Abstract
The observation of replica bands in single-unit-cell FeSe on SrTiO3 (STO)(001) by angle-resolved photoemission spectroscopy (ARPES) has led to the conjecture that the coupling between FeSe electrons and the STO phonons are responsible for the enhancement of Tc over other FeSe-based superconductors. However the recent observation of a similar superconducting gap in single-unit-cell FeSe/STO(110) raised the question of whether a similar mechanism applies. Here we report the ARPES study of the electronic structure of FeSe/STO(110). Similar to the results in FeSe/STO(001), clear replica bands are observed. We also present a comparative study of STO(001) and STO(110) bare surfaces, and observe similar replica bands separated by approximately the same energy, indicating this coupling is a generic feature of the STO surfaces and interfaces. Our findings suggest that the large superconducting gaps observed in FeSe films grown on different STO surface terminations are likely enhanced by a common mechanism.
Similar content being viewed by others
Introduction
The discovery of high-temperature superconductivity in single-unit-cell (1 UC) FeSe/STO(001) continues to attract a great deal of interest1. In particular, a recent mutual inductance measurement has shown an onset of diamagnetism at the same temperature (65 K) as when a gap emerges in angle-resolved photoemission spectroscopy (ARPES), thus supporting the superconducting origin of the observed single-particle energy gap2. Compared with the 8 K superconducting transition temperature of bulk FeSe the Tc of the 1 UC FeSe/STO(001) is almost an order of magnitude higher. This leads to a natural question regarding the cause of the Tc enhancement.
Apparently, one contributing factor is electronic doping. Earlier works3,4,5 on intercalated AxFe2−ySe2 (A=K, Tl, Cs, Rb and so on) compounds have shown superconductivity with Tc above 30 K. Recent work on a bulk crystal of Li1−xFexOHFeSe, consisting of FeSe layers intercalated with Li1−xFexOH shows Tc∼41 K (refs 6, 7). On a different front, when the top surface of a non-superconducting 3 UC FeSe/STO(001) is coated with potassium (K), a superconducting gap is observed at 48 K (ref. 8). However, despite the similarity in the fermiology of these systems with that of the 1UC FeSe/STO(001), the Tc of the later is still significantly higher. This suggests that electron doping alone is insufficient to account for the full enhancement of Tc in 1 UC FeSe/STO(001).
The foremost telling clue concerning the origin of the extra Tc enhancement in 1 UC FeSe/STO(001) comes from the ARPES observation of ‘replica bands’ at ∼100 meV below the main band9. Such replica bands are explained in terms of a ‘shake off’ phenomenon—in the photoemission process of ejecting an electron, part of the incoming photon energy can be used to excite a vibration quantum. Thus, the replica bands signify a strong coupling between the FeSe electrons and STO phonons, which in turn is conjectured to be the Tc enhancement mechanism9.
In two very recent publications scanning tunnelling microscopy and ARPES reported similar superconducting gap and gap closing temperature of 1 UC FeSe grown on the (110) surface of STO10,11. Since the (110) surface is geometrically and chemically different from that of (001) surface, it raises doubts11,12 whether the same electron–phonon-enhancement mechanism also applies.
We conducted ARPES studies of FeSe films on STO(110) to investigate this issue. In addition, we have carried out a comparative study of the electron–phonon coupling on bare STO(001) and STO(110) surfaces. Similar electron–phonon replica bands have been found for the two-dimensional electron gas formed on the (001) surface13,14. Our results show that the electron–phonon replicas at the FeSe/STO(110) interface and bare STO(110) surface are similar to its counterparts at the (001) surface, suggesting such electron–phonon coupling is a generic feature of STO surfaces and interfaces prepared under certain conditions. As such, the recent observation in the FeSe/STO(110) system is consistent with the conjecture of Tc enhancement by interface electron–phonon coupling.
