Abstract
Zeolitic imidazolate frameworks (ZIFs) are an important subclass of metal-organic frameworks (MOFs) with zeolite-type topology, which can be fabricated under ambient synthesis conditions. However, the applications of ZIFs are commonly limited due to the weak hydrostability of their metal–ligand coordination bonds, particularly under humid and aqueous conditions. In this work, as an example, the hydrolysis behaviours of ZIF-L with a special focus on ZIF-L coatings were tested at aqueous conditions with a wide range of pHs to systematically study and fundamentally understand their structural stability and degradation mechanism. Pristine ZIF-L powder and ZIF-L coatings were severely damaged after only 24 h in aqueous media. Interestingly, the ZIF-L coatings showed two distinct hydrolyzation pathways regardless of pH conditions, exhibiting either a ring-shaped etching or unfolding behaviours. While the ZIF-L powders were hydrolyzed almost identically across all pH conditions. With this new understanding, a facile silk fibroin (SF) protein modification method was developed to enhance the hydrostability of ZIF-L coatings in aqueous media. The effect of protein concentration on surface coating was systemically studied. ZIF-L coating retained its surface morphology after soaking in water and demonstrated switchable super wetting properties and superior separation performance for oil/water mixture. As a result, the quick SF protein modification significantly enhanced the stability of ZIF-L coatings under various pHs, while retaining their switchable wetting property and excellent separation performance.
Article PDF
Similar content being viewed by others
References
Zhou, H. C. J.; Kitagawa, S. Metal-organic frameworks (MOFs). Chem. Soc. Rev. 2014, 43, 5415–5418.
Seetharaj, R.; Vandana, P. V.; Arya, P.; Mathew, S. Dependence of solvents, pH, molar ratio and temperature in tuning metal-organic framework architecture. Arab. J. Chem. 2019, 12, 295–315.
Pan, Y. C.; Liu, Y. Y.; Zeng, G. F.; Zhao, L.; Lai, Z. P. Rapid synthesis of zeolitic imidazolate framework-8 (ZIF-8) nanocrystals in an aqueous system. Chem. Commun. 2011, 47, 2071–2073.
Cacho-Bailo, F.; Seoane, B.; Téllez, C.; Coronas, J. ZIF-8 continuous membrane on porous polysulfone for hydrogen separation. J. Memb. Sci. 2014, 464, 119–126.
Lei, Z. W.; Deng, Y. H.; Wang, C. Y. Multiphase surface growth of hydrophobic ZIF-8 on melamine sponge for excellent oil/water separation and effective catalysis in a Knoevenagel reaction. J. Mater. Chem. A 2018, 6, 3258–3263.
Zheng, H. Q.; Zhang, Y. N.; Liu, L. F.; Wan, W.; Guo, P.; Nyström, A. M.; Zou, X. D. One-pot synthesis of metal-organic frameworks with encapsulated target molecules and their applications for controlled drug delivery. J. Am. Chem. Soc. 2016, 138, 962–968.
Xiao, H.; Zhou, H. X.; Feng, S. S.; Gore, D. B.; Zhong, Z. X.; Xing, W. H. In situ growth of two-dimensional ZIF-L nanoflakes on ceramic membrane for efficient removal of iodine. J. Memb. Sci. 2021, 619, 118782.
Yuan, S. S.; Zhu, J. Y.; Li, Y.; Zhao, Y.; Li, J.; Van Puyvelde, P.; Van Der Bruggen, B. Structure architecture of micro/nanoscale ZIF-L on a 3D printed membrane for a superhydrophobic and underwater superoleophobic surface. J. Mater. Chem. A 2019, 7, 2723–2729.
Ding, M. L.; Cai, X. C.; Jiang, H. L. Improving MOF stability: Approaches and applications. Chem. Sci. 2019, 10, 10209–10230.
Leus, K.; Bogaerts, T.; De Decker, J.; Depauw, H.; Hendrickx, K.; Vrielinck, H.; Van Speybroeck, V.; Van Der Voort, P. Systematic study of the chemical and hydrothermal stability of selected “stable” metal-organic frameworks. Microporous Mesoporous Mater. 2016, 226, 110–116.
Park, K. S.; Ni, Z.; Côté, A. P.; Choi, J. Y.; Huang, R. D.; Uribe-Romo, F. J.; Chae, H. K.; O’Keeffe, M.; Yaghi, O. M. Exceptional chemical and thermal stability of zeolitic imidazolate frameworks. Proc. Natl. Acad. Sci. USA 2006, 103, 10186–10191.
