Abstract
Understanding the stability and current-carrying capacity of graphene spintronic devices is key to their applications in graphene channel-based spin current sensors, spin-torque oscillators, and potential spin-integrated circuits. However, despite the demonstrated high current densities in exfoliated graphene, the current-carrying capacity of large-scale chemical vapor deposited (CVD) graphene is not established. Particularly, the grainy nature of chemical vapor deposited graphene and the presence of a tunnel barrier in CVD graphene spin devices pose questions about the stability of high current electrical spin injection. In this work, we observe that despite structural imperfections, CVD graphene sustains remarkably highest currents of 5.2 × 108 A/cm2, up to two orders higher than previously reported values in multilayer CVD graphene, with the capacity primarily dependent upon the sheet resistance of graphene. Furthermore, we notice a reversible regime, up to which CVD graphene can be operated without degradation with operating currents as high as 108 A/cm2, significantly high and durable over long time of operation with spin valve signals observed up to such high current densities. At the same time, the tunnel barrier resistance can be modified by the application of high currents. Our results demonstrate the robustness of large-scale CVD graphene and bring fresh insights for engineering and harnessing pure spin currents for innovative device applications.
![](http://media.springernature.com/lw685/springer-static/image/art%3A10.1007%2Fs12274-022-5174-9/MediaObjects/12274_2022_5174_Fig1_HTML.jpg)
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Avsar, A.; Ochoa, H.; Guinea, F.; Özyilmaz, B.; van Wees, B. J.; Vera-Marun, I. J. Colloquium: Spintronics in graphene and other two-dimensional materials. Rev. Mod. Phys. 2020, 92, 021003.
Wang, P. C.; Filippi, R. G. Electromigration threshold in copper interconnects. Appl. Phys. Lett. 2001, 78, 3598–3600.
Muñoz, R.; Gómez-Aleixandre, C. Review of CVD synthesis of graphene. Chem. Vap. Depos. 2013, 19, 297–322.
Kim, K. S.; Zhao, Y.; Jang, H.; Lee, S. Y.; Kim, J. M.; Kim, K. S.; Ahn, J. H.; Kim, P.; Choi, J. Y.; Hong, B. H. Large-scale pattern growth of graphene films for stretchable transparent electrodes. Nature 2009, 457, 706–710.
Mishra, H.; Panda, J.; Maddu, R.; Sarkar, T.; Dayen, J. F.; Belotcerkovtceva, D.; Kamalakar, M. V. Experimental advances in charge and spin transport in chemical vapor deposited graphene. J. Phys. Mater. 2021, 4, 042007.
Kamalakar, M. V.; Groenveld, C.; Dankert, A.; Dash, S. P. Long distance spin communication in chemical vapour deposited graphene. Nat. Commun. 2015, 6, 6766.
Gebeyehu, Z. M.; Parui, S.; Sierra, J. F.; Timmermans, M.; Esplandiu, M. J.; Brems, S.; Huyghebaert, C.; Garello, K.; Costache, M. V.; Valenzuela, S. O. Spin communication over 30 µm long channels of chemical vapor deposited graphene on SiO2. 2D Mater. 2019, 6, 034003.
Serrano, I. G.; Panda, J.; Denoel, F.; Vallin, Ö.; Phuyal, D.; Karis, O.; Kamalakar, M. V. Two-dimensional flexible high diffusive spin circuits. Nano Lett. 2019, 19, 666–673.
Panda, J.; Ramu, M.; Karis, O.; Sarkar, T.; Kamalakar, M. V. Ultimate spin currents in commercial chemical vapor deposited graphene. ACS Nano 2020, 14, 12771–12780.
Moser, J.; Barreiro, A.; Bachtold, A. Current-induced cleaning of graphene. Appl. Phys. Lett. 2007, 91, 163513.
Murali, R.; Yang, Y. X.; Brenner, K.; Beck, T.; Meindl, J. D. Breakdown current density of graphene nanoribbons. Appl. Phys. Lett. 2009, 94, 243114.
