Abstract
Hydrogen bonds dominate many chemical and biological processes, and chemical modification enables control and modulation of host–guest systems. Here we report a targeted modification of hydrogen bonding and its effect on guest binding in redox-active materials. MFM-300(VIII) {[VIII2(OH)2(L)], LH4=biphenyl-3,3′,5,5′-tetracarboxylic acid} can be oxidized to isostructural MFM-300(VIV), [VIV2O2(L)], in which deprotonation of the bridging hydroxyl groups occurs. MFM-300(VIII) shows the second highest CO2 uptake capacity in metal-organic framework materials at 298 K and 1 bar (6.0 mmol g−1) and involves hydrogen bonding between the OH group of the host and the O-donor of CO2, which binds in an end-on manner, =1.863(1) Å. In contrast, CO2-loaded MFM-300(VIV) shows CO2 bound side-on to the oxy group and sandwiched between two phenyl groups involving a unique ···c.g.phenyl interaction [3.069(2), 3.146(3) Å]. The macroscopic packing of CO2 in the pores is directly influenced by these primary binding sites.
Similar content being viewed by others
Introduction
There is increasing interest in using porous materials for substrate binding, separation, storage, delivery and catalysis owing to their specific host–guest binding interactions1,2. Gaining molecular insights into these binding interactions is very important, but experimentally challenging. Firstly, the nature of host–guest binding is often within the regime of low-energy supramolecular contacts, and thus the guest molecules have great mobility in the pore and can be highly disordered3,4. For the study of hydrogen bonds in particular, the identification of structural and dynamic details has only been achieved via neutron scattering in exceptional cases5. Secondly, the porous nature of host materials leads to additional impediments for the in-depth investigation of host–guest systems, mostly due to the intrinsic structural disorder and overall lack of long-range order for certain types of porous materials (e.g., carbons, porous silica, large-pore zeolites)6,7. Design of a suitable host platform is the key to overcome these barriers to gain molecular information on the host–guest binding based upon multiple supramolecular contacts, particularly for hydrogen bonds.
Metal-organic frameworks (MOFs) are an emerging class of porous materials showing highly crystalline structures and great promise for gas adsorption8,9. Built from metal ions/clusters and organic ligands, MOFs often exhibit high surface areas (up to ∼7,000 m2 g−1) and, more importantly, tunable functional pore environments10,11,12. MOFs can readily incorporate desired functionality by judicious choice of metal nodes and/or organic linkers13,14,15. Post-synthetic modification, broadly defined as chemical derivatization of MOFs after their formation, can afford MOFs with additional functionalities that cannot be obtained by routine synthesis16,17. Fine-tuning of the supramolecular host–guest binding requires precise chemical modification to the functional groups on the MOF backbones. To govern the formation of hydrogen bonds in particular, such modification, involving removal/addition of protons, will trigger concurrent redox reactions to occur within the MOF hosts. Post-synthetic redox modification on MOFs without destroying/changing the pore structure, especially through a single-crystal to single-crystal transformation, rarely succeeds because of the changes in bond interactions which leads to collapse of the framework18,19,20. Redox modifications of MOFs have been reported for systems containing FeII/III, VII/III/IV, TiII/III/IV, CuI/II and CrII/III centres21,22. However, none of these MOF systems affords a pair of structural analogues (Mn+ and Mn+1-based MOF) as a platform for the direct investigation of guest binding. For example, MOF-74(Fe) features a hexagonal array of one-dimensional channels lined with co-ordinatively unsaturated FeII centres23. The oxygen adsorption isotherm indicates that FeII centres bind to O2 preferentially over N2, which is attributed to a partial electron charge transfer from FeII to O2. However, the FeIII-based MOF analogue cannot be isolated readily because, upon desorption of O2, the charge transfer is reversible.
We report herein the synthesis of single crystals of a VIII-based MOF, MFM-300(VIII) and its VIV isostructural counterpart, MFM-300(VIV), which was obtained by oxidation of the VIII precursor via a single-crystal to single-crystal transformation. These two materials show the same overall structural features with some differences in metal–ligand bond distances, but the main difference is conversion of V–(OH)–V in MFM-300(VIII) to V–O–V linkers in MFM-300(VIV). This provides a unique platform to investigate the precise role of the OH group in the supramolecular binding of guest molecules. The binding of CO2 has been thoroughly investigated in these two MOF systems via neutron diffraction and inelastic scattering, coupled with modelling. These experiments find that, surprisingly, the hydroxyl protons play a dominating role in the global binding of adsorbed CO2 molecules in the pore, rather than just providing specific binding interactions to the localized CO2 molecules nearby, as typically found in amine-functionalized MOFs24. Thus, as a result of the presence/absence of the hydroxyl proton, the binding and packing pattern for adsorbed CO2 molecules in these two iso-structural MOFs are distinct. This study represents a unique analysis of the structural and dynamic characterization of hydrogen bonds (and other associated supramolecular interactions) that are stabilizing host–guest systems in the solid state.
