Abstract
The influence of the spherical anisotropy (SA) of a middle layer on the plasmon resonance couplings in the sandwiched gold nanoshell (Au/SA/Au) has been investigated by means of a modified Mie theory. It is found that the plasmon couplings in the Au/SA/Au nanoshells are more sensitive to the permittivity along the radial direction of SA layer than the permittivity along the tangential direction. With increasing the anisotropic value of the middle layer, the dipole peaks of antisymmetric ω −− mode and symmetric ω +− mode both show blue-shifts, while the shift of the antisymmetric ω −− mode is larger than that for the symmetric ω +− mode. The larger anisotropic value of the SA layer induces the stronger near-field outside the nanoparticles for the antisymmetric ω −− mode, while the smaller anisotropic value makes the larger near-field for the symmetric ω +− mode. We further have found that the middle SA layer with smaller anisotropic value is helpful to obtain larger electric fields inside the nanoshells, which may be useful for their potential applications in nonlinear optics.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Metallodielectric layered nanoparticles and nanostructures have attracted increasing scientific and technological interest in recent years due to their importance in the fundamental physics and the potential applications in nano-electronics, biomedical imaging, nano-optical device, and optical sensing [1–5]. A special interesting structure is metal–dielectric–metal three-layered nanoparticle, whose optical properties highly depend on the couplings between the plasmons of inner core and outer shell [6–8]. Changing the internal geometry of this nanoparticle not only shifts its resonance frequencies, but also strongly modifies the relative magnitudes of the absorption and scattering cross sections [5]. Mukherjee et al. [9] have found that an asymmetric core in Au/SiO2/Au can lead to an additional high multipolar Fano resonance. A significant superscattering phenomenon also has been found in the plasmonic–dielectric–plasmonic layered nanorod [3] and nanosphere [4].
Among the metallodielectric layered nanoparticles, the spherical anisotropic (SA) material–metal nano-composite shows a growing interest because of the applications in optical devices, surface-enhanced Raman spectroscopy (SERS) and optical nonlinearity enhancement [10–12]. Spherical anisotropy indicates that the tensor for dielectric function is radially anisotropic, i.e., the dielectric function is uniaxial in spherical coordinate with ɛ r along the radial direction and ɛ t along the tangential direction. Gao et al. [10] have reported that the adjustment of the dielectric anisotropy in the core or shell could result in large enhancements of the second harmonic generation and induced third harmonic generation susceptibilities at surface plasmon resonant frequencies. Yin et al. [11] have found that the introduction of spherical anisotropy into the core or the shell provides a novel approach to tailor the surface plasmon resonant frequencies and enhanced SERS peaks. It is further found that the spherically anisotropy of inner core can strongly modulate the Fano resonance in the Ag nanoshell with a spherically anisotropic core [12]. However, the modulation of spherical anisotropy on the plasmon couplings in metallodielectric layered nanoparticles is seldom reported.
In this paper, we have investigated the optical properties of the sandwiched gold nanoshell with an SA middle layer (Au/SA/Au) by using a modified Mie theory. Spherical anisotropy was indeed found in phospholipid vesicle systems [13] and in cell membranes containing mobile charges [14]. Lucas et al. [15] have easily established the spherically anisotropic materials by using the graphitic multishells. We focus on the influence of the spherical anisotropy of the middle layer on the plasmon couplings between the inner core and outer shell. In addition, the dependence of the local electric field enhancement on the spherical anisotropy of the middle layer has been further discussed in detail.