Results
Replica bands of 1UC FeSe grown on STO(110) and STO(001)
One important difference between the interfaces of FeSe/STO(110) and FeSe/STO(001) is the distortion of the in-plane unit cell from tetragonal to orthorhombic symmetry. A comparative ARPES study of FeSe/STO(110) and FeSe/STO(001) has been recently reported by Zhang et al.11 However, the replica bands were not resolved in their experiment. By utilizing the capability of in situ MBE growth and high-resolution ARPES beamline, we have carefully studied the band strutures of the 1UC FeSe/STO(110) system. Our results show the hole band at Gamma point shifts towards lower binding energy (with the band top located at ∼20 meV below Fermi level) compared with FeSe/STO(001) (see Supplementary Fig. 1). It has been reported that the presence of incipient bands below EF may have an important role in the electron pairing15. Figure 1a shows a Fermi surface at the M point of the Brillouin zone measured at ∼25 K. Figure 1b shows the energy–momentum intensity map along a high-symmetry cut through M. It clearly shows an electron band crossing the Fermi level. The superconducting gap opening at the Fermi momentum (kF) is measured to be ∼14 meV, similar to that observed in FeSe/STO(001) (ref. 9). To better resolve the band dispersion, we show the second energy derivative of the ARPES intensity in Fig. 1d, and mark the peaks of the energy distribution curves (EDCs) with green and red squares in Fig. 1e. In Fig. 1d,e we see both an electron band crossing the Fermi level and a hole band below it. Most interestingly, at ∼100 meV below the main bands, we again see the features that can be identified as the replica bands. The replica of the hole band (red dash line) is clearly presented at Fig. 1d, the totality of the data in Fig. 1d,e also makes the replica of the electron band (green dashed line) discernable. Sketches of the main bands and replica bands are shown by the solid and dashed curves, respectively in Fig. 1c. Thus replica bands with similar energy separation as in 1UC FeSe/STO(001) have been clearly identified in FeSe/STO(110).
(a) The M point Fermi surface map of FeSe/STO(110). The yellow dashed line shows the high-symmetry cut along Γ-M direction. (b) Energy–momentum intensity map of FeSe/STO(110) around the cut marked at a. (c) Schematic representation of the electron band (green) and hole band (red) of FeSe/STO(110). The replica bands are shown as the dashed lines. (d) Second derivative image of (b). Comparison with c identifies the features associated with the main bands and the replica bands. (e) EDCs near M shown as a waterfall plot with main and replica bands marked by corresponding colour squares.
Surface electronic structure of STO(110) and STO(001)
To lend further support for the similarity of electron–phonon coupling on these surfaces and interfaces, we proceed with a comparative study the surface electronic structure of pure STO(110), in reference to the (001) surface where the replica band has been recently reported13,14. The two-dimensional electron gas (2DEG) created by exposing the STO(001) surface to synchrotron radiation in ultrahigh vacuum, that is, photodoping, has been extensively studied16,17,18. By tuning the dosage of ultra violet exposure, which increases the electron density, and by adding atomic oxygen, which decreases the electron density, very precise control of the 2DEG density can be achieved19,20. Similar to STO(001), a 2DEG has also been observed on the (110) (ref. 21) and (111) (ref. 20) surfaces of STO. In particular, ARPES has observed the photo-doped surface conduction bands as well as their quantum well subbands due to the spatial confinement.
The STO samples used in this study are from the same source as the STO(001) substrates upon which we deposited the 1UC FeSe films in ref. 9. Our results on the surface electronic structure are consistent with those reported by Wang et al.21, as shown in the Supplementary Fig. 2. We focus our discussion on lower photodoping density regime, where the replica is most visible. In Fig. 2a,c we compare the APRES data of STO(001) and STO(110) at electron density of n2D≈4.4 × 1013 and 1.8 × 1013 cm−2, respectively. These electron densities are chosen so that the kF of the main bands are similar for the two surface terminations (a schematic of the two Fermi surface is presented in supplementary Fig. 3). In this doping regime we can only resolve the parabolic dxy main bands as the quantum well subbands cannot be resolved at this doping level. Importantly, a band with similar effective mass at higher binding energy (∼100 meV) can also be resolved for both surface terminations. This is the feature we identify as the replica band. To enhance the contrast we plot the energy second derivative of the ARPES intensity in (b and d). The EDCs of STO(110) have also been shown as a waterfall plot in Fig. 2e to highlight the main band and the replica band. For both cases we determine the energy separation between the main band and the replica band to be ∼100 meV. To more accurately estimate the energy separation and compare the relative intensity between the replica and main bands we show the EDCs at kF in Fig. 2f. We have normalized the intensities, so that the peaks associated with the main bands coincide for the two surface terminations. The deduced energy separation between the main band and the replica band are the same, within the experimental error.
