Abstract
Although semiconductor excitons consist of a fermionic subsystem (electron and hole), they carry an integer net spin similar to Cooper-electron-pairs. While the latter cause superconductivity by forming a Bose–Einstein-condensate, excitonic condensation is impeded by, for example, a fast radiative decay of the electron-hole pairs. Here, we investigate the behaviour of two electron-hole pairs in a quantum dot with wurtzite crystal structure evoking a charge carrier separation on the basis of large spontaneous and piezoelectric polarizations, thus reducing carrier overlap and consequently decay probabilities. As a direct consequence, we find a hybrid-biexciton complex with a water molecule-like charge distribution enabling anomalous spin configurations. In contrast to the conventional-biexciton complex with a net spin of s=0, the hybrid-biexciton exhibits s=±3, leading to completely different photoluminescence signatures in addition to drastically enhanced charge carrier-binding energies. Consequently, the biexcitonic cascade via the dark exciton can be enhanced on the rise of temperature as approved by photon cross-correlation measurements.
Similar content being viewed by others
Introduction
Excitons carry a net spin of either 1 or 2 and are regarded as bosons. Their condensation into one macroscopic wave function1,2, however, is hampered by a couple of obstacles—to mention two of them, the fermionic substructure impairing the transition temperature3,4 and the frequently fast radiative decay5,6. The latter can be cured by a spatial separation of the electron and hole subsystem, either using two coupled quantum wells with a superposed electric field7,8 or by a single quantum well with a strong inherent electric field induced by the piezo- and/or pyroelectricity of the crystal lattice9,10,11,12. Depending on the size of the vertical charge carrier separation, the excitons exhibit a significant dipole character, thus introducing repulsive dipole–dipole interactions that hinder the formation of multiple exciton complexes.
In the case of quantum dots (QDs), the confinement along all three directions in space completely alters this picture. First of all, the confined excitonic complexes are not anymore primarily bound together by Coulomb interaction; their possible dissociation is prevented by the surrounding confinement potential13. As a result, a large number of excitonic and charged excitonic complexes can easily form, almost regardless of the binding energies between the component particles14,15. Only for QDs in the strong confinement regime16,17,18, a biexciton (XX) in its ground state consists of two electrons and two holes occupying the lowest electron and hole orbitals, each with paired spins. The total spin of the resulting XX is s=0 and this boson can decay into one of the two bright exciton (X) states with s=±1 (refs 19, 20, 21). Consequently, two pairwise cross-linearly polarized, double-peak signatures are characteristic for the decay cascade XX→X→empty QD state22,23. Such signatures are routinely analysed to support the identification of excitons and biexcitons in micro-photoluminescence (μ-PL) spectroscopy13,24,25. However, for the majority of wurtzite c-plane GaN/AlN QDs26,27 with diameters larger than ≈6 nm, this picture cannot be valid anymore for the following reasons. The strong internal piezo- and pyroelectric fields separate the electron- from the hole-subsystem and cause a very distinct confinement in the growth-direction (c-axis) for both charge carrier types. Along lateral directions, the electrons are still subject to a strong confinement in contrast to the weakly confined holes, with their large effective hole mass reducing their effective Bohr-radius a*:=(me/m*)εra0 (refs 16, 17, 18) representing a convenient measure for the critical confinement length of orbital formation. Consequently, no significant orbital structure for holes is present anymore in this, so-called hybrid-XX complex, and Coulomb forces (in particular, the hole–hole repulsion and the exchange interaction) become dominant. Hence, laterally separated hole states with parallel spins are energetically more favourable than those exhibiting antiparallel spins as in the case of strong confinement.
