Abstract
Powder metallurgy and thermal spraying has been used traditionally to manufacture functionally graded materials (FGMs). However, only simple geometries can be made with these processes and the compositional gradients cannot be tailored. These disadvantages can be overcome by employing additive manufacturing (AM). 3D plasma metal deposition (3DPMD) is a new technique that combines the advantages of plasma powder and additive processes. This process allows the production of structures with mixtures of different materials and powder fraction targeting changes in local properties and microstructures. For example, up to four powders, which can be different in terms of chemistry and powder fraction, can be mixed within one layer to adapt the local properties of the structure. The feasibility of functionally graded structures of stainless steel 316L (SS316L) and Ni80-20 alloy was studied. Two configurations, transition between the steel and the Ni-based alloy, were tested. The first one is hard transition, SS316L on the bottom and Ni80-20 on the top. The second one, a smooth transition between both materials was created with 50% of steel and 50% of Ni-based alloy. Optical microscopy and scanning electron microscopy were used to characterize the microstructures. The manufactured part showed good appearance, without any external defects and acceptable geometric accuracy. The layer thickness was around z = 1 mm for both structures. Regarding the microstructural characterization, both materials displayed a dendritic structure. In the SS316L, the microstructure was composed by an austenitic matrix with δ-ferrite located in the grain boundaries. The microstructure of the Ni80-20 was characterized as an austenitic matrix, with some M7C3 and M23C6 precipitates. In addition, the Laves phase was also observed.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
The main advantages of multi-material additive manufacturing (MMAM) are the possibility of local variation of the part properties [1] or materials composition [2] depending on the real loads. MMAM is defined as the layer-by-layer production of components made of formless material, as opposed to subtractive or formative manufacturing methodologies, with locally modified properties. The local adaptation of the component porosity, following the example of human bone, is an example of this [3,4,5]. The advantages of continuous material change are higher tolerable loads [6], lower thermal stresses [7,8,9,10,11,12], and a reduced tendency to cracks [13]. In this work, multi-material components with a continuous and abrupt transition from steel to nickel-based alloy are produced.
The advanced 3D plasma metal deposition process is used for this purpose. 3D plasma metal deposition process (3DPMD) is a development of the classic plasma transfer arc (PTA) process with adaptations to the requirements of additive manufacturing. Previous research has used the micro PTA to produce graded components from Ni-based alloy with Al2O3 ceramics [14]. However, the lower build-up rates and the higher demands on powder quality are the disadvantages compared with 3DPMD. This is characterized by a build-up rate of up to 10 kg/h, low demands on powder quality, and the ability to process up to four powders simultaneously. Further information on the process and the materials to be processed can be found in earlier publications [2, 15,16,17]. Previous work on the production of graded steel and nickel-based components has primarily used beam-based direct energy deposition processes such as laser metal deposition [18], laser cladding [19], or laser rapid forming [20]. Applications of laser-based powder bed processes are also well known [1].
In this study, an austenitic stainless steel 316L and a heat-resistance Ni-based alloy Ni80-20 are employed [20]. These alloys are used in different industries, such as petrochemical, shipbuilding, and nuclear. Multi-material structures of these alloys were manufactured using 3DPMD. Two configurations were studied; the first one is a smooth transition between both materials with a transition region of 50% SS316L/50% Ni80-20 and the second one, a hard transition (discrete transition between the materials). The effects of the process parameters on the geometry and the microstructure were investigated.
2 Materials and experimental procedure
Functionally graded structures of stainless steel 316L and Ni80-20 alloy were fabricated using 3DPMD. Table 1 shows the chemical composition of the powder used. Both materials have a FCC structure with similar lattice parameters. For the base platform (BP), a t = 10 mm thick plate of SS316L was employed. Two configurations of fabrication were used. The first one (hard transition, HT), SS316L on the bottom and Ni80-20 on the top. Fifteen layers of each material were applied for the HT configuration. The second one (smooth transition, ST), a transition region (mix zone) between both materials was made with 50% of steel and 50% of Ni-based alloy. Thirty layers in total were applied for this configuration, ten for each material. The structures have a length of l = 120 mm, width of w = 30 mm, and height of h = 30 mm. The build-up process was continuous without interruption of the welding process between the layers and with a constant layer thickness of 1 mm.
