Abstract
Recently, two-dimensional monolayer molybdenum disulfide (MoS2), a transition metal dichalcogenide, has received considerable attention due to its direct bandgap, which does not exist in its bulk form, enabling applications in optoelectronics and also thanks to its enhanced catalytic activity which allows it to be used for energy harvesting. However, growth of controllable and high-quality monolayers is still a matter of research and the parameters determining growth mechanism are not completely clear. In this work, chemical vapor deposition is utilized to grow monolayer MoS2 flakes while deposition duration and temperature effect have been systematically varied to develop a better understanding of the MoS2 film formation and the influence of these parameters on the quality of the monolayer flakes. Different from previous studies, SEM results show that single-layer MoS2 flakes do not necessarily grow flat on the surface, but rather they can stay erect and inclined at different angles on the surface, indicating possible gas-phase reactions allowing for monolayer film formation. We have also revealed that process duration influences the amount of MoO3/MoO2 within the film network. The homogeneity and the number of layers depend on the change in the desorption–adsorption of radicals together with sulfurization rates, and, inasmuch, a careful optimization of parameters is crucial. Therefore, distinct from the general trend of MoS2 monolayer formation, our films are rough and heterogeneous with monolayer MoS2 nanowalls. Despite this roughness and the heterogeneity, we observe a strong photoluminescence located around 675 nm.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
As the dimensions of materials are reduced from three dimensions (3D), the fundamental physical properties change remarkably, allowing for novel applications, which are otherwise not possible [1, 2]. Transition from 3D to two dimensions (2D) first became possible with the exfoliation of graphene, a material well-known for its high electron mobility, mechanical strength, and thermal conductivity [3–6]. Unfortunately, there are still important challenges involved in the transition of graphene from laboratories to industry especially due to its zero bandgap [7]. Therefore, researchers are still in search of a novel material system preferably with a direct bandgap to be used in electronic, photonic, and energy applications. In this regard, transition metal dichalcogenides (TMDC), MX2 (M = Mo, W; X = S, Se, Te) are receiving special attention with their peculiar optical and electronic properties [8–10] and their potential to be used in catalysis, microelectronics, batteries, hydrogen storage, medical applications, and optoelectronics [11–14]. Among the numerous candidates, monolayer MoS2 has invoked a particular interest due to its direct bandgap and it is considered to have great potential both in electronics and photonics [15–17]. MoS2-based field effect transistors (FETs) used as phototransistors, memory devices, and sensors have shown superior properties including excellent mobility, ON/OFF ratio, and sensitivity [18]. Also, MoS2 has attracted attention due to its thermal properties and its potential use in thermoelectric applications [18, 19] and catalyzing properties resulting from its active edge sites [20]. However, scalable, controllable, large-area growth of single-layer MoS2, keeping high crystal quality and large domain size, still remains a problem [14, 21]. Mechanical exfoliation, one of the most commonly used methods, is not favorable for commercial applications. Likewise, liquid exfoliation, ionic intercalation, and hydro-thermal methods still have important drawbacks where batch fabrication and device applications are concerned [22–25]. It is also possible to form different few-layer TMDCs through colloidal synthesis techniques, which are beneficial in terms of high-yield and substrate-free nanostructures [26]. However, developing a facile and reliable method for large-area growth is crucial in order to use such 2D materials in the different applications of electronics and photonics.
One method which seems particularly promising is chemical vapor deposition (CVD), as it is highly promising in its ability to grow monolayer, controlled, large-area MoS2 films [14, 21, 27–29]. CVD-based synthesis was first reported in 2012 [21, 22], showing the potential of the method to realize high-quality, controlled growth of the MoS2 flakes, and other researches have revealed that monolayer flakes deposited by CVD can be used in different applications and devices such as phototransistors [30], photodetectors [31], memories [16], and so on. Although the underlying mechanism of the monolayer MoS2 growth is still not very clear, it can allow for determining the features of the thin films through controlled synthesis [32–34].
In the present work, we have used CVD to obtain single-wall monolayer MoS2 flakes whose features can be changed through process parameters. We report the direct influence of deposition duration and process temperature on the growth mechanism and film properties. By changing process parameters, we can shift from a rough surface with MoS2 flakes scattered at different angles to a smoother and more uniform surface composed of monolayer MoS2 formations. Such single-wall MoS2 flakes, which for the most part are not flat on the surface, can be beneficial in applications including solar cells [35], energy storage [36], catalysis [11], and sensing [37] where large surface area of the flakes can increase the intended performance.