Results
Synthesis and crystal structure of MFM-300(VIII)
An oxygen-free hydrothermal reaction of VCl3, H4L (H4L=biphenyl-3,3′,5,5′-tetracarboxylic acid), HCl and water in the molar ratio of 6:1:1.5:1,600 at 210 °C for 3 days afforded MFM-300(VIII)-solv, [V2(OH)2(L)]·6H2O, as a green microcrystalline material with a yield of ca. 90%. Single crystals of MFM-300(VIII)-solv were obtained under acidic conditions (VCl3:H4L:HCl:water=16:1:53:11,000), which afforded dark green prism shaped crystals (0.5 × 0.2 × 0.2 mm; yield<5%) along with a large amount of re-crystallized organic ligand. It is likely that this highly acidic hydrothermal environment slows down the crystallization process of the MOF leading to slow growth of crystal nuclei into large crystals. Interestingly, synthesis of vanadium-based MOFs, especially in the single crystal form, has been very rarely reported25. It is also worth noting that oxygen-free conditions are necessary to prevent oxidation of VIII centres during the hydrothermal process, and MFM-300(VIII)-solv cannot be obtained in the presence of air/oxygen.
MFM-300(VIII) crystallizes in the space group I4122 and is isostructural to MFM-300(M) (M=Al, Ga, In, see Supplementary Table 1 for single crystal data)26,27,28. The VIII centre shows octahedral coordination defined by four carboxylate oxygen atoms from the ligand [V–O=2.014(2) and 2.030(2) Å] and two oxygen atoms from two hydroxyl groups [V–O=1.948(2) Å] (Fig. 1). Adjacent pairs of VIII centres are bridged by two carboxylates and a μ2-hydroxyl group forming an extended chain of [V2(OH)2O4]∞ along the c axis. The ligands further bridge the vanadium hydroxyl chains to give a three-dimensional network with square-shaped channels decorated with hydroxyl groups. The cross-section of the channel is 6.7 × 6.7 Å taking Van der Waals radii into consideration. Guest water molecules in the channel can be readily removed by heating at 150 °C under vacuum for 5 h to give the desolvated material, MFM-300(VIII), as studied by in situ single crystal diffraction, which confirmed the retention of the framework structure and negligible residual electron density within the pore. The phase purity of MFM-300(VIII)-solv was confirmed by PXRD (Supplementary Fig. 1).
Post-synthetic oxidation to synthesize MFM-300(VIV)
The as-synthesized single crystals of MFM-300(VIII) changed colour from green to dark purple by heating at 150 °C under a flow of O2 for 16 h to form MFM-300(VIV), which were analysed by in situ single-crystal diffraction. MFM-300(VIV) retains the space group I4122 and shows a slight contraction of the unit cell parameters (0.6% for a axis; 1.2% for c axis) with a similar channel size (Table 1). The most significant structural change upon oxidation is that the V–O bond length involving the bridging oxygen reduces dramatically from 1.948(2) to 1.838(1) Å (Table 1), which is between the typical bond distances for VIII–O (∼1.95 Å) and VIV=O (∼1.65 Å)21. Detailed investigation of the crystal structure revealed no residual electron density close to the bridging VIV–O–VIV oxygen atom, indicating complete removal of the proton upon oxidation, which was further confirmed by neutron diffraction (Supplementary Fig. 2). Bond valence sum calculations give a valence of 3.03 for MFM-300(VIII) and 3.96 for MFM-300(VIV). Quantitative oxidation of vanadium centres on going from MFM-300(VIII) to MFM-300(VIV) has been further confirmed by XPS spectroscopy, which shows increased binding energy for the VIV species (Fig. 2 and Supplementary Fig. 3). IR spectroscopy confirms the disappearance in MFM-300(VIV) of the νO–H stretching mode of the hydroxyl group at 3,639 cm−1 observed in MFM-300(VIII) (Fig. 6a and Supplementary Fig. 4). Thus, the post-synthetic oxidation leads to retention of the porous structures in these two materials, and therefore affords an excellent platform to compare the supramolecular binding of guest molecules as a function of the presence and absence of the hydroxyl protons within the channel. The oxidized material MFM-300(VIV) can be reduced back to MFM-300(VIII) using Na2SO3 in aqueous solution, with the colour of MFM-300(VIV) changing from dark purple back to pale green, corresponding to the re-formation of MFM-300(VIII). PXRD data, however, confirm that some partial decomposition of the framework takes place under these conditions. Therefore, a quantitative reduction of MFM-300(VIV) back to MFM-300(VIII) has not yet been achieved.
It should be noted that the post-synthetic oxidation of MFM-300(VIII) is currently the exclusive way of obtaining MFM-300(VIV); hydrothermal syntheses using VOSO4 or VO2 salts based upon conditions reported25 for other vanadium-based MOFs failed thus far to produce MFM-300(VIV) in our hands. Interestingly, MIL-47(VIII) and MIL-47(VIV) also show one-dimensional channels constructed from [V2(OH)2O4]∞ chains bridged by terephthalate ligands20. MIL-47(VIII) and MIL-47(VIV) can be synthesized directly from VIII and VIV salts, respectively, but with considerable uncoordinated terephthalic acid encapsulated in the materials. Calcination of the as-synthesized complexes in air at 250 °C can effectively remove the free ligands to generate the corresponding activated materials. However, the VIII centre was inevitably oxidized to VIV during calcination and the open form of MIL-47(VIII) could not be isolated until very recently when a new activation method based upon DMF extraction was developed that stabilized MIL-47(VIII) material. CO2 and H2O adsorption isotherms confirm that MIL-47(VIII) and MIL-47(VIV) exhibit significantly different degrees of framework flexibility upon guest inclusion, and therefore cannot be directly compared in terms of host–guest chemistry29. In contrast, MFM-300(V) incorporates a wine-rack framework connection tied together by strong cis-μ2-OH groups, resulting in isostructural, highly rigid and robust frameworks in both VIII and VIV materials.