Novoselov, K. S.; McCann, E.; Morozov, S. V.; Fal’ko, V. I.; Katsnelson, M. I.; Zeitler, U.; Jiang, D.; Schedin, F.; Geim, A. K. Unconventional quantum hall effect and Berry’s phase of 2π in bilayer graphene. Nat. Phys. 2006, 2, 177–180.
Lee, K. J.; Chandrakasan, A. P.; Kong, J. Breakdown current density of CVD-grown multilayer graphene interconnects. IEEE Electron Device Lett. 2011, 32, 557–559.
Debroy, S.; Sivasubramani, S.; Vaidya, G.; Acharyya, S. G.; Acharyya, A. Temperature and size effect on the electrical properties of monolayer graphene based interconnects for next generation MQCA based nanoelectronics. Sci. Rep. 2020, 10, 6240.
Kim, K.; Lee, Z.; Regan, W.; Kisielowski, C.; Crommie, M. F.; Zettl, A. Grain boundary mapping in polycrystalline graphene. ACS Nano 2011, 5, 2142–2146.
Fan, X.; Wagner, S.; Schädlich, P.; Speck, F.; Kataria, S.; Haraldsson, T.; Seyller, T.; Lemme, M. C.; Niklaus, F. Direct observation of grain boundaries in graphene through vapor hydrofluoric acid (VHF) exposure. Sci. Adv. 2018, 4, eaar5170.
Grosse, K. L.; Dorgan, V. E.; Estrada, D.; Wood, J. D.; Vlassiouk, I.; Eres, G.; Lyding, J. W.; King, W. P.; Pop, E. Direct observation of resistive heating at graphene wrinkles and grain boundaries. Appl. Phys. Lett. 2014, 105, 143109.
Belotcerkovtceva, D.; Maciel, R. P.; Berggren, E.; Maddu, R.; Sarkar, T.; Kvashnin, Y. O.; Thonig, D.; Lindblad, A.; Eriksson, O.; Kamalakar, M. V. Insights and implications of intricate surface charge transfer and sp3-defects in graphene/metal oxide interfaces. ACS Appl. Mater. Interfaces 2022, 14, 36209–36216.
Yu, T. H.; Lee, E. K.; Briggs, B.; Nagabhirava, B.; Yu, B. Bilayer graphene system: Current-induced reliability limit. IEEE Electron Device Lett. 2010, 31, 1155–1157.
Banszerus, L.; Schmitz, M.; Engels, S.; Goldsche, M.; Watanabe, K.; Taniguchi, T.; Beschoten, B.; Stampfer, C. Ballistic transport exceeding 28 µm in CVD grown graphene. Nano Lett. 2016, 16, 1387–1391.
Verguts, K.; Defossez, Y.; Leonhardt, A.; De Messemaeker, J.; Schouteden, K.; Van Haesendonck, C.; Huyghebaert, C.; De Gendt, S.; Brems, S. Growth of millimeter-sized graphene single crystals on Al2O3 (0001)/Pt (111) template wafers using chemical vapor deposition. ECS J. Solid State Sci. Technol. 2018, 7, M195–M200.
Vera-Marun, I. J.; van den Berg, J. J.; Dejene, F. K.; van Wees, B. J. Direct electronic measurement of Peltier cooling and heating in graphene. Nat. Commun. 2016, 7, 11525.
Breitenstein, O.; Warta, W.; Langenkamp, M. Lock-in Thermography; Springer Berlin, Heidelberg, 2005.
Harzheim, A.; Spiece, J.; Evangeli, C.; McCann, E.; Falko, V.; Sheng, Y. W.; Warner, J. H.; Briggs, G. A. D.; Mol, J. A.; Gehring, P. et al. Geometrically enhanced thermoelectric effects in graphene nanoconstrictions. Nano Lett. 2018, 18, 7719–7725.
Sierra, J. F.; Neumann, I.; Costache, M. V.; Valenzuela, S. O. Hot-carrier seebeck effect: Diffusion and remote detection of hot carriers in graphene. Nano Lett. 2015, 15, 4000–4005.