2 Experimental
The experimental setup of the CVD system is schematically shown in Fig. 1. The quartz boats containing high-purity MoO3 (14 mg, 99.9 %, Aldrich) and S powder (1.4 g, 99.5 %, Alfa) were placed at the temperature zones specified according to the melting temperatures of the precursors, 700 °C for MoO3 and 150 °C for sulfur. The MoO3 boat was located at the highest temperature zone of the furnace. In our setup, spatial locations have been critical for complete sulfurization and monolayer MoS2 formation as the temperature changes with distance. This effect was investigated by varying the distance between boats of MoO3 powder and the substrates (D s) from 9 cm (~670 °C) to 13 cm (~600 °C). The SiO2 (~300 nm)-coated Si substrates are cleaned using piranha etch solution and the RCA technique. SiO2 was thermally grown on Si, and the thickness is confirmed by ellipsometry. Before deposition started, the reaction chamber was heated to deposition temperature at a rate of 15 °C min−1 in a nitrogen environment, and at the specified deposition temperatures, Ar and H2 were introduced to the system as carrying gases at flow rates of 17 and 10 sccm, respectively. The growth duration was decreased from 10 to 5 and 3 min to observe the evolution of the flakes.
At deposition temperatures, S vapor reduced MoO3 powder to volatile suboxide MoO3−x [38] and MoS2 monolayer flakes were formed by the gas-phase reactions while the compounds diffusing on the substrate reacting with sulfur are obtained possibly through the Eqs. (1) and (2) [21]. It is suggested that if the reaction duration is not sufficient, the sulfurization process cannot be fully accomplished and intermediate products are formed, one of which is MoO2, due to its stability [38]. After the growth period was finished, a rapid cooling-down process was carried out and 500 sccm of nitrogen gas (99.999 %) was purged into the tube to avoid other products such as MoO3 formation while keeping MoS2 monolayers on the surface of the substrate.
The MoS2 monolayer formations were characterized by Raman spectroscopy, photoluminescence (PL), scanning electron microscopy (SEM), and high-resolution transmission electron microscopy (HRTEM). In the case of MoS2 deposition, Raman spectroscopy is a practical and facile way to examine the film properties including the number of layers and the imprints of other possible products such as MoO3, MoO3-x, and MoO2 [39–42]. In bulk MoS2, there are two distinctive Raman peaks corresponding to in-plane vibration of Mo and S atoms (\(E_{{2{\text{g}}}}^{1}\)) at ∼383 cm−1 and the out-of-plane vibration of S atoms (A 1g) at ∼408 cm−1 where the number of layers are determined by the change in difference between these two peaks [41]. As the number of layers decrease, the mode at \(E_{{2{\text{g}}}}^{1}\) is found to move to lower frequencies and the mode at A 1g is found to move to higher frequencies [22, 39], giving valuable information about monolayer and multi-layer MoS2 flakes. Additionally, these peaks also shift with the change in film properties, the frequency of \(E_{{2{\text{g}}}}^{1}\) vibrational mode is found to be effected by strain [43], and the frequency of A 1g vibrational mode is found to depend on electrostatic doping [44]. PL also gives valuable information about the transition from bulk or multi-layer indirect-bandgap MoS2 to direct-bandgap, few-layer or monolayer MoS2 flakes. For the PL measurements, a focused excitation laser (532 nm) was used to detect the peaks at ~670 nm (A 1 excitation of MoS2) and ~630 nm (the resonance of B1 excitation) for MoS2 films [45]. At about 645 nm, a peak which is the sign of bilayer MoS2 can also be observed [46]. While the peak at ~630 nm is related with rather thick flakes as the layers go from multi-layer to monolayer MoS2, the peak around 670 nm gets more intense and sharper [47]. In addition to number of layers, photoluminescence also depends on various parameters including grain sizes, defects, strain, and electrostatic doping [27, 32].
SEM was utilized to investigate the shapes of the flakes and see the general view of the film formations. HRTEM was used a supportive technique for further understanding about the shapes of the flakes. In addition to this analysis, investigation of defect states and vacancies is important as they affect the transport mechanism and PL of the system [48–51]. However, in this research work, we rather focused on the properties of the nanowall film formations and their dependence on the process parameters.
3 Results and Discussion
MoS2 flakes have been grown using solid MoO3 and S as precursors at different spatial locations, abbreviated as D s (distance between MoO3 powder boat and the substrates) as illustrated in Fig. 1. As shown in Fig. 2a, b, Raman scattering (excitation wavelength at 532 nm) and PL spectra are primarily analyzed to identify the film characteristics including the number of MoS2 layers and formation of other products different from MoS2 [52, 53]. In the first set of experiments, D s is changed from 10 to 13 cm while the deposition time is fixed to 10 min. The change in the distance can be indicative of the change in precursor concentration [34]. However, with our setup (Fig. 1), this effect can be ignored where the substrate temperature (T S) changing with the distance is suggested to be a rather more effective parameter to influence the film properties.
