Abstract
In the present work the effects of weld strength undermatch on fracture toughness of heat affected zone (HAZ) have been studied. In the investigation a high strength low alloyed steel (HSLA) with 800 MPa strength class was used, and the undermatched welded joints were made with two weld strength mismatch levels. Three-point bending test specimens with crack depth to specimen width ratio a/W ranging from 0.05 to 0.5 were extracted from the welded joints. The test results show that strength mismatching gives an obvious influence on the fracture toughness of coarse grained HAZ for the undermatched joints. The lower the weld strength mismatching, the higher the fracture toughness of the HAZ. In addition the tendency of fracture toughness change with crack depths is much the same as in previous studies on base metals or weld metals, that is, fracture toughness of the HAZ is increased with reduction of crack depths. From the measured results it shows that the macroscopically mechanical heterogeneity of the welds may have more important influence on the fracture toughness of the HAZ than the meso-heterogeneity in the reheated coarse grained HAZ. Furthermore, numerical verification indicates that the stress triaxiality at crack tip may be the essential reason for the change of fracture toughness of HAZ. It is also shown that the yield strength of HAZ determined by the limit load in the three-point bend test represents the combinative effects of HAZ and its surrounding materials.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Denys, R., Lefevre, A., Kvaale, P.E. and Lian, B. (1994). Effects of weldmetal matching on the fracture behavior of HAZ notched CTOD and wide plate specimens, Mis–Matching of Welds, ESIS 17. (Edited by K.H. Schwalbe and M. Kocak). Mechanical Engineering Publications, London, 445–460.
Rykalin, N.N. (1951). Calculation of Thermal Process During Welding, Moscow, Mashgiz, (in Russian).
Shi, Y.W. and Han, Z.X. (1993). Effect of weld metal strength on the fracture toughness of heat affected zone in a HSLA steel welds. Proc. Int. Conf.Mismatch `93, Reinstorf, Luneburg, Germany (26–28 May).
Shi, Y.W. and Han, Z.X. (1993). The effects of crack depth on the J–integral and CTOD fracture toughness for welded bend specimens. Fatigue and Fracture of Engineering Materials and Structures 16, 281–287.
Shi, Y.W., Han, Z.X. and Zhou, N.N. (1996). Estimates of local tensile strength of welded joints. Journal of Pressure Vessel and Piping 65, 41–45.
Sumpter, J.D.G. (1987). J–determination for shallow notch welded bend specimens. Fatigue and Fracture of Engineering Materials and Structures 10, 479–493.
Thaulow, C., Paauw, A.J., Hauge, M., Toyoda, M. and Minami, F. (1994). Fracture property of HAZ–notched weld joint with mechanical mismatching (Part 2), Mis–Matching of Welds, ESIS 17. (Edited by K.H. Schwalbe and M. Koçak), Mechanical Engineering Publications, London, 417–432.
Toyoda, M., Minami, F., Ruggieri, C., Thaulow, C. and Hauge, M. (1994). Fracture property of HAZ–notched weld joint with mechanical mismatching (Part 1), Mis–Matching of Welds, ESIS 17. (Edited by K.H. Schwalbe and M. Koçak), Mechanical Engineering Publications, London, 399–415.
Tseng, M.K. and Marcus, H.L. (1982). A single specimen determination of J1cfor aluminum alloys. Engineering Fracture Mechanics 16, 895–903.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Shi, Y., Han, Z. & Fu, J. Effects of weld strength undermatch on fracture toughness of HAZ notched weldments in a HSLA steel. International Journal of Fracture 91, 349–358 (1998). https://doi.org/10.1023/A:1007411221854
Issue Date:
DOI: https://doi.org/10.1023/A:1007411221854