Thermal gravimetric analysis (TGA) of MFM-300(VIII)-solv shows that water can be fully removed at 200 oC under N2 flow, and no further weight loss was observed to 450 °C when decomposition sets in (Supplementary Fig. 5). In contrast, the TGA of MFM-300(VIV) (prepared by heating under O2) shows ∼2% weight loss before 120 °C, attributed to adsorbed moisture during sample transportation for TGA measurement. No further weight loss was observed to 490 °C, where the MOF decomposed.
Electron paramagnetic resonance analysis
To probe the change in oxidation state of V centres, electron paramagnetic resonance (EPR) studies at X-band (9.86 GHz) and room temperature were undertaken on MFM-300(VIII) and MFM-300(VIV) (Fig. 2). MFM-300(VIII) is EPR silent under these conditions, consistent with d2 VIII centre. In six-coordinate Oh symmetry, the VIII, d2 ion has a 3T1g ground state. In lower symmetry, a 3A state often results and spin–orbit coupling and gives rise to very large zero-field splitting (up to tens of cm−1) of the S=1 state (e.g., 5 cm−1 in [V(H2O)6]3+)30. Hence, most VIII species are EPR silent at X-band where the microwave energy (hν) is only ca. 0.3 cm−1. In contrast, MFM-300(VIV) shows a strong EPR signal under the same conditions, giving a single resonance centred at g=1.955, consistent with VIV, d1 (g<ge, the free electron value), with a peak-to-peak linewidth of ca. 130 G. This broad linewidth is due to the exchange interactions in the VIV chains and results in the absence of any 51V hyperfine resolution. Thus, EPR analysis confirms the change of oxidation state of VIII to VIV in this system.
Gas adsorption analysis
N2 isotherms at 77 K for both MFM-300(V) samples show no significant adsorption uptake, probably due to an activation diffusion effect at 77 K caused by the narrow pore channels. In contrast, low-pressure CO2 isotherms of MFM-300(VIII) at ambient temperatures (273–303 K) show very high uptake capacities with a value of 8.6 mmol g−1 (37.8 wt%) recorded at 273 K and 1.0 bar (Fig. 4 and Supplementary Figs 6 and 7), surpassing those of other MFM-300 analogues (7.0 mmol g−1 for MFM-300(Al)26, 2.86 mmol g−1 for MFM-300(Ga)27 and 6.3 mmol g−1 for MFM-300(In)28) under the same conditions. The CO2 uptake of MFM-300(VIII) at 298 K and 1.0 bar is 6.0 mmol g−1 (26.4 wt%), comparable to the best-behaving materials such as MOF-74(Mg) or CPO-27(Mg) (26∼27.5 wt%) under the same conditions31. The CO2 uptake in MFM-300(VIV) is lower than that of its VIII counterpart as a result of removal of the hydroxyl group from the pore. At 1.0 bar, the CO2 uptake of MFM-300(VIV) is 3.54 mmol g−1 (15.6 wt%) at 298 K and 6.56 mmol g−1 (28.9 wt%) at 273 K, a reduction of 41 and 25%, respectively, in comparison with MFM-300(VIII). Larger reductions in CO2 uptake are observed at higher temperatures, consistent with reduced MOF-CO2 binding strengths. The difference in CO2 uptakes between these two materials is less pronounced with increasing pressure at a given temperature because the CO2 intermolecular dipole interaction becomes more apparent at higher loadings. For example, at 273 K and 20 bar, the CO2 uptake of MFM-300(VIII) and MFM-300(VIV) were recorded to be 11.7 and 10.0 mmol g−1, respectively, a difference of 14.5% (Fig. 4d). Analysis of the high-pressure CO2 adsorption isotherm at 273 K by DFT/Monte-Carlo methods gives a surface area of 1,892 and 1,565 m2 g−1, a pore size distribution centred at 5.2 and 5.4 Å, and a cumulative pore volume of 0.490 and 0.481 cm3 g−1 for MFM-300(VIII) and MFM-300(VIV), respectively (Fig. 4c and Supplementary Figs 8–13), confirming the microporous nature of these two materials. Interestingly, the slightly increased pore size (and wider distribution) of MFM-300(VIV) is consistent with the deprotonation of the hydroxyl group in the channel, leading to decreased CO2 uptake at low pressure. The pore size distribution analysis confirms a slightly smaller pore size than that measured from the X-ray single crystal structure consistent with the presence of activated diffusion in the gas adsorption isotherms. The narrow pore size can also afford enhanced overlapping potential to gas molecules, increasing the overall host–guest binding interactions, and the slightly reduced pore volume of MFM-300(VIV) is responsible for its lower uptake capacity at high pressure in comparison with MFM-300(VIII).
The isosteric heat of adsorption (Qst) for CO2 adsorption in MFM-300(VIII) (obtained using van’t Hoff Equation) lies in the range 27.5–28 kJ mol−1 for uptakes of 0.5–1.0 mmol g−1 and increases continuously thereafter to 32 kJ mol−1 at 7 mmol g−1, which is slightly higher than that of MFM-300(Al) by ∼1.0 kJ mol−1 (Fig. 4b). In comparison, the Qst for MFM-300(VIV) is 24 kJ mol−1 at low CO2 coverage and increases steadily to 29 kJ mol−1 at 7 mmol g−1, which is some ∼3 kJ mol−1 lower than that of MFM-300(VIII), confirming the presence of a weaker adsorbate–adsorbent binding interaction in MFM-300(VIV). Nevertheless, the increasing trends of the variation of Qst plots are the same for these two materials, suggesting the presence of strong CO2–CO2 interactions with increasing surface coverage in both materials.