As presented in Fig. 2a, although the two distinctive MoS2 Raman peaks (around ∼379 and ∼402 cm−1 corresponding to in-plane vibration of Mo and S atoms according to the Raman peaks) are present, we also observe Raman signatures from oxide phases (MoO3 and/or MoOx) which indicate the presence of residual oxygen associated with incomplete sulfurization. The peak at ~299 cm−1 is an indicator of nanometer-thick MoO3 sheets (as small as ~15 nm), and it can be correlated with the stoichiometry of MoO3 polycrystalline samples or a shift of an initially strong 284 cm−1 peak [54, 55]. At D S = 10 cm, a small peak located at 231 cm−1 is observed, most probably due to one-dimensional MoO2 nanorods [45], and at D S = 11 cm, another weak peak centered around 198 cm−1 is explained by the formation of thick MoO3 sheets (~300 nm) [54]. As the distance (D s) becomes larger than 12 cm, the peak at 246 cm−1 starts to be more visible, indicative of \(B_{\text{g}}^{3}\) twist mode, showing that the MoO3 nanoparticles get larger at lower substrate temperatures [54]. We can suggest that when the temperature is not sufficiently high, the activation energy of the reactions in Eq. (2) is not provided. In fact, from the Raman peaks, measured from the films formed at a distance of 10 cm (T S of ~655 °C), the imprints of MoO3 nanoparticles are also observed. In this case, it is quite probable that the diffusion of the sulfur species is degraded and formation of MoO3 nanoparticles is more likely than the formation of MoS2 flakes. These results show that balancing desorption–adsorption and sulfurization rates is crucial to obtain high-quality, monolayer MoS2 flakes. Obviously, the network that we obtained is not homogeneous, and there are different MoOx (X = 2, 3) sheets and rods being formed during the deposition, which also helps the MoS2 flakes to be suspended on the surface allowing for a larger surface area.
MoO3 and/or MoOx peaks are ignorable only for the sample deposited at D s = 11 cm (T S of ~655 °C), which suggests that the deposited MoS2 flakes are rather uniform and high quality with an optimized substrate temperature of precursor ratio of MoO3 to S. This can be explained by the efficient adsorption and diffusion of MoO3-x species on the substrate and reaction with S to form MoS2 at around 640 °C. Although other substrate temperature regimes also have been reported for MoS2 formation [14, 33], it is concluded that due to the complicated nucleation process, it is possible to find different optimal conditions to grow monolayer MoS2 flakes in different systems. Therefore, depending on the system geometry, flow rates, and other process parameters, the substrate temperature should be carefully controlled to fine-tune the adsorption/desorption of radicals and the sulfurization rate for the growth of MoS2 monolayers [56]. Our results show that the difference in Raman peaks is between 21 and 25 cm−1 corresponding to in-plane vibration of Mo and S atoms (\(E_{{2{\text{g}}}}^{1}\)) at ∼378–379 cm−1 and the out-of-plane vibration of S atoms (A 1g) at ∼400–403 cm−1. Both \(E_{{2{\text{g}}}}^{1}\) and A 1g modes exhibit a blueshift when compared to bulk MoS2 in agreement with other nanowall-like MoS2 layers [57]. However, the peak convergence is less than that of the reported monolayer MoS2 results in the literature, which can be explained by the fact that the network is not completely composed of monolayer MoS2 formations, but the film, specifically the parts closer to the substrate surface, contains oxysulfides (MoOS2), MoOx (X = 2, 3), and multi-layer flakes [51, 58, 59]. High-temperature conditions (D s = 10 cm) are considered unfavorable for MoS2 monolayer formation due to their high diffusion rate, which obstructs the growth of stable nuclei.
As shown in Fig. 2b, although their full width at half maximum (FWHM) is not narrow, the PL peaks between ~675 and ~685 nm indicate formation of monolayer MoS2 flakes, specifically at a distance (D s) of 11 cm. At this specified spatial location, more homogeneous and rather large-size MoS2 mono layers are formed and a stronger photoluminescence develops, which results from the direct excitonic transition due to the direct bandgap of monolayer MoS2 [47]. For the films deposited at other substrate temperatures, the intensity of peaks becomes lower and their FWHM becomes wider. In general, the formed structures are not uniform, and, especially at low temperatures, the roughness and heterogeneity increase.
Figure 3 exhibits the SEM pictures of the films in Fig. 2, giving information about the size, shape of the flakes, and general network of the formations. These images show features similar to nanowalls and nano-plates that are edge oriented due the basal edges deposited on the substrate [60]. Such nanowall-like structures are appealing for their potential to be used as super capacitors, specifically in Li-ion batteries [36, 61–63]. Also, high surface area can be beneficial when used in heterostructures where non-radiative energy transfer is utilized. Rather high crystal growth rate and large number of nucleation sites are considered to provide smaller crystalline grain sizes. As a result, the formed surface is not homogeneous and the surface is far from being smooth. When the substrate temperature is reduced (at D s = 13 cm), the surface roughness decreases and such nanowall-like structures become less visible (Fig. 3d).