In this work, we present our theoretical predictions along with experimental evidence for the formation of such a hybrid-XX system with a net spin of s=±3. This specific spin configuration leads to an energetic luminescence transposition between the bright X and hybrid-XX emission, as the strong repulsive dipole–dipole interaction in the hybrid-XX is naturally counterbalanced by the hole–hole exchange interaction and large correlation effects as approved by our accurate multi-particle interaction calculations. The radiative decay sequence of such a hybrid-XX is, due to angular momentum conservation, fundamentally different if compared with the one of conventional biexcitons with s=0. As its intermediate state is one of the dark excitons (s=±2) instead of the bright excitons (s=±1), the first decay stage (XX→X) is strongly altered and requires a spin reversal to proceed to the second stage (X→empty QD). Hence, the entire photoluminescence signature of the hybrid-XX reflects its decay via the dark excitons as approved by our temperature-dependent photon cross-correlation analysis and the underlying photoluminescence spectra along with their particular polarization dependence. On the basis of the presented spectroscopic analysis, we can derive all energetic level spacings involved in the hybrid-XX decay cascade in well agreement with our theoretical predictions, yielding a coherent description for this first member in the class of hybrid-quasiparticles.
Results
Extreme biexciton binding energies due to separate hole densities
As depicted in Fig. 1, the spatial separation of confined electrons and holes (a) reduces their charge-related, attractive Coulomb interaction (blue) and their spin-related, repulsive exchange interaction (red). For the conventional-XX complex in Fig. 1b, additional repulsive (red)/attractive (blue) Coulomb interactions between the charge carriers exist. Our simulations of the XX reveal a Coulomb repulsion, which overcomes the lateral confinement of the holes, leading to a separated localization of the hole wave functions at the bottom of the QD (Fig. 1c). The XX accordingly forms a hybrid system of two electrons sharing one orbital at the top, and two spatially separated holes at the bottom of the QD. In this configuration, the holes can have parallel spins, thus, reducing the energy of the hybrid-XX via the hole–hole exchange interaction (blue). Owing to the reduced hole–hole Coulomb repulsion and the additional attractive hole–hole exchange interaction (compare Fig. 1), the total energy of the hybrid-XX is drastically decreased.
A summary of our theoretical and experimental XX-binding energies (X emission energy minus XX emission energy) is given in Fig. 2. Here, the red circles mark the calculated XX-binding energies for a set of QDs assuming a constant QD aspect ratio (ar=height/diameter) of 0.2 and a reduced volume with increasing emission energy. Atomic force microscopy and transmission electron microscopy studies confirm such QD aspect ratios between 0.1 and 0.2 (refs 28, 29, 30) for wurtzite GaN/AlN QDs. Therefore, the assumption of ar=0.2 (red circles in Fig. 2) approaches a lower limit for common XX-binding energies, plotted here versus the calculated values of the X emission energies. According to the microscopic analysis, the QDs are modelled as truncated hexagonal pyramids of varying height (h=0.8–2.4 nm), including a 0.2-nm thick GaN-wetting layer. Our previous results about the excitonic fine-structure splitting31 show that the QDs have a broken C3v symmetry, here due to an in-plane diameter asymmetry of 20%. Grey dots (metalorganic chemical vapour deposition (MOCVD) growth) and circles (molecular beam epitaxy (MBE) growth15) represent measured XX-binding energies of GaN/AlN QDs in Fig. 2. Our theoretical results for ar=0.2 nicely match the results for MBE grown QDs and reproduce the sign change of the XX-binding energy, whereas they slightly underestimate the results for MOCVD grown QDs. QD growth kinetics and, thus, the resulting geometries of QDs are known to be different between MBE and MOCVD32 owing to the fundamentally different growth temperatures. However, the spread of the MOCVD results can be well described by doubling the QD diameter towards ar=0.1, marked by green arrows and the blue line in Fig. 2, indicating a grid for future explorations.
