Abstract
Poly(methyl methacrylate)-grafted montmorillonite (PMMAgMMT) clay and sodium-exchanged montmorillonite (NaMMT) clay were prepared through in situ graft polymerisation and used to remove Cd2+ and Pb2+ from synthetic wastewater. The modification of adsorbent materials was confirmed by fourier transform infra-red spectroscopy (FTIR), thermogravimetric analysis (TGA) and X-ray powder diffraction (XRD) techniques. BET surface area measurements showed NaMMT had a higher surface area than PMMAgMMT. Batch experiments were used to assess the simultaneous uptake of Cd2+ and Pb2+ from a synthetic binary solution. Pb2+ was preferentially sorbed, exhibiting greater affinity for the sorbents compared to Cd2+ as shown by its relatively higher uptake onto the sorbents than Cd2+. The maximum sorption capacities for NaMMT and PMMAgMMT were 18.73 and 19.27 mg/g for Cd2+, and 30.03 and 34.25 mg/g for Pb2+, respectively. The sorption data obeyed the Langmuir model and the pseudo-second order kinetic model with R 2 of at least 0.9800 for both models. The sorbents could also be regenerated up to three cycles without a significant loss in the sorption capacity. FTIR measurements showed the presence of metal–oxygen bonds after sorption, confirming the occurrence of adsorption as one of the heavy metal removal processes. The work demonstrated the potential of using low-cost nanoscale composite material for the removal of Cd2+ and Pb2+ from aqueous solution.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
The supply of clean water to communities is of paramount importance, and is a challenge, especially in developing countries. Heavy metals such as cadmium and lead are some of the most toxic inorganic contaminants found in water bodies (Jin et al. 2004; Tran et al. 2015). Exposure to these metals has been associated with many health effects including renal damage (Jarup et al. 2000; Nawrot et al. 2010), osteoporosis and bone defects (Alfven et al. 2002; Kazantzis 2004). These two heavy metals are released into the aquatic systems from a number of industrial processes such as metal plating, smelting, mining, cadmium–nickel and lead batteries, phosphate fertilizers, paint industries, leather tanning, pigments, textiles and alloy industries as well as from sewage (Kobya et al. 2005; Teemu 2007).
Many conventional methods for the removal of heavy metals from contaminated water such as precipitation, flocculation, solvent extraction, ion exchange, reverse osmosis and membrane filtration are limited by poor removal efficiencies and high cost (Pavasant et al. 2006; Arief et al. 2008). Sorption onto a solid matrix has become one of the preferred methods for the removal of toxic contaminants from water. This method is reported to be effective, economical, versatile and relatively simple (Garg et al. 2004). Nanoclays, especially smectites, have been widely used as adsorbents due to their high specific surface area, high chemical and mechanical stability as well as their ion exchange capabilities (Cao et al. 2009; Zhu et al. 2016a, b). Previous studies have reported enhanced removal capacities by pristine montmorillonite clay or after various treatments, e.g., acid washing, thermal treatment, or surfactant modification for the removal of specific pollutants (Fan et al. 2014; Zhu et al. 2016a, b). The use of poly(methyl methacrylate)-grafted montmorillonite in competitive sorption of heavy metals like Cd2+ and Pb2+ has not been reported elsewhere. The advantages of this sorbent include excellent sorption properties, ease of availability of montmorillonite, environmental friendliness, and its associated low cost (Qin et al. 2015; Tran et al. 2015; Xing et al. 2015; Zhu et al. 2016a, b). Generally, wastewater contains a variety of pollutants and the presence of one pollutant will affect the uptake or removal of other pollutants through sorption. Waste waters from different sources may also contain more than one metal ion, it is usually a mixture of a number of metal ions often together with organic dyes or solvents in varying concentrations. The aim of this study was therefore, to assess the simultaneous adsorption of Cd2+ and Pb2+ from aqueous solution onto polymer-grafted montmorillonite clay, and its effect on the adsorption isotherms and kinetics.
For a given mass of adsorbent, m in a solution volume, V and initial concentration C 0 , the amount of metal ions adsorbed, Q at time, t is computable using Eq. 1 (Gwenzi et al. 2014):
C t is the concentration in solution at time t.
