liquid is obtained through SQSL,spin = γT + ΔV × (∂Pjump/∂Tjump), as displayed for several values of ΔV in Fig. 4b. SQSL,spin decreased on cooling, particularly below 10 K, and fell below Smetal,el at approximately 6 K (Fig. 4b). The rather steep entropy loss at approximately 6 K implies that the 6 K anomaly observed at ambient pressure5,6,30 persists up to the Mott boundary. Because SQSL,spin must not increase on cooling, ΔV should be ~2 × 10−8 m3 mol−1 or less (Fig. 4b). We also estimated the specific heat from SQSL,spin, as shown in Supplementary Fig. 7. Although the specific heat is less reliable since it is given by the second derivative of the fitting curve of the phase boundary, the deduced specific heat appears to show a qualitative feature, that is, peak formations at approximately 6–7 K, akin to the ambient-pressure behaviour6 and suggesting that the 6 K anomaly at ambient pressure persists up to the critical pressure of the Mott transition.
For comparison, we performed a similar analysis for κ-(ET)2Cu[N(CN)2]Cl, which exhibits an antiferromagnetic order in the Mott insulating phase (Fig. 4c, d and Supplementary Fig. 5). The spin entropy of the antiferromagnetic insulator (AFI) side, SAFI,spin, rapidly decreases with temperature, even falling below Smetal,el at as high as 30 K, irrespective of the choice of ΔV value. In the insulating side on the Mott boundary, spins undergo an antiferromagnetic order at approximately TN = 15 K31. Thus, spins lose their entropy from much higher temperatures than the Néel order due to short-range ordering, as shown by the thermodynamic and magnetic measurements at ambient pressure32,33. The requirement that the entropy should die out rapidly at low temperatures narrows down the possible values of ΔV to a range of 4–6 × 10−7 m3 mol−1 (Fig. 4d), which is in good agreement with the experimentally determined value of ~5.4 × 10−7 m3 mol−1 (ref. 34, also see Supplementary Note 3) and thus corroborates the validity of the present analysis. Remarkably, the ΔV of κ-(ET)2Cu2(CN)3 is several tens of times smaller than the ΔV of κ-(ET)2Cu[N(CN)2]Cl, which provides thermodynamic evidence for the extremely weak first-order nature of the Mott transition in κ-(ET)2Cu2(CN)3, in accordance with the quasi-continuous nature of the transition revealed by the charge transport. Note that the large value of ΔV in κ-(ET)2Cu[N(CN)2]Cl holds even above TN, meaning that the extremely small ΔV value in κ-(ET)2Cu2(CN)3 is not attributable only to the paramagnetic nature of the Mott insulator.
It is suggestive that the temperature of the inflection point in the entropy decrease, 6 K, roughly coincides with T* in the metallic side at the Mott boundary. A similar anomaly suggesting the rapid release of the spin entropy was observed in the specific heat at approximately 6 K at ambient pressure6, and the formation of a spinon Fermi surface from an incoherent paramagnetic state was argued as a possible origin. The present results may suggest that the electron Fermi surface in the metallic phase and the spinon Fermi surface in the spin liquid phase take shape at similar temperatures, although the origin of the 6 K anomaly at ambient pressure is under debate.
Discussion
The charge transport in κ-(ET)2Cu2(CN)3 and the thermodynamic arguments consistently highlight the quasi-continuous nature of the Mott transition, which contradicts the conventional picture but is reconciled with the theoretical consequences of a transition from an electron Fermi surface to a spinon Fermi surface. We note, however, that the correspondence between the experiments and theories based on the Hubbard model is not exact in that κ-(ET)2Cu2(CN)3 exhibits a first-order transition, although it is extremely weak. This may indicate that some additional factors not included in the theoretical treatments affect the ground states; indeed, superconductivity appears in the metallic phase, and the 6 K anomaly is possibly suggestive of some instability of the spin liquid emerging in the insulating phase. In addition, the possible first-order transition due to long-range interactions among electrons is theoretically discussed21. Very recently, a DMFT-based theoretical treatment incorporating spinon excitations suggests the first-order nature of the Mott transition of a spinon Fermi surface35. The faint remanence of the first-order nature may have some relevance to these theoretical consequences21,35.