Calculations within the conventional-XX model for small QDs with an aspect ratio of 0.33 as shown in ref. 33 (Fig. 2, black squares) could not explain the significant zero-crossing of the XX-binding energies34, not to mention positive XX-binding energies of up to 30 meV and beyond for even flatter QDs. Our calculations use the same material parameters as refs 33, 35, without any artificial reductions of the built-in polarization fields as suggested therein. However, owing to the very large aspect ratios of the model QDs discussed in refs 33, 35, all these QDs correspond to the conventional-XX regime of strong confinement. Our non-restricted Hartree–Fock calculations in combination with our experimental evidence predict different biexcitonic regimes, which are marked by coloured areas in Fig. 2: the conventional-XX (red) for QD diameters ≲6 nm, the hybrid-XX (green) with weakly confined holes for QD diameters ≳6 nm. For QD diameters ≳12 nm, the electrons and holes encounter weak lateral confinement followed by a transition into the quantum-well XX regime without significant lateral confinement. However, please note that the depicted XX-regimes lack well-defined border lines (indicated by colour fading) owing to the wide range of structural QD parameters and are meant for rough orientation only. The orbitals, forming the hybrid-XX, have been calculated by the Hartree–Fock method (see the Simulation Methods subsection and the corresponding isosurfaces of the converged hole densities in Fig. 3b). The height of the QD can additionally influence this critical diameter, as a smaller electron-hole separation leads to a stronger lateral confinement of the holes by the attraction of the electrons. Prior two-dimensional studies of electron interactions in QDs36,37,38,39,40 raised the question whether a Wigner molecule (of electrons) is reliably described within the unrestricted Hartree–Fock method, allowing for symmetry-broken solutions41. Our study uses such a (here three-dimensional) Hartree–Fock method (see the Simulation Methods subsection), which predicts a Wigner molecule-like hole separation within the hybrid-XX model. Therefore, our method might underestimate the minimum QD diameters required for the observed lateral hole separation. However, the agreement between our theoretical and experimental data confirms the entire hybrid-XX model. Although the situation with one strongly and one weakly confined charge carrier type is similar to the situation we found in type II QDs42, a (relative to the dark X) negative XX-binding energy would prevent the formation of a XX in such QDs.
Spin properties of confined particles
The aligned hole spins of the hybrid-XX cause a total spin of s=±3 (neglecting band-intermixing effects). Therefore, the hybrid-XX can radiatively decay into the dark X states, exhibiting total spins of ±2, comparing Fig. 3a with Fig. 3b. As the electron-hole exchange interaction of symmetry-broken wave functions does not lead to a splitting of the dark X states, in contrast to the bright X states, such dark X states are expected to show a significantly smaller splitting than the bright X states of wurtzite GaN/AlN QDs (with measured bright X fine-structure splittings of 2–7 meV (ref. 31); compare the corresponding calculations within Supplementary Fig. 1(c)). Therefore, the emitted photons of the hybrid-XX show a smaller energetic splitting than expected for a conventional-XX, showing the same splitting as the bright X states13,22,23,24,25,43. Owing to the large total spin of s=±3, μ-PL experiments within magnetic fields should reveal a field strength-dependent fourfold splitting of the hybrid-XX emission line, caused by the splitting of the hybrid-XX states and the dark X states, which will become optically active. Observing such a splitting will be challenging due to the large-emission linewidths44 but seems achievable based on recent growth advances. However, even without the application of a magnetic field, one can already indirectly witness the anomalous cascade process via the dark states by a straight-forward polarization-dependent μ-PL measurement. A careful analysis of such spectra yields a polarization-dependent shift of the hybrid-XX emission line (Fig. 3c) along with a periodic intensity variation, yielding an estimate for the dark X splitting of 270±50 μeV. The corresponding bright X states show a ≈16 times larger splitting of 4.3±0.2 meV as shown in Fig. 4a. A direct comparison between our theoretical and experimental results concerning the polarization of the emission is shown in Fig. 4 for a QD with an emission energy around 4 eV. The depicted contour plots show μ-PL spectra depending on the polarization angle. On top of each contour plot, two single spectra for orthogonal polarization angles are plotted versus the emission energy, demonstrating the fully linear polarization of the bright X states luminescence (X1, X2). The intensities for the corresponding emission lines are plotted versus the polarization angle on the right side of each contour plot for a better identification of the polarization angle-dependent emission maxima. The overlap of two fully cross-polarized XX emission lines in Fig. 4a is mimicking a single, partially polarized emission line31. This observation can directly be confirmed by our simulated spectra (b) of the QD structure belonging to the upper green data point in Fig. 2, which corresponds to an aspect ratio of 0.1 and a biexciton binding energy of ≈28 meV at an emission energy of 4.08 eV. We can observe a striking agreement between experiment and theory that already supports the identification of the hybrid-XX. The only parameters that had to be matched to the experiment for the simulation are the linewidth induced by spectral diffusion44,45 and the particular excitation power and temperature dependencies, varying the intensity balance between X1, X2, XX as shown in Supplementary Figs 2 and 3. Neither material nor geometric QD parameters were varied to approach the measurement causing the apparent slight discrepancies for the luminescence energies. Therefore, also the bright X states show a QD anisotropy-dependent smaller fine-structure splitting of ≈1 meV in the simulations and a slightly larger hybrid XX-binding energy. The visible emission energy variations of the measured emission lines (a) during the polarization angle scan are caused by the spectral diffusion in GaN/AlN QDs44,45, which can be suppressed by lowering the temperature, sacrificing the intensity balance of the bright exciton states (see Fig. 5).
