Abstract
Photo-induced non-radiative energy dissipation is a potential pathway to induce structural-phase transitions in two-dimensional materials. For advancing this field, a quantitative understanding of real-time atomic motion and lattice temperature is required. However, this understanding has been incomplete due to a lack of suitable experimental techniques. Here, we use ultrafast electron diffraction to directly probe the subpicosecond conversion of photoenergy to lattice vibrations in a model bilayered semiconductor, molybdenum diselenide. We find that when creating a high charge carrier density, the energy is efficiently transferred to the lattice within one picosecond. First-principles nonadiabatic quantum molecular dynamics simulations reproduce the observed ultrafast increase in lattice temperature and the corresponding conversion of photoenergy to lattice vibrations. Nonadiabatic quantum simulations further suggest that a softening of vibrational modes in the excited state is involved in efficient and rapid energy transfer between the electronic system and the lattice.
Similar content being viewed by others
Introduction
Energy loss pathways are important considerations for the design of optoelectronic devices based on nanomaterials like transition metal dichalcogenides (TMDCs)1,2, which are promising candidates for ultrafast photodetection3, valleytronics4, and field effect transistors5,6. Much of the recent attention has been focused on the radiative relaxation and defect-mediated non-radiative bimolecular recombination of excitons, which have been shown to drastically limit photoluminescence quantum yield even at the monolayer limit (~0.4%)7,8,9,10,11,12. In addition, considerable effort has been expended in the strain engineering13,14 and in identifying strategies for chemical passivation of defects to improve light emission efficiency and device performance15,16. The nonradiative channel is the dominant energy loss pathway in defect-free monolayers at high charge carrier densities but is less well explored1,6,9,15. Recent work from Ruppert et al.17 has shown that an optically excited monolayer WS2 relaxes nonradiatively to lattice vibration, causing the absorption edge to redshift due to a small temperature jump of ~40 K. This nonradiative process is promising for triggering light-driven atomic motion required for structural-phase transition, but so far, it is not well understood due to a lack of experimental methods to quantify atomic motion and lattice temperature directly.
In this study, we utilize mega-electronvolt ultrafast electron diffraction (MeV-UED)18 as a probe to measure mean-square atomic displacements and the corresponding local temperature in bilayer MoSe2 samples photoexcited to a high carrier density (~1014 cm−2), which lies in the electron–hole plasma regime. At this high charge carrier concentration, the laser fluence of the optical pump is high enough to deposit the energy required for initiating a possible structural-phase transition (temperature jump of ~1000-K and ~0.3-Å difference of lattice constant between 2-H and 1-T phases). Time-resolved electron diffraction allows us to directly explore laser-induced atomic motion and structural disorder with ~200-fs temporal resolution, and thus to directly quantify the efficiency of nonradiative energy channels in these two-dimensional materials. We monitor the dependence of the resulting lattice disorder on the photoinjected carrier concentration by varying the pump fluence at two different wavelengths. The observed subpicosecond increase in structural disorder and lattice temperature is consistent with ultrafast conversion of electronic energy to atomic motion via softened phonon modes observed in our first-principles density functional theory (DFT) and nonadiabatic quantum molecular dynamics (NAQMD) simulations. Furthermore, the observed ultrafast temperature rise is linearly proportional to the absorption of the pump energy calibrated to a saturable absorber model, indicating a high efficiency of the nonradiative decay channel.
Results
Time-resolved electron diffraction
A schematic of the experimental procedure and a representative electron diffraction pattern and intensity profile is displayed in Fig. 1. Each diffraction pattern is generated by the accumulation of over ~7000 pulses with effective charge of ~20 fC per pulse at the sample target. Several families of diffraction planes in the reciprocal lattice are observed. All the pump-probe traces at a given reciprocal lattice vector Q (i.e., 2π/d) are averaged over six equivalent planes. Diffraction intensity for a lattice plane is calculated from the full diffraction pattern by the integration of photodetector counts on a small region around the corresponding reciprocal lattice vector. Negative delay times are shown when the electron probe beam precedes the optical pump beam on the sample target. A red kinetic plot in Fig. 1 displays a representative temporal profile of the measured diffraction intensity, which shows a rapid exponential decay of the initial diffraction intensity value I 0 to a new lower value of I at a positive delay time due to the increased incoherent atomic motion induced by the optical pumping. The ratio of these two intensities allows us to estimate the atomic disorder and the resulting temperature jump produced by the optical excitation, which will be further discussed later in this paper.
Time-resolved mega-eV electron diffraction. Snapshots of electron diffraction of MoSe2 bilayer for Debye–Waller factor (DWF) measurements. Several families of diffraction planes are labeled in the last diffraction image for clarity (i.e., {100}, {110}, {200}, {210}, {300}, and {220}). A time-resolved kinetic plot that illustrates the suppression of diffraction intensity at {110} family is shown, where I 0 and I denote the Bragg peak diffraction intensities at negative and positive delay times from the fit of experimental results. Each image is accumulated over ~7000 pulses from multiple scans with effective charge of ~20 fC per pulse at the sample target. The mean-square displacements, \(\left\langle {\Delta u^{\mathrm{2}}} \right\rangle _{\Delta T}\), are obtained by plotting \({\mathrm{ln}}\left( {\frac{{I_0}}{I}} \right)\) vs. Q 2, where Q is 2π over interplanar spacing d
Theoretical approach
Our UED experiments are further supported by NAQMD simulations on MoSe2 bilayer crystals, which follow the trajectories of all atoms while computing interatomic forces quantum mechanically from first principles19, including the dynamics of electrons and nuclei20. Electronic excitations are described within the framework of linear-response time-dependent DFT, which is a proven method to investigate ultrafast nonradiative relaxation in other electronically excited material systems21. In this study, nonadiabatic transitions between electronic excited states assisted by molecular motions are treated with a surface-hopping approach.
