Abstract
Safe, sustainable, and green production of hydrogen peroxide is an exciting proposition due to the role of hydrogen peroxide as a green oxidant and energy carrier for fuel cells. The current work reports the development of carbon dot-impregnated waterborne hyperbranched polyurethane as a heterogeneous photo-catalyst for solar-driven production of hydrogen peroxide. The results reveal that the carbon dots possess a suitable band-gap of 2.98 eV, which facilitates effective splitting of both water and ethanol under solar irradiation. Inclusion of the carbon dots within the eco-friendly polymeric material ensures their catalytic activity and also provides a facile route for easy catalyst separation, especially from a solubilizing medium. The overall process was performed in accordance with the principles of green chemistry using bio-based precursors and aqueous medium. This work highlights the potential of carbon dots as an effective photo-catalyst.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
1 Highlights
-
Polyurethane-supported carbon dots were developed as heterogeneous catalyst, and the developed catalyst was biodegradable.
-
Solar-driven H2O2 production from water, ethanol, and oxygen was achieved.
2 Introduction
Recently, greener, inexpensive, and efficient water splitting techniques have garnered significant interest in the thrust toward sustainable energy conversion processes [1–3]. In this context, photo-catalysis has been adopted as a “green” and “sustainable” technique [4]. In the last few years, much effort has been devoted toward sustainable production of hydrogen peroxide (H2O2) by photo-splitting of water (H2O). In the current scenario of rapid depletion of fossil fuels, sustainable production of H2O2 is very significant. H2O2 can be used as a fuel in one-compartment fuel cells with an output potential of 1.09 V, which is comparable to that of the hydrogen fuel cell with an output value of 1.23 V [5]. Further, H2O2 serves as a clean and green oxidant with H2O as the only by-product [6]. Thus, green and sustainable production of H2O2 is highly desirable for implementation of “green chemistry” principles and can provide a promising prospect for resolving global fuel woes.
In the conventional process, H2O2 is produced by the anthraquinone method, which is highly disadvantageous from the green chemistry point of view. The drawbacks include the multi-step process, and high energy consumption, et cetera [7]. Catalytic systems such as Pd and bi-metallic Au–Pd have been studied for the direct production of H2O2 from H2 and O2 [8–11]. Such direct methods are effective for quantitative production of H2O2, but have an attendant high risk because of the explosive nature of the H2/O2 mixture. Most recently, semiconductor-based nanocatalysts have been used for sustainable production of H2O2 from H2O and alcohols. Such methods involve irradiation of an oxygen (O2)-saturated alcohol or aqueous system under UV light in the presence of metallic semiconductors. State-of-the-art literature cites the use of different metal-based semi-conductor catalysts for sustainable production of H2O2 from H2O and alcohol. These include Ru-complexes, Ir-complexes, Ti nanoparticles, and Ni, et cetera [12–20]. However, the major concerns associated with these catalysts are their high cost, toxicity, metal-based origin, and non-degradable nature. In an effort to introduce metal-free and degradable catalysts, Shiraishi and his group reported polymeric graphitic carbon nitride (g-C3N4) for the production of H2O2 from ethanol [21]. However, the high production cost and low band-gap of g-C3N4 hamper its successful use, especially for splitting H2O under solar irradiation. Thus, the development of an eco-friendly and sustainable catalyst system with the capacity to produce H2O2 is desirable to meet the current challenges.
Carbon dots (CDs), with unique physical, chemical, and optical properties, have attracted immense interest in the scientific community based on their utility in diverse areas, such as bio-imaging, biosensors, light-emitting diodes, and other opto-electrical devices [22–25]. The unique traits of CDs include their excitation wavelength-dependent stable multi-color emission and excellent aqueous solubility with remarkable cytocompatibility. Like other quantum dots, exhibition of the “quantum confinement” effect is the typical signature of CDs. CDs consist predominantly of amorphous carbon along with sp 2 hybridized graphitic carbon. The most fascinating feature of CDs is their capability to harvest photons in the UV/visible spectral region. Such light-harvesting ability renders CDs as a potential candidate for photo-catalytic application [1, 26]. However, in practice, there are certain difficulties in the use of bare CDs as an effective photo-catalyst. CDs are soluble in water or organic solvents like ethanol. This creates serious difficulties in their separation when such media are used. However, in media where CDs are insoluble, CDs suffer solid-state quenching of the photo-activity [27]. Such obstacles restrict the practical applicability of CDs as photo-catalysts.
In this context, the use of a polymeric matrix as a support can facilitate the application of CDs. The polymer matrix can prevent solid-state quenching and also provide sufficient mechanical strength and catalytic stability and facilitate application with easy separation. Such polymer/CD nanocomposite systems have found use in opto-electrical applications. Photo-catalytic applications have also been reported recently [28]. In this regard, we found that the waterborne hyperbranched polyurethane (WPU) system is attractive as a polymer support. The solubility of both the nanomaterial and polymer in the same medium (aqueous) expedites homogeneous distribution of the CDs over the polymer matrix, thereby preserving their photo-harvesting ability. Further, the use of WPU offers additional advantages. During the polymerization reaction, WPU becomes soluble due to the creation of ionic centers along the polymer chains. Thus, it behaves like an ionomer with electron transfer capability. Hence, compared to conventional polymeric systems, WPU is expected to act as a better catalyst support for photo-catalytic reactions.
