Abstract
In the present work; the viscosities in the quaternaries CaO–Fe n O–MgO–SiO2, Fe n O-MgO–MnO–SiO2, and CaO–MgO–MnO–SiO2 and the quinary CaO–Fe n O–MgO–MnO–SiO2 were studied. The experimental technique employed was the well-established rotating cylinder method, using a Brookfield digital viscometer mounted over a specially designed graphite furnace. Generally, iron crucibles were used along with iron spindles. Periodic calibrations of the experimental setup were made using the standard reference slag recommended by the European Union. The measurement's were carried out up to a maximum temperature of 1773 K in all cases. The reliability of the measurements were checked at different rotation speeds as well as during thermal cycling, and excellent reproducibility of the results was noted. The experimental viscosity values were incorporated into a viscosity model. Equations based on the model for calculating the viscosities of the quarternary systems CaO–Fe n O–MgO–SiO2, Fe n O–MgO–MnO–SiO2, and CaO–MgO–MnO–SiO2 and the quinary system CaO–Fe n O–MgO–MnO–SiO2 are provided.
Similar content being viewed by others
REFERENCES
Du Sichen, J. Bygden, and S. Seetharaman, Met. Mat. Trans. B 25:1 (1994).
F.-Z. Ji, Du Sichen, and S. Seetharaman, TRATA MEL 176:April (1997), Theoretical Metallurgical Metallurgy, Royal Institute of Technology, Stockholm, Sweden.
F.-Z. Ji, Du Sichen, and S. Seetharaman, Met. Mat. Trans. B 28:827 (1997).
F.-Z. Ji, Du Sichen, and S. Seetharaman, Ironmaking and Steelmaking (in press, 1998).
I. Tanabe, K. Oku, and T. Honda, J. Electrochem. Soc. Japan 28:E288 (1960).
E. M. Levin, C. R. Robbins, and H. F. McMurbie, Phase Diag. ceram. Am. Ceram. Soc. 1:38 (1964).
K. C. Mills and A. A. Shirali, SRM for High Temperature Viscosities Measurements—Results for Phase 3 of the Interlaboratory Comparison Programme, NPL report (National Physical Laboratory, Teddington, Middlesex, UK, 1993).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Ji, FZ., Sichen, D. & Seetharaman, S. Viscosities of Multicomponent Silicate Melts at High Temperatures. International Journal of Thermophysics 20, 309–323 (1999). https://doi.org/10.1023/A:1021419406512
Issue Date:
DOI: https://doi.org/10.1023/A:1021419406512