Thermal occupation of exciton spin states
Temperature-dependent μ-PL measurements (Fig. 5) reveal the thermal activation of the bright exciton states (X1, X2) due to phonon-mediated spin-flip processes46, transferring the carriers between the dark and the bright exciton states. By comparing the overall exciton intensity with its biexciton counterpart in an Arrhenius plot (Fig. 5b), one determines an activation energy (EDB) of 1.0±0.3 meV resembling the average excitonic dark–bright splitting. Interestingly, the sole thermal activation of X2 in regard to X1 is a two-step process as shown in Fig. 5c. On the basis of a simple Arrhenius fit47, we extract two activation energies: EDB*=0.9±0.4 meV, again matching the average excitonic dark–bright splitting; and EBB=5.1±0.8 meV, implying the much larger fine-structure splitting of the bright exciton states. Therefore, both Arrhenius plots independently deduce EDB, in line with the theoretical prediction of an average dark–bright splitting of 0.81 meV, strongly scaling with the QD volume as demonstrated in Supplementary Fig. 1.
The thermal activation of the excitonic emission lines evidences the existence of efficient phonon-mediated spin-flip processes46 within GaN/AlN QDs. This explains the stronger X1 in comparison with X2 emission in Fig. 4, despite a much larger oscillator strength of X2 depending on the amount of fine-structure splitting between X1 and X2 (ref. 31). In addition, this unbalance in the oscillator strengths explains the observations of EDB* in the low-temperature regime of Fig. 5c. The dark X states as the final states of the initial hybrid-XX decay are expected to be long-time stable until additional carriers are captured by the QD or a phonon-mediated spin flip to a bright X state takes place as illustrated in Fig. 3b. The latter process must be efficient to explain the occurrence of intense X emission besides the hybrid-XX emission. Excitonic spin-flip times of QDs in the order of ps have already been reported48 and acoustic phonon coupling to excitons in GaN/AlN QDs is exceptionally strong49,50.
The most direct and suggestive proof for the occurrence of phonon-mediated spin-flip processes arises from temperature-dependent second-order correlation functions. At a temperature of 30 K (Fig. 6a), one observes the typical signature of a cascade process arising from the decay of the hybrid XX (start) to the ground state via the dark and bright X states (stop). By lowering the temperature to 8 K (Fig. 6b), one can efficiently suppress the phonon-mediated spin-flip processes, yielding the typical cross-correlation signature of a XX cascade via an additional intermediate level51 governing the decay dynamics. Here, the hybrid-XX decay rate (R1) is enhanced in comparison with the exciton decay rate (R2*), which is limited by the spin-flip rate from the dark into the bright states. Details regarding the convoluted fitting routine30,52,53,54 can be found in the Supplementary Note 2. Identical excitation conditions at 30K equalize R1 and R2*, proving the existence of a phonon-limited hybrid-XX cascade including a transition from the dark to the bright X states. The apparent temporally broad (≈±25 ns) bunching phenomenon in both correlation functions arises from spectral diffusion44,45 and is modelled as described by Sallen et al.55. Further standard techniques for the identification of QD emission lines are discussed in Supplementary Note 2. Consequently, a phonon-limited hybrid XX→dark X→bright X→empty QD emission cascade is witnessed at low temperatures, which is activated on the rise of temperature.
