Abstract
A series of SAPO-11 molecular sieves with hierarchical structure (Meso-SAPO-11) were synthesized by adding certain amount of carbon particles. The co-existing micropore and mesopore feature of Meso-SAPO-11 was confirmed by N2 adsorption–desorption isotherm, TEM and SEM. XRD, TEM, SEM and Py-FTIR were employed to examine the crystallization, morphology and acidity properties of the resulting meso-SAPO-11 prepared from two typical kinds of carbon material and different contents of template. The hydroisomerization performance of meso-SAPO-11 as catalyst support and acid active site, with loading 0.5 wt% Pt as metal active site, was also tested to evaluate the mesoporous effects on catalytic activity and product selectivity.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
With the environmental regulations becoming more stringent and people’s environmental awareness getting stronger, the demand for clean production of gasoline, diesel and lubricants and other products from crude oil is increasing. However, because of that crude oil is becoming heavier and poorer in quality, the deep upgrading and full utility of heavy oil attract extensive attention and also become more of a disposal challenge. Hydroisomerization, as a technology to produce higher quality petroleum products, is getting more and more attentions. In the production of gasoline, the octane number of the product can be improved by hydroisomerization. In the production of diesel and lubricants, the pour point and viscosity nature of the product can be ameliorated by hydroisomerization, while maintaining the efficiency of carbon conversion and yield target oil product for maximum [1]. The hydroisomerization catalyst is a kind of bifunctional catalyst, which includes both a metal and an acid active site. The acid function is usually provided by acidic support, such as amorphous oxide or oxide mixture (Al2O3, SiO2–Al2O3, ZrO2/SO42− treated by HF) [2, 3], aluminosilicate molecular sieves (Y, Beta, Mordenite, ZSM-5, ZSM-22) [4–6], or silicoaluminophosphate molecular sieves (SAPO-11, SAPO-31, SAPO-41) [7–10].
SAPO-11 molecular sieve, which has one-dimensional 10-ring pore structure and suitable surface acidity, has been widely used in refinery process because of the good stability and selectivity in alkane isomerization [11–15]. However, the application of traditional SAPO-11 is restricted by its microporous structure, especially for the long-chain alkane isomerization process. The reactant conversion and isomer product selectivity are significantly reduced by low mass transfer rate. As we know, hierarchical porosity by generating mesopores inside microporous molecular sieve is a feasible approach to reduce the mass transfer resistance of the reactants and construct more reactive sites inside microporous molecular sieve, furthermore to improve the reactivity [16]. Therefore, SAPO-11 with hierarchical structure (meso-SAPO-11) has been attracted more and more attention [17, 18].
Template method is commonly used to generate mesopores inside crystallized molecular sieve [19, 20]. The template commonly used to construct hierarchical structure is organic macromolecular surfactant, i.e. soft template strategy. However, specially designed organic macro molecular surfactant used to act as soft template is usually expensive, which restricts to be used in large scale, especially for industrial application. The account relative to soft template is hard template strategy, which uses a structural rigid organic or inorganic material as template. Normally, carbon material is a best choice as hard template for aluminosilicate or silicoaluminophosphate synthesis, which could be removed by simple thermal treatment in the presence of oxygen or air. As an example, hard template strategy has been applied to produce hierarchical structured zeolite, such as macroporous MFI zeolite crystals by applying polystyrene beads [21] as the macropore template or nanosized ZSM-5 crystals by carrying out the crystallization in the confined space of amorphous carbon black [22]. However, little research has been reported to construct hierarchical structure in SAPO-11 molecular sieve using hard template [23]. Herein, an approach to synthesize SAPO-11 molecular sieve with hierarchical structure (Meso-SAPO-11) using carbon nanoparticles as hard template is demonstrated. The effects of carbon template on the mesoporosity, crystallization, morphology and acidity properties of the resulting molecular sieve are examined with N2 adsorption/desorption isotherm, XRD, TEM, SEM and Py-FTIR. The catalytic performance of the as-synthesized Meso-SAPO-11 on n-dodecane hydroisomerization are investigated to evaluate the mesoporous effects on catalytic activity and products selectivity.
