Abstract
The ilmenite welding electrode has advantages of low cost and excellent welding technological properties. However, the welding quality is affected adversely by its poor crack resistance. To solve this problem, 12 kinds of rare earths coating formulas were optimized by means of orthogonal test design and curve fitting. Then the powders containing La/CeO2 were extruded into ilmenite welding electrode through screw-type pressing–scribbling machine. After that, a series of mechanical properties tests were conducted according to national standards. Next, the mechanical properties data were analyzed comprehensively by analyzing variance, boxplot as well as Minitab 3D surface chart. The results show that compared with the formula without rare earth, the deposited metal’s impact toughness, the lower yield strength, the tensile strength, and the hardness are increased by 54.44 %, 9.25 %, 6.37 %, and 4.27 %, respectively. In other words, Electrode 6 with the La/CeO2 amount of 0.5 %/0.1 % in coating has better mechanical properties.
Similar content being viewed by others
References
Vodop’yanov AG, Kozhevnikov GN. Production of titanium dioxide concentrate from slag of ilmenite reducing smelting. Russ J Appl Chem. 2013;86(1):124.
Wang H, Fan YJ, Li L, Chen ZH, Yang HB, Cao JM. Influence of drawing deformation on microstructure of TC4 wire after welding. Chin J Rare Met. 2013;37(3):506.
Chen CH, Ren RM, Wang ZB. Effect of high-energy-shot-peening on brazing of commercially pure titanium. Chin J Rare Met. 2013;37(5):732.
Yang DX, Li XY, Nie ZR. Microstructure characteristics of TIG welded Al–Mg alloy with small amount Er addition. Rare Met Mater Eng. 2012;41(10):1713.
Zhou YF, Yang YL, Qi XW. Influence of La2O3 addition on microstructure and wear resistance of Fe–Cr–C cladding formed by arc surface welding. J Rare Earths. 2012;30(10):1069.
Dai J, Huang J, Li ZG. Investigations on laser welding of magnesium alloys. Int J Mater Res. 2012;103(10):1218.
Dhakar BM, Dwivedi DK, Sharma SP. Studies on remelting of tungsten carbide and rare earth modified nickel base alloy composite coating. Surf Eng. 2012;28(1):73.
Yang DX, Li XY, He DY. Research on microstructure and properties of Er-containing aluminum alloy laser welded joints. Rare Met Mater Eng. 2012;41(1):165.
Xing SL, Yu SF, Deng Y. Effect of cerium on abrasive wear behaviour of hardfacing alloy. J Rare Earths. 2012;30(1):69.
Zhang M, Wu WG, Chu QL, Li JL, Zhang HC. Development of 0Cr13Ni5Mo steel matching electrode used pulsed DE-GMA welding brazing between magnesium and on fan impeller. Trans China Weld Inst. 2013;34(8):1.
Qin M, Zhu RR, Ding Y, Liu SH, Xiong K, Guo J. Effects of rare-earth content on electrochemical properties of La0.7(Pr0.75Nd0.25) x Mg0.3Ni3.3(Co0.7Al0.3)0.3 (x = 0.0, 0.1, 0.2, 0.3) alloy electrodes. Chin J Rare Met. 2012;36(5):732.
Li LF, Ma X, Qiu T. Effects of lanthanum on microstructure and solidification mechanism of (Ag-Cu28)-25Sn-xLa alloys. Chin J Rare Met. 2012;36(3):385.
Guo LJ, Wang XB, Wang FH. Modification of TiB2/Fe coating by SMAW with high carbon ferrochrome. Surf Eng. 2013;29(8):642.
Xu YS, Cai XT, Yuan ZJ, Lin NN. Development of 18Ni maraging steel for SMAW. Trans China Weld Inst. 2012;33(2):65.
Lou YH, Xiao HJ, Peng Y, Wang AH, Tian ZL, Peng ZH. 690 MPa study on microstructure and properties of welded joints of a 690 MPa grade HSLA steel. Mater Sci Technol. 2012;20(2):101.
Meng GG, Chu JJ, Luan JY, Gu F, Li D. Correlations between coating components and deposited metal compositions of environmental protective type basic electrode. Trans China Weld Inst. 2011;32(6):73.
Acknowledgments
This work was financially supported by the National Natural Science Foundation of China (No.51305178) and Xuzhou City Science and Technology Plan Project (No.XC12A013)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Guo, YH., Fan, XY., Zhang, L. et al. Determination of La/CeO2 content in ilmenite electrode coating. Rare Met. 34, 505–509 (2015). https://doi.org/10.1007/s12598-014-0406-0
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12598-014-0406-0