Electromagnetic scattering model
Figure 1 shows the specific geometry of a sandwiched gold nanoshell. The nanoparticle consists of a gold core with a radius of r 1, an SA middle layer with a radius of r 2, and a gold shell with a radius of r 3. The dielectric constant of embedding medium is ɛ 4. The SA middle layer is characterized by constitutive tensors of permittivity
ɛ 2r is along the radial direction and ɛ 2t is along the tangential direction. The dielectric functions of inner metal core ɛ 1 and outer metal shell ɛ 3 have real and imaginary frequency-dependent components, which are affected by the scattering of the conduction electrons in the particle surfaces. Thus, ɛ 1 and ɛ 3 are usually accounted by replacing the ideal Drude part in the dielectric function with a size-dependent one [8]. Light scattering by a spherical particle can be expressed through Debye potentials [16]. For spherical anisotropic material, the electric ψ TM and magnetic ψ TE Debye potentials are presented as [17]
Here, \( {k_0}={{{2\pi }} \left/ {\lambda } \right.} \) is the wave vector in vacuum and \( {\mu_{\mathrm{r}}}={\mu_{\mathrm{t}}}=1 \). The electromagnetic waves are expanded to spherical partial waves using vector spherical harmonics, and then, Maxwell's boundary conditions are applied to resolve the unknown expansion coefficients of the scattered and interior waves. According to the Mie scattering theory, the obtained extinction efficiency Q ext, scattering efficiency Q sca, and absorption efficiency Q abs can be expressed as [16]
Here, \( {k_4}={k_0}\sqrt{\varepsilon_4 } \), a n and b n are the scattering coefficients. The information about spherical anisotropic middle layer is presented by the order of spherical Bessel functions [17]. The order can be expressed as
Results and discussion
Figure 2a shows the extinction spectra of the Au/SA/Au nanoshells for the conditions of ρ < 1. We assume ρ as the anisotropic value of the middle layer \( {{{{\varepsilon_{{2\mathrm{t}}}}}} \left/ {{{\varepsilon_{{2\mathrm{r}}}}}} \right.} \). Here, r 1, r 2, and r 3 are fixed at 35, 50, and 65 nm, respectively. To discuss the influence of ɛ 2r on the plasmon resonances, ɛ 2t value is fixed at 2.04. The embedding medium is assumed to be water (ɛ 4 = 1.7689). The plasmon resonances in the Au/SA/Au nanoshell can be considered as an interaction between the plasmons of a gold nanosphere and a gold nanoshell [5, 8, 18]. As shown in Fig. 2a, for \( {{{{\varepsilon_{{2\mathrm{t}}}}}} \left/ {{{\varepsilon_{{2\mathrm{r}}}}}} \right.}=1 \), one dipole peak appears at 838 nm, which corresponds to the antisymmetric coupling (ω −− mode) between the plasmons of inner Au core (ω s ) and the symmetric mode of outer Au nanoshell (ω −). Another dipole peak appears at 577 nm, which corresponds to the symmetric coupling (ω +− mode) between ω s and ω − modes. The decreased ρ value means the increase of ɛ 2r value. With increasing ɛ 2r value, the dipole peak of ω +− mode shows a red-shift from 577 nm at ρ = 1 to 625 nm at ρ = 1/5, while the dipole peak of ω −− mode shows a very large red-shift from 838 nm to 1,511 nm. The increased ɛ 2r value should decrease the induced charges in the inner and outer surfaces of the middle layer [19]. In this case, the plasmon resonance energies of ω s and ω − modes decrease, and hence, the red-shifts of the ω −− and ω +− modes. According to plasmon hybridization theory [19–21], the ω −− mode is sensitive to the ω − mode, while the ω +− mode depends on the ω s mode. The large red-shift of the ω −− mode indicates that the variation of ɛ 2r has more effect on the ω − mode than the ω s mode. Figure 2b shows the extinction spectra of the Au/SA/Au nanoshells for the conditions of ρ > 1. Here, the ɛ 2r value is fixed at 2.04. The increased ρ value means the increase of ɛ 2t value. With increasing ɛ 2t value, the dipole peak of ω +− mode shows a red-shift from 577 nm at ρ = 1 to 611 nm at ρ = 5, while the dipole peak of ω −− mode shows a red-shift from 838 to 859 nm. The small red-shifts of the ω −− and ω +− modes suggest that the increased ɛ 2t value has little effect on the decrease of the induced charges in both surfaces of the middle layer. The red-shift of the mode is larger than that of the ω −− mode, which indicates the suppressed coupling between the ω s and ω − modes due to the increased ɛ 2t value.
Figure 3a, d shows the distributions of the electric field enhancement in the sandwiched nanoshell (ɛ 2t/ɛ 2r = 1) at wavelengths of 577 nm (ω +− ) and 838 nm (ω −− ), respectively. The distributions of the electric field enhancement show the typical dipole resonance properties [22]. The large electrical field on the shell occurs along the incident polarization and only locates within a few nanometer of the shell surface, while the inner core also exhibits a similar dipole pattern. In Fig. 3d, a large electric field is observed near the core mainly due to the antisymmetric coupling between the ω s and ω − modes, which leads to different kinds of charges induced in inner and outer surfaces of the middle layer [18]. Figure 3b, e shows the contour plots of the electric field enhancement in the Au/SA/Au with ρ = 1/1.1 (divided by the results of the Au/SA/Au with ρ = 1). The calculation wavelengths are fixed at 577 and 838 nm for subpanels b and e of Fig. 3, respectively. In Fig. 3b, the decrease of the induced charge in outer surface of the middle layer is larger than that in inner surface of the middle layer. For the ω −− mode, the increased ɛ 2r value induces the large electric field inside the nanoparticle. Figure 3c, f shows the contour plots of the electric field enhancement in the Au/SA/Au with ρ = 1.1 at wavelengths of 577 and 838 nm (divided by the results of the Au/SA/Au with ρ = 1), respectively. The increased ɛ 2t value should lead to the decrease of the induced charges on the inner and outer surfaces of the SA layer. It is obvious that the effects of the variation of ɛ 2t on the induced charges and the coupling between ω s and ω − modes are weaker than those due to the variation of ɛ 2r.