In order to elucidate atomic dynamics observed in our QMD simulations, we also calculated phonon dispersion curves for the ground-state and electronically excited MoSe2 bilayers using DFT and the Δ-SCF method. Specifically, for excited electron–hole concentration of 1.2 × 1014 cm−2 (2.4 × 1014 cm−2) used in this study, we promote one (two) electrons from the valence band to the conduction band. The comparison of experimental results from Si3N4-supported MoSe2 flakes to simulation results from suspended MoSe2 bilayers is justified for two reasons. First, MoSe2 bilayer forms a type-I heterojunction with the insulating Si3N4 substrate (~5-eV bandgap), which precludes a charge transfer process. Second, Raman microscopy and photoluminescence measurements from the Si3N4-supported MoSe2 agree with previous measurements on different substrates22, indicating a lack of substrate effect on MoSe2 vibration modes.
Debye–Waller response of bilayer MoSe2
Figure 2 summarizes our experimental results for bilayer MoSe2 samples photoexcited at 400 nm. The temporal evolution of the measured diffraction intensities for six diffraction families at carrier densities of 1.2 ± 0.1 × 1014 cm−2 and 1.8 ± 0.1 × 1014 cm−2 is shown in Fig. 2(a, b), respectively. Note that all the pump-probe kinetics are normalized to one at the negative delay time (I 0), so that the fractional drop of intensity can be quickly identified for different diffraction families. Each pump-probe trace is then fit to an exponential function convoluted with an ~200-fs full-width at half-maximum instrument response function (time resolution) estimated for the MeV-UED system. Thus, the obtained I and I 0 from the fit are the relative electron diffraction intensities at far positive and negative delay times, respectively, as shown in the red curves in Fig. 2a, b. The kinetic plot at a lower carrier density of 0.68 ± 0.1 × 1014 cm−2 is presented in Supplementary Fig. 2a in Supplementary Note 3. The standard deviation error bars are approximately 0.04 by using multiple scans with a total of ~7000 pulses per delay time point. The primary observation in the intensity profiles is the ultrafast subpicosecond decay of diffraction intensities for all families of planes considered in our study. This is approximately a factor two faster than the time constant reported for the monolayer MoS2 at a similar carrier density (τ ~ 1.7 ps)23. Furthermore, the invariant steady-state diffraction intensity up to ten picoseconds indicates that the lattice is thermalized for delay times longer than one picosecond after optical excitation. The experimental time constants do not show any obvious changes as a function of the carrier density produced at 400 nm and 800 nm, implying a minor role of high-order carrier kinetics in these carrier density regimes.
Pump-probe kinetics and Debye–Waller responses at 400-nm photoexcitation. Pump-probe kinetic plots for six diffraction planes at a carrier density of (a) 1.2 ± 0.1 × 1014 cm−2 and (b) 1.8 ± 0.1 × 1014 cm−2 at 400 nm excitation for the MoSe2 bilayer, and (c) Debye–Waller responses at four carrier densities. A large deviation between linear fit and experimental data occurs at the highest carrier density (red). At this density, the first five data points are used for the linear fit. The corresponding temperatures calculated from the slopes are presented in the context and Supplementary Information. Error bars represent 68% confidence interval and are calculated from the propagation of standard error of the mean from the fit of averaged multiple pump-probe scans. d Kinetic plots for {110} and {300} planes at carrier density at 1.8 ± 0.1 × 1014 cm−2 (blue) and 2.1 ± 0.1 × 1014 cm−2 (red), respectively, for comparison. A complex Bragg peak intensity decay occurs at the highest carrier density (red), which may suggest an energy redistribution between different phonons from a strong carrier-modified potential energy surface
Below, we consider three possible mechanisms to explain the ultrafast appearance of lattice disorder. First, the lattice energy could result from the high-order kinetics such as nonradiative bimolecular and Auger recombination through annihilation of photoexcited excitons. The obtained carrier density for this experiment is ~1014 cm−2 such that an electron–hole plasma is produced from screened exciton dissociation (i.e., the Mott density is ~1014 cm−2)24,25,26,27. It has been reported that the bimolecular exciton–exciton annihilation or Auger process mediated by defects/traps occurs efficiently in MoSe2 and MoS2 7,8,28. However, this happens at exciton densities below ~1013 cm−2 allowing intact excitons to annihilate each other in the time scale of a few picoseconds. At a higher charge carrier density (~1014 cm−2), excitons dissociate into free carriers due to the increased screening of Coulomb interaction in the bound charges24,27. Therefore, the exciton–exciton annihilation may not be able to account for this fast appearance of lattice disorder. Our power dependence measurement at 400 nm does not show clear changes of time constants as a function of carrier density in the electron–hole plasma regime. This suggests that the high-order carrier kinetics such as Auger processes does not play an important role in our experiments.
