Abstract
Geopolymer is synthesized by mixing material rich in alumina and silica, such as fly ash, with a highly alkaline solution to form a hardened matrix. However, when using high calcium fly ash as a precursor, a flash set frequently occurs, i.e., the mixture hardens very rapidly before casting can be completed. The use of borax as an additive has been reported due to its potential to prolong the setting time. In this study, the use of a significantly higher dosage of borax is explored. The results show that the addition of borax up to 20% of fly ash, by mass, into the alkaline solution prolongs the setting time by up to 90 min. Conversely, the addition of higher amounts of borax tends to decrease the compressive strength of the geopolymer, whereas adding a small amount of calcium oxide into the mixture increases the strength marginally, especially when the borax content is small. However, the amount of calcium oxide should be limited because at higher content, the effectiveness of borax to prolong the setting time is reduced.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
Antoni, Gunawan R, Hardjito D (2015) Rapid indicators in detecting variation of fly ash for making HVFA concrete. Appl Mech Mater 815:153–157. https://doi.org/10.4028/www.scientific.net/AMM.815.153
Antoni, Wijaya SW, Hardjito D (2016a) Compressive strength of geopolymer based on the fly ash variation. Mater Sci Forum 841:98–103. https://doi.org/10.4028/www.scientific.net/MSF.841.98
Antoni, Wijaya SW, Hardjito D (2016b) Factors affecting the setting time of fly ash-based geopolymer. Mater Sci Forum 841:90–97. https://doi.org/10.4028/www.scientific.net/MSF.841.90
Antoni, Wijaya SW, Satria J, Sugiarto A, Hardjito D (2016c) The use of borax in deterring flash setting of high calcium fly ash based geopolymer. Mater Sci Forum 857:416–420. https://doi.org/10.4028/www.scientific.net/MSF.857.416
Antoni, Herianto JG, Anastasia E, Hardjito D (2017a) Effect of adding acid solution on setting time and compressive strength of high calcium fly ash based geopolymer. AIP Conf Proc 1887:020042. https://doi.org/10.1063/1.5003525
Antoni, Satria J, Sugiarto A, Hardjito D (2017). Effect of variability of fly ash obtained from the same source on the characteristics of geopolymer. In: MATEC web conferences, vol 97, pp 9–13. https://doi.org/10.1051/matecconf/20179701026
Arioz E, Arioz O, Mete Kockar O (2012) An experimental study on the mechanical and microstructural properties of geopolymers. Procedia Engineering 42(August):100–105. https://doi.org/10.1016/j.proeng.2012.07.399
Assi LN, Deaver E, Ziehl P (2018) Using sucrose for improvement of initial and final setting times of silica fume-based activating solution of fly ash geopolymer concrete. Constr Build Mater 191:47–55. https://doi.org/10.1016/j.conbuildmat.2018.09.199
ASTM C191 (2004) Standard test method for time of setting of hydraulic cement by Vicat needle. ASTM International, West Conshohocken, PA. https://doi.org/10.1520/C0191
ASTM C618 (2010) Standard specification for coal fly ash and raw or calcined natural pozzolan for use in concrete. ASTM International, West Conshohocken, PA. https://doi.org/10.1520/C0618
ASTM D5239 (2012) Standard practice for characterizing fly ash for use in soil stabilization, vol 4. ASTM International, West Conshohocken, PA. https://doi.org/10.1520/D5239-04.2
Boonserm K, Sata V, Pimraksa K, Chindaprasirt P (2012) Microstructure and strength of blended FBC-PCC fly ash geopolymer containing gypsum as an additive. SciAsia 38(2):175–181. https://doi.org/10.2306/scienceasia1513-1874.2012.38.175
Chindaprasirt P, Chareerat T, Sirivivatnanon V (2007) Workability and strength of coarse high calcium fly ash geopolymer. Cement Concr Compos 29(3):224–229. https://doi.org/10.1016/j.cemconcomp.2006.11.002
Davidovits J (2008) Geopolymer chemistry and applications. Geopolym Inst, Saint-Quentin
Davidovits J, Davidovits R, Davidovits M (2012) US Patent no US8202362B2. United State of America: US Patent
Diaz EI, Allouche EN, Eklund S (2010) Factors affecting the suitability of fly ash as source material for geopolymers. Fuel 89(5):992–996. https://doi.org/10.1016/j.fuel.2009.09.012
Guo X, Shi H, Dick WA (2010) Compressive strength and microstructural characteristics of class C fly ash geopolymer. Cem Concr Compos 32(2):142–147. https://doi.org/10.1016/j.cemconcomp.2009.11.003