The binding energy of CO2 in both MFM-300(V) materials has also been estimated by DFT calculations at a loading of 8.6 mmol g−1 (equivalent to 2 CO2/V). The stepwise calculation was carried out by (i) optimizing the structure of the bare MOF by finding the local potential energy minimum with the final potential energy E1; (ii) optimizing the structure of the CO2-loaded MOF (2 CO2/V) with the final potential energy E2; (iii) removing the MOF host and leaving the CO2 molecules in the system to minimize the energy E3. The CO2 binding energy (ΔE), obtained by the calculation of ΔE=E1−E2+E3, was 34.9 and 29.7 kJ mol−1 for MFM-300(VIII) and MFM-300(VIV), respectively, consistent with the Qst analysis and confirming a lower CO2-MOF binding strength in MFM-300(VIV).
Structural analysis by neutron powder diffraction
In order to determine the binding sites of CO2 within these two materials, neutron powder diffraction (NPD) experiments were carried out for CO2-loaded MFM-300(VIII) and MFM-300(VIV) samples at 7 K. NPD data enabled full structural analysis via Rietveld refinement (Supplementary Figs 14–17 and Supplementary Table 2), yielding the positions, orientations and occupancies of adsorbed CO2 molecules within the materials. CO2-loaded MFM-300(VIII) retains the space group I4122 and two crystallographically independent CO2 sites (I and II) were observed (Fig. 5). Molecules CO2I are disordered with the respect to a two-fold rotation axis and are in an end-on mode interacting with the hydroxyl group with a distance of 1.863(1) Å (Fig. 5 and Supplementary Fig. 18), shorter than that obtained for MFM-300(Al) (2.298(4) Å) by PXRD at 273 K (ref. 20). This suggests a stronger hydrogen bond between adsorbed CO2 and the HO–VIII group and probably reflects the difference in the acidity between the bridging Al–OH and V–OH groups. CO2II binds to the carboxylate oxygen atoms via a dipole interaction with distances ranging from 2.984(2) to 3.369(2) Å. Further dipole interactions were observed between adsorbed CO2 molecules on sites I and II with intermolecular CI···OII distance of 3.103(1) Å in a typical T-shape arrangement (Fig. 5c), comparable to that observed in dry ice (3.178(1) Å)32. Supplementary intermolecular π···π interactions are also observed between the CO2 molecules at site II with a CII···OII distance of 2.565(2) Å.
The site occupancy of adsorbed CO2 molecules was obtained by free refinement against the NPD data (Table 2). At a CO2 loading of 1.4 CO2/V, the occupancies of CO2I and CO2II are found to be 0.82 and 0.29, respectively. As the CO2 loading was increased to 2.0 CO2 per V, the occupancy of CO2I increased slightly to 0.99, suggesting saturation of site I, while the occupancy of CO2II almost doubled from 0.29 to 0.52. This result indicates that site I which contacts with the hydroxyl group directly is the preferred location for adsorbed CO2 molecules at low surface coverage. The CO2 molecules occupying site I have a sequential effect on the population of site II, modulated by the intermolecular dipole interaction.
In contrast, the NPD pattern of CO2-loaded MFM-300(VIV) shows a change in the space group from I4122 to P4122 as indicated by the appearance of Bragg peaks (hkl, h+k+l=2n+1), which are systematically absent in I4122 (Supplementary Fig. 19). Nevertheless, the framework skeleton remains the same as that of MFM-300(VIII) and of the single crystal structure of bare MFM-300(VIV) with four independent binding sites (I′, II′, III′ and IV′) for adsorbed CO2 molecules being determined for CO2-loaded MFM-300(VIV). Most notably, the CO2 molecule at site I′ within MFM-300(VIV) is rotated by 90° (compared with that in MFM-300(VIII)) with respect to the bridging O2- group and is thus side-on to the O2- centre. It is thus sandwiched within a cleft between two phenyl rings of adjacent ligands, resulting in a highly translationally hindered site owing to the geometrical confinement (Fig. 5b). The linear CO2 points to the plane of two phenyl rings with an distance of 3.069(2) and 3.146(3) Å. To our best knowledge, CO2 binding between two phenyl rings in a ‘sandwich’ mode has not previously been experimentally observed. The CO2 molecule at site II′ is disordered over two orientations, forming contacts to the aromatic hydrogen atoms (=2.666(2) Å). CO2 molecules at sites III′ and IV′ are close to the carboxylate group of the ligand with the distance ranging from 2.843(2) to 3.057(2) Å (Fig. 5d). In the absence of strong interactions to the MOF host, adsorbed CO2 molecules in MFM-300(VIV) interact between each other with short C···O distances in the range of 2.478(1) to 3.132(1) Å, and the overall packing of CO2 in MFM-300(VIV) is more close to the dry ice structure compared with that in MFM-300(VIII), suggesting the presence of stronger intermolecular dipole interactions in MFM-300(VIV) (Supplementary Fig. 20). Refinement of the site occupancies suggests that 20 and 10% of adsorbed CO2 resides at site I′ and II′, respectively, at a loading of 1.4 CO2 per V, much lower than that (60%) for the corresponding position (site I) within MFM-300(VIII) at the same CO2 loading. This leads to 70% of adsorbed CO2 molecules residing on sites III′ and IV′, showing a dipole interaction with the carboxylate oxygen centres, clearly suggesting that these sites (III′ and IV′) now become the primary binding sites in MFM-300(VIV) in the absence of the hydroxyl proton.