The second possible explanation for the rapid decay of diffraction intensity may be due to the induction of nonthermal melting. Figure 2c shows the logarithmic ratios of measured diffraction intensities vs. the diffraction families in the square-reciprocal space at four carrier densities (i.e., ln(I 0/I) vs. Q 2). The effective mean-square displacements associated with different carrier concentrations can be estimated from the slope29,30, \(\Delta \left\langle {u^2} \right\rangle _{\Delta T}\), by using the Debye–Waller equation as shown in Eqs. (1) and (2).
The calculated mean-square displacements for the four different carrier concentrations are 5.6(±0.2) × 10−3 Å2, 9.8(±0.3) × 10−3 Å2, 13.0(±0.4) × 10−3 Å2, and 17.4(±1.2) × 10−3 Å2, respectively, corresponding to a root-mean-square atomic displacement, \(\sqrt {\Delta \left\langle {u^2} \right\rangle _{\Delta T}} \), of 0.075 ± 0.001 Å, 0.099 ± 0.002 Å, 0.114 ± 0.002 Å, and 0.132 ± 0.005 Å. These photoinduced atomic displacements range from 2% to 5% of the in-plane lattice constant of 3.3 Å31, which is below the Lindemann criterion for a solid-to-liquid phase transition (i.e., ~10%–20%)32. In addition, these displacements are much less than what would be expected for highly inertial atomic motion initiated by an intense optical excitation (highly nonthermal melting)33,34,35. We estimate a (3k B T/m)1/2 = 2.9 Å per picosecond mean atomic velocity for MoSe2 at room temperature, where k B, m, and T are the Boltzmann constant, averaged mass, and room temperature, respectively. At this velocity, the mean atomic displacements would be 1.45 Å at a 500-fs time delay, corresponding to ~44% of in-plane lattice constant. This is ~10 times higher than our observations at the highest pump fluence. Thus, our data are not consistent with a nonthermal melting and strong atomic inertial processes from potential deformation by the strong laser field.
Another possibility is the existence of strong electron–phonon coupling, which has been postulated for molybdenum chalcogenides with dynamics occuring on a subpicosecond time scale36. Figure 2d presents a comparison of kinetic plots for {110} and {300} planes at two carrier densities (i.e., 1.8 × 1014 cm−2 (blue) and 2.1 × 1014 cm−2 (red)). For the lower carrier density, a fast subpicosecond single-exponential decay of the diffraction intensity is observed. For the higher carrier density, we see an additional slower decay with a lifetime of ~10 ps in addition to the fast decay. Such a complex decay of diffraction intensity was previously reported for another layered material, graphite, where it was attributed to the coexistence of electron–phonon and phonon–phonon scattering, as well as to electron–phonon coupling to two different vibration modes29,30. In our experiments, the observed crossover from single exponential to biexponential intensity decay with increasing excited charge carrier concentration (and correspondingly different potential energy surfaces) is indicative of electron–phonon coupling to one or more decay channels at low and high charge carrier densities, respectively. The other diffraction planes also reveal two contributions from the fast and the slow decay channels, and the results are presented in Supplementary Fig. 2b.
NAQMD simulation results
To interpret this ultrafast subpicosecond change of Bragg peak intensity as a function of delay time, we performed NAQMD simulations of MoSe2 bilayer in the electronically ground and excited states, respectively. Figure 3a shows the Debye–Waller factors (DWF) for the {110} (red) and {300} (blue) families of planes calculated from an ensemble of four photoexcited NAQMD atomic trajectories and compared to the Debye–Waller factors for the unexcited MoSe2 bilayer at 10 K. Single-exponential decay fits to the {110} and {300} planes show an ultrafast increase in structural disorder with time constants of ~1 ps (gray), and magnitude of DWF decay (Δ = 0.15 and 0.3) that are qualitatively consistent with experimental measurements (circles). This subpicosecond dynamics is further supported by Fig. 3b, which shows a plot of the instantaneous temperature of atoms in the simulation cell as a function of time. The calculated temperature of the simulation cell increases from the initial value of 10 K to a steady-state value of ~350 K in a lifetime scale of ~0.89 ps. Snapshots of time-resolved atomic velocity distributions at two delay times are presented in Supplementary Fig. 3 and Supplementary Note 4 to rationalize a fast equilibration of lattice temperature in our experiments.
