Abstract
Thermal diffusion salt-bath vanadizing was finished for Cr12MoV die steel, in order to investigate the properties of vanadium carbide coatings related with the Mo contents in Cr12MoV die steel. Scanning electron microscopic observation reveals that Mo can decrease the growth rate of coating as a carbide forming element. Besides, Mo element can promote grain refinement of the coating. X-ray diffraction analysis shows that the different Mo contents have no influence on the phase structure of the coatings. Energy dispersive spectrum analysis and mechanical properties test show that Mo can diffuse into the coating and make a strengthening effect on the coating.
Similar content being viewed by others
References
Q. B. Zhang, L. Li, S. H. Li, R. Huang, Physical Testing and Chemical Analysis, Part A: Physical Testing, 40 (2004) 202–204.
Z. Z. Zhou, D. J. Kong, F. Yuan, Y. F. Yan, Die & Mould Industry 36 (2010) No. 4, 63–67.
L. W. Tang, M.B. Yang, W. L. Zhao, H. Yang, Z. F. Sun, Die & Mould Manufacture 7 (2007) No. 9, 70–72.
C. K. N. Oliveira, C. L. Benassi, L. C. Casteletti, Surf. Coat. Tech. 201 (2006) 1880–1885.
S. M. Hao, R. Y. Sun, Acta Metall. Sinica 2 (1989) 375–379.
D.J. Kong, C. Z. Zhou, J. China Univ. Min. Tech. 40 (2011) 162–166.
Z. P. Wang, Hot Working Technology 40 (2011) No. 16, 161–163.
X.J. Liu, H. C. Wang, Trans. Mater. Heat Treat. 31 (2010) 150–154.
X.J. Liu, H. C. Wang, D.W. Li, Y. X. Wu, Trans. Mater. Heat Treat. 27 (2006) 119–122.
S. H. Wang, S. T. Jin, J. Hebei Inst. Tech. 20 (1998) 8–14.
L. Liu, L. Lin, S. F. Zhao, Hot Working Technology 23 (1994) No. 3, 32–34.
T. Arai, H. Fujita, Y. Sugimoto, Y. Ohta, Industrial Heating 53 (1986) No. 9, 26–28.
Author information
Authors and Affiliations
Corresponding author
Additional information
Foundation Item: Item Sponsored by National Natural Science Foundation of China (50671012)
Rights and permissions
About this article
Cite this article
Huang, Zt., Tian, Wh. Effects of Mo Contents in Matrix on Microstructure and Properties of Vanadium Carbide Coating Formed by Thermal Diffusion Treatment. J. Iron Steel Res. Int. 21, 104–108 (2014). https://doi.org/10.1016/S1006-706X(14)60016-9
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1016/S1006-706X(14)60016-9