Adsorption isotherms provide information on the sorption of an adsorbate for a given adsorbent and predict distribution of the adsorbate between the surface and solution (Rebitanim et al. 2012). When an adsorbent is in contact with the surrounding fluid of a certain concentration, adsorption occurs and after a while the adsorbent and the fluid reach equilibrium. The commonly used adsorption isotherm models are the Langmuir and the Freundlich models (Cabrera et al. 2014). For an equilibrium amount of adsorbate, C e and equilibrium sorption capacity of adsorbent, Q e, the Langmuir model (Eq. 2) is used for the estimation of maximum adsorption capacity of the adsorbent:
where Q 0 and b are the Langmuir constants related to the adsorption capacity and the rate of adsorption, respectively.
The model assumes that absorption sites have equal affinities for molecules of the adsorbate and adsorption at one site does not affect the ability of the next site to adsorb heavy metal ions (Kumar et al. 2008; Wang et al. 2009; Rebitanim et al. 2012). Furthermore each site can accommodate only one molecule or ion and adsorption at the surface is localized, adsorbed molecules or ions are adsorbed at specific sites.
The Freundlich model (Eq. 3) describes the adsorption equilibrium at heterogeneous surfaces and does not assume monolayer capacity:
where K f and n are the Freundlich constants related to the adsorption capacity and the rate of adsorption, respectively.
Adsorption kinetics can be described using Lagergren linear first-order and second-order kinetics as described by Eqs. 4 and 5, respectively (Delval et al. 2002; Ruziwa et al. 2015). For an amount of solute adsorbed at equilibrium per unit mass of adsorbent, Q e, and amount of solute adsorbed Q t at time t, the Lagergren linear pseudo first-order equation is shown in Eq. 4:
where k 1 is the pseudo first-order rate constant.
The pseudo second-order equation is:
where k 2 is the pseudo second-order rate constant.
The pseudo second-order model assumes chemisorption and can be used to describe the adsorption mechanism for the whole sorption process.
Experimental
Materials
Dodecylbenzene sulphonic acid (DBS) and sodium metabisulphite (SMBS) from BDH Chemicals; ammonium persulphate (AMPS, 98 %) from Associated Chemical Enterprises, acetone (99 %) from SMM Chemicals and tetrahydrofuran (99.5 %) from Fluka were used without any purification or pretreatment. Pb(NO3)2 (99.5 %), methyl methacrylate (MMA, 99 %) were purchased from SAARCHEM (Pty) Ltd. MMA was first distilled before use and Pb(NO3)2 and Cd(NO3)2·4H2O were used as received. Montmorillonite (MMT) (cation exchange capacity (CEC): 91.44 meq/100 g) from BaoBio Holdings (Pty) Ltd was used as supplied.
Graft polymerization of NaMMT with PMMA
SMBS (0.0072 g) and of DBS (0.0145 g) were dissolved in deionized water (97.0 mL). Nanoclay (5 g) was added slowly to the mixture under high speed magnetic stirring. MMA (3.0 g) was added to form an emulsion and the mixture purged with dry N2. After mixing for 30 min, AMPS (0.030 g) dissolved in deionised water (10 mL) was added and the mixture heated at 60 °C under N2 for 4 h. The mixture was cooled to room temperature, and the product isolated by filtration. The product was purified by solvent extraction with tetrahydrofuran to remove ungrafted PMMA homopolymer and oven dried at 60 °C for 6 h.
Characterisation
Functional groups for NaMMT and PMMA-grafted MMT were determined using FTIR (PerkinElmer System 2000). About 2.0 mg of sample was properly mixed with 200 mg of KBr and then ground thoroughly using mortar and pestle. An appropriate amount of the ground sample was pelletized using a SPECAC bolt and nut pelletizer to give a transparent pellet. Each sample was analysed against an air background at 24 scans in the wavenumber range 4000–370 cm−1 with a resolution of 4 cm−1. Thermal stability and decomposition characteristics were determined using thermogravimetric analyser (PerkinElmer, TGA7) fitted with a thermal analysis controller (TAC7/DX) under N2. The samples were heated from 25 to 900 °C at a heating rate of 15 °C/min. X-ray diffraction analysis was carried out in locked couple mode with a Bruker AXS D8 Advance diffractometer (Cu Kα radiation with λ = 1.5406 Å, 40 kV, 40 mA, equipped with a PSD Lynx-Eye Si-strip detector (with 196 channels), at room temperature. SEM micrographs were obtained using a scanning electron microscope (Tescan, Vega3, Czech Republic). BET surface area (S BET), pore width and pore volume were measured using an automated N2 adsorption analyser (TriStar 3000 V6.08 A, Micromeritics, Norcross, USA).
