Abstract
AA6061-fly ash particle composites were fabricated using cold pressing followed by hot extrusion. Composites containing 2, 6 and 10 wt.% fly ash particles were fabricated. Matrix alloy samples without fly ash content were also prepared for comparison. Optical microscopy, Xray diffractrometry, Scanning Electron Microscopy and Transmission Electron Microscopy were adopted for characterizing the composites. Uniform distribution of fly ash particles was observed in composites. Hardness and tensile strength of the 2 wt.% fly ash composite were found to be better compared to the monolithic alloy after age-hardening. However, further increase of fly ash content resulted in poor age-hardening due to the depletion of Mg from the alloy matrix and transfer to the fly ash interface, which was confirmed by EDX analysis.
Similar content being viewed by others
References
Harrigan Jr W C, Everett R K and Arsenault R J, Metal Matrix Composites, Academic Press, New York, (1991)
Subhash K and Michael K, Mater. Sci. and Eng. A, 162 (1993) 153.
Zhang Z F, Zhang L C and Mai Y W, J. Mater. Sci. 30 (1995) 1961.
Zhao M, Wu G, Dou Z and Jiang L, Mater. Sci. & Eng. A, 374 (2004) 303.
Deonath Bhat R T and Rohatgi P K, J. Mater. Sci., 15 (1980) 1241.
Majumdar B C, Yegneshwaran A H and Rohatgi P K, Mater. Sci. & Eng., 68 (1984) 85.
Poza P and Llorca J, Mater. Sci. & Eng. A, 206 (1996) 183.
Prader P and degischer H P, Mater. Sci. & Technol., 16 (2000) 893.
Rohatgi P K and Guo R Q, J. Metall. Mater. Trans. B, 29 (1998) 519.
Guo R Q, Rohatgi P K, and Nath D, J Mater Sci 32 (1997) 3971.
Rohatgi P K, Guo R Q, Huang P, and Ray S, Metall Trans A 28 (1997) 245.
Rajan T P D, Pillai R M, Pai B C, Satyanarayana K G and Rohatgi P K, Recent Advances in Materials Processing. Proceedings of National Conference (2001) 327.
Aghajanian M K, Langensiepen R A, Rocazella M A, Leighton J T and Andersson C A, J. Mater. Sci, 28 (1993) 6683.
Deuis R L, Subramanian C and Yellup J M, Wear, 201 (1996) 132.
Ramachandra M and Radhakrishna K, Wear, 262 (2007) 1450.
Zuoyong D, Gaohui Wu, Xiaoli H, Dongli S and Longtao J, Comp. Part A, 38 (2007) 186.
Sudarshan and Surappa M K, Mater. Sci. & Eng. A, 480 (2008) 117.
Wu G H, Dou Z Y, Jiang L T and Cao J H, Material Letters, 60 (2006) 2945.
Fogagnolo J B, Robert M H and Torralba J M, J Bra. Soc. Mech. Sci. & Eng., 25 (2003) 1.
Slipenyuk A, Kuprin V, Milman Yu, Goncharuk V and Eckert J, Acta Mater., 54 (2006) 157.
Edwards G A, Stiller K, Dunlop G L and Couper M J, Acta Mater., 46 (1998) 3893.
Rohatgi P K, Kim J K, Guo R Q, Robertson D P and Gajdardziska-Josifovska, M, Metall. Trans. A, 33 (2002) 1541.
Hsu-Shen C, Kuo-Shung L and Jien-Wei Y, Metall. Trans. A, 31 (2000) 2587.
Kent D, Schaffer G B and Drennan J, Mater. Sci. & Eng. A, 405 (2005) 65.
Forn A, Teresa Baile M and Ruperez E, J. Mater. Proc. Technol. 143 (2003) 58.
Srivatsan T S, Ibrahim I A, Mohamed F A and Lavernia E J, J. Mater. Sci., 26 (1991) 5965.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kumar, P.R.S., Kumaran, S., Srinivasa Rao, T. et al. Microstructure and mechanical properties of fly ash particle reinforced AA6061 composites produced by press and extrusion. Trans Indian Inst Met 62, 559–566 (2009). https://doi.org/10.1007/s12666-009-0094-x
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-009-0094-x