A welding torch PlasmaStar MV230 (Imax = 230 A) equipped with two separate powder feeds and a power source PlasmaStar 500 (Imax = 500 A) were used to build the structures. Powders with a particle size between 50 and 150 μm of both materials were fed with a meander disk feeder. High-purity argon was employed as shielding and plasma gas. A six axis-articulated arm robot REIS RV20-16 was used as a manipulation system (Fig. 1).
vs = 10 mm s−1 and Us = 23 V were used as a constant welding speed and voltage, respectively, during the deposition of the layers. The welding current was IS = 120 A for the SS316L, IS = 105 A for the Ni80-20, and IS = 110 A for the mixture powder (50% of steel and 50% of Ni-based alloy).
For the metallographic examinations, cross-section specimens from the fabricated structures were obtained. Standard metallographic preparation was used. A total of 10% oxalic acid was used at 2 V for 30 s to reveal the microstructures of the as-build deposits. The microstructure was observed using optical microscopy (OM) and scanning electron microscopy (SEM).
3 Results and discussion
The as-build structures presented good surface appearance without external cracks, voids, and partially molten powder particles. Due to the AM typical post-processing, this is negligible. Furthermore, good bonding with the base material was observed. The ST structure fabricated by 3DPMD is shown in Fig. 2. Figure 3 depicts the macro view of the two structures. No internal irregularities were observed. As mentioned, the SS316L is located on the bottom and the Ni-based alloy on the top. The ST sample shows the continuous material transition with the transition zone (TZ) in the center. A wall thickness of t = 6.7 mm and a component height of h = 30.4 mm were measured. Concerning the number of layers of 30, a layer thickness of z = 1.01 mm was obtained. The evaluation of HT sample shows the abrupt material transition (see Fig. 3). Thus, the transition occurs in a narrow zone, one layer, compared with 10 layers of the ST structure. This was caused by the process typical dilution of the lower layer through the upper layer formation and cannot be avoided. Compared with the continuous material transition, the wall thickness is reduced by Δt = 16% to t = 5.6 mm, and the component height is increased by Δh = 6.5% to h = 32.5 mm. The layer thickness of z = 1.08 mm deviates only slightly.
The variable proportion of the nickel-based alloy in the total component can explain the variation of the component geometry. The lower thermal conductivity of the nickel-based alloy leads to heat accumulation and thus to larger melt pool geometries with effects on the geometry. The larger the proportion of the nickel-based alloy in the entire component, the greater the effect on the same.
The as-deposited microstructures of both 3D structures are shown in Fig. 4 and Fig. 5 for the ST and HT sample, respectively. Comparing both structures, no significant differences were observed in the microstructure. However, the major difference is the presence of a transition region with a chemical composition gradient in the ST sample (Fig. 4d), i)).
The microstructural characterization of the stainless steel (bottom part of the structures) showed the presence of austenite and δ-ferrite, as depicted in Fig. 4b), g) and Fig. 5b), f). At the interface with base platform, the precipitation of δ-ferrite was also observed. The γ matrix and the δ-ferrite exhibited a dendrite and vermicular morphology, respectively. At the top part of the samples (Ni80-20 region), the microstructure was recognized as austenite (γ) matrix with some M7C3 precipitates and the Laves phase (Fig. 4f), k) and Fig. 5e), i)). Intergranular and intragranular second phases were observed in the austenitic matrix. In addition, the γ matrix presented a dendrite morphology. The main element for the M7C3 precipitate is the Cr and presented a roughly round morphology. On the other hand, based on the chemical composition of the Ni80-20 alloy, the intermetallic compound laves has an A2B type structure and is classified as (Ni, Fe, Cr)2(Mo, Si). A roughly continued morphology at the grain boundaries was noticed for the Laves phase. The microstructure of the Ni80-20 for the HT sample is shown in Fig. 6.
At the mix zone of the ST structure, a dendrite morphology was observed corresponding to an austenite (γ) matrix. Moreover, M7C3 precipitates and the Laves phase were identified in the microstructure. Changes in the chemical composition of the mix zone caused the variations in the morphology of the phases. Therefore, a change of the Laves morphology was observed with a γ/laves eutectic type. Figure 7 depicts detailed view of the microstructure of the ST sample.
4 Conclusions
This work shows the feasibility of the 3D plasma metal deposition for fabrication of functionally graded structures of SS316L to Ni80-20. No external delamination or cracks were observed in the 3D structures. However, some pores were observed at the Ni-based.
The microstructural characterizations showed different phases on the 3D structures. The austenitic stainless steel showed an austenite (γ) matrix with δ-phase. The Ni80-20 exhibited austenite (γ) matrix with some M7C3 precipitates and the Laves phase. The mix zone exhibited same microstructures, however changes in the morphology were observed.
In summary, 3DPMD was qualified as an effective process in multi-material additive manufacturing of transition structures from austenitic stainless steel to nickel-based alloys. Defect-free structures with a homogeneous transition with complete mixing in the transition zones were produced. The process offers great potential for other metal transitions.