To further clarify the role of anisotropy, we keep the geometric average of dielectric components \( {\varepsilon_{\mathrm{i}}}={{{{\varepsilon_{{2\mathrm{r}}}}}} \left/ {3} \right.}+{{{2{\varepsilon_{{3\mathrm{t}}}}}} \left/ {3} \right.} \) unchanged for the SA middle layer [12], while ɛ 2t/ɛ 2r value is varied. Figure 4 shows the extinction spectra of the Au/SA/Au nanoshells with various ρ values. Here, r 1, r 2, and r 3 are fixed at 35, 50, and 65 nm, respectively. The ɛ i value is fixed at 2.04. With an increasing ρ value, the dipole peak of the ω −− mode shows a distinct blue-shift from 1,589 nm at ρ = 1/5 to 722 nm at ρ = 5, while the strength of the peak increases. At the same time, the dipole peak of the ω +− mode shows a blue-shift from 606 nm at ρ = 1/5 to 503 nm at ρ = 5, but the strength of the peak decreases. The influence of the variation of anisotropic value on the plasmon resonances in the Au/SA/Au nanoshell with ρ < 1 is stronger than that for ρ > 1. Figure 5a shows the dependences of the E-field enhancement in the Au/SA/Au nanoshell as a function of ρ value, which are calculated at the dipole resonance wavelengths of ω +− mode. In Fig. 5a, the dashed circle line for right-hand scale represents the variation of E-field enhancement maximum outside the nanoshell (EMO), which often locates on the outer surface of the particle and at the poles along the incident polarization. The dashed square line for left-hand scale shows the variation of the E-field enhancement maximum inside the nanoshell (EMI), which can be obtained on the surface of inner gold core and at the poles along the incident polarization. In Fig. 5b, the dashed circle line for right-hand scale and dashed square line for left-hand scale represent the variations of EMO and EMI, respectively, which are calculated at the dipole resonance wavelengths of ω −− mode. It is found with the increase in ρ value that the EMO for the ω +− mode decreases from 4.97 at ρ = 1/10 to 0.68 at ρ = 10, while the EMI decreases from 31.15 at ρ = 1/10 to 1.92 at ρ = 10. At the same time, the EMO for the ω −− mode increases first from 4.13 at ρ = 1/10 to 6.68 at ρ = 2 and then decreases to 6.51 at ρ = 0, while the EMI decreases from 149.00 at ρ = 1/10 to 0.85 at ρ = 10. It is found that the smaller ρ value is helpful to obtain larger electric field inside the nanoparticle. The larger ρ value of the middle SA layer can induce the larger near-field outside the nanoparticle for the ω −− mode and the smaller ρ value makes larger near-field for the ω +− mode.
Conclusion
We have investigated the plasmon resonance properties of the Au/SA/Au nanoshells. The extinction spectra and the electric field enhancement of the Au/SA/Au nanoshells have been calculated based on a modified Mie scattering theory. We focus on the influence of the spherical anisotropy of the middle layer on the plasmon resonance couplings in the Au/SA/Au nanoshells. It is found that the permittivity along the radial direction plays a dominant role on the plasmon couplings in Au/SA/Au nanoshells, and the permittivity along the tangential direction leads to significant modulations. With the increase of ρ, both the dipole peaks of the ω −− and ω +− modes show blue-shifts. The variation of the ω −− mode is stronger than the ω +− mode. The large ρ value of the middle SA layer can induce the large near-field outside the nanoparticle for the ω −− mode and the small ρ value can induce the large near-field for the ω +− mode. Such enhanced near-field can be used to the enhanced Raman excitation and emission. Furthermore, the small ρ value is helpful to obtain larger electric field inside the nanoparticle, which may be helpful for their potential applications in nonlinear optics.
