Abstract
Al7075−Cu composite joints were prepared by the squeeze overcast process. The effects of melt temperature, die temperature, and squeeze pressure on hardness and ultimate tensile strength (UTS) of squeeze overcast Al7075−Cu composite joints were studied. The experimental results depict that squeeze pressure is the most significant process parameter affecting the hardness and UTS. The optimal values of UTS (48 MPa) and hardness (76 HRB) are achieved at a melt temperature of 800 °C, a die temperature of 250 °C, and a squeeze pressure of 90 MPa. Scanning electron microscopy (SEM) shows that fractured surfaces show flat-faced morphology at the optimal experimental condition. Energy-dispersive spectroscopy (EDS) analysis depicts that the atomic weight percentage of Zn decreases with an increase in melt temperature and squeeze pressure. The optimal mechanical properties of the Al7075−Cu overcast joint were achieved at the Al2Cu eutectic phase due to the large number of copper atoms that dispersed into the aluminum melt during the solidification process and the formation of strong intermetallic bonds. Gray relational analysis integrated with the Taguchi method was used to develop an optimal set of control variables for multi-response parametric optimization. Confirmatory tests were performed to validate the effectiveness of the employed technique. The manufacturing of squeeze overcast Al7075−Cu composite joints at optimal process parameters delivers a great indication to acknowledge a new method for foundry practitioners to manufacture materials with superior mechanical properties.
Article PDF
Similar content being viewed by others
References
Sarfraz M H, Jahanzaib M, Ahmed W, et al. Multi-response parametric optimization of squeeze casting process for fabricating Al 6061−SiC composite. The International Journal of Advanced Manufacturing Technology, 2019, 102(1): 759–773.
Li J H, Sun Y, Wang Y, et al. Optimization of squeeze casting process of gearbox cover based on FEM and Box-Behnken design. The International Journal of Advanced Manufacturing Technology, 2022, 118(9): 3421–3430.
Li Y Y, Zhang W W, Zhao H D, et al. Research progress on squeeze casting in China. China Foundry, 2014, 11(4): 239–246.
Zheng Y, Duan Y P, Liu L D, et al. Growth behavior of Cu/Al intermetallic compounds in hot-dip aluminized copper. Surface and Interface Analysis, 2009, 41(5): 361–365.
Ali M A, Ishfaq K, Raza M H, et al. Mechanical characterization of aged AA2026-AA2026 overcast joints fabricated by squeeze casting. The International Journal of Advanced Manufacturing Technology, 2020, 107(7): 3277–3297.
Ali M A, Jahanzaib M, Wasim A, et al. Evaluating the effects of as-casted and aged overcasting of Al−Al joints. The International Journal of Advanced Manufacturing Technology, 2018, 96(1–4): 1377–1392.
Liu T, Wang Q D, Sui Y D, et al. Microstructure and mechanical properties of overcast 6101–6101 wrought Al alloy joint by squeeze casting. Journal of Materials Science & Technology, 2016, 32(4): 298–304.
Liu T, Wang Q D, Sui Y D, et al. An investigation into aluminum-aluminum bimetal fabrication by squeeze casting. Materials & Design, 2015, 68: 8–17.
Papis K, Hallstedt B, Lffler J F, et al. Interface formation in aluminium-aluminium compound casting. Acta Materialia, 2008, 56(13): 3036–3043.
Papis K, Löffler J F, and Uggowitzer P J. Interface formation between liquid and solid Mg alloys-An approach to continuously metallurgic joining of magnesium parts. Materials Science and Engineering: A, 2010, 527(9): 2274–2279.
Hajjari E, Divandari M, Razavi S H, et al. Dissimilar joining of Al/Mg light metals by compound casting process. Journal of Materials Science, 2011, 46(20): 6491–6499.
Feng J, Ye B, Zuo L J, et al. Bonding of aluminum alloys in compound casting. Metallurgical and Materials Transactions A, 2017, 48(10): 4632–4644.