Experimental
Synthesis of hierarchical SAPO-11 and catalyst
Based on the preparation method of traditional SAPO-11, aluminum isopropoxide, phosphoric acid and acidic silica sol were chosen as aluminum source, silicon source and phosphorus source, respectively. In a typical synthesis of hierarchical SAPO-11, the precursors were dispersed into proper amount of distilled water in a certain order under vigorously stirring. The mixture of di-n-propylamine and di-iso-propylamine was then slowly added into the solution as microporous template (SDA). The pH value of the resultant gel was adjusted to 6.86 by sulfuric acid after sufficient stirring. Carbon nanoparticles, which act as hard template, were added under vigorous stirring. The gel was then transferred into a stainless steel autoclave lined with polytetrafluorethylene, and crystallized at 473 K for 24 h. Finally, the products were washed, dried at 373 K for 12 h and calcined at 873 K for another 12 h to remove the template.
Carbon material templates used in the experiment are commonly used in industry, for instance, carbon black (Degussa Company, FW200, denoted as FW200), conductive carbon black (Carbot Company, XC72R, denoted as Carbot), carbon nanotubes (denoted as CNTS) and graphitic carbon (denoted as Graphite).
Bifunctional Pt/meso-SAPO-11 catalyst was prepared by incipient-wetness impregnation method. Chloroplatinic acid solution, as a source of platinum, was prepared according to 0.5 wt% Pt loading amount. Then, chloroplatinic acid solution was added into the pretableted meso-SAPO-11 in 20–40 mesh. The as-prepared meso-SAPO-11 with Pt precursor was deposited for 2 h. Finally, the products were dried at 373 K for 2 h and calcined at 753 K for another 4 h to transform into the final bifunctional Pt/meso-SAPO-11 catalyst.
Characterization methods
The crystallinity of the prepared SAPO-11 were analyzed by XRD, which was carried out on X’Pert PRO MPD (Netherlands, Cu target, Kα radiation λ = 0.1542 nm, 35 kV, 40 mA), using molecular sieve phase analysis method, scan angle of 5°–45°. The pore structure and morphology of molecular sieves were characterized by TEM, which was carried out on JEOL-2010 with acceleration voltage of 200 kV. The particle morphology and particle size of the samples were observed by SEM, which was carried out on S-4800 (Hitachi Company, acceleration voltage of 0.5–20 kV). N2 adsorption/desorption isotherms were recorded at 77 K with a Micromeritics TriStar 3000. The total surface area of the samples was calculated by BET method, the mesopore surface area and pore volume were calculated by BJH method based on the N2 desorption branch, and specific surface area of micropores was determined by substraction of total specific surface area from mesoporous one. The surface acidity analyses were carried out on a NEXUS FTIR (Thermo Fisher Scientific Company).
Catalytic evaluation
N-dodecane hydroisomerization was conducted in a continuously flowing tubular fixed-bed micro-reactor at ambient pressure with 1.2 g catalyst loading. The catalyst was activated in situ in an H2 flow at 673 K for 4 h prior to reaction. The reaction temperature was 603 K at the WHSV feeding condition of 1.5 h−1 with H2/n-dodecane molar ratio of 25. Products were analyzed on-line by a Agilent 7820A GC (HP-PONA capillary column size of 50 m × 0.2 mm, FID detector). The reaction conversion, selectivity and yield were calculated by the program of GC.
Results and discussion
Short survey on carbon template
Based on the typical preparation method of traditional SAPO-11, hierarchical SAPO-11 molecular sieves were synthesized using different kinds of commercially provided carbon materials as hard template. The amount of carbon templates was determined by 5 wt% weight ratios of those to theoretical yield of SAPO-11. N2 adsorption/desorption isotherms of the meso-SAPO-11s prepared with four kinds of carbon materials were measured to examine the morphology effects of carbon templates, which are presented as Fig. 1. The calculation results based on measurement are listed in Table 1.
According to N2 adsorption/desorption isotherms of meso-SAPO-11, all the meso-SAPO-11 samples present type-IV isotherm and H3 hysteresis loop according to the IUPAC classification, which indicate that samples have the characteristics of both microporosity and mesoporosity. According to the pore size distribution of meso-SAPO-11 by different carbon templates, all the samples possess abundant of mesopores concentrated at 10–30 nm. The pore size at 3.8 nm is artifact because of the Tensile Strength Effect for a forced closure of the H3 hysteresis loop [24] The hierarchical structure of as-synthesized SAPO-11 is more remarkable when taking Carbot as hard template. N2 adsorption/desorption isotherm of the sample rises most significantly at high relative pressure P/P0, and the jump segment of its hysteresis loop is the steepest. Correspondingly, the result of Table 1 shows that both the mesoporous specific surface area and pore volume of the meso-SAPO-11 templated by Carbot are relatively the largest, indicating a large content of mesopore.