Finally, we discuss the relation between the low-temperature (low-T) quantum criticality observed here and the high-temperature (high-T) quantum criticality (Fig. 1b, c). The latter has the following key features. First, it is commonly observed for various systems irrespective of lattice geometry, whether the Mott insulator is a spin liquid or an antiferromagnet or whether the Mott transition is of the first order or quasi-continuous. Second, the high-T regime should have no memories about Fermi surfaces in the metallic side and the nature of the magnetic ground state in the Mott insulating side. Third, the high-T quantum critical scaling of resistivity is reproduced by the single-site DMFT of the Hubbard model. All the above suggest that the high-T quantum criticality is a universal high-energy characteristic of the Mott transition. In contrast, the low-T quantum criticality is likely specific to the fluctuations between electron Fermi surfaces and spinon Fermi surfaces, being closely related to the kinds of ground states. In our tentative view, the Mott transition has a hierarchal energy structure. The high-energy quantum criticality is generic, whereas the low-energy one depends on the details of the lattice, and the former is characterized by the scaling function fulfilled by resistivity in contrast to the constant resistivity in the latter. The proximity of the zν values of the two criticalities may provide some insight into their possible connection, which awaits theoretical exploration.
Methods
Resistance measurements under pressure
Single crystals of κ-(ET)2Cu2(CN)3 (named #1, #2, #3 and #4) were grown by the conventional electrochemical method. The in-plane resistivity was measured with the d.c. four-probe method. Gold wires with diameters of 15–25 μm were glued onto the crystal faces with carbon paste to serve as electrodes. To apply hydrostatic pressure, we used pressure media of helium (for samples #1 and #2) for P < 200 MPa, Daphne 7373 oil (for sample #3) and DEMNUM S-20 oil (for sample #4) for P > 200 MPa. These pressure media are solidified at low temperatures. The melting temperature of helium is as low as 0–20 K for the pressures studied here (Supplementary Fig. 1), whereas those of the two oils exceed 100 K. Upon solidification of the pressure media, the pressures in the cell are somewhat reduced. The pressure reduction for the helium medium, which is in a range of 10–30 MPa, could be precisely evaluated using the method described in Supplementary Note 1. Sample #1 was studied across the helium solidification curve in Supplementary Fig. 1; the pressure was determined by the method with an accuracy of 1 MPa. Sample #2 was measured at higher temperatures than the helium solidification curve. For samples #3 and #4 in the oil media, the pressure values quoted in this article are those obtained by subtracting 300 MPa (sample #3) or 250 MPa (sample #4) from the pressures monitored at room temperature.
Data availability
The data that support the plots within this paper and other findings of this study are available from the corresponding author upon reasonable request.
References
Zhou, Y., Kanoda, K. & Ng, T.-K. Quantum spin liquid states. Rev. Mod. Phys. 89, 025003 (2017).
Balents, L. Spin liquids in frustrated magnets. Nature 464, 199–208 (2010).
Shimizu, Y., Miyagawa, K., Kanoda, K., Maesato, M. & Saito, G. Spin liquid state in an organic Mott insulator with a triangular lattice. Phys. Rev. Lett. 91, 107001 (2003).
Itou, T., Oyamada, A., Maegawa, S., Tamura, M. & Kato, R. Quantum spin liquid in the spin-1∕2 triangular antiferromagnet EtMe3Sb[Pd(dmit)2]2. Phys. Rev. B 77, 104413 (2008).
Shimizu, Y., Miyagawa, K., Kanoda, K., Maesato, M. & Saito, G. Emergence of inhomogeneous moments from spin liquid in the triangular-lattice Mott insulator κ-(ET)2Cu2(CN)3. Phys. Rev. B 73, 140407R (2006).
