Cyclodextrin–PEG conjugate-wrapped magnetic ferrite nanoparticles for enhanced drug loading and release
- 413 Downloads
Magnetic nanoparticles are envisaged to overcome the impediments in the methods of targeted drug delivery and hence cure cancer effectively. We report herein, manganese ferrite nanoparticles, coated with β-cyclodextrin-modified polyethylene glycol as a carrier for the drug, camptothecin. The particles are of the size of ~ 100 nm and they show superparamagnetic behaviour. The saturation magnetization does not get diminished on polymer coverage of the nanoparticles. The β-cyclodextrin–polyethylene glycol conjugates are characterized using NMR and mass spectrometric techniques. By coating the magnetic nanoparticles with the cyclodextrin–tethered polymer, the drug-loading capacity is enhanced and the observed release of the drug is slow and sustained. The cell viability of HEK293 and HCT15 cells is evaluated and the cytotoxicity is enhanced when the drug is loaded in the polymer-coated magnetic nanoparticles. The noncovalent-binding based and enhanced drug loading on the nanoparticles and the sustained release make the nanocarrier a promising agent for carrying the payload to the target.
KeywordsCyclodextrin PEG Camptothecin Manganese ferrite Drug release
Magnetic nanoparticle (MNP)-polymer hybrids are versatile platforms for multiple functions, such as treatment, diagnosis, and monitoring of diseases, including cancer (Lee et al. 2011; Zanganeh et al. 2016; Kim et al. 2013; Baek et al. 2016). Superparamagnetism is a magnetic phenomenon pertaining to MNPs of appropriate size, having a single magnetic domain which behaves as a ‘single super spin’. Such MNPs have a high magnetic susceptibility and hence an application of a magnetic field makes the MNPs respond strong and rapid to the field (Kodama 1999). On removal of the applied magnetic field, the MNPs do not possess residual magnetism at room temperature. Hence, they are not prone to agglomeration, which causes them escape phagocyte uptake and pose no unwarranted blockage of blood capillaries or thrombosis (Wahajuddin 2012). Iron oxide MNPs are the most commonly studied magnetic materials (Quinto et al. 2015) in the biomedical field. Apart from these, other ferrite MNPs have also been investigated (Mody et al. 2014; Choudhari et al. 2015; Hirosawa et al. 2017; Foroughi et al. 2016). Manganese ferrite NPs possess soft magnetic properties, viz., moderate saturation magnetization and low coercivity, besides good mechanical hardness and chemical stability (Carta et al. 2010). Though studied as a notable magnetic resonance imaging (MRI) contrast agent (Wang et al. 2014) and a theranostic (Wang et al. 2016), manganese ferrites do work as drug delivery vehicles (Zhao et al. 2015).
The size, shape, and surface properties of MNPs need to be wisely tuned in order to achieve a suitable drug targeting efficiency. Particles of a size smaller than 10 nm or larger than 200 nm are removed from circulation by renal clearance and spleen or phagocyte uptake (Wahajuddin 2012). An MNP having a size in the range of 10–100 nm is suitable for longer circulation and escaping reticuloendothelial system of the human body. Particles having a hydrophobic surface suffer opsonisation (adsorption on protein surface) and macrophage uptake (Veiseh et al. 2010). On the contrary, surface-engineered nanoparticles having hydrophilic polymers as sheaths can escape reticuloendothelial cells or circulating macrophages (Harris and Chess 2003). As a result, they attain enhanced residence time in the blood. Surface charges on the polymers influence the ability to get directed to the target. For instance, cationic polyethyleneimine (PEI)-coated MNPs interact with deoxyribonucleic acid (DNA) (Steitz et al. 2007) and negatively-charged functional group-containing dextran-coated MNPs couple with peptide oligomers (Hildebrandt et al. 2007). Unlike these electrostatic interactions, affinity interactions through non-covalent binding are less affected by environmental conditions including changes in pH and ionic strength (Wahajuddin 2012).