References
Hao F, Sonnefraud Y, Dorpe PV, Maier SA, Halas NJ, Nordlander P (2008) Symmetry breaking in plasmonic nanocavities: subradiant LSPR sensing and a tunable Fano resonance. Nano Lett 8:3983–3988
Kodali AK, Schulmerich MV, Palekar R, Llora X, Bhargava R (2010) Optimized nanospherical layered alternating metal-dielectric probes for optical sensing. Opt Express 18:23302–23313
Ruan ZC, Fan SH (2010) Superscattering of light from subwavelength nanostructures. Phys Rev Lett 105:013901
Ruan ZC, Fan SH (2011) Design of subwavelength superscattering nanospheres. Appl Phys Lett 98:043101
Bardhan R, Mukherjee S, Mirin NA, Levit SD, Nordlander P, Halas NJ (2010) Nanosphere-in-a-nanoshell: a simple nanomatryushka. J Phys Chem C 114:7378–7383
Xia XH, Liu Y, Backman V, Ameer GA (2006) Engineering sub-100 nm multi-layer nanoshells. Nanotechnology 17:5435–5440
Hu Y, Fleming RC, Drezek RA (2008) Optical properties of gold-silica-gold multilayer nanoshells. Opt Express 16:19579–19591
Wu DJ, Jiang SM, Liu XJ (2011) Tunable Fano resonances in three-layered bimetallic Au and Ag nanoshell. J Phys Chem C 115:23797–23801
Mukherjee S, Sobhani H, Lassiter JB, Bardhan R, Nordlander P, Halas NJ (2010) Fanoshells: nanoparticles with built-in Fano resonances. Nano Lett 10:2694–2701
Gao L, Yu XP (2007) Second- and third-harmonic generations for a nondilute suspension of coated particles with radial dielectric anisotropy. Eur Phys J B 55:403–409
Yin YD, Gao L, Qiu CW (2011) Electromagnetic theory of tunable SERS manipulated with spherical anisotropy in coated nanoparticles. J Phys Chem C 115:8893–8899
Wu DJ, Jiang SM, Liu XJ (2012) A tunable Fano resonance in silver nanoshell with a spherically anisotropic core. J Chem Phys 136:034502
Lange B, Aragon SR (1990) Mie scattering from thin anisotropic spherical shells. J Chem Phys 92:4643–4650
Ambjörnsson T, Mukhopadhyay G, Apell SP, Käll M (2006) Resonant coupling between localized plasmons and anisotropic molecular coatings in ellipsoidal metal nanoparticles. Phys Rev B 73:085412
Lucas AA, Henrard L, Lambin P (1994) Computation of the ultraviolet absorption and electron inelastic scattering cross section of multishell fullerenes. Phys Rev B 49:2888–2896
Bohren CF, Huffman DR (1983) Absorption and scattering of light by small particles. Wiley, New York
Luk’yanchuk BS, Qiu CW (2008) Enhanced scattering efficiencies in spherical particles with weakly dissipating anisotropic materials. Appl Phys A 92:773–776
Radloff C, Halas NJ (2004) Plasmonic properties of concentric nanoshells. Nano Lett 4:1323–1327
Prodan E, Lee A, Nordlander P (2002) The effect of a dielectric core and embedding medium on the polarizability of metallic nanoshells. Chem Phys Lett 360:325–332
Prodan E, Radloof C, Halas NJ, Nordlander P (2003) A hybridization model for the plasmon response of complex nanostructures. Science 302:419–422
Prodan E, Nordlander P (2004) Plasmon hybridization in spherical nanoparticles. J Chem Phys 120:5444–5454
Kelly KL, Coronado E, Zhao LL, Schatz GC (2003) The optical properties of metal nanoparticles: the influence of size, shape, and dielectric environment. J Phys Chem B 107:668–677
Acknowledgments
This work was supported by the National Basic Research Program of China under grant no. 2012CB921504, the National Natural Science Foundation of China (11174113, 10904052, 11274171, 11104319, and 11204129), and project funded by the Priority Academic Program Development of Jiangsu Higher Education Institutions.
Open Access
This article is distributed under the terms of the Creative Commons Attribution License which permits any use, distribution and reproduction in any medium, provided the original author(s) and source are credited.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License (https://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Wu, D., Jiang, S., Cheng, Y. et al. Modulation of anisotropic middle layer on the plasmon couplings in sandwiched gold nanoshells. Gold Bull 45, 197–201 (2012). https://doi.org/10.1007/s13404-012-0068-3
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13404-012-0068-3