Yamashita, S. et al. Thermodynamic properties of a spin-1/2 spin-liquid state in a κ-type organic salt. Nat. Phys. 4, 459–462 (2008).
Yamashita, M. et al. Thermal-transport measurements in a quantum spin-liquid state of the frustrated triangular magnet κ-(BEDT-TTF)2Cu2(CN)3. Nat. Phys. 5, 44–47 (2008).
Yamashita, M. et al. Highly mobile gapless excitations in a two-dimensional candidate quantum spin liquid. Science 328, 1246–1248 (2010).
Watanabe, D. et al. Novel Pauli-paramagnetic quantum phase in a Mott insulator. Nat. Commun. 3, 1090 (2012).
Motrunich, O. I. Variational study of triangular lattice spin-1∕2 model with ring exchanges and spin liquid state in κ-(ET)2Cu2(CN)3. Phys. Rev. B 72, 045105 (2005).
Lee, S. S. & Lee, P. A. U(1) gauge theory of the Hubbard model: spin liquid states and possible application to κ-(BEDT-TTF)2Cu2(CN)3. Phys. Rev. Lett. 95, 036403 (2005).
Shen, Y. et al. Evidence for a spinon Fermi surface in a triangular-lattice quantum-spin-liquid candidate. Nature 540, 559–562 (2016).
Paddison, J. A. M. et al. Continuous excitations of the triangular-lattice quantum spin liquid YbMgGaO4. Nat. Phys. 13, 117–122 (2016).
Kurosaki, Y., Shimizu, Y., Miyagawa, K., Kanoda, K. & Saito, G. Mott transition from a spin liquid to a Fermi liquid in the spin-frustrated organic conductor κ-(ET)2Cu2(CN)3. Phys. Rev. Lett. 95, 177001 (2005).
Furukawa, T., Miyagawa, K., Taniguchi, H., Kato, R. & Kanoda, K. Quantum criticality of Mott transition in organic materials. Nat. Phys. 11, 221–224 (2015).
Komatsu, T., Matsukawa, N., Inoue, T. & Saito, G. Realization of superconductivity at ambient pressure by band-filling control in κ-(BEDT-TTF)2Cu2(CN)3. J. Phys. Soc. Jpn. 65, 1340–1354 (1996).
Kato, R., Tajima, A., Nakao, A., Tajima, N., Tamura, M. in Multifunctional Conducting Molecular Materials (eds Saito, G. et al.) 32–38 (Royal Society of Chemistry, Cambridge, 2007).
Imada, M., Fujimori, A. & Tokura, Y. Metal-insulator transitions. Rev. Mod. Phys. 70, 1039–1263 (1998).
Georges, A., Kotliar, G., Krauth, W. & Rozenberg, M. J. Dynamical mean-field theory of strongly correlated fermion systems and the limit of infinite dimensions. Rev. Mod. Phys. 68, 13–125 (1996).
Mishmash, R. V., González, I., Melko, R. G., Motrunich, O. I. & Fisher, M. P. A. Continuous Mott transition between a metal and a quantum spin liquid. Phys. Rev. B 91, 235140 (2015).
Senthil, T. Theory of a continuous Mott transition in two dimensions. Phys. Rev. B 78, 045109 (2008).
Witczak-Krempa, W., Ghaemi, P., Senthil, T. & Kim, Y. B. Universal transport near a quantum critical Mott transition in two dimensions. Phys. Rev. B 86, 245102 (2012).
Kanoda, K. & Kato, R. Mott physics in organic conductors with triangular lattices. Annu. Rev. Condens. Matter Phys. 2, 167–188 (2011).
Kagawa, F., Miyagawa, K. & Kanoda, K. Unconventional critical behaviour in a quasi-two-dimensional organic conductor. Nature 436, 534–537 (2005).
Zhou, Y. & Ng, T.-K. Spin liquid states in the vicinity of a metal-insulator transition. Phys. Rev. B 88, 165130 (2013).
Watanabe, S. & Imada, M. Precise determination of phase diagram for two-dimensional Hubbard model with filling- and bandwidth-control Mott transitions: grand-canonical path-integral renormalization group approach. J. Phys. Soc. Jpn. 73, 1251–1266 (2004).
