Abstract
Aluminium powder has been attrition milled in the presence of 1.5 wt% of a wax. The aim was to achieve a mechanically alloyed powder amenable to powder metallurgy processing. Changes in particle size and form, microstructure, hardness and other properties of powders with milling time has been studied. Under the experimental conditions employed, a process time of 10 h was selected for the mechanical alloying of Al powder. The powder milled in this way shows a Vickers microhardness (127 HV) more than six times higher than the starting powder (20 HV), a coarser particle size (mean particle size is doubled) and a better flowability.
Similar content being viewed by others
References
J. S. BENJAMIN,Metall. Trans. 1 (1970) 2943.
J. S. BENJAMIN and M. J. BOMFORD,Metall. Trans. A 8 (1977) 1301.
G. JANGG,Aluminium 51 (1975) 641.
P. S. GILMAN, PhD Thesis, Stanford University, Stanford (1979).
R. F. SINGER, W. C. OLIVER and W. D. NIX,Metall. Trans. A 11 (1980) 1895.
E. A. BLOCH,Metall. Rev. 6 (1961) 193.
F. H. FROES and C. SURYANARAYANA,Metal Powder Rep. 49 (1994) 14.
G. NAESER,Int. J. Powder Metall. 6 (1970) J1.
R. SCHRADER,Technik 24 (1969) 88.
A. SZEGVARI, US Patent 2, 764,359, 25 September (1956).
J. S. BENJAMIN and T. E. VOLIN,Metall. Trans. 5 (1974) 1929.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
RODRIGUEZ, J.A., GALLARDO, J.M. & HERRERA, E.J. Structure and properties of attrition-milled aluminium powder. Journal of Materials Science 32, 3535–3539 (1997). https://doi.org/10.1023/A:1018653607670
Issue Date:
DOI: https://doi.org/10.1023/A:1018653607670