Abstract
The reversibility of electrochemical magnesium deposition from Grignard reagents was investigated with regard to potential application of magnesium as a negative electrode in rechargeable batteries. The reoxidation rate depends on the morphology of the magnesium deposit which is controlled by the substrate material. Good results were obtained using silver or gold substrates. Magnesium deposits on these materials was found to be of smooth and compact morphology. A nearly complete electrochemical reoxidation and a low self-discharge were observed.
Similar content being viewed by others
References
J. L. Robinson, in C. N. Cahoon and G. W. Heise (Eds), `The Primary Battery', vol. 2, New York (1976) p.149.
L. Jarvis, J. Power Sources 32 (1990) 271.
T. D. Gregory, R. J. Hoffman and R. C. Winterton, J. Electrochem. Soc. 137 (1990) 775.
J. P. Pereira-Ramos, R. Messina and J. Perichon, J. Electroanal. Chem. 218 (1987) 241.
P. Novak and J. Desilvestro, J. Electrochem. Soc. 140 (1993) 140.
P. Novak, W. Scheifele and O. Haas, Molten Salt Forum 1/2 (1993/94) 389.
M. E. Spahr, P. Novak, O. Haas and R. Nesper, J. Power Sources 54 (1995) 364.
D. M. Overcash and F. C. Mathers, Trans. Electrochem. Soc. 64 (1933) 305.
J. H. Connor, W. E. Reid and G. B. Wood, J. Electrochem. Soc. 104 (1957) 38.
A. Brenner and J. L. Sligh, Trans. Inst. Met. Finish. 49 (1971) 71.
A. Mayer, J. Electrochem. Soc. 137 (1990) 2806.
K. Gneupel, thesis, Merseburg (1985).
J. D. Glender and D. Pletcher, J. Electroanal. Chem. 199 (1986) 93.
H. Gerischer, D. M. Kolb and J. K. Sass, Advances in Physics 27 (1978) 437.
R. Selim and P. Bro, J. Electrochem. Soc. 121 (1974) 1457.
I. Yoshimatsu, T. Hirai and J. Yamaki, ibid. 135 (1988) 2422.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
LIEBENOW , C. Reversibility of electrochemical magnesium deposition from Grignard solutions. Journal of Applied Electrochemistry 27, 221–225 (1997). https://doi.org/10.1023/A:1018464210084
Published:
Issue Date:
DOI: https://doi.org/10.1023/A:1018464210084