Abstract
We investigated dynamic interfacial phenomena at the slag-metal-refractory three-phase interface using a high temperature X-ray radiographic technique. Dynamic movement of the metal-slag line between Fe-11%Cr alloy and CaO-(SiO2 or Al2O3) slag was observed near the MgO-6%C refractory at 1823 K. We observed corresponding local corrosion of the refractory with CaO-SiO2 slag but it was negligible with CaO-Al2O3 slag. From a thermodynamic perspective, the Marangoni convection at the slag-metal-refractory interface is not the dominant factor determining the corrosion rate of the MgO-C refractory. Rather, it is the large solubility limit and the mass transfer in the slag phase.
Similar content being viewed by others
References
K. Fujiwara, Tetsu-to-Hagane 71, 794 (1985).
C. Borgianni, G. Casella, Rev. Metall. 93, 158 (1993).
N. Bannerberg, XXXVIIth International Colloquium on Refractories: Refractories and Refractory Systems for the Production of Clean Steel, pp. 17–34, Achen, Germany (1994).
J. Potschke, K. Beimdiek, M. Ollig, UNITECR’99, Proc. Unified Int. Tech. Conf. on Refractories, 6 th Biennial World Congress / 42 nd Int. Colloq. on Refractories, pp. 166–169, Berlin, Germany (1999).
H. Soulard, J. Lehmann, M. Boher, M. C. Kaerle, C. Gaterllier, UNITECR’99, Proc. Unified Int. Tech. Conf. on Refractories, 6 th Biennial World Congress / 42 nd Int. Colloq. on Refractories, pp. 301–303, Berlin, Germany (1999).
G. Z. Ruan and N. Li, Ironmaking Steelmaking 31, 342 (2004).
J. Lee, A. Tazuke, T. Tanaka, and J. H. Park, Met. Mater. Int. 15, 501 (2009).
K. Mukai, J. M. Toguri, N. M. Stubina, and J. Yoshitomi, ISIJ Int. 29, 469 (1989).
Z. Li, K. Mukai, and Z. Tao, ISIJ Int. 40, S101 (2000).
Z. F. Yuan, W. L. Huang, and K. Mukai, J. Colloid Interface Sci. 253, 211 (2002).
T. Itoh, T. Nagasaka, and M. Hino, ISIJ Int. 40, 1051 (2000).
The Japan Society for the Promotion of Science, The 19 th Committee of Steelmaking, Steelmaking Data Sourcebook, p. 279, 288, Goldon and Breach, Montreux, Switzerland (1984).
N. Ahmadi Najafabadi, M. Hirasawa, and M. Sano, ISIJ Int. 36, 1366 (1996).
L. A. Girifalco and R. J. Good, J. Phys. Chem. 61, 904 (1957).
J. Lee et al., Met. Mater. Trans. B 36B, 241 (2005).
K. Nakashima and K. Mori, ISIJ Int. 32, 11 (1992).
T. Tanaka and S. Hara, Z. Metallkd., 90, 348 (1999).
H. S. Kim, D. J. Min, and J. H. Park, ISIJ Int., 41, 317 (2001).
J. H. Park and D. J. Min, ISIJ Int. 47, 1368 (2007).
K. C. Mills et al., Slag Atlas, 2 nd ed., VDEh, Verlag Stahleisen GmbH, Dusseldorf, Germany.
K. Ogino, Bull. Jpn. Inst. Met. 11, 323 (1972).
S. A. Nightingale, G. A. Brooks, and B. J. Mohaghan, Metall. Mater. Trans. B 36B, 453 (2005).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Shin, M., Cho, S., Lee, J. et al. In-situ observation of dynamic interfacial phenomena between CaO-(SiO2 or Al2O3) slag and Fe-11%Cr alloy near the MgO-6%C refractory at 1823 K. Met. Mater. Int. 16, 495–499 (2010). https://doi.org/10.1007/s12540-010-0623-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12540-010-0623-5