Coating of CaTiO₃ on titanium substrates by hydrothermal reactions using calcium-ethylene diamine tetra acetic acid chelate

Abstract

Titanium plates were treated in [Ti(O₂)EDTA]^2-– -Ca(EDTA)^2- mixed solutions and/or Ca(EDTA)^2- solutions (where EDTA is ethylene diamine tetra acetic acid) at pH 9–13 and 150–250 °C for 0.5–12 h. The film, about 50 μm thick, and consisting of mixtures of CaTiO₃ and TiO₂ was formed in 0.01 M [Ti(O₂)EDTA]^2- – 0.01 M Ca(EDTA)^2- mixed solution at pH 13 and 250 °C for 6 h. The film consisted of large icosahedral and hexagonal particles, of about 10 μm diameter, and small aggregated particles, of about 1 μm diameter. On the other hand, the film, about 20 μm thick, consisted of hexagonal plate-like CaTiO₃ particles, of about 1 μm diameter, was formed in 0.01 M Ca(EDTA)^2- solution at pH 13 and 250 °C for 6 h. The thickness of both films increased with time, where the film formation rate in 0.01 M [Ti(O₂)EDTA]^2- – 0.01 M Ca(EDTA)^2- mixed solution was much faster. The CaTiO₃ film formed on the surface of titanium promoted the precipitation of hydroxyapatite on the substrate by the hydrothermal reactions in Ca(EDTA)^2-–PO ^3-₄ mixed solutions.