It is expected that process duration and the concentration of the reactants also play a crucial role in the formation of MoS2 films. Therefore, to get a better understanding of the growth mechanism, we decreased the deposition duration from 10 to 5 min. Figure 4a, b shows Raman scattering and PL spectra, respectively. Indeed, both the Raman scattering and PL spectra exhibit that a more homogeneous network is obtained along with a much reduced amount of other types of formations such as MoOS2, MoO2, or MoO3. The peak at ~299 cm−1, an indicator of nanometer-thick MoO3 sheets. has nearly disappeared, and the difference in MoS2 Raman peak has become as small as ~22 cm−1. This Raman peak difference, higher than expected, could be explained with a large number of small-size grains or crystalline defects. Different from the Raman scattering spectra measured from the films deposited in 10 min, another peak at ~355 cm−1 starts to develop, indicative of m-MoO2 b-MoO3-x phase transition [64]. This suggests that in 5 min, S vapor has reduced MoO3 powder to volatile suboxide MoO3-x [32] and in 10 min, these MoO3-x regions have already been transformed into either MoS2 monolayer flakes or MoO3 nanoparticles (see Fig. 2a). As the substrate distances get larger, a peak around 365 cm−1, assigned to O–Mo–O bending and scissoring modes, also becomes more visible [65].
It should be noted that there is also a significant improvement in the PL characteristics of the films deposited in 5 min (Fig. 4b) compared to the films with a reaction period of 10 min (Fig. 2b). This improvement is observed specifically for the films that are deposited at a D S of 11 cm (TS of ~640 °C). MoS2 flakes are mostly in the form of single layers, which is understood from the disappearing peak at ~ 630 nm, an indicator of multi-layer flakes. Also, the peak at ~675 shifts to ~680 nm and becomes narrower, showing higher-quality and homogeneous flakes at a D s of 11 cm compared to the case at a D s of 13 cm. The PL spectra at 9, 10, and 12 cm are not included in the Figure because they do not show a significant difference from the peak obtained from the film deposited at the D S of 13 cm. In general, these results explain that sulfurization in the first 5 min is sufficient; however, as the deposition period is increased, other products start to develop. It is obvious that optimizing the precursor concentrations is also crucial to prevent molybdenum di/three oxide sheets and allows for the formation of large MoS2 monolayers, and these parameters are specific to the experimental setup and deposition temperature. As described by Wang et al., edge free energy and the ratio (or amount) of the precursors in the medium are the determining factors for the growing rate and hence the shape of the grains [34].
Figure 5 presents the SEM images of these films formed in 5 min. Different from the films formed in 10 min, the flakes are visible specifically when deposited at a D s of 9, 10, and 11 cm. Commonly, it is discussed that the domain shape of the flakes tend to grow in the form of a triangle or a hexagon [34]. However, most of our MoS2 flakes are in the shape of half pringles resembling truncated triangles where the shapes of domains are suggested to be controlled by the ratio of precursors effecting the kinetic growth dynamics of edges [27, 58]. SEM images also show that flakes are not flat on the surface of the substrate but rather they appear to stand erect with different angles. These observations confirm that gas-phase reactions are effective in our system making MoS2 flakes round-shaped and erect on the surface instead of being flat on the surface.
Observing the improvement in the formation of MoS2 monolayers with a decreased deposition duration of 5 min with respect to the case of 10 min, this period is further reduced to 3 min. Figure 6a shows Raman scattering spectra of the films formed in 3, 5, and 10 min when D s is fixed to 11 cm. Interestingly, the peak at ~299 cm−1 has again become visible, showing that nanometer-thick MoO3 sheets are formed on the surface. This result is due to insufficient deposition duration for MoS2 flakes to form. Figure 6b confirms that the flakes are relatively small when compared with the ones in Fig. 5.
We investigated selected-area electron diffraction and HRTEM (FEI TECNAI G2 F30 model) images with an accelerating voltage of 200 kV to have further understanding of flake structures. The HRTEM image in Fig. 7a, b exhibits a monolayer MoS2 triangular and “chips-like” shape where Fig. 7c shows the periodic atomic arrangement. As it can be observed from the SEM images (Figs. 3, 5), most of the flakes are “chip-like” in shape, and triangular-shaped flakes also exist in the film network. Figure 7d displays diffraction patterns of a monolayer triangular flake. These single flakes have been prepared using the as-grown films through simply rinsing in water and drop casting the solution on a TEM grid. The symmetry in the diffraction spots show that the flake is a continuous single crystal, and there are no rotational boundaries. Corresponding selective area electron diffraction (SAED) pattern with [001] zone axis shows hexagonally arranged diffraction spots assigned to the (100) and (110) planes [21] suggestive of the highly crystalline nature of the MoS2 flakes.