In some of the single-QD spectra, we found additional emission lines that we tentatively assign to charged excitonic complexes by comparison with our artificial polarization spectra (see Supplementary Fig. 4). A positively charged X (+X) is expected to show the same spatial hole separation as the hybrid XX. Therefore, all hole and electron spins are expected to align parallel to each other, due to the exchange interaction. The two possible +X ground states with total spins of s=±1/2±3/2±3/2=±3.5 are degenerate and exhibit a high resistance against spin dephasing, which makes the +X in GaN/AlN QDs extremely interesting for quantum-computing applications. The preparation and reading of the +X spin states should be possible in future polarized photon absorption and emission experiments.
Methods
Experimental details
The wurtzite GaN QDs grow by means of low-pressure metal-organic vapour deposition at a density of ≈6 × 109 cm−2. A detailed description of the growth conditions can be found elsewhere44,53,56,57. The sample's mesa structures (200 nm–2 μm diameter) were processed by means of e-beam lithography and plasma etching to enable single-QD spectroscopy. We used a frequency-quadrupled solid-state laser emitting at 266 nm as excitation source for the μ-PL spectra. For the temperature-dependent μ-PL measurements, the sample was situated in a Helium flow cryostat and its luminescence was dispersed by a single monochromator equipped with a charge-coupled device array. The optical resolution of this system is better than 200 μeV at a photon energy of 4 eV. A super-achromatic λ/2-waveplate in combination with a linear polarizer (contrast better than 1:5000) was used for measuring the polarization-dependent μ-PL spectra at a constant integration time of 60 s and an angular resolution of 10°. All spectra were calibrated with a mercury gas discharge lamp. For the second-order correlation measurements, the light was guided towards a non-polarizing beam splitter before each light beam was dispersed by an individual monochromator, exhibiting a variable bandpass (optical resolution better than 1meV at a photon energy of 4 eV). The light was finally detected by bialkali photomultiplier tubes with a measured biphoton time resolution of 225 ps. Conventional photon counting electronics were used to obtain the final histograms.
Simulation methods
The calculation is based on the 8-band-kp formalism described in ref. 58 including the influences of strain, pyroelectricity and piezoelectricity as well as spin orbit and crystal-field splitting. The material parameters from refs 59, 60 have been included as described in ref. 61. The sign of one of the piezoelectric constants has been corrected as described in ref. 33 based on the discussions in refs 62, 63, see summarizing Supplementary Table 1. For the calculation of the multi-particle interaction energies, the configuration interaction (CI) method is applied. This method is in principle an exact computation method, yielding the true multi-particle energies, if the number of basis states reaches infinity. Smaller basis sizes produce approximated energies for the respective excitonic complex. Besides the number of states (here we use 10 electron and 20 hole states), the quality of the approximation is sensitive to the quality of the basis states. Instead of single-particle basis states, which were used in a previous 8-band-kp study of GaN/AlN QDs33,35, we use Hartree–Fock states, representing the best possible basis states for a CI calculation. Hartree–Fock states fully include renormalization effects of particle wave functions by calculating the mean Coulomb and exchange interaction potentials iteratively. Therefore, our CI calculations only need to treat additional correlation effects, enabling us to differentiate between the contributions of renormalization and correlation effects to the particle interaction energies (see Supplementary Note 1). By including all interactions of the confined particles, our results are as exact as an 8-band-kp approach can be. As we additionally use realistic geometries for our model QDs, our simulations well describe the experimental observations.
Additional information
How to cite this article: Hönig, G. et al. Manifestation of unconventional biexciton states in quantum dots. Nat. Commun. 5:5721 doi: 10.1038/ncomms6721 (2014).
References
Einstein, A. Quantentheorie des einatomigen idealen gases. Quantum theory of the monatomic ideal gas. inSitzungsberichte der Preussischen Akademie der Wissenschaften (Berlin), Physikalisch-mathematische Klasse, Schilpp 185 261–267 (1924).
Einstein, A. Zur Quantentheorie des idealen gases. 2. Abhandlung. Quantum theory of the monatomic ideal gas, Part II. inSitzungsberichte der Preussischen Akademie der Wissenschaften (Berlin), Physikalisch-mathematische Klasse, Schilpp 194 3–14 (1925).
Blatt, J. M., Böer, K. W. & Brandt, W. Bose-Einstein condensation of excitons. Phys. Rev. 126, 1691 (1962).
Eisenstein, J. P. & Macdonald, a. H. Bose-Einstein condensation of excitons in bilayer electron systems. Nature 432, 691–694 (2004).