The location of adsorbed CO2 molecules have been determined in a number of MOF systems that primarily contain open metal sites (e.g., HKUST-1 (ref. 33) and MOF-74 (ref. 23)) or pendent functional groups (e.g., amine group24 and hydroxyl group26). These studies suggest that the open metal sites or functional groups in the pore have a specific role in CO2 binding to the localized environment; their effects upon CO2 binding on a macroscopic level are however generally overlooked. The present study of MFM-300(VIII/IV) offers a comprehensive understanding of the effect of functional groups in CO2 binding. It is found that the hydroxyl proton plays a significant role in CO2 binding, not only to its localized environment but also to those CO2 molecules residing in the centre of the pore. Thus, the overall arrangement and packing of CO2 molecules in the extended channel of these two materials are distinct with different site populations [60/40 for Site I/II in MFM-300(VIII) vs 30/70 for Sites I′+II′/III′+IV′ in MFM-300(VIV)].
Structural analysis by DFT calculation
The structures for CO2-loaded MFM-300(VIII) and MFM-300(VIV) have also been optimized by DFT calculation at the loading of 2CO2 per V. The optimized structural model of MFM-300(VIII)·4CO2 shows excellent agreement with that obtained from NPD experiment, confirming the end-on model of adsorbed CO2 molecules interacting to the hydroxyl groups (=2.076 Å, Fig. 5e and Supplementary Fig. 21a). In contrast, for MFM-300(VIV), the calculated structure model does not show the ‘sandwich’ mode of adsorbed CO2 between two phenyl rings as seen in the NPD model. This is probably because that the CO2-loaded MFM-300(VIV) system has a less distinct energy minimum than the VIII material, that is, the rotation/translation of adsorbed CO2 molecules can occur more readily in MFM-300(VIV), leading to a series of similar structural models with close energy minimum in the calculation. That said, the change of the overall arrangement and packing of CO2 molecules in the pore has been successfully predicted by DFT calculations on going from MFM-300(VIII) to MFM-300(VIV), consistent with the presence of weaker CO2–host and stronger CO2–CO2 binding interaction in MFM-300(VIV) (Fig. 5f and Supplementary Fig. 21b).
Analysis of CO2 binding via inelastic neutron scattering
Understanding the change in dynamics upon adsorption of CO2 within these porous hosts can provide fundamental insight into the formation of multiple supramolecular contacts (e.g., hydrogen bond and intermolecular dipole interactions) with the adsorbed gas molecules. INS is a powerful neutron spectroscopic technique that is particularly sensitive to the dynamics of hydrogen atoms owing to the exceptionally large cross-section for that isotope and is therefore used here to investigate the vibrational states of hydrogen bonded systems. Comparison of the INS spectra of the bare MFM-300(VIII) and MFM-300(VIV) samples shows a number of differences (Fig. 6 and Supplementary Fig. 22). The most significant change is the absence of the –OH out-of-plane bending mode at 47 meV and disappearance of a series of hydroxyl deformation modes between 40 and 70 meV in MFM-300(VIV), confirming the deprotonation of the bridging hydroxyl group upon oxidation. The peaks corresponding to the C–H wagging/bending modes (80–167 meV) remain the same between these two samples. Calculated INS spectra for these two MOFs by DFT were found to be in good agreement with the experimental INS data (Supplementary Figs 23 and 24). On addition of CO2 in MFM-300(VIII), all peaks shift slightly to higher energy, indicating a stiffening effect of the host–guest lattice. Importantly, increases in intensity were observed for the peaks at 48 and 118 meV, indicating the change of the vibrational motion of both –OH and –CH groups upon CO2 binding, consistent with the formation of hydrogen bonds and supramolecular interactions as observed in the NPD and DFT models (Fig. 6c). This is further confirmed by the difference spectrum, and significantly these changes are in excellent agreement with the calculated difference INS spectrum (Fig. 6d). In contrast, addition of CO2 in MFM-300(VIV) is accompanied by changes of the peak intensity at 32, 85, 117 and 158 meV, corresponding to the distortion of the MOF lattice, distortion of the phenyl rings, deformation of the phenyl ring and in-plane C–H bending modes, respectively. This result confirms unambiguously that the phenyl ring and –CH group now become the primary binding site for adsorbed CO2 in MFM-300(VIV), in excellent agreement with the NPD results. These changes of the INS peaks are successfully predicted from the DFT calculations with an exceptionally high degree of consistency (Fig. 6f). Thus, the INS results have confirmed (i) the deprotonation of the bridging hydroxyl group occurs on going from MFM-300(VIII) to MFM-300(VIV); (ii) in MFM-300(VIII), both –OH and –CH are active binding sites for adsorbed CO2 via formation of hydrogen bonds; (iii) in MFM-300(VIV), the –CH and phenyl groups are the active binding sites for adsorbed CO2 via formation of supramolecular contacts. These observations are consistent with the NPD/DFT studies and confirm the significant effects of bridging hydroxyl groups on guest binding in MFM-300(VIII).