XRD patterns of traditional SAPO-11 and meso-SAPO-11 templated by Carbot and FW200 are presented in Fig. 2. From the patterns, characteristic peaks at 2θ = 8.09, 9.84, 12.78, 16.10, 19.98, 21.93, 22.26, 22.49, 23.48, attributing to the typical SAPO-11 phase with AEL structures [25], could be detected. Moreover, the position and intensity of the peaks are identical to those reported for SAPO-11 without any additional diffraction peaks, indicating no significant effect of the carbon template on SAPO-11 hydrothermal crystallization.
Effects of template content
XRD patterns of meso-SAPO-11 templated by different contents of FW200 and Carbot are presented as Fig. 3. The number after abbreviation indicates the weight ratio of carbon template to theoretical yield of SAPO-11. All of the samples are highly crystallized and show well-resolved characteristic peaks for AEL structure, which indicate that the crystal structure can be properly preserved with the addition of carbon nanoparticles along the crystallization process, especially for the samples with content of 10 wt% FW200 and 15 % Carbot.
The N2 sorption isotherms and pore size distribution of meso-SAPO-11 by different contents of FW200 and Carbot templates are presented in Figs. 4 and 5, respectively. As we can see from Figs. 4a and 5a, type IV adsorption/desorption isotherms and H3 hysteresis loop for typical hierarchical structure of material are observed for all the samples. High initial uptakes at low relative pressure are followed by nearly horizontal adsorption and desorption branches. The upward turn with a hysteresis loop is indicative of the mesoporosity, which is obviously generated form the carbon template introduction. The N2 adsorption/desorption isotherms of meso-SAPO-11 templated by Carbot rising more significantly at high relative pressure P/P0, and the jump segment of its hysteresis loop being steeper. According to the pore size distribution of meso-SAPO-11 in Figs. 4b and 5b, the meso-SAPO-11 by FW200 template possesses a concentrated distribution in about 12 nm, while the meso-SAPO-11 by Carbot template possesses a concentrated distribution in about 25 nm, which is in line with the parent template diameter (12 nm for Degussa FW200 and 25 nm for Carbot XC72R).
The results of N2 adsorption/desorption isotherms of meso-SAPO-11 by different contents of FW200 and Carbot templates are listed in Tables 2 and 3. According to the results, the mesoporous specific surface area and pore volume increase with the increase of the amount of the carbon templates, which indicate that more carbon templates introduction could construct more mesopores. However, the samples prepared with excessive FW200 show a poorer nature of mesoporosity. When further increasing carbon content from 10 to 15 wt%, both the specific surface area and mesopore volume decrease. An optimal amount for FW200 as hard template is obtained, which is said to be 10 % in weight. This result could be explained that excessive carbon template constructs excessive multi-mesopores and possess poor thermal stability, leading to mesopore collapse during thermal treatment. The comprehensive consideration of the surface area and pore structure results indicate that the meso-SAPO-11 templated by 10 wt% FW200 and 15 wt% Carbot show a relatively better mesopore structure.
In situ Py-FTIR spectroscopy of meso-SAPO-11 templated by FW-200 and Carbot is presented in Fig. 6. From the figures, all the spectra of pyridine adsorbed on meso-SAPO-11 exhibit characteristic bands at 1,548 and 1,448 cm−1, which are attributed to Brønsted acid sites (B acid) and Lewis acid sites (L acid), respectively. For both two groups of samples, the amount of B acid increases with the increase of the content of the carbon templates, while the amount of L acid decreases. Meso-SAPO-11 s prepared from template contents of 10 %wt FW200 and 15 %wt Carbot possess the highest proportion of B acid and L acid.