Bakker, F. L.; Slachter, A.; Adam, J. P.; van Wees, B. J. Interplay of peltier and seebeck effects in nanoscale nonlocal spin valves. Phys. Rev. Lett. 2010, 105, 136601.
Sierra, J. F.; Neumann, I.; Cuppens, J.; Raes, B.; Costache, M. V.; Valenzuela, S. O. Thermoelectric spin voltage in graphene. Nat. Nanotechnol. 2018, 13, 107–111.
Parkin, S. S. P.; Kaiser, C.; Panchula, A.; Rice, P. M.; Hughes, B.; Samant, M.; Yang, S. H. Giant tunnelling magnetoresistance at room temperature with MgO (100) tunnel barriers. Nat. Mater. 2004, 3, 862–867.
Zhang, S.; Levy, P. M.; Marley, A. C.; Parkin, S. S. P. Quenching of magnetoresistance by hot electrons in magnetic tunnel junctions. Phys. Rev. Lett. 1997, 79, 3744–3747.
Levy, P. M.; Fert, A. Spin transfer in magnetic tunnel junctions with hot electrons. Phys. Rev. Lett. 2006, 97, 097205.
Fert, A.; Jaffrès, H. J. Conditions for efficient spin injection from a ferromagnetic metal into a semiconductor. Phys. Rev. B 2001, 64, 184420.
Durkan, C.; Xiao, Z. C. On the failure of graphene devices by joule heating under current stressing conditions. Appl. Phys. Lett. 2015, 107, 243505.
Neumann, I.; Costache, M. V.; Bridoux, G.; Sierra, J. F.; Valenzuela, S. O. Enhanced spin accumulation at room temperature in graphene spin valves with amorphous carbon interfacial layers. Appl. Phys. Lett. 2013, 103, 112401.
Kamalakar, M. V.; Dankert, A.; Bergsten, J.; Ive, T.; Dash, S. P. Enhanced tunnel spin injection into graphene using chemical vapor deposited hexagonal boron nitride. Sci. Rep. 2014, 4, 6146.
Kamalakar, M. V.; Dankert, A.; Kelly, P. J.; Dash, S. P. Inversion of spin signal and spin filtering in ferromagnet∣hexagonal boron nitride-graphene van der Waals heterostructures. Sci. Rep. 2016, 6, 21168.
Gurram, M.; Omar, S.; van Wees, B. J. Electrical spin injection, transport, and detection in graphene-hexagonal boron nitride van der Waals heterostructures: Progress and perspectives. 2D Mater. 2018, 5, 032004.
Friedman, A. L.; van’ t Erve, O. M. J.; Li, C. H.; Robinson, J. T.; Jonker, B. T. Homoepitaxial tunnel barriers with functionalized graphene-on-graphene for charge and spin transport. Nat. Commun. 2014, 5, 3161.
Dayen, J. F.; Ray, S. J.; Karis, O.; Vera-Marun, I. J.; Kamalakar, M. V. Two-dimensional van der Waals spinterfaces and magnetic-interfaces. Appl. Phys. Rev. 2020, 7, 011303.
Acknowledgements
We gratefully acknowledge funding from the European Research Council (ERC) Project SPINNER, Swedish Research Council (VR Starting Grants 2016–03278, 2017–05030, as well as project grant 2021-03675), Stiftelsen Olle Engkvist Byggmästare (No. 200–0602), Energimyndigheten (No. 48698–1), Formas (No. 2019–01326), and Wenner-Gren Stiftelserna (Nos. UPD2018-0003 and UPD2019-0166).
Funding
Open Access funding provided by Uppsala University.
Author information
Authors and Affiliations
Corresponding author
Electronic Supplementary Material
Rights and permissions
This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.
The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Belotcerkovtceva, D., Panda, J., Ramu, M. et al. High current limits in chemical vapor deposited graphene spintronic devices. Nano Res. 16, 4233–4239 (2023). https://doi.org/10.1007/s12274-022-5174-9
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12274-022-5174-9