4 Conclusions
We have shown that when substrate temperature and growth duration are controlled, MoS2 flakes with different properties including nanowall-like rough surfaces and relatively smoother monolayer MoS2 surfaces can be grown. Also, side products such as MoO3 and MoO2 can be avoided by fine-tuning the process parameters. Due to the complicated nucleation and growth process, it is important to optimize these parameters in different system geometries and flow rates to adjust the adsorption/desorption of radicals obtain sufficient sulfurization rates and find optimal conditions to grow monolayer MoS2 flakes. In our experiments, in addition to triangular flakes, we obtained rounded flakes resembling truncated triangles, which are not flat on the surface but rather erect at different angles. This result suggests that gas-phase reactions are also effective in monolayer MoS2 formation. Despite the roughness and heterogeneity of the formed network, we obtained films exhibiting a strong PL peak, a characteristic behavior of monolayer flakes, due the erect monolayer MoS2 nanowalls. These results show that such single-wall MoS2 flakes, which are mostly not flat on the surface, possess a rather larger surface area and can be beneficial in applications such as solar cells, energy storage, catalysis, and sensors with higher performance.
References
F.N. Xia, H.G. Yan, P. Avouris, The interaction of light and graphene: basics, devices, and applications. Proc. IEEE 101(7), 1717–1731 (2013). doi:10.1109/JPROC.2013.2250892
Y. Zhu, S. Murali, W. Cai, X. Li, J.W. Suk, J.R. Potts, R.S. Ruoff, Graphene and graphene oxide: synthesis, properties, and applications. Adv. Mater. 22(35), 3906–3924 (2010). doi:10.1002/adma.201001068
A.K. Geim, Graphene: status and prospects. Science 324(5934), 1530–1534 (2009). doi:10.1126/science.1158877
F. Bonaccorso, Z. Sun, T. Hasan, A.C. Ferrari, Graphene photonics and optoelectronics. Nat. Photonics 4(9), 611–622 (2010). doi:10.1038/nphoton.2010.186
E. Pop, V. Varshney, A.K. Roy, Thermal properties of graphene: fundamentals and applications. MRS Bull. 37(12), 1273–1281 (2012). doi:10.1557/mrs.2012.203
Z. Yang, R. Gao, N. Hu, J. Chai, Y. Cheng, L. Zhang, H. Wei, E.S.-W. Kong, Y. Zhang, The Prospective 2D graphene nanosheets: preparation functionalization and applications. Nano-Micro Lett. 4(1), 1–9 (2011). doi:10.3786/nml.v4i1.p1-9
F. Xia, D.B. Farmer, Y.-M. Lin, P. Avouris, Graphene field-effect transistors with high on/off current ratio and large transport band gap at room temperature. Nano Lett. 10(2), 715–718 (2010). doi:10.1021/nl9039636
Q. Xiang, J. Yu, M. Jaroniec, Synergetic effect of MoS2 and graphene as cocatalysts for enhanced photocatalytic H2 production activity of TiO2 nanoparticles. JACS 134(15), 6575–6578 (2012). doi:10.1021/ja302846n
H.-P. Komsa, A.V. Krasheninnikov, Two-dimensional transition metal dichalcogenide alloys: stability and electronic properties. J. Phys. Chem. Lett. 3(23), 3652–3656 (2012). doi:10.1021/jz301673x
T.C. Berkelbach, M.S. Hybertsen, D.R. Reichman, Theory of neutral and charged excitons in monolayer transition metal dichalcogenides. Phys. Rev. B 88(4), 045318 (2013). doi:10.1103/PhysRevB.88.045318
Y. Li, H. Wang, L. Xie, Y. Liang, G. Hong, H. Dai, MoS2 nanoparticles grown on graphene: an advanced catalyst for the hydrogen evolution reaction. JACS 133(19), 7296–7299 (2011). doi:10.1021/ja201269b
K. Chang, W. Chen, L-cysteine-assisted synthesis of layered MoS2/graphene composites with excellent electrochemical performances for lithium ion batteries. ACS Nano 5(6), 4720–4728 (2011). doi:10.1021/nn200659w
Q. Ji, Y. Zhang, T. Gao, Y. Zhang, D. Ma et al., Epitaxial monolayer MoS2 on mica with novel photoluminescence. Nano Lett. 13(8), 3870–3877 (2013). doi:10.1021/nl401938t