NAQMD simulations of bilayer MoSe2. a Debye–Waller factor for the MoSe2 bilayer as a function of delay time for the {110} and {300} planes calculated from NAQMD simulations at carrier density of 0 cm−2 (black) and 1.2 × 1014 cm−2 (red and blue lines). Photoexcitation results in a marked increase in structural disorder and a reduction in the Bragg peak intensity. Exponential fits to the simulations yield a time constant of ~1 ps, as shown in the gray curves. The experimental results shown in circles are the bilayer MoSe2 at a carrier density of 1.2 × 1014 cm−2. Note that there are no normalization factors between the experimental and simulation results. b Instantaneous temperature in the NAQMD simulation cell due to photoexcitation at time t = 0 shows a transient temperature increase from 10 K to 300 K over 1.5 ps. c, d display phonon dispersion curves for the MoSe2 bilayer at the photoexcited carrier density of c 0 cm−2, (d) 1.2 × 1014 cm−2, respectively. e, f Eigenvectors for the soft acoustic modes at the M-point and K-point, respectively
To further understand the underlying ultrafast atomistic mechanisms, we calculated phonon dispersion curves as a function of electronic excitation with the method described previously for the MoSe2 bilayer. This allows us to study the effect of excited charge carrier population on the potential energy surface of the crystal. Figure 3c, d shows the phonon dispersion of the MoSe2 bilayer in the ground and excited states, respectively. Electronic excitation causes two primary differences to the potential energy surface of the crystal. First, the frequencies of atomic vibrations decrease uniformly throughout the Brillouin zone with increasing excited charge carrier concentration, reflecting a weakening of interatomic bonds leading to greater atomic displacements. Second, with increased charge carrier concentration, softening of zone-edge phonons is observed at the M (0.5,0,0) and K (0.33,0.33,0) points in the Brillouin zone. Eigenvectors corresponding to these soft modes are shown in Fig. 3e, f, respectively. The flattening of the potential energy surface corresponding to the soft vibration mode at the M-point enables in-plane displacement of Mo ions to form Mo–Mo dimer chains and is particularly important for displacements corresponding to the 2H → 1-T’ phase transition of MoTe2 37,38. Such soft modes represent an instability in the 2-H crystal structure, but do not necessarily imply a spontaneous structural transformation from the 2H to the 1-T’ crystal structure, which would require, in addition, barrierless motion of Mo and Se atoms over 0.3 Å from the 2H to the 1-T’ lattice positions. Further, the largest observed RMS displacement in our pump-probe experiments is 0.13 Å prior to the onset of irreversible sample damage, which is significantly smaller than 0.3 Å required for a structural-phase transformation. However, the existence of such softened vibration modes induced by carrier population is an indication of strong electron–phonon coupling which could enable efficient relaxation of electronic energy to the lattice39,40. Phonon softening at M and K points in electron-doped MoS2 crystals was accompanied by large electron–phonon coupling constants at these q-points41. Similarly, in materials like amorphous bismuth and gallium, the large range of motion enabled by the soft vibrations gives rise to anomalously high electron–phonon coupling constants42.
Debye–Waller responses at 800-nm photoexcitation
This strong electron–phonon coupling enables a very efficient relaxation of excited carrier energy to the lattice disorder, and this suggests that in the electron–hole plasma regime, the transient lattice temperature rise is simply proportional to the absorbed pump energy. In order to understand the impact of excited charge carrier energy on lattice dynamics, we compare the measured lattice disorder produced by the optical pumping at 400 nm to results by 800-nm photoexcitation. In particular, at 800-nm excitation, the photon energy is half of a 400-nm photon. This allows us to produce ~50% of lattice disorder and temperature jump in comparison to 400-nm photoexcitation at a similar carrier density. Indeed, from our experiments at 800 nm, we observed a strong laser-driven Bragg peak intensity decay implying that the lattice disorder results from the electron–hole plasma-driven and phonon-softening nonradiative process. The kinetics at two different pump-probe delay ranges at 800-nm photoexcitation are shown in Fig. 4a, b, respectively. We chose similar carrier densities at 800 nm compared to 400 -nm experiments. In Fig. 4a, the resulting fast time constants are on subpicosecond time scales without any apparent Q 2 and carrier density dependence, consistent with the observation at 400-nm photoexcitation. This implies that the nonthermal melting and high-order carrier kinetics do not play an important role at 800-nm photoexcitation in this carrier density regime. Note that in our experiments, the irreversible sample damage from the accumulation of quasi-stationary heating does not exist because the heat propagation to the PMMA and silicon nitride substrate occurs on a time scale of 100 ps, as shown in Fig. 4b 23, which is eight orders of magnitude shorter than the time between electron pulses (i.e., 1/180 s). This ensures that the sample target equilibrates to room temperature before the next pump-probe cycle. This is very different from a recent experiment using Raman microscopy equipped with a CW and high-repetition-rate lasers at a diffraction-limit focus (~1 µm2)43. In that experiment, the average pump power was much higher than in the experiment presented here (i.e., 1000 W per cm2 vs. 1 W per cm2), but the peak power on the other hand is much lower. This indicates that the Raman experiments are mostly susceptible to the damage from the continuous heating, while for higher peak power, the damage results from single-shot ablation. Figure 4c shows the Debye–Waller responses as a function of carrier density at 800-nm photoexcitation, which allows us to measure mean-square displacements of a bilayer, as described previously at 400-nm photoexcitation.
