Abstract
The effects of the addition of aluminum and natural aging on the tensile properties of Sn-9Zn and Sn-9Zn-0.5Al were investigated in rapidly solidified bulk specimens. Because oxidation occurs from the eutectic cell boundary of the surface and grows simultaneously into the subsurface with increased aging time, the deterioration of the tensile properties of Sn-9Zn and Sn-9Zn-0.5Al specimens correspond to the number of days it is naturally aged. The fracture characteristics of tensile fracture surface change from ductile dimples to partially dimpled and partially intergranular. The intergranular fracture behavior is attributed to the tensile cracks initiated from the surface cell boundary, cracks caused by cell boundary oxidation. This result indicates the depth of boundary oxidation that can be promoted by alloyed 0.5% aluminum.
Similar content being viewed by others
References
M. MCCORMACK, S. JIN and H. S. CHEN, J. Elec. Mater. 23 (1994) 687.
M. MCCORMACK and S. JIN, ibid. 23 (1994) 635.
Y. NAKAMURA, in Inter. Elec. Devi. and Mater. Sym. Conf., Taiwan, 1998, p. 340.
E. P. WOOD and K. L. NIMMO, J. Elec. Mater. 23 (1994) 709.
A. SEBAOUN, D. VINCENT and D. TREHEUX, Mater. Sci. and Tech. 3 (1987) 241.
K. L. LIN, L. H. WEN and T. P. LIU, J. Elec. Mater. 27 (1998) 97.
K. L. LIN and L. H. WEN, J. Mater. Sci.—Mater. Elec. 9 (1998) 5.
B. T. LAMPLE, Weld. Res. (1976) 330s.
D. A. JONES, in “Principles and Prevention of Corrosion,” edited by D. Johnstone (Macmillan, London, 1992) p. 43. Received 20 June 2000 and accepted 3 August 2001 195
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Chuang, C.M., Lui, T.S. & Chen, L.H. Effect of aluminum addition on tensile properties of naturally aged Sn-9Zn eutectic solder. Journal of Materials Science 37, 191–195 (2002). https://doi.org/10.1023/A:1013143218738
Issue Date:
DOI: https://doi.org/10.1023/A:1013143218738