J. Shi, D. Ma, G.-F. Han, Y. Zhang, Q. Ji, T. Gao, J. Sun, X. Song, C. Li, Y. Zhang, Controllable growth and transfer of monolayer MoS2 on Au foils and its potential application in hydrogen evolution reaction. ACS Nano 8(10), 10196–10204 (2014). doi:10.1021/nn503211t
A. Splendiani, L. Sun, Y.B. Zhang, T.S. Li, J. Kim, C.Y. Chim, G. Galli, F. Wang, Emerging photoluminescence in monolayer MoS2. Nano Lett. 10(4), 1271–1275 (2010). doi:10.1021/nl903868w
X. Tong, E. Ashalley, F. Lin, H. Li, Z.M. Wang, Advances in MoS2-based field effect transistors (FETs). Nano-Micro Lett. 7(3), 203–218 (2015). doi:10.1007/s40820-015-0034-8
F. Prins, A.J. Goodman, W.A. Tisdale, Reduced dielectric screening and enhanced energy transfer in single-and few-layer MoS2. Nano Lett. 14(11), 6087–6091 (2014). doi:10.1021/nl5019386
C. Sevik, Assessment on lattice thermal properties of two-dimensional honeycomb structures: graphene, h-BN, h-MoS2, and h-MoSe2. Phys. Rev. B 89(3), 035422 (2014). doi:10.1103/PhysRevB.89.035422
W. Huang, X. Luo, C.K. Gan, S.Y. Quek, G. Liang, Theoretical study of thermoelectric properties of few-layer MoS2 and WSe2. Phys. Chem. Chem. Phys. 16(22), 10866–10874 (2014). doi:10.1039/c4cp00487f
Z. Zhou, Y. Lin, P. Zhang, E. Ashalley, M. Shafa, H. Li, J. Wu, Z. Wang, Hydrothermal fabrication of porous MoS2 and its visible light photocatalytic properties. Mater. Lett. 131, 122–124 (2014). doi:10.1016/j.matlet.2014.05.162
Y.-H. Lee, X.-Q. Zhang, W. Zhang, M.-T. Chang, C.-T. Lin et al., Synthesis of large-area MoS2 atomic layers with chemical vapor deposition. Adv. Mater. 24(17), 2320–2325 (2012). doi:10.1002/adma.201104798
Y. Zhan, Z. Liu, S. Najmaei, P.M. Ajayan, J. Lou, Large-area vapor-phase growth and characterization of MoS2 atomic layers on a SiO2 substrate. Small 8(7), 966–971 (2012). doi:10.1002/smll.201102654
S. Wu, C. Huang, G. Aivazian, J.S. Ross, D.H. Cobden, X. Xu, Vapor-solid growth of high optical quality MoS2 monolayers with near-unity valley polarization. ACS Nano 7(3), 2768–2772 (2013). doi:10.1021/nn4002038
S. Balendhran, J.Z. Ou, M. Bhaskaran, S. Sriram, S. Ippolito et al., Atomically thin layers of MoS2 via a two step thermal evaporation–exfoliation method. Nanoscale 4(2), 461–466 (2012). doi:10.1039/C1NR10803D
J.N. Coleman, M. Lotya, A. O’Neill, S.D. Bergin, P.J. King, U. Khan, K. Young, A. Gaucher, S. De, R.J. Smith, Two-dimensional nanosheets produced by liquid exfoliation of layered materials. Science 331(6017), 568–571 (2011). doi:10.1126/science.1194975
D. Sun, S. Feng, M. Terrones, R.E. Schaak, Formation and interlayer decoupling of colloidal MoSe2 nanoflowers. Chem. Mater. 27(8), 3167–3175 (2015). doi:10.1021/acs.chemmater.5b01129
A.M. van der Zande, P.Y. Huang, D.A. Chenet, T.C. Berkelbach, Y. You et al., Grains and grain boundaries in highly crystalline monolayer molybdenum disulphide. Nat. Mater. 12(6), 554–561 (2013). doi:10.1038/nmat3633
K.-K. Liu, W. Zhang, Y.-H. Lee, Y.-C. Lin, M.-T. Chang et al., Growth of large-area and highly crystalline MoS2 thin layers on insulating substrates. Nano Lett. 12(3), 1538–1544 (2012). doi:10.1021/nl2043612
Y. Shi, W. Zhou, A.-Y. Lu, W. Fang, Y.-H. Lee et al., Van der waals epitaxy of MoS2 layers using graphene as growth templates. Nano Lett. 12(6), 2784–2791 (2012). doi:10.1021/nl204562j
W. Zhang, J.K. Huang, C.H. Chen, Y.H. Chang, Y.J. Cheng, L.J. Li, High-gain phototransistors based on a CVD MoS2 monolayer. Adv. Mater. 25(25), 3456–3461 (2013). doi:10.1002/adma.201301244
W. Zhang, C.-P. Chuu, J.-K. Huang, C.-H. Chen, M.-L. Tsai et al., Ultrahigh-gain photodetectors based on atomically thin graphene-MoS2 heterostructures. Sci. Rep. 4, 3826 (2014). doi:10.1038/srep03826