One of the major limitations of drug delivery by loading drugs on surface-modified MNPs is the low entrapment efficiency of drug molecules. The other disadvantage is the failure in the release of drugs due to attachment of drugs through covalent linkages to the polymer shell (Wahajuddin 2012). The normal modes of drug release from polymers (Langer and Peppas 1981) are (1) surface erosion of the polymer and the diffusion of drug, (2) breaking of polymer bonds, and (3) physical diffusion of the encapsulated drug. At this juncture, the application of the cyclic oligosaccharides, cyclodextrins (CDs), find importance as a drug carrier. Cyclodextrins are doughnut-shaped molecules which can encapsulate a variety of drug molecules of appropriate size to fit into their cavity (Davis and Brewster 2004). CDs are non-toxic and water-soluble and possess a hydrophobic cavity and a hydrophilic exterior (Chandrasekaran et al. 2014; Yousuf et al. 2013). The drug encapsulated by CD is released in a slow and sustained manner (Davis and Brewster 2004).
With the objective to link the remarkable properties of poly(ethylene glycol) and β-cyclodextrin as drug carriers, there have been attempts to functionalize PEG with β-CD (Cesteros et al. 2006; Salmaso et al. 2007, 2004). The CD–PEG hybrid forms hydrogels and has been used in drug delivery (Cesteros et al. 2006). β-CD forms host–guest complex with the cancer drug, camptothecin (CPT) (Kang et al. 2002). On loading CPT in β-CD, the solubility and stability of the drug get enhanced. Moreover, the loading of CPT in β-CD enhances its antitumor potential (Cheng et al. 2004). The above-mentioned points intrigued framing of the present work being centered on (1) synthesis of manganese ferrite nanoparticles in a size range suitable for cancer drug targeting, (2) synthesis of CD–PEG conjugate, and (3) loading of CPT in the CD–PEG-coated MNPs (CD–PEG–MNPs@CPT) and (4) the study of cytotoxicity of the MNP–CD–PEG polymer hybrid.
The AnalaR reagents (p-toluenesulfonic anhydride, p-toluenesulfonic chloride, ethylene diamine, and polyethylene glycol) used for the synthesis of the CD-derivative of polyethylene glycol were products of Aldrich, India. β-CD was supplied by Hi-Media and polyethylene glycol by Fisher Scientific. All the solvents used for the synthesis (in AR grade) and for UV–Visible spectral measurements (in spectral grade) were purchased from Aldrich. The reagents used for the preparation of manganese ferrite MNPs, viz., manganese nitrate, ferric nitrate, ammonium hydroxide, and ethylene diamine were received from Merck, India. The purity of the chemicals was above 98%. The dialysis membranes used for the drug release study were the products of Hi-Media, India (diameter 14.33 mm, LA387–1MT). MTT (3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide) were procured from Amresco. The nuclear staining dye bis-Benzamide H 33342 trihydrochloride (Hoechst 33342) was purchased from Sigma-Aldrich. Cytoplasmic staining dye Rhodamine B was acquired from life technologies. The human embryonic kidney cells 293 (HEK 293) and human colon adenocarcinoma cells (HCT 15) were received from National Centre for Cell Science, Pune, India.
Preparation of manganese ferrite MNPs
Manganese ferrite was prepared using the procedure reported earlier (Mahmoodi 2013). Manganese nitrate (4.90 g, 1 eq.) and Ferric nitrate (13.4 g, 1.5 eq.) was dissolved in 50 mL distilled water and added to the aqueous mixed solution [4.2 g NaOH in 70 mL distilled water and 3 mL ethylenediamine (EDA)]. This solution was heated at 90 °C for 1 h to achieve complete chelation. The powder was calcined on alumina crucible at 500 °C for 1 h, with a heating rate of 10 °C/min.