Bhattacharyya, S.; Pang, S. H.; Dutzer, M. R.; Lively, R. P.; Walton, K. S.; Sholl, D. S.; Nair, S. Interactions of SO2-containing acid gases with ZIF-8: Structural changes and mechanistic investigations. J. Phys. Chem. C 2016, 120, 27221–27229.
Mottillo, C.; Friščić, T. Carbon dioxide sensitivity of zeolitic imidazolate frameworks. Angew. Chem., Int. Ed. 2014, 53, 7471–7474.
Chen, T.; Lewis, A.; Chen, Z. P.; Fan, X. F.; Radacsi, N.; Semiao, A. J. C.; Wang, H. T.; Huang, Y. Smart ZIF-L mesh films with switchable superwettability synthesized via a rapid energy-saving process. Sep. Purif. Technol. 2020, 240, 116647.
Yuan, S.; Feng, L.; Wang, K. C.; Pang, J. D.; Bosch, M.; Lollar, C.; Sun, Y. J.; Qin, J. S.; Yang, X. Y.; Zhang, P. et al. Stable metal-organic frameworks: Design, synthesis, and applications. Adv. Mater. 2018, 30, 1704303.
Qadir, N. U.; Said, S. A. M.; Bahaidarah, H. M. Structural stability of metal-organic frameworks in aqueous media—Controlling factors and methods to improve hydrostability and hydrothermal cyclic stability. Microporous Mesoporous Mater. 2015, 201, 61–90.
Gao, S.; Hou, J. W.; Deng, Z. Y.; Wang, T. S.; Beyer, S.; Buzanich, A. G.; Richardson, J. J.; Rawal, A.; Seidel, R.; Zulkifli, M. Y. et al. Improving the acidic stability of zeolitic imidazolate frameworks by biofunctional molecules. Chem 2019, 5, 1597–1608.
Liu, X. L.; Li, Y. S.; Ban, Y. J.; Peng, Y.; Jin, H.; Bux, H.; Xu, L. Y.; Caro, J.; Yang, W. S. Improvement of hydrothermal stability of zeolitic imidazolate frameworks. Chem. Commun. 2013, 49, 9140–9142.
Shih, Y. H.; Kuo, Y. C.; Lirio, S.; Wang, K. Y.; Lin, C. H.; Huang, H. Y. A simple approach to enhance the water stability of a metal-organic framework. Chem.—Eur. J. 2017, 23, 42–46.
Zu, D. D.; Lu, L.; Liu, X. Q.; Zhang, D. Y.; Sun, L. B. Improving hydrothermal stability and catalytic activity of metal-organic frameworks by graphite oxide incorporation. J. Phys. Chem. C 2014, 118, 19910–19917.
Yang, S. J.; Choi, J. Y.; Chae, H. K.; Cho, J. H.; Nahm, K. S.; Park, C. R. Preparation and enhanced hydrostability and hydrogen storage capacity of CNT@MOF-5 hybrid composite. Chem. Mater. 2009, 21, 1893–1897.
Zhang, W.; Hu, Y. L.; Ge, J.; Jiang, H. L.; Yu, S. H. A facile and general coating approach to moisture/water-resistant metal-organic frameworks with intact porosity. J. Am. Chem. Soc. 2014, 136, 16978–16981.
Zhang, F.; You, X. R.; Dou, H.; Liu, Z.; Zuo, B. Q.; Zhang, X. G. Facile fabrication of robust silk nanofibril films via direct dissolution of silk in CaCl2-formic acid solution. ACS Appl. Mater. Interfaces 2015, 7, 3352–3361.
Wang, X. Q.; Yucel, T.; Lu, Q.; Hu, X.; Kaplan, D. L. Silk nanospheres and microspheres from silk/PVA blend films for drug delivery. Biomaterials 2010, 31, 1025–1035.
Jin, H. J.; Kaplan, D. L. Mechanism of silk processing in insects and spiders. Nature 2003, 424, 1057–1061.
Zhang, L.; Hu, Y. H. Strong effects of higher-valent cations on the structure of the zeolitic Zn(2-methylimidazole)2 framework (ZIF-8). J. Phys. Chem. C 2011, 115, 7967–7971.
Lee, S.; Oh, S.; Oh, M. Atypical hybrid metal-organic frameworks (MOFs): A combinative process for MOF-on-MOF growth, etching, and structure transformation. Angew. Chem., Int. Ed. 2020, 59, 1327–1333.
Chen, R. Z.; Yao, J. F.; Gu, Q. F.; Smeets, S.; Baerlocher, C.; Gu, H. X.; Zhu, D. R.; Morris, W.; Yaghi, O. M.; Wang, H. T. A two-dimensional zeolitic imidazolate framework with a cushion-shaped cavity for CO2 adsorption. Chem. Commun. 2013, 49, 9500–9502.