Hajjari E, Divandari M, Razavi S H, et al. Intermetallic compounds and antiphase domains in Al/Mg compound casting. Intermetallics, 2012, 23: 182–186.
Jiang W, Li G, Fan Z, et al. Investigation on the interface characteristics of Al/Mg bimetallic castings processed by lost foam casting. Metallurgical and Materials Transactions A, 2016, 47(5): 2462–2470.
Liu T, Wang Q D, Sui Y D, et al. An investigation into interface formation and mechanical properties of aluminum-copper bimetal by squeeze casting. Materials & Design, 2016, 89: 1137–1146.
Rohatgi A, Sadayappan K, Clelland D, et al. Joining light metals with polymer composites through metal overcasting. Journal of Materials Processing Technology, 2021: 117257.
Vijian P and Arunachalam V. Optimization of squeeze cast parameters of LM6 aluminium alloy for surface roughness using Taguchi method. Journal of Materials Processing Technology, 2006, 180(1–3): 161–166.
Sarfraz S, Jahanzaib M, Wasim A, et al. Investigating the effects of as-casted and in situ heat-treated squeeze casting of Al−3.5% Cu alloy. The International Journal of Advanced Manufacturing Technology, 2017, 89(9): 3547–3561.
ASTM standards. Philadelphia: American Society for Testing Materials, 1958.
Koerner C, Schwankl M, and Himmler D. Aluminum-aluminum compound castings by electroless deposited zinc layers. Journal of Materials Processing Technology, 2014, 214(5): 1094–1101.
Ali M A, Ishfaq K, and Jawad M. Evaluation of surface quality and mechanical properties of squeeze casted AA2026 aluminum alloy using response surface methodology. The International Journal of Advanced Manufacturing Technology, 2019, 103(9): 4041–4054.
Concer D and Marcondes P. Experimental and numerical simulation study of porosity on high-pressure aluminum die casting process. Journal of the Brazilian Society of Mechanical Sciences and Engineering, 2017, 39(8): 3079–3088.
Arulraj M and Palani P. Parametric optimization for improving impact strength of squeeze cast of hybrid metal matrix (LM24-SiCp-coconut shell ash) composite. Journal of the Brazilian Society of Mechanical Sciences and Engineering, 2018, 40(1): 1–10.
Murray J L. The aluminium-copper system. International Metals Reviews, 1985, 30(1): 211–234.
Mufti N, Ali M A, Raza M H, et al. Analysis of annealing on the micro-porosity and ductility of squeeze-casted Al7050 alloy for the structural applications. Archives of Civil and Mechanical Engineering, 2022, 22(3): 1–16.
Arulraj M, Palani P, and Sowrirajan M. Optimization of squeeze casting parameters of hybrid aluminum matrix composite using Taguchi approach. Proceedings of the Institution of Mechanical Engineers, Part E: Journal of Process Mechanical Engineering, 2021: 235(4): 1073–1081.
Acknowledgements
The authors are very thankful to the Industrial Engineering Department of the University of Engineering & Technology Taxila for providing inspirational guidance, support, and encouragement. They also acknowledged all faculty, staff members, and especially the “Fracture Mechanics and Fatigue Lab’s technical staff members of Mechanical Engineering Department, UET Taxila” for their support and co-operation in performing experiments.
Author information
Authors and Affiliations
Corresponding author
Additional information
Conflict of interest
The authors have no conflicts to declare.
Muhammad Waqas Hanif Male, born in 1996, BSc, MSc Research Scholar. His research interests mainly focus on the evaluation of microstructure and mechanical properties of squeeze overcast 7075 Al−Cu composite joints.
Rights and permissions
About this article
Cite this article
Hanif, M.W., Wasim, A., Sajid, M. et al. Evaluation of microstructure and mechanical properties of squeeze overcast Al7075−Cu composite joints. China Foundry 20, 29–39 (2023). https://doi.org/10.1007/s41230-022-1242-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s41230-022-1242-8
Keywords
- squeeze overcast joints
- Al7075−Cu composite joints
- mechanical properties
- gray relational analysis
- Taguchi method