Sorption studies
Sorption properties of NaMMT and PMMAgMMT were studied using batch experiments. Synthetic solutions containing a mixture of Cd2+ and Pb2+ with concentrations of each metal ion ranging from 10 to 50 ppm were prepared from Cd(NO3)2.4H2O and Pb(NO3)2, respectively, based on earlier work by Chen et al. (2010). The adsorption experiments were carried out to generate isotherm and kinetics data. The conditions used to generate adsorption isotherms were as follows: adsorbent dosage was 1.25 g adsorbent per litre of solution; metal ion concentration ranges were 10–50 ppm for both Cd2+ and Pb2+; the pH was 5.0 and a temperature of 25 °C for all the adsorption experiments; the shaking time was 6 h. Aliquots were taken after 6 h for measurement with AAS (Thermo Scientific iCE 3000 Series). A blank of distilled water showed no Cd2+ or Pb2+ contamination. All measurements were performed in triplicate, and mean values calculated and reported. To assess the rate of the adsorption for both Cd2+ and Pb2+, experiments were carried out under the following conditions: amount of adsorbent used was 1.25 g per 1.0 L of solution; the initial metal concentration for both Cd2+ and Pb2+ was 50 ppm; the pH was 5.0 and the shaking time was 6 h. Aliquots of sample solutions were withdrawn at set time intervals and the concentration of each heavy metal determined by AAS. The adsorption kinetic studies were carried out separately for each heavy metal ion, and as a mixture.
Regeneration of spent sorbent
Regeneration of the adsorbents was carried out with 0.1 M HNO3 (80 mL) and the adsorbent was washed with a small volume of 0.01 M NaOH solution until the pH of the filtrate was about 5.0.
Results and discussion
Fourier transform infrared (FTIR) spectroscopy
The FTIR spectrum for NaMMT showed stretching vibrations at 467, 527, 801, 843, 886, 919, 1045, 1639, 2927, 3436 and 3636 cm−1 (Fig. 1a. These frequencies were attributed to Si–O–Si bending, Si–O–Al bending, O–Si–O asymmetric stretching, Al–OH–Mg deformation, Al–OH–Fe deformation, OH bending (Al2OH), Si–O stretching, H–O–H deformation (interlayer H2O), –CH3 asymmetric stretching, H–O–H stretching (adsorbed H2O) and structural O–H stretching vibrations, respectively (Yuan et al. 2006; Qin et al. 2015; Tran et al. 2015). The FTIR spectrum for PMMA showed peaks at 1453, 1733, 2927 and 2955 cm−1 which were attributed to: –O–CH3 (deformation), C=O, –CH2 and –CH3 stretching vibrations, respectively. The presence of the stretching vibrations at 1733 cm−1 (C=O) and 1453 cm−1 (–O–CH3 asymmetric deformation) in the THF extracted product (PMMAgMMT) confirmed that methyl methacrylate groups were covalently attached to MMT during the grafting process (Rajendran and Mahendran, 2001).
X-ray diffraction
The characteristic basal reflection peak of NaMMT occurred at 2θ = 6.22° with a basal spacing of 14.2 Å, while that for PMMAgMMT occurred at 2θ = 5.88° with a basal spacing of 15.0 Å (Fig. 1b. An increase in the basal spacing was observed after modification with PMMA. This suggested that PMMA was partially intercalated and polymerized within the interlayer space of the NaMMT, possibly because of the large molecular size of PMMA (Zehhaf et al. 2013; Qin et al. 2015; Tran et al. 2015).
Thermogravimetric analysis
The thermogram for PMMA showed that its decomposition started from 250 °C up to about 420 °C (Fig. 1c. The PMMA differential thermogram showed two decomposition peaks at 300 and 394 °C. Above 430 °C, all the PMMA was completely decomposed. The thermogram for NaMMT showed a two-step degradation process, at 90 °C, due to loss of adsorbed water, and at 500 °C due to dehydroxylation of the clay structure (Binithat and Sugunan 2006; Qin et al. 2015). The peak at 345 °C in the differential thermogram for PMMAgMMT (Fig. 1d was ascribed to the decomposition of grafted PMMA since the NaMMT differential thermogram did not show a similar peak. The grafting efficiency was estimated from the mass loss at the temperature of 345 °C. This indicated PMMAgMMT contained about 9.0 % by mass of PMMA.