(a,c) Energy–momentum intensity map of STO(001) and STO(110) with similar main bands and replica bands. The separation of two bands is estimated to be ∼100 meV in both surfaces (b,d) Second energy derivative of a,c. (e) EDCs of STO(110) shown as a waterfall plot with main and replica bands marked by red squares. (f) EDCs of STO(001) and STO(110) measured at kF, showing the similar ∼100 meV energy separation between the main and replica bands.
ARPES study of STO(110) as a function of photodoping
To further understand the electron–phonon coupling on STO surfaces, we explore its doping dependence. Figure 3 shows the band structure evolution of STO(110) with increasing photodoping. The carrier density increases from n2D≈1.8 × 1013 to 6.0 × 1013 cm−2. The upper part of each panel shows the energy second derivative of lower part in the energy range of −100 meV≤E−EF≤0. As the carrier density increases, the dxy band shifts towards higher binding energy, and its quantum well subband gradually appears, again resembling that of the STO(001) surface14. The subband is superimposed on the main band at first, then moves to lower binding energy and becomes clearly separated from the main band at higher carrier densities (the dashed yellow curve in Fig. 3h). Increased separation between the main and the subband with increased doping is consistent with the quantum well origin of the subbands. In contrast the replica band is better resolved at low carrier densities (see, for example, the red curve in Fig. 3a).
(a–h) The evolution of the ARPES dispersion as the surface carrier density increases from n2D≈1.8 × 1013–6.0 × 1013 cm−2. The red curve marks the replica band in a, while the yellow curve marks quantum well subband in h. The upper part of each panel shows the second energy derivative of the lower part in the −100 meV ≤E-EF≤0 energy window. (i) EDCs of the main band and replica band as the carrier increases from n2D≈1.8 × 1013–6.0 × 1013 cm−2. The dashed red line marked the positon of replica band.
In Fig. 3i we show the doping dependence of the replica band intensity. Here the dashed red line marks the energy position of the replica band. We have estimated the intensity ratio between the replica and the main band as a function of the electron density as shown in Supplementary Fig. 4a. The carrier density dependence described above are similar to those observed by Wang et al.14 on STO(001), consistent with a similar picture for electron–phonon coupling on STO surfaces. We also estimate the effective mass associated with the parabolic dxy bands at different carrier densities (Fig. 4b). If one attributes the change in the effective mass to the change in the electron–phonon coupling strength the result is consistent with the trend deduced from Supplementary Fig. 4a. However, it should be noted the change of effective mass has been used as a direct tool to reflect correlation effects22. The gradual doping of K on the top of FeSe single crystal shows a heavier effective mass with a higher Tc, which has been interpreted as the enhanced correlations due to the development of a two-dimensional system on top of the single crystal.
(a) All the multilayer and single crystals of iron-based superconductors show Tc lower than 50 K. (b) In contrast, monolayer FeSe on various TiO2 terminated substrates always show Tc higher than 50 K. We have observed electron–phonon coupling both at FeSe/STO(001) and FeSe/STO(110). The Tc of FeSe/STO/KTO is from ref. 32.
We also observed a similar replica band with the same phonon mode on STO(111) surface at lower doping level (see Supplementary Fig. 5), again supporting the picture of universal behaviour of electron–phonon coupling in various STO surfaces and interfaces. This suggests the possibilities of high Tc superconductivity in FeSe/STO(111) if good quality interfaces can be achieved.