Herein, a CD-impregnated WPU nanocomposite film is used as a heterogeneous photo-catalyst for solar-driven production of H2O2 by using H2O, C2H5OH, and O2 as raw materials. Further, bacterial degradation of the catalyst is carried out by using Pseudomonas aeruginosa to highlight its eco-friendly behavior. Thus, the present study reports a metal-free, low-cost, easily separable, non-toxic, and biodegradable carbon dot-impregnated polymeric nanocomposite system as a heterogeneous catalyst for sustainable and green production of H2O2.
3 Experimental
3.1 Materials
Isophorone diisocyanate (IPDI, Aldrich, Germany), poly(ethylene glycol) with a number average molecular weight (M n ) of 600 g mol−1 (PEG 600, Merck, India), 2,2-bis(hydroxymethyl) propionic acid (BMPA, Aldrich, Germany), 1,4-butanediol (BD, Merck, India), tannic acid (TA, Sigma-Aldrich, Belgium), triethylamine (TEA, Merck, India), and tetrahydrofuran (THF, Merck, India) were used for WPU preparation. Glycerol-based hyperbranched epoxy (HE) and vegetable oil-based poly(amide amine) (PAA) were used to cross-link the fabricated WPU/CD system [29, 30]. Corms of Colocasia esculenta were used to prepare the CDs. Moreover, ethanol (C2H5OH, Merck, India), Millipore water (H2O, obtained from MilliQ® Ultrapure Water Solutions, Type 1, water purifier system), and oxygen (O2, obtained from Jainex Gas Company, India) were used as starting materials in the photo-catalytic application. Potassium permanganate (KMnO4, Merck, India) was used in the estimation of hydrogen peroxide by following a titrimetric method. In the biodegradation study, the bacterial strain Pseudomonas aeruginosa (strain MTCC 7814) was used. This strain was procured from the Microbial Type Culture Collection and Gene Bank, Chandigarh, India. The bacterial culture was collected through the Department of Molecular Biology and Biotechnology, Tezpur University, India.
3.2 Catalyst Preparation
The CDs were prepared by using corms of C. esculenta as reported earlier [31]. However, a slight modification was made to the synthetic procedure. In order to exert greater control over the particle size and size distribution, a hydrothermal method was employed. Briefly, an aqueous extract (100 mL) of corms of C. esculenta was heated at 150 °C for 5 h in a Teflon-lined hydrothermal reactor (250 mL capacity). The CDs formed were dried under reduced pressure. The CD-impregnated WPU polymer was prepared via an ex situ technique according to a method described elsewhere [31]. However, in the present study, we used a high CD loading compared to that previously reported. Briefly, IPDI, PEG 600, and BD were reacted in the pre-polymerization step at a temperature of 85 ± 2 °C. In the next step, TA and BD were allowed to react with the pre-polymer formed in the first step at 70 ± 2 °C for 4–4.5 h. This process was followed by neutralization using TEA at room temperature. Finally, water was added and THF was removed under reduced pressure. Different weight percentages of CD were incorporated into the WPU matrix by using mechanical and ultra-sound energy. These nanocomposites were coded as PNC1.0, PNC2.0, PNC3.0, PNC4.0, and PNC5.0 for CD loadings of 1, 2, 3, 4, and 5 wt%, respectively. Further, the nanocomposites were cross-linked by using HE and PAA. Details of the fabrication technique are provided in Supplementary Information.
3.3 Catalyst Characterization
X-ray diffraction (XRD) patterns of the CDs and CD-impregnated WPU were obtained by using a Bruker AXS, Germany, Model: D8 Focus instrument (2θ = 10°–70° at a scanning rate of 2°min−1). The graphitic structure of the CDs was studied using Raman spectroscopy (Renishaw, UK, Renishaw Basis Series with 514 nm Laser). The shape and size of the CDs, as well as the distribution of the CDs over the WPU matrix, were visually studied by using high-resolution transmission electron microscopic (HRTEM) analysis. TEM images were obtained by using a JEOL, JEMCXII, Japan, microscope at an operating voltage of 200 kV using a Cu grid (TED PELLA INC, Ultrathin C, Type A, 400 mesh). The microscopic data were analyzed as inverse fast Fourier transform (IFFT) images by using Gatan Digital Micrograph software. A UV–visible photo-spectrometer (Thermo-Scientific, Evolve 300, USA) was used to determine the band-gap. The photoluminescence (PL) behavior was studied by using a PerkinElmer, USA, Model: LS-55 fluorescence spectrometer. The surface morphology of the biodegraded catalyst was studied by scanning electron microscopy (SEM, JEOL, JSM 6390LV) after platinum coating the surface.
