The effect of grinding on the catalytic properties of La0.8Sr0.2MnO3±λ powders prepared via a ceramic or sol–gel process was studied with respect to the carbon black combustion temperature (T C). For the ceramic process, a milling time of 5 h led to a decrease of 77°C in the T C (from 615 to 538°C) in relation with increasing BET surface area. Regarding the sol–gel process, the T C decreased from 535 to 505°C after 1 h of grinding. Nevertheless, upon further milling (10 h), the benefit of the grinding effect disappeared due to a continuous decrease in the BET surface area. Finally, grinding (when well controlled) enabled one to obtain ceramic powders showing performances as good as sol–gel materials (T C≈540°C).
Similar content being viewed by others
References
V.D. Rao, J.E. White, W.R. Wade, M.G. Aimone and H.A. Cikanek, SAE Technical Paper series no. 850014 (1985).
M.R. Montierth, SAE Technical Paper series no. 840072 (1984).
Y. Watabe, K. Irako, T. Miyajima and T. Yoshimoto, SAE Technical Paper series no. 830082 (1983).
W. Sri Rahayu, Ph.D. thesis, Compiègne (1994).
B.J. Cooper and J.E. Thoss, SAE Technical Paper series no. 890404 (1989).
R.J.H. Voorhoeve, J.P. Remeika and L.E. Trimble, Annals New York Acad. Sci. 272 (1996).
R.J.H. Voorhoeve, J.P. Remeika, L.E. Trimble, A.S. Cooper, F.J. Disalvo and P.K. Gallagher, J. Solid State Chem. 14 (1975) 395.
W. Sri Rahayu, L. Monceaux, B. Taouk and P. Courtine, CAPoC3. Stud. Surf. Sci. Catal. 96 (1995) 563.
T. Hibino, K. Suzuki, K.I. Ushiki, Y. Kuwahara and M. Mizuno, Appl. Catal. A 145 (1996) 297.
H. Arai, T. Yamada, K. Eguchi and T. Seiyama, Appl. Catal. A 26 (1986) 265.
L.W. Tai and P.A. Lessing, Mater. Res. Soc. Symp. Proc. 7 (1992) 502.
F. Padella, E. Incocciati, C.A. Nannetti, C. Colella, S. Casadio and M. Magini, Mater. Sci. Forum 269-272 (1992) 105.
L.A. Isupova, V.A. Sadykov, E.G. Avvakumov and N.V. Kosova, Chem. Sust. Devel. 6 (1998) 199.
G.K. Williamson and W.H. Hall, Acta Metall. 1 (1922) 22.
V.V. Boldyrev, J. Chim. Phys. 8 (1986) 820.
Y.G. Shirokov, Russ. J. Appl. Chem. 70 (1997) 919.
L. Aymard, B. Beaudoin, B. Dumont and A. Delahaye-Vidal, J. Mater. Chem. 6 (1996) 1537.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Soiron, S., Aymard, L., Rougier, A. et al. Mechanical Activation of Perovskite-Type Oxides for Catalytic Combustion. Topics in Catalysis 16, 391–395 (2001). https://doi.org/10.1023/A:1016633704286
Issue Date:
DOI: https://doi.org/10.1023/A:1016633704286