I.S. Kim, V.K. Sangwan, D. Jariwala, J.D. Wood, S. Park et al., Influence of stoichiometry on the optical and electrical properties of chemical vapor deposition derived MoS2. ACS Nano 8(10), 10551–10558 (2014). doi:10.1021/nn503988x
J. Zhang, H. Yu, W. Chen, X. Tian, D. Liu et al., Scalable growth of high-quality polycrystalline MoS2 monolayers on SiO2 with tunable grain sizes. ACS Nano 8(6), 6024–6030 (2014). doi:10.1021/nn5020819
S. Wang, Y. Rong, Y. Fan, M. Pacios, H. Bhaskaran, K. He, J.H. Warner, Shape evolution of monolayer MoS2 crystals grown by chemical vapor deposition. Chem. Mater. 26(22), 6371–6379 (2014). doi:10.1021/cm5025662
M.-L. Tsai, S.-H. Su, J.-K. Chang, D.-S. Tsai, C.-H. Chen, C.-I. Wu, L.-J. Li, L.-J. Chen, J.-H. He, Monolayer MoS2 heterojunction solar cells. ACS Nano 8(8), 8317–8322 (2014). doi:10.1021/nn502776h
H. Hwang, H. Kim, J. Cho, MoS2 nanoplates consisting of disordered graphene-like layers for high rate lithium battery anode materials. Nano Lett. 11(11), 4826–4830 (2011). doi:10.1021/nl202675f
H. Li, Z. Yin, Q. He, H. Li, X. Huang, G. Lu, D.W.H. Fam, A.I.Y. Tok, Q. Zhang, H. Zhang, Fabrication of single- and multilayer MoS2 film-based field-effect transistors for sensing no at room temperature. Small 8(1), 63–67 (2012). doi:10.1002/smll.201101016
X.L. Li, Y.D. Li, Formation of MoS2 inorganic fullerenes (IFs) by the reaction of MoO3 nanobelts and S. Chem. Eur. J. 9(12), 2726–2731 (2003). doi:10.1002/chem.200204635
C. Lee, H. Yan, L.E. Brus, T.F. Heinz, J. Hone, S. Ryu, Anomalous lattice vibrations of single- and few-layer MoS2. ACS Nano 4(5), 2695–2700 (2010). doi:10.1021/nn1003937
B. Windom, W.G. Sawyer, D. Hahn, A Raman spectroscopic study of MoS2 and MoO3: applications to tribological systems. Tribol. Lett. 42(3), 301–310 (2011). doi:10.1007/s11249-011-9774-x
H. Li, Q. Zhang, C.C.R. Yap, B.K. Tay, T.H.T. Edwin, A. Olivier, D. Baillargeat, From bulk to monolayer MoS2: evolution of Raman scattering. Adv. Funct. Mater. 22(7), 1385–1390 (2012). doi:10.1002/adfm.201102111
L. Kumari, Y.-R. Ma, C.-C. Tsai, Y.-W. Lin, S.Y. Wu, K.-W. Cheng, Y. Liou, X-ray diffraction and Raman scattering studies on large-area array and nanobranched structure of 1D MoO2 nanorods. Nanotechnology 18(11), 115717 (2007). doi:10.1088/0957-4484/18/11/115717
M.M. Perera, M.-W. Lin, H.-J. Chuang, B.P. Chamlagain, C. Wang, X. Tan, M.M.-C. Cheng, D. Tománek, Z. Zhou, Improved carrier mobility in few-layer MoS2 field-effect transistors with ionic-liquid gating. ACS Nano 7(5), 4449–4458 (2013). doi:10.1021/nn401053g
B. Chakraborty, A. Bera, D.V.S. Muthu, S. Bhowmick, U.V. Waghmare, A.K. Sood, Symmetry-dependent phonon renormalization in monolayer MoS2 transistor. Phys. Rev. B 85(16), 161403 (2012). doi:10.1103/PhysRevB.85.161403
M. Buscema, G. Steele, H.J. van der Zant, A. Castellanos-Gomez, The effect of the substrate on the Raman and photoluminescence emission of single-layer MoS2. Nano Res. 7(4), 561–571 (2014). doi:10.1007/s12274-014-0424-0
X.X. Wei, Y. Cheng, D. Huo, Y.H. Zhang, J.Z. Wang, Y. Hu, Y. Shi, PL enhancement of MoS2 by Au nanoparticles. Acta Phys. Sin. 63(21), 217802 (2014). doi:10.7498/aps.63.217802
A. Splendiani, L. Sun, Y. Zhang, T. Li, J. Kim, C.-Y. Chim, G. Galli, F. Wang, Emerging photoluminescence in monolayer MoS2. Nano Lett. 10(4), 1271–1275 (2010). doi:10.1021/nl903868w
L.-P. Feng, J. Su, D.-P. Li, Z.-T. Liu, Tuning the electronic properties of Ti–MoS2 contacts through introducing vacancies in monolayer MoS2. Phys. Chem. Chem. Phys. 17(10), 6700–6704 (2015). doi:10.1039/C5CP00008D
C. Ataca, S. Ciraci, Dissociation of H2O at the vacancies of single-layer MoS2. Phys. Rev. B 85(19), 195410 (2012). doi:10.1103/PhysRevB.85.195410