Synthesis of PEG-bis-(tosylate) (Ts–PEG–Ts)
PEG-bis-(tosylate) was prepared using the procedure reported earlier (Hai et al. 2003). PEG (1.0 mL, 1 eq.) TEA (2.9 mL, 2 eq.) were mixed in 200 mL of dichloromethane and stirred at 40 °C for 30 min. To this mixture, 2 eq. of tosyl chloride (3.8 g) was added to 100 mL of dichloromethane. The solution was constantly stirred using a magnetic stir bar at 40 °C for 5 h. The product obtained was washed with ethyl acetate and dried.
Synthesis of PEG-bis-(amine) (H2N–PEG–NH2)
PEG-bis-amine was prepared using a reported procedure (Hai et al. 2003). PEG-bis-sulfonate (1.0 g, 3 mmol) is dissolved with agitation in 29% aqueous ammonia to a concentration of between about 3 mmol per litre and stirred for 1 h. A dichloromethane is added to the reaction mixture and subsequently removed via phase separation. The solvent is dried and PEG-bis amine has precipitated the addition of diethyl ether.
Synthesis of β-CD–PEG conjugate
Under nitrogen atmosphere, 6-p-toluenesulfonyl-β-cyclodextrin (Ts-CD, 0.5 g, 1 eq.) and PEG-bis-(amine) (1.5 g, 1 eq.) were mixed in 5 mL of DMSO and stirred at 60 °C for 12 h. After cooling it to room temperature the mixture was poured into acetone. The precipitated product was filtered washed with acetone and dried.
CD–PEG coating of MNPs
The calcium ferrite MNPs were coated with the CD–PEG conjugate by adding 10 mg of the former with 10 mg of the latter in a slightly basic (pH 8.0) water medium (by adding 0.1 M sodium hydroxide in drops) and then sonicating to get CD–PEG–MNPs.
A Shimadzu XRD 6000 instrument with a Cu Kα radiation source (λ = 1.5418 Å) was used for measuring X-ray diffraction pattern with the generator operating at 40 kV. A JEOL JSM 6390 instrument was used to record scanning electron microscopic images. Transmission electron microscopic (TEM) images were recorded using a JEOL JSM 2100 instrument and the acceleration voltage applied was 200 kV. Dynamic light scattering (DLS) measurement was done using a Malvern Nano Zs90 Zetasizer. A qualitative estimation of the CD–PEG–MNPs was carried out using a Phi 5000 versa probe II base system X-ray photoelectron spectrometer. FT-IR spectra were recorded on a Shimadzu FT-IR spectrophotometer in the wavenumber range of 450–4000 cm−1. The sample was made as a pellet by crushing with KBr. A Netzsch STA 449 F3 Jupiter thermal analyzer was used to record the thermogravimetric profile of the PVA–CD–MNPs at a heating rate of 10 °C/min. Under N2 flow (50 mL/min). A Pt–Rh wire served as the sensor of the device. Magnetization measurements were carried out using a Lake shore 7410 vibrating sample magnetometer (VSM). 1H NMR spectrum was recorded on a Bruker Avance III spectrometer operating at an operating frequency of 400 MHz. A JOEL GC Mate spectrometer was employed to record the mass spectrum.
In vitro drug release
CD–PEG–MNP@CPT was suspended in dialysis bags which were dipped in PBS buffer solution of pH 7.4 and the other in that of pH 6.0 and shaken using a mechanical shaker at 37 °C. The solutions released outside the bags were withdrawn at regular time intervals and the concentration of the released drug was calculated using UV–Visible spectroscopy. The volume in the dialysis system was maintained constant by adding fresh PBS solutions. Three independent experiments were done and the average values were calculated.
The human embryonic kidney cells 293 (HEK 293) were grown in Dulbecco’s modified eagle’s medium (DMEM) and human colon adenocarcinoma cells (HCT 15) were maintained in Roswell Park Memorial Institute (RPMI) medium augmented with 10% fetal bovine serum (FBS, Gibco Life Technologies) and 1% penicillin–streptomycin (FBS, Gibco Life Technologies) in both the cases and grown in 37 °C incubator with 5% CO2 and 95% air with humidified condition provided.