Discussion
It is widely accepted that introduction of pendent functional groups into the pores of MOFs offers accessible binding sites for guest molecules by attracting them via specific interactions. These sites often lose activity after reaching a 1:1 host–guest complex and are thus believed to have a limited role in the entire gas uptake process. Many functional groups contain hydrogen donors (e.g., –OH, –NH2, –OCNH–, COOH, –CH3), and the direct visualization of the molecular details for host–guest binding involving potential formation of hydrogen bonds is of fundamental importance to understand the function of host–guest systems. We have reported here the synthesis and characterization of a porous material, MFM-300(VIII), and its single-crystal to single-crystal transformation via post-oxidation to give its counterpart MFM-300(VIV). The oxidation of V centres from +3 to +4 promotes deprotonation of the bridging hydroxyl group, achieving fine tuning of the pore environment. It has been confirmed that these protons play a key role in the CO2 adsorption (both uptakes and heats of adsorption) in adsorption experiments. A study combining NPD, INS and modelling has unambiguously determined the binding sites and structural dynamics for these CO2–host systems. We have confirmed that the proton on the hydroxyl group can not only attract and localize adsorbed CO2 molecules via direct formation of hydrogen bonds but also affects the macroscopic packing and arrangement of CO2 molecules in the extended channel. Interestingly, a form of CO2 binding to the phenyl rings has been observed in MFM-300(VIV) by the NPD study. Thus, this report has provided direct evidence of the role of protons for guest binding in porous MOFs and, more importantly, it suggests that the effect of the functional group (i.e., protons) goes beyond specific binding to the local site and extends to the entire pore structure.
Methods
Synthesis of single crystals of MFM-300(VIII)-solv
A mixture of VCl3 (0.076 g, 0.48 mmol), deionized water (5.0 ml) (degassed previously under Ar for 0.5 h), biphenyl-3,3′,5,5′-tetracarboxylic acid (0.010 g, 0.03 mmol) and hydrochloric acid (1.6 M, 1.0 ml) was transferred into a 23 ml Teflon lined autoclave, which was then charged with argon and sealed. Reaction took place at 210 °C for 3 days and afforded dark green prism-shaped crystals accompanied with colourless block-shaped crystals (which are MFM-300(VIII)-solv and the re-crystallized ligand, respectively). The product was soaked in fresh N,N′-dimethylformamide (DMF) overnight to remove re-crystallized ligand, pure MFM-300(VIII)-solv single crystals (ca. 5% yield) were collected by filtration and preserved in acetone.
Synthesis of bulk MFM-300(VIII)-solv
A mixture of VCl3 (0.40 g, 2.55 mmol) in deionized water (10.0 ml) (degassed previously under Ar for 0.5 h), biphenyl-3,3′,5,5′-tetracarboxylic acid (0.14 g, 0.42 mmol) and hydrochloric acid (0.3 M. 2.0 ml) was transferred into a 45-ml Teflon lined autoclave, which was then charged with Ar and sealed. The reaction was heated at 210 °C for 3 days to produce MFM-300(VIII)-solv as a green microcrystalline powder (90% yield). This was soaked in fresh DMF overnight, and collected by filtration and stored under acetone.
Preparation of desolvated MFM-300(VIII)
MFM-300(VIII)-solv was placed in a Schlenk flask, which was evacuated to <1 × 10-3 mbar at ambient temperature for 1 h, and then heated at 150 °C for overnight under vacuum. Activated MFM-300(VIII) was obtained as green powder and stored in a glovebox. An important issue in desolvating MFM-300(VIII) is to avoid oxidation. Elemental analysis for MFM-300(VIII), C16H8O10V2 (found (calculated%)): C 41.4(41.6), H 1.9(1.7), N 0.0(0.0).
Post-synthetic oxidation of MFM-300(VIII) to prepare MFM-300(VIV)
Single crystals or powder MFM-300(VIII) was heated under pure O2 flow at 150 °C overnight using a tube furnace. The temperature ramping speed was set to 1.0 °C min−1. MFM-300(VIV) was obtained as dark purple solid that was stored under N2 in a glovebox. Elemental analysis for MFM-300(VIV), C16H6O10V2 (found (calculated)%): C 41.5(41.8), H 1.5(1.3), N 0.0(0.0).
In situ single-crystal diffraction and structure determination
A single crystal of MFM-300(VIII) was selected and glued onto a MiTeGen loop with Loctite Double Bubble epoxy. This was inserted into the holder of the Advanced Light Source gas environmental cell at Beamline 11.3.1, comprising a 50 μm quartz glass tube coupled to gas handling and vacuum equipment. The cell was attached to a Bruker D8 diffractometer with a PHOTON100 CMOS detector on Beamline 11.3.1 at the Advanced Light Source equipped with an Oxford Cryosystems Cryostream 800 plus. Spheres of data were collected with λ=0.7749 Å radiation, from a channel cut Silicon [111] monochromator, at various sample temperatures and pressures. The in situ oxidation was carried out in a flow-type gas cell via flowing air through the cell that was heated at 150 °C for 2 h (see Supplementary Method for more details of structure determination).
EPR measurements
X-band (9.86 GHz) EPR spectra were recorded on powder samples of MFM-300(VIII) and MFM-300(VIV) at room temperature, using a BrukerEMX Micro EPR spectrometer equipped with an X-band microwave bridge, a high-Q resonator and a 1.0 T electromagnet. The microwave frequency was measured with a built-in digital counter and the magnetic field was calibrated using a Bruker strong pitch reference sample (g=2.0028). Modulation amplitude and microwave power used were 3 G and 2 mW, respectively. Data were analysed with the Bruker Win EPR Simfonia package.