SEM and BET
Although both micrographs show irregular surfaces and undulations, the morphology of NaMMT had a relatively smooth surface, whereas the PMMAgMMT had a rough surface indicative of the attached PMMA particles (Fig. 2). Similar results were reported for dimercaprol grafted MMT (Tran et al. 2015).
The S BET for NaMMT was about four times higher than that of PMMAgMMT (Table 1). The decrease in surface area is consistent with previous work by Qin et al. (2015) who reported a nine-fold decrease in surface area after intercalating MMT with Fe2+ ions and attributed the decrease to the adsorbed Fe2+ ions in the montmorillonite layers. The decrease in S BET for PMMAgMMT can thus be ascribed to the occupation of interlayer spaces by PMMA following intercalation, and the relatively smaller decrease could be due to the partial rather than complete intercalation process.
Adsorption isotherms
The isotherms for Cd2+ adsorption onto both NaMMT and PMMAgMMT (Fig. 3a were classified as Langmuir type 2 (L2). The isotherm for Pb2+ adsorption onto PMMAgMMT was categorized as Langmuir type 4 (L4), while the isotherm for Pb2+ adsorption onto NaMMT was identified as Langmuir type mx (Lmx) (Hinz 2001). Adsorption isotherms are classified into four major classes based on the slope of the initial portion of the curve of the equilibrium adsorbed amount (Q e) versus equilibrium adsorbate concentration (C e) and thereafter into subgroups (Hinz 2001). This was one of the methods used in the analysis of adsorption data in this study. Pb2+ had a higher equilibrium adsorbed amount (Q e) onto both NaMMT and PMMAgMMT for the binary mixture than Cd2+. The maximum sorption capacities for NaMMT and PMMAgMMT were 18.73 and 19.27 mg/g for Cd2+, and 30.03 and 34.25 mg/g for Pb2+, respectively. Other researchers have reported a maximum adsorption capacity of 10.2 mg/g for Cu2+ on surfactant treated MMT (Fan et al. 2014), and Xing et al. (2015) reported 99.5 mg/g maximum adsorption of Pb2+ on MMT. Similar findings were reported by Lv et al. (2005) in competitive studies of Cd2+, Cu2+ and Pb2+ onto microporous titanosilicate. Pb2+ has been reported to inhibit the sorption of Cd2+ in biochars, an effect attributed to the differences in ionic radii of the two metals (Wang et al. 2011; Yu et al. 2013). Nonetheless, in the current study, the presence of both heavy metals in solution did not significantly affect their sorption process, as indicated by the isotherm mode, from solution. The experimental data were fitted to linear Langmuir and Freundlich isotherm equations (Eqs. 2 and 3, respectively). R 2 values obtained for these models for the two adsorbents ranged between 0.9161 and 0.9984. A slight increase was observed in the uptake of both Cd2+ and Pb2+ onto PMMAgMMT. The Langmuir model gave higher correlation coefficients (R 2) than the Freundlich model (Fig. 3b). The adsorption of Fe2+ onto pristine montmorillonite was reported to follow the Langmuir model (Qin et al. 2015), although other studies have reported Cu2+ adsorption onto surfactant modified montmorillonite to follow the Freundlich isotherm (Fan et al. 2014). From the Langmuir adsorption capacities, it was observed that slightly less Cd2+ was adsorbed onto PMMAgMMT than on NaMMT. This is contrary to what was observed for the adsorption of Cd2+ alone onto the same adsorbents, which gave a slightly higher adsorbed amount of Cd2+ for PMMAgMMT than NaMMT. For Pb2+ adsorption, the trend was maintained as was observed for the adsorption of Pb2+ alone (Table 2).
The close correlation between Q e (Pseudo-second-order) and Q 0 (Langmuir) values showed that both models can be used to calculate the maximum amount sorbed for each metal ion.
The amount of each heavy metal sorbed on both NaMMT and PMMAgMMT decreased when the two metals coexisted in solution. A similar trend was observed from the kinetics data. Applying the student’s t test (P = 0.05) to the data showed that the uptake of Pb2+ was significantly reduced by the presence of Cd2+ ions in the same solution. Though there was a decrease in Cd2+ adsorption in the presence of Pb2+, the change was not statistically significant at 95 % confidence level. The reduction observed was attributed to the competition between the metals ions for the same adsorption sites on the adsorbent surface (Chen et al. 2010). However, the adsorption capacities found for each heavy metal were still significantly high, thus making the adsorbents suitable for use in the treatment of heavy metals contaminated water.
