In this study, the effect of Zr addition on phase formation, microstructure, and hardness of FeCrNiMnCoZr x and Al0.5FeCrNiMnCoZr x were investigated. High entropy alloys (HEA) were synthesized using arc melting technique in argon (Ar) atmosphere (x = 0, 0.1, 0.2, 0.3). Ingots were homogenized for 24 h at 900 °C in Ar atmosphere. Phase formation, microstructure and hardness of HEAs were investigated using field emission scanning electron microscope, X-ray diffraction and Vickers microhardness tester. Electron micrographs of HEAs showed majorly dendritic(DR) and interdendritic(ID) phases. For both FeCrNiMnCoZr x and Al0.5FeCrNiMnCoZr x alloys, amount of ID phases is seen to increase with increased Zr content. Aluminium containing HEAs showed fine needle-shaped precipitates dispersed throughout the matrix phase. XRD results confirmed the presence of mixed FCC/BCC phases in FeCrNiMnCoZr x alloys and BCC as majority phase in Al0.5FeCrNiMnCoZr x alloys. As the Zr content increased, hardness of HEA increased.
Similar content being viewed by others
References
Li C, Li J C, Zhao M, and Jiang Q, J Alloy Compd 475 (2009) 752.
Greer A L, Nature 366 (1993) 303.
Yeh J W, Chen Y L, Lin S J, and Chen S K, Mater Sci Forum 560 (2007) 1.
Yeh J W, Chen S K, Lin S J, Gan J Y, Chin T S, and Shun T T, Adv Eng Mater 6 (2004) 299.
Ma S G, and Zhang Y, Mater Sci Eng A 532 (2012) 480.
Hsu C Y, Sheu T S, Yeh J W, and Chen S K Wear 268 (2010) 653.
Zhang K B, Fu Z Y, Zhang J Y, Wang W M, Wang H, Wang Y C, Zhang Q J, and Shi J, Mater Sci Eng A 508 (2009) 214.
Guo S, Ng C, Lu J, and Liu C T, J Appl Phys 109 (2011) 103505.
Tang W Y, Chuang M H, Chen H Y, and Yeh J W, Adv Eng Mater 11 (2009) 788.
Acknowledgments
The authors would like to thank the Universiti Teknologi Mara for financially supporting this research under Grant No. 600-RMI/DANA 5/3/RIF (324/2012).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Pauzi, S.S.M., Darham, W., Ramli, R. et al. Effect of Zr Addition on Microstructure and Properties of FeCrNiMnCoZr x and Al0.5FeCrNiMnCoZr x High Entropy Alloys. Trans Indian Inst Met 66, 305–308 (2013). https://doi.org/10.1007/s12666-013-0264-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-013-0264-8