Abstract
The effect of direct ageing treatment on microstructure and stress-rupture properties of GH761 alloy was studied. Phosphorus was added to the tested alloy for its beneficial effect on stress-rupture life. It was found that the grain size of the tested alloy became much finer after direct ageing treatment, in comparison with the commercial GH761 alloy under standard heat treatment condition. The optimum direct ageing treatment has been determined as follows: 830 °C × 4 h, air cooling + 720 °C × 24 h, air cooling. After such treatment, the higher stress-rupture properties of the test alloy at 650 °C, 690 MPa were obtained. The role of phosphorus is still effective under the condition of direct ageing treatment.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
SUN Wen-ru. Effect of P, S and Si on the Solidification, Segregation and Mechanical Properties in GH761 Alloy [D]. Shenyang: Institute of Metal Research, the Chinese Academy of Sciences, 1993 (in Chinese).
HU Zhuang-qi, SUN Wen-ru, GUO Shou-ren. Effect of P, S and Si on the Solidification, Microstructure and Properties in Fe-Ni Base Superalloys [J]. Acta Metall Sin (English Letters), 1996, 9: 443.
SUN Wen-ru, GUO Shou-ren, LU De-zhong, et al. Effect of Phosphorous on the Microstructure and Stress-Rupture Properties in an Fe-Ni-Cr Base Superalloys [J]. Metall Mater Trans, 1997, 28A, 649.
HU Zhuang-qi, SUN Wen-ru, GUO Shou-ren, et al. Effect of Trace P on Fe-Ni Based Wrought Superalloy [J]. Chin J Non-ferrous Met, 2001, 11(6): 947 (in Chinese).
YANG Shu-lin, SUN Wen-ru, GUO Shou-ren, et al. Effect of Phosphorus on Mechanical Properties of GH761 Alloy [J]. Acta Metall Sin, 2005, 41(12): 1249 (in Chinese).
Author information
Authors and Affiliations
Corresponding author
Additional information
Foundation Item: Item Sponsored by National Natural Science Foundation of China (50271072 and 50471083)
Rights and permissions
About this article
Cite this article
Yang, Sl., Sun, Wr., Liu, F. et al. Effect of Direct Ageing Treatment on Stress-Rupture Properties of GH761 Alloy. J. Iron Steel Res. Int. 15, 61–64 (2008). https://doi.org/10.1016/S1006-706X(08)60127-2
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1016/S1006-706X(08)60127-2