The uptake of Cd2+ was consistently lower compared with Pb2+ uptake regardless of the adsorbent. The student’s t-test showed that the uptake of Cd2+ was statistically different from Pb2+ uptake at 95 % confidence level. Mobasherpour et al. (2012) reported a similar trend for the adsorption of Cd2+ and Pb2+ on nano-crystallite hydroxyapatite from aqueous solution. The higher affinity of Pb2+ for the adsorbent was attributed to the smaller hydrated radius of Pb2+ (4.01 Å) and its low hydration energy (Pb2+ = −1481 kJ/mol) relative to Cd2+ (4.19 Å, −2106 kJ/mol). Chen et al. (2010) studied the adsorption of Cd2+, Cu2+ and Pb2+ onto nano-hydroxyapatite and observed similar behaviour. Pavasant et al. (2006) also observed the same trend for Zn2+, Cu2+, Cd2+ and Pb2+ adsorption onto marine green macroalgae.
Adsorption kinetics
The systems reached equilibrium within 3 h and the uptake of Pb2+ was higher than the uptake of Cd2+ to both sorbents (Fig. 4). From the kinetic data (Table 2), it was observed that the pseudo second-order model had higher R 2 values than the pseudo first-order model. The adsorption of Cd2+ remained the same for the two adsorbents while Pb2+ uptake increased slightly for PMMAgMMT. The uptake of Pb2+ was higher than that of Cd2+ for both adsorbents. Chen et al. (2010) obtained similar results for the aqueous adsorption of Cd2+, Pb2+ and Cu2+ with nano-hydroxyapatite. The differences in the affinities of the metals for the adsorbents could still be attributed to their respective ionic radii. The pseudo first-order and pseudo second-order plots for Cd2+/Pb2+ adsorption from binary solutions (Fig. 4a, b show that the pseudo second-order model had the highest R 2 values for both metal ions (Table 2). However, the pseudo first-order R2 values were also relatively high (>0.9600) suggesting that the data could be adequately described by both models. The reason for a lower Q e value for Cd2+ adsorption onto PMMAgMMT than NaMMT was not clear. Antoniadis et al. (2007) reported a similar trend in the adsorption of Cd, Ni and Zn onto sewage sludge-amended soil.
Regeneration of spent adsorbent
As expected, the amount of both Cd2+ and Pb2+ adsorbed decreased with an increase in the number of regeneration cycles (Fig. 5a). Pb2+ uptake decreased by about 27 % while Cd2+ uptake decreased by about 23 % after three regeneration cycles. The slight decrease in the uptake of the two heavy metals suggested that PMMAgMMT can be used repeatedly for at least three regeneration cycles without a significant loss in the adsorption capacity. The desorption experiments for Pb2+ from PMMAgMMT showed that up to 96 % of the adsorbed amount could be desorbed by using 80 mL of 0.1 M HNO3, while 100 % of Cd2+ could be desorbed under similar conditions, the differences being attributed to higher affinity of Pb2+ for the adsorbent. FTIR spectra of the regenerated sorbent showed a peak at 420 cm−1 for PMMAgMMT at zero and two regeneration cycles, confirming the existence of a metal–oxygen bond (Fig. 5b) (de Portilla 1974). Chemisorption is thus a likely mechanism for the removal of Cd2+ and Pb2+ from aqueous solution.
Conclusion
The grafting of PMMA by emulsion copolymerization onto NaMMT was confirmed by FTIR, TGA and XRD results. Analysis of the materials showed that PMMA was successfully bonded onto the silanol groups on the montmorillonite clay. Adsorption studies for Cd2+ and Pb2+ adsorption on NaMMT and PMMAgMMT separately and as binary solutions, have demonstrated that it is possible to improve the sorption properties of montmorillonite clay by grafting the nanoclay with organic polymers like poly (methyl methacrylate). Pb2+ had a significantly higher sorption affinity for both NaMMT and PMMAgMMT compared with Cd2+. Competitive adsorption results showed a decrease in the uptake of both heavy metals. The competitive sorption of Cd2+ and Pb2+ did not significantly affect the sorption process of each and the mechanism of adsorption. The data also obeyed the Langmuir model and pseudo second-order model. Although there was a decrease in both Cd2+ and Pb2+ uptake, the adsorbed amounts of each metal still remained relatively high, thus making the sorbents suitable for the simultaneous removal of Cd2+ and Pb2+ from contaminated water. The fact that PMMAgMMT could be regenerated and reused for three cycles without a significant loss in sorption capacity allows for the development of a cost-effective sorbent. Overall, if properly developed through the grafting of suitable organic groups, montmorillonite nanoclay can result in low-cost, efficient and effective nanotechnology based water treatment systems.