3.4 Band-Gap
The band-gap of the CDs was evaluated by using UV–visible spectroscopy and applying Eq. 1 [32],
Here α is the absorption coefficient, C is a constant, h is Plank’s constant, ν is the frequency, and E bulk is the energy gap. In practice, the band-gap is calculated by plotting hν versus (αhν)2. Extrapolation of the curve to (αhν)2 gives the value of E bulk.
3.5 Determination of Quantum Yield
The quantum yield of the CDs and PNCs was determined by using Eq. 2 [33].
Here, Q CD is the quantum yield of the CDs, Q R is the quantum yield of the reference compound (quinine sulfate), I CD is the intensity of the emission of the CDs, I R is the intensity of the luminescence of the reference compound (quinine sulfate), A CD is the absorbance of the CDs at the given excitation wavelength (360 nm), A R is the absorbance of the reference compound (quinine sulfate) at the given excitation wavelength (360 nm), and η is the refractive index of the solvent used (water). The quantum yield of quinine sulfate at 360 nm is 54%.
3.6 Photo-catalytic Reaction
Five different compositions, i.e., H2O, C2H5OH (100%), and mixtures of H2O and C2H5OH (25, 50, and 75% (v/v)) were used as the starting materials for the solar-driven production of H2O2. The reactants were placed into a two-necked glass reactor equipped with an O2 inlet. Initially, the mixture was saturated with molecular O2 by passing the gas for 10 min and the reactor was then sealed. The system was then irradiated under normal solar light with an intensity of 80,000–100,000 lx at ca. 25 °C with a continuous supply of O2 for different time intervals (5–50 h). The production of H2O2 was estimated via the redox titrimetric method using KMnO4 [23].
3.7 Biodegradation Study
Analysis of the biodegradability of the catalyst system was carried out by using P. aeruginosa as the test organism [34]. A mineral salt solution containing 2.0 g (NH4)2SO4, 2.0 g Na2HPO4, 4.75 g KH2PO4, 1.2 g MgSO4·7H2O, 0.5 mg CaCl2·2H2O, 100 mg MnSO4·5H2O, 70 mg ZnSO4·7H2O, 10 mg H3BO3·5H2O, 100 mg CuSO4·7H2O, 1 mg FeSO4·7H2O, and 10 mg MoO3 in 1000 mL distilled water was prepared and sterilized at 120 °C under 15 lb pressure. The P. aeruginosa bacterial strain was cultured in a shaker incubator for 48 h using this medium. A 100-µL aliquot of the cultured bacteria was placed in a conical flask with 10 mL of the salt medium. UV-sterilized (wavelength 254 nm) catalyst films with a known weight were immersed in the medium and incubated at 37 °C for seven weeks. Growth of the bacteria was followed by measuring the absorbance of the medium at 600 nm at an interval of seven days. Similarly, a change in the weight of the catalyst was recorded after every seven days. SEM images of the biodegraded films were also taken after completion of the experimental period.
4 Results and Discussion
The synthesis of the CDs provides a green and sustainable route in which a large number of naturally available carbon resources are utilized [35]. In the present study, a carbohydrate-rich aqueous extract of corms of C. esculenta was used as the precursor. The CDs were obtained through a hydrothermal method. It can be assumed that in the hydrothermal process, extensive carbonization and aromatization took place through condensation and polymerization of different carbohydrate molecules at elevated temperature and pressure [33, 36].
The prepared CDs were characterized by TEM, XRD, and Raman spectroscopic techniques. As shown in Fig. 1a, b, the TEM image of the CDs indicates the formation of carbon nanoparticles with nearly spherical morphology. Statistical evaluation of the size distribution revealed that the size of the CDs ranged from 1.5 to 3.5 nm. The majority of the CDs has sizes in the range of 1.7–2.1 nm (see Fig. 1g). Compared to the simple heating process (at 150 °C for 3.5 h) reported previously by the same group, the size distribution was found to be restricted within a narrow range and with a smaller diameter [31]. Controlling the size of the CDs is important because the size can influence the band-gap, which is a critical parameter for water splitting.
Figure 1c shows the IFFT image of the CDs, indicating a layer spacing of 0.39 nm, which can be assigned to the (022) graphitic plane of the CDs. However, compared to the inter-planar distance of the pure graphitic structure (~0.34 nm), the spacing was greater in the case of the CDs. This may be ascribed to the presence of oxygeneous functionalities in the CD structure, which are intercalated between the consecutive layers, leading to a larger inter-planar seperation. In comparison, the XRD pattern of the CDs displayed a broad peak centered around 2θ = 22° (Fig. 2a). This is characteristic of a weakly crystalline graphitic structure with a large number of defect sites [33].
The Raman spectrum of the CDs displayed two distinct bands, i.e., the D band near 1360 cm−1 and the G band near 1580 cm−1 (Fig. 2b). The D band is characteristic of structural defects, and the G band is characteristic of symmetric sp 2 graphitic carbon stretching. UV–visible spectroscopy shows a peak near 270 nm, which is an indication of successful formation of the CDs (Fig. S1). Thus, TEM, XRD, Raman, and UV–visible spectroscopic analyses confirmed formation of the CDs. The CDs were incorporated into the WPU matrix for the development of a heterogeneous catalyst system for solar-driven H2O2 production.