Roussignol, P., Heller, W., Filoramo, a. & Bockelmann, U. Time-resolved spectroscopy of single quantum dots. Physica E Low dimens. Syst. Nanostruct. 2, 588–593 (1998).
Zwiller, V. et al. Time-resolved studies of single semiconductor quantum dots. Phys. Rev. B 59, 5021–5025 (1999).
Chen, Y. J., Koteless, E. S., Elman, B. S. & Armiento, C. A. Effect of electric fields on excitons in a coupled double-quantum-well structure. Phys. Rev. B 36, 4562–4565 (1987).
Fukuzawa, T., Mendez, E. E. & Hong, J. M. Phase transition of an exciton system in GaAs coupled quantum wells. Phys. Rev. Lett. 64, 3066–3069 (1990).
André, R. et al. Optical studies of the piezolectric effect in (111)-oriented CdTe/Cd1-xZnxTe strained quantum wells. Phys. Rev. B 42, R392–R395 (1990).
Bernardini, F., Fiorentini, V. & Vanderbilt, D. Spontaneous polarization and piezoelectric constants of III-V nitrides. Phys. Rev. B 56, R10024–R10027 (1997).
Im, J. S. et al. Reduction of oscillator strength due to piezoelectric fields in GaN/AlxGa1-xN quantum wells. Phys. Rev. B 57, R9435–R9438 (1998).
Takeuchi, T. et al. Determination of piezoelectric fields in strained GaInN quantum wells using the quantum-confined Stark effect. Appl. Phys. Lett. 73, 1691 (1998).
Rodt, S. et al. Repulsive exciton-exciton interaction in quantum dots. Phys. Rev. B 68, 035331 (2003).
Seguin, R. et al. Multi-excitonic complexes in single InGaN quantum dots. Appl. Phys. Lett. 84, 4023 (2004).
Simeonov, D., Dussaigne, A., Butté, R. & Grandjean, N. Complex behavior of biexcitons in GaN quantum dots due to a giant built-in polarization field. Phys. Rev. B 77, 75306 (2008).
Efros, A. L. Interband absorption of light in a semiconductor sphere. Sov. Phys. Semiconduct. 16, 772–775 (1982).
Banyai, L., Hu, Y. Z., Lindberg, M. & Koch, S. W. Third-order optical nonlinearities in semiconductor microstructures. Phys. Rev. B 38, 8142–8153 (1988).
Que, W. Excitons in quantum dots with parabolic confinement. Phys. Rev. B 45, 11036–11041 (1992).
Bassani, G. F. & Parravicini, G. P. Electronic states and optical transitions in solids. International series of monographs in the science of the solid state Pergamon Press (1975).
Bayer, M. et al. Electron and hole g factors and exchange interaction from studies of the exciton fine structure in In 0 . 60 Ga 0 . 40 As quantum dots. Phys. Rev. Lett. 82, 1748–1751 (1999).
Bester, G., Nair, S. & Zunger, A. Pseudopotential calculation of the excitonic fine structure of million-atom self-assembled In1-xGaxAs/GaAs quantum dots. Phys. Rev. B 67, 161306 (2003).
Kulakovskii, V. D. et al. Fine structure of biexciton emission in symmetric and asymmetric CdSe/ZnSe single quantum dots. Phys. Rev. Lett. 82, 1780–1783 (1999).
Stier, O., Grundmann, M. & Bimberg, D. Electronic and optical properties of strained quantum dots modeled by 8-band kp theory. Phys. Rev. B 59, 5688 (1999).
Seguin, R. et al. Size-dependent fine-structure splitting in self-organized InAs/GaAs quantum dots. Phys. Rev. Lett. 95, 257402 (2005).
Akopian, N. et al. Entangled photon pairs from semiconductor quantum dots. Phys. Rev. Lett. 96, 130501 (2006).
Tanaka, S., Iwai, S. & Aoyagi, Y. Self-assembling GaN quantum dots on AlxGa1-xN surfaces using a surfactant. Appl. Phys. Lett. 69, 4096–4098 (1996).
Daudin, B. et al. Stranski-Krastanov growth mode during the molecular beam epitaxy of highly strained GaN. Phys. Rev. B 56, 7069 (1997).