Cell viability assay
Acridine orange–ethidium bromide (AO–EB) dual staining
The AO–EB dual staining was performed to evaluate the apoptotic induction in cancer cells, which were pre-incubated with camptothecin-loaded nanoformulation (CD–PEG–MNPs@CPT). The growth medium was removed and PBS with 2 µL of AO–EB mixture (10 µg/mL of both were mixed) was used for staining and then incubated at 37 °C for 5–10 min. Then excess dyes were removed by PBS washing of the cells. Later, the stained cells were fixed with 3% paraformaldehyde for 10 min. The image of cellular morphology was then captured by EVOS FL Color, AMEFC 4300 cell imaging system (Life Technologies, USA) under the red fluorescent protein (RFP) filter for EB and green fluorescent protein (GFP) filter for AO as fluorescence images employing transmission mode for bright field images.
Rhodamine B and Hoechst 33342 staining
Combinatorial fluorescent stains (rhodamine B and Hoechst 33342) were used to visualize the intracellular morphological changes in the cytoplasm as well as the nucleus during the course of camptothecin-loaded nanoformulation treatment. Rhodamine B can be used to track the cytoplasmic vesicles and mitochondria effectively by staining the same and visualized under RFP filter. On the contrary, Hoechst 33342 nucleic acid staining dyes exclusively within the nucleus which can be tracked under DAPI filter. After the course of incubation, the cells treated with CD–PEG–MNPs@CPT were given a momentary PBS wash and then stained with 1 µL of rhodamine B (working stock concentration: 1 mg/mL) for 10 min. Then, PBS wash was given to remove the excess rhodamine B. Finally, PBS accompanied with 2 µL of Hoechst 33342 (working concentration: 10 mg/mL) were added. Final washing was done with PBS followed by fixation with 3% paraformaldehyde, and the images were captured by EVOS cell-imaging system under DAPI, GFP and RFP filter. Overlay of images obtained in all three filters dictates the morphology of both the nucleus and the cytoplasm of HCT 15 cells.
Results and discussion
Synthesis and characterization of CD–PEG
Scheme 1 illustrates the steps in the synthesis of CD–PEG. The procedure is discussed in the “Experimental” section. The synthesized CD–PEG polymer was characterized using, IR, NMR, and mass spectral methods. The spectra are shown in the Electronic Supplementary Information ESI 1.
Characterization of magnetic nanoparticles
Figure 1a shows the XRD pattern of manganese ferrite nanoparticles (as-prepared and CD–PEG coated). The crystalline nature of the MNPs is revealed by the sharp peaks. The diffraction peaks originating from (2 2 0), (3 1 1), (2 2 2), (4 0 0), (5 1 1), and (4 4 0) crystal planes suggest that the formed crystals are of spinel structure. The major peak harmonizes with the crystal reflection of MNPs in JCPDS CIF 1528316. The results from ICP–AES measure reveal that the exact composition of the ferrite MNPs is Mn0.98Fe2.03O4. The size of the grains can be calculated analyzing the (3 1 1) diffraction peak, which is the most intense peak, using the Scherrer equation (Cullity and Stock 2014):
The EDX spectrum of the as-prepared MNPs is shown in Fig. 1b. There are peaks observed at various energy (keV) values which correspond to the elements Mn, Fe, and O, indicating qualitatively the presence of these elements in the as-prepared ferrite sample and the absence of any other elements as impurities. However, we recorded XPS spectra for evaluating the CD–PEG–MNPs for a better preciseness of the elemental analysis, which will be discussed later in this section.
Figure 1c displays the TEM image of the CD–PEG–MNPs. The covered layer of the polymer is thin compared to the size of the MNPs. The average size of the MNPs is 93 ± 5 nm. This size is much larger than manganese ferrite NPs reported earlier for the purpose of MRI or other biomedical objective (Lemarchand et al. 2004; Leal et al. 2015; Beeran et al. 2015; Kang et al. 2004; Li et al. 2004; Giri et al. 2012; Mazarío et al. 2016). The hydrodynamic diameter of the CD–PEG–MNPs can be determined by dynamic light scattering (DLS) measurements. In the present case, the average hydrodynamic diameter observed is 95 ± 5 nm as can be seen from the size distribution histogram shown in Fig. 1d.