In this context, the critical issue is to obtain a homogeneous distribution of the CDs over the WPU matrix without agglomeration. Agglomeration of the CDs can lead to the loss of their light-absorbing capability, which in turn hampers their photo-catalytic activity. However, in the present study, we found that the CDs and WPU acted complementarily to produce a compatible and uniform composite system. The CDs, being a highly functional nanomaterial, undergo sufficient interactions (both covalent and non-covalent) with the hyperbranched polymer matrix (Fig. 3). Such prominent interactions, along with the dispersibility of both the polymer and the nanomaterial in the reaction medium, helped to produce a homogeneous polymer-supported nanosystem without any agglomeration.
Visual evidence obtained from the TEM image of the catalyst system confirmed the uniformity, even at high nanomaterial loading (4 wt%) (Fig. 1d). Comparison of the HRTEM images (Fig. 1b, e) and corresponding IFFT images of the CDs and PNC4.0 (Fig. 1c, f) revealed an increase in the interlayer spacing from 0.39 nm for the pristine CDs to 0.43 nm after incorporation into the polymer matrix. This may be due to the additional defects created within the CD structure during the fabrication process. Intercalation of the polymeric chains may also increase the interlayer distance. This indicates strong interaction between the polymer and nanomaterial.
The XRD pattern of PNC4.0 showed a peak corresponding to amorphous carbon near 2θ = 22°, ascribed to the (002) plane of graphitic carbon (Fig. 2a). Similar to the profile of the CDs, the Raman spectrum of PNC4.0 displayed D and G bands, albeit with a higher I D/I G ratio. This provides evidence of the generation of defects in the CDs during the fabrication process. On the other hand, modification of this system with HE and PAA is expected to provide better catalyst stability and prevent CD leaching by the formation of a cross-linked network structure.
Before studying the photo-catalytic activity of the prepared catalyst, effort was made to evaluate different parameters, which ensured suitability of the polymer-supported CD system as a photo-catalyst for H2O splitting. By virtue of their quantum dimension, the CDs possess the capability to harvest photons over the solar spectrum (covering the entire UV–visible spectral region, extending to the near IR) based on their photo-excited states [1]. The associated transient species are responsible for the bright fluorescence as well as the redox processes, which are desirable for energy conversion applications [37, 38]. However, a precise mechanistic pathway to account for the light-harvesting capability of the CDs is yet to be established. Nevertheless, recent research gives the impression of charge separation in the form of holes (radical cation) and electrons (radical anion) via photo-excitation of the core carbon nanoparticles of the CDs. The radiative recombination of these holes and electrons, which are trapped at various surface sites, results in the observed fluorescence emission [26]. Hence, to study the light-harvesting activity of the CDs, the photoluminescence behavior and HOMO–LUMO band-gap were evaluated.
Like the signature behavior of other quantum dots, the CDs also exhibit excitation wavelength-dependent PL behavior (Fig. S2). Considering quinine sulfate as the reference, the quantum yield was calculated at the excitation wavelength of 360 nm and was found to be 9.5%. Values of 5.5, 6.7, 7.4, 7.8, and 7.6% were obtained for PNC1.0, PNC2.0, PNC3.0, PNC4.0, and PNC5.0, respectively. The band-gap was calculated from UV–visible spectroscopy by plotting hν versus (αhν)2 (Tauc’s method) and was found to be 2.98 eV (Fig. 4). Here, it is pertinent to mention that the band-gap of carbon dots depends on the size and surface state of the nanoparticles, and the calculated value agreed with the literature data [39].
Generally, H2O splitting requires the bottom level of the conduction band to be more negative than the redox potential of H+/H2 (0 V vs. NHE), while the top level of the valence band should be more positive than the redox potential of H2O/O2 (1.23 V vs. NHE). Thus, the minimum value of E bulk for any photo-catalyst should be 1.23 eV for H2O splitting. However, in practice, for effective H2O splitting, the band-gap should be larger than 2.0 eV. This is because, in reality, energy losses may occur due to kinetic overpotentials.
In the present study, E bulk was evaluated as 2.98 eV for the CDs. Hence, these species satisfy the criteria to act as a catalyst for solar-driven production of H2O2. In this context, the CDs appear to be the superior catalyst compared to g-C3N4. This may be because, g-C3N4 has a band-gap of 1.4 eV, which is good enough to split alcohols but is insufficient to split H2O under solar irradiation. The photo-catalytic production of H2O2 involves photo-irradiation of O2-saturated H2O or alcohol in the presence of a photo-catalyst, i.e., the CDs in the present case.