Coraux, J. et al. Mechanism of GaN quantum dots capped with AlN: an AFM, electron microscopy, and x-ray anomalous diffraction study. Phys. Rev. B 74, 1–7 (2006).
Daudin, B. Polar and nonpolar GaN quantum dots. J Phys. 20, 473201 (2008).
Kindel, C. H. Study on Optical Polarization in Hexagonal Gallium Nitride Quantum Dots (PhD thesis (2010).
Kindel, C. et al. Exciton fine-structure splitting in GaN/AlN quantum dots. Phys. Rev. B 81, 241309 (2010).
Shchukin, V. A. & Bimberg, D. Spontaneous ordering of nanostructures on crystal surfaces. Rev. Mod. Phys. 71, 1125–1171 (1999).
Tomić, S. & Vukmirović, N. Excitonic and biexcitonic properties of single GaN quantum dots modeled by 8-band kp theory and configuration-interaction method. (2009); erratumPhys. Rev. B 86, 159902(E) (2012).
Callsen, G. et al. Steering photon statistics in single quantum dots: From one- to two-photon emission. Phys. Rev. B 87, 245314 (2013).
Tomić, S. & Vukmirović, N. Excitonic and biexcitonic properties of single GaN quantum dots modeled by 8-band kp theory and configuration-interaction method. Phys. Rev. B 79, 245330 (2009).
Yannouleas, C. & Landman, U. Spontaneous symmetry breaking in single and molecular quantum dots. Phys. Rev. Lett. 82, 5325–5328 (1999).
Yannouleas, C. & Landman, U. Erratum: Spontaneous symmetry breaking in single and molecular quantum dots. [Phys. Rev. Lett. 82, 5325 (1999) J. Phys. Rev. Lett. 85, 2220–2220 (2000).
Egger, R., Häusler, W., Mak, C. & Grabert, H. Crossover from Fermi liquid to Wigner molecule behavior in quantum dots. Phys. Rev. Lett. 82, 3320–3323 (1999).
Egger, R., Häusler, W., Mak, C. & Grabert, H. Erratum: Crossover from Fermi liquid to Wigner molecule behavior in quantum dots. [Phys. Rev. Lett. 82, 3320 (1999) J. Phys. Rev. Lett. 83, 462–462 (1999).
Reimann, S. M., Koskinen, M., Manninen, M. & Carlo, Q. M. Formation of Wigner molecules in small quantum dots. Phys. Rev. B 62, 8108–8113 (2000).
Reusch, B., Häusler, W. & Grabert, H. Wigner molecules in quantum dots. Phys. Rev. B 63, 113313 (2001).
Hayne, M. et al. Electron localization by self-assembled GaSb/GaAs quantum dots. Appl. Phys. Lett. 82, 4355 (2003).
Mlinar, V. & Zunger, A. Internal electronic structure and fine structure of multiexcitons in semiconductor quantum dots. Phys. Rev. B 80, 205311 (2009).
Kindel, C. et al. Spectral diffusion in nitride quantum dots: Emission energy dependent linewidths broadening via giant built-in dipole moments. Phys. Status Solidi 8, 408–413 (2014).
Hönig, G. et al. Identification of electric dipole moments of excitonic complexes in nitride-based quantum dots. Phys. Rev. B 88, 045309 (2013).
Liu, F. et al. Spin dynamics of negatively charged excitons in CdSe/CdS colloidal nanocrystals. Phys. Rev. B 88, 035302 (2013).
Bimberg, D., Sondergeld, M. & Grobe, E. Thermal dissociation of excitons bounds to neutral acceptors in high-purity GaAs. Phys. Rev. B 4, 3451 (1971).
Favero, I. et al. Fast exciton spin relaxation in single quantum dots. Phy. Rev. B 71, 3–6 (2005).
Rol, F. et al. Probing exciton localization in nonpolar GaN / AlN quantum dots by single-dot optical spectroscopy. Phys. Rev. B 75, 125306 (2007).
Ostapenko, I. A. et al. Exciton acoustic-phonon coupling in single GaN/AlN quantum dots. Phys. Rev. B 85, 081303(R) (2012).