Discussion
The origin of high Tc in 1UC FeSe/STO is still a question under investigation. From the experimental facts at least two contributing factors can be identified23: the electron doping and the substrate effect. The mechanism of electron doping at the interface of FeSe/STO(001) is still actively debated9,24. However the formation of oxygen vacancies may play an important role and have also been observed in FeSe/STO(110) (see Supplementary Fig. 7). The most direct evidence that electron doping raises Tc is from the studies of potassium doping on otherwise non-superconducting multilayer FeSe films (or low Tc bulk FeSe crystals). By coating the surface of bulk FeSe22,25 and multilayer FeSe films8,26,27,28,29 with potassium, Tc can be increased to as high as 48 K, at which point the Fermi surfaces have a similar area as that of 1UC FeSe/STO, indicating approximately the same electron doping level. In addition, bulk materials where various donor layers are intercalated between the FeSe layers, for example, AxFe2−ySe2 (ref. 30) and Li1−xFexOHFeSe (ref. 6) also have similar Fermi surface volume and similar range of Tc. Nonetheless, the Tc of these systems are still appreciably lower than 1UC films on STO or other titanate substrates31 (see Fig. 4).
Thus it is natural to associate the extra enhancement of Tc in the monolayer films to a substrate effect. In particular, the cross-interface coupling of the FeSe electrons and STO phonons has been proposed to enhance the Tc of heavily electron-doped FeSe systems9,22. On the surface it is unusual that electrons in the top layer of K-doped 3UC FeSe/STO cannot couple to the STO phonons, that is, the electron–phonon coupling being very local.
To answer that question we recall that the doping in 1UC FeSe/STO is due to charge transfer between STO and FeSe, so that near the FeSe-STO interface there is an electric field. Such electric field will induce a layer of dipoles, so that near the interface with FeSe, STO is strongly polarized. In ref. 9, 23 it has been argued that the phonons causing the replica are associated with the vibration of these dipoles with the displacement perpendicular to the interface, and the modulating wave vector parallel to interface. Such in-plane modulating dipole potential does not affect layers further away from the interface due to the screening by the electrons in the bottom FeSe layer. The fact that the bottom layer alone can screen the interface suggests that Coulomb attraction localizes nearly all the doped charges in the bottom FeSe layer. Thus while the top layer in K-doped 3UC FeSe/STO is equally electron-doped (by potassium rather than STO) it does not experience the modulating dipole potential due to the screening of other FeSe layers beneath it.
The above situation has a close analogy with what we observed for the doping dependence of the replica band on the surface of STO. As the photo-doped carrier density increases, the modulating dipole potential caused by the polar phonon is screened. As a result the replica band intensity vanishes.
In conclusion, we have observed the replica band for FeSe/STO(110) as well as lightly doped STO(110) surface. The similar energy separation between the main bands and replica bands for these interfaces/surfaces as those in FeSe/STO(001) and STO(001) suggest that similar electron–phonon coupling is involved in both. Our results suggest that a similar phonon-enhancement mechanism might also be at work for the superconducting FeSe/STO(110).
Methods
Samples
The pure, undoped STO substrates were degassed at 450 °C for 1 h before in situ transfer to the ARPES measurement chamber. Single unit cell FeSe films were grown on 0.05 wt% Nb-doped STO(110) substrates. Before growth, the substrates were degassed at 450 °C for 45 min, and heated to 830 °C for 30 min in the ultra high vacuum (UHV) chamber and then held at Tsub=390 °C for growth. FeSe was obtained by co-evaporating Fe and Se with a flux ratio of 1:10 and a growth rate of ∼2UC min−1. Post-annealing at 420 °C for 3 h was performed after growth.
ARPES measurements
All the measurements were performed in situ utilizing MBE+beamline ARPES systems in this work. The ARPES measurements of pure substrates were carried out at Beamline 10.0.1 of the Advanced Light Source of Lawrence Berkeley National Laboratory. The total energy resolution was ∼25 meV with photon energy of 48 eV and a base pressure better than 5 × 10−11 Torr. The measurements on 1UC FeSe/STO(110) films were performed at Beamline 5-4 of the Stanford Synchrotron Radiation Lightsource of SLAC National Accelerator Laboratory. The photon energy used was 24 eV with the total energy resolution ∼8 meV and a base pressure also better than 5 × 10−11 Torr.
Data availability
The data relevant to the findings of this study are available from the corresponding authors on reasonable request.