Semiconductors can act as photo-catalysts for light-induced redox processes due to their electronic structure, which is characterized by a filled valence band and an empty conduction band. Absorption of a photon with energy greater than the band-gap energy leads to the formation of an electron/hole pair. In the absence of suitable scavengers, the stored energy is dissipated within a few nanoseconds by recombination. A plausible mechanistic framework involves the formation of an electron (e−)/hole (h +) pair by photo-excitation of the CDs. In the case of an alcohol, h+ oxidizes the RCH2OH to generate aldehydes and a proton, while e− promotes two-electron reduction of O2 to produce H2O2 [6, 21].
When H2O is used as the raw material, h+ oxidizes H2O to O2. Similar two-electron reduction of O2 follows thereafter to produce H2O2 [21].
In the current study, we used H2O, mixtures of H2O and C2H5OH (25%, 50%, and 75% v/v), and C2H5OH (100%) saturated with molecular O2. In this regard, it is important to mention that many of the traditionally used semiconductors absorb only light energy or mostly in the UV region; hence, for a solar-driven process, dye sensitization is required [1]. However, the CDs can also absorb photons in the visible region; hence, the CDs can be readily used under sunlight. In the actual reaction setup, the reaction mixtures were irradiated under normal solar light with an intensity of 80,000–100,000 lx at ca. 25 °C for different durations.
Figure 5 shows the formation of H2O2 at different intervals using different compositions of starting materials with PNC4.0 as the photo-catalyst. The bar diagram reveals the influence of the time and the composition of the starting materials on the production of H2O2. The formation of H2O2 increased with time for the photo-reaction. Here, it is pertinent to mention that the virtual yield of H2O2 shown in the bar diagram might be less than the actual amount formed, as some amount of H2O2 is destroyed by sunlight.
Nevertheless, the increased production of H2O2 with time clearly indicates the efficiency of the polymer-supported CDs as a photo-catalyst in the H2O splitting reaction. The rate of formation of H2O2 also supports this claim (Fig. S3). Some interesting observations emerge from this study. When H2O was used by itself, less H2O2 was produced (~46 µM after 50 h of reaction) compared to that obtained with 100% C2H5OH (~82 µM). On the other hand, in the case of the C2H5OH/H2O mixtures, the H2O2 production increased with an increase in the amount of C2H5OH in the mixture (~49 µM for 25%C2H5OH/75%H2O, ~61 µM for 50%C2H5OH/50%H2O, and ~70 µM for 75%C2H5OH/25%H2O). The increased H2O2 production in the presence of C2H5OH may be because of the favorable thermodynamic driving force, which is promoted by the suitable oxidation and reduction potential of the catalyst when alcohol is used (compared to water) [6]. A previous report also suggests similar behavior of alcohol and H2O mixtures toward solar-driven water splitting [21]. Thus, these data suggest that the photo-reaction of H2O with C2H5OH can enhance the H2O2 yield.
Figure 6 shows the selectivity toward H2O2 production when different compositions of starting materials were used. When H2O was used as the starting material, 100% selectivity for the production of H2O2 was achieved. However, when C2H5OH was used, the reaction showed no selectivity. Along with H2O2, a mixture of acetaldehyde and acetic acid was also formed, in which acetaldehyde was the predominant product, as confirmed by GC analysis. With an increase in the H2O gradient in the mixtures of C2H5OH/H2O, the selectivity toward H2O2 production also increased (~48% when only C2H5OH was used, ~58% for 75%C2H5OH/25%H2O, ~62% for 50%C2H5OH/50%H2O, ~69% for 25%C2H5OH/75%H2O, and 100% for H2O only). In other words, the production of H2O2 increased with respect to the by-products. This clearly suggests that the two-electron reduction of oxygen loses its selectivity when C2H5OH is used, whereas addition of H2O enhances the selectivity. Thus, it can be inferred that photo-reaction of C2H5OH with H2O around room temperature promotes selective H2O2 production.
The influence of the CD loading on H2O2 generation was evaluated (Fig. 7). In 50 h of photo-reaction, the production of H2O2 increased with an increase in the CD content up to 4 wt%. However, from a loading of 5 wt% onwards, the production of H2O2 declined slightly. This may be because of agglomeration of the CDs at higher loading, which reduces their light-harvesting ability. The quantum yields of the PNCs also supported this claim. PNC4.0 was found to have the optimal composition for H2O2 production via the photo-splitting of H2O and C2H5OH.
Here, it is pertinent to mention that CD alone can act as an effective catalyst with higher production yield (Fig. S4). However, the ease of separation makes the polymer-supported CDs more advantageous for use as a heterogeneous catalyst than the pristine CDs. This observation can be explained based on two factors. First, the increase in the size of the CDs after incorporation into the polymer matrix (due to intercalation of the polymeric chains in-between the layers of CD, which was confirmed by the increased d-spacing) may hamper the light-harvesting ability of the CDs. Secondly, the distribution of the CDs within the polymer matrix is not as uniform as in the solution state. This also contributed to reduction of the photo-catalytic activity of the polymer-supported CDs compared to the pristine CDs.
However, despite these facts, good photo-catalytic activity was observed for the polymer-supported CDs. The reusability of the CD-containing films was evaluated over several cycles. Reusability is an important factor for any catalyst from the green chemistry point of view. Accordingly, a model reaction was performed by using PNC4.0 as the photo-catalyst with a definite amount of reactants for 50 h. After completion of the reaction, the catalyst was recovered, dried, and used again under the same reaction conditions.