Pump-probe kinetics and Debye–Waller responses at 800 nm photoexcitation. a Time-resolved kinetic plots of MoSe2 bilayer for six diffraction families, as depicted in the parenthesis at a carrier density of 2.0 ± 0.2 × 1014 cm−2 excited at 800 nm. The resultant subpicosecond time constants are consistent with measurements at 400 nm. b At the same carrier density and wavelength for the bilayer with the pump-probe scan up to 100 ps. A clear recovery of Bragg peak intensity is shown (~100 ps). This is due to the heat propagation from the bilayer MoSe2 to the substrate. c Power-dependent Debye–Waller responses of a bilayer for three effective carrier densities at 800 nm photoexcitation. Error bars represent 68% confidence interval and are obtained from the propagation of standard error of the mean from the fit of averaged multiple pump-probe scans. The mean-square displacements obtained from the linear least-square fit of data are shown in Supplementary Table 3. Note that at the highest carrier density, the Debye–Waller response is still linear without a large deviation, as seen in Fig. 2c
Temperature jump from UED measurements and correlation plots
We have also performed power dependence measurements and NAQMD simulations of monolayer MoSe2 samples, as displayed in Supplementary Figs. 4 and 5 in Supplementary Notes 5 and 6, respectively. We observed qualitatively similar time constants, Debye–Waller responses, and mean-square displacements as seen in the bilayer case. A comparison of experimental results between the monolayer and bilayer is shown in Supplementary Table 3 and Supplementary Note 2. In order to calculate the temperature jump of MoSe2 from the measured mean-square displacement, we apply an equation that employs Debye model with assumptions of harmonic approximation and isotropic vibration distribution with a cutoff frequency for the estimation of density of state44. This allows us to condense the integration of various phonon modes down to a simple analytical equation, as shown in Eqs. (3)–(5)
where ħ, m, k B, and θ D are the reduced Planck constant, averaged molecular mass, Boltzmann constant, and Debye temperature of the crystal, respectively. Here, we use 84.63 g per mole and 193 K for the averaged molar mass and Debye temperature, respectively45. Equation (4), with function \(P_{\left( {\theta _{\mathrm{D}}/T} \right)}\), can be solved analytically from the known Debye temperature, as shown in Eq. (5)46. The efficiency of optical energy conversion into the thermal motion of a lattice is estimated by a comparison of temperature jump measured from the UED experiments to temperature increase calculated using absorption of the pump beam, the specific heat of the MoSe2 (S = 0.278 J per g per K)47, sample density, and volume. Detailed estimation of the temperature jumps from the absorption is presented in Supplementary Note 1. The calculated temperature jumps in a bilayer using Eqs. (3)–(5) are 116 ± 4 K, 203 ± 7 K, 269 ± 9 K, and 359 ± 25 K, respectively, corresponding to the temperatures of 414 ± 4 K, 501 ± 7 K, 567 ± 9 K, and 657 ± 25 K at four carrier densities at 400-nm optical excitation. At similar carrier densities, optical excitation by the 400-nm pump results in a larger transient lattice temperature jump than an 800-nm pump. The measured and estimated temperatures from UED and absorption, respectively, are shown in the following section. This correlation between UED results and effective absorption allows us to directly quantify the efficiency of the nonradiative channel.
Figure 5a displays UED-measured temperatures (i.e., solid circles) as a function of pump fluence. A saturable absorber model of MoSe2 is used to calculate the effective absorption48, and the corresponding temperatures (i.e., solid lines) are plotted with the UED results (circles). We note that the reported saturation intensities (I s) from Wang et al.48 are used. The predicted temperature jumps from the saturated absorption model agree qualitatively with our UED measurements. We observe a slightly faster temperature rise for the monolayer (ML) than for the bilayer (BL). This can be rationalized as an absorption difference per unit layer between the monolayer and bilayer. In addition, photoexciting the bilayer at 800 nm reveals roughly half the temperature jump in comparison to the bilayer at 400 nm. This is a result of half the energy per 800-nm photon compared to that absorbed per 400-nm photon.
Temperature correlation plots for atomically thin MoSe2. a Temperatures of atomic thin MoSe2 from UED results (solid circles) and from effective absorption calculated from a saturable absorber model (solid lines). ΔT denotes the temperature jump above room temperature (RT). ML and BL symbolize the monolayer and bilayer, respectively. Error bars in UED results denote 68% confidence interval and are obtained from propagation of standard error of the mean from the fit of averaged multiple pump-probe scans. b Correlation plot between UED results and estimates from effective absorption. The gray solid line denotes a full linear correlation, implying a unity of nonradiative quantum yield to lattice disorder. Horizontal error bars in the absorption measurements are calculated by taking into account the uncertainties of powermeter measurements and saturation intensities in ref. 48
Figure 5b displays a correlation plot between temperature changes from UED results and from estimated absorption. The experimental results from UED correlate qualitatively with the estimated temperature jump from a saturable absorber model. From this correlation, we conclude that at the high carrier density, the average quantum yield of the nonradiative process approaches unity (0.87 ± 0.11). Most of the absorbed photon energy converts to lattice vibrations within a picosecond through strong electron–phonon interaction, and this lattice disorder recovers quickly by transporting energy to the substrates on the ~100-ps time scale. In our study, the maximum displacement prior to damage is only ~5% of the in-plane lattice constant, which is still lower than the reported theoretical value of ~11.5% for a phase transition to metallic MoSe2 49.
Discussion
In summary, we have utilized MeV UED to directly probe lattice dynamics of mono- and bilayer MoSe2. At electron–hole densities in the plasma regime, the nonradiative channel of laser-driven MoSe2 reaches near-unit efficiency with a maximum atomic displacement of ~5% of the lattice constant. The lattice motions are proportional to the injected carrier density estimated from the reported saturable absorber model. The subpicosecond suppression of Bragg peak intensity and the corresponding disorder of lattice planes are supported by first-principles NAQMD simulations, indicating that the electronic excitation-induced phonon softening is a precursor to efficient dissipation of electronic energy to lattice vibrations. This strong lattice response to optical excitations has important implications for light-induced semiconductor-to-metal structural-phase transition pathways in transition metal dichalcogenides.