Additional information
How to cite this article: Zhang, C. et al. Ubiquitous strong electron–phonon coupling at the interface of FeSe/SrTiO3. Nat. Commun. 8, 14468 doi: 10.1038/ncomms14468 (2017).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Wang, Q.-Y. et al. Interface-induced high-temperature superconductivity in single unit-cell FeSe films on SrTiO3 . Chin. Phys. Lett. 29, 037402 (2012).
Zhang, Z. et al. Onset of the Meissner effect at 65 K in FeSe thin film grown on Nb-doped SrTiO3 substrate. Sci. Bull. 60, 1301–1304 (2015).
Qian, T. et al. Absence of a holelike Fermi surface for the iron-based K0.8Fe1.7Se2 superconductor revealed by angle-resolved photoemission spectroscopy. Phys. Rev. Lett. 106, 187001 (2011).
Mou, D. et al. Distinct Fermi surface topology and nodeless superconducting gap in a (Tl0.58Rb0.42)Fe1.72Se2 superconductor. Phys. Rev. Lett. 106, 107001 (2011).
Zhang, Y. et al. Nodeless superconducting gap in A(x)Fe2Se2 (A=K,Cs) revealed by angle-resolved photoemission spectroscopy. Nat. Mater. 10, 273–277 (2011).
Lu, X. F. et al. Coexistence of superconductivity and antiferromagnetism in (Li0.8Fe0.2)OHFeSe. Nat. Mater. 14, 325–329 (2015).
Dong, X. et al. Phase diagram of (Li(1−x)Fe(x))OHFeSe: a bridge between iron selenide and arsenide superconductors. J. Am. Chem. Soc. 137, 66–69 (2015).
Miyata, Y. et al. High-temperature superconductivity in potassium-coated multilayer FeSe thin films. Nat. Mater. 14, 775–779 (2015).
Lee, J. J. et al. Interfacial mode coupling as the origin of the enhancement of Tc in FeSe films on SrTiO3 . Nature 515, 245–248 (2014).
Zhou, G. et al. Observation of interface induced high temperature superconductivity in single unit-cell FeSe films on SrTiO3(110). Appl. Phys. Lett. 108, 202603 (2016).
Zhang, P. et al. Observation of high-Tc superconductivity in rectangular FeSe/STO(110) monolayer. Phys. Rev. B 94, 104510 (2016).
Wu, X. et al. Density functional calculations of a staggered FeSe monolayer on a SrTiO3(110) surface. Phys. Rev. B 94, 045114 (2016).
Chen, C. et al. Observation of a two-dimensional liquid of Fröhlich polarons at the bare SrTiO3 surface. Nat. Commun 6, 8585 (2015).
Wang, Z. et al. Tailoring the nature and strength of electron–phonon interactions in the SrTiO3(001) 2D electron liquid. Nat. Mater. 15, 835–839 (2016).
Chen, X. et al. Electron pairing in the presence of incipient bands in iron-based superconductors. Phys. Rev. B 92, 224514 (2015).
Meevasana, W. et al. Creation and control of a two-dimensional electron liquid at the bare SrTiO3 surface. Nat. Mater. 10, 114–118 (2011).
Meevasana, W. et al. Strong energy–momentum dispersion of phonon-dressed carriers in the lightly doped band insulator SrTiO3 . New J. Phys. 12, 023004 (2010).
Santander-Syro, A. F. et al. Two-dimensional electron gas with universal subbands at the surface of SrTiO3 . Nature 469, 189–193 (2011).
McKeown Walker, S. et al. Carrier-density control of the SrTiO3(001) surface 2D electron gas studied by ARPES. Adv. Mater. 27, 3894–3899 (2015).
McKeown Walker, S. et al. Control of a two-dimensional electron gas on SrTiO3(111) by atomic oxygen. Phys. Rev. Lett. 113, 177601 (2014).
Wang, Z. et al. Anisotropic two-dimensional electron gas at SrTiO3(110). Proc. Natl Acad. Sci. USA 111, 3933–3937 (2014).
Seo, J. J. et al. Superconductivity below 20 K in heavily electron-doped surface layer of FeSe bulk crystal. Nat. Commun. 7, 11116 (2016).