Compared to the production of H2O2 (Fig. 8), there was no statistically significant difference up to the 4th cycle of use. This indicates the effectiveness of the polymer to hold CD within the matrix as well as to preserve its catalytic activity. Modification of the WPU/CD system with HE and PAA may contribute in this regard. Such modification results in a highly cross-linked system, which prevents leaching of the CDs from the polymer matrix. However, after the 5th cycle of use, a slight reduction in the yield was observed, though this reduction was not substantial. This may arise due to leaching of some amount of the CDs after several cycles of use, as was confirmed by UV–visible spectroscopy, where the spectrum of the reaction mixture showed a low-intensity peak near 270 nm (Fig. S5). Thus, the overall results confirm the utility of the polymer-supported CDs as a photo-catalyst for solar-driven production of H2O2 using O2, H2O, and C2H5OH as raw materials.
Bacterial degradation by P. aureginosae was evaluated to demonstrate the biodegradability of the catalyst system. Analysis of the bacterial degradation of PNC films revealed adequate biodegradation over the experimental period of seven weeks. The weight loss profiles confirmed that the WPU/CD nanocomposites offer a susceptible surface for bacterial adherence, resulting in high weight loss, which is almost consistent with the CD loading in the polymer matrix (Fig. 9a). The bacterial growth curves further support this observation (Fig. 9b). An increase in the bacterial population was recorded with time. With an increase in the CD loading, the rate of bacterial growth also increased. This is in contrast with the photo-catalytic activity of the PNCs, where the H2O2 production decreased when the CD loading exceeded 4 wt%. This is because P. aeruginosa is an organotroph microorganism that utilizes carbon-based materials as a source of food and energy. Hence, a high CD loading favors faster biodegradation. The SEM images (Fig. 9c, d) further confirmed significant bacterial adherence, as well as surface erosion, on the PNC films due to bacterial exposure. Thus, these results indicate the eco-friendly behavior of the catalyst system.
5 Conclusion
From the above results, it can be inferred that carbon dots dispersed in a polyurethane matrix can be used as an effective heterogeneous photo-catalyst for solar-driven hydrogen peroxide production. The overall process can be justified as a green practice. It offers the benefits of green chemistry in terms of availability, facile and sustainable preparation, catalyst stability, non-toxicity, recyclability, and biodegradability. The key components, i.e., carbon dots, were synthesized using bio-based raw material in a cost-effective, facile process. Further, preparation of the polymeric support, i.e., the polyurethane matrix, was performed in an aqueous medium with a low VOC content. The reusability test confirmed the effectiveness of the catalyst, even after several cycles of use. Compared to other metal-based catalysts that are used for hydrogen peroxide production, the present system offers the benefits of non-toxicity and biodegradability. Further, compared to graphitic carbon nitride, the present system is cost-effective with the additional capability to produce hydrogen peroxide from water under sunlight. This study may pave the way for recognition of polymer-supported carbon dots as heterogeneous photo-catalysts.
References
K.A.S. Fernando, S. Sahu, Y. Liu, W.K. Lewis, E.A. Guliants et al., Carbon quantum dots and applications in photocatalytic energy conversion. ACS Appl. Mater. Interfaces 7(16), 8363–8376 (2015). doi:10.1021/acsami.5b00448
J. Luo, J.H. Im, M.T. Mayer, M. Schreier, M.K. Nazee-ruddin et al., Water photolysis at 12.3% efficiency via perovskite photovoltaics and earth-abundant catalysts. Science 345(6204), 1593–1596 (2014). doi:10.1126/science.1258307
T.S. Teets, D.G. Nocera, Photocatalytic hydrogen production. Chem. Commun. 47(33), 9268–9274 (2011). doi:10.1039/c1cc12390d
Y.W. Su, W.H. Lin, Y.J. Hsu, K.H. Wei, Conjugated polymer/nanocrystal nanocomposites for renewable energy applications in photovoltaics and photocatalysis. Small 10(22), 4427–4442 (2014). doi:10.1002/smll.201401508