Low, Z. X.; Yao, J. F.; Liu, Q.; He, M.; Wang, Z. Y.; Suresh, A. K.; Bellare, J.; Wang, H. T. Crystal transformation in zeolitic-imidazolate framework. Cryst. Growth Des. 2014, 14, 6589–6598.
Ding, B.; Wang, X. B.; Xu, Y. F.; Feng, S. J.; Ding, Y.; Pan, Y.; Xu, W. F.; Wang, H. T. Hydrothermal preparation of hierarchical ZIF-L nanostructures for enhanced CO2 capture. J. Colloid Interface Sci. 2018, 519, 38–43.
Lo, Y.; Lam, C. H.; Chang, C. W.; Yang, A. C.; Kang, D. Y. Polymorphism/pseudopolymorphism of metal-organic frameworks composed of zinc(II) and 2-methylimidazole: Synthesis, stability, and application in gas storage. RSC Adv. 2016, 6, 89148–89156.
Zhang, H. F.; Zhao, M.; Yang, Y.; Lin, Y. S. Hydrolysis and condensation of ZIF-8 in water. Microporous Mesoporous Mater. 2019, 288, 109568.
Hu, Y.; Kazemian, H.; Rohani, S.; Huang, Y. N.; Song, Y. In situ high pressure study of ZIF-8 by FTIR spectroscopy. Chem. Commun. 2011, 47, 12694–12696.
Zhang, H. F.; Zhao, M.; Lin, Y. S. Stability of ZIF-8 in water under ambient conditions. Microporous Mesoporous Mater. 2019, 279, 201–210.
Mita, K.; Ichimura, S.; James, T. C. Highly repetitive structure and its organization of the silk fibroin gene. J. Mol. Evol. 1994, 38, 583–592.
Zhou, C. Z.; Confalonieri, F.; Medina, N.; Zivanovic, Y.; Esnault, C.; Yang, T.; Jacquet, M.; Janin, J.; Duguet, M.; Perasso, R. et al. Fine organization of Bombyx mori fibroin heavy chain gene. Nucleic Acids Res. 2000, 28, 2413–2419.
Lu, Q.; Zhu, H. S.; Zhang, C. C.; Zhang, F.; Zhang, B.; Kaplan, D. L. Silk self-assembly mechanisms and control from thermodynamics to kinetics. Biomacromolecules 2012, 13, 826–832.
Hu, Y.; Zhang, Q.; You, R.; Wang, L.; Li, M. The relationship between secondary structure and biodegradation behavior of silk fibroin scaffolds. Adv. Mater. Sci. Eng. 2012, 2012
Kundu, J.; Chung, Y. I.; Kim, Y. H.; Tae, G.; Kundu, S. C. Silk fibroin nanoparticles for cellular uptake and control release. Int. J. Pharm. 2010, 388, 242–250.
Zhang, Y. Q.; Shen, W. D.; Xiang, R. L.; Zhuge, L. J.; Gao, W. J.; Wang, W. B. Formation of silk fibroin nanoparticles in water-miscible organic solvent and their characterization. J. Nanopart. Res. 2007, 9, 885–900.
Li, Q. Q.; Deng, W. J.; Li, C. H.; Sun, Q. Y.; Huang, F. Z.; Zhao, Y.; Li, S. K. High-flux oil/water separation with interfacial capillary effect in switchable superwetting Cu(OH)2@ZIF-8 nanowire membranes. ACS Appl. Mater. Interfaces 2018, 10, 40265–40273.
Acknowledgements
This work was supported by start-up funding from the School of Engineering, at the University of Edinburgh. X. M. W. thanks the University of Edinburgh for Principal’s Career Development Ph.D. Scholarships and the School of Engineering for Edinburgh Global Research Scholarship. The authors would like to thank Fergus Dingwall for his laboratory assistance.
Author information
Authors and Affiliations
Corresponding author
Electronic Supplementary Material
12274_2024_6586_MOESM1_ESM.pdf
Improving the hydrostability of zeolitic imidazolate framework coatings using a facile silk fibroin protein modification method
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.
The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wei, X., Chen, T., Chen, S. et al. Improving the hydrostability of zeolitic imidazolate framework coatings using a facile silk fibroin protein modification method. Nano Res. (2024). https://doi.org/10.1007/s12274-024-6586-5
Received:
Revised:
Accepted:
Published:
DOI: https://doi.org/10.1007/s12274-024-6586-5