References
Alfven T, Jarup L, Elinder CG (2002) Cadmium and lead in blood in relation to low bone mineral density and tubular proteinuria. Environ. Health Persp. 110:699–702
Antoniadis V, Tsadilas CD, Ashworth DJ (2007) Monometal and competitive adsorption of heavy metals by sewage sludge-amended soil. Chemosphere 68:489–494
Arief VO, Trilestari K, Sunarso J, Indraswati N, Ismadji S (2008) Recent progress on biosorption of heavy metals from liquids using low cost biosorbents: characterization, biosorption parameters and mechanism studies. Clean Soil Air Water 36:937–962
Binithat NN, Sugunan S (2006) Preparation and characterisation and catalytic activity of titania-pillared montmorillonite clays. Micropor. Mesopor. Mater. 93:82–89
Cabrera A, Cox L, Spokas K, Hermosin MC, Cornejo J, Koskinen WC (2014) Influence of biochar amendments on the sorption-desorption of aminocyclopyrachlor, bentazone and pyraclostrobin pesticides to agricultural soil. Sci Total Environ 470–471:438–443
Cao F, Bai P, Li H, Ma Y, Deng X, Zhao C (2009) Preparation of polyethersulfone-organophilic montmorillonite hybrid particles for the removal of bisphenol A. J Hazard Mater 162:791–798
Chen SB, Ma YB, Chen L, Xian K (2010) Adsorption of aqueous Cd2+, Pb2+, Cu2+ ions by nano-hydroxyapatite: single- and multi-metal competitive study. Geochem J 44:233–239
De Portilla VIS (1974) Infrared spectroscopic investigation of the structure of some natural arsenates and the nature of H-bonds in their structures. Can Mineral 12:262–268
Delval F, Crini G, Morinc N, Vebrel J, Bertini S, Torri G (2002) The sorption of several types of dye on crosslinked polysaccharides derivatives. Dyes Pigm 53:79–92
Fan H, Zhou L, Jiang X, Huang Q, Lang W (2014) Adsorption of Cu2+ and methylene blue on dodecyl sulfobetaine surfactant-modified montmorillonite. Appl Clay Sci 95:150–158
Garg VK, Kumar R, Gupta R (2004) Removal of malachite green dye from aqueous solution by adsorption using agro-industry waste: a case study of prosopis cineraria. Dyes Pigm 62:1–10
Gwenzi W, Musarurwa T, Nyamugafata P, Chaukura N, Chaparadza A, Mbera S (2014) Adsorption of Zn2+ and Ni2+ in a binary aqueous solution by biosorbents derived from sawdust and water hyacinth (Eichhornia crassipes). Water Sci Technol 70:1419–1427
Hinz C (2001) Description of sorption data with isotherm equations. Geoderma 99:225–243
Jarup L, Hellstrom L, Alfven T, Carlsson MD, Grubb A, Persson B, Pettersson C, Spang G, Schutz A, Elinder CG (2000) Low level exposure to cadmium and early kidney damage: the OSCAR study. Occup Environ Med 57:668–672
Jin T, Nordberg G, Ye T, Bo M, Wang H, Zhu G, Kong Q, Bernard A (2004) Osteoporosis and renal dysfunction in a general population exposed to cadmium in China. Environ Res 96:353–359
Kazantzis G (2004) Cadmium, osteoporosis and calcium metabolism. Biometals 17:493–498
Kobya M, Demirbas E, Senturk E, Ince M (2005) Adsorption of heavy metal ions from aqueous solutions by activated carbon prepared from apricot stone. Bioresour Technol. 96:1518–1521
Kumar D, Singh A, Gaur JP (2008) Mono-component versus binary isotherm models for Cu (II) and Pb(II) sorption from binary metal solution by the green alga pithophora oedogonia. Bioresour Technol. 99:8280–8287
Lv L, Hor MP, Su F, Zhao XS (2005) Competitive adsorption of Pb2+, Cu2+ and Cd2+ ions on microporous titanosilicate ETS-10. J Colloid Interface Sci 287:178–184
