Abstract
The texture evolution of ferritic hot rolled Ti-IF steel during cold rolling was investigated in which the reduction was from 15% to 85%. It was found that a fibre texture was monotonously intensified with the increase in the cold rolling reduction, while γ fibre texture changed in a different way. When the cold rolling reduction was in the range of 15%–35% or 45%–75%. γ fibre texture was strengthened; however, when the cold rolling reduction was 35%–45% or 75%–85%, the intensity of γ fibre was reduced. The γ fibre displayed a maximum intensity for the reduction of 75%, and the highest average plastic strain ratio was simultaneously obtained owing to the favorable recrystallization texture.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
Li B L, Godfrey A, Liu Q. et al. Microstructural Evolution of 1F-Steel During Cold Rolling [J]. Acta Materialia. 2004. 52 (4): 1069.
CAI Yan-xia. Study on the Texture. Microstructure and Their Relation of IF Steel Sheet [D]. Shenyang: Northeastern University. 2005 (in Chinese).
Quadir M Z, Tse Y Y, Lam K T. et al. Rolling and Recrystallization Texture of Cold Rolled IF Steel: A Study From Low to High Deformation [J]. Materials Science Forum, 2004, 467–470(1): 311.
Martínez V J, Verdeja J I, Pero-Sanz J A. Interstitial Free Steel: Influence of α-Phase Hot-Rolling and Cold-Rolling Reduction to Obtain Extra-Deep Drawing Quality [J]. Materials Characterization, 2001, 46(1): 45.
LIANG Zhi-de, XU Jia-zhen, WANG Fu. Three Dimensional Orientation Distribution Analysis of Textured Materials [M]. Shenyang: Northeastern University of Technology Press, 1986 (in Chinese).
Roe R J. Description of Crystallite Orientation in Polycrystalline Materials III General Solution to Pole Figure Inversion [J]. Journal of Applied Physics, 1965, 36(6): 2024.
Matsuoka S, Morita M, Furukimi O, et al. Effect of Lubrication Condition on Recrystallization Texture of Ultra-Low C Sheet Hot-Rolled in Ferrite Region [J]. ISIJ International, 1998, 38(6): 633.
Barrett C J. Influence of Lubrication on Through Thickness Texture of Ferritically Hot Rolled Interstitial Free Steel [J]. Ironmaking and Steelmaking, 1999, 26(5): 393.
Eloot K, Okuda K, Sakata K, et al. Texture Evolution During Cold Rolling and Recrystallization of IF Steel With a Strong <1111> Hot Band Texture [J]. ISIJ International, 1998, 33 (6): 602.
Author information
Authors and Affiliations
Corresponding author
Additional information
Foundation Item: Item Sponsored by National Natural Science Foundation of China (50104001)
Rights and permissions
About this article
Cite this article
Zhang, P., Guo, Yh., Wang, Zd. et al. Texture evolution in ferritic rolled Ti-IF steel during cold rolling. J. Iron Steel Res. Int. 17, 44–48 (2010). https://doi.org/10.1016/S1006-706X(10)60043-X
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1016/S1006-706X(10)60043-X