Triangulation has been determined for the Al2O3 ― ZrO2 ― La2O3 system, and 1250 and 1650°C isothermal sections of the phase diagram have been constructed. The LaAlO3 ― La2Zr2O7 section is quasibinary, while the LaAlO3 ― T-ZrO2 and La2O3 ·11Al2O3 ― T-ZrO2 ones are partially quasibinary. The triangulation of the ternary system is based on ZrO2 and a phase containing it. No ternary compounds or regions of ternary solid solutions have been identified.
Similar content being viewed by others
REFERENCES
M. Hrovat, D. Kuscer, J. Hoic, et al., “Preliminary data on subsolidus phase equilibria in the La2O3 -(Al2O3/Fe2O3) -Y2O3 and La2O3 ?(Al2O3/Fe2O3) -ZrO2 systems,” Mater. Sci. Lett., 15, No. 4, 339-342 (1996).
N. Q. Minh, “Ceramic fuel cells,” J. Amer. Ceram. Soc., 76, No. 3, 563-588 (1993).
S. N. Lakiza, L. M. Lopato, and A. V. Shevchenko, “Interactions in the Al2O3-ZrO2-La2O3 system,” Poroshk. Metall., Nos. 9-10, 46-51 (1994).
I. A. Bondar' and N. V. Vinogradova, “Phase equilibria in the lanthanum oxide-alumina system,” Izv. AN SSSR, Ser. Khim., No. 5, 785-790 (1964).
M. Mizuno, R. Berjoar, J. P. Coutures, and M. Foex, “Phase diagram of the system Al2O3-La2O3 at elevated temperatures,” J. Ceram. Soc. Jpn., 82, No. 12, 631-636 (1974).
R. C. Ropp and G. G. Libowitz, “The nature of the alumina-rich phase in the system La2O3-Al2O3,” J. Amer. Ceram. Soc., 61, No. 11-12, 473-475 (1978).
O. Yamaguchi, K. Sagiura, A. Mitsui, and K. Shimizu, “New compound in the system La2O3-Al2O3,” J. Amer. Ceram. Soc., 68, No. 2, C44-C45 (1985).
A. Rouanet, “Etude de la refractairite et de la structure des phases de haute temperature presentées par le systeme zircone-oxide de lanthane,” Compt. Rendus, 267, No. 5, Ser. C, 395-397 (1968).
A. Rouanet, “Contribution a l'étude des systemes zircone-oxides des lanthanides au voisinage de la fusion,” Rev. Int. Hautes Temp. et Refract., 8, No. 2, 161 (1971).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Lakiza, S.M., Lopato, L.M. Interactions in the Al2O3 ― ZrO2 ― La2O3 System at 1250 and 1650°C. Powder Metallurgy and Metal Ceramics 39, 403–406 (2000). https://doi.org/10.1023/A:1026621808456
Issue Date:
DOI: https://doi.org/10.1023/A:1026621808456