After coating the MNPs with CD–PEG, the sample was used to record a thermogravimetric profile (Fig. 2). The TGA profile shows a two-step weight loss for the CD–PEG–MNPs.
An initial weight loss of nearly 10% is observed up to the temperature of 180 °C, owing to the loss of moisture, the expulsion of the surface hydrated water from CD–PEG, and any possible volatile components present. The second weight loss occurs at 380 °C, which is due to the decomposition of CD–PEG polymer. The next weight loss appears in between 600 and 800 °C due to the thermal degradation of the polymer. The TGA as carried out under an atmosphere of nitrogen in order to keep the oxidation reaction in the ferrite minimal. Hence, CD–PEG wraps around the MNPs and is considerably stable, without getting detached easily at lower temperatures.
To get additional evidence on the elemental composition and the ionic contribution to the ferrite MNPs, XPS spectra were recorded for the CD–PEG–MNPs. The XPS spectra show the peaks corresponding to the binding energies of electrons in Fe, and Mn, and O (See ESI 2). The spectra confirm the formation of crystalline manganese ferrite without impurity of other oxides. The explanations for each and every peak in the spectra are given in ESI 2.
The room temperature magnetic behaviour of the as-prepared and the CD–PEG–MNPs was studied by recording the magnetization vs applied field plot (Fig. 3). In both cases, the hysteresis loop is absent, i.e., the coercivity is almost zero. The saturation magnetization of the as-prepared MNPs is 38 emu g−1, typical of the soft magnetic manganese ferrite MNPs. Coating of CD–PEG results in the saturation magnetization decreasing by 5 emu g−1, which is due to the non-magnetic characterization of the coating polymer. The small decrease is due to just a thin shell of polymer covering up the MNPs core. The magnetization value of the MNPs is larger than that reported for MnFe2O4 by some authors (Pal et al. 2014; Naseri et al. 2011; Fahmi et al. 2015) but close to some other reports for the same nanomaterial (Vestal and Zhang 2003; Aslibeiki et al. 2016). The difference arises due to the size variations between the reported magnetic nanoparticles. The absence of hysteresis loop suggests a room temperature superparamagnetic behaviour and the size of the approximately 99 nm MNPs are within the superparamagnetic limit.
Drug loading and release
We calculated the percentage of drug loading on the CD–PEG–MNPs@CPT using Eq. (1). A pre-calculated amount of CD–PEG–MNPs@CPT was dispersed in 10 mL of water. The concentration of CPT was calculated by UV–Vis absorption (385 nm). Comparatively, the percentage of loading and efficiency of adsorption on unmodified PEG-coated MNPs (PEG–MNPs) were determined to employ the above equation, in order to comprehend the role of β-CD conjugation in drug encapsulation. The percentages of the loaded drug on CD–PEG–MNPs@CPT and PEG–MNPs are 86 and 60%, respectively.
Obliviously, the loading drug content in β-CD modified PEG is more compared to the unmodified PEG. The CPT molecule enters the space between the folded strands of PEG and resides inside the polymer shell. Moreover, it is plausible that the hydroxyl group forms hydrogen bonds with the –OH group of PEG. The weak association allows the release of drug from the polymer shell of MNPs. An enhanced loading content in the CD–PEG–MNPs@CPT suggests that the β-CD encapsulates the CPT molecule through host–guest association. Due to the larger room for accommodating the drug molecule, the enhanced loading occurs. This inference is future supported by the fact that native β-CD form host–guest complex with CPT (Kang et al. 2002). It is noteworthy that the adsorption efficiency of both the PEG–MNPs and CD–PEG–MNPs are generally large and suitable for transport of the drug cargo.