Methods
Sample preparation
Bilayer single-crystal MoSe2 samples were prepared by chemical vapor deposition (CVD) on Si/SiO2 substrates at 750 °C and characterized by micro-Raman spectroscopy and photoluminescence measurements (see Supplementary Fig. 6 and Supplementary Note 7 for details), which are consistent with other reported values on different substrates22. The MoSe2 samples were transferred onto a ten-nanometer-thick silicon nitride membrane employing a PMMA-assisted transfer technique.
Ultrafast electron diffraction
Diffraction experiments were performed at MeV-UED facility at SLAC National Accelerator Laboratory18. The pulsed electron beam was operated at a repetition rate of 180 Hz and an energy of 3.2 MeV. The beam with an ~40 µm rms spot size impinged on the sample in a normal incidence transmission geometry perpendicular to the (001) plane, therefore probing only in-plane lattice displacements29. The pulse duration and intensity of the electron beam were ~200 fs and ~20 fC, respectively. The MoSe2 bilayers were photoexcited with short optical laser pulses at 400 nm (3.1 eV) producing hot carriers, and at 800 nm (1.55 eV) producing band edge carriers. Charge carrier densities shown in all figures were estimated by taking into account the absorption cross section, reflectivity of MoSe2, and interfaces between the sample, PMMA, and silicon nitride membrane on a stack geometry of materials, as shown in Supplementary Fig. 1. The final absorption was then calibrated to a saturable absorber model, as shown in Supplementary Eq. 1 in Supplementary Note 1 48. The obtained absorption, reflectivity, carrier density, and temperature jump are displayed in Supplementary Tables 1 and 2.
Nonadiabatic quantum molecular dynamics
NAQMD simulations are performed on a MoSe2 bilayer supercell containing 54 atoms, corresponding to 3 × 3 unit cells of the 2-H ground-state crystal structure. Electronic states were calculated using the projector-augmented-wave (PAW) method, and projector functions were generated for 4d, 5s, and 5p states of Mo, and 3d, 4s, and 4p states of Se. The generalized gradient approximation (GGA) was used for the exchange-correlation energy with nonlinear core corrections. The GGA functionals used in this study do not include Hubbard on-site interaction correction. We have performed additional NAQMD simulations to confirm that the inclusion of the on-site interaction term (U = 2 eV) does not alter the time constant for lattice thermalization more than 0.01 ps nor the magnitude of atomic vibrations after excitation significantly. Van der Waals interactions were incorporated based on the DFT-D method. Plane-wave cutoff energies were 25 and 250 Ry for electronic pseudo-wave functions and pseudo-charge density, respectively. The energy functional was minimized iteratively using a preconditioned conjugate-gradient method. More details on the implementation of our QMD program can be found in ref. 20.
Density functional theory
DFT calculations were performed on a 3 × 3 supercell of the 2H-MoSe2 bilayer crystal structure containing 54 atoms. Valence electron wave functions are constructed using a plane-wave basis set containing components up to a kinetic energy of 450 eV, and the reciprocal space is sampled using a 7 × 7 × 3 Monkhorst–Pack k-point mesh with a Gaussian smearing of orbital occupancies of 0.1 eV. The Hessian matrix was generated using density functional perturbation theory, and dispersion relations for normal vibration modes of the MoSe2 unit cell were plotted using the open-source phonopy package50. For phonon dispersion calculations, excited states are described within the Δ-SCF DFT framework. In this scheme, a non-Aufbau constraint is imposed on orbital occupancies to promote electrons from the occupied Kohn–Sham energy levels to unoccupied higher-energy levels followed by relaxation of nuclear positions to minima in the potential energy surface defined by the charge density corresponding to the fixed occupancy of these energy levels. The Δ-SCF method is known to provide an inexpensive approximation to the potential energy surface of the excited-state system with accuracy comparable to time-dependent DFT methods51,52.
Data availability
The data that support the findings of this study are available from the corresponding author upon request.
Change history
15 August 2023
A Correction to this paper has been published: https://doi.org/10.1038/s41467-023-40538-w
References
Chakraborty, B. et al. Symmetry-dependent phonon renormalization in monolayer MoS2 transistor. Phys. Rev. B 85, 161403 (2012).
Butscher, S., Milde, F., Hirtschulz, M., Malić, E. & Knorr, A. Hot electron relaxation and phonon dynamics in graphene. Appl. Phys. Lett. 91, 203103 (2007).
Wang, H., Zhang, C., Chan, W., Tiwari, S. & Rana, F. Ultrafast response of monolayer molybdenum disulfide (MoS2) photodetectors. Nat. Commun. 6, 17–20 (2015).
Schaibley, J. R. et al. Valleytronics in 2D materials. Nat. Rev. Mater. 1, 16055 (2016).
Wang, Q. H., Kalantar-Zadeh, K., Kis, A., Coleman, J. N. & Strano, M. S. Electronics and optoelectronics of two-dimensional transition metal dichalcogenides. Nat. Nanotechnol. 7, 699–712 (2012).
Larentis, S., Fallahazad, B. & Tutuc, E. Field-effect transistors and intrinsic mobility in ultra-thin MoSe2 layers. Appl. Phys. Lett. 101, 223104 (2012).