A.E. Sanli, A. Aytac, Response to disselkamp: direct peroxide/peroxide fuel cell as a novel type fuel cell. Int. J. Hydrogen Energy 36(1), 869–875 (2011). doi:10.1016/j.ijhydene.2010.09.038
Y. Shiraishi, S. Kanazawa, Y. Kofuji, H. Sakamoto, S. Ichikawa, S. Tanaka, T. Hirai, Sunlight-driven hydrogen peroxide production from water and molecular oxygen by metal-free photocatalysts. Angew. Chem. Int. Ed. 53(49), 13454–13459 (2014). doi:10.1002/ange.201407938
F. Sandelin, P. Oinas, T. Salmi, J. Paloniemi, H. Haario, Kinetics of the recovery of active anthraquinones. Ind. Eng. Chem. Res. 45(3), 986–992 (2006). doi:10.1021/ie050593s
D. Gudarzi, W. Ratchananusorn, I. Turunen, T. Salmi, M. Heinonen, Preparation and study of Pd catalysts supported on activated carbon cloth (ACC) for direct synthesis of H2O2 from H2 and O2. Top. Catal. 56(9), 527–539 (2013). doi:10.1007/s11244-013-0014-5
S. Melada, R. Rioda, F. Menegazzo, F. Pinna, G. Strukul, Direct synthesis of hydrogen peroxide on zirconia-supported catalysts under mild conditions. J. Catal. 239(2), 422–430 (2006). doi:10.1016/j.jcat.2006.02.014
J.K. Edwards, B.E. Solsona, P. Landon, A.F. Carley, A. Herzing, C.J. Kiely, G.J. Hutchings, Direct synthesis of hydrogen peroxide from H2 and O2 using TiO2 supported Au–Pd catalysts. J. Catal. 236(1), 69–79 (2005). doi:10.1016/j.jcat.2005.09.015
J.C. Pritchard, Q. He, E.N. Ntainjua, M. Piccinini, J.K. Edwards, A.A. Herzing, The effect of catalyst preparation method on the performance of supported Au–Pd catalysts for the direct synthesis of hydrogen peroxide. Green Chem. 12(5), 915–921 (2010). doi:10.1039/b924472g
Y. Isaka, S. Kato, D. Hong, T. Suenobu, Y. Yamadaa, S. Fukuzumi, Bottom-up and top-down methods to improve catalytic reactivity for photocatalytic production of hydrogen peroxide using a Ru-complex and water oxidation catalysts. J. Mater. Chem. A 3(23), 12404–12412 (2015). doi:10.1039/C5TA02446C
S. Kato, J. Jung, T. Suenobu, S. Fukuzumi, Production of hydrogen peroxide as a sustainable solar fuel from water and dioxygen. Energy Environ. Sci. 6(12), 3756–3764 (2013). doi:10.1039/c3ee42815j
C. Kormann, D.W. Bahnemann, M.R. Hoffmann, Photocatalytic production of hydrogen peroxides and organic peroxides in aqueous suspensions of titanium dioxide, zinc oxide, and desert sand. Environ. Sci. Technol. 22(7), 798–806 (1988). doi:10.1021/es00172a009
R. Cai, Y. Kubota, A. Fujishima, Effect of copper ions on the formation of hydrogen peroxide from photocatalytic titanium dioxide particles. J. Catal. 219(1), 214–218 (2003). doi:10.1016/S0021-9517(03)00197-0
H. Goto, Y. Hanada, T. Ohno, M. Matsumura, Quantitative analysis of superoxide ion and hydrogen peroxide produced from molecular oxygen on photoirradiated TiO2 Particles. J. Catal. 225(1), 223–229 (2004). doi:10.1016/j.jcat.2004.04.001
V. Maurino, C. Minero, G. Mariella, E. Pelizzetti, Sustained production of H2O2 on irradiated TiO2–fluoride systems. Chem. Commun. 36(33), 2627–2629 (2005). doi:10.1039/b418789j
T. Hirakawa, Y. Nosaka, Selective production of superoxide ions and hydrogen peroxide over nitrogen-and sulfur-doped TiO2 photocatalysts with visible light in aqueous suspension systems. J. Phys. Chem. C 112(40), 15818–15823 (2008). doi:10.1021/jp8055015
M. Teranishi, S. Naya, H. Tada, In situ liquid phase synthesis of hydrogen peroxide from molecular oxygen using gold nanoparticle-loaded titanium (IV) dioxide photocatalyst. J. Am. Chem. Soc. 132(23), 7850–7851 (2010). doi:10.1021/ja102651g
D. Tsukamoto, A. Shiro, Y. Shiraishi, Y. Sugano, S. Ichikawa, S. Tanaka, Platinum nanoparticles supported on anatase titanium dioxide as highly active catalysts for aerobic oxidation under visible light irradiation. ACS Catal. 2(2), 599–603 (2012). doi:10.1021/cs300407e
Y. Shiraishi, S. Kanazawa, Y. Sugano, D. Tsukamoto, H. Sakamoto, S. Ichikawa, T. Hirai, Highly selective production of hydrogen peroxide on graphitic carbon nitride (g-C3N4) photocatalyst activated by visible light. ACS Catal. 4(3), 774–780 (2014). doi:10.1021/cs401208c
V.D. Dao, P. Kim, S. Baek, L.L. Larina, K. Yong, R. Ryoo, Facile synthesis of carbon dot-Au nanoraspberries and their application as high-performance counter electrodes in quantum dot-sensitized solar cells. Carbon 96, 139–144 (2016). doi:10.1016/j.carbon.2015.09.023