The in vitro release of CPT was studied following the procedure reported by Zhu et al. (2009). Suspensions of CD–PEG–MNPs@CPT were taken in dialysis membranes having a cut-off for molecular weight range of 12,000–14,000 Da. The membranes placed in PBS solution in two different pHs, viz., 6.0 and 7.4 were put in a shaker bath. The release of the drug was studied at two different temperatures, viz., 35 and 40 °C. UV–Vis absorption measurements were made at regular and planned intervals of time. The in vitro release profiles of CD–PEG–MNPs@CPT are shown in Fig. 4. The release profile shows that nearly 30% of the drug is released at pH 7.4 in 200 min (Fig. 4a). Further, the release rate is slow and sustained and comes up to a plateau at 800 min. Evan at this time, the released amount of drug is 54.5% and the release further continues steadily. A decrease in pH accelerates the drug release from 54.5% at pH 7.4 to 69.4% at pH 6.0. The two mentioned pH’s are chosen for the experiments since 7.4 is the normal physiological and the pH is decreased in the tumour microenvironment due to acidic metabolites caused by anaerobic glycolysis in hypoxia (Feng et al. 2018). The larger size of nanoparticles (> 100 nm) results in a slower release of loaded drugs (Zhu et al. 2009). In the present case, even though the size is smaller, the drug release is slow and sustained, which is attributed to the greater drug-carrying ability of the polymer shell.
The increase of temperature (to 40 °C) results in a quicker release of CPT (Fig. 4b), i.e., 40% of the drug in nearly 200 min. In this temperature, for the sample at pH 6.0, the release rate further gets enhanced. An elevation in temperature, hence leads to a better release of the encapsulated drug, leading to the hyperthermia based tuning of drug release from the transporting vehicle i.e., MNPs.
Cell viability assay
The cytotoxic effects of CD–PEG–MNPs and CD–PEG–MNPs@CPT were screened on HCT-15 and HEK293 quantitatively by MTT assay as shown in the Fig. 5a, b, respectively.
In the comparative analysis, the cytotoxicity was found to be increased when the drug was loaded in the CD–PEG–MNPs in both normal and cancer cell lines. These data reveal that the anti-neoplastic potential of camptothecin can be successfully utilized in MNPs for drug delivery applications.
This assay later provided the knowledge of IC50 values for different nanoformulations. From the results, CD–PEG–MNPs are found to have an IC50 value of 32.7 and 7.21 μg/mL for HCT-15 and HEK293 cells individually. The cytotoxicity found in HEK 293 cell is comparatively higher than in HCT-15 cells in the material toxicity concern. The multi-drug resistant nature of colon cancer cells (HCT-15) might be the reason behind the discrimination in toxicity. The involvement of multiple, molecular mechanisms to escape the drug burden (Uchiyama-Kokubu and Watanabe 2001) was found in the cancer regime, whereas the non-cancerous cell types do not possess such a mechanism and are more sensitive to the stress caused by therapeutic dosage. To substantiate the carrier toxicity and establish a potential drug delivery system, we compared the bare CD–PEG–MNPs and CD–PEG–MNPs@CPT on HCT-15 cell line. As expected, the bare CD–PEG–MNPs displayed a lower toxicity whereas CD–PEG–MNPs@CPT resulted with an IC50 value of 19.3 µg/mL. The manganese toxicity (Hernández et al. 2011) may be influenced by the cytotoxicity of bare CD–PEG–MNPs irrespective of cell type discrimination as in normal and cancer cell lines.
The cytotoxicity of drug-loaded MNPs was further evaluated in order to know cytotoxic-determining factors in the nanoformulation. The synergistic effect of drug alone (camptothecin) and MNPs was compared with respect to the drug-loaded metal nanocomposite (CD–PEG–MNPs@CPT). It was closely evidenced with a synergistic cytotoxic effect by the CD–PEG–MNPs@CPT. The data point of CD–PEG–MNPs@CPT in isobologram analysis was found to be way below additive lines in both the cell lines. The combined effect of MNPs and drug attributed to the strong synergistic in toxicity concerns (Fig. 5b, d). The augmented potential drug delivery strategy of the metal nanocomposite was explored in the assay and leads the study into appreciable efficacy.