Lee, D.-H. What makes the Tc of FeSe/SrTiO3 so high? Chin. Phys. B 24, 117405 (2015).
Ding, H. et al. High-temperature superconductivity in single-unit-cell FeSe films on Anatase TiO2(001). Phys. Rev. Lett. 117, 067001 (2016).
Ye, Z. R. et al. Simultaneous emergence of superconductivity, inter-pocket scattering and nematic fluctuation in potassium-coated FeSe superconductor, Preprint at http://arxiv.org/abs/1512.02526 (2015).
Wen, C. H. P. et al. Anomalous correlation effects and unique phase diagram of electron doped FeSe revealed by angle resolved photoemission spectroscopy. Nat. Commun. 7, 10840 (2016).
Tang, C. et al. Interface-enhanced electron-phonon coupling and high-temperature superconductivity in potassium-coated ultrathin FeSe films on SrTiO3 . Phys. Rev. B 93, 020507 (2016).
Tang, C. et al. Superconductivity dichotomy in K-coated single and double unit cell FeSe films on SrTiO3 . Phys. Rev. B 92, 180507 (R) (2015).
Song, C.-L. et al. Observation of double-dome superconductivity in potassium-doped FeSe Thin Films. Phys. Rev. Lett. 116, 157001 (2016).
Guo, J. et al. Superconductivity in the iron selenide KxFe2Se2(0≤x≤1.0). Phys. Rev. B 82, 180520 (R) (2010).
Peng, R. et al. Tuning the band structure and superconductivity in single-layer FeSe by interface engineering. Nat. Commun. 5, 5044 (2014).
Peng, R. et al. Measurement of an enhanced superconducting phase and a pronounced anisotropy of the energy gap of a strained FeSe single layer in FeSe/Nb: SrTiO3/KTaO3 heterostructures using photoemission spectroscopy. Phys. Rev. Lett. 112, 107001 (2014).
Acknowledgements
The work at Stanford is supported by the US DOE, Office of Basic Energy Science, Division of Materials Science and Engineering, under award number DE-AC02-76SF00515. ALS and SSRL are supported by the Office of Basic Energy Sciences, US DOE under contract No. DE-AC02-05CH11231 and DE-AC02- 76SF00515, respectively. CFZ’s postdoctoral fellowship is supported by Knut and Alice Wallenberg Foundation in Sweden. D.H.L. is supported by the US Department of Energy, Office of Science, Basic Energy Sciences, Materials Sciences and Engineering Division, grant DE-AC02-05CH11231.
Author information
Authors and Affiliations
Contributions
C.Z., Y.H., R.G.M., H.Y.H., D.L. and Z.S. proposed and designed the research. C.Z. and Z.L. carried out the ARPES measurements with help from Z.C., Y.X., J.H., S.T., T.J., W.L., H.Y. and S.N.R. S.-K.M., D.L., M.H. maintained the ARPES beamlines. C.Z. analysed the data with help from Z.L. and E.Y.M. C.Z. wrote the manuscript with D.L., R.G.M., R.H., H.Y.H. and Z.S. R.G.M, H.H., D.L., Z.S. are responsible for project direction and infrastructure. All authors discussed the results and commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-6 (PDF 993 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Zhang, C., Liu, Z., Chen, Z. et al. Ubiquitous strong electron–phonon coupling at the interface of FeSe/SrTiO3. Nat Commun 8, 14468 (2017). https://doi.org/10.1038/ncomms14468
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms14468
- Springer Nature Limited
This article is cited by
-
Emergence of two distinct phase transitions in monolayer CoSe2 on graphene
Nano Convergence (2024)
-
Evidence of electron interaction with an unidentified bosonic mode in superconductor CsCa2Fe4As4F2
Nature Communications (2024)
-
Evolution of spin excitations from bulk to monolayer FeSe
Nature Communications (2021)
-
Non-universal current flow near the metal-insulator transition in an oxide interface
Nature Communications (2021)
-
High-temperature superconductivity and its robustness against magnetic polarization in monolayer FeSe on EuTiO3
npj Quantum Materials (2021)