SEM and TEM images of traditional and hierachical SAPO-11 by the two kinds of carbon templates are shown in Fig. 7, and the original carbon templates are shown as insert images as well. According to the images, it can be seen that the surface of traditional SAPO-11 crystals is relatively complete and plane with no mesostructure presented, while the surface of the meso-SAPO-11 crystals is chipped and rough, especially for the meso-SAPO-11 templated by Carbot. The diameter of the mesopore is approximately 10–20 nm as indicated in white cycle of the images, which is in accordance with the results shown in the Figs. 4 and 5. The images of original carbon templates are also presented as insert images, which showed a worm shape. It could be found that the morphologies of carbon templates are different to the resulting meso-SAPO-11, and the role of carbon black as template during the crystallization needs further investigation.
Catalytic evaluation of meso-SAPO-11
The n-dodecane hydroisomerization evaluation of the catalysts prepared by loading 0.5 wt% Pt on above-mentioned meso-SAPO-11 samples are showed in Tables 4 and 5. From the results of Table 4, the cracking selectivity decreases at first and then increases with the increase of FW200 content, while the isomer yield increases at first and then decreases with the multibranched selectivity. The isomer yield and the multibranched selectivity reach the highest value by the content of 10 wt% FW200, while the cracking selectivity decreases to the least. It could be explained from the results that more mesopores are constructed with the increase of the content of FW200 in a certain range. However, the samples with excessive FW200 carbon templates show a poorer nature of mesopore, which indicates excessive carbon templates construct excessive multi-mesopores with poor thermal stability, leading to the collapse of the mesopores, even to block the original micropores. According to the results of Table 5, the conversion and cracking selectivity decrease while the isomer selectivity and isomer yield increase with the increase of Carbot templates content. It also can be seen that the catalytic performances of meso-SAPO-11 prepared higher than 5 wt% are better than traditional SAPO-11 as support. The results could be explained by the decrease of the crystallinity of the molecular sieves. The multibranched selectivity increases with the increase of the content of the Carbot templates, indicating that more multibranched isomerization reaction occurred in the mesopores due to the low restriction to micropores and more exposition of microporous mouth.
Conclusion
The SAPO-11 with hierarchical structure (Meso-SAPO-11) was successfully prepared with the aid of carbon materials as hard template. Compared with the traditional SAPO-11, both the mesoporous specific surface area and volume of meso-SAPO-11 were increased significantly, while the crystal structure was properly preserved. After brief survey on different kinds of carbon materials, it was found that both FW200 and Carbot nanoparticles could be used to generate hierarchical structure effectively, by which 10 wt% FW200 and 15 wt% Carbot showed the best nature of mesoporosity. The increase of mesoporosity could significantly improve the hydroisomerization performance. Correspondingly, the meso-SAPO-11 by 10 wt% FW200 and 15 wt% Carbot showed the best performance on n-dodecane isomer product yield.
References
Kobayashi M, Saitoh M, Togawa S, Ishida K (2008) Branching structure of diesel and lubricant base oils prepared by isomerization/hydrocracking of fischer−tropsch waxes and α-olefins. Energy Fuels 23:513–518
Lin L (1964) Isomerization of n-alkanes. In Research Report Bulletin of Institute of Chemical Physics, Chinese Academy of Sciences. Beijing Science & Technology Press
Calemma V, Peratello S, Perego C (2000) Hydroisomerization and hydrocracking of long-chain n-alkanes on Pt/amorphous SiO2–Al2O3 catalysts. Appl Catal A 190:207–218
Blomsma E, Martens JA, Jacobs PA (1997) Hydroisomerization and hydrocracking of heptane over bimetallic bifunctional Pt-Pd/H-Beta and Pt-Pd/USY zeolite catalysts. J Catal 165:241–248