Mobasherpour I, Salahi E, Pazouki M (2012) Comparative of the removal of Pb2+, Cd2+ and Ni2+ by nano crystallite hydroxyapatite from aqueous solutions: adsorption isotherm study. Arab J. Chem. 5:439–446
Nawrot TS, Staessen JA, Roels HA, Munters E, Cuypers A, Richart T, Ruttens A, Smeets K, Clijsters H, Vangronsveld J (2010) Cadmium exposure in the population: from health risks to strategies of prevention. Biometals 23:769–782
Pavasant P, Apiratikul R, Sungkhum V, Suthiparinyanont P, Wattanachira S, Marhaba TF (2006) Biosorption of Cu2+, Cd2+, Pb2+, and Zn2+ using dried marine green macroalga Caulerpa lentillifera. Bioresour Technol 97:2321–2329
Qin D, Niu X, Qiao M, Liu G, Li H, Meng Z (2015) Adsorption of ferrous ions onto montmorillonites. Appl Surf Sci 333:170–177
Rajendran SKR, Mahendran O (2001) An electrochemical investigation on PMMA/PVDF blend-based polymer electrolytes. Mater Lett 49:172–179
Rebitanim NZ, Ghani WA, Mahmoud DK, Rebitanin NA, Salleh MAM (2012) Adsorption of methylene blue by agricultural solid waste pyrolysed from EFB biochar. J. Purity Util. React. Environ. 1:346–360
Ruziwa DT, Chaukura N, Gwenzi W, Pumure I (2015) Removal of Zn2+ and Pb2+ from water using sulphonated waste polystyrene. J Environ Chem Eng 3:2528–2537
Teemu H (2007) Removal of cadmium, lead and arsenic from water by lactic acid bacteria. Functional Foods Forum, Turkey
Tran L, Wu P, Zhu Y, Liu S, Zhu N (2015) Comparative study of Hg(II) adsorption by thiol- and hydroxyl-containing bifunctional montmorillonite and vermiculite. Appl Surf Sci 256:91–101
Wang S, Dong Y, He M, Chen L, Yu X (2009) Characterization of GMZ bentonite and its application in the adsorption of Pb(II) from aqueous solutions. Appl Clay Sci 43:164–171
Wang XS, Miao HH, He W, Shen HL (2011) Competitive adsorption of Pb(II), Cu(II), and Cd(II) ions on wheat-residue derived black carbon. J Chem Eng Data 56:444–449
Xing X, Lv G, Zhu W, He C, Liao L, Mei L, Li Z, Li G (2015) The binding energy between the interlayer cations and montmorillonite layers and its influence on Pb2+ adsorption. Appl Clay Sci 112–113:117–122
Yu J, Wang L, Chi R, Zhang Y, Xu Z, Guo J (2013) Competitive adsorption of Pb2+ and Cd2+ on magnetic modified sugarcane bagasse prepared by two simple steps. Appl Surf Sci 268:163–170
Yuan P, He H, Bergaya FA, Wu D, Zhou Q, Zhu J (2006) Synthesis and characterization of delaminated iron-pillared clay with meso-microporous structure. Microporous Mesoporous Mater 88:8–15
Zehhaf A, Morallon E, Benyoucef A (2013) Polyaniline/montmorillonite nanocomposites obtained by in situ intercalation and oxidative polymerization in cationic modified-clay (sodium, copper and iron). J Inorg Organomet Polym 23:1485–1491
Zhu R, Zhu R, Ge F, Xu Y, Liu J, Zhu J, He H (2016a) Effect of heating temperature on the sequestration of Cr3+ cations on montmorillonite. Appl Clay Sci 121–122:111–118
Zhu R, Chen Q, Zhou Q, Xi Y, Zhu J, He H (2016b) Adsorbents based on montmorillonite for contaminant removal from water: a review. Appl Clay Sci 123:239–258
Acknowledgments
The authors would like to thank Govan Mbeki Research and Development Centre (University of Fort Hare) and iThemba Labs for access to XRD instruments.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Bunhu, T., Tichagwa, L. & Chaukura, N. Competitive sorption of Cd2+ and Pb2+ from a binary aqueous solution by poly (methyl methacrylate)-grafted montmorillonite clay nanocomposite. Appl Water Sci 7, 2287–2295 (2017). https://doi.org/10.1007/s13201-016-0404-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13201-016-0404-5