D. Liu, Y. Guo, L. Fang, J. Robertson, Sulfur vacancies in monolayer MoS2 and its electrical contacts. Appl. Phys. Lett. 103(18), 183113 (2013). doi:10.1063/1.4824893
W. Zhou, X. Zou, S. Najmaei, Z. Liu, Y. Shi, J. Kong, J. Lou, P.M. Ajayan, B.I. Yakobson, J.-C. Idrobo, Intrinsic structural defects in monolayer molybdenum disulfide. Nano Lett. 13(6), 2615–2622 (2013). doi:10.1021/nl4007479
S. Bertolazzi, D. Krasnozhon, A. Kis, Nonvolatile memory cells based on MoS2/graphene heterostructures. ACS Nano 7(4), 3246–3252 (2013). doi:10.1021/nn3059136
Z. Yin, H. Li, H. Li, L. Jiang, Y. Shi, Y. Sun, G. Lu, Q. Zhang, X. Chen, H. Zhang, Single-layer MoS2 phototransistors. ACS Nano 6(1), 74–80 (2011). doi:10.1021/nn2024557
K. Kalantar-Zadeh, J. Tang, M. Wang, K.L. Wang, A. Shailos et al., Synthesis of nanometre-thick MoO3 sheets. Nanoscale 2(3), 429–433 (2010). doi:10.1039/B9NR00320G
J.V. Silveira, L.L. Vieira, A.J. Sampaio, O.L. Alves, A.G. Souza Filho, Temperature-dependent Raman spectroscopy study in MoO3 nanoribbons. J. Raman Spectrosc. 43(10), 1407–1412 (2012). doi:10.1002/jrs.4058
Q. Ji, Y. Zhang, Y. Zhang, Z. Liu, Chemical vapour deposition of group-VIB metal dichalcogenide monolayers: engineered substrates from amorphous to single crystalline. Chem. Soc. Rev. 44, 2587–2602 (2015). Advance Article
J. Guo, X. Chen, S. Jin, M. Zhang, C. Liang, Synthesis of graphene-like MoS2 nanowall/graphene nanosheet hybrid materials with high lithium storage performance. Catal. Today 246, 165–171 (2015). doi:10.1016/j.cattod.2014.09.028
S. Najmaei, Z. Liu, W. Zhou, X. Zou, G. Shi, S. Lei, B.I. Yakobson, J.-C. Idrobo, P.M. Ajayan, J. Lou, Vapour phase growth and grain boundary structure of molybdenum disulphide atomic layers. Nat. Mater. 12(8), 754–759 (2013). doi:10.1038/nmat3673
B. Li, S. Yang, N. Huo, Y. Li, J. Yang, R. Li, C. Fan, F. Lu, Growth of large area few-layer or monolayer MoS2 from controllable MoO3 nanowire nuclei. RSC Adv. 4(50), 26407–26412 (2014). doi:10.1039/c4ra01632g
J.M. Soon, K.P. Loh, Electrochemical double-layer capacitance of MoS2 nanowall films. Electrochem. Solid-State Lett. 10(11), A250–A254 (2007). doi:10.1149/1.2778851
Z. Fan, J. Chen, B. Zhang, B. Liu, X. Zhong, Y. Kuang, High dispersion of γ-MnO2 on well-aligned carbon nanotube arrays and its application in supercapacitors. Diam. Relat. Mater. 17(11), 1943–1948 (2008). doi:10.1016/j.diamond.2008.04.015
A. Sharma, A. Nayak, R. Ghosh, H.-Y. Chang, The Optoelectronic Properties of CVD Grown MoS2 Nanowalls. in NCUR 2014, University of Kentucky, Lexington, 3–5 April 2014
U.K. Sen, S. Mitra, High-rate and high-energy-density lithium-ion battery anode containing 2D MoS2 nanowall and cellulose binder. ACS Appl. Mater. Interf. 5(4), 1240–1247 (2013). doi:10.1021/am3022015
M.A. Camacho-López, L. Escobar-Alarcón, M. Picquart, R. Arroyo, G. Córdoba, E. Haro-Poniatowski, Micro-Raman study of the m-MoO2 to α-MoO3 transformation induced by CW-laser irradiation. Opt. Mater. 33(3), 480–484 (2011). doi:10.1016/j.optmat.2010.10.028
T. Siciliano, A. Tepore, E. Filippo, G. Micocci, M. Tepore, Characteristics of molybdenum trioxide nanobelts prepared by thermal evaporation technique. Mater. Chem. Phys. 114(2), 687–691 (2009). doi:10.1016/j.matchemphys.2008.10.018
Acknowledgments
This work was supported by Anadolu University BAP 1407F335 and BAP 1505F271 Projects. The authors are pleased to acknowledge Prof. H. V. Demir, Aydan Yeltik, Assoc. Prof. F. Ay and Assoc. Prof. C. Sevik for fruitful discussions and kind support.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Perkgoz, N.K., Bay, M. Investigation of Single-Wall MoS2 Monolayer Flakes Grown by Chemical Vapor Deposition. Nano-Micro Lett. 8, 70–79 (2016). https://doi.org/10.1007/s40820-015-0064-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40820-015-0064-2