References
Popovich VA, Borisov EV, Popovich AA, Sufiiarov VS, Masaylo DV, Alzina L (2017) Functionally graded Inconel 718 processed by additive manufacturing: crystallographic texture, anisotropy of microstructure and mechanical properties. Adv Mater Res-Switz 114:441–449
Hoefer K, Nitsche A, Abstoß K-G, Ertugrul G, Haelsig A, Mayr P (2019) Multi-material additive manufacturing by 3D plasma metal deposition for graded structures of super duplex alloy 1.4410 and the austenitic corrosion resistant alloy 1.4404. JOM 71:1554–1559
Bandyopadhyay A, Krishna BV, Xue W, Bose S (2009) Application of laser engineered net shaping (LENS) to manufacture porous and functionally graded structures for load bearing implants. J Mater Sci Mater Med 20:29–34
Parthasarathy J, Starly B, Raman S (2011) A design for additive manufacture of functionally graded porous structures with tailored mechanical properties for biomedical applications. J Manuf Process 13:160–170
Murr LE, Gaytan SM, Martinez E, Medina F, Wicker RB (2012) Metal fabrication by additive manufacturing using laser and electron beam melting technologies. Int J Biomater 28:1–14
Sampath S, Herman H, Shimoda N, Saito T (1995) Thermal spray processing of FGMs. MRS Bull 20:27–31
Suresh S, Giannakopoulos AE, Alcalá J (1997) Sherical indentation of compositionally graded materials: theory and experiments. Acta Mater 45:1307–1321
Giannakopoulos AE, Suresh S (1997) Indentation of solids with gradients in elastic properties: part II axisymmetric indentors. Int J Solids Struct 34:2393–2428
Giannakopoulos AE, Suresh S, Finot M, Olsson M (1995) Elastoplastic analysis of thermal cycling: layered materials with compositional gradients. Acta Metall Mater 43:1335–1354
Williamson RL, Rabin RH, Drake JT (1993) Finite elements analysis of thermal residual stresses at graded ceramic-metal interfaces. J Appl Phys 74:1310–1320
Drake JT, Williamson RL, Rabin RH (1993) Finite elemete analysis of thermal residual stresses at graded ceramic-metal interfaces – part II microstructure. J Appl Phys 74:1321–1326
Erdogan F (1995) Fracture mechanics of functionally graded materials. Compos Eng 5:753–770
Zou H, Zhang H, Guilan W, Li J (2009) Rapid manufacturing of FGM components by using electromagnetic compressed plasma deposition. Electromagnetics research symposium (Moskau), pp.1953–1957
Hoefer K, Hälsig A, Mayr P (2018) Arc-based additive manufacturing of steel components -comparison of wire- and powder-based variants. Weld World 62:243–247
Hoefer K, Mayr P (2018) 3DPMD – additive manufacturing of titanium parts using 3D plasma metal deposition. Mater Sci Forum 941:2137–2141
Hoefer K, Teichgraeber C, Mayr P, Berger M (2017) Arc-based additive manufacturing – 3DPMD (Generative Fertigung mit Lichtbogenprozessen). In: Mayr P, Berger M (eds) Fümotec. Chemnitz University of Technology, Chemnitz, pp 1–14 (German)
Pulugurtha SR, Newkirk J, Liou F, Chou H (2010) Functionally graded materials by laser metal deposition (preprint). Proceedings of the 21st Annual International Solid Freeform Fabrication Symposium (2010, Austin, TX), University of Texas Press
Abboud JH, Rawlings RD, West DRF (1995) Functionally graded nickel-aluminide and iron-aluminide coatings produced via laser cladding. J Mater Sci 30:5931–5938
Xu X, Lin X, Chen J, He F, Huang W (2007) Laser rapid forming of Ti-Ni functionally graded alloy. Mater Sci Forum 561-565:227–230
Hüpf T, Cagran C, Kaschnitz E, Pottlacher G (2009) Thermophysical properties of Ni80Cr20. Thermochim Acta 494:40–44
Funding
Open Access funding provided by Projekt DEAL.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher’s note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
This article is part of the collection Additive Manufacturing - Processes, Simulation and Inspection Recommended for publication by Commission I - Additive Manufacturing, Surfacing, and Thermal Cutting
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hoefer, K., Rodriguez, J., Haelsig, A. et al. Fabrication of SS316L to Ni80Cr20 graded structures by 3D plasma metal deposition. Weld World 64, 1307–1311 (2020). https://doi.org/10.1007/s40194-020-00870-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40194-020-00870-x