Abstract
Inverse suspension polymerization method was applied to prepare poly(itaconic acid) based superabsorbent particles. The polymerization process was investigated to determine the influence of different parameters on the water absorption properties. It was found that processing parameters, such as oil/aqueous phase ratio, surfactant, stirring speed, as well as concentrations of initiator and crosslinker needed to be optimized to achieve high water absorbency. The hydrolysis sensitivity of the divinyl crosslinker in water affected the crosslinking efficiency to show better performance with hydrolytically stable diacrylamide than diacrylate. The washing solvent to remove surfactant also highly influence the water absorbency of the prepared SAP particles, and solvent with lower polarity induced the collapse of the pores in the SAP particles to give lower value of water absorbency.
Similar content being viewed by others
References
E. M. Ahmed, J. Adv. Res., 6, 105 (2015).
T. Shimomura and T. Namba in “Superabsorbent Polymers” (F. L. Buchholz and N. A. Peppas Eds.), pp.112–127, American Chemical Society, Washington, D.C., 1994.
Y. Li, H. Shi, H. Zhang, and S. Chen, Peer J., 7, e6073 (2019).
X. Xie, J. Bahnemann, S. Wang, Y. Yang, and M. R. Hoffmann, Sci. Rep., 6, 20516 (2016).
A. Mignon, N. De Belie, P. Dubruel, and S. Van Vlierberghe, Eur. Polym. J., 117, 165 (2019).
C. J. Hong, Text. Sci. Eng., 55, 304 (2018).
T. K. Mudiyanselage and D. C. Neckers, J. Polym. Sci. Part A: Polym. Chem., 46, 1357 (2008).
A. Pourjavadi, M. Kurdtabar, G. R. Mahdavinia, and H. Hosseinzadeh, Polym. Bull., 57, 813 (2006).
W. F. Lee and Y. C. Chen, Eur. Polym. J., 41, 1605 (2005).
H. Omidian, S. A. Hashemi, P. G. Sammes, and I. Meldrum, Polymer, 40, 1753 (1999).
D. W. Lim, K. G. Song, K. J. Yoon, and S. W. Ko, Eur. Polym. J., 38, 579 (2002).
P. Bajaj, T. V. Sreekumar, and K. Sen, Polymer, 42, 1707 (2001).
S. Y. Ko, A. Sand, N. J. Shin, and Y.-J. Kwark, Fiber. Polym., 19, 255 (2018).
E. Riscaldati, M. Moresi, M. Petruccioli, and F. Federici, J. Biotechnol., 83, 219 (2000).
K. Kirimura, T. Sato, N. Nakanishi, M. Terada, and S. Usami, Appl. Microbiol. Biotechnol., 47, 127 (1997).
J. H. Kim, J. S. Kim, J. H. Jang, M. S. Kim, Y.-W. Chang, D. Y. Lim, and D. H. Kim, Fiber. Polym., 17, 671 (2016).
A. Pourjavadi and Z. M. Tehrani, Mater. Sci. Eng. C, 61, 782 (2016).
Z. M. O. Rzayev, M. Şimşek, U. Bunyatova, and B. Salamov, Colloids Surf. A, 492, 26 (2016).
S. Brännström, E. Malmström, and M. Johansson, J. Coat. Technol. Res., 14, 851 (2017).
J. S. Vuković, A. A. Perić-Grujić, D. S. Mitić-Ćulafić, B. Dj. B. Nedeljković, and S. Lj. Tomić, Macrmol. Res., 28, 382 (2020).
J. A. Davies and P. C. Griffiths, Macromolecules, 36, 950 (2003).
S. J. Velićković, E. S. Džunuzović, P. C. Griffiths, I. Lacik, J. Filipović, and I. G. Popović, J. Appl. Polym. Sci., 110, 3275 (2008).
B. E. Tate in “Advances in Polymer Science” (H.-J. Cantow, G. Dall’Asta, J. D. Ferry, W. Kern, G. Natta, S. Okamura, C. G. Overberger, W. Prints, G. V. Schultz, W. P. Slichter, A. J. Staverman, J. K. Stille, and H. A. Stuart Eds.), Vol. 5, pp.214–232, Springer, New York, 1967.
P. Li, J. Zhang, and A. Wang, Macromol. Mater. Eng., 292, 962 (2007).
S. K. Bajpai, M. Bajpai, and L. Sharma, Des. Monomers Polym., 10, 181 (2007).
S. Kiatkamjornwong and P. Phunchareon, J. Appl. Polym. Sci., 72, 1349 (1999).
E. Mendizabal, J. R. Castellanos-Ortega, and J. E. Puig, Colloids Surf., 63, 209 (1992).
H. Hosseinzadeh, A. Pourjavadi, G. R. Mahdavinia, and M. J. Zohuriaan-Mehr, J. Bioact. Compat. Polym., 20, 475 (2005).
G. Bagheri Marandi, N. Sharifnia, and H. Hosseinzadeh, J. Appl. Polym. Sci., 101, 2927 (2006).
J. W. Chen and Y. M. Zhao, J. Appl. Polym. Sci., 75, 808 (2000).
L. Fang, Y. Zhao, and T. W. Tan, J. Polym. Res., 13, 145 (2006).
Acknowledgement
This research was supported by a grant from the Technology Innovation Program (Grant no. 10050526) funded by the Ministry of Trade, Industry and Energy, Republic of Korea.
Author information
Authors and Affiliations
Corresponding author
Supporting Information
12221_2021_459_MOESM1_ESM.pdf
Effects of Reaction Parameters on Water Absorption of Poly(itaconic acid) Superabsorbent Particles Synthesized by Inverse Suspension Polymerization
Rights and permissions
About this article
Cite this article
Sand, A., Shin, NJ., Nam, HG. et al. Effects of Reaction Parameters on Water Absorption of Poly(itaconic acid) Superabsorbent Particles Synthesized by Inverse Suspension Polymerization. Fibers Polym 22, 898–903 (2021). https://doi.org/10.1007/s12221-021-0459-2
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12221-021-0459-2