Kumar, N. et al. Exciton-exciton annihilation in MoSe2 monolayers. Phys. Rev. B 89, 125427 (2014).
Sun, D. et al. Observation of rapid exciton-exciton annihilation in monolayer molybdenum disulfide. Nano Lett. 14, 5625–5629 (2014).
Yu, Y. et al. Fundamental limits of exciton-exciton annihilation for light emission in transition metal dichalcogenide monolayers. Phys. Rev. B 93, 201111 (2016).
Wang, H., Zhang, C. & Rana, F. Ultrafast dynamics of defect-assisted electron-hole recombination in monolayer MoS2. Nano Lett. 15, 339–345 (2015).
Wang, H. et al. Fast exciton annihilation by capture of electrons or holes by defects via Auger scattering in monolayer metal dichalcogenides. Phys. Rev. B 91, 165411 (2015).
Mak, K. F., Lee, C., Hone, J., Shan, J. & Heinz, T. F. Atomically thin MoS2: a new direct-gap semiconductor. Phys. Rev. Lett. 105, 136805 (2010).
Defo, R. K. et al. Strain dependence of band gaps and exciton energies in pure and mixed transition-metal dichalcogenides. Phys. Rev. B 94, 155310 (2016).
Shen, T., Penumatcha, A. V. & Appenzeller, J. Strain engineering for transition metal dichalcogenides based field effect transistors. ACS Nano 10, 4712–4718 (2016).
Amani, M. et al. Near-unity photoluminescence quantum yield in MoS2. Science 350, 1065–1068 (2015).
Han, H.-V. et al. Photoluminescence enhancement and structure repairing of monolayer MoSe2 by hydrohalic acid treatment. ACS Nano 10, 1454–1461 (2016).
Ruppert, C., Chernikov, A., Hill, H. M., Rigosi, A. F. & Heinz, T. F. The role of electronic and phononic excitation in the optical response of monolayer WS2 after ultrafast excitation. Nano Lett. 17, 644–651 (2017).
Weathersby, S. P. et al. Mega-electron-volt ultrafast electron diffraction at SLAC national accelerator laboratory. Rev. Sci. Instrum. 86, 73702 (2015).
Shimamura, K. et al. Hydrogen-on-demand using metallic alloy nanoparticles in water. Nano Lett. 14, 4090–4096 (2014).
Shimojo, F. et al. A divide-conquer-recombine algorithmic paradigm for large spatiotemporal quantum molecular dynamics simulations. J. Chem. Phys. 140, 18A529 (2014).
Meng, S. & Kaxiras, E. Mechanisms for ultrafast nonradiative relaxation in electronically excited eumelanin constituents. Biophys. J. 95, 4396–4402 (2008).
Ugeda, M. M. et al. Giant bandgap renormalization and excitonic effects in a monolayer transition metal dichalcogenide semiconductor. Nat. Mater. 13, 1091–1095 (2014).
Mannebach, E. M. et al. Dynamic structural response and deformations of monolayer MoS2 visualized by femtosecond electron diffraction. Nano. Lett. 15, 6889–6895 (2015).
Steinhoff, A., Rosner, M., Jahnke, F., Wehling, T. O. & Gies, C. Influence of excited carriers on the optical and electronic properties of MoS2. Nano Lett. 14, 3743–3748 (2014).
Chernikov, A., Ruppert, C., Hill, H. M., Rigosi, A. F. & Heinz, T. F. Population inversion and giant bandgap renormalization in atomically thin WS2 layers. Nat. Photonics 9, 466–470 (2015).
Nie, Z. et al. Ultrafast carrier thermalization and cooling dynamics in Few-Layer MoS2. ACS Nano 8, 10931–10940 (2014).
Qiu, D. Y., da Jornada, F. H. & Louie, S. G. Screening and many-body effects in two-dimensional crystals: Monolayer MoS2. Phys. Rev. B 93, 235435 (2016).
Wang, H., Zhang, C. & Rana, F. Surface recombination limited lifetimes of photoexcited carriers in Few-Layer transition metal dichalcogenide MoS2. Nano Lett. 15, 8204–8210 (2015).
Chatelain, R. P., Morrison, V. R., Klarenaar, B. L. M. & Siwick, B. J. Coherent and incoherent electron-phonon coupling in graphite observed with radio-frequency compressed ultrafast electron diffraction. Phys. Rev. Lett. 113, 235502 (2014).
Harb, M. et al. Phonon-phonon interactions in photoexcited graphite studied by ultrafast electron diffraction. Phys. Rev. B 93, 104104 (2016).
Lundberg, M. The crystal structure of MoSe2. Acta. Crystallogr. 16, 1183 (1963).
Sokolowski-Tinten, K. et al. Femtosecond X-ray measurement of coherent lattice vibrations near the Lindemann stability limit. Nature 422, 287–289 (2003).
Lindenberg, A. M. et al. Atomic-Scale visualization of inertial dynamics. Science 308, 392–395 (2005).
Gaffney, K. J. et al. Observation of structural anisotropy and the onset of liquidlike motion during the nonthermal melting of InSb. Phys. Rev. Lett. 95, 125701 (2005).
Sciaini, G. et al. Electronic acceleration of atomic motions and disordering in bismuth. Nature 458, 56–59 (2009).
