Abstract
Applying Linear Elastic Fracture Mechanics equations and sample compliance variation to quantify the instantaneous crack length, the R-curve behavior of alumina-mullite-zirconia composites obtained by reaction sintering, was evaluated as a function of zirconia and mullite content. Changes in the R-curve profile as a function of the notch geometry (Chevron and straight-through notch) was observed and discussed, based on the analysis of the y(α) function applied to each notch type. The influence of the y(α) function in the R-curve shape was observed in both the initial and the final crack propagation region where, in the latter, the R-curves presented a sharp increase. In order to suppress these effects, the R-curve values for pure alumina were deducted from those obtained for the different composites produced. The analysis of the resulting curves highlights the influence of the amount of zirconia and mullite inclusions in these composites.
Similar content being viewed by others
References
E. D. Zanotto and A. R. Migliore, Cerâ mica 37 (1991) 247.
A. G. Evans and R. M. Cannon, Acta. Metal. 34 (1986) 5.
E. C. Subbarao in “Science and Technology of Zirconia-Advances in Ceramics”, Vol. 3, edited by A. H. Heuer and L. W. Hobbs (Cleveland, Ohio, 1981) p. 1-24.
F. Cambier, C. Baudin, P. Pilati and A. Lerich, Brit. Cer. Trans. Journ. 83 (1984) 196.
S. Prochaska, J. S. Wallace and N. Claussen, Jour. of the Amer. Ceram. Soc. 66[N-8] c125-7.
M. Sakai and R. C. Bradt, Journ. of Ceram. Soc. Jap. Int. 96 (1988) 779. 7. Standard Test Method for Plane Strain Fracture Toughness of Metallic Materials ASTM E-399 (1981).
P. S. Shah and C. Ouyang, Journ. Eng. Mat. and Tech. 115 (1993) 300.
Rilem Draft Recommendations, TC 89-FMT, Materials and Structures 23 (1990) 457.
H. HÑbner and W. Jillek, Journ. of Mat. Sci. 12 (1977) 117.
M. F. A. Magon, J. A. Rodrigues and V. C. Pandolfelli, Proceedings of the 39th Congresso Brasileiro de Cerâ micas, Águas de Lindó ia, SP, Brazil (Associa¸cã o Brasileira de Cerâ micas, 1995). Vol I, p. 478.
A. C. A. Mazzei and J. A. Rodrigues, J. Mater. Sci. 35 (2000) 2807.
J. A. Rodrigues, E. R. Zamprogno and V. C. PANDOLFELLI, Proceedings of the 41st Congresso Brasileiro e Cerâ micas, Sã o Paulo-SP, Brazil, junho de 1997 (Associaç ã o Brasileira de Cerâ mica, 1997) Vol II, p. 510.
J. E. Srawley and B. Gross, ASTM STP601 (American Ceramic Society for Testing and Materials, 1976) p. 559.
L. P. Pook. Int. J. Fract. Mechanics. 8 (1972) 103.
F. W. Kleinlein and H. Hubner, Fracture 3 (1977) 19.
R. W. Steinbrech, “R-Curve Behavior of Ceramics” in “Fracture Mechanics of Ceramics”, Vol. 9 edited by R. C. Bradt, D. P. H. Hasselman, D. Munz and M. Sakai, (Plenum Press, NY, 1992) p. 187.
A. C. A. Mazzei, J. A. Rodrigues and V. C. Pandolfelli, Proceedings of the 41st Congresso Brasileiro e Cerâ micas, Sã o Paulo-SP, Brazil, junho de 1997 (Associaç ã o Brasileira de Cerâ mica, 1997) Vol. I, p. 237.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Mazzei, A.C., Rodrigues, J.A. & Pandolfelli, V.C. Alumina-mullite-zirconia composites obtained by reaction sintering Part II. R-Curve behavior. Journal of Materials Science 35, 2815–2824 (2000). https://doi.org/10.1023/A:1004765326780
Issue Date:
DOI: https://doi.org/10.1023/A:1004765326780