Abstract
Alloy 304HCu is an austenitic stainless, developed from TP304H with the addition of copper and niobium for power plant applications. Solidification cracking is major issue in welding of austenitic stainless steels. In this paper, solidification cracking behaviour of alloy 304HCu with three different fillers viz., nickel fortified near-matching alloy 304HCu, ER NiCrCoMo-1 and ER NiCrMo-3 using Varestraint weldability testing. The solidification cracking behaviour of the parent material and different welds were assessed under different strain rates and the mechanisms were discussed, addressing the microstructural evolution and compositional changes. The weld materials were characterized for their mechanical properties both at ambient conditions and at elevated temperature, highlighting their usefulness in the power sector.
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs12666-020-02028-1/MediaObjects/12666_2020_2028_Fig1_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs12666-020-02028-1/MediaObjects/12666_2020_2028_Fig2_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs12666-020-02028-1/MediaObjects/12666_2020_2028_Fig3_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs12666-020-02028-1/MediaObjects/12666_2020_2028_Fig4_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs12666-020-02028-1/MediaObjects/12666_2020_2028_Fig5_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs12666-020-02028-1/MediaObjects/12666_2020_2028_Fig6_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs12666-020-02028-1/MediaObjects/12666_2020_2028_Fig7_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs12666-020-02028-1/MediaObjects/12666_2020_2028_Fig8_HTML.png)
Similar content being viewed by others
References
Vekeman J, Huysmans S, and De Bruycker E, Weld World 58 (2014) 873.
Siefert J A, and David S A, Sci Technol Weld Join 19 (2014) 271.
David S A, Siefert J A, DuPont J N, and Shingledecker J P, Sci Technol Weld Join 20 (2015) 532.
Katayama S, Fujimoto T, and Matsunawa A, Trans JWRI Weld Res Inst Osaka Univ 14 (1985) 12.
Kujanpaa V P, David S A, and White C L, Weld Res Suppl Weld J 65 (1986) 203s.
Lippold J C, and Savage V V F, Weld J 61 (1982) 388s.
Hull F C, Weld J 46 (1967) 399s.
Brooks J A, and Lambert F J Weld J 57 (1978) 39s.
Kotecki D J, and Siewert T A Weld J 71 (1992) 171s.
Lundin C D, Lee C H, and Qiao C Y P Weld J 7 (1993) 321s.
Lingenfelter C Weld J 51 (1972) 430s.
Ogawa T, and Tsunetomi E Weld J 61 (1982) 82s.
Andersson J, Jacobsson J, Brederholm A, and Hänninen H, in Improved Understanding of Varestraint Testing—Nickel-Based Superalloys, Cracking Phenomena in Welds IV, (eds) Böllinghaus T, Lippold J, and Cross C E, Springer, Cham (2016), p 25.
Tripathy H, Subramanian R, Hajra R N, Rai A K, Rengachari M, Saibaba S, and Jayakumar T, Metallurg Mater Trans E 3E (2016) 234.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Ravibharath, R., Muthupandi, V., Bala Srinivasan, P. et al. Characterization of Solidification Cracking in 304HCu Austenitic Stainless Steel Welds. Trans Indian Inst Met 73, 2345–2353 (2020). https://doi.org/10.1007/s12666-020-02028-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-020-02028-1