Martens JA, Parton R, Uytterhoeven L, Jacobs PA (1991) Selective conversion of decane into branched isomers : a comparison of platinum/ZSM-22, platium/ZSM-5 and platium/USY zeolite catalysts. Appl Catal A 76:95–116
Souverijns W, Martens JA, Froment GF, Jacobs PA (1998) Hydrocracking of isoheptadecanes on Pt/H-ZSM-22: a example of pore-mouth catalysis. J Catal 174:177–184
Miller SJ (1992) Wax isomerization using catalyst of specific pore geometry. US. Patent. 5135638, Chevron Res & Tech 1992-08-04
Meriaudeau P, Tuan VA, Lefebvre F, Nghiem VT, Naccache C (1998) Synthesis and characterization of SAPO-41:effect of silicon content and the crystal size on the hydroisomerization of n-octane over Pt-Pd/SAPO-41. Microporous Mesoporous Mater 26:161–173
Sinha AK, Sivasanker S, Ratnasamy P (1998) Hydroisomerization of n-alkanes over Pt/SAPO-11 and SAPO-31 synthesized from aqueous and nonaqueous media. Ind Eng Chem Res 37:2208–2214
Mériaudeau P, Tuan VuA, Nghiem VuT, Sapaly G, Naccache C (1999) Comparative evaluation of the catalytic properties of SAPO-11 and ZSM-48 for hydroisomerization of octane: effect of the acidity. J Catal 185:435–444
Taylor RJ, Petty RH (1994) Selective hydroisomerization of long chain normal paraffins. Appl Catal A 119:121–138
Park KC, Ihm SK (2000) Comparison of Pt/zeolite catalysts for n-hexadecane hydroisomerization. Appl Catal A 203:201–209
Girgis MJ, Tsao YP (1996) Impact of catalyst metal-acid balance in n-hexadecane hydroisomerization and hydrocracking. Ind Eng Chem Res 35:386–396
Corma A, Palomares A, Mrquez F (1997) Determining the nature of the active sites of Cu-beta zeolites for the selective catalytic reduction (SCR) of NOx by using a coupled reaction-XAES/XPS study. J Catal 170:132–139
Miller SJ (1994) New molecular sieve process for lube dewaxing by wax isomerization. Microporous Mater 2:439–449
Lopez-Orozco S, Inayat A, Schwab A, Selvam T, Schwieger W (2011) Zeolitic materials with hierarchical porous structures. Adv Mater 23:2602–2615
Yang X, Lu T, Chen C, Zhou LP, Wang F, Su YL, Xu J (2011) Synthesis of hierarchical AlPO-n molecular sieves templated by saccharides. Microporous Mesoporous Mater 144:176–182
Fan Y, Xiao H, Shi G, Liu H, Bao XJ (2012) Alkylphosphonic acid- and small amine-templated synthesis of hierarchical silicoaluminophosphate molecular sieves with high isomerization selectivity to di-branched paraffins. J Catal 285:251–259
Egeblad K, Christensen CH, Kustova M, Christensen CH (2007) Templating mesoporous zeolites. Chem Mater 20:946–960
Yang XY, Li Y, Lemaire A, Yu JG, Su BL (2009) Hierarchically structured functional materials: synthesis strategies for multimodal porous networks. Pure Appl Chem 81:2265–2307
Holland BT, Abrams L, Stein A (1999) Dual templating of macroporous silicates with zeolitic microporous frameworks. J Am Chem Soc 121:4308–4309
Madsen C, Jacobsen CJH (1999) Nanosized zeolite crystals—convenient control of crystal size distribution by confined space synthesis. Chem Commun 673–674
Liang J, Wang FP (2011) Synthesis and characterization of mesoporous SAPO-11 by using carbon particles. Adv Mater Res 306:1576–1579
Groen JC, Peffer LAA, Pérez Ramírez J (2003) Pore size determination in modified micro- and mesoporous materials. Pitfalls and limitations in gas adsorption data analysis. Microporous Mesoporous Mater 60:1–17
Wilson ST, Lok BM, Messina CA, Cannan TR, Flanigen EM (1982) Aluminophosphate molecular sieves: a new class of microporous crystalline inorganic solids. J Am Chem Soc 104:1146–1147
Acknowledgments
This work was supported by Science and Technology Development Project of CNPC (No. 11-13-01-05); National Science Foundation China (U1362202 and 21206196), Innovation Foundation of CNPC (2013D-5006-0404), and Funds for Distinguished Young Scientists of Shandong Province (BS2012NJ013).
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution License which permits any use, distribution, and reproduction in any medium, provided the original author(s) and the source are credited.
About this article
Cite this article
Ma, Z., Liu, Z., Song, H. et al. Synthesis of hierarchical SAPO-11 for hydroisomerization reaction in refinery processes. Appl Petrochem Res 4, 351–358 (2014). https://doi.org/10.1007/s13203-014-0071-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13203-014-0071-0