Z. Yang, Z. Li, M. Xu, Y. Ma, J. Zhang et al., Controllable synthesis of fluorescent carbon dots and their detection application as nanoprobes. Nano-Micro Lett. 5(4), 247–259 (2013). doi:10.5101/nml.v5i4.p247-259
W. Kwon, S. Do, J. Lee, S. Hwang, J.K. Kim, S.W. Rhee, Freestanding luminescent films of nitrogen-rich carbon nanodots toward large scale phosphor based white light emitting devices. Chem. Mater. 25(9), 1893–1899 (2013). doi:10.1021/cm400517g
Z. Song, F. Quan, Y. Xu, M. Liu, L. Cui, J. Liu, Multifunctional N, S co-doped carbon quantum dots with pH- and thermo-dependent switchable fluorescent properties and highly selective detection of glutathione. Carbon 104, 169–178 (2016). doi:10.1016/j.carbon.2016.04.003
S. Sahu, Y. Liu, P. Wang, C.E. Bunker, K.A.S. Fernando et al., Visible-light photoconversion of carbon dioxide into organic acids in an aqueous solution of carbon dots. Langmuir 30(28), 8631–8636 (2014). doi:10.1021/la5010209
B. De, B. Voit, N. Karak, Carbon dot reduced Cu2O nanohybrid/hyperbranched epoxy nanocomposite: mechanical, thermal and photocatalytic activity. RSC Adv. 4(102), 58453–58459 (2014). doi:10.1039/C4RA11120F
D. Mosconi, D. Mazzier, S. Silvestrini, A. Privitera, C. Marega, L. Franco, Synthesis and photochemical applications of processable polymers enclosing photoluminescent carbon quantum dots. ACS Nano 9(4), 4156–4164 (2015). doi:10.1021/acsnano.5b00319
S. Barua, G. Dutta, N. Karak, Glycerol based tough hyperbranched epoxy: synthesis, statistical optimization and property evaluation. Chem. Eng. Sci. 95(3), 138–147 (2013). doi:10.1016/j.ces.2013.03.026
S. Gogoi, N. Karak, Bio-based high-performance waterborne hyperbranched polyurethane thermoset. Polym. Adv. Technol. 26(6), 589–596 (2015). doi:10.1002/pat.3490
S. Gogoi, M. Kumar, B.B. Mandal, N. Karak, High performance luminescent thermosetting waterborne hyperbranched polyurethane/carbon quantum dot nanocomposite with in vitro cytocompatibility. Compos. Sci. Technol. 118, 39–46 (2015). doi:10.1016/j.compscitech.2015.08.010
C. Zhu, S. Guo, Y. Fang, S. Dong, Reducing sugar: new functional molecules for the green synthesis of graphene nanosheets. ACS Nano 4(4), 2429–3247 (2010). doi:10.1021/nn1002387
B. De, N. Karak, A green and facile approach for the synthesis of water soluble fluorescent carbon dots from banana juice. RSC Adv. 3(22), 8286–8290 (2013). doi:10.1039/c3ra00088e
S. Pramanik, R. Konwarh, K. Sagar, B.K. Konwar, N. Karak, Bio-degradable vegetable oil based hyperbranched poly(ester amide) as an advanced surface coating material. Prog. Org. Coat. 76(4), 689–697 (2013). doi:10.1016/j.porgcoat.2012.12.011
L. Zhu, Y. Yin, C.F. Wang, S. Chen, Plant leaf-derived fluorescent carbon dots for sensing, patterning and coding. J. Mater. Chem. C 1(32), 4925–4932 (2013). doi:10.1039/c3tc30701h
S. Sahu, B. Behera, T.K. Maiti, S. Mohapatra, Simple one-step synthesis of highly luminescent carbon dots from orange juice: application as excellent bio-imaging agents. Chem. Commun. 48(70), 8835–8837 (2012). doi:10.1039/c2cc33796g
L. Cao, S. Sahu, P. Anilkumar, C.E. Bunker, J. Xu, K.A.S. Fernando et al., Carbon nanoparticles as visible light photocatalysts for efficient CO2 conversion and beyond. J. Am. Chem. Soc. 133(13), 4754–4757 (2011). doi:10.1021/ja200804h
J. Wang, S. Sahu, S.K. Sonkar, K.N. Tackett, K.W. Sun et al., Versatility with carbon dots-from overcooked BBQ to brightly fluorescent agents and photocatalysts. RSC Adv. 3(36), 15604–15607 (2013). doi:10.1039/c3ra42302f
Y. Yang, W. Kong, H. Li, J. Liu, M. Yang et al., Fluorescent N-doped carbon dots as in vitro and in vivo nanothermometer. ACS Appl. Mater. Interfaces 7(49), 27324–27330 (2015). doi:10.1021/acsami.5b08782
Acknowledgements
The authors acknowledge DBT (Grant No. BT/235/NE/TBP/2011 Dated April 30, 2012), India, for financial support and SAIF, NEHU, Shillong for TEM analysis.
Author information
Authors and Affiliations
Corresponding author
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Gogoi, S., Karak, N. Solar-Driven Hydrogen Peroxide Production Using Polymer-Supported Carbon Dots as Heterogeneous Catalyst. Nano-Micro Lett. 9, 40 (2017). https://doi.org/10.1007/s40820-017-0143-7