Kodriano, Y. et al. Radiative cascade from quantum dot metastable spin-blockaded biexciton. Phys. Rev. B 82, 1–6 (2010).
Moreau, E., Robert, I. & Manin, L. Quantum cascade of photons in semiconductor quantum dots. Phys. Rev. Lett. 87, 183601–183601 (2001).
Kako, S. et al. A gallium nitride single-photon source operating at 200 K. Nat. Mater. 5, 887 (2006).
Shields, A. J. Semiconductor quantum light sources. Nat. Photonics 1, 215 (2007).
Sallen, G. et al. Subnanosecond spectral diffusion measurement using photon correlation. Nat. Photonics 4, 696 (2010).
Miyamura, M., Tachibana, K. & Arakawa, Y. High-density and size-controlled GaN self-assembled quantum dots grown by metalorganic chemical vapor deposition. Appl. Phys. Lett. 80, 3937–3939 (2002).
Hoshino, K., Kako, S. & Arakawa, Y. Formation and optical properties of stacked GaN self-assembled quantum dots grown by metalorganic chemical vapor deposition. Appl. Phys. Lett. 85, 1262 (2004).
Winkelnkemper, M., Schliwa, A. & Bimberg, D. Interrelation of structural and electronic properties in InxGa1-xN/GaN quantum dots using an eight-band kp model. Phys. Rev. B 74, 155322 (2006).
Rinke, P. et al. Consistent set of band parameters for the group-III nitrides AlN, GaN, and InN. Phys. Rev. B 77, 16 (2008).
Vurgaftman, I. & Meyer, J. R. Band parameters for nitrogen-containing semiconductors. J. Appl. Phys. 94, 3675 (2003).
Winkelnkemper, M. et al. Origin of the broad lifetime distribution of localized excitons in InGaN/GaN quantum dots. Phys. Status Solidi (b) 245, 2766–2770 (2008).
Pal, J., Tse, G., Haxha, V., Migliorato, M. A. & Tomić, S. Second-order piezoelectricity in wurtzite III-N semiconductors. Phys. Rev. B 84, 085211 (2011).
Schulz, S., Mourad, D., Schumacher, S. & Czycholl, G. Tight-binding model for the electronic and optical properties of nitride-based quantum dots. Phys. Status Solidi 248, 1853–1866 (2011).
Acknowledgements
This work was supported by the German Research Foundation within the Collaborative Research Center (CRC 787).
Author information
Authors and Affiliations
Contributions
G.H. and G.C. contributed equally to the manuscript: G. H. developed the hybrid-XX concept, implemented the particle interaction algorithms and calculated as well as evaluated the numerical data; G. C. designed the entire experimental setup and provided the experimental evidence for the hybrid-XX by measuring and evaluating the spectroscopic data, associated with the spectroscopic anomalies predicted by G.Hönig. A.S. implemented and evaluated the rate equation model in the Supplementary Information. The measurements were supported by S. Kal. and C.K., while early publications of C.K. triggered first discussions. S. Kako and Y.A. contributed the samples and fostered the GaN quantum dot project. A.S. and D.B. supported and financed the theoretical contribution. A.H. supervised and financed the entire project.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-4, Supplementary Table 1, Supplementary Notes 1-3 and Supplementary References (PDF 1233 kb)
Rights and permissions
About this article
Cite this article
Hönig, G., Callsen, G., Schliwa, A. et al. Manifestation of unconventional biexciton states in quantum dots. Nat Commun 5, 5721 (2014). https://doi.org/10.1038/ncomms6721
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms6721
- Springer Nature Limited
This article is cited by
-
Recent advances in room temperature single-photon emitters
Quantum Information Processing (2023)
-
Crystal orientation effects on the optical properties of wurtzite GaN/AlN quantum dots on semi-polar substrates
Optical and Quantum Electronics (2023)
-
Single photon emission and recombination dynamics in self-assembled GaN/AlN quantum dots
Light: Science & Applications (2022)
-
Modeling electronic and optical properties of III–V quantum dots—selected recent developments
Light: Science & Applications (2022)
-
Suppression of the quantum-confined Stark effect in polar nitride heterostructures
Communications Physics (2018)