Acridine orange–ethidium bromide (AO–EB) staining
To critically evaluate the mechanism of cell death by CD–PEG–MNPs@CPT, a combinatorial staining procedure was followed in HCT-15 cell line and observed under the fluorescence microscope. Viable healthy cells can eliminate EB stain. So nucleus of such cells appears in green because of AO fluorescence alone (Fig. 6a). The cells underwent treatment with the IC50 concentration of CD–PEG–MNPs@CPT showed significant morphometric changes of the cell and owing apoptotic cells (Matai et al. 2015) (Fig. 6b).
Rhodamine B and Hoechst 33342 staining
Rhodamine B and Hoechst 33342 can be effectively used to stain the cytoplasm as well as the nucleus to detect the morphological changes after the incubation of CD–PEG–MNPs@CPT nanoformulations. Consecutive cascade events of apoptosis were assessed in HCT-15 incubated with CD–PEG–MNPs@CPT nanoformulations. The drastic reduction in the rhodamine B fluorescence in the cytoplasm’s of the CD–PEG–MNPs@CPT (Fig. 7b) treated cells clearly suggested cytoplasmic constrictions, further in the same order while compared with untreated controls (Fig. 7a). Moreover, non-uniform spotted blue stains of Hoechst 33342 in nucleus provided the clue for nuclear fragmentation in treated cells (Fig. 7b), which stains the nucleus uniformly in untreated control (Fig. 7a) (Kumar and Gopinath 2015). The methods involved in the work are summarized in Scheme 2.
In this work, a new combination Mn0.98Fe2.02O4–β-cyclodextrin–PEG conjugate hybrid is developed. The size of the MNPs is ~ 90 nm, which is suitable for magnetic drug targeting as the nanomaterial, with this size, can escape renal clearance and uptake by the reticuloendothelial system. The CD–PEG-coated MNPs are superparamagnetic which is suitable for rapid magnetization on the application of external magnetic field and demagnetization when it is lifted. The percentage of loading of camptothecin gets enhanced from 60% in MNPs coated with unmodified PEG to 86% in CD–PEG-coated ones. The release of the drug from CD–PEG–MNPs is slow and sustained up to 800 min. A decrease of pH from 7.4 to 6.0 and an increase of temperature both lead to the faster release of the drug, which enables stimuli-responsive release from the nanocarrier. The cytotoxicity of the bare CD–PEG–MNPs in HEK 293 and HCT 15 cell lines is lesser than that of the camptothecin-loaded ones. With the PEG aiding a possible escape from macrophage uptake, β-CD facilitating enhanced drug loading and sustained release, and the ferrite MNPs enabling magnetic field-directed targeting, the CD–PEG wrapped MNPs will be a promising drug carrier for sharpshooting cancer cells.
IVMVE thanks the management of Karunya University for the assistance in setting up a new Nanotoxicology lab.
- Cullity BD, Stock SR (2014) Elements of X–ray diffraction. Addison–Wesley, New YorkGoogle Scholar
- Hai T, Markoski L, Pereira D, Nordhaus M (2003) US 2003/0149307 A1Google Scholar
- Hildebrandt N, Hermsdorf D, Signorell R, Schmidtz SA, Diederichsena U (2007) Superparamagnetic iron oxide nanoparticles functionalized with peptides by electrostatic interactions. ARKIVOC 79:90Google Scholar
- Hirosawa F, Iwasaki T, Watano S (2017) Synthesis and magnetic induction heating properties of Gd-substituted Mg–Zn ferrite nanoparticles. 7:209–214Google Scholar
- Zanganeh S, Hutter G, Spitler R, Lenkov O, Mahmoudi M, Shaw A, Pajarien JS, Nejadnik H, Goodman S, Moseley M, Coussens LM, Daldrup-Link HE (2016) Iron oxide nanoparticles inhibit tumour growth by inducing pro-inflammatory macrophage polarization in tumour tissues. Nat Nanotechnol 11:986–994CrossRefGoogle Scholar