Neutron powder diffraction
NPD experiments were undertaken at the WISH diffractometer at the ISIS Facility. MFM-300(V) was loaded into a 6 mm diameter vanadium sample can and outgassed at 1 × 10−7 mbar and 100 °C for 1 day. The sample was then loaded into a liquid helium cryostat and cooled to 7 K for data collection. CO2 gas was introduced by warming the samples to 290 K, and the gas was dosed volumetrically from a calibrated volume. The gas-loaded sample was then cooled to 7 K over a period of 2 h to ensure good mobility of adsorbed CO2 within the crystalline structure of MFM-300(V). The sample was kept at 7 K for an additional half an hour before data collection to ensure the thermal equilibrium (see Supplementary Method for more details).
Inelastic neutron scattering
INS experiments were undertaken using the TOSCA spectrometer at the ISIS Facility. MFM-300(V) was loaded into an 11 mm diameter vanadium sample can and outgassed at 1 × 10−7 mbar and 100 °C for 1 day. The sample was loaded into a helium closed cycle refrigerator cryostat and cooled to 11 K for data collection. CO2 gas was introduced by warming the samples to 290 K, and the gas was dosed volumetrically from a calibrated volume. The gas-loaded sample was then cooled to 11 K over a period of 2 h to ensure good mobility of adsorbed CO2 within the crystalline structure of MFM-300(V). The sample was kept at 11 K for an additional half an hour before data collection to ensure the thermal equilibrium (see Supplementary Method for more details of DFT Calculation for INS spectra).
Infrared measurements of gas-loaded MFM-300(V)
Infrared spectroscopic measurements of crystals of MFM-300(VIII) and MFM-300(VIV) were carried out using a Bruker Hyperion 3000 microscope equipped with an LN2 cooled MCT detector, coupled to a Bruker Vertex spectrometer supplied with broad band radiation from beamline B22 of the Diamond Light Source. Experiments were carried out using a Linkam FTIR600 environmental gas stage under a constant (100 cm3 min−1) flow of dry He. The desolvated sample was generated in situ by heating the sample to 393 K for 2 h, and 256 scan spectra were collected at 298 K.
Data availability
Single crystal data of MFM-300(VIII) and MFM-300(VIV) are deposited at Cambridge Crystallographic Data Centre (CCDC) with numbers of 1479680–1479681, and numbers of 1481144–1481147 are for CO2-loaded MFM-300(V) samples obtained from NPD. The data that support the findings of this study are available from the corresponding author on request.
Additional information
How to cite this article: Lu, Z. et al. Modulating supramolecular binding of carbon dioxide in a redox-active porous metal-organic framework. Nat. Commun. 8, 14212 doi: 10.1038/ncomms14212 (2017).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Davis, M. E. Ordered porous materials for emerging applications. Nature 417, 813–821 (2002).
Zhou, H. C., Long, J. R. & Yaghi, O. M. Introduction to metal-organic frameworks. Chem. Rev. 112, 673–674 (2012).
Férey, G. Why hybrid porous solids capture greenhouse gases. Chem. Soc. Rev. 40, 550–562 (2011).
Ma, X. & Zhao, Y. Biomedical applications of supramolecular systems based on host-guest interactions. Chem. Rev. 115, 7794–7839 (2015).
Pantatosaki, E. Probing the hydrogen equilibrium and kinetics in zeolite imidazolate frameworks via molecular dynamics and quasi-elastic neutron scattering experiments. J. Chem. Phys. 138, 034706 (2013).
Li, W. & Zhao, D. An overview of the synthesis of ordered mesoporous materials. Chem. Commun. 49, 943–946 (2013).
Wan, Y., Yang, H. & Zhao, D. ‘Host−Guest’ chemistry in the synthesis of ordered nonsiliceous mesoporous materials. Acc. Chem. Res. 39, 423–432 (2006).
Nugent, P. et al. Porous materials with optimal adsorption thermodynamics and kinetics for CO2 separation. Nature 495, 80–84 (2013).
Mason, J. A. et al. Methane storage in flexible metal-organic frameworks with intrinsic thermal management. Nature 527, 357–361 (2015).
McDonald, T. M. et al. Cooperative insertion of CO2 in diamine-appended metal-organic frameworks. Nature 519, 303–308 (2015).
Nguyen, N. T. T. et al. Selective capture of carbon dioxide under humid conditions by hydrophobic chabazite-type zeolitic imidazolate frameworks. Angew. Chem. Int. Ed. 53, 10645–10648 (2014).
Foo, M. L. et al. An adsorbate discriminatory gate effect in a flexible porous coordination polymer for selective adsorption of CO2 over C2H2 . J. Am. Chem. Soc. 138, 3022–3030 (2016).
Yanai, N. et al. Gas detection by structural variations of fluorescent guest molecules in a flexible porous coordination polymer. Nat. Mater. 10, 787–793 (2011).
Cho, H. S. et al. Extra adsorption and adsorbate superlattice formation in metal-organic frameworks. Nature 527, 503–507 (2015).
Gassensmith, J. J. et al. A metal-organic framework-based material for electrochemical sensing of carbon dioxide. J. Am. Chem. Soc. 136, 8277–8282 (2014).
Wang, Z. & Cohen, S. M. Post synthetic modification of metal-organic frameworks. Chem. Soc. Rev. 38, 1315–1329 (2009).
Islamoglu, T. et al. Systematic post synthetic modification of nanoporous organic frameworks for enhanced CO2 capture from flue gas and landfill gas. J. Phys. Chem. C 120, 2592–2599 (2016).
Liu, T.-F. et al. Stepwise synthesis of robust metal-organic frameworks via post-synthetic metathesis and oxidation of metal nodes in a single-crystal to single-crystal transformation. J. Am. Chem. Soc. 136, 7813–7816 (2014).