Hardjito Djwantoro, Wallah Steenie E, Sumajouw Dody MJ, Rangan BV (2004) Factors influencing the compressive strength of fly ash-based geopolymer concrete. Civ Eng Dimens 6(2):88–93. https://doi.org/10.9744/ced.6.2
Huang CH, Lin SK, Chang CS, Chen HJ (2013) Mix proportions and mechanical properties of concrete containing very high-volume of Class F fly ash. Constr Build Mater 46:71–78. https://doi.org/10.1016/j.conbuildmat.2013.04.016
Kusbiantoro A, Ibrahim MS, Muthusamy K, Alias A (2013) Development of sucrose and citric acid as the natural based admixture for fly ash based geopolymer. Procedia Environ Sci 17:596–602
Li X, Ma X, Zhang S, Zheng E (2013) Mechanical properties and microstructure of class C fly ash-based geopolymer paste and Mortar. Materials 6(1):1485–1495. https://doi.org/10.3390/ma6041485
Li Z, Zhang W, Wang R, Chen F, Jia X, Cong P (2019) Effects of reactive MgO on the reaction process of geopolymer. Materials 12(3):526. https://doi.org/10.3390/ma12030526
Mustafa M, Bakri A, Mohammed H, Kamarudin H, Niza IK, Zarina Y et al (2011) Review on fly ash-based geopolymer concrete without Portland Cement. J Eng Technol Res 3(1):1–4
Nazari A, Maghsoudpour A, Sanjayan JG (2014) Characteristics of boroaluminosilicate geopolymers. Constr Build Mater 70:262–268. https://doi.org/10.1016/j.conbuildmat.2014.07.087
Nicholson CL, Murray BJ, Fletcher RA, Brew DRM, MacKenzie KJD, Schmücker M (2005) Novel geopolymer materials containing borate structural units. In: World Congress Geopolymer 2005, pp 31–33
Rangan V (2010) Geopolymer concrete with fly ash. In: 2nd International conference on sustainable construction materials and technologies. 3:1493–1504
Rashad AM (2015) A brief on high-volume Class F fly ash as cement replacement—a guide for Civil Engineer. Int J Sustain Built Environ 4(2):278–306. https://doi.org/10.1016/j.ijsbe.2015.10.002
Rattanasak U, Chindaprasirt P (2009) Influence of NaOH solution on the synthesis of fly ash geopolymer. Miner Eng 22(12):1073–1078. https://doi.org/10.1016/j.mineng.2009.03.022
Sethi H, Bansal PP, Sharma R (2018) Effect of addition of GGBS and glass powder on the properties of geopolymer concrete. Trans Civ Eng Iran J Sci Technol. https://doi.org/10.1007/s40996-018-0202-4
Taveri G, Bernardo E, Dlouhy I (2018) Mechanical performance of glass-based geopolymer matrix composites reinforced with cellulose fibers. Materials 11(12):1. https://doi.org/10.3390/ma11122395
Temuujin J, van Riessen A, Williams R (2009) Influence of calcium compounds on the mechanical properties of fly ash geopolymer pastes. J Hazard Mater 167(1–3):82–88. https://doi.org/10.1016/j.jhazmat.2008.12.121
Thunuguntla CS, Gunneswara Rao TD (2018) Appraisal on strength characteristics of alkali-activated GGBFS with low concentrations of sodium hydroxide. Trans Civ Eng Iran J Sci Technol 42(3):231–243. https://doi.org/10.1007/s40996-018-0113-4
Topark-Ngarm P, Chindaprasirt P, Sata V (2015) Setting time, strength, and bond of high-calcium fly ash geopolymer concrete. J Mater Civ Eng 27(7):04014198. https://doi.org/10.1061/(ASCE)MT.1943-5533.0001157
Wattimena OK, Antoni, Wattimena OK (2017) A review on the effect of fly ash characteristics and their variations on the synthesis of fly ash based geopolymer. AIP Conf Proc. https://doi.org/10.1063/1.5003524
Yildirim H, Sümer M, Akyüncü V, Gürbüz E (2011) Comparison on efficiency factors of F and C types of fly ashes. Constr Build Mater 25(6):2939–2947. https://doi.org/10.1016/j.conbuildmat.2010.12.009
Acknowledgements
The authors would like to acknowledge The Ministry of Research, Technology, and Higher Education, Indonesia, for providing financial support for this research.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
On behalf of all authors, the corresponding author states that there is no conflict of interest.
Rights and permissions
About this article
Cite this article
Antoni, A., Purwantoro, A.A.T., Suyanto, W.S.P.D. et al. Fresh and Hardened Properties of High Calcium Fly Ash-Based Geopolymer Matrix with High Dosage of Borax. Iran J Sci Technol Trans Civ Eng 44 (Suppl 1), 535–543 (2020). https://doi.org/10.1007/s40996-019-00330-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40996-019-00330-7