Laubach, M., Thomale, R., Platt, C., Hanke, W. & Li, G. Phase diagram of the Hubbard model on the anisotropic triangular lattice. Phys. Rev. B 91, 245125 (2015).
Pinterić, M. et al. Anisotropic charge dynamics in the quantum spin-liquid candidate κ-(BEDT-TTF)2Cu2(CN)3. Phys. Rev. B 90, 195139 (2014).
Shimizu, Y. et al. Pressure-induced superconductivity and Mott transition in spin-liquid κ-(ET)2Cu2(CN)3 probed by 13C NMR. Phys. Rev. B 81, 224508 (2010).
Manna, R. S., de Souza, M., Brühl, A., Schlueter, J. A. & Lang, M. Lattice effects and entropy release at the low-temperature phase transition in the spin-liquid candidate κ-(BEDT-TTF)2Cu2(CN)3. Phys. Rev. Lett. 104, 016403 (2010).
Lefebvre, S. et al. Mott transition, antiferromagnetism, and unconventional superconductivity in layered organic superconductors. Phys. Rev. Lett. 85, 5420–5423 (2000).
Nakazawa, Y. & Kanoda, K. Electronic structure of insulating salts of the κ-(BEDT-TTF)2X family studied by low-temperature specific-heat measurements. Phys. Rev. B 53, R8875–R8878 (1996).
Kagawa, F., Kurosaki, Y., Miyagawa, K. & Kanoda, K. Field-induced staggered magnetic moment in the quasi-two-dimensional organic Mott insulator κ-(BEDT-TTF)2Cu[N(CN)2]Cl. Phys. Rev. B 78, 184402 (2008).
Gati, E. et al. Breakdown of Hooke’s law of elasticity at the Mott critical endpoint in an organic conductor. Sci. Adv. 2, e1601646 (2016).
Lee, T.-H., Florens, S. & Dobrosavljević, V. Fate of spinons at the Mott point. Phys. Rev. Lett. 117, 136601 (2016).
Nakazawa, Y., Taniguchi, H., Kawamoto, A. & Kanoda, K. Electronic specific heat at the boundary region of the metal-insulator transition in the two-dimensional electronic system of κ-(BEDT-TTF)2Cu[N(CN)2]Br. Phys. Rev. B 61, R16295–R16298 (2000).
Acknowledgements
This work was supported in part by JSPS KAKENHI under Grant Nos. 20110002, 25220709, 24654101 and 17K05532 and the US National Science Foundation under Grant No. PHYS-1066293 and the hospitality of the Aspen Center for Physics.
Author information
Authors and Affiliations
Contributions
T.F. and K. Kanoda designed the experiments. T.F., K. Kobashi and Y.K. performed the resistance measurements. K.M. grew the single crystal for the study. All authors interpreted the data. T.F. wrote the manuscript with the assistance of K.M. and K. Kanoda. K. Kanoda headed this project.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Furukawa, T., Kobashi, K., Kurosaki, Y. et al. Quasi-continuous transition from a Fermi liquid to a spin liquid in κ-(ET)2Cu2(CN)3. Nat Commun 9, 307 (2018). https://doi.org/10.1038/s41467-017-02679-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-017-02679-7
- Springer Nature Limited
This article is cited by
-
Thermodynamic determination of the equilibrium first-order phase-transition line hidden by hysteresis in a phase diagram
Scientific Reports (2023)
-
Thermoelectric signature of quantum critical phase in a doped spin-liquid candidate
Nature Communications (2023)
-
Chasing the spin gap through the phase diagram of a frustrated Mott insulator
Nature Communications (2023)
-
Mechanism of the insulator-to-metal transition and superconductivity in the spin liquid candidate NaYbSe2 under pressure
npj Quantum Materials (2022)
-
Low-temperature dielectric anomaly arising from electronic phase separation at the Mott insulator-metal transition
npj Quantum Materials (2021)