Falkowski, J. M., Wang, C. & Lin, W. Actuation of asymmetric cyclopropanation catalysts: reversible single-crystal to single-crystal reduction of metal-organic frameworks. Angew. Chem. Int. Ed. 50, 8674–8678 (2011).
Barthelet, K., Marrot, J., Riou, D. & Férey, G. A breathing hybrid organic-inorganic solid with very large pores and high magnetic characteristics. Angew. Chem. Int. Ed. 41, 281–284 (2002).
D'Alessandro, D. M. Exploiting redox activity in metal–organic frameworks: concepts, trends and perspectives. Chem. Commun. 52, 8957–8971 (2016).
Brozek, C. K. & Dincă, M. Ti3+-, V2+/3+-, Cr2+/3+-, Mn2+-, and Fe2+-substituted MOF–5 and redox reactivity in Cr- and Fe-MOF-5. J. Am. Chem. Soc. 135, 12886–12891 (2013).
Bloch, E. D. et al. Selective binding of O2 over N2 in a redox-active metal-organic framework with open iron(II) coordination sites. J. Am. Chem. Soc. 133, 14814–14822 (2011).
Vaidhyanathan, R. et al. Direct observation and quantification of CO2 binding in an amine modified nanoporous solid. Science 330, 650–653 (2010).
Van Der Voort, P. et al. Vanadium metal-organic frameworks: structures and applications. New J. Chem. 38, 1853–1867 (2014).
Yang, S. et al. Selectivity and direct visualization of carbon dioxide and sulfur dioxide in a decorated porous host. Nat. Chem. 4, 887–894 (2012).
Krap, C. P. et al. Enhancement of CO2 adsorption and catalytic properties by Fe-doping of [Ga2(OH)2(L)] (H4L=biphenyl-3,3′,5,5′-tetracarboxylic acid), MFM-300(Ga2). Inorg. Chem. 55, 1076–1088 (2016).
Savage, M. et al. Selective adsorption of sulphur dioxide in a robust metal-organic framework material. Adv. Mater. 28, 8705–8711 (2016).
Leclerc, H. et al. Influence of the oxidation state of the metal center on the flexibility and adsorption properties of a porous metal organic framework: MIL-47(V). J. Phys. Chem. C. 115, 19828–19840 (2011).
Tregenna-Piggott, P. L. W. et al. High-field, multifrequency EPR study of the vanadium(III) hexaaqua cation. Inorg. Chem. 38, 5928–5929 (1999).
Sumida, K. et al. Carbon dioxide capture in metal-organic frameworks. Chem. Rev. 112, 724–781 (2012).
Simon, A. & Peters, K. Single-crystal refinement of the structure of carbon dioxide. Acta Crystallogr. B 36, 2750–2751 (1980).
Millward, A. R. & Yaghi, O. M. Metal-organic frameworks with exceptionally high capacity for storage of carbon dioxide at room temperature. J. Am. Chem. Soc. 127, 17998–17999 (2005).
Acknowledgements
We thank EPSRC, ERC and University of Manchester for funding. We thank EPSRC for funding of the UK National EPR Facility at Manchester. We are especially grateful to STFC and the ISIS Neutron Facility for access to the Beamlines TOSCA and WISH, to Diamond Light Source for access to Beamline B22, to the Advanced Light Source for access to Beamline 11.3.1 and to ORNL for access to Beamline VISION. The computing resources were made available through the VirtuES (Virtual Experiments in Spectroscopy) project, funded by Laboratory Directed Research and Development program (LDRD 7739) at the Oak Ridge National Laboratory. The Advanced Light Source is supported by the Director, Office of Science, Office of Basic Energy Sciences, of the U.S. Department of Energy under Contract No. DE-AC02-05CH11231. The development of the gas cell used in this work was partially funded by the Center for Gas Separations Relevant to Clean Energy Technologies, an Energy Frontier Research Center funded by the U.S. Department of Energy, Office of Science, Basic Energy Sciences under Award # DE-SC0001015.
Author information
Authors and Affiliations
Contributions
Z.L., H.G.W.G., T.L.E.: syntheses, characterization of MOF samples, measurements and analysis of adsorption isotherms. Z.L., S.J.T., K.J.G. and S.Y.: syntheses, collection and analysis of single crystal structures. Z.L., F.T., and E.J.L.M.: collection and analysis of the EPR data. M.Sa., T.L.E. and M.D.F.: collection of synchrotron IR data. Z.L., H.G.W.G., I.S., Y.C., M.Sa., P.M., S.R., A.J.R.-C, S.Y.: collection and analysis of neutron scattering data. S.Y. and M.Sc.: overall direction and design of project. Z.L., S.Y. and M.Sc. with all authors: preparation of the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures, Supplementary Tables, Supplementary Methods and Supplementary References (PDF 1782 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Lu, Z., Godfrey, H., da Silva, I. et al. Modulating supramolecular binding of carbon dioxide in a redox-active porous metal-organic framework. Nat Commun 8, 14212 (2017). https://doi.org/10.1038/ncomms14212
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms14212
- Springer Nature Limited
This article is cited by
-
Construction of C-C bonds via photoreductive coupling of ketones and aldehydes in the metal-organic-framework MFM-300(Cr)
Nature Communications (2021)
-
MOFs in the time domain
Nature Reviews Chemistry (2021)
-
Structural dynamics of a metal–organic framework induced by CO2 migration in its non-uniform porous structure