Abstract
Nylon 4, which can be synthesized by anionic ring-opening polymerization, has good mechanical properties and a very high affinity for water owing to its high polarity. On the other hand, despite its high melting temperature, the polymer has not been commercialized because of its low thermal stability. In this study, copolymerization of 2-pyrrolidone (C4) with 2-piperidone (C5) was performed to reduce the melting temperature of Nylon 4 homopolymer. The copolymerization reaction was controlled by changing the comonomer content, catalyst content, temperature, initiator content, and reaction time. The Nylon copolymers were characterized by 1H-nuclear magnetic resonance (NMR) spectroscopy, differential scanning calorimetry, and thermogravimetric analysis. The hydrophilic properties of Nylon 4 and its copolymers were evaluated by surface free energy analysis and moisture regain measurement. The intrinsic viscosity and polymerization yield of Nylon 4 increased with increasing catalyst concentration until 5 mole% and decreased with further increases in catalyst loading. The proton NMR spectrum revealed the composition of the Nylon 4/5 copolymer to be 62.5 % C4 moiety at a 5:5 comonomer feed ratio. The melting temperature of the Nylon 4/5 copolymers decreased considerably according to the composition. The moisture regain of the Nylon 4/5 copolymer was higher than 6.4 % even at 77.3 % C4 in composition.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
Y. Li and D. Yan, Polymer, 42, 5055 (2001).
W. O. Ney, Jr., W. R. Nummy, and C. E. Barnes, U. S. Patent, 2,638,463 (1953).
N. Yamano, A. Nakayama, N. Kawasaki, N. Yamamoto, and S. Aiba, J. Polym. Env., 16, 141 (2008).
R. Y. M. Huang, U. Y. Kim, J. M. Dickson, D. R. Lloyd, and C. Y. Peng, J. Appl. Polym. Sci., 26, 1135 (1981).
C. E. Barnes, U. S. Patent, 3,721,652 (1973).
W. O. Ney and M. Crowther, U. S. Patent, 2,739,959 (1956).
T. Hisaya and K. Tuyoshi, J. Polym. Sci., 6, 2281 (1968).
F. Kobayashi and K. Matsuya, J. Polym. Sci. Part A, 1, 111 (1963).
S. Bar-zakay, M. Levy, and D. Vofsi, J. Polym. Sci. Part A-1, 5, 965 (1967).
K. Hashimoto, E. Sudo, T. Sugimura, and Y. Inagaki, J. Appl. Polym. Sci., 92, 3492 (2004).
C. E. Barnes, Lenzinger Berichte, 62, 62 (1987).
K. Tachibana, K. Hashimoto, N. Tansho, and H. Okawa, J. Polym. Sci. Part A, 49, 2495 (2011).
N. Kawasaki, A. Nakayama, N. Yamano, S. Takeda, Y. Kawata, S. Aiba, and N. Yamamoto, Polymer, 46, 9987 (2005).
M. Kakuta, M. Hirata, and Y. Kimura, Polym. Rev., 49, 107 (2009).
M. Bermúdez, S. León, C. Alemán, and S. Muñoz-Guerra, J. Polym. Sci., 41, 8961 (2000).
C. E. Barnes, W. R. Nummy, and W. O. Ney, Jr., U. S. Patent, 2,806,941 (1957).
N. Yoda and A. Miyake, J. Polym. Sci., 43, 117 (1960).
S. Chrzczonowicz and M. Wslodarczyk, Die Makromol., Chem., 48, 135 (1961).
G. Champetier and H. Sekiguchi, J. Polym. Sci., 11, 1601 (1973).
R. Bacskai, U. S. Patent, 4,107,154 (1978).
N. C. Kim, J.-H. Kim, S. W. Nam, B. S. Jeon, Y.-T. Yoon, and Y. J. Kim, Polymer (Korea), 37, 211 (2013).
Y. Tamai, K. Makuuchi, and M. Suzuki, J. Phys. Chem., 71, 4176 (1967).
L. Ricco, S. Russo, G. Orefice, and F. Riva, Macromol. Chem. Phys., 202, 2114 (2001).
Gh. Rusu, M. Rusu, E. Rusu, A. Stoleriu, and C. A. Teaca, Polym.-Plast. Tech. Eng., 39, 233 (2000).
J. Kondelkova, Z. Tuzar, J. Kralicecck, K. Sandova, M. Strohalmova, and V. Kubanek, Angew. Makromol. Chem. 64, 123 (1977).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kang, KS., Hong, YK., Kim, Y.J. et al. Synthesis and properties of Nylon 4/5 copolymers for hydrophilic fibers. Fibers Polym 15, 1343–1348 (2014). https://doi.org/10.1007/s12221-014-1343-0
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12221-014-1343-0