Bader, S. D., Sinha, S. K., Schweiss, B. P. & Renker, B. in Superconductivity in Ternary Compounds I : 223–239 (Springer-Verlag, Berlin Heidelberg, 1982).
Keum, D. H. et al. Bandgap opening in few-layered monoclinic MoTe2. Nat. Phys. 11, 482–486 (2015).
Kolobov, A. V., Fons, P. & Tominaga, J. Electronic excitation-induced semiconductor-to-metal transition in monolayer MoTe2. Phys. Rev. B 94, 94114 (2016).
Allen, P. B. & Cohen, M. L. Superconductivity and phonon softening. Phys. Rev. Lett. 29, 1593–1596 (1972).
Moussa, J. E. & Cohen, M. L. Two bounds on the maximum phonon-mediated superconducting transition temperature. Phys. Rev. B 74, 94520 (2006).
Zeng, S., Zhao, Y., Li, G. & Ni, J. Strongly enhanced superconductivity in doped monolayer MoS2 by strain. Phys. Rev. B 94, 24501 (2016).
Poole, C., Farach, H. & Creswick, R. Handbook of Superconductivity. Ch 9 (Academic Press, 2000).
Cadiz, F. et al. Ultralow power threshold for laser induced changes in optical properties of 2D Molybdenum dichalcogenides. 2D Mater. 3, 45008 (2016).
Als-Nielsen, J. & McMorrow, D. Elements of Modern X-ray Physics: 2nd Edn. (WILEY, Chichester, 2011).
Liu, Y. et al. Thermally driven (Mo, W)-(S2, Se2) phonon and photon energy relaxation dynamics. J. Phys. Chem. C 119, 25071–25076 (2015).
Hardy, K. A., Parker, F. T. & Walker, J. C. A better approximation to the Debye-Waller factor. Nucl. Instrum. Methods 86, 171–172 (1970).
Kiwia, H. L. & Westrum, E. F. Low-temperature heat capacities of molybdenum diselenide and ditelluride. J. Chem. Thermodyn. 7, 683–691 (1975).
Wang, K. et al. Broadband ultrafast nonlinear absorption and nonlinear refraction of layered molybdenum dichalcogenide semiconductors. Nanoscale 6, 10530–10535 (2014).
Yun, W. S., Han, S. W., Hong, S. C., Kim, I. G. & Lee, J. D. Thickness and strain effects on electronic structures of transition metal dichalcogenides: 2H-MX2 semiconductors (M = Mo,W; X = S,Se,Te). Phys. Rev. B 85, 33305 (2012).
Togo, A. & Tanaka, I. First principles phonon calculations in materials science. Scr. Mater. 108, 1–5 (2015).
Gavnholt, J., Olsen, T., Engelund, M. & Schiøtz, J. Δ self-consistent field method to obtain potential energy surfaces of excited molecules on surfaces. Phys. Rev. B 78, 75441 (2008).
Kowalczyk, T., Yost, S. R. & Van Voorhis, T. Assessment of the ΔSCF density functional theory approach for electronic excitations in organic dyes. J. Chem. Phys. 134, 54128 (2011).
Acknowledgements
This work was supported as part of the Computational Materials Sciences Program funded by the U.S. Department of Energy, Office of Science, and Basic Energy Sciences, under Award Number DE-SC00014607. The UED work was performed at SLAC MeV-UED, which is supported in part by the DOE BES SUF Division Accelerator & Detector R&D program, the LCLS Facility, and SLAC under contract Nos. DE-AC02-05-CH11231 and DE-AC02-76SF00515. Simulations were performed at the Argonne Leadership Computing Facility under the DOE INCITE program at the Center for High Performance Computing of the University of Southern California and the Extreme Science and Engineering Discovery Environment (XSEDE), which is supported by National Science Foundation grant number ACI-1548562. The authors would like to thank Prof. Aaron Lindenberg and Dr. Ehern Mannebach for their valuable discussions of data analysis in electron diffraction.
Author information
Authors and Affiliations
Contributions
A.N., D.M.F., P.A., P.V., R.K. and U.B.: Designed the research. V.K., X.Z., A.A., C.S.T. and P.A.: Synthesized and characterized the experimental samples. C.W., M.-F.L., Q.Z., R.L. and X.W.: Performed the UED experiment. A.K., A.N., F.S., L.B.O., P.V. and R.K.: Performed ab initio calculations. All authors contributed to the analysis, discussion, and preparation of the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Lin, MF., Kochat, V., Krishnamoorthy, A. et al. Ultrafast non-radiative dynamics of atomically thin MoSe2. Nat Commun 8, 1745 (2017). https://doi.org/10.1038/s41467-017-01844-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-017-01844-2
- Springer Nature Limited
This article is cited by
-
Ultrafast reversible phase engineering in MoTe2 thin film via polaron formation
Journal of the Korean Physical Society (2024)
-
Engineering Materials at the Atomic Scale for Energy, Environment and Health-Care Applications
Transactions of the Indian National Academy of Engineering (2023)
-
Bidirectional phonon emission in two-dimensional heterostructures triggered by ultrafast charge transfer
Nature Nanotechnology (2023)
-
Anisotropic structural dynamics of monolayer crystals revealed by femtosecond surface X-ray scattering
Nature Photonics (2019)